By Elizabeth M. Ho

Oxidants are added in uranium leaching in acid media to convert iron(II) in solution to iron(III). Iron(III) has an important role in the leaching of uranium by acting as an electron transfer agent for the oxidation of uranium(IV) to uranium(VI). The oxidation of iron(II) to iron(III) in sulfate solutions using sulfur dioxide/oxygen (SO2/O2) was carried out under typical uranium leaching conditions (pH 1-2, 20-50°C) to confirm literature trends and this work was then extended to the use of SO2/O2 in the leaching of uranium ore. The oxidation rate was found to be dependent on the initial SO2/O2 volumetric ratio and the oxygen mass transfer rate, but was independent of the initial iron(III) concentration above about 200 ppm at pH 2. The presence of 55 ppm organic extractant (Alamine 336) decreased the reaction rate. The oxygen mass transfer coefficient (kLa) for the mixing tank system was measured and was found to decrease with increasing solids density in a 1 g L-1 MgSO4.7H2O solution.

Jan 1, 2003

By R Bartlett

Process engineering-science originally developed for percolation leaching of ore in heaps is extended to the decontamination of unsaturated soil, either in situ or after excavation and emplacement as a soil heap on an impervious pad. Phenomena considered include: soil matrix porosity and permeability; percolating solution retention, capillarity and flow; washing sweep efficiency; optimum solution application rates during leaching; soil agglomeration to improve soil permeability and soluble contaminant transport by diffusion in soil agglomerates. Practical aspects briefly discussed include leach pad construction, solution distribution and recovery from the soil, and solution containment.

Jan 1, 1994

By James T. Skoch

With the ongoing pressure on the secondary aluminum business to limit the amount of waste generated from processing aluminum dross, it becomes very advantageous to preprocess the dross to reduce waste. The advantage of preprocessing is that it significantly reduces the oxides and salt cake generated when melted. Various products can be produced from the oxides for the steel industry. The following paper will demonstrate that removal of oxide fines before melting will result in large volumes of material not being landfilled. We will show that the end result of this technology is to significantly reduce the amount of salt cake sent to a landfill while maximizing the recyclability of the aluminum dross.

Jan 1, 1995

By Olga Karabelchtchikova

Keywords: Multipass grinding, Residual stress, Retained austenite, X-ray diffraction The study investigated residual stresses behaviors and their superposition effect in D2 dies for thread-rolling applications. A nested factorial experiment was applied to test hypotheses that the residual stresses profiles change due to combination of heat treatment and multipass grinding operations, and that certain patterns can be derived due to the memory relationship between pre-existing and final residual stresses distributions. The amount of the retained austenite along with residual stresses in variation with depth was measured using x-ray diffraction technique. Statistical analyses indicate that the proposed hypotheses hold. Residual stresses distributions as well as tensile peak location were found to be significantly influenced by the treatment parameters used. Unique characteristic patterns in the residual stresses profiles were observed due to multipass grinding technique across all experimental conditions. This finding suggested a plausible memory relationship between the cutting passes, and the causes of the foregoing results are further proposed and discussed.

Jan 1, 2005

By Yurniko Nakamura

Hydriding properties and crystal structure of a Ti-V- Mn solid solution alloy have been studied by P-C isotherm measurements and neutron and X-ray powder diffraction. The absorption P-C isotherm at 298K shows two plateau regions at 0.01MPa and 1MPa. The X-ray diffraction data have demonstrated that three phases with a BCC, a pseudo-cubic FCC and an FCC structure form subsequently with increase of the hydrogen content. Crystal structure of the latter two phases has been determined by Rietveld refinement of the neutron diffraction data. The FCC phase is the di-hydride of CaF2 type with hydrogen occupation in the T sites. The pseudo-cubic FCC phase is the mono-hydride of NaCl-type with hydrogen occupation in the 0 sites, which has not been reported so far. The lattice constants of the mono-hydride (Ti1.0V1.1Mn0.9)H_2.7 are a'=0.407 nm for two axes and c'=0.390 nm for the third axis. The a'axis is shorter by 4% than the c'axis. This pseudo-cubic FCC lattice is formed by contraction of 5% of the a axis and expansion of about 30% of the c axis from the original BCC lattice.

Jan 1, 2002

By Dimitrios Fillippou

Magnesium hydroxide is used in a number of industrial applications, from the neutralisation of acid effluents to the production of pharmaceuticals. High-quality magnesium hydroxide powders can be produced by hydrating slow-reacting magnesia in dilute magnesium acetate solutions. The process of magnesia hydration shows many similarities with a typical hydrometallurgical leaching operation; however, its kinetics are crucial not only for process design and control, but also for the production of powders with a desirable particle morphology. This article shows the results of an experimental work whereby industrial heavily-burned magnesia powders were hydrated in 0.01 to 0.1 mol/L magnesium acetate solutions at temperatures ranging between 333 and 363 K. Examination of the magnesium hydroxide produced and the analysis of the kinetic data suggest that the hydration of heavily-burned magnesia in magnesium acetate solutions is a dissolution-precipitation process controlled by the dissolution of magnesia particles. The activation energy was estimated to be 60 kJ/mol, while the reaction order with respect to magnesium acetate concentration was found to be about one.

Jan 1, 1999

By Andre L. De Vegt

For the past eight years Paques has been engaged in the development and installation of treatment systems based on biotechnological processes to remove sulfur compounds from water, air and gaseous streams. Metal and sulfate can be removed from mine waters using two biological steps: 1. Sulfate reducing bacteria convert sulfate to hydrogen sulfide (HzS). The HzS reacts with the dissolved metals to form insoluble metal sulfide precipitates. 2. Sulfide oxidizing bacteria convert excess H2S to elemental sulfur. Paques has designed and installed a groundwater treatment system for the Budelco zinc refinery in the Netherlands to remove metals and sulfate as described above. The system has been operating since May 1992 treating a flow of 5000 m3/d. A test program, utilizing a large scale pilot plant, will commence in November 1995 at a copper mine in the U.S.A. to remediate groundwater contaminated with sulfate and heavy metals. Biological reactor performance and selective metal recovery will be studied. Sulfur dioxide (S00 can be removed from fluegas using a combination of scrubber technology and the two biological steps. The end product is elemental sulfur. A commercial size biological desulfurization plant has been in operation since July 1994 treating 50,000 Nm3/h of fluegas. Sulfide can be removed from mining waters or anaerobic wetlands using a THIOPAQ® Sulfide Oxidizing reactor.

Jan 1, 1996

By Z. Yang, R. W. Smith, Jr. Wharton

"Microorganisms have the ability to remarkably adsorb and/or absorb heavy metal ions. Hence they are being studied widely as a means of removing metal ions from aqueous solutions both in order to clean up toxic streams and to recover valuable metals from these and other streams. It is often difficult to harvest organisms such as bacteria and unicellular algae since they are usually too small to be readily screened out. Froth flotation may prove to be a feasible method to harvest such organisms subsequent to the ad/absortion of the metal Ions. The present paper discusses the surface/electrokinetic properties of microorganisms and the modifier-collect conditions under which they should float. The zeta potential of the green alga Chlorella vulgaris was measured in the presence of AI(III) and Pb(II) ions and in the presence of dodecylammonium chloride and sodium dodecylsulfate. Present and past data suggest that the organisms should behave similarly to other finely divided, charged (polar) solids with their behavior sometimes modified by the non-polar surface regions present.IntroductionThe overall field of bioengineering is growing at a remarkably accelerating rate. Hydrometallurgy and mineral processing are included among those disciplines where there has been actual or proposed commercial use of bioorganisms. Further, the actual or proposed use includes bacterial enhancement of leaching of a number of different types of ores (1-5), modification of the flotation or oil agglomeration separation of minerals by bacteria (6,7) and microorganism (algae, bacteria or fungi) concentration of metal ions present in effluent or other mineral processing or hydrometallurgy aqueous streams (8-23)."

Jan 1, 1988

By Thais Cristina da Costa Caldas, Alline Sardinha Cordeiro Morais, Carlos Maurício Fontes Vieira, Sergio Neves Monteiro

"This work has as its objective to evaluate the firing behavior of a kaolinitic clayey body from Campos dos Goytacazes-RJ incorporated with flat glass waste (FGW) from civil construction. Incorporations of the waste, with a particle size less than 74 µm (200 mesh), were performed in the red ceramic in the following amounts: 0, 2.5, 5 and 10 wt%. Specimens were prepared by uniaxial press-molding and then fired at 850 and 1050°C. The characterization of FGW was done by X-ray Fluorescence. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural rupture strength. The microstructure of the fired ceramics was evaluated by optical microscopy (OM). The obtained results showed that the flat glass waste can be used as a component of ceramic bodies once it was noticed tolerable modifications of technological behavior.IntroductionBrazil is one of the world’s largest producers and consumers of clayey ceramic. Campos dos Goytacazes is located in the north of the State of Rio de Janeiro, southeast of Brazil, it’s known as a large producer of red ceramics. It is estimated that the production of bricks can reach 1 billion pieces per year [1].Nowadays, recycling processes became more and more important, due the generation of wastes in large scale and the preoccupation with environmental. The amount of glass waste has been exponentially growing with the growth of the population. It is estimated that the amount of discarded glass as bottles, construction windows, packing and other glass waste represented in 2006 an amount of 7.5% of the total weight of the world´s domestic garbage [2]."

Jan 1, 2012

By J. M. Skeaff

As much as 100% of the gold and 67% of the silver in a sulphur-bearing hydrometallurgical leach residue have been transferred to copper metal at copper smelting temperatures by dissolving the partially calcined residue in an iron-bearing slag maintained in equilibrium with the liquid copper metal and matte phases. The precious metals can then be recovered by conventional refining techniques. Copper can be recycled at least four times without any detrimental effects on gold and silver transfers and recoveries. Apparent copper recovery in the .process can be over 100% because of the copper content of the residue. Based on slag analys.es, the overal1 recovery of gold in the copper metal and matte phases varies from 94% to 100% under all conditions investigated. On the? same basis, silver recovery varies .from 9S% ?to 99% under optimum conditions, but is only 4S% to 73% under other, less attractive conditions. Unaccounted for silver losses of' about 30% make it difficult to determine the major factors affecting ?silver transfer and recovery. A method for implementing the technology on a commercial scale at a Canadian copper/zinc smelter has been proposed. A preliminary economic assessment and comparison of the proposed pyrometallurgical process with conventional cyanidation indicates that either process is economically attractive for recovering gold and silver from leach residues. Although the capital costs are higher, the pyrometallurgical process is simpler, has higher recoveries, lower operating costs and no .potential environmental problems related to cyanide disposal.

Jan 1, 1989

By Liyuan Chai, Bing Peng, Ji Peng, Di Yu

"Electric arc furnace (EAF) stainless steel dust has been classified as a hazardous waste by various government regulatory agencies as it releases heavy metals to environment. The solidification of EAF dust is to stabilize the hazardous components to the amorphous silica-alumina-based clays. The process of solidification is investigated and the softening temperatures of dust and additive clay mixtures are measured for economical thermal treatment. The results indicate that the mixture of dust and local clay with the ratio of 1:1 has the lowest softening temperature 1100 °C and it could pass the toxicity characteristics leaching procedure (TCLP) test for the environmental regulatory limits after thermally treated at softening temperature for 15 min. Major phases of thermal solidification product clinker are CaAl2Si2O8, (Fe, Cr)2O3, (Fe, Mg)(Cr, Al)2O4 and Al6Si2O13.IntroductionThe yield of stainless steels in China arrived to 10 million tons in 2006 and more than 0.2 million tons of stainless steel dust are produced annually. Approximately 1-2 wt.% of scrap charged to an electric arc furnace (EAF) enters the off-gases and then is converted into the dust and reported to the bag-house. The disposal or landfill of the dust becomes a serious environmental problem in China due to the increased production of stainless steels in recent years. The dust contains elements such as chromium (Cr), nickel (Ni), lead (Pb), zinc (Zn), cadmium (Cd) and their solubility in leaching media exceeds the environmental regulatory limits [1]. Even though easily feasible for low-grade MgO, it is not appropriate to stabilize the heavy metals from the heavily contaminated soils after the dust landfill [2]. Several dust treatment technologies have been developed and they can be divided into two types. One is to recover the metals from the dust [3, 4] and another is to stabilize hazardous components present in the dust [5, 6]. Recycling of the dust generated in EAF is a remediation option for cleaner production. Direct recycling of EAF stainless steel dust was developed to recover the metal value from the dust and protect the environment [7], but it was only suitable for the dust with high contents of Ni, Cr and Fe. As for the dust with low valuable metal content, thermal solidification is an appropriate choice for the dust treatment."

Jan 1, 2012

By Jiling Wang, Xuefeng Liu, Haojian Duan, Lifeng Zhang, Ying Ren, Wen Yang

"In order to study the influence of MgO-C refractory on steel cleanliness and inclusions during steelmaking process, and to understand the reaction mechanism deeply, laboratory deoxidation and equilibrium experiments were respectively performed in MgO crucibles at 1873K. In the former experiment, after Al addition, steel samples were taken at different holding time. In the latter experiment, different slag components and different contents of carbon and aluminum in steel were considered respectively. The inclusion characteristics of each experiment were analyzed. The results showed that with the increasing of holding time after deoxidation by Al, MgO existed in the small inclusions firstly, and then in the large ones such as the clusters. The MgO content in the inclusions increased with the increasing of holding time, indicating that the MgO in crucible could be individually reduced by the aluminum in the molten steel. The reaction could occur within nine minutes.IntroductionNon-metallic inclusions would have positive or negative effect on steel quality depend on the quantity, size and composition of inclusions. Large inclusions are always detrimental. From the point of view of inclusion property, plastic inclusions are required by steel cord, while hard inclusions are preferred by pipeline steel. One of the most important ways to increase the steel quality is reducing the inclusion size and controlling the inclusion composition in steel. Nowadays, MgO based refractory is used as ladle glaze material with more and more frequency, which results in different inclusion characteristics in molten steel, for example, the inevitable generation of MgO contained inclusions during ladle treatment of steel. In other words, the inclusions in this type ladle will influence on the steel cleanliness and the product property. Thus, keeping an eye on the inclusion formation behavior in the steel with MgO-C ladle glaze is important for the steel industry. There have been a few studies in this regard. Li et al[l] studied the reactions between MgO-C refractory, molten slag and metal using a high temperature X-ray radiographic apparatus. They found that the local corrosion was regarded as due to the cyclic dissolution of MgO and graphite in the refractory into slag and metal phase. The gas bubbles formed according to the reaction of (FeO)+C(s)=Fe(l)+CO(g) greatly influenced the corrosion. On an industrial scale, Du[2] found that ladle glaze is a major source of inclusions in the ladle. An experimental study has been performed by Lehmann in order to estimate the importance of the reaction between a MgO-based tundish refractory and an Al-killed steel[3]."

Jan 1, 2014

By Petrus Christiaan Pistorius, Farzin Fatollahi-Fard

The production of titanium oxycarbide – a consumable anode material used in molten-salt processes for electrowinning titanium – from heavy mineral concentrate, such as a high-titania leucoxene and natural rutile is described. The oxycarbide is prepared by carbothermic reduction of the oxide at elevated temperature. Particle size distribution (of the titanium oxide raw material) and temperature have large effects on the kinetics of the reaction, which seem to follow a “shrinking-core” model. It is anticipated that low porosity (in the anode pellets) would be advantageous during electrolysis. Particle size distribution, extent of reaction during carbothermic reduction, and sintering temperature are expected to affect pellet porosity after sintering, and are being tested experimentally.

Jan 1, 2015

By Douglas M. Matson, Rongbiao Gu, Christopher San Marchi, Anil Saigal

"Hydrogen embrittles most structural metals, although the form and magnitude of embrittlement depends on the source of the hydrogen as well as the stress in the metal. Hydrogen fuel cell systems typically store gaseous hydrogen fuel at high-pressure, which provides both a source of hydrogen and high stresses in the containment materials. Understanding and measuring the effects of hydrogen on the mechanical properties of common structural metals, especially fatigue properties, is important for safe, long-term operation of such systems. This work explores the use of thermography to efficiently and quantitatively evaluate hydrogen-assisted fatigue of type 304 austenitic stainless steel. In particular, thermographic analysis was used with rotating-beam fatigue testing and shown to provide repeatable results which are in general independent of test cycle frequency while reducing test times by several orders of magnitude. The effects of hydrogen were studied by thermally precharging fatigue test specimens in gaseous hydrogen prior to thermography-assisted fatigue testing and then compared to testing of non-charged specimens. Hydrogen-precharging increased the strength of this type 304 austenitic stainless steel and increased the fatigue life by a factor of about 50-100.IntroductionThe world is facing a severe energy and environmental challenge: how to provide competitive and clean energy for its citizens in light of an escalating global energy demand and concerns over energy supply security, climate change and local air pollution. As a carbon-free energy carrier, hydrogen provides a promising vector for storing and distributing renewable energy. Hydrogen is an important industrial gas that is used extensively in many industries. However, with growing demand for clean energy, hydrogen fuel cell systems are being developed for use in consumer products, such as fuel cell vehicles, which changes the landscape for safe design of high-pressure gaseous hydrogen systems."

Jan 1, 2012

By Huayi Yin, Wang. Dihua, Wei Xiao, Xuhui Mao, Diyong Tang

"The world production of crude steel reached 1.55 billion tons in 2012,which generated ~2.5 billion tons of CO2. Electrochemical metallurgy especially through high temperature molten salt electrolysis with renewable electricity stands for a great opportunity for producing “green” metals. In recent years, electrolytic production of iron without emission of CO2 in different molten salt systems has been reported. A cost-affordable inert anode is the key to produce acceptable eco-friendly iron by the novel molten salt electrolysis processes. Based on the authors’ research, this paper will discuss iron production by molten salt electrolysis using a nickel alloy inert anode. On the other hand, the paper also covers a novel molten salt CO2 capture and electrochemical transformation (MSCC-ET) process, in which CO2 is effectively converted to value-added carbon and oxygen in a molten bath using a cost-affordable nonconsumable SnO2 anode.1. IntroductionEnergy and materials are cornerstones to support the development of human society. The traditional primary metal production, especially iron and steel, and electricity production are mainly based on the reactions between carbon (coal) and oxygen (represented by equations (1) and (2) respectively), which produce huge amount of CO2.MxOy + 0.5y C = x M + 0.5y CO2 (g) + Q1 ( 1 )C + O2 (g) = CO2 (g) + Q2 ( 2 )In 2012, the world production of crude steel reached 1.55 billion tons, of which 46.3 %, ~0.7165 billion tons were produced in China. Based on the average level of 1.7t CO2 emission per ton steel, more than 1 billion tons of CO2 generated from steel industry in China in the year. Besides the iron and steel industry, thermal power plant leads the CO2 emission in both USA and China. The total consumed electricity in China increased to 4959 billion kWh in 2012, ~70% of it was from coal fired power plant. The average CO2 emission for electricity production in the typical thermal power plant in China is around 0.78 kg kWh-1. It accounts for ~ 3.868 billion tons of CO2 emission from thermal power plant in 2012 in China."

Jan 1, 2014

By Regina Maria Pinheiro

This work has for objectives to characterize a waste generated in the form of sludge during the treatment of the effluent of a paper making industry and to evaluate the effect of its incorporation in the amount of 10 wt.% on the properties and microstructure of a clayey body used for brick production. For the characterization of the waste the following techniques were used: X-ray diffraction, X-ray fluorescence, differential thermal analysis and termogravimetric analysis. Incorporated bricks were produced in industrial scale before firing at 750°C in a Modified Caieira type furnace. The physical and mechanical properties evaluated were water absorption and compression strength. The microstructure of the fired ceramic was evaluated by optical microscopy. The environmental evaluation was made by solution test and atmospheric emission by monitoring the release of SO2, NOx and particulate material. The results showed that, in agreement with the characteristics of the waste, its recycling into red ceramic can contribute to decrease the consumption of fuel during the firing stage. The properties of the fired ceramic attend the norms. With respect to the environmental aspect, the incorporation of the waste did not impact the environment.

Jan 1, 2009

By Kurt Westerlund

Three. years operating experience of the FLUXFLOW waste heat boiler (WHB) 20.000 nm /h at Boliden Ronnskar Sweden on a TBRC smelting palena (PbS). Operating experience from the Kivset flash WHB 11.900 nm /h at Samim, Porto Vesme, Sardinia, Italy. Conceptual features of the 93.600 nm3 /h FLUXFLOW (WHB) on the Isasmelt smelting in melt furnace for 180.000 t Cu/a at Mount Isa, Australia.

Jan 1, 1992

By P. A. Rusin

Many manganiferous silver deposits remain undeveloped because standard chemical extraction methods yield poor recoveries or are ' environmentally unacceptable. Biotreatment of such ore deposits in our laboratory resulted in manganese and silver recoveries of greater than 90%. Ore and sediment samples were collected from mining sites in Colorado and Arizona. Portions of samples were incubated in a semi-solid mineral salts medium amended with 20 mM glucose mid manganese dioxide (Mn medium). The cultures were incubated at 3(fC until manganese reduction was detected by a .color change fr:om .black to clear. Bacteria from these cultures were purified on Tryptic Soy Agar and individual isolates were retested for Mn reduction by an agar overlay method. Bacteria were identified according to Bergefs Manual ?of Systematic . Bacteriology. Most of the Mn-reducing bacteria are Bacillus species. Bacterial manganese reduction kinetic experiments were performed in 52 ml mineral salts broth supplemented with manganiferous silver ore instead of manganese dioiide. These cultures were incubated with agitation for 16 d. Aliquots were removed periodically and analyzed for solubilized manganese by atoniic absorption (AA). Cyanide (1,0 M) Vias added to the remaining ore-medium mixture for a 24 h bottle roll. The supernatant was analyzed for soluble silver by AA. Similar experiments were conducted on a larger scale using 15% pulp density. After bfotreatment of the ore, standard bottle rolls were performed. The pregnant solutions and the residues were analyzed for manganese and silver?using AA or fire assay as appropriate. In sterile. controls-which received no biotreatment, manganese and silver recoveries were 0.3% and 10% respectively; During biotreatment, total manganese solubilizatiori was as high as 99.8%. The reduced manganese could . be stripped from ?the growth medium using hydrometallurgical techniques. Silver recovery vaned from 70% to 92.5%. Microbial treatment of refractory mangairlferous ores can result in high recoveries of manganese and silver. Retention time varies depending upon the relative concentrations of manganese, silver, and other metals in the ore with only two days required in some cases, The biotreatment of ore is environmentally' acceptable while the use. of chemicals such as sulfur dioxide is less so.

Jan 1, 1991

By Frank Field, Randolph Kirchain, Elisa Alonso, Richard Roth, Nathan Fleming

"High material prices and price uncertainty can be harmful to manufacturing firms. Increased use of recycled materials, industry-wide, can lower both material prices and price variability; moreover, increased recycling decreases the use of primary material, which mitigates price increases due to scarcity effects. These stabilizing and price lowering effects are explored using an Aluminum industry model. We show that (a) increased recycling leads to smaller price fluctuations in the presence of a primary metal supply perturbation, and (b) that the more substitutable the secondary metal is for the primary metal, the lower the overall material price is.IntroductionThe price of an industrial metal is expected to be a function of both the marginal cost of extraction and its scarcity[l-2]: where scarcity can be defined as the degree to which anticipated demand exceeds the known supply. Recycling end-of-life metal increases the apparent supply of the metal, or-in a functionally equivalent, but alternative conception-lowers the demand for primary metal; this lowers primary metal scarcity and should, theoretically, reduce its price. To the extent that this theoretical prediction holds true, recycling can provide benefits to consumers of industrial metals in the form of lower prices.Using a platinum industry model, prior work by Alonso[3] has shown that increased industrywide recycling can reduce metal price volatility because the secondary metal production (a) offsets virgin metal depletion, and (b) responds to supply-demand balance fluctuations more rapidly than the primary market. However, Platinum is not a typical industrial metal in the sense that secondary metal is perfectly substitutable for primary metal: Both primary and secondary platinum metal are functionally equivalent and have a common price. Other metals, such as secondary aluminum which is used as an example case in this study, contain varying degrees of other elements that were either intentionally added, or were inadvertently mixed in with the metal during the scrap recovery process. Consequently, different grades of scrap exist that have different profiles of elements in their composition. Depending on their particular profile of elements, more or less of a given grade can be used as a mass fraction of the final alloy-the secondary metal is not perfectly substitutable for the primary metal. For the purposes of this paper, the aluminum mass fraction of the final alloy that can be made up of secondary aluminum is termed the secondary substitutability of that grade in that alloy."

Jan 1, 2011

By Ximeng Zhu

In the transpassive region, about 0.4 to 0.8 V (SCE), aggressive oxidation of pyrite occurred. The reaction products in this region were Fe(III) oxide, sulfate ion and partially oxidized sulfur intermediates. The growth kinetics of the reaction product film, resulting from transpassive oxidation of pyrite were studied using chronoamperometry measurement with both stationary and rotating disk electrodes. The effect of electrode rotation speed, solution pH and temperature were examined. Potentiostatic measurements were well correlated by a paralinear rate equation, suggesting the formation of an intermediate passive film, associated with the simultaneous dissolution of the outer layer of the film. Activation energies of 66.17 kJ/mole (15.83 kcal/mole) and 38.67 kJ/mole (9.25 kcal/mole) were obtained for associated parabolic and linear rate constants respectively, at an applied potential of 0.6 V.

Jan 1, 1993