By Marco Pasetto

The possibility to re-use marginal materials (by-products) deriving from industrial activities in the construction of road infrastructures, as total or partial substitution of natural aggregates, successfully combines demands for economy and environmental sustainability. The paper presents the results of a laboratory study, conducted at the Experimental Road Laboratory of the University of Padova, to verify the suitability of a particular type of electric arc furnace slag to be recycled in the lithic skeleton of high-performance asphalt mixes (porous asphalt, high modulus mixes, stone mastic asphalt, nonskid surfacings) for road and airport flexible pavements. the process of transformation of iron and steel slag into a product that can be used in road building is described, along with the characterisation of the mixtures, plus an analysis of the results of a wide battery of mechanical-performance tests. This study forms part of wider theoretical ? experimental research being done at the University of Padova in order to improve knowledge of the characteristics of succedaneum materials and check their possible applications in road and airport construction.

Jan 1, 2006

By B. J. Beaudry

The effect of various levels of purity of the rare earth fluorides and the calcium reductant used to prepare rare earth metals were determined. Metals which have low melting points such as La, Ce, Pr and Nd are not purified by distillation or sublimation. Impurities in the reactants remain as contaminants in these metals. Gd, Tb, Y and Lu which have slightly higher vapor pressures at their melting points than the first four metals are usually distilled to remove the Ta or W impurity introduced by the crucible and are purified slightly with respect to 0 and N by distillation. Rare earth metals that have high vapor pressures such as Sc, Dy, Ho and Er can be purified with respect to 0, N, C, as well as Ta or W by sublimation. The most volatile rare earth metals Sm, Eu, Tm and Yb are readily purified by sublimation and are usually prepared by a reduction-distillation process directly from the oxide. The importance of each step of the processes in determining the final purity of the individual rare earth metals is discussed.

Jan 1, 1989

By Y. W. Miao

Along the south-west coast of Taiwan is about 550,000 metric tons of heavy sand deposit containing about 10 % black monazite. The Institute has developed a separation process to recover the individual rare earths and the developed process has been commercialized by a local private company. The decomposition of the local black monazite by sodium hydroxide through hydrothermal and fusion methods has been investigated. In the hydrothermal process 4.5 wt. % of aqueous alkali solution was used in an autoclave. In the fusion process, caustic soda (9.8% NaOH) was employed in am open cylindrical reactor. The same product of hydrous rare earth oxides were obtained and then dissolved by hydrochloric acid and the p-H adjusted in order to separate the thorium from the rare earths. After filtration, the filtrate contained rare earth chloride and the cake contained mainly the silica and thorium hydroxide. Both methods give a yield of 90 % with respect to the rare earths recovery. A detailed description of operation and comparison of the two methods are given.

Jan 1, 1989

By Katsunori Yamaguchi

The zinc, lead and alumina contents in copper smelting slag are increasing with the increase in waste recycling. The recovery of base metals such as lead and zinc from copper converter slag is important from both an economical and environmental perspective. As a fundamental study of the metal recovery by reduction process, activity coefficients of ZnO and PbO in the CaO-SiO2-FeOx-5mass%AlO1.5 slag under iron saturation at 1573K are derived from the data of slag-metal equilibrium experiments. On the basis of the obtained data, the activity coefficients of ZnO and PbO in the CaO-SiO2-FeOx-5mass%AlO1.5 slag were compared with those of the CaO-SiO2-FeOx ternary system. Addition of alumina increases activities coefficient of ZnO and PbO in SiO2 rich side of the slag, and decreases them in CaO rich side.

Jan 1, 2006

By S. Motoiu

Data acquisition is widely used for controlling flash smelting furnaces. A Romanian smelter from which a large amount of data can be collected uses such a technique. A computer program was developed for interpretation of the data. Inputs to the program are the process data files. Abnormal data are identified using standard statistical techniques; they can be edited if necessary. The following methods can be used for the analysis: linear correlation (single or multiple), polynomial correlation or comparison of two average values. Time variation graphs and histograms can be displayed. The random balance method was used for determination of significant parameters influencing the process performance. Not all process parameters are recorded, and some of them are not even measured. The software can compute some of these parameters such as: air flow rate required and the oxygen content of the gas: exiting the reaction tower. The software was used for the interpretation of a large amount of process data. The analysis showed that the process did not operate properly at some times.

Jan 1, 1999

By Roberto Parra

The wear and corrosion phenomena in the furnace lining of the ferrous and non ferrous pyrometallurgical processes are complex problems where chemical, interfacial and mechanical phenomena are presents. The characteristics of the processes determine the conditions to which these materials are submitted, where the thermal conditions reached during the operation is one of the most important parameter. Assuming that all the degradation phenomena are thermal activated, the rate of the different steps of the wear mechanism will depend on the thermal field in the lining. In view to apply the independent physicochemical knowledge of degradation mechanisms to the analysis and design of furnace lining the methodology of the Nodal Wear Model (NWM) was done. It combines the mathematical modelling of the heat transfer in the lining with the physicochemical control equation for the wear-corrosion phenomena. The NWM has been applied to different examples: theoretical analysis, laboratory scale test and industrial applications. We present in this paper the theoretical background of the model and two examples of applications: the sole of an electric furnace and the earth of a blast furnace.

Jan 1, 2006

By David G. Dixon

From its first implementation for the recovery of gold from low-grade ores by cyanidation in the early 1970s, heap leaching has developed into a key hydrometallurgical technology, in conjunction with solvent extraction and electrowinning, for the recovery of base metals, including most notably copper from both oxides and secondary sulphides, and more recently, nickel and zinc. And, given recent advances in bioleaching with thermophilic microbes, the successful application of heap leaching technology to low-grade primary copper ores seems only a matter of time. However, with each new development, it becomes increasingly apparent that the successful application of heap leaching technology will ultimately depend on our having an ever more complete understanding of the fundamental processes underlying it. Much work has been done toward the development of this understanding, on many different fronts. In this paper, a critical overview of heap leach modeling work to date is presented in terms of the most important phenomena which occur during heap leaching, and potential directions for future work are discussed.

Jan 1, 2003

By G. Achurra

The products of the smelting of copper concentrates in an El Teniente Converter (CT) are a high grade matte, analyzing 74-76% Cu; and a highly oxidized slag, typically containing 15-20% Fe3O4 and 4-10% Cu. The El Teniente Division of CODELCO¬CHILE has developed a slag reduction-cleaning process, that is practised in a tilting, horizontal furnace, to recover copper from these slags. The El Teniente slag cleaning process has been successfully implemented at the El Teniente Caletones smelter and various other smelters in Chile: Today, eight such slag cleaning furnaces, each with a capacity of 800-1000 tonnes/day, are in operation in Chile. This paper discusses basic laboratory research and industrial tests that led to substantial reductions in the slag cleaning cycle time and the specific consumption of fuel and reductants. Simultaneously, the slag cleaning off-gas quality was improved. Based on the experimental results, recommendations were made to improve the practice of the El Teniente slag cleaning process. The recommended modifications have been fully implemented at the Caletones smelter.

Jan 1, 1999

By Steven E. Follin

In-situ leaching is commonly used to recover uranium from low-grade deposits in sandstone formations. Acceptable recovery rates can only be obtained if the formation retains its permeability during leaching. Field experiences indicate that microbial growth, stimulated by the leaching pro- cess, can cause plugging problems. To investigate this hypothesis, leach solution and solid samples from well casings and submersible pumps were obtained from four in-situ mining sites. Chemical and microbiological analyses were performed. Bacillus species, Micrococcus species, pseudomonads, and xanthomonads were isolated from these samples. A mixed culture of these organisms was inoculated into a uranium core that was being leached in the laboratory. The permeability of this ore sample decreased to one-third its original value after 16 days. The addition of hydrogen peroxide (0.2 g L-1) to the leach solution killed the microbes and restored the permeability to its original value. This suggests that periodic injection of hydrogen peroxide into production wells may reduce microbial plugging in these wells and the immediate surrounding formation.

Jan 1, 1985

By Khosrow Nikkhah

Increasingly ion exchange systems are being included in design of hydrometallurgical plants for metal extraction or impurity removal. Because such systems operate sequentially and are based on resins that exchange one ion for another, store it temporarily and release it to a regenerating solution, the usual steady state heat and mass balancing tools and spreadsheets cannot be used to design them successfully. This paper outlines the role of dynamic simulation in design of ion exchange systems. Examples are given for use of dynamic simulation in design and investigation of equipment based on consideration of the effect of input criteria such as expected ion loading and elution profiles. The methodology for dynamic modeling using IDEAS in design of multi column ion exchange trains operating in parallel is presented. Results shown include the non-steady state distribution of extracted metal and limitations imposed on operating conditions. These conditions include proposed sequencing of columns for loading and elution cycles, loading, elution and recycle flow rates as well as size and choice of related ion exchange plant equipment.

Jan 1, 2003

By N. Kanarin

A thermodynamic study is reported on the chlorination of Fe(1-x.)O, Fe2O3, Cr2O3, MgO, Mg2SiO4 with chlorine in the presence or the absence of reducing atmospheres. The reactivities of these compounds as well as that of Mg3Si2O5(OH)4 using Cl2+N2, Cl2+air, and Cl2+CO gas mixtures were studied by non isothermal thermogravimetric analysis between 20 and 1000 °C. The same solids were chlorinated in a horizontal experimental set, during two hours between 350 and 1000 °C, in reducing and oxidizing atmospheres: The chlorination products were examined by XRD and SEM, and possible reaction paths were examined. Results indicate that the carbochlorination of these solids was better than their chlorination; Furthermore, the carbochlorination was performed at lower temperatures than those of the chlorination. Finally, the reaction extent was higher in the case of carbo-chlorination of these compounds. Based on these results, a process was suggested for the selective recovery of chromium compounds from the chromite concentrate.

Jan 1, 1995

By L. Béjar-Gómez

The aim of this research work is to study and characterize the precipitates in structural microalloyed steel by transmission electron microscopy and analysis by low resolution. Microalloyed steel with niobium was produced by casting in an electrical induction oven of 25 Kg capacity. Carbon content in steel was less than 0.1 % and 0.036% of niobium. Steel was processed thermomechanically; reheated to 1250 °C and hot rolled on a laboratory mill to a 13.0 mm thick plate with a finish rolling temperature of 900ºC and a thickness reduction of 80% . This work shows what precipitates are present in steel, the type of precipitates and their morphology. Analysis by transmission electron microscopy of low resolution was applied to obtain the chemical analysis of precipitates and the matrix. Spectroscopy of dispersive energy (STEM - EDS) was applied to obtain the element profile of precipitates. Particles of precipitates of NbC were found; with cubic morphology and size from 70 to 130 nm, circular morphology and size from 10 to 70 nm, polygonal morphology and size from 10 to 80 nm.

Jan 1, 2006

By Jeong-Hwan Kim

The liquid-liquid reactive process (solution process) is often adopted as a synthetic method for precipitated calcium carbonate (PCC) in laboratory studies for its simplicity in operation or ease in controlling process variables. Still, PCC are produced commercially by passing carbon dioxide through a milk of lime, i.e., by a gas-liquid reacting method (carbonation process). Few studies on the carbonation process have been conducted, since the process variables are interrelated and difficult to control compared to the solution process. In this study, both carbonation and solution processes were employed to study the polymorphs of calcium carbonate and growth rate of PCC crystals. The effects of the characteristics of limestone ores as a raw material in the synthetic system of PCC on the synthetic characteristics of PCC were also investigated. To control the nucleation rate in the synthetic systems, the shape factor was considered most important. Single-phase aragonite PCC could be synthesized under a variety of controlled experimental conditions such as ionic strength, solution composition, concentrations of additive ions, and temperature.

Jan 1, 2006

By T. L. Baum

External oxidation during in-line heat treatment of TRIP steels can cause problems for the subsequent coating process. This research aims to elucidate the kinetic rates of internal oxidation, external oxidation and decarburization and their interdependence under different gas atmospheres and temperatures. A rolled steel sample chemistry of 0.14 wt.% C, 1.8 wt% Mn, 0.6 wt.% Si and 1 wt.% Al is used as a case study. Thermogravimetric techniques are used to examine the net mass change in a sample during heat treatment and the results show an initial mass decrease and later an increase for particular partial pressures of H2O. SEM-EDS, optical microscopy and glancing-angle x-ray are used to quantify the microstructure. The cross-section of the samples have 4 distinct zones: (i) an external scale, rich in fayalite, (ii) an internally oxidized region with Al, Si and Mn oxides in an Fe matrix, (iii) a decarburized steel region, characterized by large ferrite grains and low carbon content, and (iv) a relatively unaffected steel core with a structure similar to the starting material.

Jan 1, 2006

By John M. Gaines

Lead concentrates from the Viburnum Trend in Southeast Missouri are sintered, prior to smelting, to bind the particles together, homogenize the feed, and reduce the sulfur content. About 20% of the sinter at some plants is classified as bad sinter. A total of 130 samples of good and bad sinters were studied by reflected light microscopy, scanning electron microscopy-energy dispersive analysis, and electron microprobe analysis to characterize their differences in mineralogy and textures. Good sinters consist predominantly of hardysonite, franklinite, lead silicate matrix, and large crystals of calcium-magnesium-iron silicate, together with minor amounts of lead oxides, lead-zinc silicate, metallic lead, specular hematite, magnetite, lead-iron-bearing zincite, and zinc-lead-magnesium-bearing wustite in a tightly intergrown mesh of crystals and with an evenly distributed porosity of about 15-20%. Bad sinters contain larger amounts of lead silicate matrix, galena, metallic lead, and lead oxides, but smaller amounts of hardysonite, franklinite, and calcium-magnesium-iron silicate, lack intimate intergrowth of the phases, and have lower (0-5%) and unevenly distributed porosity.

Jan 1, 1992

By M. A. Rabah, F. E. Farghaly, M. A. Motaleb

"Wastewater from industrial galvanization industry was reclaimed under current flow stream conditions. Results showed that the raw water contains 0.7 % by weight total suspended solids (TSS) causing turbidity amounting to 30. Measurements of Zeta potential as a function of pH revealed that solid separation takes place at pH 9. Addition of H2O2 to the polmer solution helps to oxdize ions of iron and zinc metals toinsoluble ferric oxide and zinc hydroxide to a higher state of oxidation. Addition of 5 mg/L of cationic magna flocculants polymeric solution helps the rapid separation of the turbidity. Separation of floccules so formed takes place by filtration. Addition of peroxide ions to the turbid wastewater confirms the physical stability of the flocs so formed. Impurity flocculation takes place in few seconds. Maximum temperature for safe solid removal was <30°C. The treated water was pure and safe for recycling or use in domestic purposes.IntroductionStocks and et. al. [1] show that the galvanizing process introduces spent pickling acid waste production, but its major constituent, could be used. Survey of the operational procedures adopted and the acid wastes produced by UK Galvanizers are reported. Various methods to recovery spent acid of suitable composition and to eliminate zinc contamination was considered. Application of the Kleingarn acid management system reduces waste volume, saves hydrochloric acid (HCl) and increases component throughput whilst, in conjunction with zinc elimination, could allow recycling of the majority of galvanizer’s acid wastes.Dahab [2]; Kerney [3] reported recycling of galvanizing products, including pickleliquor. Kerney suggested a mobile treatment plant for recycling pickling acids. Dahab found that pollution reduction could be achieved by relatively simple operational changes to the process that gave fairly short payback times.Rozenblat and et. al.[4] studied the extraction of zinc (II), iron(III) and iron(II) with Tributyl phosphate (TBP) from hydrochloric acid solutions containing high zinc(II) concentration. Two technological approaches for the separation are considered. Firstly, the selective extraction of iron(III) (iron(II) is oxidized to iron(III)) over zinc(II) with TBP deficiency. Secondly, iron(III) reduction to iron(II) followed by zinc(II) selective extraction with an excess of TBP. Prior stripping, the organic phase was washed with small amounts of water. Scrubbing of TBP solutions containing iron(III) contaminated with zinc(II) gives always a mixture of zinc(II) and iron(III) which must be recycled to the extraction step in continuous process. The following technological concept is proposed: reduction of iron(III) to iron(II), extraction of zinc(II) with 5-10 volume excess of TBP, washing of TBP phase contaminated with iron(II) with small volumes of water and recycling of the scrubbings and stripping of zinc with water."

Jan 1, 2008

By C. Koopman

During the production of phosphoric acid from phosphate ore and sulfuric acid, large amounts of calcium sulfate are formed, in which impurities from the feedstock are incorporated. To use the calcium sulfate in, for example, the building industry, a lower concentration of impurities is desired. Mercury, copper, lead, and cadmium were extracted from clear industrial recrystallization acid (0.8-3.9 mol/kg H3PO4, 0.2-0:5 mol/kg H2SO4) by supported solvent extraction with the extracting agent Cyanex 302 in kerosene in a transverse flow hollow fiber module. The permeability for the mercury ion was 1.4.10-6 m/s, whereas that for the copper ion was calculated to be 1.5.10 m/s. Cadmium, lead, and copper were extracted during the recrystallization of calcium sulfate hemihydrate to dihydrate, an existing step within the ,phosphoric acid production process, by solvent extraction with the same extracting agent. The concentrations of cadmium and zinc in the newly formed calcium sulfate were proven to be decreased. Unfortunately, concentrations of mercury and lead were too low for analysis.

Jan 1, 1999

By Taiping Lou

The effects of slag composition, additive agents, and heat treatment conditions on the perovskite (CaO ? TiO2) crystal morphology, the precipitation behavior, the crystal growth and the volume fraction (VF) in the Ti-bearing blast furnace slags were investigated. The morphology of perovskite is dispersed dendriform in molten slags. The crystal growth mechanism of the remelting of fine dendrites and the coarsening of larger grains exists throughout the solidification of molten slags. With the temperature decrease, the VF was increased and Perovskite transformed from fine dendrites to coarsening ones or equiaxed grains. The lower cooling rate can increase the VF and coarsen the grain obviously, while higher cooling rate will decrease the VF and reduce the average equivalent diameter (AED) of Perovskite. When .increasing the content of CaO and Fe20}, the VF can increase obviosly. However, high basicity will give rise to the increasing of viscosity of slag, which result in the reducing of the AED. The experimental results showed that additive CaF2 and MnO can efficiently decreased the viscosity of the slags, and obviously improved the morphology of perovskite and promote growth.

Jan 1, 2000

By Qiang Zhong, Bin Xu, Qian Li, Yongbin Yang, Tao Jiang

Viscosity of slag determines the production efficiency, energy consumption and distribution of elements between metal and slag, which is very important for pyrometallurgy. Slag of goldantimony ore blast furnace smelting has seldom been studied. In this paper, the viscosities of gold-antimony ore smelting slags of different composition have been studied by the rotating cylinder method. The results showed that, for a slag of 38.95% SiO2, 16.17% CaO, 25.97% FeO, 10.25% Al2O3, 5.17% MgO, the viscosity can be decreased by reducing 3.24%-8.5% SiO2 or increasing 3.31%-9.56% CaO content. Complex SixOy z- from SiO2 acts as the main cause for the high viscosity in a slag of high SiO2. The increasing of CaO causes the decreasing of the amount of SixOy z- and the O2- dissociated from CaO breaks the complex SixOy z-, which can decrease the viscosity. Viscosity of different composition slag in the appropriate range temperature can be calculated from the Arrhenius equation.

Jan 1, 2015

By Wen-Ming Chien

Keywords: AN-KN Phase Transition, Lattice Parameters of AN-KN, X-ray Diffraction The lattice parameters of the low and high temperature phase of KNO3-rich (in NH4NO3) solid solutions have been determined by the X-ray diffraction method. The low temperature single KNO3 phase (KN II) are from 92%-100% KNO3 in NH4NO3 composition range and from room temperature to 393 K showing in X-ray diffraction patterns. The high temperature KNO3 phase (KN I) showed very broad composition range between 20% to 100% KNO3. The lattice parameters of KNO3-rich (KN II and KN I) solid solutions have been calculated at different temperature range. The volumes of orthorhombic KN II phase decrease from 0.3208(3) to 0.3195(3) nm³ at the room temperature as the compositions increase from 95% to 100% KNO3. The lattice constants of the hexagonal KN I phase show that there is no significant change in a-direction when the temperature increases. Details X-ray results and lattice expansion equations during heating will be presented.

Jan 1, 2005