By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By B. Q. Li, Y. Shu, K Lynn

"This paper discusses the effects of magnetic field and internal radiation on the melt flow and solidification morphology during solidification processing of oxide crystals for optoelectronic and remote sensing applications. The numerical solution of the integral differential equation characterizing the internal radiation and the magnetohydrodynamic equations describing the magnetic and transport phenomena is obtained by applying the combined discontinuous and continuous finite element method. The results show that both internal radiation and an externally applied magnetic field can have important effects on the melt flow and solidification behavior during the melt processing of oxide materials.IntroductionOptical single crystals are widely used in optical and electronic devices. These crystals are often grown from high temperature oxide melts under strictly controlled conditions. As in the well-known single crystal growth processes for semiconductor wafers, thermal gradient in the melt is a major contributing fuctor to the oxide melt pool. Unlike the semiconductor single crystal growth processes, however, the oxide melt is semitransparent and internal thermal radiation plays an important role in redistributing the thermal energy in the melt pool. Our recent experience with pilot-scale plant measurements also shows that the oxide melt is electrically conducting, although its electrical conductivity is considered much lower than the liquid metal or semiconductor melt.The fact that the oxide melt is absorbing and emitting in the thermal radiation frequency range makes it difficult to study the thermal energy transport in the melt pool. This is because thermal radiation is governed by a hyperbolic differential equation, which is different from those describing the transport processes in liquids. Also, our understanding of how thermal radiation interacts with other transport mechanisms such as convection and conduction is rather limited at point in time, in particular in high temperature oxide melts for optical single crystal processing."

Jan 1, 2004

By Balladares V. Eduardo

Most of the arsenic contained in copper concentrates is removed in the gas phase during the smelting and converting processes and, according to recent environmental regulations, it is required to fix it in a solid stable form. In this regards, ferric arsenate has been reported as thermal and aqueous stable compound. Therefore, various alternatives for treating gas containing arsenic were considered in this work. From data obtained at laboratory scale on fixation of arsenic using iron oxide, a new process to treat copper concentrates containing arsenic was evaluated. The effect of temperature, oxygen potential and the sample porosity on the fixation of arsenic contained in a gaseous stream was studied, and the iron oxide converted into ferric arsenate was up to 10%. The obtained results suggest a new alternative for gas treatment with an interesting and attractive technical development. The arsenic was retained as ferric arsenate with thermal and aqueous stability, and it allows a safe disposal keeping the environmental restrictions. The kinetics parameters are used to scale up laboratory results to higher processing rates.

Jan 1, 2005

By R. Winand, M. Degrez, C. Temmerman

"The influence of the copper electro crystallization inhibitors (mainly thiourea, gelatin and chloride ions) is studied in a new fully automatic pilot plan. This paper describes the conception and the building of this plan. The new approach is to reproduce the experimental conditions observed in the industry with the three additives present simultaneously in the electrolyte and secondly to study the influence of a slight modification of the concentration of one inhibitor, the others being present in the electrolyte with their industrial nominalconcentrations.1. INTRODUCTIONDespite the fact that gelatine, thiourea and chloride ions have been used in copper electrorefining for a long time, precise knowledge concerning their influence on the cathode deposit, metallographic structure and associated properties is still lacking.Many authors studied the influence of each additive separately, or of two added at a time. Only a few authors studied the combined influence of the three additives added simultaneously. The general conclusion that can be drawn is that the combined influence is far from that forseen from the influence of each additive separately, or even from two additives used at a time. Moreover most of the experiments described in the literature were performed by adding all additives at once initially. It is however, well known that gelatine looses a great part of its activity during the first half hour due to degradation by sulfuric acid (as shown by the cathode overpotential drop). Thiourea is rapidly replaced by a number of degradation mole,cules and complex ions including cations from the solution, changing even the equilibrium between Cu, Cu(I) and Cu(II).Chloride ions are consumed by precipitation.A number of successive research projects [1-9] led pregressively to the concept that, in order to obtain reproducible results representative of industrial cathodes, it was necessary to simulate as far as possible industrial conditions. It was essential that all additives were added continuously during the electrolysis, with, as consequence, a continuous bleed.The purpose of this paper is to describe the concept of a new fully automatic pilot plan for copper electrorefining and to present the first results."

Jan 1, 1997

By Emmanuel N. Zevgolis

In the present work, a reduction roasting experimental study of Greek nickeliferous laterite samples with a gaseous reducing mixture ? CO:N2- is presented. The effect of parameters such as temperature, ore grain size, and composition of the reducing mixture were examined. It is deduced that the reducibility of intermediate type laterite sample, where iron appears mainly in the form of goethite (a-FeOOH), is considerably higher than that of limonitic type laterite samples, where hematite (a-Fe2O3) is the predominant iron mineral phase. The degree of reduction of the limonitic type laterite samples does not exceed 50%, while it reaches 95% in the case of the intermediate-type laterite sample under the same experimental conditions. Increasing the temperature in the range 750-900°C does not considerably favor the reduction of the limonitic type laterites, whereas decrease of ore grain size of the limonitic-type ore samples and more intense reducing conditions increase the reduction. The considerably higher specific surface area values of the intermediate laterite samples, diminishes the effect of the ore grain size and this can be regarded as the critical parameter leading to the higher reducibility of this ore.

Jan 1, 2009

By Esperidiana A. B. Moura, Célio H. Wataya, Roberta A. Lima, Rene R. Oliveira

Biodegradable starch/copolyesters/silica nanocomposite films were prepared by melt extrusion, using a twin screw extruder machine and blown extrusion process. The influence of the silica nanoparticle addition on mechanical and thermal properties of nanocomposite films was investigated by tensile tests; X-rays diffraction (XRD), differential scanning calorimetry (DSC) and Scanning electron microscopy (SEM) analysis and the correlation between properties was discussed. The results showed that incorporation of 2 % (wt %) of SiO2 nanoparticle in the blend matrix of PBAT/Starch, resulted in a gain of mechanical properties of blend.

Jan 1, 2015

By A. D. Zunkel

The zinc in electric arc furnace dust (EAFD) arises from the fuming and oxidation of the zinc present, mainly as galvanizing, in automotive scrap. The dust is collected from the electric furnace offgases in bag filters and is classified by the EPA as a hazardous waste (K061). As more zinc is used in galvanized sheet on automobiles and more automobile scrap is recycled via the EAF, the more zinc will be available for recovery and recycling. EAFD will become a more prevalent and important source of zinc compared to the traditional zinc sulfide concentrates ifit can be cost effectively processed.

Jan 1, 1995

By Tiejun Chun, Jian Pan, Deqing Zhu, Vinicius Mendes

"Fine manganese fines are characterized by large amount and low price compared to lump manganese ores. However, fine manganese must be agglomerated as EAF (electric arc furnace) feed. In this paper, high quality fired pellets were produced by simulating grate-kiln process to supply the feed for EAF from some imported manganese ore fines containing high combined water. Manganese ore fines assaying 44.47wt%Mn, 5.89wt%Fe, 12.09%LOI and with 72.7wt% ranging between 0.5mm and 8mm, are pretreated up to the particle size of 84.7wt% passing 0.074mm by HPGR (high press grinding roller) twice in open circuit. The finely ground manganese fines were mixed with 1.2wt% bentonite, balled at 15% moisture for 7min in disc pelletizer. The drop numbers, compressive strength and thermal shock temperature of green balls reach 11 times/0.5m, 11 N/pellet and 360oC, respectively. After the green balls drying in the oven, the dry pellets were preheated at 1050oC for 12 min and then fired at 1300oC for 12 min in electric tube furnace. The compressive strength of fired pellets reaches 2621 N/pellet. Therefore, these pellets are high quality burden for blast furnace or EAF due to high mechanical strength and high Mn grade of 49.11wt% and low detrimental elements.IntroductionManganese, mainly using as deoxidizing agent, desulfurization agent and alloying elements, is widely used in the steel company. With the rapid development of iron and steel industry in China, domestic manganese ores cannot meet the requirement, resulting large quantities manganese ores import to China [1-4]. Compared to lump manganese ores, fine manganese ores containing high combined water are characterized by large amount and low price. However, they must be agglomerated as EAF (electric arc furnace) feed. There are three ways to agglomerate the manganese fine ores, sintering, briquetting and pelletizing [5-6]. Compared to the other two methods, pelletizing technology possesses the following superiorities, such as uniform size distribution of product, stabilizing chemical composition of product and lower energy consumption in producing. Therefore, pelletizing is a superior way to treat the fine manganese ores [7]. The systematic research of producing manganese oxide pellets by fine manganese ores containing high combined water was studied in this paper."

Jan 1, 2011

By Y. Moriya, Y. Sadayoshi, Y. Nonogaki, Y. Takeda

"Preparation and growth processes of CaF2 on Si(111) and of . InxGa1-x,As islands on CaF2 by molecular beam epitaxy (MBE) are described. It was found that first of all the Si(111) surface treatment process to obtain the 7x7 reconstructed structure was necessary to ensure the cleanness of the surface and to grow a flat and high quality CaF2 on it. Growth of InxGa11-x,As islands on CaF2 was tried by droplet heteroepitaxy using the same MBE reactor. In,GaxGa1-xAs islands were successfully grown epitaxially, and the size and density of the islands dependent on the In composition were investigated.IntroductionThough semiconductor/semiconductor heterostructures are widely used for many device applications, small band off-sets of the conduction bands and the valence bands restrict the utilization of the intra-subband transitions to far-infrared regions. With InAs as the quantum well and fluorides as the barrier layers, we can design three-electronic-level systems in the infrared region, which is the low loss transmission window of the silica optical fibers. To realize those structures, we have grown InxGa1-xAs islands on CaF2 thin films that were epitaxially formed on Si(111) substrates by molecular beam epitaxy. By the droplet heteroepitaxy that we invented, the InxGa1-xAs islands with height of -10 nm have been obtained successfully. Optimum processing to obtain atomically smooth surfaces of Si and CaF2 and high quality InxGa1-xAs islands is reported.ExperimentsMBEMachineCaF2 was grown on Si(111) and InxGa1-xAs islands were grown on CaF2 successively by MBE. The MBE machine consisted of a growth (or reactor) chamber and a loading chamber. The reactor chamber was equipped with Ga, In, As and Er metal source cells and CaF2 and BaF2 source cells. Cell materials were P-BN for Ga, In and As metals, and were graphite for CaF 2, BaF 2 and Er to avoid reaction with BN cells. The electron gun and screen were attached to the reactor to observe the RHEED pattern during the substrate surface treatment and the growth of CaF2 and InxGa1-xAs islands. The substrate manipulator was designed to heat up the Si substrate up to 1,200°C for the surface cleaning. The QMS was also equipped to analyze the residual gas species in the reactor chamber. The base pressure of the reactor chamber was 2-5x10-11 Torr, being pumped by ion pump and the liquid nitrogen shroud"

Jan 1, 2000

By Zengjie Wang

Investigation on hydrochloric acid leaching of the ilmenite from Panzhihua, China was carried out to prepare synthetic rutile. The leaching parameters were optimized to obtain high content of TiO2 in the products. The experimental data suggest that an optimum leaching can be realized with 30% acid, a solid/liquid ratio of 1/4 at 95°C for 4h, and ore ground for -400 mesh size. After the acid leaching, an additional alkaline leaching process using hot NaOH solution was performed, and then the products was in grain form followed by heat treated at 900°C for 2h in order to extract Si and increase the particle size of synthetic rutile. The final product has a high content of TiO2 (about 95%), a low content of chlorine consuming elements (total CaO+MgO =0.07%) and a suitable particle size distribution for chlorination process.

Jan 1, 2008

By Chonghun Han, Tae-Hwa Choi, Young-Hwan Chu

"A statistical optimization method is proposed to maintain stable operation in a blast furnace with stave coolers. The objective of this study is to find the operating condition which maximizes productivity as well as minimizes the heat load on the stave coolers. In this method, we first analyzed historical data and calculated the heat flux of stave coolers and the burden distribution by mathematical models. In this approach, we determined the variables to optimize and manipulated variables to adjust these response variables. Next, we collected the necessary data for the data variables after preprocessing such as removal of noise and outlier. Finally, we constructed empirical models describing the patterns of response variables in terms of manipulated variables by partial least squares regression method, and then these models were used as objective functions for entire optimization problem. By using appropriate optimization algorithm, we determined the compromised optimum operating condition considering all response variables from the past operating conditions.IntroductionBlast furnace operation which is accompanied by complex physical and chemical phenomena is an essential process for steel industry. In this process, iron ore which is charged into the blast furnace from the top goes downward. It is reduced to iron by CO gas and is melted by the heat of combustion of coke and pulverized coal. The pig iron is tapped at the bottom in liquid phase after removing the slag, which floats on the pig iron.The cooling equipment of the blast furnace wall is changed from the plate type to the stave cooler recently. In order to cool the shell uniformly and eliminate shell spray cooling, Pohang No.2 blast furnace of POSCO (Pohang Iron & Steel Company) was equipped with 11 rows of stave coolers. These staves are only 350mm-thick including the 170 mm-deep refractory on the hot face."

Jan 1, 2001

By Run Huang, Xuewei Lv, Lei Lei, Guibao Qiu, Chenguang Bai

"The TiO2-rich slag and pig iron can be produced from ilmenite concentrate by the electric furnace process. In this study, ilmenite concentrate was reduced in a vertical furnace equipped with a weighting data acquisition system. The effects of reducing agent (carbon) amount on the iron reduction were studied. The phase transformation, morphology and chemical compositions of reduced samples were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), respectively. It was found that the reductive degree of ilmenite concentrate increased with the increase of reducing time. The phases of reduced samples were mostly iron, rutile, Ti3O5 and Fe2TiO5. The mass loss percentage increased with increasing the carbon amount from 8% to 12%. When the carbon amount exceeded 12%, the mass loss percentage decreased with the increasing of carbon amount.IntroductionIlmenite and rutile are the main raw materials for producing titania pigment and titanium metal. With the development of the titanium industry, huge amounts of titanium resources are needed. As sources of high-grade titania mineral decrease worldwide, more attention should be paid to the processes involving low grade mineral such as ilmenite ore. In ilmenite, MgO and CaO are the gangue parts. Therefore, the ilmenite refining becomes more and more popular. In the previous studies, the methods of ilmenite refining are electric furnace smelting, direct acid leaching, selective chlorination and thermal reduction [1]. Electric furnace smelting method is widely used in the titanium industry, however, which consumes a great deal of energies and has a high CO2 emission. Its essence is to remove iron oxides and obtain a high titania slag. So the thermal reduction of ilmenite concentrate is an important step in titanium industry, which can decrease carbon reagent consumption and save energy.Over the past several decades, many studies have been carried out on the mechanism and kinetics of the reduction of different ilmenite ores, which are as follows: The carbothermal reduction of Panzhihua ilmenite initiated at about 860 oC. In the temperatures ranging from 900 oC to 1400 oC, the reaction rate was changed like a shape of “M”. That was to say that the reaction rate increased with the growth of temperature at first, then decreased, afterward increased again and at last the reaction was arrested [2]. The Mohammad A.R group [3, 4] showed that the carbothermal reduction of primary ilmenite concentrate was faster in hydrogen and initiated at a lower reduced temperature than in argon and helium. The reduction in argon and helium had about the same rate and extent. Titanium oxycarbide started at 1000°C in hydrogen. The conversion of primary ilmenite concentrate to metallic iron and titanium oxycarbide at 1200 °C was completed in 300 minutes. Monoxide as the reductant to reduce ilmenite had been studied intensively by a few research groups [5, 6]. The rate and the degree of reduction depended on the formation of a metallic shell of iron which inhibited the transfer of CO to the reaction zones; titanium had a strong effect on the mechanism and rate of reduction of iron oxides. Wang and Yuan [7] studied the reductive kinetics of the reaction between a natural ilmenite and carbon. At temperature below 1100°C, chemical reaction was the rate controlling step, at 1100 to 1250°C mixed controlling was rate controlling step, above 1250°C diffusion through the product layer controlled the reaction. Zhang [8] investigated the reduction of natural, sintered and preoxidized ilmenite concentrates in hydrogen methane mixtures. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron."

Jan 1, 2011

By F. M. Wang, J. P. Lin, G. Y. Tang, H. C. Zhou, Y. F. Liang, F. Ye

"Fe-6.5%Si alloy is a very excellent soft magnetic material compared with conventional Si steel (Si content ~ 3.5%), especially in high frequencies with reduced iron losses and noises. But it is hard to be fabricated due to its brittleness at room temperature. Dynamic electropulsing is applied to the cold rolled Fe-6.5%Si sheet during tensile deformation. Mechanical and microstructural properties are investigated with different electropulsing and strain rate. It is found that the yield stress decreases and the elongation increases dramatically with the application of dynamic electropulsing. It is indicated that the work hardening could be reduced with the dynamic electropulsing during deformation, which provides a promising way to fabricate this alloy sheet much easier.Introduction Fe-6.5%Si (weight percent, same as below) alloy has more excellent soft magnetic properties compared with conventional silicon steel (Si content ~ 3.5%), such as higher resistivity, higher permeability, near zero magnetostriction, etc. and exhibits much lower core losses and noises [1]. However, Fe-6.5%Si is very brittle at room temperature and hard to be fabricated in strip by conventional hot-cold rolling process [2]. This lack of low-temperature ductility has been generally attributed to structural ordering ofB2 and D03 phases [3]. Several methods have been developed to avoid its brittleness, such as chemical vapor deposition (CVD) [4], rapid quenching [5, 6], dipping and diffusion [7, 8], direct powder rolling (DPR) [9], etc. However, hot-cold rolling method is still of interest for industrial applications. In our previous work, this alloy can be cold rolled after certain thermomechanical process and heat treatment [10-13]. The cold rolled sheet exhibits some extent of ductility [11]. However, side cracks are common for the rolled sheet, it is very necessary to improve the ductility of this alloy by other technical applications."

Jan 1, 2012

By Mokka Rao, Asdrubal Serrano

"A mathematical model is developed which describes the movement of the minerals present where the vertical and angular velocities are related with the different operative parameters involved in the process of separation of silica from iron ore, which permit maximise the capacity of the spirals to obtain major productivity. The process is realised in two steps, of the rough dressing and other cleaning. Through the results obtained for chemical analysis of the final products of each spiral and the equation of movement of particles, it is proved the applicatibility and efficiency of mathematical model to operating parameters of the spiral. Moreover, it is determined though the recuperation of the final products of quality in the use spiral HC 1870 and HG 8/7. INTRODUCTIONThere is prospetive of increasing the production the iron ore in agreement with the demand of siderurgical proyects united with the external demand of quality 40 million tons per year. The Ferrominera de Orinoco Company is experimenting two types of modem spirals, Humprey (HC 1870) and Reichart (HG 8/7) which have limited capacity. For this reason this investigation designed a mathematical model with which larger units can be designed for increasing the capacity of the spiral."

Jan 1, 1999

By Sun Ying, Zhang Jing, Li Qiu-ju, Wang Yan-ze

Copper smelter slag was leached using sulphuric acid solutions under atmospheric conditions. Base on the composition and phase of copper slag, the effect of the concentration of sulfuric acid and leaching temperature to the leaching growth rate of Fe, Cu, Co and Ni in the copper slag were investigated in this paper. Simultaneously, the influence of sulfuric acid concentration, leaching time, leaching temperature and the amount of sulfuric acid (solid-liquid ratio) to the leaching rate of these metal elements were researched. Experimental results showed that: with the increasing temperature, the dissolution rates of the metals elements increased first and then decreased. Due to the influence of silica gel which was obtained in beginning of leaching, the higher the concentration of sulfuric acid is not conducive to dissolution of the valuable metal elements. The dissolution degree of Fe, Cu, Co and Ni were 92.83% 96.76% 93.62% and 63.41% respectively.

Jan 1, 2016

By Francois Barthelat, Sam Goroshin, David Frost, Alexander Cappozi, Atefeh Nabavi

"In this study, a novel chromium–chromium sulfide cermet was produced by self-propagating high-temperature synthesis (SHS). Conventional techniques for manufacturing metal sulfides are complex, environmentally harmful, and not suitable for producing complex-shape articles. To overcome these disadvantages, a new method for the preparation of the metal-sulfur precursor charge is proposed, which can be described as reactive casting. The first cermet samples produced with the SHS process were found to be very porous, brittle, and have low mechanical strength. The possible sources for the generation of porosity were identified and analyzed and the process for manufacturing the cermet was modified. By improving the manufacturing process, the porosity inside the produced cermets was reduced from 70% to 12%.IntroductionMetal sulfide composites are in high demand in the chemical, metallurgical, and electrical industries because of their valuable characteristics such as hardness, semi-conductivity, electroluminescence, infrared transparency and catalytic properties. Current manufacturing methods for metal sulfides usually involve one of two different principal methods, including a complex multistage wet chemical process involving the precipitation of the corresponding salts from an aqueous solution with hydrogen sulfide, or hot sintering of the respective elemental reactant powders in a resistive furnace in a high-pressure inert or hydrogen-sulfide atmosphere [1, 2]. These conventional methods for synthesizing ceramic metal composites are complex, extremely time and energy consuming, environmentally harmful, and rarely able to manufacture articles with complex shapes. Therefore, in order to overcome these disadvantages, self-propagating high-temperature synthesis (SHS) was considered as an alternative method that offers significant improvements over the traditional cermet manufacturing methods [3]. SHS, which is a relatively new and attractive method for producing a wide range of advanced materials, is based on the self-sustaining feature of the highly exothermic reactions of the reactants. The SHS process results in high product purity, since the high temperatures generatedin the reaction cause any impurities to volatilize [4, 5]. SHS has low energy consumption and doesn’t require an external energy source and complex equipment, and it is self-contained [1, 5]. Since combustion synthesis has low power requirements, it is one of the few methods of materials synthesis that is feasible in outer space. Also, the process has a low cost and is capable of directly synthesizing articles with the desired shape, size and structure [5, 6]. The chemical reactions associated with SHS are typically completed in a few seconds leading to the formation of the condensed product. The high reaction rates and relatively rapid cooling in SHS reactions can avoid undesirable grain growth in products which often occurs with the conventional sintering method [3, 5, 7]. The traditional method for sample preparation in the SHS technique is to compact the reactant mixture powders in a steel die by a press to a typical density of about 80% of the theoretical maximum value, before igniting the mixture [8]. This method requires a large compression force to increase the green density and to minimize any pores in the green compact. To overcome these disadvantages, a new method for the preparation of the precursor charge in metal-sulfur by SHS is proposed which can be described as melt casting of a reactive mixture, or reactive casting in short."

Jan 1, 2012

By Jewel Gomes

Green rust is an important intermediate in oxidative transformation of Fe(II) phase. This unstable compound contains a mixture of ferrous and ferric hydroxides that belong to a family of minerals known as layered double hydroxides (LDH). Its general formula is [FeII(6-x) FeIIIx (OH)12]x+[Ax/n-*yH2O] x-, where A is an n-valent anion mainly Cl-, CO3-2 and SO4-2, and in which either the bivalent or the trivalent iron can be replaced for other trivalent or bivalent metal ions. It was first identified as corrosion product, later in soils as a product of interactions between microbes and metals in soils. Due to its high reactivity, it is used in the reduction of organic and inorganic compounds, As removal, and the treatment of acid mine drainage. In this paper, we described the method of electrochemical generation of green rust, its characterization by XRD, SEM and FT-IR, and its implications to electrocoagulation.

Jan 1, 2009

By Yang Hong-ying, Yu Juan

Electrochemical behavior of natural chalcopyrite in electrolyte solution at pH value of 6.97 was studied by cyclic voltammetry, X-ray photoelectron spectroscopy and electrochemical impedance spectroscopy. The results showed that the electrochemical processes occurred on electrode surface were controlled mainly by the growth of sulfur species at lower applied potentials (<0.35Vvs.SHE), and the oxidative dissolution of sulfur species and the hydroxylation of iron at higher applied potential (>0.45V). The EIS spectra of oxide product layers could be illustrated by the equivalent circuit of Re(QdlRct(QfRf)), and the degree of hydrophilicity for chalcopyrite was higher when the value of charge transfer resistance Rct. was greater. The optimum potential range for the floatation of chalcopyrite in collectorless solution at pH value of 6.97 was between OCP (0.165V) and 0.35V.`

Jan 1, 2015

By J. T. I. Poijärvi

The smelter off-gas cleaning and the weak acid treatment at Outokumpu Harjavalta Metals Oy are presented and described in this paper. The smelter consists of the copper and nickel smelters and the acid plant of three separate acid plants two of which are double contact and one single plant and of one liquid sulphur dioxide plant. The preliminary cooling and flue dust separation of the smelter off-gases from the copper and nickel flash smelting furnaces and converters in the waste heat boilers and in the hot electrostatic precipitators are described. The final cooling and cleaning of the gases in the scrubbers at the sulphuric acid plant and the treatment of the weak acid in the vacuum and in the submerged combustion evaporators for the removal of impurities are pre¬sented as well as the treatment of the condensates from the evaporators. The attention is paid to the generation of sulphur trioxide in the smelter off-gas and to the treatment of that in the weak acid bleed-off and to the utilization of the treated acid.

Jan 1, 1992

By Jose Bengoa

Low metal prices and environmental restrictions are always a challenge for copper smelters operation and its productivity. Thus, in order to reduce production costs and control gas emissions, improvements of the Teniente Converter (CT) operation were made at 110 Smelter Plant of Southern Peru Copper Co" 110, Peru, and the main objective was to increase its capacity for smelting copper concentrates without affecting normal operation, The present work eorresponds to a recent study conducted during the normal industrial operation of the Teniente Converter in this plant and, it shows the effect of increasing air oxygen enrichment from 28 to 34% on its productivity. The results show an increasing of concentrate smelting rate from 800 to 1370 tpd and hence a notorious improving in copper production, and practically no effect on the refractory consumption. The increment of the concentrate throughput, increases also the SO2 concentration and the sulfuric acid production, showing the effort done by this operation in order to accomplish the environmental Peruvian regulation,

Jan 1, 2003