The characteristics of top charging coke (coke 1) and stamp charging coke (coke2) were investigated. The weight loss ratios of two kinds of cokes with and without alkalis were measured after reacting with CO under the temperature of 2 900, 1000, 1100 and 1200 °C respectively. The microstructures of original cokes were observed by SEM. The experiment results show that, with no addition of alkali, the weight loss ratios of coke 1 and coke 2 were nearly the same under the temperature of 900 and 1000 °C. While the weight loss ratio of coke 2 was much larger than coke 1 under the temperature of 1200 °C. With alkali-rich, the weight loss ratio of the two cokes was almost the same at 1100–1200 °C.

Mar 1, 2017

By Chang Wei, Zhigan Deng, Minting Li, Cunxiong Li, Gang Fan, Xingbin Li

Molybdenum and nickel in black shale ore exists as amorphous sulfides which has highly active, and easily oxide to sulfuric acid and sulfate at low temperature in the presence of excess oxygen. Take advantage of the characteristic to leach molybdenum and nickel from black shale. Oxidation, conversion and dissolution behavior of amorphous colloidal molybdenum and nickel sulfide in pressure leaching process was studied. The effects of stirring speed, temperature, concentration of sulphuric acid, oxygen process and mineral granularity on molybdenum and nickel leaching were investigated. The results showed that dissolution rate increased with increasing temperature and stirring speed, but decreased with increasing concentration of sulphuric acid. And dissolution of molybdenum and nickel from ore only need oxygen without any other reagent.

Mar 1, 2017

By Daoxin Wu, Zhong Cao, Yan Shi, Yu Ding, Huanli Yang, Zhongliang Xiao

"2-substituted benzimidazole-zinc and 2-substituted benzimidazole-copper complexes were main components of organic solderability preservative (OSP) in PCB producing process and affect the thermal stability of OSP film. So these four complexes were prepared by 2-substitutedbenzimidazole reacting with zinc ion and copper ion, the complexes crystals were determined by IR, its thermal stabilities were studied by TG method. The results indicated that the thermal stability of 2-substituted benzimidazole-zinc is higher than the 2-substituted benzimidazole copper,and the thermal decomposition mechanism was presentedIntroductionImidazole compounds which is an important heterocyclic compound shows the important value and outstanding prospects[I-3l in field of biological engineering, medicine, and high-performance composites. It's said that imidazole compounds is an excellent new metal surface treatment[4] agent, because it has good reaction activity with metals and can form a chemical layer on the metal surface. The complexes of imidazole were main components of organic solderability preservative (OSP) in PCB producing process and affect the thermal stability of OSP film. The mechanism of imodazole combined with metal and film deposited has been reported, but the opinions about thermal stability of film have bifurcation, let alone the thermal decomposition mechanism of film at high temperature. The complexes were prepared by combining of 2- substituted-benzimidazole with zinc and copper iron, which were studied by IR and TG method, in order to get thermal stability of different complexes."

Jan 1, 2011

By K. R. Robilliard

Ausmelt Technology has been developed to process copper concentrates containing significant levels of lead, arsenic and antimony. A process was developed aimed at smelting these concentrate materials to remove the contaminants to fume and produce a clean copper product. The production of clean copper and the potential economic benefits of this process step over the sale of impure concentrates is discussed.

Jan 1, 1995

By Yanhui Sun, Yanan Zeng, Kaike Cai

"Hot ductility of Nb-V-containing steel has been studied by theoretical calculation and thermal simulation experiment. Meanwhile, microsegregation and precipitates were analyzed. The results showed that segregation degree of elements S, P, 0 is greater in mushy zone, while, the hot ductility was deteriorated by inclusions of Fe(S,O), (Fe,Mn,Si,Al)(S,O) in the interdendritic region. At the temperature 1100°C, a few NbN particles, 60-70nm, have little effect on mechanical property. In the temperature range 1000°C to 975°C, R.A declined rapidly from 82.36% to 69.61% with the diameters decreasing from 20 to 10nm and quantity of particles increased 23 to 45inds/µm2, respectively. In the temperature range from 900°C to 850°C, R.A reduced unobviously from 34.27 % to 30.01 % with ferric films thickening gradually. The critical stress, 52.38MPa, was equal to tensile strength at 975°C. Intergranular fracture was easy to occur with higher critical stress below 975° C.IntroductionProductivity and product quality of slab are seriously affected by cracks during continuous casting and the influencing factors of cracks are various[l]. From microcosmic angle, resisting deformation ability of initial solidification shell decreases obviously with solute elements segregation which can urge the low melting point ofliquid film to form at grain boundaries[2, 3]. Meanwhile, with temperature decreasing, particles would precipitate as the practical solubility product is greater than equilibrium solubility product. The carbonitrides would lead to stress concentration at austenite grain boundaries. Therefore, the transverse cracks of microalloyed steel would form during the straightening operation in the continuous casting process. The hot ductility of steels in the temperature of mushy zone was characterized by microalloy elements segregation, zero strength temperature (ZST) and zero ductility temperature (ZDT). The nature, shape, and size of precipitates have been investigated by TEM (JEM2100). Hot tensile test with low strain rate was simulated by Gleeble-1500. The objective of present study is to provide reference for zero defect of microalloyed steel during continuous casting process."

Jan 1, 2013

By Zhanjun Wang, Mei Zhang, Zuotai Zhang, Min Guo

In this study, the viscous flow and crystallization behavior of CaO–SiO2–MgO–Al2O3–FetO–P2O5–TiO2 steelmaking slags have been investigated over a wide range of temperatures. The results indicated that the viscosity of the slags slightly decreased with increasing TiO2 content. The constructed non-isothermal continuous cooling transformation (CCT) diagrams revealed that the addition of TiO2 lowered the crystallization temperatures. This can mainly be ascribed that the addition of TiO2 promotes the formation of [TiO6]-octahedra units, thereby MgFe2O4–Mg2TiO4 solid solution is formed. Moreover, the decreasing viscosity has a significant effect on the diffusion of ion units, such as Ca2+ and [TiO4]-tetrahedra, from bulk melts to crystal-melt interface. The crystallization of CaTiO3 and CaSiTiO5 was therefore accelerated, which can improve the phosphorus content in P-enriched phase.

Mar 1, 2017

Rapidly solidified TiAl-Cr-xNb-Y(x=2,4,6, at.%) alloys have been produced using a single roller melt spinning method. The microstructure of alloy ribbon was refined and component became more homogeneously by rapid solidification technology. There were two phases in alloy ribbons, including -TiAl and 2-Ti3Al phases, yet the amount of 2-Ti3Al phase in matrix obviously increased by rapid solidification than cast alloys. The micro-hardness testing also carried out. Compared to the cast alloys, the alloy ribbons have much higher hardness.

Jan 1, 2009

By Jinsheng Wang, Wei Lv, Xuewei Lv, Pingsheng Lai, Jie Dang

The isothermal reduction kinetics of vanadium titanium magnetite sintering ore was investigated by thermo-gravimetric analysis at a temperature range of 1123–1223 K under 30% CO + 70% N2 gas mixtures. The apparent activation energy of reduction was calculated by iso-conversional method and its value is 36.7 kJ/mol. The model function describing the reduction mechanism was discussed by Sharp analysis and the results revealed that the reduction process is controlled first by random nucleation and nucleus growth mechanism (RNNGM) as reduction degree is lower than 0.5, followed by the mixed influence of RNNGM and phase boundary reaction when reduction degree is higher than 0.5.

Mar 1, 2017

By Jesus Gonzalez

Peirce-Smith converters (PSC) are long cylindrical chemical reactors where copper matte reacts with air. Traditionally, air is injected laterally through submerged tuyeres at different subsonic velocities. However, the accumulated experience in steelmaking, particularly in the basic oxygen furnace (BOF) process, shows that the gas bottom injection may improve the mixing efficiency of a liquid pool. The aim of bottom injection is to maximize the copper kinetic energy meanwhile avoiding excessive reactor splashing. When gas is injected from a single orifice at the bottom of a liquid pool, two main gas flow regimes can be identified, bubbling and jetting. In this work, a PSC with bottom air injection is studied by means of multiphase 3D CFD numerical simulations considering multiple air velocities. Special attention is paid to the bubbles and jet formation mechanism. The mixing efficiency is measured by calculating the turbulent kinetic energy of the copper matte.

Jan 1, 2008

By Ruiqing Li

It is possible to purify some liquid metals by exploiting the difference between the vapour pressure of the bulk metal and the minor constituents or impurities. The rates of purification can be improved by carrying out the process under reduced pressure, that is, so called, vacuum. Some commercial examples of vacuum refining are the purification of molten tin to eliminate trace amounts of lead and the refining of cobalt, also to remove lead. The objective of this paper is to review the basic theory behind vacuum refining technology in order to show how the feasibility of vacuum refining can be determined simply for a particular system by evaluating Olette's Volatility Refining Criteriont.

Jan 1, 1991

By Andrzej Warczok

Liquid slags produced in smelting of copper concentrates contain copper in a dissolved form as well as mechanically entrained inclusions of copper matte. Coalescence and sedimentation of inclusions during slag cleaning plays a key role in copper recovery. Liquid matte inclusion in a molten slag presents a system of metallic conductor in an ionic solution. Constant electric field induces migration of the matte droplet along the current lines. Additional phenomena occur in a system under crossed electric and magnetic fields. Electromagnetic buoyancy force acting on the inclusion affects its settling rate. Electromagnetic buoyancy force of insulating and metal spheres has been measured in a liquid synthetic slag. It was found that depolarisation of the metal sphere, related to the electrode reactions occurring in the surface, plays an important role in the determination of the direction and magnitude of the electromagnetic force. On the basis of the existing theories and results of measurements a mathematical model describing the behaviour of metallic inclusions in the liquid slag under the influence of crossed electric and magnetic fields was developed. Simulation of behaviour of copper matte inclusions under crossed fields showed trajectory of motion in a liquid slag as a function of the slag properties and the inclusion size.

Jan 1, 2003

By Yun Guo, Min-Min Lin, Bing Xie, Hong-Yi Li

The extraction of vanadium from vanadium-containing APV-precipitated wastewater by W/O microemulsion system was studied. In the N263/n-heptane/isoamyl alcohol/NaCl microemulsion system, N263 played double functions of cationic surfactant and extractant to form microemulsion in n-heptane, and isoamyl alcohol was added in the microemulsion as a cosurfactant. The extraction of vanadium by W/O microemulsion systems effectively accelerated the extraction and improved the extractatability because of the enormous increase in the micro-interfacial surface area. Due to ion association with extractant, vanadium was extracted into the microemulsion phase. The influence of different parameters on the extraction ratio (E%) were investigated, including the volume ratio of aqueous phase to microemulsion, surfactant concentration, pH value of the feed solutions, cosurfactant concentration, extraction time as well as temperature. In optimum conditions, the extraction ratio (E%) can reach 97.2%.

Mar 1, 2018

By Qingguo Xue, Jingsong Wang, Yingli Liu, Guang Wang

In the dropping zone of blast furnace (BF), primary slag absorbing ash of pulverized coal and coke become to be intermediate slag. Due to viscosity and surface tension of slag and the pore between cokes, some slag remained in coke layer and affected the permeability of blast furnace. The flow behavior of slag with different basicity (0.55–1.10) and Al/Si (0.35–0.50) were studied. Meanwhile, the viscosity and surface tension of slag were calculated. The results showed that, with the increasing basicity of slag, surface tension increased and viscosity decreased. With the Al/Si increase, surface tension and viscosity increased. The smallest pore that all slag can pass through was 4.5 mm. However, the height between slag droplets and the bottom of crucible indicated that the ability of slag to pass through pore were weakened with the increasing basicity and Al/Si. Thus, slag which absorbed ash from fuel become difficult to pass through coke layer.

Mar 1, 2017

By A. D. Neuman, C. C. Davis, M. R. Lopez, A. C. Martinez, T. A. Nothwang, F. G. Hampel, S. L. Voit

"One of the thrust areas for the Global Nuclear Energy Partnership (GNEP) program is the development of actinide bearing fuels for transmutation in a fast reactor. Mixed Oxide (MOX) fuel has an extensive fast reactor irradiation history and thus is being considered for use as a baseline composition from which minor actinides can be incorporated for use as a transmutation fuel. The current study involves characterization of precursor powders and pellets destined for the Advanced Test Reactor in Idaho. These pellets will have three compositions: one standard MOX composition, (U0.80Pu0.20)O1.98, and two compositions of minor actinide mixed oxide (MAMOX) with oxygen to metal ratios (O/M) of (U0.75Pu0.20Am0.03Np0.02)O1.98 and (U0.75Pu0.20Am0.03Np0.02)O1.95. The precursor powders were characterized using a field emission gun scanning electron microscope (FEG-SEM) to determine particle morphology, size, and size distribution. An electron probe microanalyzer (EPMA) was used to characterize element distributions in the pellets.IntroductionThe fundamental purpose of GNEP is to enable a fuel recycling partnership between member nations. The customer nations utilize the fuel for electricity generation provided by and subsequently recycled by the supplier nation. The supplier nation recycles the actinide constituents, mainly uranium and plutonium, in advanced nuclear power reactors, and thus reducing waste volumes [1, 2]. Nuclear materials are strictly controlled through the International Atomic Energy Agency. One of the thrust areas supported by the GNEP program is the development of actinide bearing fuels for transmutation in a fast reactor under the U.S. Advanced Fuel Cycle Initiative (AFCI) in order to transmute long-lived transuranic actinide isotopes into shorter-lived fission products [3].MOX fuel has an extensive fast reactor irradiation history and thus is being considered for use as a baseline composition into which minor actinides can be incorporated for use as a transmutation fuel [4]. Irradiation performance data on oxide fuels with high concentrations of minor actinides is limited, which has prompted this study. This paper discusses the characterization results of precursor powders and pellets prepared for the Advanced Test Reactor in Idaho to determine the effects of including minor actinides in the fuel, and addresses two fuel test matrices proposed by Hilton et al. [3]. The pellets will have three compositions: one standard MOX composition, (U0.80Pu0.20)O1.98, and two compositions of MA-MOX with O/M of (U0.75Pu0.20Am0.03Np0.02)O1.98 and (U0.75Pu0.20Am0.03Np0.02)O1.95. The precursor powders, uranium oxide (depleted, DUO2 and highly enriched, HEUO2), neptunium oxide, NpO2, americium oxide, AmO2, and plutonium oxide, PuO2, were characterized using a FEG-SEM for particle morphology, size, and size distribution. The morphology of the actinide powders was studied in the areas of flowability and porosity in order to predict manufacturability. The MOX pellets were characterized using an EPMA in order to determine impurity levels and locations."

Jan 1, 2008

By Chen Song

Cobalt basic carbonate particles were precipitated from 1.0mol cobalt nitrate or cobalt sulfate solution with ammonia carbonate. By controlling the zeta-potential of the particles and the ionic strength of the solution, the uniform particles with ellipsoid or rod shapes were obtained. During the precipitation process, the interface tension was diminished to the minimum and therefore the Ostwald ripening and secondary nucleation were both inhibited. The morphology and the size control by zeta-potential seem to be the result of thermodynamics rather than classical crystalline kinetics. The particle sizes were in the range of 0.4-0.6, 0.3-0.4 micrometer. After thermolysis, the spinel-type C0304 particles were produced. The morphologies of C0304 particles were similar to that of their precursors.

Jan 1, 2003

By Dae Jin Ha

Sticking phenomenon occurring during hot rolling of two STS 430JlL ferritic stainless steels was analyzed by hot-rolling simulation tests. The sticking started from the initial nucleation stage in which the rolled materials were stuck onto the roll specimen surface, proceeded to the growth stage in which stuck fragments grew further, and reached the saturation stage. The modified 430JlL steel had a smaller number of sticking nucleation sites and slower growth rate than the conventional 430JlL steel because of higher high temperature hardness, thereby leading to less serious sticking. When the simulation test was conducted at 1070 °c, Cr oxides were formed on the surface of the rolled materials, and thus the sticking was drastically reduced because of the increased surface hardness of the rolled materials. In order to prevent the sticking, high-temperature properties of the rolled materials should be enhanced when rolled at 900°C or 1000 °C, and rolling conditions and alloying compositions, under which the oxide formation was promoted, were more important than high-temperature properties when rolled at higher temperatures than 1000 oC.

Jan 1, 2008

By W. H. (Bill) Jay

The destruction of cyanide creates a significant impost on the financial returns of gold mines. These losses increase substantially when ores containing cyanide-soluble copper are treated. Failure to remove or destroy free or WAD cyanide before it is discharged into tailings dams has, on a number of occasions, led to significant fish, bird and animal deaths. Thus, the retention of cyanide within the leach circuit and the recovery or removal of stable metal cyanide complexes needs to become standard practice for all gold mining operations. Furthermore, reducing cyanide purchases will minimise the quantity of cyanide transported to the mine site thereby reducing the opportunity for spillage of this chemical. Many different physical and chemical methods have been investigated for the removal of cyanide from process solutions. All cyanide destruction methods create a financial impost on the economic viability of the gold mine. To reduce these costs, the recycle of cyanide and the economic recovery of the metals solubilised by cyanide is of prime importance. The alternative methods currently in use, or under consideration for the treatment of copper cyanide, entail high reagent costs, produce the recovered metal in a contaminated form and require the safe handling of hydrogen cyanide. These processes will be briefly discussed within this report Environmental and financial benefits are enhanced by recent laboratory and pilot plant studies conducted by Oretek Limited. The Oretek CPC process for the recovery of copper and the recycle of cyanide from copper cyanide-containing solutions does not require pH adjustment to the alkaline cyanide leach conditions. Copper ions are coordinated to a water-soluble and/or an organic soluble polychelating agent under alkaline conditions and the cyanide ions are displaced Membrane separation, or phase separation of the polychelated copper from the cyanide ions enables the cyanide ions to be recycled and the copper to be directly electrowon from the polychelating polymer. The polychelating polymer is then recycled. Ion exchange resins and solvent extraction systems which may be incorporated into the above process will also be discussed in detail.

Jan 1, 1998

By Robert L. Opila

Negative electrodes for alkaline nickel-metal hydride batteries composed of MmNi3.5Al0.8Co0.7, where Mm is misch metal, have been characterized electrochermically and using x-ray photoelectron spectroscopy. The stability and rapid hydriding and dehydriding kinetics of the alloy in KOH are attibuted to a surface film. The protective surface film is shown to consist of an porous, outer hydrated layer and a dense, inner oxide layer. In addition, metallic nickel and cobalt are found throughout the film, and are presumed to form a conductive, percolative network that permits rapid electron transfer from the bulk to the solution, allowing rapid electrochemical formation of atomic hydrogen.

Jan 1, 1997

By Bin Zhu, Mingmei Zhu, Hong Zhou, Xiaofei Dou, Bin Xie, Yu Wang, Tiancheng Lin

In this study, the formation of 2CaO·SiO2 and 3CaO·P2O5 solid solution (nC2S-C3P) in hot metal dephosphorization process is discussed. The variations of CaO and SiO2 mass, both in nC2S-C3P solid solution phase and liquid slag phase with increasing P2O5 mass in CaO-SiO2-FetO-P2O5 slags were calculated using Factsage software. CaO-SiO2-FeOt-P2O5 slag containing up to 18 % P2O5 was melted at 1823 K then cooled to 1673 K. The contents of CaO and SiO2 both in the solid solution phase and liquid slag phase of quenched samples were observed and analyzed by SEM/EDS. Both the calculated and experimental results show that the contents of CaO and SiO2 in the solid solution phase decreased, just opposite in the liquid slag phase, with increasing P2O5 content in the slags. Formation mechanism of nC2S-C3P solid solution in the slags was derived based on the ionic structure theory of molten slag. The SiO4 4- in the nC2S-C3P solid solution can be replaced by PO4 3- in the liquid phase resulting in the increasing of free Ca2+ and SiO4 4- in liquid phase.

Jan 1, 2015

By Gary A. Wickham

In the zinc industry, this past decade has seen both prosperity and depression. Significant changes have occurred throughout the world in mining, smelting, refining, and marketing. This paper will review many of the industrywide changes of recent years and the potential impact for 1990s. In addition to an historical review of supply and demand are discussion of technology considerations for zinc and zinc based products, effects of geographical shifting of markets, and projections for the 1990s.

Jan 1, 1990