By N. Ono, H. Fujiwara, S. Otsuka-Yao-Matsuo, T. Omata

"The electrical conductivity and the oxygen release and uptake of sintered indium tin oxide (ITO) upon heating and cooling under the condition that P(O2)/P*=4.9X10-4 (P* = atmospheric pressure), :when P(O2) was approximately 50Pa, were simultaneously measured by using a closed-system oxygen-gas analyzer. A large increasing in -the electrical conductivity - upon the· oxygen release detected in 1130<T<1273K was observed. Quantitative relationship between the number of oxygen atom released from ITO and the conduction electron density in ITO was studied. The release of one oxygen atom agreed with the generation of two conduction electrons, i.e., the efficiency-carrier-generation for the oxygen release from the ITO was almost one. The oxygen atom released must be originally at the quasi-anion site in the C-type rare-earth lattice, i.e., the 16c site in the space group of Ia3, as an interstitial excess oxygen, Oi"". It was concluded that the mechanism of conduction carrier generation and compensation upon SnO2 doping into In2O3 can be expressed by the defect equation, 2SnO2-2Sn1n +2(1-z)e'+zOi""+3O0 x+(l-z)/2O2, and that the oxygen release bringing the increase in the electrical · conductivity can be expressed by the equation, Oi""-1/2O2+2e'.IntroductionThin films of SnO2-doped In2O 3 (generally designated as ITO, for indium tin oxide), which have high optical transparency for visible light and high electrical conductivity, have been used as transparent electrodes for liquid crystal and electrochromic displays. It is well known that the electrical conductivity of ITO depends on the content of SnOi-dopant and oxygen. However, a reliable relationship between electrical conductivity and the absolute oxygen content in ITO has yet to be reported. The elucidation of such a relationship is one of the important clues for realizing extremely highly conductive ITO electrodes."

Jan 1, 2000

By Takashi Ikeda, Masafumi Maeda

"Demand for solar cells is increasing linearly throughout the world. Last year production totaled 3000 tons worldwide. The market size of solar silicon is expected to increase further because of international ""political"" demand to reduce carbonaceous emission from energy consumed. Most elemental silicon is produced by the carbon reduction of Silica in an electric arc furnace. Purity of silicon at this stage is 90-99%. Major impurities are Fe, Ti, Ca· and Al, and minor ones are P, B and carbon. The oxidizing metallurgical process is no longer effective to remove transitfon metals because those are less noble to silicon. Nonmetallic impurities such as phosphorus and boron must be reduced to 0.001ppm for semiconductor use. The most common process for high purity silicon is the Siemens C process, which is basically distillation of hydro-chlorinated silicon followed by CVD of SiHCl3. The cost of such silicon is expensive to allow its popular use in solar cells. Currently scrap silicon -of semiconductors is used for this; however, the supply-of that scrap is limited to just a portion of semiconductor production.In this paper world demand for silicon will be reviewed and some of the processes proposed summarized.IntroductionSilicon is element 14 in atomic number and has an atomic weight of 28.0855. Little elemental silicon is found in the earth, and it is mostly found as oxides or silicate. The Clark number of silicon is very large and the second in its number. If we were discussing the volatility of silicon element on the globe, we would never worry about it. However, it is very difficult to obtain pure elemental silicon because a high purity silicon compound is very rare. In most cases these are silica (silicon oxide SiO2). As shown in Table 1, there are many grades of silica ore classified mainly by their content of iron and alumina."

Jan 1, 2000

By Burcu Ertug, Necip Ünlü

"On average, one out of two glass bottles coming on to the market is provided by recycling processes in Europe. Glass recycling has been started by the early of 1970s in Turkey, and the recycling amount has been reached to 70 thousand tons recently, while 4.2 million tons which represents only 25 percent of total glass manufactured, is the amount of glass collected annually for recycling in the world. The glass recycle process basically involves collecting, sorting, then crushing and grinding after which glass cullet is produced as the secondary raw material. Removing of the contaminants from the glass cullet, and then melting are the next steps. In this study, recent developments of 100% recyclable without any deterioration in quality, and never decomposable glass, are discussed detailed in terms of glass production processes.1.IntroductionIn many countries, waste glass constitutes a large proportion of solid wastes, and recycling the glass is a major environmental problem all over the world [1]. Among the diverse types of waste, glass is one of the most valuable recycling materials because it can be revived and recycled completely and hardly decomposes [2]. Between 80% and 85% of the mass output from the worldwide glass industry is either in the form of containers for the food, beverage, and pharmaceutical industries, or flat glass for building construction or for motor vehicle manufacture. Other product segments, whilst only constituting about 15% of the mass output, produce high value technical and consumer products by comparison with container and flat glass [3].In the present study, the recycling of Liquid Crystal Display (LCD), Cathode Ray Tubes (CRT) and Printed Circuit Boards (PCB) were examined. The production of glasses and glass-ceramics from glass cullet, synthesis of different compounds from recycled glass were other subjects of interest. The use of recycled glass for construction industry and using glass as aggregate were emphasized. Finally the recovery of glass fibers were investigated."

Jan 1, 2012

By Jay. M. Khodadadi, Josef Štetina, František Kavicka

"With the aid of the proper original numerical model of solidification the instruction for preparation of input parameters for numerical simulation of technological processes, with change of the phase or structure, will be presented. A method of calculation analysis of influence of therrpophysical properties of materials entering the system of casting-mould-cores environment, and also of boundary conditions on the required simulation accuracy will be suggested. For the cast material, the influence of heat .conductivity, specific heat capacity, density and latent heat of phase transformation also has been analysed. For metallic or non-metallic moulding material"" the influence of the see main parameters has been analysed and, furthermore, their combination, influence of thermal conductivity, and of heat storage. The order of influence of all quoted parameters of a casting and moulding material was established. For example heat conductivity in the liquid state is on the last place. From the boundary conditions the -most important influence on the total solidification time and · on the mechanism of forming of temperature field has the ·boundary condition on the casting mould boundary, then follows the boundary condition on the level of a molten metal. The negligible influence has the boundary condition on the mould frame and on the bottom.IntroductionThe original and universal mathematical model of solidification, cooling and heating has been set up and checked, in order to be capable of analysing a one- to three-dimensional steady or unsteady temperature field of the casting-mould-environment system and, namely, of the system as a whole or its arbitrary parts, during any industrial technological process whose individual processes could be solidification, cooling, heating, refrigeration and others, in any sequence or singly. The model enables the simulation of traditional and also non-traditional technologies of casting in foundries, metallurgical plants, forging operations, heat treatment processes, etc. If solidification is not the matter, the metal part of the system need not be called the casting but a component, a block, a forging and the like."

Jan 1, 2000

By Muhlis Nezihi Saridede, Burak Birol

"Plastic wastes become a huge problem day after day due to the growth of plastic industry. Hence, plastic wastes are used as a raw material for other industries to eliminate this problem. Polyethylene Terephthalate (PET), which is a commonly used for plastic bottles, may be used as a reductant for iron production because of its C and H content. In this study, composite pellets containing iron ore concentrate, flux and reductant were prepared. Crystallized PET bottles and coke were used as reductant after ground. The prepared pellets were reduced at 1400°C for 30 min. and iron nuggets were produced successfully. Usage of waste PET purely as reductant in composite pellets gives a higher metallization degree and proper carbon content than coke or PET and coke mixture.IntroductionPlastics can be seen everywhere, especially at packaging industry in our common life. The increase of plastic usage ends up with an important problem, the increase of plastic wastes. Many studies have been carried out about usage of plastics as reductant in blast furnace such as Ogaki et al.[1], Heo and Baek [2], Saridede [3], Minoru et al.[4], etc. Besides, Kato et al. [5], Nomura and Kato [ 6] and Rongfang et al. [7] have pointed out the use of plastics in coke ovens regarding to its calorific content. In EAF steelmaking, a mixture of coal/coke and plastics can be used as an energy resource instead of only coal or coke. [8] Also, the usage of PET and PC in self-reducing composite pellets increased the reduction rate. [12]PET (Polyethylene terephthalate ), which is commonly used for soft drink plastic bottles, is an important municipal waste due to its C and H content. Its molecular formula is (C10H8O 4)n. Demir and Dincer showed that PET can be crystallized at 250°C to have the ability to be ground to a size of -100 µm. [11]"

Jan 1, 2011

By Huimin Lu, Min Li, Jinghua Zou

"Zeolitic imidazolate frameworks (ZIFs) are new type of porous materials, form inerratic polyhedral in three-dimensional with large cages and small apertures, and appear structural diversity. Their hole size can be adjusted. These materials have high selective adsorption capacity to carbon dioxide. In this paper, zeolitic imidazolate frameworks were synthesized by solvothermal synthesis method with dimethylformamide (DMF) as solvent and structuredirecting agent, divalent metallic ions as cation, and imidazole as ligand. The crystals were characterized with XRD, SEM for their crystal structures and physical properties, the adsorption of the crystals for carbon dioxide was also tested, and the result suggests that these porous materials have a capacity of 1.35ml/g for storing carbon dioxide at 273 Kelvin under ambient pressure.IntroductionGlobal warming caused by the increase of carbon dioxide in the atmosphere has become one of the main environment problems, contemporary research has focused on ways to slow or stop this trend. CO2 capture has attracted attention due to the potential to trap and sequester large amounts of CO2 from concentrated sources such as power plants [1]. Traditional technologies in capturing CO2 include absorption by aqueous amines [2]. However, utilization of this process is energy intensive and expensive. Carbon dioxide storage materials investigated so far can be divided into two categories: chemical storage adsorbents and physical storage media [3]. The first kind of materials can chemically adsorb carbon dioxide within their structures and need thermal energy to release the adsorbed carbon dioxide. The examples of the chemical adsorbents include aqueous amines, gas-hyperbranched aminosilicas [4]. The physical adsorbents store carbon dioxide by physical adsorption of carbon dioxide at elevated pressure and release the adsorbed carbon dioxide at low pressure. The physical adsorbents that have been investigated for carbon dioxide storage include zeolites, carbonaceous materials and other porous materials. Until recently, a new type of microporous material, known as zeolitic imidazolate frameworks (ZIFs), has been reported as promising adsorbents for carbon dioxide storage [5 ~ 10]."

Jan 1, 2010

By Chuanfu Zhang, Jinliang Wang

"Brickless reaction shaft is the latest progress for flash smelting furnace. However, there are many factors influence the melting point of the freeze slag inside brickless reaction shaft, and their variational regularities are not obvious, thus, it is difficult for conventional methods to analyze accurately the complex data. In this research, the experiment data of slag melting point were processed based on optimal discrimination plane. For this method, two orthogonal vectors were firstly built up based on the Fisher's criterion, and then the experiment data were projected onto the two vectors, thus, two-dimensional feature vectors were extracted as criteria to determine the factors effect degree on the slag melting point. Results show that the CaO content is the greatest factor to the melting point of the freeze slag inside brickless reaction shaft, the content of Fe3O4, SiO2, Cu2 O and MgO is the second, and the FeO content is the last.IntroductionBrickless reaction shaft is the latest progress of flash smelting furnace reaction shaft. To research the influence factors on the slag melting point inside the brickless reaction shaft is significant to form freeze slag with compact structure, good heat insulation, certain intensity, appropriate thickness and reasonable distribution, to extend furnace life, to reduce energy consumption, and to promote safe production.However, due to the complex components, there are many factors influence the melting points of the freeze slag inside brickless reaction shaft, and their variational regularities are not obvious. Therefore, it is difficult for conventional methods, such as variance analysis, data fitting, etc., to analyze accurately the complex experiment data.Pattern recognition can easily classify information, even if there are many influencing factors. For pattern recognition, there are some sub-disciplines such as discriminant analysis, feature extraction, error estimation, cluster analysis (together sometimes called statistical pattern recognition), grammatical inference, parsing and matching (sometimes called syntactical and structural pattern recognition) [1, 2]."

Jan 1, 2012

By Leonardo Mota, Felipe Perissé Duarte Lopes, Marcelo Gomes da Silva, Sergio Neves Monteiro, Helion Vargas

"Natural fibers, as a class of material, are attracting the interest of engineering sectors owing to specific advantages such as comparatively reduced cost and lower density as well as environmental benefits associated with renewability and biodegradability. For industrial applications, thermal properties, among others, are required. These are major requirements, especially in the case of an insulating natural fiber. In the present work, thermal properties of the curaua were investigated by photothermal techniques, i.e., the open photoacoustic cell and a method based upon the monitoring of the temperature evolution as a function of time. This investigation, in tum, permitted to evaluate two important thermal properties: the thermal diffusivity and the specific heat capacity of the curaua fibers. Indirectly, by means of simple mathematical relations, the thermal conductivity was also obtained. The results were compared with other materials and characterize the curaua fiber as an efficient insulator.IntroductionMaterials are gaining attention in recent years owing to their benefits for the environment as compared to synthetics. Being biodegradable, yearly renewable and recyclable, the natural planted-based are considered fully sustainable [1]. In particular, their life-cycle, from growing to industrial processing, absorbs as much C02 as it is emitted and makes them neutral with respect to greenhouse gases responsible for global warming [2]. Typical examples of these environmentfriendly materials are the lignocellulosic fibers that have been used in simple items such as ropes, baskets, textile, modest roofing, etc, since the beginning of our civilization [3]. In the past few decades, these natural fibers have been extensively investigated [ 4-1 O] as a possible reinforcement phase of polymer composites in substitution for synthetic fibers. In fact, engineering application of lignocellulosic composites are today in the market, especially in the automobile industry [11-13]. Out of the hundreds available natural fibers, only part of them exhibits superior properties to be qualified for composite reinforcement."

Jan 1, 2011

By C. A. Nogueira, F. Pedrosa, F. Margarido, R. N. G. Guerra

"A hydrometallurgical process for recycling spent Zn-MnO2 batteries was developed, involving leaching with sulfuric acid, purification by precipitation and metals separation for further recovery. Leaching of zinc oxide was easily attained while for manganese oxide was rather difficult depending on temperature and acid concentration. At 90°C and with the liquid/solid ratio of 20 L/kg, more than 95% of zinc is recovered in 30 minutes with 0.5M H2SO4. To attain similar recovery for manganese, higher levels of acid concentration and time are needed (e.g 0.7 M and 2 hours). After leaching a purification step is necessary to remove iron co-dissolved through Fe(III) precipitation. Separation of zinc from manganese by solvent extraction with 1M DEHPA follows in the process route. The countercurrent multistage separation diagram developed allows the production of a zinc electrolyte with 120 g/L Zn and 0.005 g/L Mn, and a raffinate with 16 g/L Mn and 0.013 g/L Zn.IntroductionThe recycling of spent Zn-MnO2 batteries is carried out by dedicated recyclers using several process alternatives [1]. Most of the running processes use pyrometallurgical technologies [2] based on zinc distillation. Alternative treatments by hydrometallurgy have been reported [3-5] but its application is scarce.In order to contribute to the development of alternative solutions, a process for recycling batteries based on Zn-MnO2 systems has been studied. The process is based on the hydrometallurgical treatment of spent batteries in sulfuric acid media (Figure 1). The process starts with the physical processing by shredding using cutting grinders, where the batteries are opened and size reduced, allowing the liberation of the interior electrode particles or pastes. The fines can be then separated and the coarse material containing the steel scrap can be treated to remove the remaining aggregate electrode. The final scrap also contains some plastics and other non-metal materials and can be further valorized."

Jan 1, 2008

By E. Yegan Erdem, Fiona M. Doyle, Alyssa A. Maich

"There is an expanding interest in synthesizing high quality magnetic nanoparticles, most notably for biomedical applications. Different processing routes have been reported for the synthesis of magnetite and maghemite. However, some ambiguity remains on their precise chemistry, intermediates, and final products, due to the structural similarity of maghemite and magnetite, and the relative ease of redox transitions during synthesis. Here we present the results of TEM, x-ray and electron diffraction, and SQUID studies aimed at characterizing the products from two different reaction systems, thereby clarifying the reaction chemistry. The first system hydrolyzed aqueous FeCh and FeCb chlorides with ammonia in a micro fluidic reactor at ambient temperature; although the reaction product displayed a uniform distribution, it included non-magnetic goethite and lepidocrocite. If the aqueous solutions contained dissolved oxygen, there appeared to be extensive oxidation of Fe(II). The second system thermally decomposed iron (III) acetylacetonate in ether. In prior studies, oleylamine has been reported to serve as both a reducing agent and capping ligand to control particle characteristics; however, our studies revealed little reduction, with maghemite dominating the reaction products.IntroductionMagnetite and maghemite nanoparticles are co=only used in ferrofluids, in medical applications, and in drug delivery. Superparamagnetic properties, along with low cytotoxicity, colloid stability and bioactive molecule conjugation capability, make these nanomagnets ideal for both in-vitro and in-vivo biomedical applications [1]. One of the major constraints on widespread adoption of nanoparticles for these applications is the amount needed. Typical batch synthesis methods produce polydispersed nanoparticles, which require further size selection procedures to isolate the mono disperse nanoparticle population needed for many applications. In order to maximize the yield of usable particles from a synthesis operation, the reaction conditions must be closely controlled. This requires full knowledge of how the reaction conditions control the various aspects of nanoparticle growth. Many methods have been used to synthesize iron oxides, including sonochemical reactions, mechanochemical synthesis, hydrolysis and thermal decomposition. This work examines the latter two methods, focusing on oxidation and reduction of iron."

Jan 1, 2012

By Nourredine Menad, Christian Lucion, Maurice Save, Paul Hubaux, Solène Touzé

"The collection and treatment of WEEE has recently become mandatory in Europe and is now being organized. As the first step in current treatment processes is manual dismantling, we decided to investigate the development of an entirely automatic WEEE treatment procedure using physical separation techniques so as to limit manual sorting to the removal of hazardous components. Our approach was to test different wet and dry physical separation methods on bulk WEEE; i.e. gravity separation (jig and pneumatic table), electric conductivity separation (eddy currents), and particle shape separation (Lavodune classifier and vibrating helical conveyors). The results enabled us to determine a global treatment flowsheet of shredding, electromagnetic separation, eddy current separation, screening (2 mm), sink&float separation (d=1), and jigging. All the end products, except for the fine fraction, have possible recycling outlets. Batches of WEEE can thus be treated automatically once the problem of non-ferrous wires is resolved.IntroductionAccording to Ademe (French Agency for Environment and Energy Management; www.ademe.fr), France's annual production of WEEE is between 1.7 and 2.0 million tonnes. This waste, although of very varied composition, consists mainly of plastics and metals, and its collection and treatment has been mandatory in France since 2006; the modalities are gradually becoming organized. Existing treatment processes rely on a first step of manual dismantling which, though essential for removing dangerous components from the WEEE (e.g. batteries, cathode-ray tubes, ink cartridges, etc.), also includes separating out the decimetre-size plastic parts and metal parts. No fully automatic process has yet been developed for this type of waste. Moreover, the dismantling units in Europe are highly subsidized and call upon social workers. As this situation is not conceivable for the long-term, it is obviously important to develop entirely automatic WEEE-treatment technologies based on physical separation techniques. This would limit manual sorting to the removal of toxic components."

Jan 1, 2008

By Dhanesh Chandra

Metal carbonyls are of great importance in chemical vapor deposition (CVD), composite materials fabrication, and other near-net shape technologies. Carbonyl CVD application applies to deposition of high-purity metallic/alloy coatings. Vapor pressures of solid Os3(CO)12,Rh6(CO)16, Ru3(CO)12, Ir4(CO)12, Re2(CO)10, Co2(CO)8, Cr(CO)12,, and W(CO)6carbonyls have been measured using gravimetric-torsion effusion system. The vapor pressure data is used for many low and high temperature CVD applications. Interesting decomposition/disproportionation vaporization behavior has been notedfor Rh6(CO)16, Ru3(CO)12 and Co2(CO)8. The vaporization studies of Rh6(CO)16 showed virtually complete decomposition to Rh metal and the measured molecular weight of the effusing gas from the solid Rh6(CO)16 was 27.75 g/mol, close to that of carbon monoxide as compared to 1065.56 g/mol for the value of solid Rh6(CO)16. Electron microscopic characterization, X-ray line broadening results for Rh carbonyl has been performed on the vaporization product. However, Ru3(CO)12, Co2(CO)8 showed very complex behavior. The molecular weights of the vaporizing species have been estimated and the numbers of vaporizing species are proposed. For example, there was partial decomposition of Ru3(CO)12to(approx. 52%) metallic Ru and CO gas during vaporization, as suggested by the difference in the molecular weight of the vaporizing species of 107.58 g/mol compared to the actual value of 639.33 g/mol. The dimer Co2(CO)8 partially disproportionates to tetramer Co4(CO)12, monomer Co(CO)4, and CO gas. Whereas, the Os3(CO)12, Cr(CO)12,, and W(CO)6have shown virtually no disproportionation. The total vapor pressures of all the above-motioned carbonyls, partial pressures of various species, average molecular weights of the effusing gases, equilibrium constants for the vaporization reactions, their enthalpies, entropies, and Gibbs energies will be presented.

Jan 1, 2006

By Zhu Fangyi

"The article introduces the process EAF with De-P hot metal charging for Melting Stainless Steel in Baosteel stainless steel Branch. Based on the practice of production, the main effect on the Cr Loss during EAF with De-P Hot Metal Charging Melting Stainless Steel including using oxygen, the material charging and making slag are theoretically analyzed. The optimization of using oxygen can reduce the oxidation of Cr during EAF Melting Stainless Steel. The optimization of material charging, especially Si content is suitable can reduce the loss of Cr. Effective reduction can realize the lowest Cr oxide in slag. Based on the character of the process EAF with De-P hot metal charging for Melting Stainless Steel, applied the integrated control method, the Cr loss during EAF melting stainless steel decreased 43.10%. 1 INTRODUCTION EAF with De-P HM charging for melting stainless steel is a technology for stainless steel making. Practice prove that the new process can shorten tap to tap time, reduce the special power consumption, dilute the impurity element from the stainless steel scrap that is propitious to produce the high quality stainless steel, alleviate the shortage of stainless steel scrap to the production. As a new technology, the process has some technical problems and difficulties. The proportion of Cr alloy charging exceeds 20% during EAF with De-P hot metal charging melting stainless steel. As Cr alloy is difficult melting and easy oxidation, too much Cr alloy charging result in Cr loss too much and tap to tap time too long for EAF production. By applying the new technology, Baosteel stainless steel branch has increased the technology level and economy index. Now the content of Cr oxide in slag reduce from 8.59% to less than 6.0%. The Cr loss during EAF melting stainless steel decreased 43.10%. According to the practice application, the process of EAF with De-P HM melting stainless steel are theoretically analyzed. The main factors affecting the Cr loss during EAF with De-P hot metal charging melting stainless steel are discussed."

Jan 1, 2008

By Zhang Libo, Wang Xin, Peng Jin-hui, Ju Shaohua, Guo Sheng-hui, Xu Lei, Huang Meng-yang

"China is lacking high grade titanium ores. This work intends to leach impurities such as Fe, Ca and Mg from a low grade titanium ore, to increase the grade. The original material contained 65% TiO2 , 16.12% Fe, 9.4% CaO + MgO, 4.2% SiO2, 1.25% A12O3, and the particle size is between 0.053-0.045mm. Microwave energy was used to enhance the leaching effect. The results showed that when normal heating was used to leach the mineral, the extraction of impurities Fe, Ca and Mg was very low. However, when microwave energy is introduced, the extraction of Fe, Ca and Mg increased dramatically. The optimized conditions are: relative power 5W/g, the ratio of concentrate to HC1 isl5%, leaching at 160°C for 20 min with a ratio of liquid to solid 12:1 mL/g. The material obtained under these conditions contains 92.73% TiO2, 0.207% Ca + Mg, 0.8% Fe, with 94.6% Ti recovery. The poduct meets with the quality for boiling chlorine.IntroductionThe resources of titanium are very abundant, and are distributed all over the world. There are almost 140 minerals containing TiO2 with a content of more than 1%. However, there are only several minerals which can be used for producing sponge titanium. They are mainly rutile and ilmenite. The grade of nature rutile concentrates is higher than 95% TiO2, and it is a high quality raw material. But the resources of nature rutile are relatively low; after mining for many years, its resources are exhausting gradually. Although ilmenite reserves are great, ilmenite cannot be used as a raw material because of its low content of TiO2, only 45-70%; also it has a high impurity content of Ca, Mg and Fe. In these years, there is a tendency for titanium industry to use high grade concentrate."

Jan 1, 2012

By Larry M. Southwick

Pneumatic converting (Bessemerizing) of iron revolutionized the steel industry. Bessemerizing of copper (conversion of copper sulfide matte to copper metal) was proposed at almost the same time, but it was slow in being accepted. The differences between iron and copper converting were great and technical problems were substantial. It took 25 years for the process to become viable and another 25 years before a truly economical solution was found. A major economical and productivity problem was the short life for converter refractory linings. The first converters had acid (silica) linings, which were quickly consumed since silica was a flux for the process. Converters had to be relined at least once per day, a laboriously expensive manual process with only the most rudimentary mechanical aids available to assist. The industry was revolutionized almost overnight when finally a viable basic (magnesite) lining was developed. This lasted 100&apos;s of days versus less than one, leading to converters that were easier to operate and which handled larger charges. This change occurred after W.H. Peirce and E.A.C. Smith, with support from the Guggenheim interests, successfully operated a basic lined converter in a copper refinery in Baltimore. While Peirce and Smith are generally given credit for the development and explosive acceptance of this idea, a Pittsburgh industrialist, Ralph M. Baggaley, working in an independent smelter in Butte, Montana, successfully built and operated a basic lined converter four years before they did. In fact, the early support for Peirce and Smith likely occurred because Guggenheim&apos;s staff were encouraged after thoroughly examining Baggaley on his earlier successes. The questions of technology primacy between Baggaley and Peirce/Smith are ironically similar to those between Wm. Kelly and Bessemer in converting iron to steel. This paper will review what Baggaley (and other early researchers) accomplished, examine why he (or they) did not receive credit equal to Peirce and Smith and explore what his (their) place should be in the development of successful basic linings. More suspects than a Victorian Whodunit.

Jan 1, 1999

By J. R. Odekirk

The nature of mineral distributions and locking characteristics in mill products are important factors in understanding mill performance. Such data are obtained by microscopic point counting methods. Reduction &apos;of point-count data from volume to weight percentages, and reduction of data for each size fraction back to a head sample requires lengthy hand calculations. The use of computer processing for such data reduction results in obtaining information on a realistic time basis. An example of computer processed point-count data is presented.

Jan 1, 1981

By Rajesh Kumar Mishra

About 500,000 troy ounces of Platinum Group Metals (PGM) will be available for recycling each year from spent automobile catalytic converters in North America alone. Platinum Group Metals? from spent catalyst can be extracted by Hydrometallurgical, Pyrometallurgical or Gas Phase volatilization processes. This paper is a review and comparative study of various processes investigated for PGM extraction. A number of processes described in this paper have already been commercialized. The technical and environmental aspects of the important processes are discussed.

Jan 1, 1989

By Gus Van Weert

The cost of oxygen is a major and common factor in the hydrometallurgical processes developed or proposed tor the oxidation of refractory pyrites. This cost involves charges for the generation and the transfer of the 02 to the mineral slurry. Bio-oxidation faces considerable design demands which require large scale equipment to be resolved. Nitric acid assisted oxidation offers low cost oxygen units; this method of pyrite oxidation deserves a closer look for large scale plants treating pyritic gold ores and concentrates.

Jan 1, 1990

By SM Rao

Nuclear Fuel Complex (NFC ) , Hyderabad (IN DIA ) , is engaged in the manufacture of nuclear fuel assemblies and zircaloy structural components required for the Indian nuclear power reactors. The production of zirconium oxide, sponge and zircaloy materials through chemical and hydro - metallurgical processes generates many effluents containing valuable zirconium and hafnium . This paper deals with the various processes such as multiple crystalization, phosphate precipitation, ion-exchanges amine solvent extraction etc, for the treatment of these effluents and subsequent recovery of valuable zirconium and hafnium .

Jan 1, 1992

By Niander A. Cerqueira, Pâmela Berçot, Afonso G. Azevedo, Victor B. Souza, Victor T. Bartolazzi, Bruno Padilha

In recent years, concern about environmental issues has become a parameter to consider in the projects in engineering. In order to reduce the impact that the tire improper disposal may result for the environment, we sought a solution to this problem. This article proposes the use of rubber scrap tires as fine aggregate in concrete production. The material produced was analyzed by a bending test, resulting in product quality, in particular for application in situations requiring a more ductile material.

Mar 1, 2017