By Jiang Diao, Xuan Liu, Tao Zhang, Bing Xie

In the present study, the oxidation process of vanadium and chromium bearing hot metal was investigated by using CaO-FetO-SiO2 slags at 1653K in MoSi2 furnace. The results indicated that both the vanadium distribution LV and chromium distribution LCr were of the orders of 2.2~2.4 with the basicity range of 1.32~1.78 and FeO weight percent range of 28%~45%. Both LV and LCr decreased with increasing basicity and decreasing FeO weight percent. The phosphorus distribution LP was of the order of 1.34~1.56. However, LP increased with increasing basicity and decreasing FeO weight percent. The oxidation ratio values of V and Cr in hot metal were above 84% and the values of P were nearly 50%. In other words, it means the addition of CaO in vanadium slag provided a certain ability of dephosphorization along with keeping high oxidation ratios of V and Cr.

Jan 1, 2015

By Pengfu Tan

NiModel, a thermodynamic model, database and computer program, has been developed to predict the distribution behavior of Ni, Cu, Co, Fe, S, O, As, Sb and Bi, and heat balance in the nickel pyrometallurgical processes such as Outokumpu flash smelting, Outokumpu direct high-grade matte smelting, INCO flash smelting, and Peirce-Smith converting processes. In this model, as much as 16 elements (Ni, Cu, Co, Fe, As, Sb, Bi, S, O, Al, Ca, Mg, Si, N, C and H) are considered. The compositions of matte, slag and gaseous phases, and heat balance are calculated using the thermodynamic data and the activity coefficients of the components derived from the experimental data. The model predictions were compared with the known industrial data from Kalgoorlie Nickel Smelter in Australia, Outokumpu Harjavalta Nickel Smelter in Finland and INCO Metals Company in Canada, and an excellent agreement was obtained. In this paper, the applications of NiModel in the nickel pyrometallurgical industries have been presented. NiModel has been used by Jinchuan Group Limited in China.

Jan 1, 2004

By Olga Frank-Kamenetskaya

The experimental results of study of atmospheric corrosion processes on Saint-Petersburg bronze monuments surface, received in situ and by means of simulating experiments, have been discussed. Influence of the time factor on corrosion film (patina) mineral composition has been analyzed. Direct dependence between patina mineral composition and environmental conditions has been proved. The sequence of patina phases crystallization has been established. Effect of the chemical composition and heterogeneity of artistic bronze and also monument surface structure on the rate of corrosion process has been regarded. The time variations of mass of the crystallized in the hydrochloric acid vapor phases have been investigated. The kinetic laws of their development at the initial stage of formation, indicating simple (non chain) reactions, have been revealed.

Jan 1, 2006

By Yang Hong-ying, Yu Juan

Electrochemical behavior of natural chalcopyrite in electrolyte solution at pH value of 6.97 was studied by cyclic voltammetry, X-ray photoelectron spectroscopy and electrochemical impedance spectroscopy. The results showed that the electrochemical processes occurred on electrode surface were controlled mainly by the growth of sulfur species at lower applied potentials (<0.35Vvs.SHE), and the oxidative dissolution of sulfur species and the hydroxylation of iron at higher applied potential (>0.45V). The EIS spectra of oxide product layers could be illustrated by the equivalent circuit of Re(QdlRct(QfRf)), and the degree of hydrophilicity for chalcopyrite was higher when the value of charge transfer resistance Rct. was greater. The optimum potential range for the floatation of chalcopyrite in collectorless solution at pH value of 6.97 was between OCP (0.165V) and 0.35V.`

Jan 1, 2015

By Robert Fritzsch, Ragnhild E. Aune, Mark William Kennedy, Behzad Mirzaei

"The quantitative particle concentration can give important information about the cleanliness of melts for quality control in primary and secondary production of aluminum. Manual quantification of the particle concentration is normally a time consuming process and human control can bias the acquired images and particle count.The present paper explains the automated image-processing steps for the quantification of SiC-particles, with equivalent diameters from 2 to 25 µm, in solidified A356. A total of 700 micrographs, acquired with a standard white light microscope with 10 x magnification, were analyzed. The applied software (Image Pro-Plus 7.0 from MediaCybemetics®) allows for programming of macros which in tum provides the user with a higher degree of control. The automated results are compared with the results obtained by manually counting the particles in the same micrographs. The impact of the automated results on the estimated filtration efficiency was established to be only -3%.IntroductionInclusions are both indigenous and exogenous particulates that are present in commercial metals such as aluminum. If large individual or large numbers of inclusions are present, they can have a significant negative impact on the appearance, mechanical and chemical behavior of products produced from the metal. Aluminum is known to contain large numbers of inclusions: =50 µm in size, e.g. typically <l ppm by volume or <100,000 inclusions of>20 µm per kg of metal as detectable using a Liquid Metal Cleanliness Analyzer, LiMCA [1]. Depending on the final application of the aluminum, inclusions can render the metal 'not fit for purpose', and result in serious economic consequences to metal producers.It is not surprising that the aluminum industry has developed a number of treatment processes to improve metal cleanliness, given the large number of high value products whose quality can be adversely affected by inclusions. CFFs are the most commonly applied filtration process and have been used to filter >50% of the world production of aluminum since the 1990's [2].Inclusions in aluminum may be particles, bifilms [3] or clusters of: oxides (Al2O3 , SiO2), spinels (MgO· Al2O3), carbides (SiC, Al4C3), nitrides (AlN), borides (TiB2), sulfides, phosphides and intermetallics [ 4]."

Jan 1, 2013

By J. McKelliget, J. Szekely, Oreper. G. M.

"1. INTRODUCTIONThis paper is concerned with heat and fluid flow phenomena in arc welding operations. Fig. 1 shows a schematic sketch of a typical arc welding arrangement. It is seen that an arc is being struck between an inert electrode and a metal surface and that the resultant current and energy flow will case the formation of a molten weldpool.It is clearly appreciated that the weldpool shape and the nature of circulation in the weldpool may play an important part in determining the ultimate weld quality. It is known, furthermore,· that the weldpool behavior in turn will be affected by the spatial distribution of the current and the heat flux it receives from the arc. Indeed, the inherent coupling between the arc and the weldpool is a key feature of welding operations.Up to the present useful work has been done on the modelling of heat transfer and melt circulation in weldpools (1,2,3,4) and also on the description of arcs, including welding arcs (5,6,7,8). However, the coupling between these two sets of phenomena is relatively unexplored in a qualitative sense. The purpose of the present paper is to examine the interaction between welding arcs and weldpools. The actual material will be presented under the following headings:"

Jan 1, 1986

By A. Gibson

Most methods for the treatment of scrap printed circuit boards do not reclaim the components in working order as the boards are either fed to a copper smelter, to recover the valuable elements, or, simply landfilled. This work reports the dissolution of the solder in fluoroboric acid containing Ti4+ ions which was particularly selective for solder, allowing the components to be recovered. The solder was subsequently electrowon from the leachant. The boards were then shredded and the copper dissolved in ammonium sulfate and, then treated via solvent extraction to give an electrolyte suitable for electrowinning. The remainder of the metals were dissolved aqua regia, silver remained unattacked by the aqua regia, palladium precipitated as Pd(NH4)Cl6 in the presence of zinc and nickel, the gold was removed by solvent extraction and precipitated as nanoparticles. The aqua regia was then diluted and the zinc and nickel separated by solvent extraction.

Jan 1, 2009

By F. Qian

Direct impingement of molten metal baths by a gas jet is commonly encountered in such processes as BOF and electric arc furnace steelmaking. Shape and local fluid mechanics in the impinging region is important because it determines the interaction of the metal pool with the surroundings. Goal of the present work is to characterize and understand the interfaces at the impinging region. Using a physical model consisting of water/corn oil and water/kerosene as surrogates for metal/slag, interface shapes for slag-gas, slag-metal and metal-gas are investigated. Influence of transport properties of the two liquids on the shape and flow fields are also experimentally determined under various impinging jet conditions, namely jet momentum and jet height. The viscosity of the slag layer (corn oil or kerosene) has the most significant effect on the interface shape and the induced flow fields. The interface shapes were measured both photographically and by using a surface- tracking resistance probe. The limiting condition at which the jet breaks through the corn oil or kerosene layer and reaches the water layer was determined experimentally

Jan 1, 1994

By S. K. Kawatra

"A typical steelmaking facility produced 50,000 tons per year of slag in their hot-metal desulfurization process. This slag had a sufficiently high iron content that it could be beneficiated and recycled in a blast furnace, provided that the slag could be agglomerated into pellets suitable for use as blast furnace feed. In this work, beneficiated slag was agglomerated using both a conventional bentonite binder, and a fly-ash-based binder (FBB) that was formulated by the investigators. The FBB consisted of a combination of highcarbon fly ash with calcium hydroxide activator, allowing the FBB to exhibit binding properties when moistened. It was determined that beneficiated slag agglomerated with FBB had superior compressive strengths compared to slag agglomerated with conventional bentonite binder. The FBB is therefore a satisfactory method of binding the agglomerated slag. Since the fly-ash component of the FBB is commonly discarded as waste, this approach also provides a means for utilizing high-carbon fly-ashes that currently have very little commercial value.IntroductionIn 2006 approximately 72.4 million short tons of fly-ash were produce in the United States [1]. The majority of fly-ash which was used that year was consumed concrete, structural fills, and cement. It is also used in road base, aggregate, and other applications. However, 55.2% of the fly-ash produced in 2006 was not utilized and ended up being sent to a landfill. Essentially all of the land filled fly-ash could be a suitable binder for pelletizing desulfurization slag and other steel plant waste oxide materials. Fly-ash based binders (FBB) have been shown in laboratory studies to be suitable for producing iron ore concentrate pellets of equivalent strengths as those bonded with bentonite [2,3,4]. The utilization of highcarbon fly-ash within the market is important for reducing the volume of currently unmarketable and land filled fly-ashes. FBB would be a much cheaper alternative to the current bentonite binder or organic binders used for iron ore concentrate and would help to reduce pellet costs. Currently, transportation more than doubles the final cost of bentonite since it is produced hundreds of miles from the pelletizing plants, while fly-ash is produced from power plants located nearby pellet plants and steel mills. FBB’s also show promise for use in other high volume applications such as foundry sand mold binders."

Jan 1, 2008

By Klaus-Markus Peters, James G. Hemrick, John Damiano

"Work was performed by Oak Ridge National Laboratory (ORNL), in collaboration with industrial refractory manufacturers, refractory users, and academic institutions, to employ novel refractory systems and techniques to reduce energy consumption of molten material processing vessels found in industries such as aluminum, glass and pulp and paper. The energy savings strategies discussed are achieved through reduction of chemical reactions, elimination of mechanical degradation caused by the service environment, reduction of temperature limitations of materials, and elimination of costly installation and repair needs. Key results of several case studies resulting from US Department of Energy (DOE) funded research programs are discussed with emphasis on applicability of these results to high temperature processing industries.IntroductionRefractory materials are limited in their application by many factors including chemical reactions between the service environment and the refractory material, mechanical degradation of the refractory material by the service environment, temperature limitations on the use of a particular refractory material, and the inability to install or repair the refractory material in a cost effective manner or while the vessel is in service. All of these limitations reduce the energy efficiency of the process as degraded refractory materials lead to loss of process heat (reduced insulation by refractories) and the need for maintenance through repair or replacement of refractory linings.This situation is conceptualized in Figure 1 which shows that when the thickness of the refractory wall is reduced by chemical or mechanical degradation, the heat losses through the wall increase exponentially. The subsequent maintenance to repair such conditions often requires cooling of the furnace or refractory lined vessel which entails loss of energy due to cooling and consumption of energy due to reheating. Additionally, production time and capability are sacrificed.Additionally, in most applications where refractories are used (metal melting furnaces, glass furnaces, steel making furnaces, gasifiers, etc.) wear of the refractory lining is not uniform. Very often, specific areas will wear (become thinner) more rapidly due to exposure to more corrosive or erosive conditions. This concept is illustrated in Figure 2, through the example of excessive metal line corrosion."

Jan 1, 2009

By S. Ozbilen

"Al-Li binary alloys with nominal Li contents of0.15, 1.1and2.8 (in wt%) were aged naturally at room temperature for two months, aged at low temperatures ( 65 and 1 OOEC) for up to 2 months and aged artificially at 190EC for 4 days after water quenching to 25EC following solutionizing at 530EC for 20 minutes. Ageing behavior of these binary alloys were studied by Vicker's Hardness measurements and DSC thermal analysis. Thermal analysis results indicate the formation of GP zones of Al-Li system in Al-2.8wt%Li binary alloy. In the same alloy, rapid quenching from one phase region (a) gives rise to precipitation of small o' particles in a matrix (a) with still high supersaturation. During ageing of this alloy below lOOEC an additional transformation, i.e., GP zone formation occurs proceeding at a very high rate which is described on the basis of the theoretical analysis for the quenched Al-Li system proposed by Khachaturyan et al [6]. Ageing at temperatures below 11 OEC takes place slowly by the formation of small d' particles of lower thermal stability than the quenched-in d precipitates in addition to GP zones resulting in an increase in hardness compared to water quenched samples. During artificial ageing, GP zones transform by dissolution to d' precipitates while d' particles already in the microstructure coarsen during under aged condition at which hardness increases with time till peak aged condition.IntroductionIn binary Al-Li alloys the d' (Al3Li) fully coherent internally ordered inetastable phase of Li2 structure with a=0.4038d [1-5] forms homogeneously between 120 and 190EC before the formation of stable d' (A!Li) phase and cause the superior mechanical properties. This is due to an appreciable age hardening effect resulting because of the d' precipitation during ageing [1]. The response of d' to decomposition and its formation kinetics have been studied previously and it is believed that the decomposition of the a-supersaturated solid solution occurs in a two stage process; i.e., a 6 d' (Al3Li) 6 d(A!Li). Khachturyan et al [6] theoretically investigated precipitation of the d' phase and gave an interpretation of the transformation paths of the quenched Al-Li alloys. They predict that the disordered supersaturated solid solution congruently orders, and then the uniformly ordered solution decomposes into ordered regions that differ in Li-content. Finally, ordered d' phase forms in the disordered matrix."

Jan 1, 1998

By Claudio Toro, Alex Moyano, Rodrigo Díaz, Hugo Jara, Carlos Caballero, Pedro Morales, Leandro Guzmán

"During 2007, Codelco-Chile carried out industrial tests to validate the Continuous Converting Process in the Teniente Converter of the Codelco Norte smelter.For planning and starting up the tests, a predictive, analytical and dynamic model was developed to support operational decisions. The dynamic model was developed using the METSIM® platform and dynamic data exchange (DDE) to operate smoothly with MS Excel®. The main feature of this real-time model was the on/off-line ability to work and gather data from either the smelter’s PI system® or database, and simulate the operation with or without scheduled events and controls.The main model development aspects, which include thermodynamics, metallurgical and kinetic considerations, slag-type and on-line mass and heat balances of the process, as well as the successful validation of the model, are presented and discussed in the present paper."

Jan 1, 2009

By P. A. Davidson, D. J. Short

"In this paper we describe a 'non-contact' electromagnetic nozzle suitable for sprayforming and gas atomization processes. In such processes there is a need to control the flow rate and diameter of the liquid metal jet whilst minimising contamination of the stream. This can be achieved using an electromagnetic valve, which partially levitates the jet in freespace, using a segmented cylinder surrounded by an induction coil. This valve will significantly enhance the quality of the titanium alloys and nickel-based superalloys used in sprayforming and gas atomization. This paper describes the design and test of a laboratory prototype valve based on experiments performed with liquid tin.1. Introduction In many industries there is an increasing need for clean, high quality metals and alloys based on titanium and nickel. Two important processes are: 1) Spray deposition which allows the liquid metal to be converted to a near-net shape, thus alleviating the need for subsequent forging and extensive machining and; 2) Powder production of titanium by gas atomisation.In centrifugal spray deposition of titanium (see figure 1) the metal is induction melted in a cold crucible. The crucible consists of a number of water-cooled segments, which allows the high frequency magnetic field of the coil to pass through the crucible, and into the melt. The charge is melted by the induced eddy currents. Locally at the crucible walls the liquid metal solidifies, and is contained within a. 'skull' of its own solid, thus reducing contamination from the crucible wall. Once melted the metal is poured through an electrically heated graphite nozzle and into the spray forming chamber. The principal limitation of the process to-date, however, is that it currently uses a graphite and /or ceramic nozzle to direct the flow of liquid metal to the atomizing disk and as such there is considerable risk of nozzle erosion with inevitable effects in terms of contamination of the melt stream and variability in flow conditions. In this research programme we develop a. non-contact electromagnetic nozzle, which will totally eliminate refractories and/or ceramic materials from the melting and casting process. This will greatly enhance the technological capabilities of sprayforming and gas atomization processes."

Jan 1, 1999

By Duan Xin-hui, Wang Xin, Peng Jin-hui, C. Srinivasakannan, Zhang Li-bo

The work attempts to optimize the process of preparation of modified semi-coke from semi-coke using phosphoric acid (H3P04) as the activating agent using the response surface methodology (RSM). The influences of three major dependent variables, the impregnation ratio, activation time, and activation temperature were assessed on the independent variables yield and the iodine number. The empirical relationship between the dependent and the independent variables were established using the quadratic response surface models, which were utilized to optimize the process parameters. The significance of each of the parameters and interaction among the parameters on the independent variable was assessed based on analysis of variance (ANOVA). The process variables were varied within the range of impregnation ratio (IR) from 1.5 to 4, activation time from 30 to 90 min and activation temperature from 550 'C to 650 'C. The optimized process conditions were estimated to be an IR of 2.29, activation time of 32 min, and an activation temperature of 605°C respectively using the process optimization tool. The BET surface area of modified semi-coke of the optimized sample was estimated to be 915m2/g, with the pore volume of0.71cm3/g, with an average pore diameter of 3.09 nm, with micropore volume fraction being 52.36%. The scanning electron microscope (SEM) images were utilized to visualize the surface pore structure.

Jan 1, 2013

By Yoshifumi Abe, Akinori Toraiwa

"Nippon Mining & Metals started a new copper anode slime treatment plant that processes slimes in a chloride media. The basic plan of the process was proposed by Mr. James E. Hoffmann and Nippon Mining & Metals modified and advanced to produce precious metals in acceptable qualities for the company. The process has a wet chlorination stage of decopperized slimes, a solvent extraction and a reduction stages of gold, a silver chloride reduction stage and separative reduction stage of its gold extraction raffinate. The new plant of this process started in 1997 and has been operated in good condition.IntroductionThe old anode slime treatment plant of Nippon Mining & Metals, located in it's Hitachi Refinery, processed anode slimes through a combination of pyrometarllurgical processing and electrorefining. There was a need to plan a future of the plant because the maintenance cost increased year by year and a new selenium registration was going to be applied to the plant. Some plans were discussed and the result was that the process proposed by Mr. Hoffmann was superior among them.Nippon Mining & Metals started 'to examine the process and the experimental result showed that the process had an ability to be its new process but further research should be necessary to produce precious metals in acceptable qualities. The final process flow has some modified and additional stages to be suitable for its requirement. Silver processing stage is quite changed. Gold extraction stage has a new step to polish gold loading DBC. Gold extraction raffinate treatment stage is advanced to be able to recover precious metals, selenium and tellurium, separately. Aeration under atmospheric pressure is employed in decopperizing stage.The basic design of the new plant started in 1995 and finished in 1997. The construction of the new plant began in April 1997 and finished in October. The plant has been operating well after the four months test operation."

Jan 1, 2000

By K. P. V. Lei

The U.S. Bureau of Mines investigated a hydrothermal sulfidation procedure to recover lead and silver from plumbojarosite. The plumbojarosite, generated during pressure-oxidative leaching of zinc concentrate in a commercial operation, contained, in percent, 25.4 pb, 18.8 Fe, 1.4 Zn, 29.5 SO,2-, 3.2 s?, 13.4 total sulfur, and 7.4 oz/ton Ag. The sulfidation was conducted in an autoclave and converted the plumbojarosite to amorphous iron oxide and liberated the lead and silver as sulfides. The best operating conditions were using 50 9 of plumbojarosite and 7 pct s? (2.04 9 S? added) in 500 mL of 2.0 mol/L NH3, 150? C, and 1 h. The sulfidation product contained, in percent, 37 Pb, 28 Fe, 6 S2-, 2 SO,2-, and 11.2 oz/st Ag. Ferric chloride leaching extracted 98 pct Pb and 97 pct Ag from the sulfidation product.

Jan 1, 1990

By J. F. White

An experimental study was undertaken to evaluate the feasibility of a selective chloridizing roasting pre?treatment process for the elimination of impurities from zinc feed?stocks prior to recovering zinc by conventional unit operations. In this investigation, a number of chemistries that might serve as a basis for such a pre? treatment process were examined. A variety of chloridizing agents were admixed with EAF dust to promote the selective removal of lead and cadmium by the formation of volatile metal chlorides, he results of the experimentation firmly establish that selective chloridizing roasting is a technically feasible means of eliminating lead and cadmium from EAF dust. Excellent extraction efficiencies were accomplished with a number of chloride additives; as high as 98 percent lead extraction and 88 percent cadmium extraction were attained with minimal zinc losses, Continuous pilot?scale tests reinforced the trends established by laboratory?scale experimentation, Attempts of chlorine elimination using pyrohydrolysis were less successful. The extent of chlorine elimination was found to be highly dependent upon EAF dust sample type and treatment temperature.

Jan 1, 1996

By XUEWEN WANG, Xingming Wang, Xuehui Liu, Mingyu Wang

The Panzhihua titanium concentrate contains high contents impurity of Mg and Al, and it is difficult to prepare high grade titanium slag. To solve this problem, a sodium salt roasting-acid leaching process was proposed for removing the impurities in titanium concentrate. Na2CO3 and titanium concentrate were mixed with the proportion of 1:4, and then the mixture was roasted at 700 for 2h. After roasting, the calcine was leached with HCl solution. The experimental results showed that the removal rate of silicon and aluminum can reach more than 85% and 80%, respectively, at leaching temperature of 70 , leaching time of 4h, HCl addition of 5ml and liquid-solid ratio of 4:1.

Jan 1, 2016

By Eric Pirard

Theoretical studies carried out on shape analysis supply mathematical tools to analyze the influence of grain shapes on ore beneficiation. In the case of statistic images like those encountered in applied mineralogy parametrical and harmonical analysis methods are used. It is important that the shape parameters are adapted to the specific processes involved in ore beneficiation, while remaining easy to manipulate. The inertia parameters are considered in the scope of granulometric and gravimetric processes It appears that they are able to distinguish between the resulting products where very popular shape parameters are not. The measured statistics are analyzed through discriminant analysis procedures in order to estimate the importance of morphological differentiation and the aptitude of shape parameters to account for this.

Jan 1, 1989

By R. G. Haire

Studies of the f-elements under pressure provide important insights into their solid state chemistry and physics. From such studies, of the elements and their alloys, it has been established that the normally localized f- electrons of several of these elements can become, involved in bonding under pressure. The electronic behavior of f-element compounds under pressure tend to be more difficult to interpret, due to the variety and the nature of electronic orbitals that are present. The 4f-elements and some 60% of the 5f-elements have been studied under The systematic comparisons that have been established for these materials are discussed.

Jan 1, 1992