Search Documents

By Jayagopal Ucbil, M. Krishna, V. T. Vijayalakshmi

"The pitting susceptibility of aluminium metal matrix composites reinforced with garnet particles has been examined using static weight loss method by exposing the metal matrix composites (MMC) specimens to the action of IN HCI acid at laboratory temperature for different time intervals. It was found that the corrosion rate decreased with increase in weight percentage of reinforcement while the corrosion rate was a function of the matrix alloy but not of the reinforcement material. Further, it was found that the rate of corrosion was dependent on the interface region formed between the reinforcement and the matrix. A comparison of the base matrix with the corresponding composite when subjected to heat treatment for varying periods of 4, 8, and 12 hours respectively was made. The comparison revealed that corrosion resistance of the composite increased with the duration of heat treatment and this has established a considerable improvement in corrosion resistance of the composite when compared with the base matrix.IntroductionMetal matrix composites (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and light weight [1-5]. The trend is towards safe usage of the MMC parts in the automobile engine, which work particularly at high temperature and pressure environments [6-7]. Particles reinforced MMCs have been most popular over the last two decades. Among the MMCs, the most popular families are represented by aluminium reinforced with ceramic particles. Although the incorporation of the second phase into a matrix material can enhance the physical and mechanical properties of the base metal, it could also significantly change the corrosion behavior."

Jan 1, 2000

By J. A. Eisele

There is currently much interest in how extraction of gold and silver from ores with acidic thiourea solution compares with extraction using alkaline cyanide solution. Agitation leaching tests were performed by the Bureau of Mines on 14 precious metal ores using sodium cyanide (?NaCN) and thiourea [(NH2)2CS) as extractants. The objective was to compare the results of the two extractants. NaCN was used at a concentration of 2 g/L with and without H202 as an oxidant. (NH2)2CS was used at concentrations of 2 and 20 gjL, and the solution potential was controlled at 390 to 420 mV standard hydrogen electrode (Eh) with Fe2(S04)3. With both reagents a.t 2 g/L extractant levels, NaCN extracted more gold and silver than (NH2liCS from all of the ores. At 20 g/L (NH2)2CS compared with 2 g/L NaCN, (NH2)2CS extracted more gold than NaCN from two ores, the same amount from one ore, and more silver from one ore. NaCN extracted more gold than (NH2 )2CS from 10 ores and more silver from 4 ores.

Jan 1, 1989

By Mark Kruzynski, Srinivas Garimella, James T. Wiswall

"A flue gas recirculation (FGR) system for a combustion fired aluminum melting furnace is experimentally investigated. The FGR system flows combustion air in a turbulent jet within the flue gas stream, and the turbulent jet flow is collected in a tube at a distance from the jet exit. Entrainment of the flue gases as well as heat transfer between the flue gases and the jet occurs over the length of the exposed jet. Heat transfer between the flue gases and the jet, and the amount of flue gas entrained into the jet (derived from temperature, flow rate and oxygen fraction measurements) were measured as a function of nozzle exit velocity and the distance between the nozzle exit and collection tube. In addition to flue gas entrainment, a fuel savings of up to 7%, due to heat transfer over the length of the jet, was projected from the measurements obtained.IntroductionFlue gas recirculation can be applied to aluminum melting furnaces to control combustion temperature. When coupled with a device to improve furnace efficiency by recovering heat from the furnace exhaust, flue gas recirculation provides a control technique that is integral to achieving the goals of reducing fuel consumption, increasing product yield, increasing the longevity of infrastructure, and reducing pollutant emissions. In particular, combustion temperature control can help reduce reactivity of the products of combustion with the molten metal surface and furnace refractory materials. Combustion temperature control can also help improve the life of heat exchangers used to recover energy lost to the environment in the flue gases, and reduce NOx formation in the combustion process. Flue gas recirculation can also dilute oxygen used in oxy-fuel combustion to reduce reactivity.Flue gas recirculation has been used since the 1970s to control flame temperatures in the automotive industry [1-3] and has successfully reduced NOx emissions. Many different flue gas recirculation approaches for high temperature melting such as melting aluminum and glass have been patented since the 1980s [4-12]. There has also been academic interest to determine the fundamental performance characteristics of flue gas recirculation in high temperature furnaces and in combustion [13-15]."

Jan 1, 2014

By M. J. Adam

The Bureau of Mines is investigating the feasibility of partitioning complex sulfide minerals to simpler sulfide phases by sulfidation reactions. Such partitioning can afford opportunity to improve selective extraction of mineral constituents of value. This report describes research involving sulfidation partitioning of byproduct chalcopyrite concentrates from Missouri lead ore processing, and a Utah chalcopyrite concentrate from Cu ore processing. Small chalcopyrite samples were sulfidized with elemental S in glass capsules sealed after evacuating and backfilling with He, by heating for 1 to 24 h at specific temperatures in the range of 250? to 500? C, extending from below to above the boiling point of S (-4450 C).

Jan 1, 1987

By Hideki Yamamoto, Shigeno Matsumoto, Junji Shibata

"Some fundamental studies were carried out in order to produce composite powders comprising of two or three metal oxides ~y using liquid-liquid extraction and to develop the control technology of the particle size. The combination of samarium and cobalt was selected as the two component composite powders. Both stripping and crystallization occurred at the same time by emulsifying the organic phase loading the two metals extracted with Versatic Acid 10 and the aqueous solution containing oxalic acid. The effect of aqueous pH, oxalic acid concentration and agitation speed was examined on some properties such as crystallization percent, particle size and shape of each metal oxide powders obtained in this process. The analysis by using EDX showed that the two metal oxides were distributed uniformly.IntroductionComposite metal and metal oxide powders with high purity are indispensable as industrial materials in the fields of electrical engineering, electronics and metallurgy. It is difficult to mix metal powders or metal oxide powders uniformly for the production of alloy powders. If insoluble metal salts are allowed to collect as crystallization products in the crystallization-stripping process, the conventional melting and crushing process can be avoided. After mixing of the organic phase containing metals in fixed composition, fine metal and metal oxide powders of alloy composition are produced by using a crystallization-stripping method. Versatic Acid 10 and D2EHPA, both acidic extractants, were chosen in this experiment, and the metal oxide powders were produced by using oxalic acid as a crystallization reagent. Mixed metal oxalates containing samarium and cobalt were precipitated from the mixed organic phase containing these metals. Furthermore, the physical properties of the powders, such as particle size, shape and thermal decomposition, were measured in order to evaluate them for industrial purposes."

Jan 1, 2000

By William Petruk

The development of automatic image analysers brought the application of image analysis into process mineralogy because the analysers can measure parameters more easily, quickly and accurately than by manual grain counting techniques, and can also collect data unobtainable by manual grain counting. Data from ore specimens and mill products are used to predict and to define the behaviour of minerals during processing. The analyses are generally performed on the basis of either surface areas or linear intercepts of grains in polished or thin sections, and the data are computer processed to give mineral quantities, liberations, size distributions, and characteristics of middling particles. For analysis, the minerals must be detectable and discriminatable from each other. An image editor is usually used when minerals are not easily discriminated. In addition BSE-8EM photographs have been used where the silicate minerals could not be discriminated from the mounting media. Methods of analysis, typical results, and their applications are discussed.

Jan 1, 1982

By K. Osseo-Asare

It is possible to form a two-phase system in certain polymerlinorganic salt/water mixtures, such as those containing the polymer polyethylene glycol (PEG). Such aqueous biphase systems have many of the separation characteristics of conventional solvent? extraction systems, but are environmentally friendlier. Just like the well-known organic solvent/water two-phase system, the top polymer-rich phase is more hydrophobic. and the bottom salt-rich phase more hydrophilic. The partition of dispersed? particles is dependent on the interfacial interaction between the particles and the conjugate aqueous biphase solutions. In particular, the hydrophilic/hydrophobic properties of the surface determine the transfer of the dispersed particles into either the top (more hydrophilic) phase or the bottom (more hydrophobic) phase. Accordingly, differences in the surface chemistry of particles can be exploited to achieve selective separations. In this work, several approaches to separation control will be discussed. using pyrite (FeS2), alumina (AI203). hematite (Fe203), silica (Si02), and titania (Ti02) as model particulate materials. For metal sulfides, pH and redox potential can be used to alter the hydrophobicity/hydrophilicity of the particles. In ?the case of oxides. polymer adsorption and collector adsorption may be exploited to facilitate particle transfer.

Jan 1, 1999

By M. Urda-Kiel

Stainless steel is increasingly used as a cathode starting sheet. It was shown earlier that even when depositing copper on copper, a substrate-influenced zone appears in the deposit structure, followed by a transition zone and finally by the electrolysis-influenced structure. On copper, the substrate-influenced zone has a thickness of twenty micrometers and on titanium, eventually more than fifty micrometers. Initial nucleation and growth have a considerable influence. In this paper, copper was deposited in a channel cell on four different 304 stainless steel substrates: mechanically polished and anodized, respectively, at 0, +400 and +800 mV/SHE in 1M H2SO4 at 20°C. Copper was deposited under electrowinning conditions after solvent extraction (SX) (40 g/l Cu++, 180 gh/l, H2SO4, 20 or 60°C). The results showed that, although Auger surface analyses of the substrates were only slightly different one from another including the oxide thickness, nucleation and initial stages of growth were very sensitive to the surface treatment of the substrate. Potential step and current step methods gave similar results : progressive nucleation followed by 3D diffusion controlled growth. The highest nucleation frequency was observed on stainless steel anodized at 0 mV/SHE, under various electrolysis conditions. The potential influence of these findings on industrial practice is discussed.

Jan 1, 1999

By KNona C. Liddell

The time and spatial dependence of component and species concentrations during in situ uraninite leaching have been modeled using a reactive transport model based on partial equilibrium between reactive minerals and the solution. The flow field is represented by mixing cells in series. The effects of the H2O2, (NH4)2CO3, and NH4HCO3 component concentrations have been simulated, and results are presented for a one-dimensional flow field.

Jan 1, 1995

By A. V. Tarasov, A. D. Besser

A processing flowsheet has been developed for treating substandard lead-containing polymetallic bulk concentrates and intermediate flotation products containing precious metals, which comprises oxidizing roasting in a calcination kiln and electrothermic smelting generating low volumes of off-gas. The proposed flowsheet also incorporates a dust collection system and sulfur dioxide recovery from off-gas. It is proposed to implement this process by using a reaction smelting technique. For this purpose, the charge to be fed to the smelting furnace after its calcination in a drum-type rotary kiln must have a ratio of sulfide sulfur to sulfate sulfur of at least 1 :2. Electric smelting makes it possible to produce lead bullion that also collects the precious metals contained in the feed, as well as copper-lead matte and slag containing zinc. The recovery of lead into lead bullion and into matte is approximately 83% and 14%, respectively (thus the overall recovery is 97%); the total recovery of gold and silver into lead bullion and matte is 98%; th\lt of copper into matte is 89%; the recovery of zinc into slag is 96%; and that of sulfur into sulfuric acid or gypsum is 90%. After the recovery of zinc from slag, the latter can be utilized in the construction industry.

Jan 1, 2000

By Xiang Li, Merete Tangstad

Currently, the main carbonaceous material for Mn-alloys production is solid carbon, i.e. coke, charcoal and petroleum coke, which is produced with large CO2 emissions. Due to the simple purification, high carbon activity and low CO2 emissions, natural gas has some advantages compared with conventional reducing agents. The aim of the present project is to develop a new technology for production of Mn-alloys using natural gas as a source of carbon. Experimental results indicated that injection of CH4 gas directly into melted slag reduced slightly the MnO and SiO2. However, the metal yield was much less than the theoretical value due to a relative low residence time of CH4 in the slag. The alternative approach was to use carbon black as reductant, produced by CH4 decomposition. The preliminary experimental results showed a high reduction rate using carbon black.

Mar 1, 2017

By Carl A. Kuehn

At Carlin, Nevada, non-indigenous hydrocarbons were introduced as a bitumen phase which was mobilized due to burial under the Roberts Mountains allochthon. similarly, some indigenous organic matter was locally mobilized. Fluid inclusion and paragenetic data of veinlets formed during this hydrocarbon stage, combined with quantitative modelling or organic maturation, indicate that host rocks had evolved past dry gas conditions of around 1550 and l.l+0.2 Kb in the presence of CH4-saturated, highly saline brine by no later than early to middle Cretaceous time. All hydrocarbons present would have been rendered immobile under these catagenic conditions. Crosscutting relationships at several scales suggest that hydrocarbon mobility may have ceased prior to the intrusion of a series of dikes in the mine which have subsequently been altered and mineralized. Apart from subsequent oxidation, the current distribution and high maturity of carbon-rich zones were established prior to gold introduction. No Evidence has been found supporting proposed hydrocarbon "remobilization" during or after gold mineralization and alteration. The high density of the CH4-bearing fluid requires formation at high pressures (near 1 Kb) and precludes their formation as a result of the "cracking-off" of CH4 from organic matter during a thermal event associated with a shallow hydrothermal system. The density and composition of the fluid inclusions restricted to the early hydrocarbon-stages of the Carlin paragenesis are not unique to the sediment-hosted gold deposit environment of north-central Nevada. Similar inclusions are found in authigenic quartz crystals from Paleozoic carbonaceous shales in central Pennsylvania which have experienced normal metagenesis of indigenous organic matter due to deep burial.

Jan 1, 1987

By Liping Gu, Gordon A. Irons

"A 1/3 scale ""thin-slice"" model of an electric arc furnace was developed so that gas could be injected to simulate foaming gas evolution. The influence of arc jets, oxygen lancing and bottom bubbling was also simulated. Liquid velocities were measured by a white light particle image velocimetry system. Numerical simulations of some of these effects were made using commercial CFD packages. Comparisons with measured results show that considerable care is required to select the appropriate model and to interpret the computational results.INTRODUCTIONDuring recent years electric arc furnaces (EAF) have captured a significant share of steel production, partially due to increased productivity through the introduction of advanced technology such as oxygen injection, slag foaming and long-arc operation, process automation and post-combustion. However, systematic analysis of the process and these effects on heat transfer and fluid flow in the furnace is still in its infancy. Most investigationsl1 6l have been restricted to a specific application such as oxygen lancing or bottom stirring. In addition, it is very difficult to make comparisons between these computed results and experimental/industrial results. In this work a 1/3-scale ""thin-slice"" model of Dofasco's 190 ton EAF was built. The fluid flow in the bath due to the arc jets, bottom stirring, oxygen lancing and CO evolution was simulated. The velocity distributions in the bath were measured using Particle Image Velocimetry (PIV) System. In addition, numerical simulations of bottom stirring and CO evolution were carried out using two commercial CFD packages (Fluent and Phoenics). The objective of this work is to validate the mathematical models so that they can be applied to the full-scale furnaces."

Jan 1, 1999

By Fiseha Tesfaye, Pekka Taskinen

"A thermodynamic study of the equilibrium phase assemblage AgBi3S5-Bi2S3-S was made by an EMF-technique, using the RbAg4l5 solid electrolyte. The ternary phase was synthesized from the pure Ag2S and Bi2S3 in an evacuated silica ampoule and grinded into powder and mixed with appropriate compositions of B12S3 and S, in a series of experiments, for pressing in to pellets. The pellets were assembled to form the galvanic cells Pt (-) | Ag ] RbAg4ls | AgBi3S5+ Bi2S3 + S + (C) I Pt (+). The EMF-measurements were made in the temperature range 299 - 460 K.In this paper, thermodynamic functions of the ternary phase AgBi3S5 (pavonite) have been determined. The agreement between the obtained results and the literature values were established.IntroductionThe complex group of ore minerals constitutes from trace amounts to a major proportions of sulfosalts. Although the sulfosalts rarely form massive ore bodies, they are commonly associated with rich sulfide ore minerals for the base and precious metals and widely distributed in a metal poor sulfide minerals [1]. For instance, Ag-bearing sulfosalts are encountered in ore minerals for the production of the base metals and are common sources of silver. Nevertheless, thermodynamic properties of the sulfosalts are poorly known.Reliable thermochemical data are essential for quantitative modeling of the chemical behavior of the sulfosalts in equilibrium with sulfides, which in turn would promote the optimization of complex minerals treatment and extractive metallurgy of the valuable metals."

Jan 1, 2012

By Norihiko Fukatsu

In order to use effectively the previously reported new sensing system for hydrogen and oxygen potentials in molten copper, the criteria of the potentials for getting sound castings have been determined in the laboratory experiment. The copper melt equilibrated with a given hydrogen and an oxygen potential was rapidly quenched in the crucible. The relations between the holding potentials and the gas porosity in the solidified sample were investigated by measuring the density of the sample and microscopic observations. It was found that the defects of the gas porosity became the maximum at the potentials where the dissolved amount of hydrogen and oxygen was in the mole ratio 2:1. The samples having the density more than 99% of the theoretieal value were obtained in the higher oxygen and lower hydrogen potential region or in the lower oxygen and higher hydrogen potential region. The criteria thus determined were examined by comparing with the measured potentials in the practical casting machine. In tough-pitch copper casting, the problem due to gas porosity was found to be serious when the hydrogen potential increased. In the. oxygen-free copper casting, the evolution of hydrogen was found not avoided. The gas porosity in the casting, however, was found eliminated when the oxygen potential was kept at a low value.

Jan 1, 2003

By R. Chiarizia

Third phase formation, i.e., the splitting of the organic phase in two layers, is a common feature observed, under conditions of high loading, for many solvent extraction systems of both analytical and industrial interest. Although this phenomenon has been investigated in a large number of works, a structural and physico-chemical description is still lacking. In this work, small-angle neutron scattering (SANS) data for the tri-n-butylphosphate (TBP)-n-octane,Th(NO3)4-HNO3 solvent extraction system have been interpreted using the Baxter model for hard-spheres with surface adhesion. The increase in scattering intensity in the low Q range, observed when increasing amounts of HNO3 and/or Th(NO3)4 are introduced into the organic phase, has been interpreted as arising from interactions between small reverse micelles containing three TBP molecules plus solutes in their polar core. This intermicellar attraction, under appropriate conditions, leads to third phase formation.

Jan 1, 2003

By L. Lewczuk

A detailed mineralogical and liberation study was performed on the iron ore mill products from the Scully concentrator of Wabush Mines, Newfoundland. Automated image analysis techniques were applied to deter-mine grain size distribution and liberation of all mineral components of the ore. As a result of the study it was indicated that iron recovery can be improved and the Mn minerals reduced in the iron ore concentrate by (a) increasing spiral middlings, (b) regrinding the middlings, and (c) separating the Mn minerals from the iron minerals in the reground middlings.

Jan 1, 1988

By Satu Jyrkönen

A single-particle laminar-flow technique was used to study reactions of sulfidic nickel particles. The studied materials were three natural nickel concentrates and four synthesised nickel mattes. The variables of the experiments were the gas preheating temperature (500 - 1300°C), the composition of the reaction gas (N2 + 0 - 75 vol-% 02) and the ,particle size of the feed. Chemical analysis of the particles was used to determine the oxidation degree of the materials, and optical and scanning electron microscopy were used to detect alteration in their morphology, internal composition and structure. General reactivity of the materials was monitored by the extent of sulfur removal. The reaction mechanism of the studied materials was found to depend primarily on the materials composition as well as oxygen content of the reaction gas.

Jan 1, 1998

By Jinqian Zhao, Jiarong Li, Shizhong Liu

"Creep cavitation of in single crystal (SX) superalloy was investigated. The constant load creep tests, in single crystal superalloys DD6, were conducted at the conditions of 800°C/700MPa, 850°C/550MPa and 900°C/450MPa, respectively. It was found that there were square facets on the stress fracture surface, and microscopic cavities in the ruptured specimens in the vicinity of the fracture surface. Both the square facets on the fracture surface and microscopic cavities in the section of the ruptured specimens show the morphology of the same thing at the different views, namely creep cavities, which are take the form of flatten cuboid. In fact, creep cavities are the longitudinally tensiled creep cracks slowly growing during the stress tensiling. The factors of creep cracks nucleation and growth conditions include: (a) enough high temperature to activate diffusion (b) casting pores as nucleation origination (c) high strains and strain rates. Eventually, the instantaneous fracture mechanism of creep specimen is cleavage fracture.IntroductionFor the materials used in elevated temperature service, creep behavior has to be accounted for. It is well recognized that creep rupture in polycrystalline materials at high temperature occurs principally by the nucleation and growth of microscopic cavities at grain boundaries, followed by microscopic cavities linkage to form micro- and eventually macro-intergranular cracks[l,2]. Without the usual grain boundaries, SX superalloys have superior capabilities at high temperatures to polycrystalline superalloys, and have become an established feature of gas turbine technology where they are commonly employed in the manufacture of high performance blades[3]. A considerable amount of work has been done over the past tens of years, and many models for nucleation and growth of creep cavities have been proposed, however, those are mainly for polycrystalline materials.In order to improve creep resistance that single crystal superalloys, in which grain boundaries are removed, have been developed. Because there don't exist grain boundaries in SX superalloy, the mechanism of nucleation and growth of creep cavities must be different from that in polycrystalline materials.Understanding the formation and characteristics of creep cavitation is crucial to model the lives of single crystal superalloys.M. Marchionni and L.G. Zhao et al. found that there were square facets on the stress fracture surface [4,5]. Roger C. Reed pointed out creep cavities lie in the necked region[6]. In this paper, the effects on the formation of creep cavities are discussed, as well as the morphology of creep cavities and fracture mechanism of SX superalloys."

Jan 1, 2013

By Mustapha A. Raji, Alafara A. Baba, Kuranga I. Ayinla, Misitura Lawal, Abdul G. F. Alabi, Aishat Y. Abdulkareem, Rafiu B. Bale, Folahan A. Adekola, Muhammed O. Muhammed

Increasing demands for pure wolframite ore in the form of ammonium paratungstate (APT), tungsten oxide cannot be over emphasized. Thus, treatment of a Nigerian wolframite ore containing admixtures of scheelite (CaWO4: 96-900-9631) and stolzite (PbWO4: 96-900-9813) by hydrometallurgical route was investigated in hydrochloric acid chelated with phosphoric acid to extract tungsten via solvent extraction. During leaching, parameters such as leachant concentration, chelate dosage and reaction temperature on ore dissolution were examined. At optimal conditions (1.5 mol/L HCl + 2.0 mol/L H3PO4 solution; 75 °C), 95.0% of the initial 10 g/L ore reacted within 120 min. The derived activation energy of 56.80 kJ/mol supported the proposed dissolution mechanism. The unreacted product analyzed by XRD was found to contain siliceous impurities. Tungsten recovery from leachate was carried out by solvent extraction with Aliquat 336 in kerosene. Pure tungsten was recovered as APT and beneficiated to produce high grade industrial tungsten oxide of industrial values.

Mar 1, 2018