By Fathi Habashi

Nitric Acid has been used for over 50 years in the uranium industry and in phosphate fertilizer manufacture. Its application in the treatment of sulfide concentrates is relatively recent. A review of recent developments is given.

Jan 1, 1999

By Asmo Vartiainen

The viscosity of liquid Fe-O-SiO2 -slag at copper smelting conditions was investigated using a rotational viscometer. The studied parameters were oxygen partial pressure (10" °-10"6 bar ); composition of slag (Fe/SiO2 ratio), and temperature (1250-1400°C). The viscosity values are presented as a function of Fe/SiO2 ratio and as isoviscosity curves in ternary FeO-Fe2O3-SiO2 diagrams. The increase in viscosity at high silica contents can be accounted for the polymerisation effect of SiO4/4- -anions. At high ferric iron contents, higher oxygen partial pressure, the viscosity values increase especially near the magnetite saturation. The viscosity values are highest at the double saturation of silica and magnetite. At lower silica and ferric iron contents the viscosity values are more uniform in the homogenous liquid slag area. The viscosity values were lowest at high temperatures and highest at low temperatures.

Jan 1, 1998

By Bora Derin

The partial pressure ratios of sulfur and oxygen for several copper flash smelting plants were derived using the Reddy-Blander (RB) model and predicted dissolved sulfur contents available in the literature. The sulfide capacities (Cs) of six different flash smelting plants (FeO-CuO0.5- CaO-MgO-FeOwAIOl.s?SiO2) slags were calculated. The log (Po2/PS2) versus matte grades of various industrial processes was determined. The PoiPS2 ratio increased with an increase of copper grade. The calculated partial pressure ratios for the copper flash smelting are in good agreement with those of the experimental data.

Jan 1, 2003

By Zhi-biao Yin

Copper smelter flue dusts often cannot be directly recycled to the smelting process and accumulate as hazardous wastes requiring environmentally acceptable disposal. Because of the limited amount of flue dust, a separate copper extraction process must be simple and require-a small plant investment. A flue dust process has been developed, consisting of the following steps: (1) roasting a pelletized mixture of hydrated lime and flue dust to fix arsenic and sulfur as insoluble calcium salts, (2) heap leaching the roasted pellets with a buffered ammonia/ammonium salt solution to extract copper as an ammine complex in a lined cell that is the final repository of the leached pellets, and (3) boiling ammonia from the lixiviant to precipitate copper. Condensed ammonia and the filtered solution are returned to leaching. Heap leaching in the final repository cell lowers the capital investment significantly compared with competing extraction processes. Chemistry with respect to arsenic, sulfur and copper is discussed.

Jan 1, 1992

By Ali S. Al-Watban

"In this paper, the room temperature friction and deformation properties of various polycrystalline diamonds; i.e. aggregates of diamond crystals with a ""binder"" phase of cobalt and a polycrystalline coating produced by a chemical vapour deposition processes (CVD) were studied when softer metallic and ceramic sliders were used. The experiments were conducted· at relatively low sliding speeds (10 mm/min), in a vacuum of 10-5 mbr after having cleaned the specimen surfaces by out-gassing them for about 30 min at 800 °C. As a result of increasing the number of traversals significant wear of the coated diamond by softer metallic sliders (aluminium and mild steel) was observed. With ceramic sliders, it is shown that the multiple traversals result in the formation of wear groove. With diamond silicon carbide, high friction and adhesion lead to significant metal transfer which then pre-empts cumulative deformation of the harder materials. With the diamond-cobalt composite, the friction is surprisingly low, there accumulation of wear debris on the tip of the slider but no permanent transfer of metal and the harder specimen is not damaged even after 5000 traversal.IntroductionPolycrystalline diamond is mainly produced as tool materials for the machining of hard metals and composites. Thus, the sliding friction and wear resistance are amongst the most important properties relevant to those applications.During cutting by PCD the wear mechanism is mostly influenced by the chemical affinity between the tool material and the workpiece. For example, diamond based materials are not recommended for machining ferrous materials because carbon is highly solubie in iron: This leads to the graphitisation of diamond particles and hence a high rate of diffusion wear is observed (Brookes and Lambert, 1982)."

Jan 1, 2000

By P. Peczak

A Monte Carlo simulation technique has been used to study dynamic recrystallization in polycrystals. A continuum microstructure of the polycrystal is modeled employing a discrete lattice. The response of the material to hot deformation is simulated by adding stored energy and recrystallization nuclei continuously with time. The experimentally observed nonuniform character of deformation substructures is modeled by employing a phenomenological expression for inhomogeneous distribution of the stored energy. All simulations were performed on HP-Apollo 9000 Series 700 workstations. A program written in FORTRAN with use of PHIGS graphics library calls was used to interactively monitor the current state of the matrix and all relevant parameters: deformation stress, average grain size and effective nucleation rate. Visual analysis of the simulated microstructure allows a better understanding of the data developed by averaging over a number of very long Monte Carlo runs. Since the essential features of dynamic recrystallization are accurately reproduced by the model, it is used to discuss the role of the controlling mechanisms of the dynamic recrystallization in real polycrystal.

Jan 1, 1993

By T. T. Chen, J. E. Dutrizac

Noranda Inc., CEZinc presently employs a cement-stabilization (jarofix) process to stabilize its jarosite residues for direct disposal. In this process, Portland cement partly decomposes Na-jarosite to form Ca6Fe2(SC>4)3(OH)i2.nH20, ferric hydroxide and sodium sulphate which further reacts to form gypsum; approximately one-third of the Na-jarosite reacts in the current commercial product. The cured jarofix products also contain minor amounts of various Ca-Al-Fe silicate-sulphate-hydrate phases and traces of calcite. Together with gypsum and a Ca-Fe sulphate phase, these species bond the various particles together, imparting mechanical strength and reducing the permeability. Water-soluble Zn and Mg are stabilized in the Ca-Al-Fe silicate-sulphate-hydrate phases. The freshly cured products usually contain small amounts of moisture and traces of residual Portland cement, which provides additional alkalinity for the neutralization of any residual acid species. Jarofix products stored for more than six years in the laboratory, after curing, are usually dry and exhibit the same micro-textures as those of the freshly cured products. However, the stored products are depleted in the Ca6Fe2(S04)3(OH)i2.nH20 and Portland cement phases, and are enriched in gypsum and calcite which reflects the highly alkaline environment of the jarofix products. The aged products also have increased amounts of the Ca-Al-Fe silicate-sulphate-hydrate phases which have elevated Zn and Mg contents. This implies a further immobilization of residual water-soluble Zn and Mg during stora

Jan 1, 2000

By Antonio de Ita, Isaias Hilerio, Miguel Barron

"The influence of an unconventional lance with a central nozzle on the multiphase fluid flow in a steelmaking converter is studied in this work by means of computer simulations. The lance has four peripheral supersonic nozzles and a vertical central nozzle. Besides, the oxygen flow in the central nozzle is considered independent from the main oxygen supply. Transient two-dimensional numerical simulations were carried out considering just molten steel and gaseous oxygen as the existing phases. Numerical results show that bath agitation and droplet generation are enhanced as a result of the central nozzle. However, the performance of this lance strongly depends on the distance of the lance tip to the molten steel surface and the velocity of the oxygen jet.IntroductionCurrently, two thirds of the world crude steel is produced through the steelmaking oxygen converter [1]. Given the unquestionable economic importance of this technology, any improvement or optimization proposal is welcome. In the majority of current oxygen converters a top oxygen supersonic jet is blown onto the molten steel through a water-cooled lance to eliminate by oxidation some impurities such as carbon and phosphorus. Conventional lances have inclined peripheral nozzles whose number depends on the converter capacity. During the process, a large amount of gases evolves, forming metal droplets and a metal-slag-gas emulsion [2]. The droplets and the resultant emulsion increase the reaction interfacial area, promoting in this way carbon removal and dephosphorization of the molten steel bath [3]. However, during the blowing stage, the emulsion rises towards the lance and converter mouth and frequently forms layers which accumulate in the lance, reducing the life of the lance tip [4, 5]. It is possible that some freezing of the molten metal occurs due to the low oxygen injection temperature, however there are no reports on this. Besides, frequently undesirable operating phenomena such as spitting and slopping may arise as a result of inappropriate blowing practices or bad lance design. In the oxygen steelmaking industry, novel lances design are needed in order to enhance the decaburization rate and the slag formation and, at the same time, preventing operating practices that decrease productivity and move away the shop from safety standards."

Jan 1, 2012

By Bo Björkman

A controlled dust generation whereby the dust generated would be enriched with specific metals would considerably facilitate the possibilities of recovering metals from such dusts. A basic understanding of the dust forming mechanisms is of fundamental importance to achieve a controlled dust generation. The present study deals with dust formation in a copper converting process. Dust samples collected from various places in the gas cleaning system were characterised for chemical and mineralogical composition using chemical analysis as well as microprobe analysis. Thermodynamic calculations were used to predict the formation of chemically formed dust at various temperatures and amounts of leakage air to the gas system. The results show that a separation of mechanically formed dust. e.g . Si0:2. Cu and chemically formed dust. e.g .? Ph, Zn, As, Bi. could, to some extent, be obtained due to their different particle sizes. A selective condensation of Pb, Zn and As at various temperatures could. according to thermodynamic calculations, he possible at high temperature. A selective condensation of metals requires an airtight gas cleaning system or a gas cleaning system with a limited amount of leakage air in order to maintain the desired temperature level.

Jan 1, 1996

By Ray D. Peterson

The hydrothermal enrichment of chalcopyrite by CuSO, occurs in the absence of oxidizing or reducing reagants. Kinetics of the enrichment process were determined under autoclave conditions in the temperature range of 398°K (125°C) to 473°K (200°C). Covellite (CuS) formed first, followed by digenite (Cu,,,S), with rejection of iron to the solution. The kinetics have been explained by a model which includes diffusion during the first stage formation of covellite followed by surface reaction rate control when digenite be. The effects of particle size, temperature, pH, and cupric and ferrous ion concentrations on the leaching kinetics were examined. Additions of ferrous ion to solution markedly increased the rate of reaction.

Jan 1, 1994

By Marcelo B. Mourao

Interactions of carbonaceous materials with liquid Fe-C melts have been investigated experimentally by determining the volatile yield due to rapid devolatilization (Flash Pyrolysis) and rates of dissolution at temperatures ranging from 1623 to 1873 K. The volatile yield increased with increasing the temperature. The comparison of results of different types of carbonaceous materials was possible by expressing the volatile yield in terms of Enhancement Factor, fE. The rates of dissolution of spectroscopic graphite and an industrial coke seemed to obey the correlation for natural convection under turbulent conditions. The experimental data for the graphite suggested that the rate of dissolution was controlled by the mass-transfer in the liquid boundary layer adjacent to the solid sample. The value for the empirical parameter correlating the dissolution coefficient and the operating variables was found to be 0.19 which was close to that reported in the literature. The comparison of the results obtained for the coke samples with those for the graphite revealed that the impurities and the porosity of the samples can effect the dissolution rates.

Jan 1, 1992

By J. Szekely, S. Rhee

"A mathematical formulation has been presented to describe heat and fluid flow phenomena in CVD operations. In the statement of the problem, which included consideration of plasma enhanced CVD systems, emphasis was placed on identifying the parameters which play a key role in determining the rate and the spatial uniformity of the deposition process. This was done both through the appropriate dimensionless groups and by presenting an extensive set of computed results. The main conclusions that may be drawn from this work are that the deposition rate will be inherently non-uniform for atmospheric CVD systems; this may be somewhat ameliorated by inclining the susceptor or changing the vessel contours. Operation at greatly redeced pressures and for PECVD systems will give a much more spatially uniform deposition rate.1. INTRODUCTIONIn recent years, there has been a growing interest in chemical vapor deposition techniques for the preparation of thin films for semiconductor, photovoltaic applications and for coatings in general, as evidenced by numerous journal articles and symposium proceedings devoted to this topic (1-6). An interesting variant of this technique is to perform the deposition in a plasma or glow discharge at low pressures because this technology obviates the need for the thermal decomposition of the precursor at the substrate surface and permits operation at greatly reduced temperatures (7-10).By far, the largest portion of the reported work dealing with both these aspects of the technology has been concerned with the characterization of the deposit, quite properly so. However, in more recent times it has been realized that the transport aspects of these processes are also deserving of attention because the understanding of heat flow, fluid flow and diffusional phenomena may provide the key to the solution of problems associated with obtaining uniform deposits and the proper scaling of laboratory measurements in order to design industrial CVD systems."

Jan 1, 1986

By Jana Dobrovska

Solidification and cooling of a continuously cast slab and simultaneous heating of a mould is a very complicated problem of transient heat and mass transfer. Nowadays, the solving of such a problem is impossible without numerical models of the temperature field not only of the slab itself, while it is being processed through the whole concasting machine (Caster), but of the mould as well. Two original numerical models have been developed and used in the investigation of a continuously cast steel slab. The first (one of two) 3D model of the temperature field of a concasting is capable of simulating the temperature field of a caster. Experimental research and data acquisition have to be conducted simultaneously with the numerical computation-not only to confront it with the actual numerical model, but also to make it more accurate throughout the process. After computation, it is possible to obtain the temperatures al each node of the network, and at each time of the process. The utilization of the numerical model of solidification and cooling of a concasting plays an indispensable role in practice. The potential change of technology-on the basis of computation-is constantly guided by the effort to optimize, i.e. to maximize the quality of the process. The user can therefore choose any appropriate longitudinal or cross-section of a slab and display or print the temperature field in a 3D or 20 graph whenever necessary. The second numerical model of dendritic segregation of elements assesses critical points of slabs from the viewpoint of their increased susceptibility to crack and fissure. In order to apply this model, it is necessary to analyze the heterogeneity of samples of the constituent elements (Mn, Si and others) and impurities (P, S and others) in characteristic places of the solidifying slab. The numerical model, based on measurement results obtained by an electron micro-probe, generates distribution curves showing the dendritic segregation of the analyzed element, together with the distribution coefficients of the elements between the liquid and solid states. The combination of both models enables the prediction of cracks and fissures in critical points of the continuously cast carbon-steel slab. Both models had been applied in the industrial investigation of a cast low-carbon-steel slab.

Jan 1, 2003

By Jan Dabrovska

Solidification and cooling of a continuously cast slab and simultaneous heating of a mould is a very complicated problem of transient heat and mass transfer. Nowadays, the solving of such a problem is impossible without numerical models of the temperature field not only of the slab itself, while it is being processed through the whole concasting machine (Caster), but of the mould as well. Two original numerical models have been developed and used in the investigation of a continuously cast steel slab. The first (one of two) 3D model of the temperature field of a concasting is capable of simulating the temperature field of a caster. Experimental research and data acquisition have to be conducted simultaneously with the numerical computation-not only to confront it with the actual numerical model, but also to make it more accurate throughout the process. After computation, it is possible to obtain the temperatures at each node of the network, and at each time of the process. The utilization of the numerical model of solidification and cooling of a concasting plays an indispensable role in practice. The potential change of technology-on the basis of computation-is constantly guided by the effort to optimize, i.e. to maximize the quality of the process. The user can therefore choose any appropriate longitudinal or cross-section of a slab and display or print the temperature field in a 3D or 2D graph whenever necessary. The second numerical model of dendritic segregation of elements assesses critical points of slabs from the viewpoint of their increased susceptibility to crack and fissure. In order to apply this model, it is necessary to analyze the heterogeneity of samples of the constituent elements (Mu, Si and others) and impurities (P, S and others) in characteristic places of the solidifying slab. The numerical model, based on measurement results obtained by an electron micro-probe, generates distribution curves showing the dendritic segregation of the analyzed element, together with the distribution coefficients of the elements between the liquid and solid states. The combination of both models enables the prediction of cracks and fissures in critical points of the continuously cast carbon-steel slab. Both models had been applied in the industrial investigation of a cast low-carbon-steel slab.

Jan 1, 2003

By W. R. McDonald

The U.S. Bureau of Mines investigated treatment of gold and silver refractory ores and concentrates that respond poorly to conventional cyanidation techniques due to the complex mineralogy of the ore. Three types of ores were investigated: gold locked placer sands, gold locked in sulfides, and gold that is robbed from the pregnant cyanide solutions by minerals in the ore. Ore treatment included grinding, flotation, cyanidation, air oxidation, pressure oxidation, hypochlorite oxidation, roasting, and carbon in leach.

Jan 1, 1991

By J. Fraser Forbes

"The meaning of the term ""process control"" has evolved significantly since its widespread use began in the manufacturing industries in the 1940s. Further, the scope of process control applications has drastically increased both in terms of the breadth of industries using process automation technologies and the vertical integration of these technologies within a single industry. This evolution and integration of process control technologies within the manufacturing industries has proceeded to such an extent that process automation is an integral part of modern business practices.This paper will examine the current status of process control technology from simple process regulation through process performance optimization to business planning. Each layer of the operations automation hierarchy will be discussed both in. terms of the current state-of-the-art and the directions in which these technologies are evolving. The key tools and tasks necessary for success at every level of the automation hierarchy will be introduced. Finally, the critical challenges that must be faced in accomplishing the goal of complete Computer Integrated Manufacturing (CIM) will be described.Finally, although this paper addresses issues of practical importance to any manufacturing company, the discussions will be framed in terms of the particular challenges facing and the opportunities available within the materials manufacturing industries."

Jan 1, 2000

By I. A. Ibrahim, A. K. Ismail, A. A. I. Afifi

"Synthetic rutile for paints industry is conventionally produced by a combined smelting and leaching process. Smelting process is an energy intensive step and represents economic burden in view of the increasing energy costs. Egyptian ilmenite ore containing 40% TiO2 and 38% total Fe was thus directly leached with sulphuric acid to produce eventually synthetic rutile. The process-involves digestion of the ore with sulphuric acid whereby both TiO2 and Fe are dissolved. The solution was then treated with iron powder to convert Fe3+ to Fe2+ to avoid co-precipitation of iron during the hydrolysis step. After solid/liquid separation and clarification, Fe was crystallized as ferrous sulphate hydrate by chilling. The titanium pregnant liquor was concentrated by evaporation and then hydrolyzed to precipitate hydrated titanium dioxide which was then calcined to produce synthetic rutile containing 98.6 TiO2 and 0.58% Fe2O 3. The optimum conditions of all the processing stages were determined.IntroductionSynthetic rutile for paints, welding rods and other industries could be produced from ilmenite ore by sulfuric acid leaching process. This process is a batch process and nearly 80% of all TiO2 produced in the world is made by this process [1]. Figure l shows simple block flowsheet of the process. The process involves the following stages.Digestion: In this stage, ilmenite ore is treated with concentrated sulfuric acid where both iron and titanium are converted to their respective sulfates according to the following equations:"

Jan 1, 2000

By Gopalakrishna M. Rao

"Several industrial and government laboratories are of the opinion that solar--cell technology will grow into a billion-dollar industry by the year 2000, especially if oil prices rise again. Of the variety of materials that have been investigated as the major component of photovoltaic systems, silicon appears to have an outstanding advantage. The cost factor is the primary importance in photovoltaic development, since the technology to make silicon cells of acceptable efficiency and life time has existed since the early stage of the space program. Electrometallurgy is one of the low--cost processes for the production of silicon, since it allows direct, single-stage production from some abundant, inexpensive source materials such as silica and fluorosilicates. Among several systems, two are given particular attention, using inorganic baths with Si0 2 or K2SiF6 as the source of silicon respectively. They appear capable of development to commercial production. Conceptual designs of a commercial--scale cell for silicon production at temperatures above its melting point, and of a pilot' plant for plating silicon from an all-fluoride bath are presented. Energy ProspectsThe major changes in the world energy since the first energy crisis in 1970 have impacted on our community. When oil was $40 a barrel in the mid-1970s, we became obsessed with the energy conservation and a search for alternate energies. Even though the crude oil fell below $15 a barrel during the last several years, our energy security fears continue to haunt us. This time it is not the scarcity, but the abundance of foreign oil and the decline in the domestic production.The prospects of energy depends on the demand and supply of energy. These, in turn, depend on future energy prices, which are linked to economic factors, political events, and unforeseen circumstances. Although no one can predict the future with certainty, three energy consumption patterns used by the Ford Foundation are as shown in Fig. 1."

Jan 1, 1988

By R. Cavanagh

Studies relating to the fixation of sulfur by reaction of 4 to 8 mm diameter cylinders of calcined limestone or dolomite with high strength sulfur dioxide in the temperature range 880°C to 1020°C were undertaken. Dolomites are far superior in sulfate capacity and reactivity than dense limestones even at high strength SO2. The sulfation reaction was first order with respect to SO2 concentration below 100 percent. Zero reaction rate at 100 percent SO2 concentration indicates that sulfate was the exclusive reaction product and that sulfite had no role in the reaction. At relatively low SO2 concentrations gaseous diffusion through the reaction product layer has a marked effect on the rate. As SO2 concentrations were increased up to 100 percent more complex rate controlling mechanisms unfold. By sectioning partially reacted dolomitic limestone pellets a moving interface was observed. Reaction ceased because of pore plugging for dense non-porous limestones at 30% conversion. With dolomitic material virtually complete sulfation of the calcium was observed. S.E.M. analysis showed that the average atom ratio Ca:S was 1.01, thus supporting the argument that little if any of the magnesium was sulfated.

Jan 1, 1996

By Y. Huang, P. B. Prangnell

"An Al-0.1Mg alloy was firstly deformed at room temperature by ECAE to a true strain of 10, where a steady state deformation was established and further processing had little effect on grain refinement. The ECAE samples, with an average grain size of ~0.55µm, were then compressed in a channel die at 77K- 473K to various reductions. Microstructures were characterized by electron backscatter imaging and EBSD in a FEGSEM. Grain refinement to the ECAE submicron structure occurred during deformation at cryogenic temperatures of 77 – 213K, whereas coarsening took place during deformation at elevated temperatures. A steady state deformation was observed at all temperatures where a constant grain structure was developed and maintained upon further straining due to dynamic recovery. The mechanisms of dynamic recovery during steady state deformation at cryogenic temperatures are discussed.IntroductionSevere deformation processing (SDP) has been successfully used to produce submicron grain structures, and in some cases nano-scale crystallite sizes, in a wide range of alloys. However, the rate of grain refinement becomes increasingly inefficient at high strains as a steady state grain structure is approached [1-3]. Steady-state grain sizes have also been reported in other ultra-high strain deformation processes, like cryogenic ball-milling [4]. There is thus a minimum grain size achievable in a material by a given SPD process under constant deformation conditions.It is well documented that a steady state subgrain size is observed in warm deformation of metals due to dynamic recovery (e.g. [5]). In severely deformed alloys a constant grain size at ultra-high strains has similarly been attributed to dynamic recovery [1-3]. Mechanisms have been proposed, for rapid deformation induced grain growth including stress driven boundary migration and breakaway from solute pinning [2]. However, as pointed out by Humphreys et al. [2] the restoration processes are currently poorly understood, particularly at low temperatures, where the boundary migration rates required to maintain a constant grain size are orders of magnitude higher than can be satisfactory explained from diffusion controlled migration. Similar to the subgrain size, the steady state grain size obtained during SDP is generally related to the temperature compensated strain rate [2, 6]. Thermally activated restoration processes are thus expected to be suppressed by lowering the deformation temperature and a smaller steady state grain size can be achieved."

Jan 1, 2012