By Zhao-Qun Ke, Wen-Feng Tan, Jiang Diao, Yu-Hao Liu, Bing Xie, Zhang Tao, Wang Zhou, Hong-Yi Li

An effective way to decrease the dephosphorization burden in the current vanadium extraction-steelmaking process is slagging with CaO in vanadium extraction step. The phase composition of vanadium slag with different basicity and the regularities distribution of elements have been investigated by X-ray diffraction analysis and scanning electron microscopy combining with energy disperse X-ray spectrometry, respectively. The results indicate that V mainly concentrates in the spinel phases; Ca and P are rich in the silicate phases. Fe2SiO4 transform to CaFeSiO4, while the basicity of vanadium slag is 1.3. With further increase of basicity, 2CaOSiO2 could form in the silicate phases. Moreover, the phosphorus-containing phase will transform from Ca3(PO4)2 to Ca3(PO4)2-nCa2SiO4. With the increase of P2O5 content, the crystallization rate of spinels decrease obviously. Furthermore, the peak temperature for crystallization of spinels decrease 5 K with the P2O5 content increasing 1 wt%.

Mar 1, 2017

By A. V. Tarasov

A flow-sheet for waste-less processing of spent lead batteries comprises mechanized separation of batteries, smelting of the metallic fraction in a kettle, electrothermal smelting of oxysulfate fraction, refining of crude lead and processing of reverts to produce commercial products. Smelting of lead-containing fraction is performed in an electrothermal furnace using a processing technology developed in the Gintsvetmet Institute and differing from conventional processes by the fact that it does not require any fluxing agent (soda); no matte is formed in the process and the amount of slag produced is minimal, because its formation depends only on the ash content of coke and the quality of battery scrap separation. The process has been patented. It has been introduced on a commercial scale in 1.8 MVA furnaces at the plant of A0 "RyazTsvetmet" (Ryazan, Russia). The process has the following main advantages as compared with conventional shaft-furnace smelting and smelting in a short-drum furnace: the process does not require technical-grade oxygen, the amount of process gas generated is minimized ensuring a decrease in lead-containing dust and sulfur dioxide emissions by 3 to 5 times per unit of lead recovered; a decrease in dust entrainment resulting in lower amounts of recycled dust; lower slag yield (a decrease from 20-25% to 3-5%); lower coke requirement (a decrease from 10-14% to 3-4%). Refining of crude lead is performed using conventional technology but there are several unique features for which know-how is available. Processing of by-products of electrothermal smelting and secondary lead refining (slag, drosses, skimmings) and ebonite fraction (crushed battery casings) is performed in a slag-fuming furnace.

Jan 1, 2002

By Min Chen, Lei Xu, Liang-yu Jin, Xue-liang Yin

For the purpose to reduce the high cost and heat storage loss of Al2O3-MgO bricks used as ladle linings, Al2O3-MgO-CaO bricks with lower theoretical density were fabricated and the densification behavior as well as mechanical property of this refractory was investigated. With addition of CaO, the initial sintering temperature of Al2O3-MgO refractory was decreased from 1300 to 1100°C associated with the expansive formation of CA2, and the compressive strength was also enhanced owing to the formation of bond linkage between CA6 and spinel. At high temperature, brick with 4% CaO content showed poor sinterability with high porosity because of the formation of platelet structure of CA6 grains, whereas brick with 8% CaO content was well sintered with higher relative density but lower bulk density than Al2O3-MgO brick, indicating that the densification as well as lightweight of Al2O3-MgO refractory was effectively promoted.

Jan 1, 2015

By F. Robert Hubbard

IMCO Recycling Inc. has developed a new, patented technology for the production of fertilizer, K-SOIL?, as a by-product of its aluminum recycling operations. This new technology can substitute for conventional technology which now results in a saltcake residue that is placed in 'landfills. Four years of research and development work by IMCO culminated in a U. S. patent issued April 5, 1994. As part of the technology development effort, IMCO engaged the services of a nationally renowned research organization and a prominent university. These two organizations have conducted in-depth agronomy studies In the laboratory, greenhouse, and the field. Results have shown K-SOIL? to be performance equivalent, on a nutrient content basis, to conventional potash fertilizer. The first field applications on commercial farms were made in the spring of 1994. K-SOIL? is a potassium-bearIng, granular solid which may find use in fertilizer blends, direct application, and other forms of fertilizer products. The overall benefit of this new technology is to create a useful by-product rather than generate a useless residue and, thereby, reduce or eliminate the amount of salt cake now placed in landfills. As such, It is a significant, step toward IMCO's ultimate goal of complete recycle.

Jan 1, 1995

By Yoichi Takeda

The CaO-FeO,-Cu20 slag has been practically applied to continuous converting of copper, and also has potential for refining of copper. Liquidus lines of the slag system and phase stability diagram for the liquid slag and the existing solid compounds under copper saturation are presented. Liquidus composition was determined by chemical analysis of slag sample saturated primary solid. The temperatures of invariant equilibria were investigated by thermal analyses. Oxygen potentials on the liquidus lines, the univariant and invariant equilibria were estimated from the relation slag composition and oxygen potential that relation was confirmed in separate experiments.

Jan 1, 2003

By H. Hahn, B. H. Kear, K. Kan, S. C. Danforth, G. Skandan, W. Chang

"A new chemical synthetic process for the production of non-agglomeratednano structured ceramic (n-ceramic) powders, starting from metalorganic precursors, is described. The process combines rapid thermal decomposition of a precursor/carrier gas stream in a hot tubular reactor with rapid condensation of the product particle species on a cold substrate. Critical to the success of this Chemical Vapor Condensation (CVC) process are (1) a low concentration of precursor compound in the carrier gas, (2) rapid expansion of the gas stream through an uniformly heated tubular reactor under a reduced inert gas pressure of 1-35 mbar, and (3) rapid quenching of the gas phase nucleated clusters or nanoparticles as they exit from the reactor tube. A wide variety of metal organic precursors is available commercially, all of which can be utilized in the CVC process to produce n-ceramic powders, including single phase, multiphase and multicomponent systems.The CVC process has been used to synthesize non-agglomerated n-SiCxNy and n-ZrOxCy powders, with controlled particle size in the range 2-20 nm. Heat treatment of the assynthesized n-powders in various high purity gas streams causes compositional and structural modifications, including particle purification and crystallization, as well as transformation to a whisker-like morphology. Thus, as-synthesized amorphous n-SiCxNy particles transform to (1) cubic n-SiC particles, when heated in flowing argon at temperatures> 1350 °C, (2) hexagonal n-Si3N4 whiskers, when heated in flowing NH3IH2 at 1400 °C, and (3) cubic nSiC whiskers, when heated in flowing H2 at 1400 °C.Non-agglomerated n-ceramic powders form uniformly dense powder compacts by cold pressing, which can be sintered to theoretical density at temperatures as low as 0.5 Tm' For example, full densification ofn-Zr02 powder compacts under free sintering conditions can be achieved at 1125 °C."

Jan 1, 1994

By Renaud Metz

The DOPA process (Direct Oxidation of a Precursor Alloy) was used to prepare ceramic powders based on doped SnO2 and ZnO. The DOPA process consists essentially in the direct oxidation of a homogeneous precursor alloy. A unique advantage of this process is its rather benign environmental impact since no dangerous reactants are used and no harmful by-products are generated. Only oxygen and the alloy metals participate on the chemical reaction to produce the multi-component oxide. Homogeneous alloys of niobium, cobalt and chromium doped tin have been prepared. The molten metal alloy is atomised in air using a double fluid nozzle to produce metallic powders. A subsequent thermal treatment is carried out to fully oxidise the sprayed metal alloy powders. These raw powders are used to prepare a ceramic powder through a mill homogenisation and atomisation process. The ceramic powder is then uniaxially compacted in disc shape and sintered in an oxidising atmosphere. The resulting sintered bodies are metallised on their flat faces and the cylindrical surface is passivated using lead free glass enamel. These ceramics present excellent semiconducting properties with non-linear (non-ohmic) characteristics. The DOPA process is found to be an attractive procedure to obtain ceramic powders for the preparation of SnO2 varistors.

Jan 1, 2006

By Johne Jesus Mol Peixoto, Ciro Azevedo Silva, Itavahn Alves da Silva, Weslei Viana Gabriel, Leticia Queiroz Ribeiro, Carlos Antonio da Silva, Varadarajan Seshadri

In this study,the influence of the immersion depth, casting speed on the flow characteristics in a beam blank mold with two tubular nozzles have been investigated using a physical model as well as CFD simulations.The results of CFD simulations were found to be consistent with the results of experiments in the physical model.The liquid jet spreads faster the flange region compared to the web region. This can lead to a non-uniform shell thickness along the cross section resulting in uneven solidification of the skin. The jet penetration depth ranged between 66 and 77 cm. The average intensity of meniscus fluctuation was 0.22 mm, and the maximum fluctuation was found to be 0.85 mm. Based on these results, the suggested optimum operating parameters for immersion depth and casting speed were 75 mm and maximum casting speed of 1 m/min.

Mar 1, 2017

By Makoto Ohlsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SME). The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force. The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films. The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a Ni50Mn25Ga25 or Ni52Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace. The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains. After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature. The martensitic transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated. After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found. The constraint-aged films also showed the two-way 3ME by thermal cycling.

Jan 1, 2003

By Makoto Ohtsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SMB), The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force, The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films, The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a NisoMn2sGa25 or Nis2Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace, The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains, After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature, The martcnsitie transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated, After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found, The constraint-aged films also showed the two-way 5MB by thermal cycling,

Jan 1, 2003

By Richard S. Dennis

Acid recovery employs ion exchange (I-X) resin as separation media for inorganic acids from dissolved metallic salts by physical adsorption and without the use of chemicals. This technology has been used for years on spent etching and plating liquors to recover acid for reuse in the bath and to reduce waste acid neutralization costs. It is also used for electrolyte treatment to facilitate valuable metal recovery via acidity reduction. TETRA's ccrxr'" I-X contactor has been used successfully for acid separation from its metallic salt counterpart in a simple, continuous operating mode using strong base anion resins. Efficient separation is enhanced by acid reconcentration to nearly its original strength or as high as 14-20%. Continuous treatment also recovers heat to the tankhouse or bath and improves metal quality due to consistent acid quality. Conventional fixed bed ion exchange (I-X) systems are impractical for acid recovery because of complex control design and large resin inventories needed to process very low liquid-to-resin treatment ratios associated with strong acid concentrations.

Jan 1, 1996

By G. Belardi

A study has been conducted to assess a new wet beneficiation treatment for the recovery of the sulphuric-acid-soluble titanium oxide contained in the waste from an Italian TiO2-pigment facility. The waste is produced during treatment of a Ti-enriched slag and contains as main components TiO2 (54%, of which 42% acid-soluble and 12% insoluble), SiO2 (27%) and A1203 (6%). Eighty percent of the material is finer than 50pm. The first step was to ascertain the possibilities offered by size classification, wet gravity separation, froth flotation and wet high-intensity magnetic separation to improve the grade and recovery of Ti02 and reduce the SiO2 content. The next step was to optimize the operating conditions of the various separations and assemble them into a complete flow- sheet. Beneficiation ensures potentially 70% recovery of the TiO2 with a concentrate grade of 80%.

Jan 1, 1998

By Fuming Wang, Xi Chen, Shuai Liu, Changrong Li, Dan Wu, Yaxu Zheng

The effects of B content and austenitizing temperature on hardenability and toughness of Cr–Mo alloy steel have been studied. The results show that the hardenability is deteriorated with increasing B content and austenitizing temperature. With increasing temperature, more and more B containing particles were dissolved in austenite and increase the amount of B atoms segregating at grain boundaries. Moreover, the coarsening grains reduce area of grain boundaries and also increase the amount of B atoms at unit grain boundary, excessive B atoms segregating at grain boundaries promotes precipitation of M2B, which accelerates ferrite nucleation and reduces hardenability. The main elements in M2B phase are Fe, Cr, Mo and B. The B atoms segregating at grain boundaries during austenitizing promote precipitation of M2B during tempering which deteriorate toughness significantly.

Mar 1, 2018

By Hong Yong Sohn, Miguel Olivas-Martinez, Zhixue Yuan

A novel flash ironmaking process that directly reduces iron oxide concentrate particles by gas is under development. The goal of this work was to study the possibility of reoxidation of iron particles in various gas mixtures. As the product iron cools down in the lower part of the flash reactor, conditions may become favorable for reoxidation because of equilibrium and high reactivity of iron particles. The effects of temperature (823 – 973 K) and H2O partial pressure (40 – 100 pct., Ptotal = 86.1 kPa) on the reoxidation rate were examined. The pressure dependence was first order with respect to water vapor, and the activation energy was 146 kJ/mol. A complete rate equation that adequately represents the experimental data was developed. For oxidation in O2-N2 mixtures, the effects of temperature (673 – 873 K) and O2 partial pressure (5 – 21 pct., Ptotal = 86.1 kPa) were determined. Reoxidation in pure CO2 was also investigated at 873 – 1073 K for comparison.

Jan 1, 2014

By C. Isaac Garcia, Sihai Jiao, Anthony J. DeArdo

"A practical model based on the Hill analysis has been developed to calculate the Lankford value of interstitial free (IF) steels and its distribution in different rolling directions, by considering only a few selected texture components. The Texture Intensity Ratio (TIR), i.e. (111 ) /(100), was used in the model to describe texture. By using the new TIR parameter, the texture-based prediction models can be used more easily to predict the Lankford value in a rather straightforward way.IntroductionThe deep drawing capacity of sheet steels is generally indicated by the Lankford value, which is mainly determined by the texture in steels1. Traditionally, various models derived from the Taylor model are employed to calculate the Lankford value from the texture2-4. In such models, the plastic deformation of steel is assumed to be the result of the slip of dislocations in certain slip systems, i.e., by either pencil glide or restraint glide. The slip direction is the <111> direction. In the case of pencil glide, the slip is thought to be possible in all crystal planes with the <111> crystal direction. Assuming the material is elongated in the X1-direction by d n and compressed in the X2 and x3-direction by qd n and (l-q)d n, respectively, corresponding to a deformation tensor"

Jan 1, 2001

By Xinlei Jia, Wenming Guo, Yanling Zhang

A large amount of stainless steel dust rich in Fe, Cr, and Ni has been being generated in China. Smelting treatment is accepted as a practical method for the recovery/reutilization of these second resources, during which Fe, Cr, and Ni is reduced into one metal phase and then separated from the residue slag. Based on the typical compositions of stainless steel dust, the residual slag can be termed as CaO-SiO2-MgO-Al2O3 system. In this paper, the activity coefficients of Cr in Fe-Cr-Ni-C (-Si/Al) melt and the properties of CaO-SiO2-MgO-Al2O3- 1%CrO system thermodynamically approached. Then, in laboratory experiments, the recovery ratios of Cr and its distribution behaviors between Fe-Cr-Ni-C melt and CaO-SiO2-MgO-Al2O3 slag system were examined.

Jan 1, 2015

By P. R. Taylor, B. N. Carlson

Rare earth magnets play an increasingly important role in high end technology, and the manufacture of rare earth magnets, such as the NdFeB type, consume a large amount of the rare earths produced. Recycling of this material could provide an important domestic source for these materials. A selective sulfation roast has been proposed; the central principle of which is to take advantage of the differing stabilities of the rare earth sulfates as compared to those of iron under an air/SO2 atmosphere. Experiments show iron is found to be stable as an oxide, however, neodymium is found to form an oxy-sulfate phase.

Mar 1, 2017

By R. Padilla

A thermogravimetric study has been conducted to follow the decomposition and volatilization of arsenic from enargite concentrate in nitrogen and slightly oxidizing atmospheres. Temperature has a large effect on the rate of volatilization of arsenic. Fractional volatilization of arsenic as high as 98% were obtained in less than 60 min at 650°C in nitrogen atmosphere, while in slightly oxidizing atmosphere the same volatilization could be achieved in 30 min. It was found that arsenic volatilizes as sulfide in nitrogen atmosphere and as 4xture of sulfide and oxide in atmospheres containing 1% oxygen. By using the pore blocking and the first order kinetic models, apparent activation energies of 213 and 200 kJ/mol for the temperature range of 780 - 900 K and 205 and 184 kJ/mol for the temperature range of 900 - 985 K were determined for enargite and copper concentrate, respectively.

Jan 1, 1997

By F. Leclerc, V. Rebeyrolle, M. Revil-Baudard, A. Jardy, M. Založnik, H. Combeau

"Since the quality of Vacuum Arc Remelted ingots is linked to their chemical homogeneity and metallurgical structure, a modeling study of the solidification during VAR has been undertaken. It is based on the solution of the coupled transient heat, momentum and solute transport equations during the remelting of a cylindrical ingot. Solidification mechanisms implemented in the model include a full coupling between energy and solute transport in the mushy zone, and accounting for nucleation and finite diffusion of solutes at the microscopic scale, in both solid and liquid phases. This modeling can be applied to actual multi-component alloys. In this paper, the macrosegregation in Zircaloy 4 ingots is investigated. To validate the model, one single melt of a homogeneous electrode has been specifically performed. The comparison between the predicted macrosegregation and the experimental results shows the importance of accounting for solutal convection to forecast properly the macrosegregation in remelted ingots.IntroductionVacuum Arc Remelting of zirconium alloy ingots is a key step in the manufacturing process of fuel assembly components in nuclear reactors. The control of the chemical homogeneity is indeed fundamental to ensure the quality and the in-reactor performance of the final products. Despite the use of electromagnetic stirring to homogenize the liquid melt composition, chemical heterogeneities develop in the mushy zone during the solidification stage. One of the main challenges for zirconium producers, as well as titanium producers, is to master the VAR process in order to control the macrosegregation in remelted ingots. Macrosegregation results from the association of microsegregation and transport phenomena. The latter are primarily due to the flow in the liquid and mushy parts. It is now well established [1-4] that the hydrodynamics of the melt pool in a VAR ingot depends on the combined action of the followings: thermal and solutal buoyancy, self-induced electromagnetic force and the periodic centrifugal force caused by the angular movement generated by the stirring. However, for zirconium alloy ingots, the effects of thermal and solutal buoyancy forces on macrosegregation through their influence on the flow in the mushy zone have not been clearly identified."

Jan 1, 2012

By J. R. Wynnyckyj, R. Marr

Continuous measurement based on radiation pyrometry has often met with difficulties whose causes have been obscure. In this paper the experience gained with on-line pyrometry in utility and Kraft recovery boilers in the range 800-l400oC will be reported. It is shown that the inherent problems are best resolved by using a spectral pyrometer not sensitive to gas radiation. The radiation from the suspended particles thus provides the signal. It is further shown that the principle cause of difficulties is signal calibration drift caused by heat fluxes originating from surrounding surfaces and reflected by the particles to the pyrometer. Several examples are given how such problems may be resolved using process information and/or additional measurements, fed to and processed by and on-line microcomputer.

Jan 1, 1989