By Stein Tore Johansen

Some ferro-silicon furnaces have heat-recovery equipment. Here, the recovery of electric energy from the off-gases can be increased by increasing the off-gas temperature. This is easily done by reducing the amount of air which usually is mixed into the?off?gas to cool the gas mixture. If the off-gas becomes too hot problems with severe fouling or clogging of the gas channels close to the furnace is observed. The result is irregular stops to clean the off-gas channels. The paper focuses on the nature of the clogging phenomena and some of the ways to avoid clogging. A detailed experimental study was carried out at the Elkem Thamshavn Plant. Theoretical studies were performed to understand the particle deposition, turbulent multiphase fluid flow and off gas combustion in the off-gas channels. The study has resulted in reduced clogging.

Jan 1, 1992

By Stein Tore Johansen

Some ferro-silicon fumaces have heat-recovery equipment. Here, the recovery of electric energy from the off-gases can be increased by increasing the off-gas temperature. This is easily done by reducing the amount of air which usually is mixed into the off-gas to cool the gas mixture. If the off-gas becomes too hot problems with severe fouling or clogging of the gas channels? close to the fumace is observed~ The result is irregular stops to clean the off-gas channels. The paper focuses on the nature? of the clogging phenomena and some of the ways to avoid clogging. A detailed experimental study was carried out at the Elkem Thamshavn Plant. Theoretical studies were performed to understand the particle deposition, turbulent multiphase fluid flow and off gas combustion in the off-gas channels. The study has resulted in reduced clogging.

Jan 1, 1992

By Tian Sugui

By means of the long-term aging treated, creep properties measuring and microstructure observation, an investigation has been made into the microstructure and creep behavior of the casting and rolling GH4169 superalloy after long-term aged. Results show that, after the casting and rolling GH4169 superalloy treated by long-term aged, significant amount of " phase are dispersedly precipitated within the grains of the alloy, and some of the NbC, Cr7C3 carbide are distributed along the grain boundaries. In the range of the applied stresses and temperatures, the creep activation energies and stress exponents of LTA GH4169 alloy during steady state creep are calculated to be Q=541.1kJ/mol and n=16.2, respectively. During creep, the deformation mechanism of LTA GH4169 is thought to be the twinning and dislocation slipping within the twinning regions, and the damaging mode of the alloy is the intergranular fracture, and the non-smooth crystal surface is displayed in the fracture regions of the alloy. Thereinto, the carbides film formed along the grain boundaies has a few effect on the strength between the boundaries, which is a main reason of resulting in the alloy possessing a longer creep lifetimes.

Jan 1, 2009

By Teruo Bitoh, Shogo Izumi

"The effect of B203 flux melting on the structure and the soft magnetic properties of the (Feo.1sBo.20Sio.os)96Nb4 bulk metallic glasses prepared by casting has been investigated. The ringshaped bulk specimens were prepared by the B203 flux melting and copper mold casting. It was confirmed that the flux melting promotes the precipitation of the a-Fe(-Si) and Fe2B phases in the central region of the specimens. The ring-shaped bulk specimens show a flat hysteresis curve, indicating a good linear relationship between the magnetic induction and the applied magnetic field. These results show that it is possible to develop a new soft magnetic material that exhibits constant permeability, which is necessary for producing inductors and choke coils.IntroductionSince the success of forming Fe-based bulk metallic glasses (BMGs) with good soft magnetic properties, great attention has been developed to synthesis and properties of the BMGs [l, 2]. The BMGs have high glass-forming ability (GFA) and, therefore, they can be used to prepare bulk amorphous alloys with a thickness of the order of a few millimeters by casting. The soft magnetic properties of Fe-based BMGs are better than those of ordinary amorphous alloys; therefore, these BMGs have wider applications as soft magnetic materials [3-5]. It is often required for soft magnetic materials that the shape of the hysteresis curve is changed according to the demands of applications. For example, materials with ""flat hysteresis curves,"" which means the magnetic flux density (B) and the applied magnetic field (H) show a linear relationship up to rather high magnetic field, are necessary for producing inductors and choke coils. Flat hysteresis curves can be easily achieved by creating an air gap in the magnetic path. However, magnetic flux leakage generated in the air gap inhibits high-density packing of the electronic components. In order to achieve flat hysteresis curves without creating an air gap, Fe-based ordinary amorphous alloys are subjected to crystallization by annealing and transformed into thin surface layers of a-Fe; the crystallization results in the compression of the remained amorphous phase [6]. Another way to achieve flat hysteresis curves is the formation of secondary phase (such as Fe2B) that act as pinning site of magnetic domain wall displacements [7]."

Jan 1, 2013

By Shadia J. Ikhmayies

SnO2:F/CdS:In bilayers were produced by the spray pyrolysis technique on glass substrates. The structures were characterized by recording and investigating their transmittance curves, I-V plots, X-ray difractograms (XRD) and by observing their scanning electron microscope (SEM) images. From the I-V plots it was found that the SnO2:F forms an ohmic or quasi-ohmic contact with CdS:In. XRD patterns show the polycrystalline nature of the films and show that there is a small shift in the position of the (200) line of SnO2:F without the appearance of new peaks. The morphology of the structures are compared with those of SnO2:F alone and CdS:In alone on glass substrates.

Jan 1, 2009

By P. N. Anyalebechi

Keywords: Aluminum alloy 3004, Solidification rate, Homogenization, Second phase particles The effects of the fineness of as-solidified cast microstructure and temperature on the response of aluminum alloy 3004 to homogenization heat treatment (a.k.a. preheat) have been investigated. The study was conducted at 538oC and 595oC on directionally solidified laboratory-size ingots with a range of solidification rate of 0.10oC/s to 29.4oC/s. Optical and electron microscopy, quantitative image analysis, electrical conductivity, and electron probe microanalysis were used to quantify the effects of the homogenization heat treatment on the microstructure of aluminum alloy 3004. In general, increase in fineness of as-cast microstructure and homogenization temperature enhances the a-transformation reaction, dissolution of Mg2Si, elimination of dendritic microsegregation, and dispersoid formation. The homogenization heat treatment reduces the average size of second phase particles in castings solidified at <1oC/s. However, in castings solidified at above 1oC /s, homogenization causes the coarsening of the second phase particles. Mn in solid solution is independent of homogenization heat treatment temperature.

Jan 1, 2005

By Hubert Bril, Priscilla Pareuil, François Bordas, Emmanuel Joussein, Jean-Claude Bollinger

"According to the legislation, valorization type, origin and characteristics of waste material, various standard procedures are available to evaluate environmental impacts. A Mn-rich slag was sampled from a metallurgical plant. After its characterization (elementary analysis and mineralogy), five standard procedures were carried out (i.e. TCLP, EN 12457-1). Each fixed parameter of the standards was systematically studied in a large range: pH, Liquid/Solid ratio, contact time. For example, EN 12457-1 led to a low ME mobilization, increasing with the L/S ratio, the contact time and an acidic pH. As a conclusion, the representativeness of the considered parameters and their potential variations are predominant to assess of the real environmental impact during slag reuse. Introduction Recent studies have been carried out about environmental impacts of waste containing metallic elements (ME) because of their potential mobility [1-7]. Indeed, slags are either dumped or valorized in various activities such as building materials. In order to assess environmental risk, various standard procedures are used depending on country legislation, origin of waste and valorization way. Results of leaching tests are linked either to special legislation (e.g. Dumping: EC, Council Decision 2003/33/EC, Construction products: EC, Council Directive 89/106/EEC) or to legal levels used in drinking water (Directive 98/83/CE) when leachates could migrate to groundwater. If ME in leachates are lower than drinking water authorized levels, the waste will be considered as non-hazardous. On the contrary, if the leachable amounts exceed them, the question about the risk has to be posed. Beyond the abundance of leaching tests available, variety of operational conditions induced by these regulatory tests does not make the choice easier. According to operational conditions induced, ME release could vary from one test to another one. ME concentrations in leachates depend on pH, Liquid/Solid ratio, contact time and particle size [3]. To highlight the importance of these operational parameters, potential risk for valorization of a manganese-rich slag was assessed by comparing several standard leaching protocols [8-12] with a global study dealing with the influence of operational conditions. For each regulatory protocol, the most influential parameters (L/S ratio, pH, particle size and contact time) have been studied in a large range."

Jan 1, 2008

By A. A. Shook

For relatively little capital outlay, the metal delivery control system in the BHP Copper Rod Plant at San Manuel&apos; was significantly upgraded using the UNAC process simulation and control system (CICS Automation, Newcastle, Australia). An accurate simulation of the metal delivery process was developed with UNAC, which was then used to design a robust controller capable of dealing with plant complexities such as noise, time delays, and nonlinearities. This controller was implemented online using UNAC. Thanks to the extensive preparatory simulation, the controller worked immediately and required no additional online "tuning". Operator response has been favorable, and the UNAC control system has become part of the standard operation of the plant.

Jan 1, 1999

By P. Balachandran

The paper outlines the existing facilities and working practices at the Khetri electro-refinery of Hindustan Copper Limited. Plans have been drawn up to mechanize some key operations to improve the quality of cathodes and the working environment as well as economize the refinery operations. The economic analysis for determining various optimum operational parameters under conditions existing in India have also been outlined. The impact of capacity utilization and mechanization under different sets of conditions on operational costs have been highlighted.

Jan 1, 1987

By Jian-hua Ren, Guang-liang Wu

A lot of dust is produced in iron and steel enterprises, giving rise to serious environment pollution, with which all countries are trying to find methods to deal. The influence of relevant technological factors on dephosphorization was investigated in laboratory, and the effect laws of that were analyzed. The results demonstrate that, in the given conditions of the best slag-metal proportion for hot metal dephosphorization is 1:10, and the optimum temperature is 1350 , The phosphorus distribution ratio of dephosphorization agent containing converter dust of 30% has the maximal value, with dephosphorization rate reaching 85%. Under the optimal conditions, premelting dephosphorization agent can significantly improve the ability of dephosphorization, dephosphorization efficiency increasing to 92%. Therefore, the dust can substitute the oxidant and fixative of dephosphorization agent, be used in hot metal dephosphorization, to enhance the efficiency of utilization.

Jan 1, 2016

By Manoj Kumar, Vinay Kumar, Nikhil Dhawan, Manish Wadhwa

"Electronic waste (e-waste) is a collective name given to discarded electronic devices such as Television, Cellular Phones and Personal Computers. Among the heterogeneous metals present in the e-waste are the base metals: copper, aluminium, nickel, tin, zinc, iron and precious metals: gold, silver, palladium, platinum apart from several hazardous and halogens metals. Hence there is a need to recover these metals from electronic scrap by recycling and then re-use, which can meet large amount of metals demand. Hydrometallurgical processing was employed for the recovery of metals from television printed circuit board (TV PCB). Different lixiviants such as hydrochloric acid, Sulphuric acid, and nitric acid were used to understand the dissolution behavior of copper, iron and lead present in the TV PCB. Effect of increasing concentration of nitric acid was also studied. Selective recovery of tin over 95% in the form of tin oxide was precipitated. The precipitated tin oxide was identified by X-ray diffraction technique. Tin oxide of purity more than 99.9% was obtained.IntroductionThe electrical and electronic industries comprising computers, television, mobiles, etc, which are manufactured utilizing printed circuit, boards, capacitors, resistance, soldering material etc. During production, at the end-of service life and degradation due to the advanced version with latest features generate valuable metallic and non-metallic constituents. European Union Council on waste electrical and electronic equipment (WEEE) has classified these into different categories as listed in Table 1 [Streicher-Porte et al., 2005]. Among these the information technology, telecommunications and consumer equipment constitute electronic waste (e-waste) [EC, 2002]. Almost all e-waste consists of an integrated part of printed circuit boards which is a valuable source of several metals such as copper, tin, lead, aluminium, iron, silver, gold, platinum etc. [Relay et al., 1990]."

Jan 1, 2008

By Nina Bianco, Diana Drinkwater

MetSkill is a professional development program for metallurgical engineers that integrates with normal duties in their first one or two years of service. Graduates work together on a structured technical project, facilitated by specialists and supported by formal learning, and ultimately reported to their technical managers. The program enables graduates to “fill the gaps” in their undergraduate education, which is increasingly pertinent as engineering degrees become more general. Participants report that they enjoy the focus on more challenging (rewarding) aspects of their jobs and feel more confident about problem solving. Sponsor companies add that the relationships developed with external technical specialists enhances opportunities for innovation and development. MetSkill was delivered to two major resource companies in Australia in 2012. This paper provides an outline of the program and the reasons for its success, and demonstrates how the learning model could be applied to groups of graduates in other engineering disciplines.

Jan 1, 2014

By I. Gaballah

Jarosite contains up to 15 % of heavy metal compounds &apos;HMC&apos;. The current waste disposal methods will not be allowed in the near future due to new environmental regulations and pollution risks. For these reasons, thermal treatments of raw or decomposed jarosite, in controlled atmospheres, were investigated. The aim of these treatments is to decontaminate the jarosite and/ or to recover the HMC for recycling. According to physico-chemical characteristics of the samples, the thermal treatments in controlled atmospheres N2, CO+N2 and C12+air lead to the extraction rate that vary from 93 to 98 %. Heavy metal compounds were separated by cooling the gaseous phase. The treatments&apos; residue was almost free from HMC. Between 700 "C and 800 "C, the chlorinating treatment was successful of eliminating more than 97 % of HMC contained in four different samples.

Jan 1, 1999

By J. P. Downey, T. Salisbury, M. Berlin, E. Rosenberg, G. Pinson, R. Christianson, K. Gleason, W. Gleason, S. Davis

"Direct digital manufacturing offers promise as a technique for fabricating complex hydrogen purification membrane support structures. Free form fabrication methods can produce parts with complex structures, and sintering parameters can be controlled to adjust the density, pore structure, pore pathways and strength in catalytic substrate constructs. Efforts are underway to define the influence of selected process variables on the chemical and mechanical properties.IntroductionThe Center for Advanced Mineral and Metallurgical Processes (CAMP), in collaboration with the Metallurgical and Materials Engineering Department at Montana Tech and the Chemistry Department at the University of Montana, is engaged in the development of new methods and materials for hydrogen purification membrane production. Because hydrogen readily passes through palladium, a structurally sound palladium-based membrane is capable of separating relatively pure hydrogen from other gases. In order for this technology to succeed, a suitable substrate material must be identified.High purity hydrogen is produced by various means. A common method involves a two-stage process for separating hydrogen from a hydrocarbon gas stream: 1) hydrogen-rich syngas is produced by the catalytic reaction of natural gas or another light hydrocarbon gas with steam, and 2) hydrogen is separated from the other syngas components by pressure swing adsorption (PSA) (US. Energy Information Agency, 2011). In PSA, gases enter a column that is packed with a material that absorbs gases as the chamber is filled and pressurized. As the pressure is slowly relieved, the absorbent material releases hydrogen at a higher pressure than the impurity gases. PSA processes produce 99.99% pure hydrogen at a high recovery rate. These systems typically demand a high capital investment due to the high pressure and multiple stages (columns) needed to attain high hydrogen production rates.Research geared toward reducing hydrogen production cost is focused on the development of improved catalysts and adsorbent materials as well as more effective single-stage separation processes. An interesting method combines hydrogen reduction catalysis and filtration. Nascent hydrogen is separated from other gases as it selectively permeates the filter. Catalyst filters may be made of gold, silver, platinum, palladium or precious metal alloys (Davis, 2009)."

Jan 1, 2012

By George Oprea, Tom Troczynski, Joe A. Rigby, Waiman Lo

The refractory lining of the tuyere line in Peirce Smith converters have usually much shorter life in service than the rest of the lining, above or below it. There are already recognized chemical, thermal and mechanical factors which contribute to the wear of the lining. Our study presents the experimental results on microstructural changes occurring on these tuyere line bricks in a nickelcopper converter. The experimental bricks, after use at the tuyere line, were investigated using SEM/EDS and XRD techniques, to identify the mineralogical changes due to interactions with the nickel-copper matte or fayalite type slag at the process temperatures. The microstructural changes were correlated with physical and mechanical properties of the brick before and after use and a wear mechanism was suggested. Although the matte does not theoretically react with the mineralogical components of the brick, a partial oxidation of the Ni-Cu sulphides was identified using a line analysis by SEM/EDS in the densified layer at the hot face, which allows for mineralogical changes at the matte-refractory interfaces, with a high probability of microcrack formation due to the thermal cycling during use. These microcracks were also identified to open through inter-granular fractures parallel to the hot face, which appeared to be the main cause of lost lining during use. The reactions between the fayalite slag and refractory brick could eventually play a role in chemical dissolution of the brick only in the superficial layer at the hot face, as no slag components were identified deep into the brick.

Jan 1, 2009

By Ray Y. Lin, Sunil G. Warrier

"Low cost processing of metal matrix composites is an essential requirement for this class of materials to be acceptable in commercial application. In an effort to reduce the cost of processing of metal matrix composites, an infrared pressureless liquid infiltration technique has been developed. The salient features of infrared infiltration are that it is rapid, simple and a low cost process. The rapid processing capability causes very little oxide formation on the alloy resulting in both improved wetting and flow characteristics and reduced oxygen contamination in the composite. Thus, vacuum is normally not required. Using infrared inflltration, aluminum and titanium matrix composites have been prepared under an ambient argon atmosphere. Reinforcements in these composites include carbon fibers, silicon carbide Nicalon fibers and Textron's SCS fibers. Microstructural and mechanical test results indicate that completely consolidated composites with good fiber distribution, limited interfacial reaction and high mechanical properties can be manufactured by this process. IntroductionAluminum and titanium matrix composites reinforced with ceramic reinforcements are strong candidates for numerous applications in the aerospace and automotive industries. Aluminum matrix composites are commonly fabricated by either solid state vacuum hot pressing, liquid state pressure infiltration or squeeze casting [1]. Although liquid state pressure infiltration and squeeze casting has significant advantages over solid state processes, the requirement for pressure makes these composites uneconomical for large scale industrial application. Titanium matrix composites are primarily fabricated by solid state diffusion bonding [2]. Pressureless liquid infiltration can significantly reduce the cost of fabrication in both the composite systems. However, during pressureless infiltration processes, several complications concerning the wetting characteristics and chemical compatibility arise."

Jan 1, 1994

By J. Pérez

A lead smelter slag with high copper, lead, arsenic and silver contents was treated at laboratory scale for arsenic removal. The slag was first leached at atmospberic pressure with sulfuric acid and oxygen. According to arsenic contents leaching of most of the arsenic was achieved in either one or two stages, producing a lead-silver rich residue and a solution high in copper and arsenic concentrations. Alternative routes were considered to treat the resulting solution. Firstly, solvent extraction of arsenic with a mixture of TBP and 2-etbyl-bexanol was tested and extractions of over 95 percent of arsenic were achieved. Secondly, a copper arsenate precipitation treatment was done to eliminate arsenic and copper from solution.

Jan 1, 1996

Cuspidine (3CaO?2SiO2?CaF2) is one of the most important compounds crystallized in mold flux films during casting in the continuous casting process of steel. The primary crystallization field of cuspidine has been experimentally developed in the CaO-SiOrCaF2-SiF4 system. The cuspidine-NaF binary and cuspidine-CaF2-NaF ternary systems have been also experimentally determined to study effects of addition of NaF on the primary field of cuspidine. In order to discuss its thermodynamic stability the standard Gibbs energy of formation of cuspidine has been determined by an electromotive force method using CaF2 as solid electrolyte and a transpiration method as follows: The chemical potential diagram and constituent activities for the CaO-Si02-CaF2 system have been evaluated based on the obtained thermodynamic data.

Jan 1, 2003

By Pan Gu, Zhen Zhang, Jiang Diao, Bing Xie, Hongyi Li

Furnace refractories are in most cases chemically incompatible with smelter slag, which leads to a steady erosion in their thickness over time. Once too thin, refractory walls become mechanically unstable and catastrophic failure can result. Historically, external shell cooling was applied to generate a freeze lining of slag and thus prevent refractory erosion. Many modern high intensity smelting furnaces instead maintain their physical integrity by the use of internally cooled wall panels, plates or finger coolers. An initial refractory lining is often installed inside of the coolers, such that the furnace originally operates with a temperature (insulated) rather than a heat flux (freeze lined) boundary condition. This paper examines the change in slag-wall heat transfer coefficient and slag superheat as a function of process intensity. The implications of the changes in heat transfer on residual brick thickness are explored using analytical modelling.

Jan 1, 2016

By P. C. Chaubal

The overall kinetics of oxidation of single partic1es of chalcopyrite have been studied for temperatures up to 1273 K. The experiments were conducted in a stationary bed reactor using a non-isothermal technique. Any mass and heat transfer effects on the kinetics of oxidation were eliminated by using a high-enough gas flowrate. Up to temperatures of 873 K, pore-bl1ocking kinetics were applicable, whereas above 873 K, power-law kinetics gave a satisfactory fit of the data. The activation energy was 215 kJ/mol below 754 Kand 23.7 kJ/mol above 1,060 K. Predominance area diagrams were constructed at various temperatures and used in conjunction with X-ray analyses of partially oxidized samples to determine the intermediate phases formed during the reaction. The analysi1s also provides a justification for the kinetic models used. The results indicate that the reaction rate is first order with respect to oxygen concentration and inversely proportional to the square of the particle size throughout the ranges of temperature studied.

Jan 1, 1985