By Aichun Dou

Au-Sb alloy sample in which the total amount of Cu and Ni is below 25% (wt. %). In practice, Cu and Ni were difficult to be dissolved in sulphuric acid solution by oxidative leaching under the atmospheric pressure conditions, because of the lower concentration of Cu and Ni in the sample. In this paper, pressure oxidation leaching in sulphuric acid system (POLS) followed by hydrochloric acid leaching (HAL) was employed to remove impurities in the Au-Sb alloy. The effects of variables in POLS on leaching ratios of different metals were investigated in detail. Under the optimal conditions: the concentration of H2SO4 is 1.5 mol/L, liquid-solid ratio is 7:1, the amount of oxidizer is 1.2 times of the theoretical amount, leaching time is 4h and leaching temperature is 427K, the leaching ratios of copper and nickel reached up to 99%, antimony, lead and silver were not dissolved in dilute sulphuric acid solution. The residue from POLS was then treated with hydrochloric acid solution in fixed conditions, the leaching ratio of antimony reached over 92%, the grade of gold in the ultima residue was enriched up to 66%.

Jan 1, 2016

By I. H. Bonekamp

Norddeutsche Affinerie has operated an Outokurnpu type flash smelter for more than 25 years. In recent years, the concentrate smelting capacity was increased to 750,000 tpy, double of the initial design capacity. Maintaining this high performance level requires very good metallurgical process control. It is not enough to base this control on thermodynamics and kinetics since the furnace is highly dynamic. Understanding these dynamics and being able to quantify them can have significant financial benefits. A mass and energy balance model was developed and is discussed based on measured data. At this time the model is based on the major elements copper, iron, sulfur and silica. With it is possible to quantify the differences of the various material streams such as matte, slag, flue dust, matte carry-over to settling furnace, etc. Comparing the reconciled energy balance model with the fundamental thermodynamic model makes it possible to quantify the dynamics. These dynamics are related to input parameters using methods such as statistics and neural nets. In the future this database will be used to improve the understanding of the dynamic process as well as the dynamic process control.

Jan 1, 1999

By Tuomas Hirsi

The world’s first large scale modular solvent extraction plants have been delivered by Outotec. The first of these is now in operation and has proven that the VSF®X technology can deliver the excellent performance of the Outotec VSF® solvent extraction process. Modular delivery allows site work to be minimized and the manufacturing done in a controlled environment, allowing for serial production manufacturing benefits. Container based delivery was found to be a highly efficient way of utilizing the standardized transportation methods on a global scale. Site work with modular units was found to be efficient and highly predictable. In this paper, we present the first successful Outotec VSF®X deliveries and discuss the benefits of the modular delivery and design compared to the standard solvent extraction installation’s delivery. The process performance of the VSF®X is also discussed with experiences from the first industrial reference presented.

By John W. Pickens

The recycling of industrial wastes and by-products is an important component of ecologically responsible industrial management. Converting waste streams into value-added products or material and energy resources with a profit margin assures the continued viability and practice of recycling. The recycling of aluminum stands out as one of the best examples with major economic and environmental benefit. However, the benefits are compromised by landfilling of black dross and salt cake, waste streams produced from within the recycling process itself. This paper reviews Alumitech's strategy and progress in establishing a tertiary aluminum industry based on closed-loop recycling of black dross/saltcake; one which does not compete with the primary and secondary aluminum industries, but rather serves their needs to ensure the continued economic benefits of aluminum recycling and elimination of environmental liablJity associated with landfilling of black dross/saltcake. Alumitech has made significant progress toward that goal in operation of its new recycling facilities in Cleveland where recovered aluminum and nonmetallic residue from salt based drosses is being converted into commercial products, eliminating the landfilling of the greatest portion of dross/saltcake. The economic strategy for recycling saltcake and its progressive achievement is reviewed.

Jan 1, 2000

By Gabriel Bartholazzi Lugão de Carvalho, Sergio Neves Monteiro, Fabio Da Costa Garcia Filho

The thermochemical treatment of Pulsed Plasma Nitriding is employed as an alternative to improve the surface properties of metals, such as: increase surface hardness, improve wear resistance, extend fatigue life and also create a barrier to the diffusion of hydrogen into the steel to reduce the susceptibility to hydrogen embrittlement. In this study, the effect of such treatment on ASTM A36 steel is analyzed through two different nitriding conditions: 5 h and 660 Pa for the first condition and 15 h and 720 Pa for the second one. In both cases, the temperature was held at 300 °C. Thus, in order to verify the results, Vickers hardness analysis and metallographic observation were carried out under an optical microscope. Only the second condition was able to achieve what was proposed, the formation of a uniform nitriding layer and an expressive increase of hardening on the surface.

Mar 1, 2018

By D. Neuschiltz, M. Witthaut, R. Cremer

"Metastable (Ti,Al)N coatings with fee structure have been shown to exhibit superior performance as compared to TiN under conditions of wear at elevated temperatures due to their better oxidation resistance and hardness. The oxidation resistance of these coatings increases significantly with increasing Al-content. However, the deposition of (Ti,Al)N films with Ti/ Al ratios below about 30/70 leads to a hexagonal structure which is not suitable for tribological coatings. Only little is known about the location of the cubic to hexagonal phase transition and hence about the optimum composition of (Ti,Al)N hard coatings.To determine the position of this transition, Tii-xAlxN films with different Ti/Al ratios were deposited on high speed steel at substrate temperatures between 100 and 700 °C by means of reactive MSIP. The composition of the films was determined by electron probe microanalysis (EPMA) and X-ray photoelectron spectroscopy (XPS), the crystallographic structure by thin film X-ray diffraction (XRD).It could be shown that in case of deposition temperatures of 300-700 °C a two-phase region exists in the metastable TiN-AlN phase diagram, which expands with increasing temperature, wheras at 100 °C substrate temperature no two-phase region was observed. But in opposition to the phase diagram known from literature, which is based on thermodynamic estimations, the detected two-phase region is narrow for typical PVD temperatures, thus allowing the deposition of cubic single-phase Al-rich (Ti,Al)N hardcoatings for tribological applications. Based on these results, a new Ti1-xAlxN film with x = 0.62 has been developed, which showed an increase of oxidation resistance by a factor of 4."

Jan 1, 1998

By Brajendra Mishra, Mark L. Strauss, Gerard P. Martins

Europium is a critical material required for LED, florescent lamp, cell phone screen, and flat panel display production. This process recycling europium from waste lamp phosphors is an innovative method to supply europium. The selective reduction and precipitation method using sulfate precipitation is investigated to recover high-purity europium from yttrium-europium mixed solutions.

Mar 1, 2017

By Jong-Shin Chang

The Onsan smelter has tried to do various activities to decrease operation costs. With several expansion projects, the Onsan smelter has aimed at not only a quantitative growth but also qualitative growth through efforts improving operations equipment and processes. Activities to reduce operation costs have been one of those efforts. In particular, the energy cost of operation has been a main target for reduction. The activities to save energy have been carried out in two ways. One is to recover and utilize waste heat as much as possible and another is to replace existing equipment and processes with more energy-efficient ones. This paper reviews recent improvements and future plans for energy saving activities at the Onsan smelter.

Jan 1, 2006

By Shufang Ding, Fukun Yan, Zhiqiang Shan, Wei Chen, Cuicui Ji

"To remove aluminum ion from chlorinated rare earth solution, this paper used hydrolysis method to explore the hydrolysis behavior of aluminum ion in aluminum chloride solution and confirm the optimum conditions of aluminum ion hydrolysis, which are pH value, temperature and initial concentration of Al203 and so on. The experimental results show that single treatment can make aluminum precipitation rates of chlorinated rare earth solution reach about 90% by hydrolysis precipitation; and then several recycle disposal can get precipitation rates of 89% for aluminum and 2.86% for rare earth.IntroductionIn China, rare earth resources are very rich and unique minerals, complete variety, and rare earth products are very large in the domestic reserves. Rare-earth and application products have been deep into all areas of our life, permanent magnet material of rare earth is one of the most popular application areas[11. Binary oxides such as praseodymium neodymium have been widely applied in the fields of glass, ceramics, magnetic materials, catalysts and so on. Especially, the advent of the Pr-Nd-Fe-B magnets which makes the world magnetic material into a new stage of development [2•3]With the development of science and technology, for industrial, physical and chemical indicators of raw materials Pr-Nd oxides (such as particle size, specific surface area and non rare earth impurities etc.) are also getting higher and higher. The oxide size has an important influence on sludge formation in the electrolytic process. If the size is too large, added oxides have settled on the bottom of slot before melting, and then generated sludge; if the particle is too small, it can cause dust dispersion, enlarge oxide unit consumption and increase the cost of production in the charging process. Some early processes use oxalic acid to make chloride neodymium praseodymium settle, and impurity can be removed cleanly, but the cost is high, it is not suitable for production. At present, most enterprises are using ammonium hydrogen carbonate to precipitate chlorinated neodymium praseodymium, but chlorinated neodymium praseodymium such as iron and aluminum and so on can easily form gel in the precipitation process, seriously affect the growth of neodymium praseodymium carbonate crystal and often leads to particle meticulous, even may also generate gel-like neodymium praseodymium sediments and cause centrifugal or suction filtration difficult. Now the actions and their removal of impurity such as iron and aluminum have done a lot of research in the production process of rare earth, removing aluminum craft with alkaline (sodium hydroxide) and acid (oxalic acid) has good effect, but the cost is higher[41; used adding complex agent to remove aluminum method which is simple and easy to operate, but aluminum removal rate is not high, and also changed the sediment of crystal type[51, and etc. This paper discusses the removal of chlorine from rare earth solution on the basis of the hydrolysis property differences betweenAJ3+ and rare earth ion."

Jan 1, 2013

By Ephraim Jeya Kumari

The demand for the titanium dioxide pigments and the shortage of higher-grade titaniferous ores with low radioactivity and zircon sands worldwide has encouraged the development of new techniques for the beneficiation of lesser grade titaniferous ores. The inferior quality ores are invariably richer in radio-active and lanthanide oxides, which severely interfere with the fluidized bed chlorination reaction (FBCR), in which ultra-high purity titanium tetrachloride is distilled off for pigment manufacture. However the present beneficiation techniques require high quality ilmenite ores and are not suitable for upgrading lower grade ilmenite ores which do posses trace metals in the form of lanthanides and actinides as Al-phosphates and zirconium silicates, respectively. The presence of mineral hosts, zircon sand and monazite in ilmenite and anatase also increase in chlorine gas consumption in the FBCR and contribute to a larger volume of hazardous waste production, which must be neutralised at a significant cost before being disposed off safely. In view of the problems described for lanthanide (Ce, Nd etc) and actinide (Th, U) trace impurities in titaniferous ores, an alternative route, which is flexible and more accommodating for processing difficult ores, is discussed. In the new process, which may be used for richer grades of ores too, the ore is roasted in air with sodium carbonate below 950°C to promote the formation of water-soluble sodium ferrite and insoluble sodium titanate phases. In this investigation, the high-temperature roasting process and the ensuing hydrometallurgical leaching steps have been analysed in the context of selective separation of lanthanide and actinide minerals from the main titaniferous mineral structures. Evidences for the selective separation are presented based on the chemical (XRD, XRF, AA) and microstructural analysis (SEM, EDX, EPMA) of roasted mass and the leached product. The efficiency of selective separation is also reported based on the chemicals analysis and the particle size of the materials derived after leaching. The paper highlights the various thermodynamic aspects of reaction equilibrium in the Fe-Ti-O-Na system, and the effect of Eh-pH diagram in the determination of pH required for the better control of the removal of iron and sodium. Two different types of Ti ores, namely ilmenite and anatase, their crystal structure and the phase transformation will also be explained on the basis of wet chemical analysis, XRF, XRD, EPMA and SEM-EDX studies. The method developed examines the technological feasibility of the selective separation process.

Jan 1, 2006

By Georgina De Micco

The National Commission of Atomic Energy is investigating a suitable physicochemical process for the conditioning of spent nuclear fuel and treatment of the scrap of research reactors of the Al-UxSiy type. A possible way of processing is through dry chlorination of the cladding with the purpose of selective separation of the aluminium from the remaining elements such as Fe, Ni, Zn, Cu, etc. transforming them into volatile chlorides. Some important advantages of this method are the thermal stability of the chlorides that allow the easy separation of the halides by physical methods and the low volume of radioactive waste generated. The interactions in the following systems were studied in the range of temperature between 150º-500°C: Al-Fe, Al-Ni, Al-Cu, Al-Zn, Cu-Zn and the pure metals. We found that the reactivity was different depending on if the elements were alloyed or separated. The separation factors of the systems under study were determined. Nickel is perfectly separated from aluminium for all temperatures, whereas good conditions for copper separation were achieved below 400ºC. In the case of iron, complete isolation was never attained. However, by decreasing temperature to 150ºC it is possible to obtain aluminium chloride with less iron content. The separation of zinc from the product was also difficult. It was detected that zinc chloride volatilization decreases when other chlorides were present, for example cooper chlorides. In the Cu-Zn alloy, zinc chlorides remained in the condensed product due to interactions with copper. The samples were characterized by scanning- electron microscopy (SEM), X ray diffraction (XRD) and atomic absorption.

Jan 1, 2006

By T. T. Chen

Raw anode slimes consisting primarily of PbSO4, AgCuSe, Cu3Se2, Cu2-x Se, Cu2O, CuSO4.5H2O, Sn arsenate and Sb-Bi-As oxide are batch-leached with electrolyte-O2 to dissolve Cu. During this process, Cu2O and CuSO4.5H2O are solubilized and the Cu in the selenides is leached with the formation of Ag2Se and Se. A small amount of Cu remains in the Ag2Se, Sn arsenate and Sb-Bi-As oxide. The decopperized slimes are repulped in Na2CO3 solution to convert most of the PbSO4 to NaPb2(CO3)2(OH). The Sn arsenate and Sb-Bi-As oxide partly react, but the Ag2Se is not significantly affected by the Na2CO3 solution. The NaPb2(CO3)2(OH) intermediate phase is dissolved in acetic acid to leave a final product consisting of Ag2Se, Se, Sn arsenate and Sb-Bi-As oxide, together with small amounts of PbSO4, NaPb2(CO3)2(OH) and various gangue constituents.

Jan 1, 1993

By Takeo Fujino, Nobuaki Sato, Yarong Wang, Kohta Yamada

"Ternary mixed sulfides of some transition metals MTS3 (M=Ba, ·Pb, T=Ti, Zr) were synthesized by a relatively low temperature process using sulfur melt. The mixture of starting materials, such as, metals and/or binary sulfides and a large excess of sulfur was reacted in a vacuum-sealed Pyrex or quartz ampoule at 350- 600 °C for one to three weeks. After the reaction, the remaining sulfur was completely removed by a process composed of filtration of sulfur melt and followed dissolution in CS2• The binary sulfides impurities coexisted in the products were removed by rinsing the products in water and acetone. By using the above method, BaTiS3, PbTiS3 and BaZrS3 'Were obtained in pure form. The effect of addition of halides on the yields of these ternary sulfides were also discussed.IntroductionThere have been a vast number of studies on the preparation and physical and /or chemical properties of mixed metal oxides. As is well known, some of such compounds exhibit excellent materials properties, causing them for use in mechanical, electronic, magnetic and chemical devices. Not a few mixed metal sulfides show similar physico-chemical properties to those of the corresponding mixed metal oxides. However, the study of the mixed sulfide crystals is rather sparse mainly due to difficulties in preparing these compounds. In various methods which have been adopted for preparing mixed sulfides, the simplest method would be the solid-solid reaction of the component binary sulfides or elements. However, there are always diffusional constraints with regard to the reactions in solid phases causing it necessary to heat the reactants at sufficiently high temperatures, viz. 800-1200°C. On the other hand, some mixed sulfides are unstable at high temperatures or to change their materials properties due to sulfur nonstoichiometry and structural modification depending on temperature, i.e., synthesis of such compounds needs to be made at lower temperatures. Processing in alkali halide melts is hopeful to overcome the above problems but to obtain the halide melts the temperatures above ~ 600 °C is needed. Low temperature reaction has been carried out for the preparation of Hg1.24TiS4, which was formed by the ·combination of TiS2 and molten Hg metal at 320°C[l]. Reaction of WS2 with LiBH4 melt at 350°C yielded LixWS2[2]. These sophisticated methods, however, can be applied only to the vary special cases."

Jan 1, 2000

By Takashi Miyamoto, Hideo Nakae, Hideki Yamaura, Takeshi Yanagihara

"For the production of partially composed metal matrix composites, namely discontinuous MMCs, using a casting· process, the interpenetrated phase composites with SiC particles were fabricated by pressureless iDfiltration using molten Al-Si alloys. This process is based on a wetting phenomenon, therefore, we discussed the technique based on the reactive wetting. The SiC particles coated by diluted water glass were sintered in a mullite Tammann tube and simultaneously infiltrated with molten Al-Si alloys in air at 1173~1573K. As for the improvement of the wettability between the SiC and the liquid aluminum alloy, Fe3O 4 powder was mixed with the water glass due to the thermit reaction between Fe3O4 and molten aluminum alloy. In some experiments, pure aluminum powder was placed on the sintered SiC to increase the interfacial area and the chemical reaction between the sintered Sic. and the melt. By combining these conditions, we succeeded in the complete infiltration without pressure at 1173K.IntroductionAs is well known, the mechanical properties of metal matrix composites (abbreviated MMCs) are superior than that of ordinary metals. However, their use has not been widely accepted because the production cost is very high due to their poor machinability. Therefore, the production of partially composed, namely discontinuous MMCs, by as the Lanxide process [l,2] has been investigated for many years. The Lanxide process, it takes a long time, sometimes up to 10h, in a nitrogen atmosphere for the infiltration. Therefore, the cost will be higher for common use. On the other hand, a high 'pressure process has been adopted for the production of discontinuous MMCs by the Toyota Motor Corp.[3]."

Jan 1, 2000

By Timothy W. Ellis

"This paper presents the basic theory of operation, physical chemistry and phase equilibria which allow the development of liquid-liquid extraction circuits based on metallic solvents. The incorporation of reduction and reduction/diffusion processes into the process scheme is discussed and a detailed description of several liquid-liquid extraction schemes are developed. A synopsis of experimental results obtained using this method to separate rare earth and other metal based materials will be given.IntroductionConcerns over the effects of waste materials in the environment has been one of the significant social hallmarks of the late 20th century. Essentially every industrialized country has had to incorporate the cost of waste material into the equation of production. Legislative initiatives have led to the passing of very tough laws, by historical standards, which govern the environmental impact of materials processing.Liquid-Liquid extraction is a very common unit operation normally using aqueous and/or organic based solvents. Early work at the Ames Laboratory focused on the use of this technique for the reprocessing of spent fuel from liquid metal breeder reactors by the use of metallic solvents. Recently, we have revisited this area as a means to recycle/reprocess several emerging rare earth based materials, although this method has a much wider range of application. The reinvestigation of this technology is particularly timely as hydrometallurgical based processes are coming under increasing scrutiny in the U.S.A. by the Environmental Protection Agency (EPA). Although technology currently exists to remove contaminants from aqueous based waste streams, often the application of such methods is expensive. With proper design and judicious selection of reagents liquid metal extraction can achieve a high recovery along with a benign waste stream.This process has several possible advantages over other technologies. First is the elimination of aqueous solvents. Therefore, problems associated with disposal or reprocessing of the aqueous carrier are eliminated. Second, with proper system design, very high separation coefficients can be obtained thus limiting the number of stages required. Third, metals are extracted from metals with a metallic product, thereby eliminating the need to re-reduce metal for oxides or other compounds which are the common output for aqueous based extraction procedures."

Jan 1, 1996

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999

By Antti Roine

Sulfidic zinc concentrates are usually roasted in a fluidized bed furnace into sulfur-free oxide form. Metallic zinc is produced from this oxidic calcine using hydrometallurgical leaching, solution purification and electrowinning stages. The roasting step is necessary because zinc oxides are easier to dissolve using traditional leaching methods than zinc sulfides. The Kokkola Zinc smelter uses various types of zinc concentrates and secondary materials as feed mixture. This makes it difficult to find optimum process parameters for the roaster when the composition and particle size distribution of the feed mixture varies even on a daily basis. Certain conditions may even cause difficult accretion problems or increase the amount of calcine in the process off-gas line excessively. A thermochemical heat and material balance model was developed for process advisor, in order to estimate the effects of different process parameters (temperature, process air coefficient, concentrate feed, oxygen enrichment, water feed, etc.) on the heat balance, roasting temperature and calcine composition. This model was constructed using the heat balance module of HSC Chemistry 4.0 software. The prevailing chemical compounds in the concentrate and calcine were verified using mineralogical analyses and equilibrium calculations. The roasting process seems to operate near chemical equilibrium conditions, if the behavior of the main components is considered. This paper describes briefly the basic principles of the calculation model and outlines the results with several diagrams and discussion. The calculated results were in reasonable agreement with the recent process air oxygen enrichment and water feed test campaigns carried out at Kokkola in 1999.

Jan 1, 2000

By N. S. Narayanan

Monazite, one of the major sources of rare earths, is normally opened by digestion with hot concentrated caustic soda solution. Caustic digestion dissolves phosphate and leaves a hydrated mixed metal oxides cake containing thorium, uranium and rare earths. By leaching this cake with hydrochloric acid at pH 3.0 to 3.2 bulk of the rare earths are preferentially removed and separated. The slurry left after removal of major portion of rare earths contains all the thorium and uranium present In the feed monazite. In addition this slurry also contains substantial quantities of rare earths. Solvent extraction tests were carried out to develop a process to separate rare earths, thorium and uranium present in the mixed chloride solution obtained by dissolving the above slurry in hydrochloric acid. Based on these tests a solvent extraction flow sheet was developed with di-2-ethyl hexyl phosphonic acid mono 2-ethyl hexyl ester as the extractant. The details of experimental work and results obtained are discussed and a flow sheet for processing monazite Incorporating the new process is suggested.

Jan 1, 1997

By Caisa Samuelsson, Sina Mostaghel, Theo Lehner

"Rönnskär smelter of Boliden Mineral AB, Sweden, is well known for recycling of base and precious metals. Slag from the electrical furnace is processed at the fuming plant to produce zinc clinker. The granulated slag is a by-product used as e.g. construction material. In this paper, influences of Al2O3 on mineralogy of the slag, which can affect its chemical and physical properties, are investigated. Different mixtures of Al2O3/fumed slag were prepared. Re-melting was carried out in a Thermo-Gravimetry (TG) furnace with an inert atmosphere. Scanning electron microscopy (SEM) and X-ray diffractometer (XRD) were then applied for the analyses. Investigations depict that addition of alumina to slag, results in an increase in the number of spinels and a transformation from iron rich to aluminum rich spinels. Anorthite (CaAl2Si2O8) will also be formed.IntroductionRönnskär smelter of Boliden Mineral AB is located in north of Sweden; the main products of this smelter are: Copper, Zinc clinker, Lead, Gold, and Silver, while sulphuric acid, liquid sulphuric dioxide, and Iron sand are some of the by-products. Reducing the energy consumption and decreasing the usage of finite natural resources are becoming more and more important for the Rönnskär smelter; this result in use of different recycling and scrap materials. Metal residues, from brass foundries, steel mills, and electronic scrap are recycled at Rönnskär smelter [1]. Most of the electronic scraps contain mixtures of various metals together with plastics and ceramics, which can affect the composition and properties of the slag considerably [2]. At the same time, treatment of slag and controlling its composition and properties are of much interest for Base Metals producers from different aspects. Composition of slag influences the physical properties such as: 1) Liquidus temperature [3-4] 2) Viscosity, which controls separation of valuable metals, especially copper by gravity separation [2] and also heat and mass transfer [5] 3) Electrical conductivity [6]."

Jan 1, 2008

By J. H. de. Visser

The transfer of molten metal in smelting or refining operations is typically performed in open trough-type launders that are constructed of either water-cooled copper troughs or refractory lined steel jackets. This transfer can be either continuous or batch. Batch operations transfer metal through an open launder. The uncovered launder has many operational and environmental drawbacks. In order to improve workplace hygiene, designs have evolved toward ventilated launder covers that .are connected to secondary exhaust systems that use negative pressure under the cover removing fume and hot gases to secondary fume control devices. In smelting operations, a variety of covers have been employed which insulate the launder and contain the fumes and also provide additional heat along the length of the launder through a series of premix or inspiration-type burners that add combustion products to the normal fume load in the launder. Cover designs have proven to be inadequate in that hinged unventilated covers hinder convenient access while heated ventilated covers are costly to maintain. Covers that employ refractory bricks and overhead enclosure-type exhaust hoods have been somewhat successful, but restrict operator movement and require large volumes of exhaust air. An example is given of a cover and off-gas system for launders that is designed to provide superior insulation and heating capabilities, as well: as better control of the fume gases-and ease of maintenance. The cover system must maintain the balance between maintaining launder heat and fume removal. The construction of the covers must be able to withstand high internal temperatures and maintain its structural properties.

Jan 1, 1999