By S. Yuan

Oxygen ion conducting yttria-stabilized zirconia (YSZ) tube was used to remove oxygen from molten Cu at 1373K. Outer surface of the tube was in contact with the melt and the inner surface containing a thin layer of porous Ni-ZrO2 cermet electrode was in contact with a reducing gas. The migration of oxygen species (O2-) from the Cu melt through the YSZ tube is accompanied by an equal and opposite flux of electrons maintaining electroneutrality. Without applying an external EMF, the fluxes are maximized by short circuiting the melt with the cermet electrode. For efficient oxygen removal, the YSZ tube must be thin, contact resistances should be negligible, and the electrodes must be porous and cover the entire electrolyte surface for charge transfer. This refining process is environmentally sound, can use reducing gases such as H2, CH4 and CO without running the risk of increasing H or C content of the melt.

Jan 1, 1993

By Sridhar Seetharuman

Sulfur and oxygen dissolved in nickel and cupronickel melts can be removed as gaseous oxides of sulfur by a vacuum treatment. Presented in this paper is a new matched thermochemical diagram that permits direct evaluation of the equilibrium partial pressure of SO, as a function of temperature over an alloy of specified composition. The matched thermochemical diagram consists of a central plot which shows the integral Gibbs' energy of mixing for the binary system S-O2, at different temperatures. The central plot is flanked on either side by terminal plots of the chemical potentials of oxygen and sulfur, as functions of temperature, for different alloy compositions. By projecting the chemical potentials of oxygen and sulfur from the terminal plots on to the central diagram, the equilibrium pressure of SO2,can be directly read on the nomograms on the central plot at different temperatures. The matched thermochemical diaerams are - useful in assuring the efficiency of vacuum refining.

Jan 1, 1993

By D. W. Ashman

The zinc pressure leaching plant at Cominco's Trail Operations is now in its ninth year of production. The plant produces a zinc sulphate and jarosite slurry which is further processed in the calcine leaching circuit. Elemental sulphur, a by-product of the process, is sold in the North American market. During the past eight years, a number of changes have been made to the plant to remove known production bottlenecks and to improve leaching extraction. These changes have raised production rates above the initial design so that the plant currently accounts for approximately 20 percent of Trail s zinc production. These rates are expected to be increased further upon the completion of the alterations currently in progress. The knowledge gained over the operating life of this plant has allowed Cominco to plan for a possible future expansion of the zinc pressure leaching plant. If expanded, zinc pressure leaching would account for approximately 48 percent of cominco?s zinc production.

Jan 1, 1990

By P. A. Manohar

This paper describes an implementation of the Potts model for simulation of grain growth in 2D on a distributed-memory parallel architecture. The simulation scheme utilizes a continuous-time, asynchronous parallel version of the n-fold way algorithm. Each Processing Element (PE) carries a piece of the global simulation domain while the virtual topology of the PEs is in the form of a square grid in 2D and Torus in 3D. Different PEs have different local simulated times. Inter-processor communication is carried by the Message Passing Interface (MPI) routines. Sample results for grain growth simulation in 2D are presented for a 840 x 840 global domain size distributed over 16 PEs. The grain growth kinetics obtained in the simulation of pure, isotropic systems is in good agreement with the theory. Grain size distributions obtained in the parallel simulation are well described by the lognormal distribution, thus validating the simulation procedure. Keywords: Metropolis algorithm. n-fold way algorithm, asynchronous parallelization, grain growth

Jan 1, 2003

By B. R. Westphal

The Integral Fast Reactor (IFR) concept being developed by Argonne National Laboratory is based on the pyrometallurgical processing of spent nuclear metallic fuel with subsequent fabrication into new reactor fuel by an injection casting process. During fabrication, a dilute scrap stream containing uranium alloy fines and broken quartz (Vycor) molds is produced. Waste characterization of this stream, developed by using present operating data and chemical analysis, was used to evaluate different uranium recovery methods and possible process variations for the return of the recovered metal. Two methods, comminution with size separation and electrostatic separation, have been tested and can successfully recover over 94% of the metal. Recycling the recovered metal to the injection casting process was evaluated for the different economic and process impacts. The physical waste parameters and the important separation process variables are discussed relative to their effects on the viability of recycling the material. A discussion of the criteria that is being used to establish the acceptable operating limits is also presented.

Jan 1, 1992

By Rafael Padilla

In the production of copper from chalcopyrite (CuFeS2) concentrates by the smelting and converting technology, the ambient pollution with gaseous S02 and toxic metals such as arsenic compounds is still a serious problem, especial1y in the converting step due to the batch nature of the conventional Peirce Smith process. Non-SO2 emitting alternatives are leaching processes. However, few of them have had a limited industrial application and they are not very effective in discarding safely the toxic impurities. A combination of pyro-hydrometal1urgical methods: the sulfidation of chalcopyrite and subsequent leaching of the sulfidized material is a non-polluting alternative to treat not only clean chalcopyrite concentrates but also complex chalcopyrite-enargite concentrates. In this article, this alternative is discussed concerning the thermodynamics and kinetics of the sulfidation of chalcopyrite with gaseous sulfur. The kinetics of the leaching of the sulfidized concentrate in an H2SO4-NaCI-O2 system is also discussed.

Jan 1, 2003

Lead removal has been problematic in nickel production by electrowinning from chloride solutions, as developed by Falconbridge. The C12 leach liquor needs to be diluted by electrolyte to allow precipitation of the lead prior to electrowinning. This results in higher solution purification costs and an aversion to consider lead contaminated (secondary) feeds. In this paper, the electrowinning of nickel chloride is carried out in a membrane equipped electrolytic cell. When lead containing nickel solutions are fed into the anode compartment and the anolyte is separated from the catholyte with a cation exchange membrane, lead remains in the anolyte due to the presence of a negatively charged chloride complex. The positive nickel ions migrate preferentially through the membrane to the catholyte, allowing a lower lead nickel cathode to be produced. Lead concentration in the catholyte and the cathode product has been tested as a function of lead concentration in the anolyte. Results are presented and discussed.

Jan 1, 1998

By C. Cánepa

In the treatment of many problems related with the optimization of a given ore dressing process, microscopic studies can provide invaluable assistance. Such studies are generally carried out through mineralogical determinations both qualitatively and quantitatively. Frequently the solution of a specific problem requires the combination of these in adequate proportions. Often the nature? of the problem poses some conditions regarding the way the microscopic determinations are made in order to yield useful information. Most publications applied to mineral beneficiation show results of ore microscopy without mentioning the methodological details involved in the determinative work and therefore it is not possible to judge their reliability and/or their relevance. As methodology must necessarily change from case to case, it is very important for the microscopist to identify first the direct and indirect mineralogical information required to solve the problem. Without such guidelines selection of methods for the qualitative and/or quantitative determinations cannot be made.

Jan 1, 1981

By Bin Du

In recent years, concurrent product design and process is gaining popularity and will become a norm of the industry of the future. Forging has been a critical manufacturing process for production of components with superior tensile strength, toughness and grain flow. This paper describes an expen system which is being developed for forging die design and forging process analysis in concurrent engineering environment. Rules and guidelines pertaining to forgeability are formulated and incorporated into the knowledge-base in building the system. The system is built using an object-oriented paradigm. The object-oriented approach and hierarchical rule structure paradigm are briefly discussed. Finite element analysis packages (ALPID-2D) were incorporated into the program to give the simulation result of the forging process. The system can automatically produce a competent design and recommend a set of processing parameters for a given product. The designer can modify the design according to the result of the simulation.

Jan 1, 1992

By V. Reiter, K. Reinharter, C. Wenzl, D. Gregurek, A. Spanring

The refractory linings in lead furnaces are exposed to several stresses rather complex in their interaction. In the present study the magnesia-chromite brick out of a lead recycling furnace suffered from a high chemical attack by the process slag. The high CaO, BaO and sulfur bearing silicate slag, as well as a high NaO2 supply from soda resulted both in a deep-reaching infiltration of the brick microstructure and a severe corrosion of the brick components. Both the sintered magnesia and chromite were attacked chemically. The FactSage calculations showed the formation of high amounts of liquid phase in the infiltrated microstructure. Further phenomena affecting the refractory performance such as iron oxide attack, redox effects, and boron attack are also discussed in the paper. The obtained information and insights serve as a basis for improving refractory materials (i.e., choice of refractories for individual process and new developments) and consequently furnace operations.

Mar 1, 2017

By T. A. Larssen

The efficiency in production of manganese ferroalloys is dependent on the gaseous reduction of the higher manganese oxides in the ores used as raw materials. The materials, descending in the furnace, will meet the furnace gas that contains significant amounts of CO(g) and reduce in subsequent steps, the last step being reduction of Mn3O4 to MnO. This step may to varying extent occur at temperatures exceeding 800 °C, i.e. in the active region of the Boudouard reaction. The gas reduction of Assmang and Comilog manganese ores were investigated in CO-CO2-atmosphere at temperatures up to 1000 °C. It was seen that decreasing ore size correlates to a lower reduction temperature and increasing reduction rate. Similar effect was observed with increasing CO-content in the gas atmosphere. Further, it was found that Comilog ore obtained a complete prereduction at 600 °C, whereas reduction of Assmang ore was not complete at 800 °C for the majority of the experiments.

By Dachun Liu, Lei Shi, Yongnian Dai, Bin Yang, Yang Tian, Tao Qu

The carbonthermal reduction of high Mg–Si nickel laterite was studied under vacuum. The effects of adding calcium oxide and the reducing agent on the reduction of silicon in residue were studied at pressures of 10–200 Pa and different temperatures, with varying proportions of carbon and CaO. The analysis of the residue was performed using X-ray diffraction and chemical composition analysis. The results show the following: At 1350 °C with a C/O ratio of 1.5:1, the recovery of Si reached a maximum 71.09%. Under these conditions, Si exists mainly in the forms of Fe3Si, Fe2Si, FeSi and SiC. The recovery of Si was above 80% when the temperature was 1450 °C, the C/O ratio 1:1, and 15% addition of CaO. When CaO addition was 22.61%, all of the solid phase was Ca2SiO4.

Mar 1, 2017

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG, HUI XIAO

Carbonaceous refractory materials are widely accepted in many reducing smelting processes such as iron and ferroalloys. Oxidizing processes such as copper concentrate smelting traditionally use magnesia and/or alumina/silica refractory materials. The main objection to the use of carbon-based refractories as the exposed working lining in oxidizing applications is the potential for free oxygen to react with the carbon at high temperature, which could rapidly degrade the refractory lining. In 2013, Outotec and GrafTech conducted joint trials of a thermally conductive, carbonaceous lining for smelting copper concentrates in the Outotec® pilot-scale top-submerged-lance (TSL) furnace in Dandenong, Australia. This testwork had two equally important goals; to demonstrate the ability of carbon refractories to withstand oxidizing process conditions, while ensuring that neither furnace operating conditions nor process stability were negatively affected by the refractory material. The paper discusses the input parameters of the trials, key observations during the testwork program, and the results and conclusions from both process and refractory design standpoints.

Jan 1, 2016

By Junbiao Liu

Rutile is mostly produced from placer sands. Its beneficiation from primary deposits has rarely been investigated. However, there is interest in primary deposit because of the depletion of sand deposits. The Zaoyang deposit in China is the only rutile primary deposit currently mined. The plant employs a Tabling-Magnetic process which recovers only 20% Ti02 at a grade of 87%. This study shows that significant improvement on the recovery (52% at the same grade) can be achieved. This study includes a detailed mineralogical examination and the development of a processing flowsheet of the ore. The gangues are primarily amphiboles, garnets, zoisites, and chlorites. The liberation of rutile occurs at about 200 mesh. Gravitational, flotation, and magnetic separations are all employed in the process developed, depending on the mineral characteristics and experimental results. The flotations circuit utilizes benzyl arsonic acid to float rutile and sodium fluosilicate to depress the gangues. This is a new reagent scheme for rutile flotation.

Jan 1, 1989

By Kai Kang, Jun Bao, Shouping Liu, Xiao Sun

Powder characteristics have a significant influence on selective laser melting (SLM) process. In this research, particle size, surface contour and the microstructure of IN718 powder used in SLM were tested, and the physical and chemical changes during heating process of the powder were investigated as well. The shape characteristic and fluid properties of IN718 powder were defined and measured. It is shows that most particles of IN718 powder exhibited nearly spherical shapes, and the particle size is about 22.95μm. On this basis, IN718 sample was fabricated by SLM process using the powder and the microstructure of the fabricated sample was investigated. The results indicated that the sample has a dense microstructure, no macro-defects but a few micropores and porosity. Compared with the powder, there was no new phase formed in the sample and melting point of the sample was little less than that of the powder.

Jan 1, 2015

By Ritayan Chatterjee, P. K. Mukhopadhyay, Surajit Biswas, Dinabandhu Ghosh, Sandeep Agarwal

An Indian magnetite ore from the Nagaland region was characterized by powder X-ray diffraction, spectroscopies (ultraviolet-visible and Raman), high temperature magnetization and thermal analysis. A Rietveld refinement of the diffraction data revealed that the principal phase present in the sample is magnetite with partial substitution of Fe with Mg (mainly) and Cr, leading to the chemical formula of MgCr0.2Fe1.8O4. The UV-visible spectra of the sample in MeCN solution showed three distinct peaks. The lower region bands are due to metal-oxygen charge transitions and the other band is for d-d transition of iron. Raman spectral study at room temperature gave four characteristics bands of magnetite. The sample underwent a magnetic transition at high temperature and the thermomagnetization curve shows hysteresis during cooling cycle which indicates the possibility of first order structural transition at high temperature. The thermal property of the concentrate was studied by differential scanning calorimetric technique.

Mar 1, 2018

By Kevin Trumble, David Johnson, Kyungjean Min

The electrolytic manganese dioxide (EMD) production through electrodeposition from manganese nodules by reduction leaching in H2SO4 medium using sucrose as reductant followed by purification through 2-stage precipitation methods is described. The purified leach liquor was the starting solution for electrodeposition. Influence of in situ addition of a cationic surfactant Cetyltri-methylammonium bromide (CTAB) (0–500 mg dm −3) on the surface morphology and electrochemical properties of the EMD was examined. The XRD patterns of the deposited material were indexed to the c-MnO2 phase. FESEM results demonstrated that in the presence of CTAB uniform nanofibrous type grains were formed. Higher concentration of CTAB in the electrolytic bath however, drastically decreased the current efficiency (CE) and increased the energy consumption (EC) during electrodeposition. Under the optimum CTAB concentration of 100 mg dm −3 the obtained CE and EC values were 87.64% and 1.70 kWh/Kg respectively.

Mar 1, 2018

By W. K. Choi

Stainless steel exposed to wet environments at ambient temperature is subject to the formation of a surface biofilm. Depending upon the prevailing environmental conditions (dissolved oxygen, pH, Eh, concentration of cationic/anionic species), the biofilm may stimulate corrosion through formation of differential aeration zones and concentration cells. Corrosion significantly impacts the United States economy, since on a yearly basis, corrosion induced losses are estimated to be over $200 billion. A large portion of this corrosion is imputable to bacterial activity, and basic information is needed for a better understanding and control of the biocorrosion phenomenon. The present study has investigated the influence of Thiobacillus ferrooxidans in the corrosion of American Iron and Steel Institute (AISI) 304, 316 and 416 stainless steel samples. The formation of biofilm and microstructural changes on the surface of stainless steel samples and their weldments were assessed by microscopic examination, and the changes in the mechanical properties by stress-strain measurements. The significance of the results will be discussed.

Jan 1, 1993

By C. Lupi

In 1996 the Italian Agency for Environmental Protection (ANPA) has initiated a study of the environmental impact of the industrial sector of steel produced by Electric Arc Furnace (EAF). Within the framework of this study a hydrometallurgical process to treat EAF dusts was considered and developed. The paper describes the zinc and lead recovery from fumes coming from carbon steel production. The zinc extraction consists in acidic leaching followed by SX-EW steps. The leaching sludge containing lead sulfates was treated to obtain pure lead salt and inert solid residue. The whole process, that minimizes effluents by recycling the main liquid streams, has been developed to obtain marketable products. The solid waste, containing spinels, was subjected to elution tests in order to verify its compatibility with environmental regulation. The process, that has been set-up and tested in the laboratories of the University of Rome, will be transferred and studied on a pilot plant in order to assess its industrial and economical feasibility.

Jan 1, 1999

By Zuomei Jin

The Mineralogical form of Silver in a Ag-rich complex ore was determined. In the complex sulfide ore, acidic thiourea leaching resulted in 35% extraction of silver directly. In the same complex sulfide ore, under the effect of ultrasonic treatment, 65% of silver can be ex¬tracted. After the above ore had been roasted and acidically leached of Zn and Cu, the silver extracted from this Pb-Ag residue was 96.8%. The effets of temperature, thiourea and ferric ion concentrations and partical size were examined. The leaching rate of silver from the Pb-Ag residue was diffusion controlled. The activation energy was calculated to be 10. 49%KJ/mole. The kinetic model for the thiourea leaching of silver from Pb-Ag residue was obtained and is given by, The kinetics of silver cementation by aluminium in thiourea solutions was also investigated. The activation energy was calculated to be 65. 13KJ/mole, which is reasonable fora rate-limiting surface reaction.

Jan 1, 1995