By Lilong Zhu, Shaoda Zhang, Qian Wang, Shengping He

The effects of ZrO2, Y2O3 and Sc2O3, which are transition metal oxides, on the melting temperature, viscosity at 1300 °C, and break temperature of three mold fluxes (two weak-reactive type and one non-reactive type) designed for the high manganese and high aluminum steels, and one another conventional CaO-SiO2 based mold flux is studied. The results indicate that the melting temperature and viscosity increases slightly, and the break temperature increases dramatically with the addition of ZrO2, Y2O3 and Sc2O3 content in the conventional CaO-SiO2 based mold flux system. While, the addition of ZrO2, Y2O3 and Sc2O3 in the weak-reactive or non-reactive mold flux systems has a negligible in fluence on the melting temperature, viscosity and break temperature, suggesting that these transition metal oxides are possible to regulate radiation heat transfer without changing the basic properties of mold fluxes.

Mar 1, 2018

By Fiseha Tesfaye, Pekka Taskinen

"A thermodynamic study of the equilibrium phase assemblage AgBi3S5-Bi2S3-S was made by an EMF-technique, using the RbAg4l5 solid electrolyte. The ternary phase was synthesized from the pure Ag2S and Bi2S3 in an evacuated silica ampoule and grinded into powder and mixed with appropriate compositions of B12S3 and S, in a series of experiments, for pressing in to pellets. The pellets were assembled to form the galvanic cells Pt (-) | Ag ] RbAg4ls | AgBi3S5+ Bi2S3 + S + (C) I Pt (+). The EMF-measurements were made in the temperature range 299 - 460 K.In this paper, thermodynamic functions of the ternary phase AgBi3S5 (pavonite) have been determined. The agreement between the obtained results and the literature values were established.IntroductionThe complex group of ore minerals constitutes from trace amounts to a major proportions of sulfosalts. Although the sulfosalts rarely form massive ore bodies, they are commonly associated with rich sulfide ore minerals for the base and precious metals and widely distributed in a metal poor sulfide minerals [1]. For instance, Ag-bearing sulfosalts are encountered in ore minerals for the production of the base metals and are common sources of silver. Nevertheless, thermodynamic properties of the sulfosalts are poorly known.Reliable thermochemical data are essential for quantitative modeling of the chemical behavior of the sulfosalts in equilibrium with sulfides, which in turn would promote the optimization of complex minerals treatment and extractive metallurgy of the valuable metals."

Jan 1, 2012

By U. Kammer

The reduction of the lead content in the separator fraction produced during the mechanical processing of spent lead-acid batteries is an important environmental and economical issues. The reduction of lead down to less than 1 percent is very difficult using hydroseparators that are common in battery recycling facilities. Very promising results were achieved performing experiments on a test rig using a new technology in battery treatment: a discharge-type jigging unit. The materials is fed onto the jigging bed and transported through the machine. Due to the intensive movement of the feed, an additional washing effect is also obtained in addition to separation of the lead and plastic fractions. The knowledge gained from this development work at UVR-FIA GmbH in Freiberg, Germany, led to a patent application. This paper focuses on the results of the development work and the start-up and one year's operation of the industrial-scale application at Harz-Metall GmbH in Goslar, Gennany.

Jan 1, 2000

By Pedro A. Netto, Giulio R. Altoé, Sergio N. Monteiro, Ygor M. Moraes, Frederico M. Margem, Gabriel O. Glória

Since environmental issues are becoming more and more important Worldwide. Nowadays, Natural fibers are been used to substitute the synthetic ones. Although PALF fiber is an important natural fiber and its mechanical Properties surpass in various aspects some other lignocelluloses fibers, such few studies have been conducted with the fiber obtained from leaf of PALF plant. In order to better evaluate the mechanical properties and possible applications, this paper aims to improve the elastic modulus of the PALF fiber by Weibull statistics, by evaluating their mechanicals properties and possible applications. The fibers were divided in diameter intervals and the tensile strength and elasticity modulus were measured in each range. The fractured surface was examined using scanning electron microscopy. The results, interpreted by the Weibull statistical method, showed a correlation between the fiber elastic modulus and its diameter.

Jan 1, 2015

By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By Henrik Gudbrandsen, Anne Støre, Ana Maria Martinez, Karen Sende Osen, Ole Kjos

The light rare earth metals Nd, Pr, La, Ce as well as some alloys with Fe, are today produced in China by electrolysis in molten fluorides using oxide raw materials. A major challenge is to obtain a good cell operation without de-composing the electrolyte leading to emissions of per fluorinated carbon (PFC) green-house gases to the atmosphere. This work is focused on understanding the fundamental requirements to run the electrolysis cells for DyFe alloy production in an ef ficient and environmental friendly way. Electrolysis experiments was carried out in DyF 3-LiF melts at 1050 °C. A Fe rod was used as consumable cathode and the (consumable) anode was made of graphite. To establish at which anode potential PFC occurred and thus enabling optimisation of the oxide batch feed rate, analysis of the anode gases was performed with Fourier Transform Infrared Spectrometer (FTIR). The produced DyFe alloy was characterised by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS).

Mar 1, 2017

By José Carlos D?Abreu

The Tecnored process is a new ironmaking technology, developed on a unique approach that combined empirical and theoretical knowledge backed by extensive tests carried out in a dedicated pilot-plant and with close support of universities and research centers. Campaigns in the pilot-plant focused on operate different reactors of different sizes, including a full size slice of the industrial furnace. This approach provided actual conditions to develop the main features of the process such as the internal dimensions, raceway pattern, thermal and gaseous profiles, etc, besides provide reliable data to feed and calibrate a specific mathematical process modeling. This paper presents the first computer model used by the Tecnored technical staff, focusing the behavior of a self reducing agglomerate in the upper shaft of the furnace (zone of solid state reduction). Some results of this model are given and discussed.

Jan 1, 2006

By Byung-Su Kim

The reaction between calcium sulfate and hydrogen is of interest both as a means of regenerating calcium sulfide as a reductant of sulhr dioxide to elemental sulhr and for producing elemental sulhr from gypsum. This reaction was investigated using a thermogravimetric analysis technique in the absence and presence of nickel catalyst. The reaction temperature was varied between 973 and 1153 K, while the hydrogen partial pressures of 12.9 - 86.1 kPa were utilized. At 1073 K and a hydrogen partial pressure of 86.1 kPa, 60 % of the original calcium sulfate in the absence, and 95 % in the presence, of the nickel catalyst was converted to calcium sulfide in one hour.

Jan 1, 1999

By R. G. Robins

The effective removal of arsenic(V) from process streams and waste waters by precipitation with excess iron(II1) is sometimes attributed to the formation of basic ferric arsenates. The authors have investigated this system extensively using a variety of techniques and conclude that the solid phase produced is iron(II1) oxyhydroxide (ferrihydrite) with arsenic(V) adsorptively bound to the 2-3 nm particles.

Jan 1, 1992

By Hidefusa Takahara, Koichi Miyake, Dierk Raabe

"Mechanical properties of copper wires were examined. The copper wires containing 5-10 mass % chromium and 1-3 mass % silver were produced through heavily cold deformation. It was expected that the copper wire was easily fractured during cold deformation because of the existence of brittle chromium phase in the alloy. In fact, the copper wire was fractured due to large work hardening, when the true strain [n] exceeded 5. However, the copper wire annealed at 1273K for 6 ks ·in the middle of deformation process could be smoothly drawn to 11=8. After precipitation treatment for silver phase at 473k for 1.8 ks, the wire was able to further drawn to n=8.4. The final deformed wire showed tensile strength higher than 1200MPa.IntroductionDownsizing of electronic devices has led to the demand of finer and higher strength materials for cables. Conventional copper alloys have about 800MPa in ultimate tensile strength. These strength are mainly obtained by precipitation hardening. Nowadays, a process for higher strength wire has been developed, where dual phase copper alloy is used. When it is drawn heavily, the' second phase is elongated along drawing direction and the wire gets high strength due to fiber reinforcement (1). That alloy is so called in-situ formed fiber reinforced ·alloy. Cu-Ag(2), Cu-Nb(3) and Cu-Cr(4) systems are well known as such alloys. It is also well known that chromium is brittle material except single crystal and high purity of chromium. However, Mihara et al. C5l have achieved 1 GPa in ultimate tensile strength in the Cu-Cr-Zr and Cu-Cr-Ti alloys by appropriate thermo-mechanical processing.In this study, the Cu-Cr-Ag systems were investigated: The alloys contained 10 or 5% chromium and 3 or 1 % silver. It was demonstrated that silver precipitated in copper matrix contributed on further hardening."

Jan 1, 2000

By Fuqiang Zheng, Yufeng Guo, Guanzhou Qiu, Tao Jiang, Xiaoming Qu

MxTi3-xO5 is the main titanium-bearing mineral in the titanium-bearing electric furnace slag (TEFS), which is produced by direct reduction-electric furnace smelting process with vanadium titanomagnetite concentrate in Panzhihua-Xichang region of China. In order to effectively utilize the titanium resource in TEFS, the thermomechanical analysis and conditions for the growing up of MxTi3-xO5 grain were investigated, which emphasized on the effects of CaF2 and cooling rate on the crystallization of MxTi3-xO5 in the melting process. The mineral phase and morphology of titanium-bearing slag were determined by XRD and electron microscope technique, respectively. The results indicated that the average grain size of MxTi3-xO5 grown up from 30 to 92 lm and the area fraction of MxTi3-xO5 reached about 66% from 61% under the conditions of 5 wt% CaF2 and cooling rate at 1 °C/min.

Mar 1, 2017

By Yang Hai-long, FAN Gang, LI Cun-xiong, WEI Chang, LI Min-ting, LI Xing-bin, DENG Zhi-gan

Hydrothermal sulfidation of pure cerussite with elemental sulfur has been reported in the present paper. The variables considered in the study were temperature, time, particle size and elemental sulfur fraction in the reacting mixture. Temperature was the most important factor at temperatures above 180 , PbS and PbSO4 were the only stable reaction products in the sulfidation of cerussite. The experimental data indicated that under the hydrothermal conditions with a particle size of -74+58 μm and sulfur fraction in reacting mixture of 15% at 200 °C for 120 min, and 92% of lead sulfidation rate was achieved.

Jan 1, 2016

By J. M. Shneerson

At Gipronickel Institute a technological flowsheet of pressure leaching of copper from rich copper concentrates (i.e. containing: Cu -59-75%; Ni -D.5-4.64%; Fe -D.2-J.3%; S -21.8-26.9%) was developed. As a result, the possibility of deep decomposition of copper-containing minerals with extraction of elemental sulphur (up to 90-95%) was established. The obtained sulphur concentrates contain 80-90% of elemental sulphur, which can be separated from sulphide residue through autoclave melting and settling. As a rule, sulphide concentrates remaining after extraction of sulphur contain up to 1-2% of noble metals. The sulphide concentrate can be purified to the level of rich concentrates or pure metals using the well-known methods as in the case of tankhouse slimes. The presented research specifies the parameters of main operations: pressure leaching and sulphur extraction. It was established that 98% of copper could be transferred into solution at temperatures of 108-1 10°C and oxygen partial pressure 0.4-0.6 MPa. Experiments were carried out in autoclaves of various volumes using the products of nickel matte processing.

Jan 1, 2003

By R. H. Rubisov

Sulphuric acid pressure leaching of nickeliferous laterites has attracted considerable attention from the nickel industry during the past five years. The process is especially advantageous for limonitic laterites that mostly contain goethite, because iron precipitates releasing acid and thus rendering low acid consumption. It is also applicable to mixtures of limonites and saprolites, although at higher acid consumption due to magnesium. Effective process design requires the solubility of metals that precipitate during the process to be known. In the present work, determination of metal solubilities is based on a simple speciation program that assumes the presence of only one dominant complex for each metal. The thermodynamic data for the precipitation reactions are extracted from high-temperature experiments with monometallic systems published previously. The validity of the approach is then tested against mixed bimetallic systems, and finally applied to calculate the solubility of aluminium, iron and magnesium in laterite leaching effluents "at temperature". In both cases of limonitic feed and limoniticfsaprolitic blends, the prediction closely follows metal solubilities measured experimentally at temperatures from 230 to 270°C and at terminal he acidities ranging from 10 to 75 g/L.

Jan 1, 1999

By P. N. Anyalebechi

The effects of application of steady and pulsed electric current on the cast microstructures of ingots of a 7050 type aluminum alloy have been experimentally investigated over a solidification rate range of 0.1-10 K/s. This involved the application of an electric current of 465-930 mA/cm2 of melt surface area to laboratory-size ingots solidified in a unidirectional manner. Within the ranges of electric current density and solidification rate investigated, the applied electric current reduced the average dendrite, grain, and second-phase particle size. It also made the size distribution of the second-phase particles more uniform. The mechanism for the observed refinement of the cast microstructure by the applied electric current is not well understood. The potential effects of heat-induced local convections, shear stress-induced fragmentation of dendrites, increased temperature gradient due to Joule heating and the thermal and constitutional supercooling engendered by Peltier, Thompson, and Joule heating are discussed.

Jan 1, 2009

By Jean-Christophe Gebelin, Mark Jolly, Samantha Jones

"The de-waxing process in investment casting is truly a black art which is carried out in a black hole - the autoclave. The process involves exposing wax, coated by a porous ceramic shell, to steam at a pressure of 10 bar and a temperature of about 180°C. The processes which then occur are truly multi-media and multi-physics. Steam condenses in the porous ceramic, wax melts and flows, the shells expand and sometimes crack. Why the shells crack is one of the most difficult questions asked in the industry.Modelling and validating the de-waxing process is not simple. The IRC at the University of Birmingham is attempting to model this process using Physica+ a code developed in the UK. This paper will present the latest results in this attempt to model one of the casting industries most intractable problems.IntroductionThe de-waxing process using an autoclave involves the following physical phenomena:· Flow of the steam in the autoclave;· Heat transfer from the steam to the wax, possibly through the shell;· Melting and flow of the wax.At the same time, other phenomena may occur, such as the flow of the steam through the shell, the condensation of the steam on the shell surface and on the wax pattern surface, the flow of wax the through the shell, etc ...This shows how complex the de-waxing process is from a physical point of view. The main defect that appears during this process is the cracking of the shell. Previous modelling work carried out by Snow [1] has shown that it is possible to predict the stress in the shell, making numerous assumptions. In this paper, the modelling to predict the state of stress in the shell that is currently in development at the University of Birmingham is presented together with the presentation ofthe physical phenomena to model and the assumptions used. The parameters that are needed in such models will also be discussed, and some experimental work undertaken at the moment presented."

Jan 1, 2001

By Cheng Pan, Xuewei Lv, Guibao Qiu, Chenguang Bai, Meilong Hu

"Physic-chemical properties of slag at high temperature play an important role in the pyrometallurgical process of production of ferronickel alloy. It determines the operation efficiency, metal recovery ratio, energy consumption and the distribution of elements like S and P between the slag and metals. In the present work, the effect of MgO content in the slag on melting features and viscosity of the slag was investigated. The MgO content in the SiO2-CaO-MgO-Al2O3 -FeO in the quinary slag system varied from 14.5% to 22.5%. The results shown that all slag samples begin to softening at the same temperature, the softening temperature, melting temperature, flowing temperature decrease with the increase of MgO content when the MgO content is in range of 14.5 and 20.5 pct mass, and when MgO content up to 22.5 percent, the temperatures increase sharply. Besides the inflection point temperature of viscosity-temperature curve increase with the increase of MgO when the MgO content is in range 16 and 22.5 pct mass.IntroductionNickel is very important to modern society, without it, we would not be able to share many things in our daily life, such as airplanes, computers and many stainless steel appliances in our homes and workplaces1.. It is the essential element of the stainless steel making, and about 65% of the nickel consumed in the world is used to make stainless steel2., so with the increase of stainless steel, the nickel production and demand has continued to increase3.Nickel is produced from two distinct ore types: nickel sulfide deposits and oxide nickel laterite deposits. The great majority of world’s known nickel resources are contained in laterite deposits3.. The laterite ores are normal classified into two groups: the high-iron laterite ore and high-magnesia laterite ore1. Typical composition of high-magnesia laterite ore is in the range 1-3%, and these ores are suitable for pyrometallurgical process to produce ferronickel4."

Jan 1, 2012

By D. Death

The Tapping Camera Prototype (TCP) is an instrument being developed to record and analyse video of the molten metal stream entering a tapping crucible as it is tapped from an aluminium reduction cell. The development aims to provide potroom floor operators with continuous real time vision of the tapping process and provide an alert in the event of excessive bath contamination in the extracted metal stream. Longer term the system may provide sufficient data to enable control of the tapping process. The TCP mounts a wireless camera and periscope to view the molten metal stream via a peephole in the tapping crucible. Real time video is recorded to either digital video tape or computer disk for subsequent video analysis to quantify the bath material drawn into the tapping crucible with the molten aluminium. The images transmitted by the camera are available on a handheld LCD video screen. This work is an initiative of the CSIRO?s Light Metals Flagship.

Jan 1, 2006

By Shawn A. Cefalu, Matthew J. M. Krane, Kent J. VanEvery

"Segregation during electroslag remelting (ESR) of a nickel-chromium-molybdenum alloy (Ni-8 wt% Cr-25 wt% Mo) has been modeled. Features of the model include species transport and AC electromagnetic effects coupled with fluid flow, heat transfer, and solidification. The effect of varying ingot diameter and melt rate, on macrosegregation patterns, local solidification time, and liquid pool profiles obtained from this model are demonstrated. The results show that the macrosegregation in the ingots correlates to the filling velocity.IntroductionElectroslag remelting (ESR) is a secondary melting process used to refine the chemical composition and the microstructure of metals. Macrosegregation of solute elements causes defects in ESR ingots, including freckles and the maldistribution of phases. These defects are not correctable through heat treatment due to the large length scales over which they occur. However, the frequency and distribution of these defects may be minimized, or even prevented, through process control based on an understanding of the conditions that lead to their formation.In the past, studies have been conducted on the effect of the process parameters on the shape of the melt pool and the thickness of the mushy zone [1-7]. In these studies, the shape of the liquid pool is determined by consideration of the heat and fluid flow induced by electromagnetic (Lorentz) force and thermal buoyancy. The transport of solute and the resultant solutal buoyancy effects were not considered in these macroscopic models. Defect formation is tied to formation of secondary phases (e.g., freckling and white spots in nickel superalloys) [5,8]. In cases where secondary phase formation is calculated (e.g., [6]), phase fractions are determined using a micro-scale model given the local solidification time (LST) and local thermal history from the macroscale model.Using the local thermal history from the macroscopic transport model to predict microstructure increases the importance of the accuracy of those results. This investigation models the macrosegregation of molybdenum during the ESR of a Ni-Cr-Mo alloy. The effect of macrosegregation on pool shape and depth is demonstrated, along with its effect on the local solidification time. By comparing the relative effects of the melt rate and ingot radius, a better understanding of the factors that affect macrosegregation, and ultimately secondary phase formation may be obtained."

Jan 1, 2004

By Tiejun Chun, Jian Pan, Deqing Zhu, Zhiyong Ruan

"In this paper, the desulfuration of pyrite cinder pellets was carried out. Phase analysis shows that most sulfur of pyrite cinder exists in the form of elementary sulfur. Most sulfur was removed in preheating stage. 81.25% sulfur was removed and the average SO2 concentration of exhaust gas was 1365ppm when the pellets were preheated at 950oC for 9 min. The final product, assaying 62.42wt%Fe and 0.02wt%S content at 96.88% desulfuration was achieved under the conditions of preheating at 950? for 9 min and roasting at 1200? for 15 min, which can be used as the burden for blast furnace.IntroductionPyrite cinder, as a subsidiary product of sulfuric acid production by roasting of pyrite ores, was solid waste in sulfuric acid enterprises. According to the statistics, the annual production of pyrite cinder is about 15 million tons in China. Besides, there is lots of pyrite cinder deposited for many years [1-3]. The pyrite cinder consumed in the cement and other industries as auxiliary additives only accounts for less 30% of its total discharge and the left is stored in waste pond, occupying much land and polluting environment in China [4-5]. Moreover, pyrite cinder contains iron between 30-63% which can be utilized as a cheap raw material for ironmaking by sintering or pelletizing processes, which can not only prevent pollution but also provide cheap raw materials for ironmaking [6-7]. However, compared to traditional iron ore concentrate, pyrite cinder possesses higher sulfur content."

Jan 1, 2012