By Yu-ki Taninouchi, Toru H. Okabe

Among platinum group metals (PGMs), Pt, Pd, and Rh are the essential constituents of automotive catalysts. Recovery of PGMs from catalyst scrap is important, but it is difficult because PGMs are chemically stable and are present as minor components in the scrap. A vapor treatment method using FeCl2 vapor to alloy PGMs with iron, enabling subsequent magnetic separation, is developed and tested on Pt, Pd, and Rh wires.

Mar 1, 2017

By A. V. Kuznetsov, R. I. Kamkin, V. M. Paretskiy, A. Y. Mamaev, V. P. Bystrov, A. S. Vernigora

"Vanukov furnace technology is an efficient, proven pyrometallurgical injection technology, used extensively in Russia and Kazakhstan for a number of different applications. The technology was most widely adopted for processing copper sulfide concentrates for matte in smelters in Norilsk, Revda (Russia) and Balkhash (Kazakhstan). The following applications also were developed and tested at industrial scale: treatment of sulfide lead and lead-zinc concentrates, laterite nickel ore, production of cast iron, treatment of antimony gold-containing ores, and municipal solid waste. In this paper, current experience of Vanukov furnace application to these technologies is described with a number of general development trends and new areas of application.IntroductionAt the present time, the Vanukov process, developed at the Moscow State Institute of Steel and Alloys at the Department of metallurgy of non-ferrous, rare and noble metals with collaboration with other research organizations, is a highly efficient technological solution for processing different kinds of raw materials. The process was invented by Professor Andrey Vladimirovich Vanukov, whose research work began in 1949. From 1956 to 1975 test runs of the technology were carried out at the smelters in Norilsk and Balkhash. In 1976 a pilot Vanukov furnace was built in Ryazan. Furnace designs was modified to suit the various test programs. A major objective of each experiment was the determination of optimal working conditions for processing different types of raw materials such as copper, copper-nickel, copper-zinc, lead or pyrite concentrates, and materials containing secondary lead and zinc. After the death of Andrey Vladimirovich Vanukov in 1986, this technology and furnaces based on the technology were named after him: “Vanukov process” and “Vanukov furnace”. Today, the following furnaces based on Vanukov technology are either working or were tested at semi-industrial scale: three in Norilsk, two in Revda (Russia) and two in Balkhash (Kazakhstan) for treatment of copper sulfide concentrates for matte, one in Orsk (Russia) for processing laterite nickel ore, one in the Buruktal plant (Russia) for antimony gold-containing ores for antimony oxide sublimates and gold-containing metallic antimony, and one in China for processing sulfide lead and lead-zinc concentrates for production of black lead and zinc-containing sublimates."

Jan 1, 2011

By D. M. Hausen

A computer program has been developed by Newmont Exploration to convert mineralogic data by XRD into rock type and ore type classifications. This method has proven useful in identifying lithology from cuttings samples, where percussion drilling was an alternative to expensive core drilling. Computer printouts of rock type and ore type identifications can be generated simultaneously with mineralogic analyses, resulting in a considerable time savings in manual calculation. XRD-computer logging was first applied to the Carlin mine in north central Nevada, and later to the Maggie Creek and Gold Quarry gold deposits, southeast of the Carlin mine. Impure Paleozoic limestones of the "lower plate" Roberts Mountain Formation and the "upper plate" transitional facies have been decarbonatized to altered siltstones and shaley units along vertical faults and permeable stratiform horizons. Advanced stages of decarbonatization were accompanied by silicification. Quantitative XRD data are initially sorted into principal rock type units (limestones, siltstones, dolostones, shales) based on major mineralogic components (calcite, quartz, dolomite, clays). On the basis of relative amounts of less major constituents, descriptive subclassifications (dolomitic limestones, dolomitic siltstones, argillaceous cherts) are made. XRD lithologic data provide assistance in correlating lithologic units, and delineating favorable replacement horizons associated with gold mineralization.

Jan 1, 1982

By Toshihide Takenaka, Takashi Matsui, Nao Murakami, Masahiro Kawakami

"Electrowinning of Ti have been investigated in a LiF-NaF-KF melt including K2TiF6 at 773-923K by applying electrochemical oxidation ofH2 gas as an anodic reaction. The cathodic behavior of titanium and the anodic behavior of H2 gas were studied by voltammetry in detail to clarify the electrolytic condition for the process. The electrowinning of Ti was carried out by potentiostatic _electrolysis. Steady electrolysis was achieved under the suitable electrolytic condition without breaking out the anode effect. Titanium metal was electrodeposited on a Ti cathode though the deposits were usually powdery. It is concluded that this process is potential if the morphology of the deposit can be improved.IntroductionTitanium has such good properties as high specific strength and high corrosion resistance. However, the availability of Ti has been limited because the price of Ti is much higher than those of other common metals, such as Fe and Al. The production process of Ti ingot from its ore is rather intricate so that the production cost is high. If the simpler process is developed, the production cost should be retrenched. Titanium metal is usually produced by the Kroll process, which consists of the electrowinning of Mg metal in molten salt and the chemical reduction of TiCl.i by Mg metal. The Kroll process is very elabrate, but not simple. Because the chemical reduction ofTiCl4 by Mg metal is highly exothermic, a considerable amount of energy is wasted.Titanium metal can be electrowon in molten salt bath in principle. A simpler and more effective process than the Kroll process may be realized by the direct electrowinning so that the electrowinning of Ti metal has been studied widely[ 1]. Some researchs progressed to a pilot plant stages [2], but the electrowinning of Ti has not been industrialized yet."

Jan 1, 2000

By Huang Kai

By adding the solid oxalate acid powder into the solution of nickel chloride or its ammonia coordinated solution, the uniform compound particles were prepared and the precipitated particles were transferred to the mono-dispersed NiO particles by calcination. In this study, the various experimental conditions were investigated, the characteristics of the corresponding obtained particles were analyzed, and the formation mechanism of the particles was elucidated. It was found that the solid oxalate acid provided the solid-solution interface for the precipitation and induced the nucleation and growth of the product particles.

Jan 1, 2005

By S. Sundarraj

The morphological transition between columnar and equiaxed structures is an important solidification phenomenon frequently observed in castings, especially complex parts with varying cross-section, The mechanical properties and the occurrence of defects such as hot tears are strongly dependent on the structure formed in the casting. Hence, it is important to understand the conditions leading to columnar or equiaxed structures. Although extensive work has been done in modeling solidification systems, almost all of the existing models are based on the assumption that the structure formed in the casting is either purely columnar or purely equiaxed. Prediction of the columnar-equiaxed transition (CET) requires a solidification model which accounts for the formation of both columnar and equiaxed structures, along with related microscopic and macroscopic solidification phenomena. In this paper a CET model is presented which: (i) takes account of both columnar and equiaxed structures, (ii) accounts for macroscopic heat transfer coupled with microscopic phenomena such as nucleation, growth and microsegregation, (iii) satisfies solute conservation, and (iv) is easy to implement in commercial finite element and finite difference software. The proposed model predictions of CET have been validated with available experimental results for a uni-directional solidification of an aluminum-copper alloy. A sensitivity analysis has also been carried out to determine the effects of various parameters on the CET model predictions. The model is being extended to other alloy systems and more complex geometries. This work will be published in due course.

Jan 1, 1996

By Dao-Wu Yang, Ju-Lan Zeng, Li-Xian Sun, Yan Yao

"The hydration heat of the pure cement, the fly ash single-dopped cement, as well as the fly ash and fluorgypsum co-dopped cement were investigated by means of micro-calorimety with an eight-channel micro-calorimeter (TAM Air). The results showed that the hydration heat and the hydration rate could be reduced significantly by fly ash and fluorgypsum. However, the reduction was not proportional to the loading of dopant. The exothermic peak of the fly ash and fluorgypsum co-doped cement was appeared earlier than the fly ash single-doped cement. As the temperature decreased, the hydration heat and the hydration rate of the doped cement were reduced, and the exothermic peak appeared later. The effects of fly ash and fluorgypsum on the compressive strength of cement were also investigated. The results revealed that the early compressive strength of concrete made up of the co-doped cement was largely higher than that of the fly ash single-doped cement. Based on the experiment results obtained in this paper, we could conclude that fluorgypsum is a suitable additive for fly ash-doped cement.IntroductionFly ash and fluorgypsum are industrial waste. In 2008, nearly 400 million tons of fly ash has been produced by coal-burning power plants in China. And it is estimated that this number would exceed 500 million at the year of 2015. Besides, every year the fluoride salt factories in China discharge more than 100 million tons of fluorgypsum. Tremendous of fly ash and fluorgypsum occupy considerable land and contaminate air and water sources [1]. As a result, comprehensive utilization of this two industrial waste has draw great attention from all over the world.Cement is the most-used construction material on earth. But the production of cement consumes huge energy and destroys the environment. This problem might can be partly solved by applying fly ash and fluorgypsum as additive for cement [2-4]. During the last decade, some papers that focused on applying fly ash and fluorgypsum as additive for cement have been published [5, 6]. However, to the best of our knowledge, none of these papers investigated the hydration heat of the fly ash and fluorgypsum co-doped cement.The hydration of cement is an exothermic reaction, which can result in serious problem for mass concrete: The interior of the concrete could reach very high temperature as the hydration proceeded [7-9]. As a result, the great temperature difference between the interior and the outer of the concrete would exist and cause serious thermal stresses. Thus, the concrete would be destroyed by the cracks which in tum are resulted from the thermal stresses [10, 11]. The heat released by the cement hydration and the hydration rate is commonly regulated by adding mixed materials or transferring additive such as fly ash and fluorgypsum [12-14]."

Jan 1, 2011

By Kumar M. Lyer

Residence time distribution (RTD) of light and heavy liquids in a pyrometallurgical channel reactor was mathematically modeled by representing the reactor as a combination of ideal reactors. Cold model studies simulated the counter-current flow of slag and matte (or metal) with high-strength bottom gas injection. The experimental variables include flow rates, heights, density and viscosity of the two liquids; gas flow rate; injector diameter; and distance between injectors. The experiments covered a wide range, of the appropriate dimensionless parameter, including conditions in ferrous and nonferrous extractive metallurgy. Dispersion modeling studies were also carried out to determine the degree of backmixing. Results indicate that the degree of backmixing in the channel reactor for various operating conditions corresponds to that for 3-20 perfectly mixed reactors in series.

Jan 1, 1993

By Jayagopal Uchil, M. Krishna, Shanta Sastcy

"Damping behaviour of aluminite particulate reinforced ZA-27 alloy metal matrix composites processed by compocasting method is studied. The weight percentage of particulate reinforcement is 0,1,2,3, and 4%. A dynamic mechanical· analyzer is used ·to measure the damping capacity and dynamic modulus at the natural frequency of the specimen over a temperature range of 30°C to 300 °C both in the heating and cooling cycle. The damping capacity of the material is found to increase with increase in temperature and weight percentage of aluminite reinforcement although this is accompanied by a decrease in dyliamic modulus.The damping capacity and dynamic young's modulus exhibit a sharp decrease in their values around 300 °C a8 ZA-27 alloy undergoes a first order phase transition in this region which is confirmed by Differential scanning calorimetric studies. Several damping mechanisms have been evaluated theoretically for the material under study. The damping capacity at low temperatures is attributed primarily to coefficient of thermal expansion mismatch induced dislocations and high intrinsic damping of the matrix. At higher temperatures the damping capacity is attributed to ZA-27/aluminite interface, phase transformations and thermoelastic damping.IntroductionMetal matrix composites. (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and lightweight [1-5]. At present, the usage of ceramic particles as reinforcement in MMCs has attracted considerable interest from scientists and engineers. The MMCs show substantially improved elastic modulus, strength, stiffiless, and tribological properties with low coefficient of thermal expansion compared with the unreinforced matrix material."

Jan 1, 2000

By Rodney L. Williamson

Optimal estimation theory has been applied to the problem of estimating process variables during vacuum arc remelting (V AR), a process widely used in the specialty metals industry to cast large ingots of segregation sensitive and/or reactive metal alloys. Four state variables were used to develop a simple state-space model of the V AR process: electrode gap (G), electrode mass (M), electrode position (X) and electrode melting rate (R). The optimal estimator consists of a Kalman filter that incorporates the model and uses electrode feed rate and measurement based estimates of G, M and X to produce optimal estimates of all four state variables. Simulations show that the filter provides estimates that have error variances between one and three orders-of-magnitude less than estimates based solely on measurements. Examples are presented that verify this for electrode gap, an extremely important control parameter for the process.

Jan 1, 2001

By David J. Krichten

A method of retrofitting air-fuel burners with oxy-fuel capability overcomes the potential problems associated with oxygen combustion in aluminum melting furnaces. The retrofit burner uses the existing combustion air connection, burner housing, and burner tile and replaces the gas tube with an oxy-gas burner. Maintaining a portion of the air flow to the burner reduces the potential for localized overheating. Proper design of the burner reduces NOx emissions by moderating the flame temperature with furnace gas recirculation. Economic analysis of using oxygen shows the benefits are increased productivity and reduced overall unit cost of melting. In practice, the melt rate in rotary furnaces increases by up to 50% and by up to 35% in reverberatory furnaces. Oxygen utilization reduces total melting cost by 112-314 cents per pound of aluminum melted.

Jan 1, 1997

By Kazuyuki Kakegawa

The sintering characteristics and the change in the compositional distribution in the PbTiO3-PbZrO3-Pb(Mg1/3Nb2/3)O3) system during the sintering process by spark plasma sintering (SPS) method were examined. They were compared with those by a normal sintering method. The densifieation by the normal sintering was slow even at high temperatures. When SPS method was employed, much lower temperature and shorter period resulted in sintered bodies having almost the theoretical density. As expected in normal sintering, the compositional distribution decreased as the sintered density increased. On the contrary, the change in the compositional distribution by SPS was much smaller than that in the normal sintering. This sintering characteristic of SPS suggested a possibility of fabrication of sintered material having a desired compositional distribution.

Jan 1, 2003

By Niko Hellstén

To capture efficiently the valuable trace metals from nickel slag using electric furnace, it is important to study their distributions between the slag and metallic phases in the furnace. It is impossible to calculate accurately these distributions without experimental measurements. Therefore, in this work, selected trace metal distributions and phase equilibria between K2O containing iron-silicate slags and a metallic Ni-Fe-Cu alloy in nickel slag cleaning furnace conditions were studied. The experimental method developed and applied during the work, involved a modified quenching technique that included equilibration of the samples in semi-sealed quartz ampoules in an inert atmosphere and metallic Fe saturation. The use of the semi-sealed quartz ampoule prevents the escape of volatile elements from the sample during equilibration. Chemical compositions of the phases and the trace elements were analysed by EPMA. From the measured compositions, the trace metal distribution coefficients between the molten Ni-Fe-Cu alloy and slag were calculated.

By Vaughan R. Voller

"The wide range of length and time scales found in solidification processes are outlined and discussed. Methods for Direct Microstructure Simulation (DMS) are introduced. Key features in sharp interface and phase field models are presented. Concepts in micro-macro solidification modeling are covered. Basic details of microstructure and segregation models are provided. A description of a recent segregation micro-macro model is presented in detail.IntroductionA solidification process involves the containment of a liquid region, which, due to cooling, transforms over time to form a fully solid product. The development of the solid microstructure and the segregation of solute components during this transformation are controlled by phenomena that occur across a wide range of length and time scales. A ""successful"" model of a given solidification process needs to account for these phenomena. Standard models of solidification employ a discrete grid of node points and associated volume elements in the special domain, with a discrete time step to track the transient changes of nodal values, describing the composition and microstructure. Through the use of such models significant progress has been made towards a complete understanding of solidification process and phenomena (see the conference proceedings in Refs [1-9]). As solidification models become more sophisticated, however, they all run into the problem of resolving the full range of disparate space and time scales.Two approaches can deal with this problem1. Direct Microstructure Simulation (DMS) where the grid size and time step are chosen to scale with the smallest length and time scales of the given problem.2. Micro-macro modeling where the grid size and time step scale with the macroscopic process scale and phenomena at smaller scales are accounted for via sub-grid modeling and volume averaging.Currently full DMS of solidification is beyond the reach of available computer power and the application and development of micro-macro models is an important and critical research area."

Jan 1, 2001

By Mansoor Barati, Yindong Yang, Yonggang Wei, Bo Li, Alexander McLean

Reduction roasting followed by magnetic separation is an important method for treating laterite nickel ores. In this work, garnierite type laterite ore from Yunnan province in China was reduced by methane under different conditions followed by magnetic separation to obtain the ferronickel concentrate. The phase and microstructure transformations of garnierite in the reduction process were investigated using XRD and SEM-EDS. The experimental results showed that reduction temperature from 873 to 1173 K had only a small effect on content and recovery of nickel and iron. The content and recovery of nickel and iron in the concentrates increased slightly with prolonging reduction time. In addition, the nickel and iron content decreased with increasing methane concentration, but the recovery of nickel and iron increases. A decrease in the iron content and recovery were observed when the dosage of sodium sulfate varied from 5 to 20% at a temperature of 1073 K and reducing time of 90 min, while the nickel content and recovery gradually increased.

Mar 1, 2018

By Anat Deepatana

Bioleaching of nickel laterite ores is the extraction technology based on the use of heterotrophic micro-organisms and their organic acid products to dissolve metals from oxide minerals. This study examined the chemical leaching kinetics of limonite and nontronite ores with metabolites including citric, lactic and malic acids. The leaching process was found to follow the chemically controlled model. The leaching kinetics was found to be significantly influenced by the acid strength or dissociation of acids in solution. Although increasing the acid strength increased the rates of leaching, this trend was not indefinite. An optimal acid concentration that defined the fastest leaching rates was identified for each acid. The amenabilities of the minerals hosting the nickel and cobalt in limonite and nontronite to organic acid leaching were also established.

Jan 1, 2006

By Peter V. Barr

Despite the advent of modem firing control systems reheating furnace operations frequently allow significant thermal excursions in the discharged slabs or billets after furnace delays. Although HSM furnaces are not immune to this and other related problems, mini-mill operations are most vulnerable due to their more frequent delays and (often) less sophisticated control systems. In order to reduce these problems control systems will commonly include a thermal model, operating either on-line (interacting directly with the controller logic) or in an advisory, off-line mode. Using a new 'fast' thermal model, the paper examines the thermal response of a typical mini-mill furnace during both delays and the subsequent recovery period. A variety of firing strategies are explored and compared on the basis of maintaining thermal excursions within allowable limits for rolling. Other factors, such as the potential for overheating of billets within the furnace during delays and the overall thermal state of the furnace, are also considered in some detail. Although common practice, the use of conventional thermocouple zone temperatures for furnace control during and after delays is shown to be a dubious proposition. Keywords: Reheat Furnace, Modeling, Process Control

Jan 1, 2003

By C. F. Feng, L. Froyen

"In-situ processes have emerged as new and promising techniques for metal matrix composite fabrication. They offer significant technical and economic advantages over conventional processing. One of the in-situ processing routes that have been used is reactive free sintering of a mixture of powder reactants. However, materials synthesised via this route are always porous because of density differences between reactants and products. An example are the porous Al/(TiB2+Ah03) MMCs obtained by heating powder mixtures of Al+ Ti02+B with Ti02 and B in stoichiometric ratios for forming TiB2• In this study, porous Al/(TiB2+Ah03) composites were further processed by hot-pressing at temperatures above 600°C. This processing cycle was designed so that the composites could be densified. Furthermore, the reaction kinetics of the in-situ processing are studied by means of DSC analysis measured at different heating rates. The activation energies of the three intermediate steps that are involved in the reactive processing for preparing AV(TiB2+Alz03) MMCs are determined to be 923 kJ/mole, 241 kJ/mole and 235 kJ/mole respectively.XRD proved that the hot-pressed products consist of Al, TiB2 and Al203- Properties of the products are assessed by microstructural characterisation (LOM, SEM and EDS), microhardness, Young's modulus and bending tests. The results show that good microstructures, elastic properties and strengths, as well as acceptable ductilities were achieved. For the composition 79.74wt% Al-15.95wt% Ti0z-4.31wt% B, after the reactive free-sintering and hot-pressing cycles, Young's modulus is 105 GPa, bending strength is 509 MPa and maximum strain is 5.0%; for composition 88.73wt% Al-8.87wt% Ti0z-2.40wt% B, they are 89 GPa, 311 MPa and 8.2% respectively. It can be seen that the properties of products can be tailored by adjusting the relative amounts of reactants in green samples. Furthermore, for comparison reasons, Al and a binary system Al-Ti02 were identically processed as the ternary systems. Their microstructures and properties were studied."

Jan 1, 1998

Equilibrium calculational software programs can be effectively utilized to illustrate the importance of activity or concentration, solubility, temperature, solution pH, solution potential, and ligand complexation to students studying hydrometallurgy. The calculational program STABCAL will be demonstrated. illustrative examples for the creation of diagrams such as EH-pH, activity or concentration-pH and activity or concentration-EH will be presented to demonstrate the fundamentals of real hydrometallurgical systems. Speciation, titration and mixing will be used to simulate or predict operational processes. Applications will include treatment of Acid Mine Drainage (Berkeley Pitlake water and sediments), mass balance potential/pH diagrams, leaching and selective separation of metals from electroplating sludge, metal adsorption at femhydrite surfaces, and flowsheet development for treating mercury sulfide K106 sludge.

Jan 1, 2002

By R. David Prengaman

During the past several years a new insoluble lead anode has been developed for copper electrowinning. The new anode consists of a rolled lead-calcium-tin alloy sheet attached to a slotted copper bus bar by a soldering process which produces a complete metallurgical bond between bar and sheet. The metallurgical bond greatly reduces the resistance between the bus bar and the lead sheet and the high conductivity does not deteriorate during the life of the anode. The rolled anode thins uniformly and does not suffer preferential grain boundary or internal corrosion commonly seen in cast anodes. The lead-calcium alloy containing a high tin content corrodes slowly because the rolling process produces a uniform, fine grained structure. The wrought product is very strong and ductile; and contains no internal defects, segregation, cracks, or pores which can reduce the life of the anode. Because the anodes corrode uniformly, a high percentage of the anode thickness can be utilized thus extending the life of the wrought anodes. The anode alloy composition which is stable only in wrought form, produces exceptional resistance to passivation during current interruptions. First introduced into liberator cells, the new electrowinning anodes have been specified as the anodes of choice for every new SX-EW tankhouse constructed in the last two years. This paper describes the new anode, its method of construction, service history, and how it differs from present copper electrowinning anodes.

Jan 1, 1987