By P. Meyers, F. DeSilva, L. Gottlieb

A number of tests looking at lead removal using ion exchange resins of various types from various aqueous streams have been undertaken. The tests focused on strong acid cation (SAC) and weak acid cation 0N AC) resins. It was found that the mechanism of lead removal is partly by lead filtration rather than solely by ion exchange in a large portion of the applications studied. This is not surprising since lead carbonate is essentially insoluble and almost all water supplies contain at least some carbonate alkalinity. Regeneration of lead from exhausted resins containing significant amounts of lead may not be practical in some cases because of the large chemical and waste volumes involved. Since lead, .·along with many other very insoluble metals, is often present as a suspended solid rather than in ionic form, ion exchange is probably not always the best technology for bulk lead removal.

Jan 1, 2000

By Filippos Patsiogiannis

Laboratory size (5 kg) aluminum killed low carbon steel melts were desulfurized with synthetic fluxes in zirconia crucibles. The sulfur, oxygen, aluminum, silicon, and manganese contents in the melt were determined as a function of refining time and temperature. With a good argon shield and synthetic flux cover, melt reoxidation was not observed. Sulfur removal followed first order reaction kinetics. The effectiveness of calcia saturated calcium-aluminate (12CaO.7Al2O3) based fluxes in desulfurizing the steel melts was evaluated. The effects of initial sulfur level of the melt, weight of the flux (slag), and additions of tellurium, fluorspar, and barium oxide to the melt on the kinetics of desulfurization were also studied.

Jan 1, 1993

Thermodynamics and kinetics? of the removal of Va elements (As,Sb,Bi) from copper were investigated 1n the fire relining by alkaline carbonate fluxes such as Li 2co3 , Na 2CO3 and K2CO3. The distribution coefficients of As, Sb and Bl between alkaline carbonate fluxes and mo) ten copper were ?obtained at 1200°C under the different oxygen potentials. As and Sb were easily removed from copper to fluxes as pentavalent oxide form. On the other hand, Bi was hardly removed except by a Ll2CO3 flux. The removal rates of Va elements from copper were also measured In the temperature range of 1150°C.- 1250°C. The removal rates of As and Sb were much higher than that of Bi. The removal rates of Va elements showed the same order of the distribution coefficients. The removal rate could be expressed by following equation. (1).

Jan 1, 1987

By Zeljka Pokrajcic

Crushing and grinding, or comminution, circuits are the most energy intensive process of a mineral processing plant. Comminution involves the physical size reduction of an orebody to a particle size sufficient for recovery of the mineral values. However, the comminution process remains inherently inefficient. The inefficiency is a result of the operating nature of comminution devices such as grinding mills, where transfer of energy between grinding media and particles in unconstrained and completely random. New comminution circuit design strategies are presented in this paper. The aim of the new strategies is to improve the overall efficiency of the comminution process and reduce the total energy consumption of a comminution circuit. The energy efficient strategies include the: ? rejection of coarse size liberated gangue from the comminution circuit and further downstream size reduction ? use of more efficient grinding and crushing equipment ? the selection of coarser particle product sizes to alleviate the increased energy intensity required to achieve finer product sizes Singularly and when combined, these energy efficient strategies can significantly decrease the overall energy consumption of a comminution circuit. This paper also explores the financial impact of certain energy efficient strategies using an analysis tool called EcoNomics?. It shows that substantial financial gains can be made by including more efficient technologies and methods in comminution circuit design.

Jan 1, 2010

By Christina Viklund-White

Life Cycle Assessment has been used to compare the environmental performance of landfilling versus recycling of the zinc used for galvanizing steel. Hypothetical process routes were com-posed involving four different EAF dust treatment processes; Waelz kiln, DC-furnace, EZINEX and slag fuming, as well as scrap dezincing. The study shows that recycling of zinc used for galvanizing steel has environmental benefits in that it saves zinc resources. However, zinc recovery does not necessarily decrease the potential impact on global warming and acidification. The magnitude of these two impact categories is tightly correlated with the amount and type of primary energy consumed in a process. Due to the high electricity consumption in the dezincing process, this route has the highest impact on Global Warming Potential as well as Acidification Potential. The major part of the energy requirement for the production of zinc from primary and secondary sources is consumed in the reduction of ZnO to Zn. The consequence is that the theoretically possible savings in primary energy by recycling zinc-containing materials are relatively minor. The impact categories "land use" and "waste generation" are not considered in this study, but most likely the evaluation of such impacts would further increase the potential environmental impact of the landfill alternative. The results also show that the location of an electricity-intensive process highly affects the potential environmental impact. Comparing process and material alternatives in LCA studies where branch average data is used, is considerably more complex than when LCA is used within a company.

Jan 1, 2000

By R. J. Dippenaar, W. H. Van Niekerk

"An injectable lime-based desulphurization reagent for the treatment of liquid iron was developed. Firstly, selected lime based slags containing small quantities of CaF2 to increase fluidity, and Na20 to increase the basicity, have been evaluated on laboratory scale from a thermodynamic point of view. Subsequently, pilot plant and full scale industrial injection trials were conducted. It was found that lime-based slags, containing Na20 and CaF2, are able to desulphurize liquid iron efficiently. By the injection of a lime based reagent consisting of 60% lime, 25% soda ash and 15% fluorspar at a rate of 7 kg reagent/ton hot metal, the sulphur level in the metal (115kg) was reduced from 0,07% to 0,01 % within 5 minutes. The lime-based reagent developed in this study was successfully injected, both from a metallurgical and from a pneumatic point of view, on an industrial scale. The mathematical model utilised in this study, can be used successfully to predict the course and extent of desulphurization by lime-based slags. IntroductionMainly due to environmental difficulties encountered with pure soda ash, dry slag formation with CaC2 and high cost when Mg are used as desulphurizers, much incentive exists for the development of an inexpensive, environmentally friendlier desulphurization reagent. As a first step in the development of such a reagent, selected lime based slags containing small quantities of CaF2 to increase fluidity, and Na2O to increase the basicity, have been evaluated on laboratory scale from a thermodynamic point of view. This was followed by pilot plant injection experiments in which the kinetics of the relevant desulphurization reactions were evaluated. Finally, full scale industrial trials were conducted. All three phases of the investigation will be discussed with the major emphasis being placed on the kinetic study."

Jan 1, 1996

By A. H. Rhoades

The modern polarizing microscope with such accessories as cameras, infrared devices, reflectance and/or transmission photometers, indention hardness, and heating stage is used to characterize coal, coke, and other carbon forms. It allows characterization of coke by-products, such as tars and pitches and their insoluble residues. A useful product of the microscopic approach is the coal petrographic analysis which permits the prediction of coke strength carbonization pressure and volume change. Carbonization tests are expensive, time-consuming and require large amounts of coal. Tests on the coke show it to be strong or weak but give no indication of why. Petrographic analysis requires grams of coal and yields data that indicates why the coal produces coke of a given quality. Small samples from drill cores are sufficient for petrographic analysis. These data are also used to optimize blends for coke production. When coke-plant problems occur, ~he microscope can be used to check the coal blend proportions, as well as for weathered coal. Microscopy is useful in spore correlation work which may be a prerequisite to sound coal reserve estimates. Dispersed vitrinoid reflectance studies are used to determine the degree of organic metamorphism which serves to establish oil and gas deadlines. Tars and pitches are examined microscopically for the amount of normal solids as well as the size of undesirable carry-over solids resulting from pollution abatement practices in coke works. The microscope is also used to study coals for gasification and liquefaction.

Jan 1, 1981

By Roderick I. L. Guthrie, Donghui Li, Mihaiela Isac, Luis Calzado

The HSBC is an ideal process for the production of BMG strips. The purpose of the present work was to investigate the casting of Ca-based, bulk amorphous strips. The possibility of casting three Ca-based alloys (60Ca-20Mg-20Al, 60Ca-15Mg-10Al-15Zn and 55Ca-15Mg-10Al-15Zn- 5Cu (at.%).) was investigated, using the HSBC simulator. Numerical simulation and mathematical modeling were used to predict temperature variations and cooling rates, under different interfacial gaseous atmospheres (helium and air) near the meniscus region. Given the critical cooling rates and glass temperatures needed to be reached for the vitrification of the respective alloys, this leads to predictions of the critical thicknesses possible with this novel casting process. To validate our predictions, these alloys were then prepared and cast onto the sand-blasted, solid copper substrate mould of the HSBC simulator. The possibility of producing Ca-based metallic glassy strips via the HSBC processes was confirmed, using optical microscopy, X-ray diffraction and Scanning Electron Microscopy, to characterize the glassy properties of the cast strips. It was found that the HSBC process would be able to provide sufficient cooling to form amorphous strips for the 60CA-15Mg-10Al-15Zn and 55Ca-15Mg- 10Al-15Zn-5Cu alloys, but not the 60Ca-20Mg-20Al alloy.

Jan 1, 2014

By T. Maruyama

The Tamano Smelter of Hibi Kyodo Smelting CO. ,Ltd. went into operation in 1972. The Flash Smelting Furnace that was originally adapted was equipped with electrodes that were attached to the settler substitute of the slag cleaning furnace. Later the development of our own original coke combustion technology was promoted and a new Tamano Type Flash Smelting Furnace (T-FSF), without electrodes, was put into operation in 1988. The technology of coke combustion and combustion the burner have continued to improve. As a result the copper losses in the slag have been reduced as well as a stable operation has been achieved. Furthermore, this has been accomplished while increasing the concentration feed and the matte grade The current objective is to continue to strive for high matte grade operation and to raise production efficiency while paying attention to the important subject of copper losses in the slag. In this report, the data related to the copper loss in the slag reduction are presented along with the influence of the thickness, settling time and coke. The recent operation conditions of the T- FSF are also presented.

Jan 1, 2003

By Li Kaihua, Li Liang, Miao Qingdong, Wang Cong

The current process of production of titanium sponge involves the use of TiCl4 as a feed material and a huge amount of heat is generated during the magnesiothermic reduction process. For this reason, it is possible to agglomerate into a titanium lump with the partial high temperature. And, it is difficult to obtain soft titanium sponge with low content of impurities. In order to solve the current problems in the titanium sponge production process, process optimization experiments study of TiCl4 feeding speed, vacuum distillation temperature, system pressure and time control had been conducted for obtain high quality titanium sponge. Experimental results show that lower feeding speed can improve the output capacity of titanium sponge and softer products can be obtained. The product grade rate of titanium sponge improved significantly.

Jan 1, 2015

By Minge Zhao, Yuandong Pei, Zhixing Zhao, Zejun Ma, Lili Ban

"Confocal scanning laser microscope (CSLM) has been applied to carry out the in-situ observation of melting and solidifying characteristics during iron ore sintering process, accompanied with TG-DSC test. It can be found that apparent Liquid phase forming temperature(LFT) and ending solidifying temperature(EST) is about 1190? and 1160?, respectively. Forming liquid phase during sintering process goes through four courses, these are shrinking, expanding, shrinking and expanding coexisting and expanding totally. For Yandi fine, the corresponding temperature of these four courses is about 1120-1160?, 1190-1196?, 1218-1220? and 1233-1270?, respectively. Although CAJ fine has more difficulty in forming initial liquid phase, but when liquid phase expands, it may have better fluidity and easier for liquid phase formation. Adding enough CaO, CAJ fine takes on high fluidity like Yandi fine, because liquid phase during sintering process is formed mainly by reaction between CaO and Fe2O3.IntroductionConfocal scanning laser microscope (CSLM for short) has been applied to carry out the in-situ observation of metallurgical phenomena, especially in steelmaking process. Recently, many researches on ironmaking process were conducted with CLSM. While for high temperature properties during sintering process, there are limited reports on in situ observation1-2). In this paper, melting and solidifying characteristics of iron ore were observed with CLSM under simulated sintering temperature, and high temperature properties of iron ore during sintering process was clarified based on the in situ observation results and TG-DSC research."

Jan 1, 2012

By Thomas J. O'Keefe, Pu Yu, George Houlachi, Xuewen Tang

"Impedance measurements were used to investigate the electrochemical characteristics of acidic zinc sulphate electrolytes containing Sb3+, gelatin and their mixtures. The data were correlated with cyclic voltammetry curves made using synthetic as well as industrial electrolytes. The cyclic voltammetry results were similar to those obtained in previous studies in that antimony caused a depolarizing effect while gelatin gave an increase in the potential for zinc nucleation on an aluminum substrate.The electrochemical impedance spectroscopy (ElS) evaluations were conducted on electrodeposited zinc at three overpotential values. The potentials were chosen to represent various current density regions in the zinc polarization curves. The antimony and gelatin gave characteristic impedance plots which correlated with expected behavior, particularly current efficiency. Both antimony and glue appear to modify the intermediate zinc reaction sequence, but in different ways. The data strongly suggest that film formation and stability are major factors in the zinc ion reduction mechanism.IntroductionThe zinc electrodeposition process is sensitive to the presence of a variety of organic and inorganic chemical species in the electrolyte [I]. Such components can produce either beneficial or harmful effects, depending on their relative concentrations and electrochemical behavior. Extensive investigations have been made to gain a better understanding of the changes occurring during zinc deposition in the presence of such additives. Techniques employed include microscopy, x-ray diffraction, dynamic voitammetry, current imd energy efficiency studies [2-5]. Ultimately, the objectives are to identify the factors which most affect the efficiency of the process and to provide a means to effectively control them.One of the most harmful impurities is antimony, which can be detrimental when present at concentrations as low as 10 to 20 parts per billion. Dramatic changes in zinc polarization behavior, deposition structure and current efficiency have been observed with antimony in the electrolyte. Antimony appears to lower the hydrogen overpotential by hydride formation or a similar catalytic mechanism, which allows an increase in localized corrosion and zinc dissolution [6-8]."

Jan 1, 1997

By Chao Li, Qian Li, Yong-bin Yang, Kai Li, Qiang Xie, Yuan-yuan Zhu, Dong-ye Li, Qi-bing Tan

"The permeability of sintering mix is a vital technological property in sintering process. However, it can only be measured by off-line method on samples picked from the production. In order to acquire the properties of sintering mix accurately, on-line measuring of permeability is urgently required. Based on the reflection characteristics of bed permeability on pipe flowing parameters, a new method is presented in this paper for on-line measuring of sintering mix permeability. The measurement can be performed by blowing gas flow in the bed with the measuring pipe. Measuring results are obtained by picking the data on flowing rate and pressure in the pipe. The function of flowing rate to pressure may be certain for samples with the same permeability. Thus, the permeability was determined by contrasting this function to the result of off-line measuring, and the relative coefficient or R2 value was more than 99%.IntroductionThe permeability of sintering mix is a vital technological property in sintering process, which directly determines production and quality of sinter, or even determines whether the sinter production is carried out smoothly [1,3].The permeability have more obvious influence on vertical sintering speed, which is mainly related to air quantity passing through material bed. Under certain inducing capacity and negative pressure, the vertical sintering speed mainly depends on the permeability of sintering mix. Low permeability may make burning through point of sintering move back, and the sinter mix cannot be burnt through. High permeability may make burning through point of sintering move forward, improving production efficiency by increasing the speed of sintering machine [4] Good permeability means a small resistance of fan ,reduction of negative pressure of sintering machine, and full contact between air and sulfide, which can strengthen physical-chemical reaction during sintering process and increase desulphurization rate. In gas well through material layer process, gas-solid desulfurization reaction and gas-solid-liquid heat exchange are completed and hot gas through the combustion zone supplies the sintering process with heat. Finally uniform sintering of the material layer in height and width direction is achieved [5] While high permeability index leads to weak sinter strength, fast sintering speed, short residence time of high temperature region and little liquid phase. Moreover, liquid phase in the fast cooling process is too late to fully crystallize but forming glass phase which is harmful to sinter strength as well. Bad permeability means a big fan resistance and increase of negative pressure of sintering machine, which make the air pass through material layer difficultly. When air and mix contact difficultly, removal of sulfide reduces so that desulfurization is incomplete. Meanwhile, low caking efficiency, slow sintering speed and easily burnt sinter , reduce sinter output. Therefore appropriate permeability of sintering mix is the premise of stable burning through point and satisfactory sinter output and quality."

Jan 1, 2013

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were carefully examined during the entire growth stage of bacteria (fermentation). Several very important discoveries were made. For example, the pyrite surface invariably drastically changed its properties at the second day of fermentation. Beyond two days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became insensitive to convective diffusion in solution (stirring).

Jan 1, 1990

By Minjun Tang, Jianfeng Zhou, Feng Chen, Linjiang Qing, Xiaolei Song, Yufeng Guo, Tao Jiang

"Reduction swellability index (Rsn and low temperature reduction disintegration index (RDI) of vanadium-titanium magnetite oxidized pellets are harmful to the processing of ironmaking, for example, causing serious gas permeability, decreased yield, higher coke ratio and more furnace dust. Thus, the improvements of RSI and RDI of vanadium-titanium magnetite oxidized pellets were investigated in this paper, including the pretreatment of raw material, additives of dolomite or boric acid, pellets treated in chloride solution and so on. The results showed that damp milling as pretreatment and boric acid added in pelletizing were conducive to the RSI which decreased 5% and 7% respectively, while they were not efficient enough in improving RDI. Dolomite was efficient in improving RSI, but had negative effect on RDI. There was no evidence to show that RSI and RDI would be improved when pellets were treated in chloride solution. Pursuing this further, the mechanism of those improvements were investigated.IntroductionIn the world, vanadium-titanium magnetite utilization is investigated around how to recover iron, titanium, vanadium, and divided into blast-furnace method and non-blast-furnace method according to respective characteristics. Blast furnace method [1, 2] can recover iron and vanadium effectively, but Ti02 cannot be recycled. Non-blast-furnace methods include rotary kiln-electric furnace method, pre-reduction electric furnace method, reduction- grinding method and sodium vanadium-rotary kiln-electric furnace method and so on. [3-7]Comparing to the Non-blast-furnace method, the method of blast furnace smelting has been put into industrial applications. And it has the following advantages: First of all, effective recycling iron and vanadium; Second, technical problems of high titanium slag in blast furnace smelting; Third, it has mature technology in blast furnace smelting."

Jan 1, 2013

By J. A. Innes

"""The oxygen, next uniting with the carbon, sent up an ever-increasing stream of sparks and a voluminous white flame. Then followed a succession of mild explosions, throwing molten slags and splashes of metal high up into the air, the apparatus becoming a veritable volcano in a state of active eruption.""IntroductionHenry Bessemer F.R.S(An autobiography, 1905)Thank you Mr Chairman for the opportunity to speak: at this, the opening session of your International Symposium on the subject of ""Injection in Pyrometallurgy"". Judging from the list of papers to be presented over the next three days, the Symposium promises to provide a most valuable addition to our existing knowledge base in what is now an extremely active area of R&D investigations. Whilst we have obviously come a long way since Sir Henry Bessemer's pioneering experiments of the mid-19th century, there is still much for us to learn.Most importantly, the Symposium offers a further opportunity to acknowledge the many significant technical contributions made in this field by the Organising Committee's special guest, Professor Howard Worner - one of this country's most respected research leaders.When first approached to give this talk I had two areas of concern. Firstly, I was not entirely clear just what injection metallurgy was meant to cover. How should the overall scope of this particular subject be defined?My second concern related to Howard Worner himself - a man for whom I have the highest personal regard and who, in fact, played a most influential role in respect of shaping my own career. Having already spoken about Howard's achievements on earlier occasions, I wondered what I could sensibly add.Notwithstanding these personal reservations, I am delighted to be here with you this morning. If my thoughts on the meaning and scope of injection metallurgy appear to be slightly off-course, and if Howard should perhaps recognise some repetition in my remarks, then I hope I can be forgiven."

Jan 1, 1996

By C. Ek

In bismuth metallurgy, low-copper high-sodium mattes are by-produced. Different charges containing mixtures- of crude mattes, oxidized matte, and/or copper sulfide concentrate and/or copper silicate ore have been smelted to give a rich matte and a disposable slag, then converted to obtain blister copper with high recovery and a rich slag to be recycled.

Jan 1, 1983

By Arthur S. Klein, Hugh R. Lowry

"The Levitation Casting Process is a new continuous casting method that uses an electromagnetic levitation field, instead of a mold, to support and contain a column of solidifying metal. By counteracting gravitational forces and hydrostatic pressure on the metal column, this process eliminates friction and adhesion at the interface between the solidifying metal and the cooled walls of the casting chamber. The process inherently provides high casting speeds, excellent dimensional control and smooth, continuous emergence of solidified product from the top of the casting chamber.Of major importance is that the electromagnetic field produces an intense stirring of the liquid metal both before and during solidification. As a result of this stirring, the cast product has a homogeneous, equiaxed, fine grain structure generally suitable for immediate drawing or other forming operations without the need for hot rolling or other expensive additional processing.This paper reviews the fundamentals of the Levitation Casting Process, results obtained in casting various pure metals and alloys, and the production sized system at Lowell, MA, that uses this process. IntroductionThe Levitation Casting process was specifically developed to meet several requirements including:• Economic at low casting rates• Usable with pure metals and alloys• High, uniform product quality suitable for fine wire drawing or cold rolling into flat strip and tape• Easy cast product shape and size changes• Process inherently stable and easily automatedIn meeting these criteria it was also desired to retain the advantages of General Electric's well known Dip Forming continuous casting process; namely the inherent ""fail-safe"" properties of upward casting, solidifying metal by means other than pressure contact with a cooled mold, and use of a sealed furnace, casting chamber and cooling tower, filled with a protective atmosphere, to prevent oxidation of the molten metal or cast product."

Jan 1, 1988

By Guanghui Li, Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Xiaohui Fan, Zhiyuan Yu

With the increase of proportion of biochar(without modified) replacing coke breeze, the physical strength of sinter decreases due to the faster burning speed of biochar. An investigation upon passivating biochar with boric acid was then conducted to strengthen sintering in this paper. A layer of thin film of B2O3 distributed in the surface of biochar was observed, which could reduce the contact between reaction gas and biochar. So the burning speed of biochar was decreased properly after passivation, and the combustion efficiency increased due to the inhibition of carbon gasification. The comprehensive effects of above changes could increase the maximum temperature of sintering bed, which facilitated to the mineralization of sintering mixtures. Eventually sintering indices got reinforced. Thus the indices of sinter as applying 40% passivated biochar were comparable with that of 100% coke breeze.

Jan 1, 2015

By Michael J. Marinigh

"Increased safety requirements, higher operational costs, greater environmental restrictions, and new competitive processing techniques are the challenges smelter operators must confront in order to remain economically viable.In converting furnaces which have tuyères such as the Noranda Reactor and the Teniente, Peirce- Smith and Hoboken converters, efficient tuyère line management is critical to optimizing blowing rates, increasing refractory life, and improving safety.This paper will describe recent improvements made to equipment used for tuyère punching, tuyère silencing, tuyère pyrometry and refractory drilling of tuyères and how the proper application of the equipment can lead to operational and safety improvements."

Jan 1, 2009