By I. Gaballah

Decontamination of synthetic solutions of PbC12 containing 10, 100 and 1000 ppm of lead, using chemically treated barks had been studied. The percentage of !cad cations' removal from solutions depends upon the pH and the initial concentration. About 99 % of the initial lead content can be removed at pH of about 3.5, 5.5 and 6.5 for initial concentrations of 10, 100 and 1000 ppm respectively. The maximum retention capacity of the treated bark is about 83 mg of lead per gram of modified bark. Bark loaded with lead had been analyzed by Infra Red spectroscopy. It seems that lead reacts with hydroxyl groups of the phenolic constituents of the bark. On the other hand, the removal of a lead cation by the bark leads to the release of two H+. This seems to show that the removal of lead could be interpreted as an ion exchange with hydrogen belonging to the hydroxyl groups of the modified bark.

Jan 1, 1994

By N. Kanari

The thermal decomposition studies of two zinc basic carbonate samples were carried out up to 400 "C by thermogravimetric analysis, boat experiments and differential scanning calorimetry measurements 'DSC'. The initial samples and the solid decomposition products were analyzed by scanning electron microscopy, x-ray diffraction and laser particle size analyzer. The thermal decomposition of both samples started at about 150 "C and the rate of decomposition became significant at temperatures higher than 200 "C. The apparent activation energies 'Ea' in the temperature range 150-240 "C for sample decomposition were between 132 and 153 kJ1mole depending on the sample origin. The XRD analyses of the intermediately decomposed samples and the DSC results up to 400 "C suggest that the decomposition reaction probably occur in a single step.

Jan 1, 2002

By Lifeng Zhang, Zineb Benouahmane, Yaqiong Li

Experimental oxidation tests at high temperature (1000-1200 °C) on SiC samples have been respectively performed under wet and dry air atmosphere for different holding times. The thickness of thermally grown oxide was experimentally measured by DEKTAK Stylus Profilometry. The results showed that the oxidation rate was increased with temperature and holding time, corresponding to a passive oxidation regime which led to the formation of SiO2 layer. The sessile drop method was employed in order to measure the contact angles between Si and SiC at high temperature. Contact angle can be varied from 39.6° to 75.6° by controlling the atmosphere. The deoxidation of the oxide layer and infiltration of liquid silicon caused a decrease in the contact angle.

Jan 1, 2016

By A. De, J. S. Zuback, T. Mukherjee, T. DebRoy

For successful commercial applications of additive manufacturing, metallic parts need to be defect free, structurally sound and reliable. However, additively manufactured metallic parts are susceptible to distortion, lack of fusion defects and compositional changes. Methods to measure susceptibilities of various alloys to these defects are needed but not currently available. Here we show that the necessary theories can be developed based on a well-tested numerical heat transfer and fluid flow model and decades of research in the field of welding. The proposed theories are validated with experimental results reported in the literature.

Jan 1, 2016

By Hui Lu

The structural changes in solutionized AA2618 during natural aging and their effects on subsequent artificial aging were investigated by hardness measurements, X-ray diffraction, differential scanning calorimetry and transmission electron microscopy. The changes in lattice parameter and hardness during natural aging indicate that copper-enriched clusters form in the earliest stage, followed by the formation of magnesium-enriched clusters and coppermagnesium co-clusters. Prior natural aging consistently weakened the hardening during subsequent artificial aging at 180, 200 and 230 °C but had no effects on artificial aging at 150 °C. The decreased age hardening was attributed to the reversion of small clusters/zones that formed during prior natural aging. The lattice parameter exhibited erratic changes with increasing artificial aging time, reflecting the complex sequence of the reversion and precipitation.

Jan 1, 2006

By Guanghui Li, Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Xiaohui Fan, Zhiyuan Yu

With the increase of proportion of biochar(without modified) replacing coke breeze, the physical strength of sinter decreases due to the faster burning speed of biochar. An investigation upon passivating biochar with boric acid was then conducted to strengthen sintering in this paper. A layer of thin film of B2O3 distributed in the surface of biochar was observed, which could reduce the contact between reaction gas and biochar. So the burning speed of biochar was decreased properly after passivation, and the combustion efficiency increased due to the inhibition of carbon gasification. The comprehensive effects of above changes could increase the maximum temperature of sintering bed, which facilitated to the mineralization of sintering mixtures. Eventually sintering indices got reinforced. Thus the indices of sinter as applying 40% passivated biochar were comparable with that of 100% coke breeze.

Jan 1, 2015

By Jian Li, S. Penttila, W. Zheng

"Materials selection for Gen IV supercritical water reactor in-core components faces major challenges due to severe operating condition. Beside high-temperature mechanical properties, SCC and general corrosion resistance of commercially available materials are also major focuses in recent research. Recent reports suggest that certain types of surface modifications are beneficial to SCW corrosion resistance. In this study, the effects of surface modifications are investigated, and possible mechanisms for improved corrosion performance are discussed.IntroductionThe current Canadian pressure-tube supercritical water reactor (SCW) design specifies a core outlet temperature of 625°C under 25 MPa of pressure, with peak cladding temperature as high as 850°C. Challenges in materials selection include high-temperature mechanical properties, corrosion resistance, SCC resistance and radiation damage. Most of the SCW corrosion test results available are below 730°C. Early work by Allen [1] summarized the corrosion resistance of alloy groups including Ni-based super alloys, stainless and ferritic/matensitic (F/M) steels that can potentially be used for SCW reactors. F/M steels can only be used at low temperature sites (e.g. down stream piping). At 500°C and 25 MPa, F/M steels develop a thick but mechanically stable oxide layer. However, the long term stability of the surface oxide layer is largely unknown. Ni-based alloys appear to form very thin surface oxide, however pitting was observed in the vicinity of some intermetallic precipitates [2-5], and dissolution of major alloying components could pose significant problems for down stream piping [6]. In addition, concerns of Helium formation due to Ni transmutation prevented this alloy group to be used as fuel cladding. The corrosion resistant austenitic stainless steels (e.g. 316L) are found to be susceptible to localized corrosion such as pitting, intergranular attack and stress corrosion cracking (SCC) [7]."

Jan 1, 2012

By G. G. Krishna Murthy

Several experiments were carried out to simulate the bath smelting reactions where iron oxide particles were dropped on to an iron-carbon bath containing molten CaO-SiO2-Al2O3 slag layer on its surface. The composition of the slags used in the experiments was %CaO:46.1; %SiO2:41.7; and %A1203:12.2. Experiments were con¬ducted with carbon saturated iron melts contained in either a pure graphite crucible whose walls were covered with a pure alumina tube, or a pure flat bottom alumina crucible, at 1723-1823 K. Degree of reduction of a pure iron oxide particle was linear with time in the initial stages (up to about 20% oxygen of the original pellet was reduced). The rate of reduction of smaller oxide pellets was smaller than that of a bigger pellet - the time for complete reduction of a 5.6 g wustite pellet was smaller than that for a 1.2 g wustite pellet. It was also established that the interaction rates obtained by adding a molten pure oxide particle of given weight to the system were lower than that determined by using a solid oxide particle of same weight. The overall rates of reduction decreased with decreasing the bath temperature. The experimentally determined rates of reduction based on the time for 70% reduction were influenced substantially by addition of slag up to about 50 g on to a bath of 78.8 mm in diameter, and remained constant when slag present on the bath surface was between 50 g and 200 g.

Jan 1, 1993

By Lianjun Liu, Ying Li, Qianyi Zhang

"Photocatalytic reduction of CO2 by H2O for production of Cl fuels (CO and CH4) was studied using copper and iodine co-modified TiO2 (Cu-IffiO2) nanocomposites, with copper deposited on the surface and iodine doped in the lattice. The nanocomposites were prepared via a combined hydrothermal and wet impregnation process. All I-doped samples demonstrated visible light activity. Under UV-vis irradiation, co-modification of Cu and I significantly increased TiO2 photoactivity compared with bare TiO2 or those modified with only one species.IntroductionThe photoreduction of CO2 into fuels on photocatalysts such as TiO2 has been regarded as an important approach to solve both energy shortage and globe warming problems [1]. However, the wide band gap and fast recombination ofphotoinduced hole (h+) and electrons (e"") limited the application of TiO2 in CO2 photoreduction reaction. Extensive research has been conducted to improve the photocatalytic ability ofTiO2 by depositing or doping foreign ions that can enhance charge transfer and/or creates intra-band-gap states to induce visible light absorption at the subband- gap energy. Compared with mono-doping, co-doping of metal/nonmetal species has been reported to have higher photocatalytic activity for TiO2 [1-3]. Our previous studies showed that Cu deposited on TiO2 [4] or iodine doped in TiO2 [5] significantly enhanced the catalytic efficiency for CO2 photoreduction and increased the response to visible light. We hypothesize that there could be a synergetic effect if TiO2 is co-modified by both Cu and I species resulting in further improvement in CO2 reduction efficiency. In this work, we synthesized and characterized Cu-IffiO2 samples and investigated their activity toward CO2 reduction under visible and UV-vis illumination, respectively.Experimental MethodsMaterialsTitanium tetra-isopropoxide (TTIP, 98%) and isopropanol (C3HsO, 99.8%) were purchased from Acros Organic. Iodic acid (HIO3,99.8%) and Copper Chloride (CuCh, 99.9%) were purchased from Alfa Aesar. All other chemicals were analytical grade and used without further treatment."

Jan 1, 2012

By Eren Hüseyin Obuz

In this study, the leaching kinetics of rare-earth elements were investigated using HCl and HNO3 solutions. A standard crushed complex ore was utilized as raw material. The complex ore (particle size of under 54 μm) contains REE (Ce, La, Nd, Pr, etc.). Different leaching durations were selected for the kinetic studies. The highest leaching efficiency was obtained in HCl solution, and the leaching mechanism was identified to diffusion through a product layer. The rate constants of Ce, La, Nd, and Pr were calculated as 1.08 × 10−2, 0.86 × 10−2, 1.87 × 10−2, and 1.34 × 10−2 h−1, respectively.

Rapidly solidified TiAl-Cr-xNb-Y(x=2,4,6, at.%) alloys have been produced using a single roller melt spinning method. The microstructure of alloy ribbon was refined and component became more homogeneously by rapid solidification technology. There were two phases in alloy ribbons, including -TiAl and 2-Ti3Al phases, yet the amount of 2-Ti3Al phase in matrix obviously increased by rapid solidification than cast alloys. The micro-hardness testing also carried out. Compared to the cast alloys, the alloy ribbons have much higher hardness.

Jan 1, 2009

By M. Vijayalakshmi, S. Saroja, C. Sudha, T. N. Prasanthi

"Ti-5Ta-2Nb alloy and 304L austenitic stainless steel were joined by explosive cladding process. Investigations on 'as received' explosive clad revealed high hardness very near the interface due to martensitic transformation of 304L steel base plate. To improve ductility, explosive clads were heat treated in the temperature range of 823 to 1073 K for 1 to 20 h. Consequent change in the microstructure and microchemistry of the clad interface was studied. No change in the interface microstructure was observed for heat treatment at 823 K. Increase in temperature lead to the formation of various reaction zones at the interface, their number and width increase with temperature and time of thermal exposure. Growth kinetics of the reaction zones was monitored and activation energy required for formation was calculated. From elemental redistribution profiles, effective inter-diffusivities of alloying elements were calculated as a function of concentration and activation energy required for inter-diffusion was evaluated.IntroductionFor engineering components exposed to highly oxidizing and corrosive environments, a titanium based alloy i.e Ti-5Ta-2Nb (Ti-Ta-Nb) is often chosen as a structural material [1,2]. For economic consideration, vessels and piping exposed to non-oxidizing conditions are fabricated from 304L austenitic stainless steel (304L SS). Hence, dissimilar joint of Ti-5Ta-2Nb alloy and austenitic stainless steel becomes unavoidable. Fusion welding processes are not suitable for joining Ti and Fe based alloys due to the propensity for the formation of intermetallic phases and subsequent reduction in the bond strength [3,4]. Hence, explosive cladding, a solid state welding technique, was used to achieve high integrity, corrosion resistant joints between the two alloys."

Jan 1, 2012

By Russell E. Clemons

Coarse-crystalline granite, quartz syenite, syenite, meladiorite, and anorthosite in the Florida Mountains, southeast of Deming, New Mexico, were originally mapped as Precambrian. They were remapped in 1971 and some of them described as Mesozoic intrusives. Several subsequent papers presented Precambrian and Ordovician ages. Zinc, lead, copper, silver, gold, manganese, fluorite, and barite mineralization in the Florida Mountains invite more extensive exploration. Clarification of ages of rocks and periods of alteration and mineralization are necessary for efficient exploration. Field observations combined with petrographic studies strongly suggest that all the coarse plutonic rocks are Precambrian and most were altered extensively by late Tertiary hydrothermal activity.

Jan 1, 1982

By Kandipati Sreenivasarao

Ion flotation is a promising separation process for continuously removing toxic metal ions from dilute process effluents. After treating the effluent with appropriate surfactant(s), the metal- bearing species adsorb onto the surface of rising gas bubbles and can be collected as foams. Suitable collectors have been identified for most of the elements of the periodic table. However, a better understanding of the thermodynamic, kinetic and engineering principles that determine the performance of ion flotation systems would facilitate commercial utilization of this technology. A model system of sodium dodecylsulfate-ethanol has been studied for the removal of Cu (11) from dilute solutions, using laboratory-scale flotation columns. This paper reports the effects of the air flow rate, solution height, foam drainage zone height and col1ector:metal ion ratio on the flotation kinetics, ultimate recovery of metal, flotation product grade, foam losses and effluent quality. Preliminary results for Pb (11) removal are also reported.

Jan 1, 1993

By Murat Baydogan

Effect of retrogression and reaging treatment on hardness and stress corrosion cracking resistance of 7075 aluminum alloy was investigated. As received 7075 alloys in T6 temper condition were retrogressed at 170, 220, 240 and 380°C for different durations between 15 s and 60 min. Subsequent reaging was made at the T6 aging condition. Treated materials exhibited higher hardness and better stress corrosion cracking resistance than T6 temper in a wide range of retrogression temperature and time. The highest hardness was obtained after retrogression at 170°C for 210 s followed by reaging, corresponding to 20% hardness improvement. Improvement in stress corrosion cracking resistance of the alloy by as much as 85% was also observed. In this paper, improvements in hardness and stress corrosion cracking resistance are discussed on the basis of the microstructural changes during retrogression and reaging treatment.

Jan 1, 2006

By Yang Hong-ying, Yu Juan

Electrochemical behavior of natural chalcopyrite in electrolyte solution at pH value of 6.97 was studied by cyclic voltammetry, X-ray photoelectron spectroscopy and electrochemical impedance spectroscopy. The results showed that the electrochemical processes occurred on electrode surface were controlled mainly by the growth of sulfur species at lower applied potentials (<0.35Vvs.SHE), and the oxidative dissolution of sulfur species and the hydroxylation of iron at higher applied potential (>0.45V). The EIS spectra of oxide product layers could be illustrated by the equivalent circuit of Re(QdlRct(QfRf)), and the degree of hydrophilicity for chalcopyrite was higher when the value of charge transfer resistance Rct. was greater. The optimum potential range for the floatation of chalcopyrite in collectorless solution at pH value of 6.97 was between OCP (0.165V) and 0.35V.`

Jan 1, 2015

By Jing Zhong, Yugang Li, Chen Yan, Shaoda Zhang, Qian Wang

Online surface quenching technology has been developed for the hot charging process to prevent the surface cracks in high strength low-alloy steel slabs. In this paper, a two-dimensional heat transfer model of surface quenching process was presented. This finite element model includes nonlinear thermodynamic properties, by which the slab temperature distributions were computed. The model predicted temperatures show reasonable agreement with the measurements. The effects of the water flow rate and slab movement velocity on temperature variation during the quenching and subsequent tempering process were investigated. The result shows that the temperature drop increases but the tempering temperature changes slightly with increasing water flow rate and decreasing slab velocity. Keeping the slab movement velocity at 1.2-2.1m/min and the water flow rate at 55-70m3/h, the slab surface experiences a temperature drop of 400-600 firstly, then recovers above 650, the quenching and energy-saving effect are remarkable.

Jan 1, 2015

By A. F. Sidorov

A method of improving mineral recoveries from ores by modifying the physical and chemical properties of minerals using radioisotope radiation was tested. It was observed that irradiation modifies mineral cell sizes, changes the crystal structure of some minerals, reduces the sulfur content 1 to 1.5 % in sulfides, changes the zeta potential, alters the surface properties of mineral grains I and produces other changes. Preliminary tests indicate that accelerated electron treatment of ores in connection with mineral processing has a potential for improving mineral recoveries by flotation and by magnetic separations.

Jan 1, 1989

By H. Y. Sohn, S. PalDey

"A new chemical synthesis process for the preparation of intermetallic compounds has been developed. It involves the vapor-phase reduction of mixtures of constituent metal chlorides by magnesium vapor to produce intermetallic compounds in the form of fine powder. The advantages of the process include (a) the use of inexpensive raw materials, (b) low reaction temperatures, and (c) products in the form of fine particles. Titanium and nickel aluminides were prepared by this method. The effect of AlCl/TiCl3 partial pressure ratio on the formation of different titanium aluminides was studied. A two-phase mixture containing 80 mol % of TiAl and 20 mol % of TiA13 formed at an AlC13/TiC13 ratio of 10. The amount of TiA13 was maximized to 72 mol% at an AlC13/TiC13 ratio of 16. The maximum conversion of the limiting chloride TiCl3 was 94 % . In the case of nickel aluminides, NiAI, NiAl3, and Ni2Al3 were formed by reducing mixtures of NiC12 and A1Cl3 vapors. The effect of the partial pressure ratios AlCl3/NiC12 and Mg/NiC12 on the formation of nickel aluminides was studied. The maximum content of NiAl obtained was 98 mol % . At the AlC13/NiC12 ratio of 19, a two-phase mixture of 17 mol% of NiAl and 83 mol% of NiA13 was produced. The product particles were very fine in the size range of 0.05 to 0.2 µm.A. IntroductionIntermetallic compounds are attracting much attention [1]. Titanium and nickel aluminides have attracted a great deal of attention from the aerospace as well as automobile industries because of their potential for high-temperature application (e.g., low density, good oxidation resistance, and high-temperature strength retention [2, 3]). Gamma TiAl and two-phase (TiAl and Ti3Al) alloys [4] are used for gas turbine engine rotational components as well as automobile exhaust valves. TiAl3 is one of the most extensively investigated aluminum-rich intermetallics. Nickel aluminides are attractive because of their low densities, relatively high melting point and good high-temperature strength properties. For example, Ni3Al shows increasing rather than decreasing yield strength with increasing temperature [5]."

Jan 1, 1998

By Christoph Zschiesche

Managing complex material streams within a lead smelting/reduction process has a long history at Aurubis. After modernization of the secondary lead smelter in 1991, Aurubis operates an electric furnace and a Peirce Smith converter to process complex secondary materials. This process links the copper and the lead metallurgy allowing Aurubis to properly combine primary and secondary process lines to optimize the processing of complex raw materials and smelter intermediates. However, combination of copper and lead metallurgy processing requires a continuous evaluation as raw material quality and composition varies. This paper describes Aurubis lead smelter processing and provides some fundamental considerations to optimize the lead processing, in particular with aspects related to speiss formation