By Zhen Zhang, Jiang Diao, Xuan Liu, Tao Zhang, Bing Xie, Hong-Yi Li

Extracting vanadium from vanadium containing hot metal by LD process has been proven an effective solution for the utilization of vanadium-titanium magnetite ore, but the systematic analyses of vanadium extraction rate and mechanism by basic slag are seldom reported. In this study, mathematical model of vanadium transfer from metal to slag was formulated and the rates of vanadium extraction of hot metal with basic slag were investigated. The results indicated that the apparent vanadium extraction rate constant, kp, were in the range of 1.33~9.07×10-4g/(cm3·s). And the rate constant was increased with the increase of final slag basicity, reaction temperature and stirring gas flow. The apparent of mass transfer parameter decreases significantly from 0.13 cm3/ s to 0 cm3/ s in 20min, and the data changed as negative due to the decrease of slag oxidation and recovery of vanadium from slag to metal.

Jan 1, 2015

By Edgar E. Vidal, Keith Smith, James A. Yurko

Beryllium, like many other reactive metals, is extracted from a halide (generally BeF2) using magnesiothermic reduction, also known as the Kroll process. The beryllium is produced in a molten state, which when solidified resemble "pebbles". Although beryllium is used in limited quantities compared to other metals (< 100 Mt/annual), it is a critical material for the nuclear, defense/aerospace, and large science markets because of its unique nuclear and mechanical properties. Beryllium processing has unique environmental, health, and safety concerns which must be handled appropriately in the 21st century from a worker and environmental safety perspective, and must be designed with this first in mind. In 2011, Materion began operations of its new Kroll plant – informally known as the “Pebbles Plant” - in Elmore, Ohio. The plant was majority funded by a U.S. Department of Defense Production Act (DPA) Title III grant, which is a unique government/industry partnership program to, "create assured, affordable, and commercially viable production capabilities and capacities for items essential for national defense." After a twelve year hiatus from primary beryllium production, Materion has reentered its extraction business and has relearned how to make pebbles. The purpose of this presentation is to give an overview on beryllium extraction and discuss some of the unique aspects of building and operating a safe beryllium facility during the production scale-up phase.

Jan 1, 2015

By Xiang Ma, Halvor Dalaker, Kai Tang, Stefan Andersson

Silicon carbide (SiC) is one of the most important non-oxide ceramic materials for many industrial applications and is mainly synthesized by carbothermic reduction of silicon oxide by coke above 2200°C. Replacing natural gas (mostly methane, CH4) for coke in SiC synthesis could considerably reduce energy consumption and CO2-emissions owing to higher carbon activity of CH4 at lower temperature. The generally accepted reaction mechanism is that SiC is synthesized through gaseous intermediate silicon monoxide, SiO. In the present study, the reaction mechanism for the SiO and CH4 gaseous mixture has been examined using atomic scale modelling. Molecular dynamics (MD) using a reactive force field (ReaxFF) has been utilized to examine the initial stages of reactions involving a gas mixture of SiO and CH4 and surfaces of SiC. The MD results revealed some interesting SiC formation mechanisms. The reaction energies of the critical intermediate species were also estimated by density functional theory (DFT) calculations and the implications for the force field parameters used in ReaxFF was discussed.

Jan 1, 2015

By Shuqiang Guo, Gonghui Yang, Xingxing Zhang, Yuyang Bian, Song Chen, Weizhong Ding, Yinhe Liu, Lan Jiang

One of the most promising refractory materials for application is zirconia in melting superalloy. In this work, the properties and phase composition of magnesia partially stabilized zirconia ceramics (MgO-PSZ) under different sintering temperatures were systematically investigated. Commercial magnesia partially stabilized zirconia (MgO-PSZ) powders were selected as the starting materials. The magnesia partially stabilized zirconia phase composition was measured by X-ray diffraction (XRD), the density of sintered samples was tested by vacuum density instrument, the thermal expansion were obtained by thermal dilatometer from ambient temperature up to 1450°C, and the microstructures of MgO-PSZ were characterised by scanning electron microscope (SEM). The results indicated that the properties of thermal expansion, densification, microstructures and phase composition were significantly affected by sintering temperature. Densification was consistent with SEM micrographs of MgO-PSZ at different sintering temperatures.

Jan 1, 2015

By Dany Racine, Daniel Marceau, Denis Laroche, Dmitry Lukovnikov

Carbon base materials play a critical role in the performance of Hall-Héroult cell. The determination of their thermo-physical properties is of primary importance for modeling and designing complete cell systems. However, overcoming the associated experimental hurdles is complex and often underestimated. Of them are the Poisson’s ratio measurements and the continuous oxidation/burning of the materials at temperatures above 200°C. The novel procedure developed in this research is based on the Gleeble® 3800 system. Its vacuum chamber allows test with a chosen atmosphere at temperature of more than 1000°C. Young’s modulus, Poisson’s ratio and the coefficient of thermal expansion values can all be adequately measured using a single test. Cylindrical carbon samples (: 50mm, L: 100mm) were tested in the modified system at temperatures ranging from room to 950°C without any trace of oxidation. The resulting values were also in good agreement with literature data for a specific graphite material.

Jan 1, 2015

By Marcos Aurélio S. Costa, Nilton F. Nagem, Andreia B. Henriques, Herman S. Mansur, Alexandra A. P. Mansur, Antonio E. C. Peres, Valeria G. Silva

The superfine material generated in the Bayer process was used in one innovatively way as a precursor to geopolymerization techniques because of the presence of Gibbsite. Gibbsite can play a role in system adjustment because of the SiO2/Al2O3 ratio. Furthermore in the geopolymeric system it was studied the influenceof the additives such as kaolin, metakaolin and sodium trisilicate in an alkaline media. Others conditions to form the geopolymer were also evaluated such as solid/liquid ratio, SiO2/Al2O3 ratio and total alkaline. The raw materials and geopolymeric products were characterized by several techniques e.g. XRD, DSC, FTIR and SEM. Through the FTIR technique it was observed an increase in intensity and bandwidth in the region centered at 1010 cm-1, which is related to the asymmetric vibration Si(Al)-O, this is an indicating of the possible geopolymer formation This broadening of the band promotes a relative disappearance (overlapping) peaks at 965 and 935 cm-1 associated with raw material (ESPDust).

Jan 1, 2015

By Chunyang Guan, Jilai Xue, Zengjie Wang, Qiaochu Liu

Molten salts electrolysis method to prepare Al-RE alloys has attracted increasing attention recently. CaCl2 and Na3AlF6 were the most often used melts for this purpose. In this work, Al-Sc alloys prepared by electrolytic deposition process in both CaCl2 and Na3AlF6 melts were investigated, respectively. It was found that Sc distributes almost uniformly and Sc contents increase with increasing current intensity in both melts. Current efficiency was measured for comparison among various current densities applied. The alloy products were analyzed using XRD and SEM, where the formation behaviors of Al-Sc intermetallics were investigated in details. The experimental and theoretical results demonstrate that Al3Sc and Al0.968Sc0.032 are the major precipitates in the Al-Sc alloys prepared by molten electrolysis. The results are useful for selection and optimization of the molten salts compositions and the parameters of electrolysis operation.

Jan 1, 2015

By R. Padilla, M. C. Ruiz

Arsenic, antimony and bismuth are commonly found in copper concentrates usually as the minerals enargite, stibnite and bismuthinite, respectively. Concentrates having high levels of arsenic and antimony must be pretreated before smelting. Roasting is the preferred method for removing these toxic impurities from concentrates; However, the removal of As, Sb and Bi in oxidizing roasting by volatilization may not be complete due to the slow reaction rates at 500- 700 °C. Oxidizing/volatilization data were obtained from pure mineral mixtures and from arsenic rich copper concentrate. The reaction mechanism for the volatilization of arsenic and antimony were discussed. Near 100% As and over 95% Sb volatilized in the oxidation of a mixture of pure minerals at 700 °C, 1% oxygen, while over 95% As, and 35% Sb volatilized at 600 °C in 1% oxygen atmosphere when using a copper concentrate containing 3.51% As, 0.14% Sb, and 0.01% Bi. Bismuth did not volatilize.

Jan 1, 2015

By Zhenyang Wang, Yiran LIU, Xiangdong Xing, Jianliang Zhang, Zhengjian Liu

Basic characteristics of marine placer were systematically studied by chemical analyze, scanning electron microscope and X-ray diffraction in this paper. It could be found that the marine placer mainly consists of titanomagnetite and titanohematite. A series of experiments were performed to investigate reduction-magnetic separation for Fe and Ti from the marine placer. Effects of reduction temperature, reduction time, carbon ratio, magnetic density, and grinding fineness on the reduction-magnetic separation process were investigated. And the optimal process parameters were obtained as follows: the reduction temperature 1300, the reduction time 30 min, the carbon ratio 1.1, the magnetic density 50mT, and the grinding fineness of 0.074μm 86.34%. Under such conditions, the metallization rate, iron grade of magnetic substance and iron recovery reached to 94.23%, 97.19% and 90.28% respectively, and the titanium grade in non-magnetic substance and recovery of was 57.94% and 87.22% respectively. The effective separation of iron and titanium could be achieved in reduction-magnetic separation process.

Jan 1, 2015

By Shengli Wu, Jinming Zhu, Wei Huang, Xinliang Liu

The sinter of high basicity would interact with lump ores or acid pellets in the cohesive zone of blast furnace due to the difference of chemical composition and micro structures. The results of this work showed that the softening-melting properties of lump ores and acid pellet would be obviously improved by the high temperature interaction. However, the high temperature interaction index (INI) would be influenced by many factors, such as chemical composition, porosity, interaction interface and so on. The INI between sinter and porous limonite lump ore (L-2) was much higher than that of dense hematite lump ore (L-1) and acid pellet (P-1). In addition, though the softening and melting properties of L-2 were poorest in respective iron ores, the softening and melting properties of integrated burden B (consist of sinter and L-2) were not worse than other integrated burdens due to the strong high temperature interaction.

Jan 1, 2015

By Martin Reyes, Juan Hernández, Julio Cesar Juárez, Isauro Rivera, Ma. de los Ángeles Hernández, Francisco Patiño

The dissolution of Ag contained in metallurgical tailings was studied by adding ions Cu2+ and Zn2+ in S2O3 2- medium. Chemical analysis of mine tailings by cupellation revealed a Ag concentration of 71 g/ton. The XRF and XRD analysis confirmed the preponderance of SiO2 in the mineral matrix. The experimental dissolution process was conducted in alkaline solution using six concentrations of NaOH and five of S2O3 2-, at different temperatures, also using five concentrations of Cu2+ and Zn2+ as a catalyst. The results showed similar values for both systems (96.8% and 97.13%). The ion Cu2+ and Zn2+ increases the dissolution of Ag, and decrease the reaction time of dissolution. Under the conditions used, pH and stirring rate did not affect the dissolution of Ag.

Jan 1, 2015

By Messias dos Santos Machado, Renato B. Godoy, Roberta Lima, Andressa Silva, Francisco Valenzuela-Díaz, Rene R. Oliveira, Esperidiana Moura

This work aims to incorporate the Bof White Clay, from Boa Vista, Paraiba State, Brazil, as natural nanofiller in Ehylene vinyl alcohol copolymer (EVOH) and obtain flexible films. Nanocomposite was obtained using a twin-screw extruder, and film formed using a blow extruder machine. The flexible film nanocomposite was characterized, by tensile tests, XRD, DSC and their properties were evaluated. The results showed a good interaction between the clay and the EVOH resulting in an increase of properties of films nanocomposites as compared to films neat polymer.

Jan 1, 2015

By Run-sheng xu, Hai-yang WANG, Di ZHAO, Teng-fei SONG, Jian-Liang Zhang

This paper was mainly focused on the different semi-cokes and charcoal which could be new fuels for blast furnace injection. Through the comparative study with bituminous coal and anthracite coal, the properties of semi-cokes and charcoal were presented in this research. 10 indexes of different fuels were obtained by different standard experiment, including proximate analysis, ultimate analysis, igniting point, explosivity, transportation characteristic, ash properties, grindability, calorific value, combustibility and reactivity with CO2. According to the data analysis, it provided a theoretical basis for rational utilization of various blast furnace fuels, and helped to broaden the scope of the blast furnace injection fuels. This research could contribute to energy conservation, emissions reduction, and sustainable development of iron and steel enterprises.

Jan 1, 2015

By Frederico Muylaert Margem, Giulio Rodrigues Altoé, Glenio Daniel, Pedro Amoy Netto, Sergio Neves Monteiro, Maria Carolina Andrade Teles

The environmental concern is creating pressure for the substitution of high energy consumption materials for natural and sustainable ones. Compared to synthetic fibers, natural fibers have shown advantages in technical aspects such as flexibility and toughness. So there is a growing worldwide interest in the use of these fibers. Fique fiber extracted from fique plant, presents some significant characteristic, but until now only few studies on fique fiber were performed. This work aims to make the analysis of the tensile strength of polyester composites reinforced with fique fibers. The fibers were incorporated into the polyester matrix with volume fraction from 0 to 30%. After fracture the specimens were analyzed by a SEM (scanning electron microscope).

Jan 1, 2015

By Cheng Yan, Yugang Li, Qian Wang, Lizhi Zhang

In continuous casting process, mold powder has lots of metallurgical effects, such as covering the molten steel to prevent liquid steel from oxidation by air, preserving heat for top layer liquid steel, lubricating initial shell and so on. However, mold powder also can deteriorate the quality of final products obviously after the entrapment of mold powder in steel. In the present work, based on the similarity theory the effect of technological parameters on mold powder entrainment was investigated by water model. Experiment was carried out in the water mold using oil and water to simulate slag and steel, respectively. The results showed that increasing casting speed increased the water-oil interfacial fluctuation and entrainment frequency; viscosity of oil also had a great impact on the interface fluctuation and entrainment; water-oil interfacial tension effect the entrainment while not changing the interfacial fluctuation; submergence depth had little impact on entrainment and interfacial fluctuation.

Jan 1, 2015

By Bingyi Bai, Lifeng Yang, Yanling Guo, Jieyu Zhang, Guoding Gao

In terms of special resources with iron, niobium and rare earth coexisting in Baiyuneboite, the new smelting technology of ferrocolumbite was studied. Reduction experients for the Baiyuneboite and explores ore phase change of Baiyuneboite in the process of reduction was conducted with graphitic carbon as the main reducer and a temperature below 1000 ℃. Moreover, it studies the influence of reducer, roasting temperature and grind fineness on the reduction as well as focuses on the evolution course of iron phase. Through the analysis on in-situ XRD of the raw ore and carbon addition ore, it also develops microstructure change rules of Fe ore phase and ore phase of paragenetic elements for composite ore(Ca, Si, Nb, F) in the process of reduction roasting. In addition, the impacts of temperature on the reduction process are also discussed. With regard to minerals of different particle sizes, the thesis will explore their ore phase changes and microstructures after 10 hours’ reduction under 900 ℃.

Jan 1, 2015

By Jianguo Yin, Wenqiang Yang, Xiaoli Yuan, Juan An, Wentang Xia

Low grade iron ore with phosphorus (LGIOWP), a raw and wasted industrial solid material was used as an adsorbent to remove Pb(II) from wastewater. The effects of initial pH value, adsorptive time, initial Pb(II) concentration, adsorptive temperature and LGIOWP dosage on the Pb(II) removal efficiency were studied. The results show that the Pb(II) removal efficiencies exceed 99.4% and Pb(II) concentrations are less than 0.30 mg/L under the conditions of pH value 7.0, adsorptive temperature 50 oC, adsorptive time 30 min, initial Pb(II) concentration 100 mg/L, particle size <0.25 mm, adsorbent dosage 5 g/L and stirring speed 260 r/min. After Pb(II) removal reaction, the Pb(II) concentrations of wastewater completely accord with the requirement of national discharge standards of pollutants from lead and zinc industries (GB 25466-2010) (TPb= 0.5 mg/L) in China. Therefore, it can be concluded that LGIOWP is a new low-cost adsorbent which is suitable for the adsorption of Pb(II) from wastewater.

Jan 1, 2015

By Guangshi Li, Xionggang Lu, Xueliang Xie, Xingli Zou, Yuyang Bian, Hongwei Cheng, Kai Zheng, Changyuan Lu

The corrosion resistance and corroded microstructure of MgO-C refractory in molten slag are investigated by immersion test in muffle furnace at 1600 °C . The microstructure and chemical compositions of the specimens after erosion experiment are characterized by scanning electron microscope (SEM) and energy dispersive X-ray (EDX). The results confirm that the oxidation of graphite is the most important degradation mode of MgO-C refractory. The structure of the refractory material is damaged due to the decrease of graphite, as a result, the periclase substrate reacts with the molten slag directly. The corrosion process is controlled by the dissolution of the refractory materials into slag, low melting point oxides are therefore generated which lead to the damage of MgO-C refractory finally.

Jan 1, 2015

By Markus Aspiala, Fiseha Tesfaye, Pekka Taskinen

In this paper, the standard thermodynamic properties of Ag3Sb and Ag6Sb intermetallic compounds have been studied by the solid state EMF-method, using Ag+ ion conducting β- alumina and AgI. The intermetallic compounds were synthesized from pure substances in evacuated silica ampoules and their formation were confirmed by the SEM-EDS analyses. The EMF measurements were made on electrochemical cells of the type [Ag | β-alumina | Ag-Sb] and [Ag | AgI | Ag-Sb]. The usage of β-alumina electrolyte, in this study, enabled thermodynamic measurements of the Ag-Sb-intermetallic compounds above 710 K, hitherto unreported. Based on the new experimental data, thermodynamic properties of the Ag-Sb-intermetallic compounds have been determined. The obtained experimental values have been compared with the available literature data.

Jan 1, 2015

By Tao Zhang, Wen-tao YU, Hai-bin ZUO, Jian-Liang Zhang

Sintering-pot tests and metallurgical performances of sinter with 4 kind of different Al2O3 contents are experimented in this paper. Results show: when the Al2O3 contents increase from 2.0% to 3.5%, acicular calcium ferrites in mine phase will be gradually replaced by plate-like iron calcium. The increase of Al2O3 contents will lead to the addition of liquid viscosity and the reduction of permeability of sinter bed. Sintering time will be prolonged. The rate of yield is stable basically but production is low; besides, the increase of liquid viscosity will decrease of drum strength. The change of permeability of the material layer will make RDI +3.15 decrease first and then increase when Al2O3 contents changed from 2.0% to 3.5%. RI of sinter shows a contrary trend because many open voids are formed by deterioration of liquidity first and then pores closed.

Jan 1, 2015