By William D. Klopp, Joseph R. Stephens

Chromium alloys were coated with silicon, alumi-nuw, and boron by pack cementation. None of these simple coatings provided adequate nitridation/oxida-tion protection for a Cr -0.17pct Y alloy substrate as shown by a substantial Increase in the ductile -brittle transition temperature after air exposure for 100 hr at 2100°F. Iron-modified silicide coatings afforded good protection, holding the transition temperature of air-exposed specimens to 350° F compared to 200° F for uncoated unexposed specimens and 800°F for un-coated exposed specimens. Additional attractive cant-binations of modi-tying elements included Fe-mo, Fe-Mo-W, Fe-,Mo-W-Ti, and V-Mo-W-Ti. THE desirability of increased operating tempera-tures as a mcans of improving the performance of ad-vanced air breathing engines has resulted in emphasis on the development of materials with high operating temperature capabilities. Chromium, because of its relatively low density (7.19 g per cu cm), high melt-ing point (3410°F), and adequate strength upon alloy-ing, is a candidate material for turbine buckets and stator vanes of advanced air breathing engines. How-even, chromium is not without severe limitations, the major one being susceptibility to nitrogen embrittle-ment upon exposure to air at high temperatures.1,2 For example, a 25-hr air exposure of a Cr-5 pct W* * All compositions in wt pct. alloy at 2100°F produces a 600°F increase in the duc-tile-brittle transition temperature.' Although dilute alloying with such elements as yttrium, lanthanum, arid thorium3,4 or strong nitride formers5 has been shown capable of reducing nitrogen embrittlement, it is apparent that some additional form of surface protection, such as coatings or claddings, will be required for long time service in air breathing engines. Studies of aluiminide6 and silicide7 coatings and of nickel-base claddingsl on chromium alloys to date have suggested that these protection systems are inadequate. Of the aluminidc systems Studied,6 a simple aluminum and an Fe-Al coating on a Cr-5 pct W-0.1 pct Y alloy showed the lowest air exposure weight gains. However, the air exposures raised the ductile-brittle transition temperature of the coated specimens to above 1600°F from an initial level in unexposed specimens of about 500°F. A second in-vestigation for protection of Cr-5 pct W-0.1 pct Y employed gas pressure bonded alloy foils as protective claddings.1 An aluminized Ni-20 pct Cr-20 pct W alloy plus an unalloyed tungsten barrier layer gave the best performance with air exposure lives based on appearance and weight gains of over 600 hr at 2100°F. However, the bend ductile-brittle transition tempera-ture was increased to at least 1000°F after 100 hr at

Jan 1, 1970

By William M. Boorstein, Robert D. Pehlke

The rates of solution (of hydrogen in liquid pure iron and in several liquid binary iron alloys were meas-ured using a constant volume technique. The rates of absorption and desorption were found to be equal un-der all experimental conditions. increasing concen-trations of S, Si, or Te decrease the rate of hydrogen uptake but additions of Al, B, Cr, Cu, or Ni have no measurable effect up to concentrations normally en-countered in steelmaking practice. No relation ship was found between the effect of an alloying element on the equilibrium solubility of hydrogen in liquid iron and its effect on the solution rate constant. Mathe-rnatical analysis of the data indicates that under the present experimental conditions the rate of reaction of hydrogen with liquid iron is controlled by transport of gas solute atoms in the metal phase. Comparison of the present resuts with data on nitrogen taken un der similar conditions establishes that the hydrody-nurnic conditions which exist near the surface of a metal bath are best approximated mathematically by a surface renewal model for the case of rapid in-ductive stirring and by a boundary layer model for more quiescent melts. HYDROGEN has long been recognized as being a detrimental constituent in steel. If dissolved in the molten metal in excess of its solid solubility, hydro-gen can be evolved during solidification and cause bleeding or porosity in ingots and castings. In the solid metal, lesser amounts play a definite role in causing other defects such as hairline cracks, blisters, and embrittlement. For significant refinements to be made in metallurgical procedures designed to control or eliminate hydrogen from liquid iron or steel dur-ing processing, available equilibrium solubility data must be supplemented with reliable fundamental in-formation pertaining to the kinetic factors involved in the transfer of hydrogen to or from the metal. The scarcity of such information in the literature prompted the present investigation. PREVIOUS RESEARCH Whereas much of the existing data on the solution kinetics of gases such as nitrogen were obtained during the course of thermodynamic investigations, the solu-tion rate of hydrogen has been found too rapid to be accurately determined by conventional solubility meas-urement techniques. Consequently, little work on hy-drogen solution kinetics has been reported in the lit-erature. Carney, Chipman, and crant1 attempted to study the rate of solution and evolution of hydrogen from liquid iron by employing a newly devised sampling method. Although no significant quantitative data could be obtained, it was observed that the rate of solution was approximately equal to the rate of evolution of hy-drogen from the melt. Karnaukov and Morozov2 stud-ied the rate of absorption and Knuppel and Oeters3 the rate of desorption of hydrogen from molten iron by measuring pressure changes with time in a constant volume system. Karnaukov and Morozov determined the hydrogen pressures over their inductively stirred melts with the aid of a McLeod gage and therefore, were forced to work at pressures not in excess of 40 mm of Hg. Their experimental data conformed to a mathematical correlation based on diffusion control: and the rate coefficients calculated on this basis were shown to be independent of the initial absorption pres-sure. These authors reported the solution rate of hy-drogen to be eight-to-ten times higher than they had found for nitrogen in a previous study. They also re-ported that under identical conditions, hydrogen dis-solves somewhat more slowly in iron-columbium alloys than in pure iron. Knuppel and Oeters found that the desorption of hydrogen from pure iron at 1600°C was controlled in all cases investigated by diffusion in the metal bath as long as bubble formation was sup-pressed. This was substantiated by Levin, Kurochkin, and umrikhin4 who studied the kinetics of hydrogen evolution from liquid (technical) iron while applying a vacuum. Salter5 measured the rate of hydrogen ab-sorbed by iron buttons, arc-melted by direct current, as a function of hydrogen partial pressure in a hy-drogen-argon atmosphere. A carrier gas technique was used for analysis of the hydrogen absorbed. The initial rate of absorption was found to increase di-rectly with the square root of the partial pressure of hydrogen. EXPERIMENTAL METHOD Because of the rapid uptake and evolution of hydro-gen by iron-base melts, a constant volume technique was devised in order to obtain meaningful kinetic data over the entire course of the solution process. Apparatus. A schematic view of the experimental apparatus is given in Fig. 1. The hydrogen-liquid iron reaction system consisted of a gas storage bulb con-nected to a meltcontaining reaction chamber through a normally-closed solenoid valve. The gas storage bulb, an inverted 250 ml round-bottomed Pyrex flask was joined to the inlet port of the solenoid valve by a glass-to-metal seal. A more detailed illustration of the reaction chamber is shown in Fig. 2. The design of the Vycor reaction bulb was essentially that de-scribed by Weinstein and Elliott6 with the exception of a shorter, larger diameter gas inlet for this kinetic study. In position, the reaction bulb was closely by an eight-turn coil of water-cooled copper tubing which, when energized by a 400-kc oscillator, provided the inductive heating source. The walls of the bulb were maintained relatively cool by circulating cold water along their outer surface, thus preventing

Jan 1, 1970

By Willard L. Hunter

Four solvent extraction systems were studied to determine their efficiency jor extraction and separation of tantalum and columbium. Aqueous feed solutions of varying HF-HCl concentrations and metal content were contacted with equal volumes of cyclohexanone, 3-methyl-2-butanone, and 2-pentanone and solutions of varying HF-H2S04 concentrations were contacted with equal volumes of 2-pentanone. One multistage continuous test was made in a polyethylene pulse column using cy clohexanone as the organic phase. In each system studied, columbium and tantalum purities in excess of 95 pct with respect to each other were obtained in single-stage tests at low acidities in the feed solution. Separation factors ranging from 1700 to 2400 were obtained when rising HF-HCl mixtures in the aqueous phase. Best results were obtained when a solution of HF-H2S04 was used as the aqueous phase and 2-pentanone as the organic phase. A separation factor in excess of 6000 was obtained in one stage with aqueous solution concentrations of 2 _N HF and 2N H2S0,. When acid concentrations were increaszd to 52 HF and 10 _N H2S0,, 99.9 pct of the tantalum and 98.2 pct of the columbium initially present in the feed solution were transferred to the organic phase. The separation of columnbium and tantalum obtainable by means of the solvent extraction systems presented in this paper was found to corn -pare favorably with other systems, including the HF-H2SO4-methyl isobutyl ketone system currently used by most producers for the extraction and separation of these metals. TANTALUM and columbium are always found together in minerals of commercial significance, although the proportion of the two metals in ores varies within broad limits. Columbium is estimated to be 13 times more abundant than tantalum. Five methods generally employed for the separat:ion of these metals are: 1) fractional crystallization (the Marignac process),2 2) solvent separation, 3) fractional distillation of their chlorides, 4) ion exchange, and 5) selective reduction. Of these methods, the one currently used by industry to the greatest extent is that of solvent separation. One of the early technical developments in solvent separation of tantalum from columbium was reported by the Bureau of Mines: the HF-HC1-methyl isobutyl ketone system; data were presented for both laboratory and pilot-plant experimentation.3 Of twenty-eight organic solvents tested for their ability to extract tantalum from an HF-HC1 solution of columbium and tantalum, 3-pentanone (diethyl ke-tone), cyclohexanone, 2-pentanone, and 3-methyl-2-butanone were chosen for further study. Data on the HF-HC1-diethyl ketone system has been published4 and data describing the use of cy clohexanone, 2-pentanone, and 3-methyl-2-butanone as the organic phase are included in this report. RAW MATERIAL The source of tantalum and columbium oxides for this study was ('Geomines" tin slag from the Manono Smelter, Cie Geomines, Gelges, S.A., Congo. In order to extract the valuable Ta-Cb content, the slags were carbided, chlorinated, and the sublimate from chlo-rination was hydrolized and washed free of chloride with water. The washed material was air-dried and stored in a stoppered container. Throughout the paper, "feed material" refers to this mixture of hydrated oxides which was employed because of its high solubility in aqueous solutions. Typical analysis of the hydrated oxides is shown in Table I. I) HF-HC1-CYCLOHEXANONE SYSTEM Batch Separation. Effect of Acid Concentration. To determine the effect of varying the acid concentration upon the transfer of tantalum and columbium, a series of tests was made in which approximately 2.5 g of feed material was added to 25 ml solutions of 2, 4, 6, 8, and 10 N HF and 0 through 5 N HC1. Tantalum pentoxide concentration of the solu%ons was approximately 21 g per liter and columbium pentoxide was 14 g per liter. These starting solutions were shaken with equal volumes of cyclohexanone in 100 ml polyethylene bottles for 30 min. The phases were carefully separated in 125 ml glass separatory funnels. The time of contact of the solutions with the separatory funnels was kept at a minimum to reduce silica contamination. The measured phases were separated into 400 ml polyethylene beakers and the metal contents of each were precipitated by addition of an excess of ammonium hydroxide. Precipitate from each phase was filtered on ashless filter paper, ignited at 800" to 1000°C for 45 min, weighed, and analyzed by X-ray fluorescence.5 Data tabulated in Table I1 and illustrated in Fig. 1, show that maximum separation of tantalum from columbium for each HF concentration was obtained with no HCl present. The purest tantalum product was obtained with some HCl present. The highest separation factor was obtained at 2 N HF and

Jan 1, 1970

By Roy Greenfield

Estimates are given for the distance from a seismometer at which a miner can probably be detected. The procedure in making these estimates was to first establish the natural noise levels at the output of a surface seismometer for the 25 to 100 Hz frequency passband. The noise levels give the range of values which may be expected in areas with no man-made noise. For each noise level, we give the detection threshold which, when exceeded, indicates that a signal has been received. Based on the signals recorded by Westinghouse, curves are given which show the peak signal amplitude as a function of source- to-receiver distance (slant range). Curves are given for the Westinghouse seismic thumper, a 50-pound timber, and a sledge. For a given type of source, the receive signal strength depends more strongly on slant range than on any other factor. However, there is approximately a five-to-one scatter in the amplitudes. Thus, further study of factors affecting the signal amplitude might allow better estimates to be made for any particular geological setting. Combining the signal amplitude with the detection thresholds for the different noise conditions gives the distances at which a miner should be detected. These are given in Table l* below. [ ] The text also gives the increase in detection ranges which should occur if steps are taken to increase S/N by 10 dB. We feel that 10 dB is a conservative estimate of the improvement possible. During an actual rescue operation, the seismic crew and system should be capable of making on-site estimates of their detection capability, based on measurements of the site noise, and upon the best available estimates of the

Jan 1, 1974

By R. B. Gordon, D. A. Koss

Ultrasonic-atlenuation changes due to the formation of free dislocations have been observed during tensile tests of magnesium and LiF single crystals and samples of polycrystalline Results on the LiF and samples are similar: A preyield attenzration increase is observed which, however, be-corlzes smaller as the magnitude of the drop in load al yielding increases. This indicates that the yield point observed in these materials is due to dislovation rather than dislocation unpinning and that the initial density ' free dislocations must be low if the yield point is to be sharp,. Tests on the magnesium ere conducted at both 27" and 200C. Magnesium has the unusual property that the yield drop is larger at the higher test temperature and is accomplished by a decrease in attenuation. The latter is due principally to the temprovary pinning of detained dislocations by highly solute atoms. After strain aging., a stress as low as 0.3 bur suffices to unpin dislocations; microstrain measuements of sufficient sensitivity should. reveal plastic flow at stress levels this low IN another paper,' we describe the technique of simultaneously observing ultrasonic-attenuation changes and plastic microstrain during deformation of spher-oidized carbon steels. Changes of ultrasonic attenuation indicate damping effects caused by the oscillation of long, freely moving dislocation segments. Simultaneous microstrain measurements are used to indicate total dislocation motion. The dislocation-damping observations are most useful in the study of the early stages of deformation where the dislocation density is low and the plastic strain is small and relatively difficult to measure. Particularly interesting results are found in materials which display sharp yield points. Observations of these phenomena are reported here for three materials: single-crystal LiF and magnesium, and poly crystalline molybdenum. EXPERIMENTS Dislocation-damping effects were observed by measuring changes in acoustic attenuation with the ultrasonic-pulse method. The end faces of each of the specimens were ground flat and parallel and a quartz 10 Mc per sec, x-cut transducer was attached to one face. The bonding agents used were: a) "Nonaq" stopcock grease with magnesium, b) beeswax with LiF, and c) salol with molybdenum. With the LiF, the best acoustic signals were obtained at 45 and 50 Mc per sec; all other measurements reported are at 10 MC per sec. The Sperry Ultrasonic Attenuation Comparator2 was used to measure attenuation changes. In the

Jan 1, 1967

By R. H. Richman, F. Borik

A 0.3 pct C-12 pct Cr-6 pct Ni steel was rolled to 93 pct reduclion in area as austenite at 510°C, and then partially transformed as desired to ~rlartensite by qnenching to - 196°C. Pole figures for the austenitic matrix and for the martensitic product were separately determined by an X-ray transmission method. The deforitration texture of' the warm-worked austenite is characlerized by (110)(225) components, and is thus closely similar to those produced in a brasses. The pole jigure of the martensite in partially transformed material agrees well with that which can be constructed by transfortnation of the {110)(225) orientations according to either the Kuvdjuniov- Sacks or the Nishi-yatuu relatiotship. Howeuer, an important result of this construction is that me-third of the predicted orientations are missing. A graphical analysis can then be used to show that in deformed austenite certain crystallographic variants of martensite (related to the most probable austenite slip systems) are suppressed, resulting in this preferred transformation. The evidence for preferred transformation is corroborated by the measured elastic anisotropy of warm-rolled and fully transformed H-11 steel. EXTENSIVE plastic deformation of a polycrystal-line aggregate in a manner that causes flow predominantly in one direction results in a preferred orientation of the constituent crystallites. The particular orientations that are produced depend upon the crystal structure and composition of the material, as well as upon the temperature, mode, and degree of deformation; in any case, the preferred crystallo-graphic orientations, or textures, are reflected in directionality of mechanical properties. Although such anisotropy may be exploited in certain specialized applications, it is more commonly diminished or eliminated by heat treatment lest it interfere undesirably in subsequent forming operations or in structural design. In the recently developed thermomechanical treatments that significantly enhance the strength of some steels,1,2 considerable deformation of the metastable austenite prior to the martensite transformation is essential to the strengthening process. If the austenite is textured by the deformation, and if the transformation to martensite proceeds according to one of the relationships established for transformation in annealed austenite, then it must be expected that the martensite will also possess a preferred orientation even though the multiplicity of martensite orientations possible in a given austen- ite crystal will tend to restore some degree of randomness. The existence of a residual anisotropy, both mechanical 3-6 and crystallographic,' has been substantiated. In the latter crystallographic investigation, preferred orientations were determined for the martensitic structure of an SAE 4340 steel rolled 72 pct as austenite at 833°C and then quenched. However, the choice of a composition that transformed almost completely to martensite during the quench to room temperature did not permit direct measurement of the prior austenitic texture. In fact, when the "ideal orientations'' associated with well-known fcc rolling textures were converted, alone or in combination, to martensite according to the Kur-djumov-Sachs (K-s)' or Nishiyama8 relations, the agreement obtained with the observed martensite texture was only fair at best. Recently a pertinent aspect of the austenite to martensite transformation was reported by Bokros and parker,10 who found that certain habit-plane variants of martensite were suppressed by tensile deformation of Fe-31.7 Ni single crystals prior to the necessary subzero cooling. It might be anticipated that the consequences of such preferred transformation are sustained during the formation of martensite in warm-worked austenite that has a well-developed deformation texture. The present investigation was undertaken first to establish more firmly the relation between preferred orientations in plastically deformed austenite and in the resulting martensite, and second to examine the textures for evidence of deformation-induced preferred transformation. EXPERIMENTAL PROCEDURES An alloy containing 0.3 pct C, 12 pct Cr, 6 pct Ni, and the balance iron, was selected because the mar-tensite-start temperature (M,) of about -100°C allowed convenient experimental manipulation of either austenite or martensite at room temperature. Furthermore, this composition can be readily deformed as metastable austenite at moderately elevated temperatures without intervention of appreciable isothermal or athermal decomposition products. The alloy was austenitized at 1150°C, aircooled to 510°C, rolled unidirectionally at this temperature to 93 pct reduction of cross-sectional area, and finally oil-quenched to room temperature. Partial transformation to martensite was accomplished by quenching to -196°C as needed. The rolled stock was reduced in thickness from 0.067 to 0.010 in. by etching in a solution of 5 pct HC1, 45 pct HNO3, and 50 pct water, and further thinned by careful mechanical polishing to maintain the two sides of the sheet parallel within 0.0003 in. After mechanical polishing to 0.005 in., electropolishing in 1:9 perchloric-acetic acid solution produced a final thickness of 0.002 in. The preferred orientations were determined from

Jan 1, 1968

By J. D. Verhoeven

The effectiue distriblltion coefficient has been Measured in a series of vertical, normal freezing experirtzents with large current densities passing through the solid-liquid interface. The results indicate that the effect of the current on solute redistribution is due to electvotransport in the liquid. The high currents produced extensive mixing in the liquid which was considerably reduced by solidifying in small lubing. Analysis of the convection indicates that it probably vesulls from a horizontal temperature gradient produced by the Joule heating- of the electvic crirver~t. Due to the strong dependence of this convection upon the specimen radius, it is conclnded that only for specit~ens with radii of less than somewhere between 1 and 2 mm wilt electric field freezing be getlerally effec-tire at enhancing the purification of zone-melting experittierats in loe-melting alloys. Experiments on 0.8-mm lubes illustrate some interesting potential applications of this techniqne as a means of solute control on smcrll specimens. In a number of papers published within the last few years'-4 it has been found that passage of large dc currents through the solid-liquid interface of a freezing alloy produces a change in the solute redistribution accompanying the solidification. It had been predicted theoretically by Hucke et al.s and by Pfann and Wagner that such an effect would occur as the result of electrotransport within the liquid boundary layer at the solid-liquid interface. These authors independently derived the following relation between the effective distribution coefficient and the variables of the process: Where k0 is the equilibrium distribution coefficient, V is the mobility of the solute relative to the solvent, E is the electric field intensity, D is the solute diffusion coefficient, R is the rate of interface motion, and 6 is the boundary layer thickness. Both groups of authors show that this equation predicts the possibility of extending the purification ability of zone-melting experiments by the addition of an electric current. However, there are other effects in addition to electro-transport which could be produced by the high dc current and might, perhaps, invalidate the applicability of Eq. [I]. For example, high electric current might affect the interface reaction or perhaps the equilibrium distribution which was assumed to exist at the interface. It was the purpose of this work to determine the applicability of Eq. [I] by systematically investigating a simple system for which all of the necessary parameters were known. It was of particular interest for speculating on the potential usefulness of this technique to determine the maximum practical field intensities obtainable, and the effect of these high fields upon convective mixing in the liquid. The initial work in this study was published in a previous paper3 which will be referred to as I. In that work, a current density of 2000 amps per sq cm was used with specimen diameters of 5 mm. The results gave a qualitative confirmation of Eq. [I.], and also showed that a large amount of convective mixing was produced in the liquid by the current. The present study is an extension of that work to smaller specimen diameters and higher current densities. Two points were overlooked in I and will be emphasized here: a) the value of ko has not been well-established in the Sn-Bi system and b) the observed convection could be due to thermal convection produced from the Joule heating. EVALUATION OF k0 To evaluate Eq. [ I.] it is necessary to know the value of the equilibrium distribution coefficient, k,. Tn I the value of k, was taken as 0.3 from a published phase diagram.7 According to ansen' the best data on the phase boundaries of the Sn-Bi system are those of Davidson.5 The data of Davidson give a k, value ranging from 0.21 to 0.25 for the compositions studied in this work, or an average value of around 0.23. In a recent publication, Rigaud and Tougas'10 determined ko by means of a solidification technique. For an alloy of approximately the same composition as that used in this work they obtained a ko value of 0.39. Hence, there is considerable uncertainty in the value of ko and, consequently, a series of experiments were made to determine k, more accurately.

Jan 1, 1968

By C. A. Stickels, C. M. Yen

Secondary recrystallization was investigated in vacuum-melted electrolytic iron to which 70 pm N was vacuum-meltedadded. The secondary texture is "near {554}<225>" for material cold-rolled 75 to 90 pct, the sharpness of the texture increasing with increased rolling reduction and with decreased annealing temperature. At reductions of 95 and 97.5 pct the secondary texture is &apos;"near {322)(296)". Both secondary orientations also exist as major components of the primary re-crystallization texture. Development of a strong "near {554) (225)" secondary texture appears to depend on the evolution of the Primary texture to a transition texture depleted in orientations near the secondary orientation before the onset of secondary growth. A variety of qualitative experinzents have been used to show that nitrogen is important in limiling primary grain growth. The presence of nitrogen does not seem essential for the establishment of a transition texture, but a loss of nitrogen during annealing may facilitate growth of grains in the secondary orientation. Secondary grains we shown to form initially at the specimen surface. This is not thought to indicate that surface energies are important in the growth process. It is proposed that the quasi-two-dimensional character of surface grains permits discontinuous growth parallel to the surface before secondary growth of interior grains is possible. An earlier study of recrystallization textures in 90 pct cold-rolled electrolytic iron showed that secondary recrystallization occurred after annealing for several days at 700C1 This type of secondary recrystallization, which had not been reported previously, results in the formation of a strong texture, best described by the indices "near {554}(225)". The purpose of the present work was to investigate the effect of various processing variables on secondary recrystallization in this material and determine the mechanism of secondary grain growth. LITERATURE REVIEW An understanding of the mechanism of a secondary recrystallization process depends on knowing: 1) how grains in the secondary orientation come to be in the primary recrystallization texture; 2) why normal grain growth does not occur; and 3) what factors determine the strength of the secondary texture. For secondary growth of grains of a particular orientation, a certain minimum fraction of the grains must be in that orientation after primary recrystallization. This requirement is apparently satisfied "naturally" in certain systems, i.e., when the primary texture obtained by rolling and recrystallizing material initially randomly oriented contains a sufficient fraction of primaries in the secondary orientation. However, in other cases, e.g., {110}<001> and {100}<001> secondary growth in silicon iron,2 it is necessary to enhance the fraction of primary grains in the secondary orientation by rolling and recrystallizing textured material. In the present case, the "near {554}<225>" orientation is contained within the spread of orientations found in the primary recrystallization texture of iron or bbc iron-base alloys. In systems where the main driving force for secondary growth is the reduction in total grain boundary energy, secondary growth is observed only when normal grain growth is minimized. Four ways in which normal grain growth can be limited are: 1) Limitation by a strong primary texture. When a very strong primary texture consisting of a single component or twin-related components develop, most primary grains are separated from one another by relatively immobile small-angle grain boundaries. The classic instance of this is secondary growth into the primary cube texture in some fcc metals. 2) Limitation by precipitates. Precipitates present in the proper volume fraction with a suitable dispersion will limit primary grain growth. The role of MnS inclusions in impeding normal grain growth in Si-Fe is well-documented.5 3) Limitation by sheet thickness. Normal grain growth slows drastically when the mean grain diameter is of the same order as the sheet thickness. This effect has been used to obtain secondary recrystallization in thin sheets of high-purity silicon iron.&apos; 4) Limitation by solute impurities. It is well-established that certain impurity elements in solution can have a large effect on grain boundary mobility.&apos; However, there does not seem to be any secondary recrystallization process in which primary grain size stabilization has been shown to be due to the drag exerted on grain boundaries by dissolved impurities. In certain systems, e.g., secondary recrystallization in silver,&apos; the means by which normal grain growth is limited has not been identified, and solute-impurity limitation might be suspected. In order to understand the factors which determine secondary texture strength in three-dimensional growth, it is necessary to examine in more detail the current picture of general secondary recrystallization processes. Following Cahn,9 it is assumed that the primary grains have a range of sizes and that secondary growth of one of the large grains in this distribution is possible when it exceeds a critical size with respect to its neighboring grains. The critical size depends on the ratio ?S/?p, where ?s is some sort of average grain boundary energy between the potential secondary and the primary grains and ?p is some sort of average grain boundary energy between primary grains. For a constant primary grain size, the critical size for secondary growth increases as ?$/?p increases. May and Turnbull5 have incorporated the

Jan 1, 1969

By T. H. Alden, H. W. Schadler

The strain rate dependence of the flow stress of the eutectoid Zn-Al alloy has been determined as a function of mechanical processing, microstructure, and temperature. The best superplastic properties result from the ultrafine, equiaxed structure produced by solution treatment and isothermal transformation at 0°C. Lamellar structures produced by isothermal transformation and coarse equiaxed structures produced by annealing also exhibit strain rate sensitivity in excess of 0.5, but at higher stresses and lower strain rates than the finest structure. Solution treatment and isothermal transformation eliminate the effect of prior processing history. Small composition variations in the binary alloy do not influence the mechanical properties. Below the eutectoid transformation temperature (.275C) increasing temperature lowers the flow stress at all strain rates. The data do not favor any of the present proposals for the mechanism of superplastic flow. ALLOYS of zinc and aluminum, near the eutectoid composition, have been investigated for: 1) the flow stress-strain rate and elongation behavior,1, 2) the transformation kinetics,3 and 3) structure,3"5 but the structure sensitivity of the mechanical properties is poorly understood. Using a near eutectoid alloy water-quenched from 380°C, Backofen et aL2 estab- high and increases with increasing strain rate. They found a correlation between strain rate sensitivity and tensile elongation as expected from the increased resistance to necking that a high strain rate sensitivity provides.296 The large elongation at high strain rates is attractive for metal forming. Since most other superplastic alloys7-l3 do not show high strain rate sensitivity at such a high strain rate (for the exception see Ref. 12) there is the possibility of a unique deformation mechanism for this alloy. The sensitivity of the mechanical properties of the eutectoid alloy to thermal history1 suggests a structure sensitivity that has not been demonstrated. Gar-wood and Hopkins3 identified a lamellar product for material transformed between 200" and 260°C. The size of the lamellae decreased with decreasing temperature. They also demonstrated that an unresolved transformation product formed below 200°C. A granular two-phase material was resolved for specimens quenched to below 150°C by Mitbauer and sauerwald4 who observed coarsening of the structure after annealing. The role of grain boundaries in superplastic deformation is suggested by the strong effect of grain refinement in encouraging this phenomenon at high strain rateS7-11, 13 and is emphasized in several proposals about rnechanism7, 8, 12 and in a theory14 of high-temperature deformation. Alden8 showed metallographic evidence that grain boundary sliding is occurring extensively at strain rates where m is large but less at high strain rates where normal plasticity is observed. Holt and Backofen10 have shown that sliding also oc-

Jan 1, 1969

By T. W. Watson, D. R. Flynn

,Measurements are reported for the thermal conductivity of four heat-resistant alloys which were measured at the National Bureau of Standards. Data are given for two samples of AISI Type 316 stainless steel covering a combined temperature range from -150° to + 800°C. The thermal conductivities of three samples of AISI Type 347 were measured over the temperature range from -150° to +150C. Thermal conductivity values are given for Carpenter 20 stainless steel from 100" to 800" C. Data are given for Inconel 702, in both the solution-annealed and the age-hardened condition, over the temperature range from -150" to +800C. SINCE 1958 the National Bureau of Standards, at the request of other government agencies or private laboratories, has carried out measurements of the thermal conductivity of a number of metals and alloys. This paper presents available thermal conductivity data obtained in this way on samples of four heat-resistant alloys. The data presented for Carpenter 20* stainless steel are, to the best of our knowledge, the only thermal conductivity values which have been reported for this alloy to date. Although thermal conductivity values for AISI stainless steels 316 and 347 have been reported by previous investigators, the present data are believed to be of particular interest because, for each alloy, the effect on thermal conductivity of small changes in chemical composition can be observed. The data on Inconel 702&apos; are of interest, not only for

Jan 1, 1969

By J. T. Berling, J. B. Conway

MANY studies have been devoted to the correlation of low-cycle fatigue behavior. Several of these have also been concerned with the identification of an effective approach to the prediction of low-cycle fatigue behavior from short-term tensile data. Perhaps the first such approach was that reported by coffin1 in the form: where is the plastic strain range, Nf is the number of cycles to failure, and c is a constant characteristic of a material. In this analysis by Coffin it was reasoned that in a short-term tensile test the value of Nf could be considered as equal to a , in which case the value of c is interpreted as the tensile ductility, f, measured in such a test. If, therefore, the Coffin equation is assumed to be applicable to a given material, it is a simple matter to predict the low-cycle fatigue behavior. Once the tensile ductility is known, this point is located at Nf = 1/4 on a log-log plot of vs Nf and a line is drawn through this point with a slope of to yield a prediction for the fatigue life. Actually, while this equation is quite useful it is not generally applicable, for experiment has shown that the value of —$ does not reflect the relationship between and Nf for all materials or even for a given material over all temperature ranges. An equation similar to the Coffin equation was prepared almost simultaneously by Manson.2 This expression had the form: In this case the exponent on Nf was not assigned any particular numerical value in accord with the various values of this exponent which had been observed for different materials and at different test conditions. Because of this characteristic it will be recognized that little use can be made of this expression in predicting low-cycle fatigue results. A fairly effective expression for use in predicting fatigue behavior was proposed by Manson3 based on a study of numerous sets of experimental results. This relation (Method of Universal Slopes) makes use of modulus of elasticity, ultimate strength, and tensile ductility, and assumes an exponent on Nf equal to 0.6 in representing the plastic strain range contribution to total strain range. While this equation of Man-Son does not yield completely accurate results it must be recognized as being the best means available at

Jan 1, 1970

By J. C. Swartz

New measurements of graphite and cementite solubilities in ferrite have been obtained to resolve disagreements among previous data. To measure graphite solubility, specimens of iron were equilibrated with rarious carburizing atmospheres at temperatures be-twee~z 480" and 1435°C. The carbon activity of each atmosphere relative to graphite was taken from published data. After quenching from each equilibration treatment the concentration of carbon (typically 10 pprn by wt) was determined from the height of the Snoek peak in the internal friction spectrum. A few inclividual analyses by combustion support the reszdts of Smith on the solubility of graphite near the eutectoid temperature. Combination of these combustion and internal friction analyses determines In a, (at 0.01 wt pct) = 24,000/RT - 12.72, where a, is the activtity relative to graphite in ferrite at fixed cornposition. The same specimens were used to determine the solubility of self-stressed cementite precipitates. The results indicate solubilities of 6.3, 23.2, and 68 pprn carbon by wt at respectively 400°, 500". and 600°C. The once large discrepancy between the cementite solubility determined by internal frictiori and that calculated from flee energy data has been almost completely resolved. A recent study1 (hereafter designated I) on the solubility of cementite in a iron did not fully resolve the disagreement among previous data. The remaining disagreement is illustrated by the phase diagram in Fig. L The data of I are represented by the line labeled "stress-free" cementite. They determine a heat of solution of cementite of (14.8 * 0.2) kcal per mole which contrasts with the (20 * 1) kcal per mole derived from Smith&apos;s graphite solubility2 and the formation energy of cementite.3 Toward resolving this disagreement we have obtained new data on the solubilities of graphite and cementite. METHODS As in I the Snoek peak in the internal friction spectrum was used to measure the concentration of carbon dissolved in ferrite. This method relies on the relation C=kQ-1 [1] in which C is the concentration of dissolved carbon, Q-I is the Snoek peak height, and k is a proportionality factor which is a function of the peak temperature, polycrystalline texture, and other parameters characteristic of the ferrite lattice. To determine true heats of solution via Eq. [1], it is necessary to establish that k is independent of the temperature from which the specimen is quenched. Some evidence on this point is contained in a separate report.* Additional evidence is shown by the data points in Fig. 1. These represent the Snoek peaks of two specimens carburized to about 10 ppm C, copper plated, and quenched first from 888º then from 588°C. The copper plate was removed before each Snoek peak measurement. These data show that there is no detectable dependence of k on quenching temperature. The solubility of graphite was determined by repeatedly carburizing various specimens of iron wire with gas mixtures of known carbon activity relative to graphite. To cover a wide temperature range within the a phase boundaries it is desirable to use as low a carbon concentration as is compatible with reasonable precision. With the present internal friction apparatus the best compromise of these desires is a concentration near 10 wt ppm. The dashed line in Fig. 1 was used to approximate the activity of carbon* for

Jan 1, 1970

By E. J. Efsic, C. M. Wayman

The fcc to bcc y to a transformation in an Fe-24.5 at. pct Pt alloy was studied and found to be martensitic. Large martensite plates are formed in this alloy which are ideal for crystallographic studies; the Ms temperature is about -5°C. Ordering of the parent phase prior to transformation to martensite causes a pronounced lowering of the Ms temperature. For the first time in the case of alloys of iron, measurements of the habit plune, orientation relationship, and magnitude and direction of the shape stvain have been obtained on preselected martensite plates. It is shown that by measuring the initial and displaced (as a result of the shape strain) positions of three or more non-parallel fiducial scratches on one reference surfice the maguitude and direction of the shape strain and the state of distovtion at the parent-mavtensite interface can be determined with a reasonable degree of accuvacy. The agreement between the phenomenolog-cal crystallographic theory of martensitic transformations and the experimental results habit plune, orientation relationship, and nlagnitude and direction of the shape strain) is essentially perfect, and is thought to be the best reported to date for iron alloys. THE comparatively few investigations on binary Fe-Pt alloys have been concerned with magnetic properties, ordered phases, and the equilibrium diagram itself. Various investigations have shown that the equilibrium diagram is of the open y field type; in addition there is a peritectic transformation, a minimum melting point, and three ordered phases: Fe3Pt, FePt, and FePt3. The results of a number of investigators1-6 have shown that the temperature dependence of the y to a (and reverse) transformation in iron-rich alloys is reasonably well-established. The Fe3Pt phase was first noted by Kussman and Rittberg,7 and its existence was later confirmed by Franklin et al,8 Steijn and Donahoe,9 and Berkowitz et al.10 The FePt phase was reported by Isaac and amman&apos; and later confirmed by a host of others.3,6,7,12,13 Kussman and Rittberg7 noted the existence of the superlattice FePt3. Prior to 1956, the 1 to a transformation in iron-rich Fe-Pt alloys was termed "irreversible". In 1957 Klokholm and Donahoe" termed this transformation martensitic, presumably because of its occurrence at temperatures well below those where diffusion normally takes place. This observation served as a point of departure for the present investigation, and in the very early stages of the work to be discussed it was readily verified that the y to a transformation in iron-rich Fe-Pt alloys is indeed martensitic. Quite large martensite plates exhibiting the well-known surface tilt were observed. These plates are ideal in the sense that the boundaries between the parent and product phases were usually very straight. It thus appeared that Fe-Pt martensites would be ideal for crystallographic studies, and this was the purpose of the present investigation. Details of the crystallography of martensitic transformations (particularly for iron alloys) and the phe-nomenological crystallographic theories15-l7 have been discussed many times and thus will require very little elaboration here. The end result of these theories, given in matrix form, is

Jan 1, 1968

By N. A. Gjostein

The real and apparent dependence of the surface self-diffusion coefficient, Ds, of gold on crystallo-graphic orientation has been investigated by isolated scratch smoothing and grain boundary grooving experiments. No systematic variation of Ds with orientation was found along the [100] zone. In view of the experimental scatter in these results, however, only aniso-tropy ratios, p, greater than -1.3 would be detectable. Anomalously low values of Ds were found on the [0ll] and [110] zones when the diffusion direction lies along (the scratch or grain boundary groove is perpendicular to) these zones. By comparing these results with a previous y plot study of gold, it is hypothesized that this is not an intrinsic diffusivity effect, but rather it results from a decreased driving force for mass transfer at orientations where the y-plot curvature is negative and appreciable in magnitude relative to y. The characteristics of this type of anisotropy do not appear sEVERAL investigations1-7 have dealt with the anisotropy of the surface self-diffusion coefficient, Ds, of metals as measured by the decay of single or multiple to be in agreement with the hypothesis of fast diffusion along ledges in the surface structure. In certain cases the Fourier method of determining Ds, described in Paper I of this series9 was compared with the second moment analysis in order to determine whether or not the method of analysis affects the anisotropy ratio. While the type of analysis does influence the magnitude of the anisotropy ratio, this effect is not associated with the shape of the profile, but rather is connected with the iterative volume diffusion correction used in conjunction with the second moment analysis. It is further demonstrated that the volume diffusion correction can be too large by either method when the y-plot curvature effect is large. Certain orientations exhibit an unusual temperature dependence of Ds ; this is discussed in terms of the y-plot curvature effect and/or the influence of impurities on Ds . scratches in the surface. Depending on the system investigated, both large1"3&apos;6&apos;7 and small4&apos;5 anisotropies in Ds have been found. Although adsorbed impurities undoubtedly play an important role in determining the magnitude of the anisotropy,8 there are other factors that can give rise to an apparent anisotropy in Ds, thus obscuring the true nature of an intrinsic anisotropy in

Jan 1, 1968

By J. W. Spretnak, V. Kandarpa, G. W. Powell, R. A. Erickson

Neutron-diffraction pattens were obtained at room temperature from two austenitic manganese steels, oxc wth n carbon content of 1.23 zct PC/ and the olher 0.63 wt pct. Analysis of the data showed that the curOan atols (ions) occupy tile octaheadral site. any of the cavbon is in the tetahedral site, tile concentration is too strzall lo be detecled by tzeulr-on d$facton. AS part of a long-range investigation of eutectoid decomposition, a study of the structure of austenite has been undertaken in order to characterize as best as possible the parent phase in the Fe-C system. Austenite is a solid solution of carbon atoms in fcc iron, the carbon atoms being located in interstitial positions. Of the two kinds of interstitial sites, octahedral (0, +, +) and tetrahedral (4, a, $), in this lattice, the larger octahedral sites are usually considered as the probable position of carbon. The strain energy involved in pytting a neutral carbon atom (covalent di; ameter 1.54)&apos; into a tetrahedral site (diameter 0.56A) is considerably greater than that associated with p2tting carbon into the octahedral site (diameter 1.08A). Dayal and arkeen&apos; observed the migration of carbon in iron under the influence of an electric field indicating tha tye carbon is ionized. pe ionic radius of C&apos;4 is 0.15A and that of C" is 0.29. Consequently, it is conceivable that carbon ions could occupy the tetrahedral sites if one considers only the strain energy. Size considerations alone do not provide a complete explanation for the formation of the interstitial solid solutions, however. because metals such as copper, zinc, and cadmium do not appear to form interstitial solid solutions in spite of their large interstitial sites. Evidence which suggests partial ioni-zation of the carbon in austenite has also been obtained by Speiser, Spretnak, and alor who derived formu- lae relating the observed change in lattice parameter to the effective diameter of the solute atom. Assuming the carbon occupies the octahedral site. they computed the effective diameter of carbon to be 1.33A whereas the covalent diameter is 1.54A. petch5 concluded from powder X-ray diffraction experiments that carbon atoms occupy the octahedral sites. His conclusion was based on the general trend observed in the intensity of the diffraction lines as the carbon content of the austenite was increased. However, the major difficulty associated with application of X-ray diffraction to this particular problem is the relatively poor scattering power of carbon. Williamson and smallman&apos; utilized X-ray diffraction to study the line broadening caused by the strain field about carbon atoms inferrite: these investigators concluded that at least 85 pct of the carbon in ferrite occupies the octahedral (0: 3, B) site rather than the larger

Jan 1, 1967

By H. Conrad, V. V. Damiano, G. J. London

The slip mode activated during the c axis compression of single crystals of commercial-purity ingot SR beryllium, high-purity (twelve-zone-pass) beryllium, and Be-4.4 wt pct Cu and Be-5.2 wt pct Ni alloys in the temperature range of 25° to 364°C was determined using two-surface slip trace analysis, slip-step height analysis, and electron transmission microscopy. All three techniques indicated the occurrence of copious pyramidal {1 122) (1123) slip in the alloys over the entire temperature range, the amount increasing with temperature. Pyramidal slip was also indicated in the high-purity beryllium by slip trace analysis and electron transmission microscopy, but the amount was somewhat less than in the alloys. For the commercial-purity ingot crystals, only a very small number of pyramidal slip lines were observed, and these were in the immediate vicinity of the fracture surface. No pyramidal dislocations could be detected by electron transmission microscopy in this material. Dislocatransmissiontions with Burgers vectors [0001] and +(ll20) were identified by electron transmission microscopy inthe (1122) slip bands, as well as those with the j (1123) vector. This was interpreted to indicate that the edge components of the 3(1123) vector dislocations activated during c axis compression dissociate upon unloading according to the reaction i (1123) — [0001] + 3(1120) THE microstrain c axis compression of single crystals of commercial-purity ingot SR beryllium (99.6 pct), high-purity twelve-zone-pass beryllium (99.98 pct), Be-5.24 pct Ni and Be-4.37 pct Cu alloys was described in a previous paper.1 This paper covers in detail the analysis of slip traces observed on two mutually perpendicular lateral surfaces of these specimens, and a detailed description of transmission electron microscopy studies performed on foils cut from the bulk crystals after they had been deformed to fracture in the c axis compression. Observation of slip traces on single surfaces of deformed single crystals are generally insufficient to positively identify slip or twinning modes. The use of two carefully cut and oriented perpendicular surfaces can greatly aid in the positive identification and index- ing of slip traces, although even this technique may be quite inadequate if more than one type of slip system operates and if an insufficient number of traces are observed on the surfaces. The problem is greatly simplified for symmetric cases like that for c axis compression of an hep crystal such as beryllium, in which the operating slip systems are all equally inclined to the direction of the applied stress, and each slip system of a given slip mode has an equal chance of operating. For such cases, the traces of any given slip mode observed on the surfaces cut parallel to the c axis are symmetrically tilted about the c axis. It is therefore possible to quickly determine whether one or more slip modes are operating. Confirmatory evidence in support of the observations made on the external surfaces can be obtained from foils cut from the deformed crystals and examined by transmission electron microscopy. This latter technique serves to identify not only the operating slip plane but also the Burgers vector of the dislocations which participate in the slip. For this purpose, a simplified technique based upon a double tetrahedron notation is used in the present paper. The planes and directions in the hep lattice are all designated by letters rather than indices and extinction conditions are easily determined if the Burgers vector lies in the plane contributing to the diffraction. RESULTS 1) Slip Trace Analysis. The standard (0001) stereo-graphic projection of beryllium is shown in Fig. 1. The two mutually perpendicular, lateral surfaces of the compression specimen are represented by the diametrical planes AA&apos; and BB&apos;, also referred to as surface A and surface B. For the specific case represented (a Be-5.24 pct Ni specimen deformed by c axis compression at room temperature), the A surface is tilted 5 deg to the (10i0&apos;) plane and the B surface is tilted 5 deg to the (1120) plane. Two surface trace analyses may be facilitated by examining in turn the intersection of various great circle traces of specific pyramidal planes with two surfaces and comparing the angles made with the (0001) plane with those actually observed on the two surfaces. One then identifies the slip traces by trial and error on a best-fit basis. The (1122) type planes (it was found that slip occurred on these planes) are shown plotted on the stereographic projection in Fig. 1. One obtains directly the angles between the (0001) plane and the {1122) traces by measuring the angle from the periphery to the point of intersection along the lines

Jan 1, 1969

By H. Conrad, V. V. Damiano, G. J. London

A method is described for producing single crystals of high-purity beryllium, Be-4.37pct Cu, and Be-5.24 pct Ni. These crystals were prepared for testing in compression parallel to the [0001] by orienting and lapping to within ±3&apos; of arc of the (0001). Microstrain testing apparatus is described along with c axis compression results for ingot purity beryllium, twelve-zone-pass material, and the above-mentioned alloys. Results show no measurable plasticity for the ingot purity material from -196" to 400°C, although some surface traces of (1122) slip was observed at 200°C and above. The twelve-zone-pass material shows substantial microstrain plasticity at 220°C with slip on (1122). Both alloys show significant plasticity at room temperature and above with slip also on (1122) planes. THE two slip systems which normally operate during the plastic deformation of beryllium in the vicinity of room temperature are:&apos; basal slip (0001)(1120) and prism slip . Pyramidal slip with a vector inclined to the basal plane has been reported for elevated temperatures,&apos;-a but occurs near room temperature only at very high stresses.~ A summary of the available data on the effect of temperature on the critical resolved shear stress for slip on these systems has been compiled by Conrad and Perlmutter.~ It has been postulated6&apos;7 that one of the principal factors contributing to the brittleness of poly crystalline beryllium at temperatures below about 200°C is the difficulty of operating pyramidal slip with a vector inclined to the basal plane. Hence, detailed information on the operation of such a slip system is important to understanding the brittleness of beryllium. The operation of pyramidal slip with a vector inclined to the basal plane is best accomplished in beryllium by compressing single crystals in a direction parallel to the c axis. In such a test the resolved macroscopic shear strzss on the basal and prism planes is zero and (1012) twinning which is favored by tension along the c axis does not occur. Hence, in c axis compression of beryllium the normal deformation modes are inhibited and the operation of pyramidal slip with a vector inclined to the basal plane is favored. In the present investigation, c axis compression tests were performed on beryllium single crystal as a function of temperature (77" to 700°K), purity (commercial and twelve zone pass), and alloy content (4.37 wt pct Cu and 5.24 wt pct Ni). Presented here is a description of the test techniques employed and the gross mechanical behavior observed. A detailed analysis of the slip traces developed on the surfaces of the deformed specimens during these tests and the results of electron transmission studies of the deformed crystals are given in a separate paper.B PROCEDURE 1) Materials and Preparation. Single crystals about 1 in. diam were prepared of the following materials: commercial-purity beryllium, high-purity beryllium, and two beryllium alloys, one with 4.37 wt pct Cu and the other with 5.24 wt pct Ni. The commercial-purity single crystals were obtained by cutting specimens from large-grained ingot of Pechiney SR material, which is approximately 99.98 pct pure. The high-purity crystals were prepared by floating-zone refining (twelve passes) a rod (7 in. by 1 in, diam) of Pechiney SR grade cast and extruded beryllium. Although an absolute chemical analysis of the zone-refined material was not established, mass spectro-graphic analysis, emission spectrographic analysis, and y activation analysis indicated that it contained in atomic fractions about 5 to 10 ppm each of carbon and oxygen, 1 to 5 ppm each of nickel and iron, and about 1 to 2 ppm of copper, with the remaining residual impurities being less than 1 ppm. Further indication of the purity of this material is provided by the critical resolved shear stress for basal slip, which was approximately 300 psi. The starting material for the alloy single crystals was 1-in.-diam floating-zone-refined (six passes) rod of Pechiney SR grade beryllium. Two such rods were wrapped respectively with sufficient weight of wire of high-purity copper (99.999 pct) or nickel (99.999 pct) to yield a 5 wt pct alloy. A seventh floating-zone pass was then applied to each of the rods to accomplish the initial alloying and an eighth pass for homogenization. Analytical samples were taken from regions of the rod immediately adjacent to where the mechanical test specimens were cut; these indicated 4.37 wt pct Cu and 5.24 wt pct Ni. 2) Crystal Orientation. To avoid the occurrence of basal slip during c axis compression testing, it is necessary to load the crystals as nearly parallel to the c axis as possible. Preliminary c axis compression tests indicated that plastic flow and/or fracture occurred at stresses of the order of 300,000 psi; hence on the basis of a critical resolved shear stress for basal slip of 300 to 400 psi, the maximum crystal misorientation permitted is about 4 to 5&apos; of arc. Since this accuracy cannot be obtained using the usual back-

Jan 1, 1969

By R. L. Pober, L. Kaufman, E. V. Clougherty

Composite structure of hafnium, zirconium, and titanium diboride with additions of metals and/or compound phases were prepared by reactive high-pressure hot pvessing and evaluated in air and in mixtures of oxygen and helium at temperatures up to 2400°K and at linear flow rates of 0.1 to 0.2 ft per sec stp. Oxidation characteristics, principally depth of conversion of diboride to dioxide, were determined by a gas analysis method and by postoxidation metallo-graphic analyses. The best oxidation resistance was observed for hafnium diboride-silicon carbide composite which exhibited a 6-mil conversion to dioxide for a 1-hv oxidation in air at 2200°K compared to a 20-mil recession for hafnium diboride with no additive. Analogous improvements in oxidation resistance were observed for the addition of silicon carbide to zirconium. EARLIER investigationof the oxidation behavior of the diborides of the transition elements of Groups IVA and VA in flowing gas mixtures have produced a ranking of these compounds according to which HfB2 is the most oxidation-resistant followed in turn by ZrB2 > TiB2 > TaBz > NbB2. Other ~tudies~-~ have examined the physical, thermal, and thermodynamic properties of these diborides to provide a sound basis for the more detailed and specialized investigations which are required to generate the information needed to assess the usefulness of such materials in high-temperature oxidizing environments. Recent oxidation studies7 have examined the effect of variations of metal and boron content on the oxidation characteristics of zirconium and hafnium diboride in flowing gas mixtures including air and helium plus oxygen. Results obtained in the latter investigation confirmed the superior oxidation resistance of HfB2 over ZrB2. Moreover, metal-rich compositions of hafnium diboride showed improved oxidation resistance over boron-rich compositions at temperatures up to 2000°K; at higher temperatures the differences are not distinguishable. In particular HfBI.7 exhibited a diboride to dioxide conversion depth of 4 mils in 1 hr at 2000°K; HfB2. 2 exhibited a conversion depth of 16 mils for the same exposure.~ Specimens for the study of metal and boron stoichiometry on the oxidation characteristics of HfB2 and ZrB2 were prepared by high-pressure hot pressing, a specialized type of fabrication which produced dense crack-free bodies of the desired compositions with no significant impurity introductions. The purpose of the present investigation was to explore the possibility of further improving the oxidation resistance of the metal-rich ZrB, and HfB2. The plan to accomplish this objective was based in the formulation of several diboride compositions containing other compounds and phases which are generally known to have good oxidation resistance in one or more types of test environment. Ideally, such additives would also enhance or at least not diminish other boride property values principally mechanical strength and those parameters related to thermal stress resistance. The additions selected for HfBz included zirconium, aluminum, and (Ta + TaB2) designed to produce ternary metal diborides, hafnium to form a discrete HfB phase, chromium to provide a metal skeletal phase, (Hf + Si) to form a discrete hafnium silicide phase, and Sic to provide a discrete second phase. Additions to ZrB2 included A1 + B designed to produce a ternary metal diboride, Zr + Si to form a discrete zirconium silicide phase, and Sic to provide a discrete second phase. All the specimens were prepared by high-pressure hot pressing which was used to advantage to fabricate billets of the variety of compositions desired and suitable for oxidation testing. The present investigation also included the evaluation of high-pressure hot-pressed TiB2and TiB2-20 vol pct Sic, conventionally hot-pressed Boride 2,&apos; and KT silicon carbide. Boride

Jan 1, 1969

By R. E. Miner, J. K. Jackson, T. L. Wilson

THE nature of the decomposition reactions producing hardening in aluminum-rich A1-Ag alloys is now fairly well understood. The silver is not uniformly dispersed even at temperatures above the solvus line: rather, it is clustered into zones and associated with dislocations.&apos; During quenching, nearly all of the silver segregates into zones&apos; and some is attracted to dislocations, producing stacking faults. Growth of these faults produces the semicoherent y precipitate.1 During aging, the larger zones and the y precipitates grow at the expense of the smaller zones. The large zones persist up to about 350°C; where they redissolve in favor of the y&apos; and y precipitates.&apos; The equilibrium hcp y precipitate occurs both by a cellular reaction at the grain boundaries1 and by growth of the Y&apos; plates to a critical size where incoherency results. Damask and Nowick 4 observed an internal friction peak in an A1-6 at. pct Ag alloy at about 140°C (0.25 cps). The peak was found to exhibit a systematic instability. After aging at successively higher temperatures between 155&apos; and 23Z°C, the peak first migrated to higher temperatures while increasing in height, then returned to lower temperatures and decreased in height. After aging at temperatures above about 200°C, the peak position remained constant while the height decreased very slowly. In quenched specimens, elastic after-effect measurements inhcated a rapid initial transient in peak position from low temperatures up to 155°C. The authors concluded that a stress induced growth and resolution of the clusters and the 7&apos; was the most reasonable mechanism to account for the behavior. It would seem, however, very unlikely that both the clusters and the y&apos; precipitate would provide damping contributions whose relaxation time and activation energies were identical, which is required for them to produce the same internal friction peak. The present investigation was motivated by this apparent anomaly and the development of a very low thermal inertia torsion pendulum5 capable of monitoring transient behavior. Low frequency internal friction measurements were made on four binary A1-Ag alloys nominally containing 5, 10: 15, and 20 at. pct Ag. The results of measurements made on a 10 at. pct Ag alloy in the quenched condition are shown in Fig. 1. There are two peaks apparent in the spectrum, one centered at about 160°C, the second at about 210°C. The two peak spectrum was observed in each alloy, but it was best resolved in the 10 pct Ag specimens. Because of the instability in the internal friction, 4 it seemed possible that the second peak was not a peak at all, but simply a manifestation of a single, sharply transient, peak. This effect has been observed in Au-Ni alloys.6 The existence of the higher tempera-

Jan 1, 1970

By R. J. Fruehan

The oxygen activity and concentration were measured in Fe-Cr-0 melts in equilibrium with an oxide phase at 1600°C (2912°F). The activity was determined by ,use of the following solid oxide -electrolyte galvanic cell CY-Cr8,(s) I ZrOz(CaO) I Fe-CY-G(saturated)(l) The oxygen concentration decreases with increasing Cr concentration to about 270 ppm 0 at about 7pct CY and then increases gradually. The activity coefficient of oxygen (fo) decreases with increasing Cr. In melts containing up to about 20 pct Cr, log f is approximately a linear function of wt pct Cr with a slope (e q 2) of —0.037. The activity of chromium was calculated and found to exhibit a small negative deviation from Raoult&apos;s law. From the activity and solubility data for low chromium melts, the free energy of formation of chromite, FeCr204, was found to be -79.8kcal per mole where pure liquid chromium and oxygen at I wt pct in Fe are the standard states. ThE effect of chromium on the chemical behavior of dissolved oxygen in liquid iron is of great importance in controlling the deoxidation of steels containing a significant amount of chromium. Chen and chipman&apos; equilibrated Fe-Cr melts in the presence and absence of slag with hydrogen-water vapor mixtures. They concluded that at 1595°C chromite was the oxide phase in equilibrium with Fe-Cr alloys containing less than 5.5 pct Cr while at higher chromium concentration Cr,O, was the stable phase. In the composition range 0 to 10 pct Cr they found that the interaction coefficient, was equal to -0.041. Turk-dogan,&apos; Schenck and Steinmetz,, and pargeter4 measured egr) in a similar manner and found the value to be -0.064,-0.04, and -0.052, respectively. McLean and Be11 evaluated egr) from their data on the equilibrium of Fe-Cr-Al-0 alloys with H2/H20 mixtures and found it to be -0.058. However, McLean and Bell&apos;s value should only be considered an estimate because the effect of aluminum on the activity coefficient of oxygen is about a hundred times greater than that of chromium. Consequently, an error in the value of egl) used, which at the present time is not well-known, or an error in aluminum analysis, which is present in very small quantities, will result in a significant error in egr). Fischer et a1.6 determined the interaction coefficient (eEr) in Fe-Cr-0 melts not in equilibrium with an oxide phase and containing less than 18 wt pct Cr at 1600°C electrochemically. They determined a value of -0.031 for egr). Hilty et aL7 measured the oxygen content of Fe-Cr melts in equilibrium with an oxide phase containing up to 50 pct Cr. They found that the solubility of oxygen decreased as the chromium content increased to about 6 pct Cr and then increased gradually. They concluded that the equilibrium oxide phase was chromite below 3 pct Cr, distorted spinel from 3 to 9 pct Cr, and Cr,04 above 9 pct Cr. Adachi and lwamotoa also investigated this system, but did not find Cr30,. They X-rayed the equilibrium oxide phases and did not find the presence of Cr,O,. They also X-rayed the oxide phase extracted from a 65 pct Cr melt which was heat treated and did not find metallic chromium as would be expected if Cr3O4 were the equilibrium oxide phase as indicated by the reaction : 3Cr3O4 — 4Cr2O:, + Cr [lj It was the purpose of the present investigation to determine the effect of chromium on the activity coefficient of oxygen in Fe-Cr melts by measuring the activity and solubility of oxygen equilibrated with an oxide phase in the composition range 0.18 to 50.5 wt pct Cr at 1600°C (2912°F). The activity of oxygen in the melts was determined by use of the following galvanic cell: The relationship between the partial pressure of oxygen in equilibrium with the melt and the reversible electromotive force of the cell (E) is where 11 = 4, F is the Faraday constant, pb, is the oxygen pressure in equilibrium with the meit and is the oxygen pressure in equilibrium with Cr203 as determined from the free energy data compiled by Elliott et al? The oxide phase in equilibrium with pure chromium was assumed to be Cr If Cr30, were the equilibrium phase the activities derived would be approximately the same, since the best estimated free energy of formation of Cr,O,, if it does exist, is approximately % the free energy of formation of The activity of chromium in Fe-Cr alloys at 1600° C was also determined from the measured electromotive force. The activity of chromium (aCr) is related to the electromotive force as follows: , The oxide phase in equilibrium with pure chromium and Fe-Cr melts from 10 to 52 pct is assumed to be Cr203 so that n equals three. If future work proves the existence of Crs04 in equilibrium with Fe-Cr melts and pure chromium, the experimental results can be reevaluated using a value of $ for n in Eq. 141. A value of ^ for n will make the activities about 10 pct higher. In order for Eqs. 131 and [4J to be valid the electrolyte, ZrOa(CaO), must exhibit predominantly ionic conduction at the temperature and oxygen partial pressure of its use. Previous work1&apos; has demonstrated that ZrOz(Ca0) is predonlinantly an ionic conductor

Jan 1, 1970