By D. E. Woolley

The rate of reduction of iron oxide from calcia-silica-alumina slag by carbon in liquid iron has been measured over the temperature range 1400-1600°C by monitoring the rate of carbon monoxide (CO) evolution. Slags containing ferric iron have been used in order to study the reduction of both ferric and ferrous cations. Results show that ferric iron is reduced before ferrous iron, so that the ferrous iron concentration increases initially. It is also shown that the rate constant, k, decreases at low reaction rates, or, equivalently, at low concentrations. The authors conclude that the reaction occurs in two periods. During the first period, ferric iron is reduced to ferrous iron. During the second period, ferrous iron is reduced to metallic iron, and the rate-limiting step during the second period is the mass transfer of ferrous cations in the slag phase to the slag-metal interface.

Jan 1, 1998

By P. J. Bhonde, R. D. Angal

Conventionally low carbon ferromanganese is manufactured globally by refining high carbon ferromanganese in liquid state. This process is an expensive and lengthy technique. Hence, the present work was undertaken with the objective of understanding the feasibility and kinetics of the solid state refining of ferromanganese. The process involved transformation of carbon rich carbides viz. Mn3C2, Mn7C3 into metal rich carbide i.e. Mn15C4, Mn23C6 by subjecting the alloy powder to a flowing stream of carbon dioxide. Effect of the process governing parameters such as time, temperature, particle size, pressure on the extent of decarburization was studied. Without any loss of manganese in the form of fumes or slag, it was observed that, there was substantial reduction, viz. 65 per cent in the total carbon content, by this technique. Subsequently, the process was investigated to find out the mechanism of carbon removal. Depending upon the temperature and the particle size, it was found that the rate controlling mechanism changes from chemical reaction control to product layer (ash) diffusion control. The activation energy for each of the aforesaid mechanism was computed. The values thus obtained substantiated the aforesaid mechanisms.

Jan 1, 2004

By F. Dai

Due to difficulties associated with gripping in direct tension, indirect methods are commonly used to measure rock tensile strength. In this work, we adopt an innovative indirect tensile test method: Semi-Circular Bend (SCB) to measure the tensile/flexural strength of Laurentian granite (LG). The static tests are carried out with a servo-controlled material testing machine and the dynamic tests are conduced with a Split Hopkinson Pressure Bar (SHPB) system. Pulse shaping technique is adopted to achieve dynamic force equilibrium in SHPB to facilitate data regression. Finite element method is used to relate the failure load to the tensile strength. Strong rate dependence of the tensile strength is observed. The flexural strength is higher than the tensile strength measured using Brazilian Disc (BD). This difference is rationalized using the non-local theory. To further validate the method, a coupled Finite element/Discrete element method (Fem/Dem) in conjunction with the smeared crack model is utilized to simulate the fracture process during dynamic SCB tests. The resulting fracture patterns are qualitatively consistent with those from recovered samples. Both the experimental and numerical methods have validated the results and this new method is readily to be used for other rocks and other brittle materials.

May 1, 2009

By Winn B. Frank

Events of the mid-1970's have materially affected US coal production and transportation by railroad. Coal, as a replacement or substitute for petroleum fuels, has been hauled in significantly increased tonnages. Concurrent with the new demand, the railroad regulatory environment has undergone major changes, especially in "deregulation" activity. Those two events have produced considerable Litigation regarding coal rates. This paper discusses the factors involved with railroad rates and topics such as revenue adequacy, Ramsey Pricing, stand-alone cost, and differential pricing. In addition, an update on the western railroad merger situation and the implications for coal transportation are presented. The paper concludes with an evaluation of the current regulatory climate and future prospects.

Jan 1, 1983

By W. C. Meyer

A physical model of flotation, derived from viewing froth as a kinetic species since it constitutes the carrier of ore particles, not only agrees with and is simulated by engineering math models, but is statistically verified by actual laboratory flotation data. The model couples the mechanical removal of froth using paddles with the more rapid chemical interactions taking place in the bath. It clearly shows that the kinetics of mass removal is dictated by flotation cell dimensions, paddle speed, and, more importantly, froth characteristics. Some conclusions and predictions of the model are presented.

Jan 1, 1982

By Alexander Field

THE rate of elimination of carbon largely controls the time required to make a heat of steel by the basic open-hearth process and to an important degree determines the cost of refining. Practical experience has led to the generally accepted belief that the use of slags relatively high in iron oxide, such as are required to bring about rapid refining, leads to a certain sacrifice of quality in the product. As a consequence, a compromise must be made between the exceedingly slow rate of carbon drop which would correspond to the ideal case and the rapid rate which would best satisfy the condition of minimum cost. An increase in rate of refining necessarily implies an increase in the concentration of iron oxide dissolved in the metal. However, even for the infinitely slow rate that corresponds to slag-metal equilibrium, the metal would contain a certain definite concentration of dissolved iron oxide. It is a matter of great practical importance, therefore, to determine the quantitative relation between the minimum or equilibrium concentration of iron oxide in the metal and the higher concentrations which must actually obtain in practice. The present paper is devoted to the development of certain equations, derived from the established laws of physical chemistry, which will enable this relation between rate of refining and the degree of oxidation of the metal bath to be computed from operating data. No attempt is made to exhaust the possibilities of this general method of treatment. In considering rate of refining, attention is mainly confined to rate of carbon elimination. However, the equations are of a more general nature and their application may readily be extended. The results of the preliminary calculations given herein indicate that increased rate of refining may have a decided effect in increasing the concentration of iron oxide dissolved in the metal. The uncertainty. which attaches to the calculated value for this relationship arises in part from probable errors in experimental data on which the calculations are based, and in part from the lack of complete or favorably disposed information on basic open-hearth practice.

Jan 1, 1928

By Alexander Field

IN THE light of the experimental data on equilibrium for the reaction C + FeO = Fe + CO in molten steel recently obtained by Kinzel and I Egan,1 it is necessary to revise current theories regarding the nature of equilibrium between carbon and FeO in the basic open-hearth furnace. According to the measurements of these investigators the equilibrium constant m for the above reaction for a pressure of dissolved CO equal to 1 atm. is equal to 0.0005 at 1550° C., when concentrations of carbon and. FeO are expressed in percentages by weight. Their work also shows that, with the pressure of CO fixed at 1 atm., not only is the product of carbon and FeO constant, but carbon and FeO are each independently constant-a circumstance which might have been predicted from theoretical considerations. At 1550° C., carbon is constant at about 0.025 per cent. and FeO at about 0.020 per cent., with the pressure of dissolved -CO equal to 1 atm., the product of these two constants being equal to the originally mentioned constant of 0.0005. Available data on the dissolved FeO content of samples taken from the metal bath at practical slag-metal equilibrium prove that this FeO content is determined solely by temperature and the effective FeO content of the slag. The distribution constant r at 1550° C., as determined by Herty, Gaines, Larsen, Simkins, Geruso and Watkins2 is equal to 0.0086. A slag would have to contain 0.020/0.0086 = 2.3 per cent. effective FeO or less in order to prevent the metal from containing more dissolved FeO than that required for equilibrium with CO at 1 atm. pressure. Such low percentages of FeO are never found in basic open-hearth slags at the completion of a heat when rate of carbon drop has become practi-

Jan 1, 1930

By J. B. Goddard

Abstract. Leaching of, uranium in situ from sandstone deposits with ammonium carbonate solution containing: dissolved oxygen occurs rapidly compared with the leaching of the bulk of the sulfur present as FeS2. However because of their high reducing, capacity and their relative abundance, the FeS2 minerals consume; the bulk of the oxidants A pressure leach apparatus was-construtted which permitted the measurement of oxygen consumtion by FeS2. Oxygen consumption by FeS2 is best described by a first-order reaction. The experimental rate constants for various cores are roughly proportional to their FeS2 contents.

Jan 1, 1980

By Cyril Wells

THE diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migra-tion of carbon in gamma iron occurs.1,2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with com-position, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schönert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Cyril Wells, Robert F. Mehl

THE practical importance of a knowledge of the rates of diffusion of carbon and of alloying elements in steel has often been pointed out 1,13 This importance ties chiefly, though by no means only, in the study of carburizing and in the study of reactions involved in the eutectoid inversion in steel The present paper is one of a series in which the rates of diffusion of carbon and of alloying elements in y-Fe and their mutual effects are measured with precision The present paper reports the results of meas¬urements of diffusion coefficients D of manganese in -y-Fe over wide ranges of temperature, and concentration, and of the effect of carbon and impurities and of grain size upon these diffusion coefficients [$] Data on the rate of diffusion of manganese in y-Fe have been reported by Fry2 and by Paschke and Hauttmann 3 Claussen4 calculated the diffusion coefficient D from Fry's data as 3 X 10-10 sq cm per sec at 960°, which will be shown to be incorrect by many orders of magnitude Paschke and Hauttmann gave a rough value of 9 6 X 10-8 sq cm per sec at 1400° Neither of these workers considered the variation of D with concentration and with temperature, and neither studied the effect of carbon METHOD AND MATERIALS Method -The method employed is identical with that used earlier 5 Owing to the volatility of manganese and the consequent loss of manganese from the outer surfaces of the welded diffusion bars, these surfaces were discarded The diffusion anneals were performed in argon, except one (test 18) in which hydrogen was employed for purposes noted below The temperatures reported are accurate to about 3° and constant within I°C , the diffusion times are reported to the nearest half hour The specimens were furnace-cooled after the diffusion anneal at about 2° per min Layers, usually 0 004 in thick, parallel to the welded interface, were machined from the specimens after the diffusion anneal and analyzed for manganese to 0 01 per cent Mn, the distances of these layers from the interface was measured to ±0 0002 in The concentration-penetration curves obtained were analyzed by both the Grube and the Matano solutions e The D values calculated by these two methods do not differ appreciably 5 The Grube solution was used except in tests in which the effect of concentration upon D was greater than 50 per cent, in such cases the Matano method, which explicitly provides for the variation of D with concentration,1 is the more reliable In general, the number of layers machined from the zones of variable composition were large enough to permit the use of the average layer composition as that of the center of the layer In 3 of the 30 tests, however, this is not justified, and the D values

Jan 1, 1941

By Cyril Wells, Robert F. Mehl

THE two earlier papers in this series1,2 presented data on the rate of diffusion of carbon and of manganese in gamma iron. Apart from their scientific interest, these [] data are needed chiefly in order to treat data on carburization, on the rate of formation of pearlite, and on the rate of austenizing in a quantitative way. 1,2,9,10 In the present investigation rates of diffusion of nickel in -?-Fe over wide temperature and concentration ranges have been determined, and the effects of carbon, of impurities, and of grain size on these rates have been studied. Claussen,3 using the data of Fry,4 has calculated the diffusion coefficient of nickel [ ] in -?-Fe as 9.2 X 10-11 sq. cm. per sec. at 1200T., but had no data from which to calculate the variation of D with concentration, temperature, and percentage of carbon. METHOD AND MATERIALS Method.-Nickel was diffused along the axis of a cylindrical specimen across a concentration gradient, concentration-penetration curves were determined and D values calculated from Grube or Matano solutions.5 Details of the method are given

Jan 1, 1941

By R. F. Mehl, B. Lustman

THE formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.1 It is necessary here only to enumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type-i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained-the isothermal growth of the phase follows a simple parabolic equation: [1 = ki [I]] where X is the thickness of the alloy layer, k the reaction rate constant, and [t] the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such a plot has been considered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.3 In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varies with temperature according to the Arrhenius equation: [k = Ae-QIRT [2]] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. All phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase.4 The reaction layers tend to have a

Jan 1, 1942

By R. F. Mehl, B. Lustman

THE formation of intermediate phase layers in cementation processes has been subjected to extensive qualitative investigation though to relatively little quantitative study; this work has recently been fully summarized by F. N. Rhines.1 It is necessary here only to enumerate the general conclusions drawn concerning the kinetic laws governing the growth of intermediate layers and to state what is known concerning the structural changes accompanying the generation of phase layers. I. When the intermediate phase is protective in type-i.e., when its density is less than that of the base metal, so that a continuous coating is formed and maintained the isothermal growth of the phase follows a simple parabolic equation: X2 = kt [I] where X is the thickness of the alloy layer, k the reaction rate constant, and t the time. The applicability of this equation to diffusion processes is tested by plotting the square of the thickness versus time, or by plotting the thickness versus the square root of time; the resultant achievement of a straight line in such. a plot has been con¬sidered sufficient proof of the validity of this equation. Exceptions have been found where liquid phases are involved in the reaction, where the diffusion layer is cracked,2 and where thin semimetallic oxide and sulphide coatings are formed on metals.3 In the first two cases the thickness increases linearly with time, and in the latter it is a logarithmic function of time. 2. The rate of thickening varies with temperature according to the Arrhenius equation k = Ae-Q/RT [2] where k is the parabolic rate constant of Eq. I, or some other rate-descriptive function, A is the action constant, e the base of natural logarithms, Q the heat of activation, R the gas constant, and T absolute temperature. This equation has been found to be generally valid except when transformations occur during reaction in either the base metal or in the reaction layer; in such instances Eq. 2 is still applicable with different values for the constants A and Q above and below the transformation temperature. 3. All phases that are stable at the temperature at which diffusion occurs will appear in the interdiffusion of two components. In some cases certain of the phases may be too thin to be observed and identified easily. Nonequilibrium phases have never been noted in thick reaction layers; i.e., layers of a thickness that may be discerned microscopically. The relative, thickness of each phase in a diffusion layer is proportional to the concentration gradient and to the rate of diffusion in that phase .4 The reaction layers tend to have a

Jan 1, 1942

By Sadegh Safarzadeh, Anne-Marie Suriano, Stanley Howard

The electrodeposition of metal ions from aqueous electrolyte solutions has been a well-known process for the last half century. With numerous industrial applications such as electroplating, electrowinning and electrorefining, the kinetics of electrochemical reactions involved in the process has been extensively researched. Arrhenius-type rate equations, the Butler-Volmer equation, and the empirical Tafel equation are among the most important models to explain the rate of electrochemical reactions. The study of the kinetics of metal deposition is critical to understanding the underlying mechanisms through which a certain morphology of metal deposit is formed on the cathode. The purpose of this paper is to elucidate the influence of experimental parameters such as pH and additives on the rate and the reaction mechanism determining the rate limiting step of the electrodeposition reactions.

Jan 1, 2015

By Frederick C. Hull, Robert F. Mehl, Robert A. Colton

IT is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth 12 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in 1939 3 Two types of process were described (I) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemispheres and then after impingement as roughly radial-columnar structures, and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth Both cases are met in the formation of pearlite from austenite (Fig 1),2,3 the former, occurring near the knee of the S-curve has been named "grain-boundary transformation," and the latter, occurring at temperatures near AeI, has been named "group-nodule transformation " In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important''' to obtain data on the rate of nucleation and the rate of growth of pearlite Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the actors that affect hardenability, when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite 2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature,, and the degree of homogeneity of the parent austenite The studies are restricted chiefly to plain carbon commercial steels PREVIOUS DATA ON RAID OF NUCLEATION AND RATE OF GROWTH Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Mehl,1 and by Dorn, De Garmo and Flanigan22 It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc ), austenite grain size, and mode of formation of pearlite at the temperatures given

Jan 1, 1942

By Frederick C. Hull, Robert F. Mehl, Robert A. Colton

IT is known that pearlite forms from austenite by a process of nucleation and growth, and that the rate of formation of pearlite may be described by a rate of nucleation and a rate of growth.1,2 The manner in which these two quantities operate to produce the observed isothermal reaction curve has been analyzed in a paper published in 1939.3 Two types of process were described: (1) that in which nucleation occurs at the grain boundaries of the parent phase, with the nodules growing toward the centers of the grains, initially as hemi¬spheres and then after impingement as roughly radial-columnar structures; and (2) that in which nucleation occurs generally, with the nodules growing to full spheres until impingement with other growing nodules restricts growth. Both cases are met in the formation of pearlite from austenite (Fig. 1);2.4 the former, occurring near the knee of the S-curve has been named "grain-boundary transformation," and the latter, occurring at temperatures near Ae1, has been named "group-nodule transformation." In developing our knowledge of the factors that determine the rate of formation of pearlite from austenite, it is important 1,2 to obtain data on the rate of nucleation and the rate of growth of pearlite. Such data, when obtained near the knee of the S-curve, will furnish information of use in understanding the factors that affect hardenability; when obtained at higher temperatures, such data will be useful in understanding the behavior of steels that during heat-treatment react to pearlite.2 It is the purpose of this paper to present data on the rate of nucleation and the rate of growth of pearlite in dependence upon composition, grain size, temperature, and the degree of homogeneity of the parent austenite. The studies are restricted chiefly to plain carbon commercial steels.* PREVIOUS DATA ON RATE OF NUCLEATION AND RATE OF GROWTH Data on the rate of nucleation and the rate of growth of pearlite have been published by Scheil and Lange-Weise,5 by Mirkin and Blanter,6,7 by Mehl,1 and by Dorn, De Garmo and Flanigan.2 It is difficult to interpret the data, for in most cases too little information is given on austenitizing temperatures and times, the state of homogeneity of the austenite (presence or absence of carbide, etc.), austenite grain size, and mode of formation of pearlite at the temperatures given.

Jan 1, 1942

By Curtis Wilson

FROM the results of his investigation of the hardenable copper-nickel-silicon and copper-cobalt-silicon alloys, M. G. Corson1 explained the dispersion-hardening effect by assuming the precipitation of the inter-metallic compounds nickel silicide and cobalt silicide, and on this basis he constructed diagrams for the pseudobinary systems copper-nickel silicide and copper-cobalt silicide. A consideration of these diagrams and of the factors that exert such an important influence upon the rate of precipitation, such as degree of supersaturation, nucleus number and rate of diffusion, leads to the expectation that the rate of precipitation of the silicides on reheating the quenched solid solutions at temperatures below the alpha-phase boundary should increase continuously as the reheating temperature is raised. The present investigation shows that while this rate does increase with the reheating temperature in a general way, it does not do so continuously. Supplements to Corson's diagrams are offered, showing the discontinuities, and slight modifications in the solubility curves are suggested.

Jan 1, 1933

By John R. Lewis

DURING the past few years there has been considerable interest in the sizing and the preparation of the iron ore fed into blast furnaces. Furnacemen know that proper sizing of ore tends to increase the efficiency of the furnace. It has been shown by Joseph1 and his associates that there is a direct relationship between the porosity of an ore particle and the time required for its reduction in the blast furnace. This relationship may be stated as follows: All other factors remaining constant, the time for reduction of a given sample of ore is inversely proportional to its porosity. As a consequence, large pieces of very porous ore, say 3 or 4 in. in cross section, will be completely reduced by the time they reach the hot zone just above the tuyeres, while large pieces of dense, nonporous ore may reach the hot zone with their centers unreduced. This means that for the latter complete reduction will be accomplished by the so-called "direct method;" i.e., where carbon reacts directly with the ore. Some recent work by Philbrook2 seems to contradict this rule. He found that of two unlike ores he studied, the one with the lower porosity reduced more readily. He explained his results as "possibly due to an apparently greater tendency of the `A' ore (lower porosity) to crack during preliminary dehydration and during reduction." This brings his results in line with the rule stated above. It is not the author's intention to enter into a discussion of the merits of "direct" versus "indirect" reduction. It is enough to say that, in general, indirect reduction is desirable. For the greatest efficiency, Gruner's theorem3 requires that all reduction in the blast furnace be indirect. Joseph seems to believe this also, because in his recent article on Some Comparisons between Iron Ore, Sinter and Nodules as Blast Furnace Feed' he concludes that: "In general, the carbon in blast-furnace coke is used most efficiently when the largest amount of the carbon charged reaches the tuyeres." However, P. V. Martin,' in an excellent paper, has shown that some direct reduction may actually increase the efficiency of the furnace; that is, increase its rate of production while maintaining maximum fuel economy. For nonporous ores there is more opportunity to have an excess of direct reduction unless the factors that make for indirect reduction are favored; for instance; the proper sizing of the ore particles. Another factor that has an important bearing on the reduction rate, as it is affected by particle size, is the flow of heat into the particle. The ore particle

Jan 1, 1947

By J. D. T. Capocchi, M. B. Mourao

The rate of reaction between iron oxides and carbonaceous materials, agglomerated as pellets, was studied experimentally by measuring the weight loss as a function of time. The effects of temperature, carbon type, inert gas flow rate, pellet size and additions (sodium. carbonate and Portland cement) were determined. It was shown that the value of the apparent activation energy can display large deviations under different experimental conditions; in the present work it was found to be 226.6 kJ/mol. The reaction with coke is slower than with charcoal, and the rate increases as the flow of inert gas in the reaction vessel decreases. Comparison of the rates for pellets of different sizes has shown that for small pellets the initial rate is faster but that it slows down at high conversions owing to the penetration of inert gas into the pellet. Additions of sodium carbonate and Portland cement increase the rate; sodium. carbonate promotes the catalysis of the Boudouard reaction, which is the slowest of the partial reactions. The increase in the rate with Portland cement is attributed to the release of water vapour

Jun 18, 1905

By K. Y. Lee, J. M. Park, C. W. Park

Laboratory-scale experiments were carried out to investigate the effect of ladle slag composition on the decreasing behaviour of aluminum content in steel, i.e., reoxidation of molten steel in contact with slag, using a vertical tube furnace. The steel composition and the slag system chosen were for ultra low carbon and CaO-Al2O3-FeO-MnO-MgO based to simulate ULC steel grades. It has been observed that the reoxidation rate shows a good relationship with (T. Fe) content in slag. In case of (T. Fe) content higher than 1.5 weight per cent, the reoxidation rate increases linearly with increasing (T. Fe) content. For a given (T. Fe) content, it decreases with the increasing (CaO)/(Al2O3) ratio of the slag. However, in the case of (T. Fe) content lower than 1.5 weight percent, no particular relationships are observed between the reoxidation rate and (T. Fe) content or the (CaO)/(Al2O3) ratio of the slag. These results were used to propose for an aim a slag composition for the ULC steel grades in a steelmaking plant. Keywords: slag deoxidation, slag killing, slag composition control, IF steel, ULC steel grade

Jan 1, 2004