By I. S. Servi, N. F. Graves

THE etch-pit technique has long been used to reveal low-angle boundaries and, in general, the distribution of dislocations in high-purity metals. Often this technique is amenable to quantitative computations,' but generally is affected by some degree of uncertainty because etch pits can be nucleated not only by dislocations, but also by inclusions and surface imperfections. In the case of high-purity zinc, Gilman' reported that etch pits were produced only after adding 0.1 atomic per cent of cadmium to the crystals and aging at a proper temperature. In the course of a study of low-angle boundary behavior in zinc crystals, etch pits were produced in 99.999 pct zinc without resorting to intentional contamination, by etching in a 50:50 HNO3H2O solution. The technique consists of etching until the heat of reaction brings the solution to a boil, and in displacing the etchant rapidly with a stream of cold water, thus avoiding staining. The undesirable features of this technique are the heating effect and the removal of a considerable amount of material. A high polish is obtained if staining is controlled properly; therefore, the etch pits appear very clearly and with excellent contrast when observed under dark field illumination. This is especially helpful for cursory examinations at low magnifications. Several observations were made on zinc crystals of square cross section, having one face parallel to the basal plane and one edge parallel to a slip direction, Fig. l(a). When such a crystal was bent about 2" over a glass die and annealed at 390°C, a sharp boundary was formed only in the inner portion of the crystal. Near the two prismatic faces, perpendicular to the basal plane, the boundary was always branched into many lower-angle boundaries, Fig. 1(b). Attempts to move the main boundary by applying a shear stress to the specimen invariably resulted in curving the boundary, the branched ends remaining pinned in their original location, Fig. 1 (c). The prismatic face, when etched as indicated in the foregoing, revealed the existence of numerous (sometimes up to 30) fine boundaries, nearly parallel to each other. Pre-existing lineage boundaries, generally parallel to the direction of growth, were barriers to the formation of polygonization boundaries and interrupted the continuity of the substructure, Fig. 2. Twin

Jan 1, 1959

By W. D. Forgeng, B. F. Decker

IT has been known for almost a century' that silicon and nitrogen combine when heated to a high temperature. Three nitrides have been reported, SiN, Si3N,, and Si,N, containing 33.3, 40.0 and 42.9 pct nitrogen by weight, respectively. The existence of SisN, is well established but that of Si,N, and SiN is doubtful. The first systematic study of the reaction between silicon and nitrogen was made in 1910 by Weiss and Engelhart" who determined the rate at which silicon absorbed nitrogen at temperatures from 1250°C to

Jan 1, 1959

By W. Rostoker, A. S. Yamamoto, K. Anderko

ALTHOUGH the corrosion resistance of magnesium and its alloys is closely related to iron content, there has been no direct measurement of the solid solubility of iron in magnesium. Bulian and Fahrenhors;1 and Mitchel]2 agree that pure iron or a limited terminal solid solution crystallizes from the Mg-rich liquid. For this reason a magnetic-moment method was selected to estimate that portion of the total iron content which is not in solid solution. Since iron in solid solution in magnesium cannot contribute to ferromagnetism, the difference between chemical and magnetic-iron analyses should yield the solid solubility. By experimentation it was found that the melting of pure sublimed magnesium (99.995 wt pet purity) in Armco-iron crucibles at about 800°C is a convenient way to introduce small amounts of iron. Melts retained 5, 10 and 20 min at 800°C analyzed 0.003,, 0.005,, and 0.018 & 0.001 weight pet Fe, respectively, after being stirred, heated to 850°C, and cast into graphite molds. The as-cast alloys were pickled in acid (dilute HC1 + HNO3), annealed at 600°C for 3 days, scalped on a lathe to remove the pitted surface, pickled again, extruded at about 100°C to 3-mm wire, reannealed 41/2 days at 500°C, and water-quenched. The specimens were again scalped, pickled, and used both for chemical and for magnetic analysis. Most of the precautions described were intended to prevent iron pickup by contact with tools or superficial iron enrichment by volatilization of magnesium during heat-treatment. It is believed that the specimens ultimately used for test were homogeneous and characteristic of phase equilibria at 500°C. Magnetic Analyses A susceptibility apparatus of the Curie type was used for magnetic analyses. Field strengths of up to 10,400 oersteds could be generated. By this method, an analytical balance measures the force of attraction which a calibrated magnetic field exerts on a suspended specimen. The force equation is as follows f/m = M dh/dy where f/m = force per unit mass of sample M = magnetic moment per unit mass dH/dy = magnetic field gradient The dH/dy characteristic of the instrument is determined by the use of a standard palladium sample, and the calibration is made independently for all values of H. Since a large finite field is required to saturate an assembly of ferromagnets, it is necessary to measure the apparent magnetic moment for increasing steps of H until a saturation value is obtained. The percentage of iron in the sample as free ferromagnetic iron may then be computed simply C= 100 (M1/M1) where C = percent content of undissolved iron in sample M1 = saturation magnetic moment of sample per unit mass M1 = saturation magnetic moment of iron per unit mass taken as 217 emu-cm per gm There is no serious difficulty in applying this method except for the unusual magnetic behavior of very fine particles of ferromagnetic substances. It has been found and is the basis for a widely accepted theory that with sufficient subdivision, the magnetic fields required to saturate and the coercive force after saturation rise to exceedingly high values. Recent work on precipitates of Fe and Co from copper solid solutions8 showed that about 5000 oersteds were necessary to approach saturation. The magnetic moments as a function of field strength measured in the present investigation are listed in Table I. Only the 0.018 wt pet Fe alloy yielded a magnetization curve with a fairly well-defined saturation plateau at 3.76x10 -2 emu-cm/ gm. This corresponds to 0.017 & 0.001 wt pet Fe in the alloy. This indicates that the solid solubility must be of the order of 0.001 wt pet Fe. The magnetic-moment data of the other two alloys are badly scattered, indicating that the amount of ferromagnetic iron in these samples is so low that the magnetic forces acting on them cannot be measured accurately by the analytical balance used. Nevertheless, the fact that even the 0.003, wt pet Fe alloy shows ferromagnetism indicates that the solid solubility must be below that value. Acknowledgment This work was sponsored by the Pitman-Dunn Laboratory of Frankford Arsenal, Philadelphia, Pa. The support and permission to publish are gratefully acknowledged. References W. Bulian and E. Fahrenhorst: Zeic. Metallkunde, 1942, vol. 34, pp. 116-170. 2 D. W. Mitchell: AIME Transactions, 1948, vol. 175, pp. 570-578. 3 G. Bate, D. Schofield, and W. Sucksmith: Philosophical Magnsine, 1955, vol. 46, pp. 621-631.

Jan 1, 1959

By G. C. Fryburg, H. M. Murphy

ThE rates of oxidation of metals are usually obtained by heating the metal specimens in furnaces. Such a procedure is satisfactory for most metals. However, there are several metals that oxidize according to the reaction.

Jan 1, 1959

By E. A. Gulbransen, K. F. Andrew

The vacuum-microbalance method was used to study the oxidation behavior of Zircaloy-2 and -3A over the temperature range of 300 to 850°C and at 0.1 atm pressure. The results fit in well with the authors' earlier studies on zirconium. Tin was found to increase the rate of oxidation and also the temperature at which the metal burns. Both the cubic-rate law and the parabolic-rate law gave imperfect fits to the rate data. Since the parabolic-rate law has been derived from accepted physical principles, this rate law was used to interpret the rate data. A heat of activation of 28,600 cal per mole was calculated. The transition phenomenon previously observed in hot-water and steam-corrosion processes was studied systematically for oxygen atmospheres. Observations on the rate of oxidation, color and properties of the oxide films show that the transition phenomenon was associated with a failure in the adherence of the oxide to the alloy. ZIRCALOY-2 and -3A have found important uses in the field of reactor metals due to their low neutron adsorption, good strength and good resistance to corrosion. One feature of the corrosion reaction in steam or hot water is the sharp transition in the rate of corrosion to a higher value after a certain amount of reaction has occurred. This paper presents a study of the reaction of Zircaloy-2 and -3A with oxygen including a study of the transition phenomenon which has been found to occur also in oxygen atmospheres. A comparison will be made between the oxidation behavior of these alloys and the pure metal. It was hoped that a study of the details of the oxygen reaction would lead to a better understanding of the reactions occurring in hot-water and steam atmospheres. Literature Kinetics-—The reaction of Zircaloy-2 and -3A with hot-water and steam atmospheres has been studied by Thomas.' Goldman and Thomas,' Thomas and Forscher," and Thomas and Kass.' Empirical equations for the kinetics of the reaction have been given by Thomas and Forscher." The change from the initial slow rate of reaction to the final rapid rate of reaction has been termed transition with the post-transition corrosion kinetics following a simple linear equation in time. The corrosion behavior in high-temperature steam was similar in many features to the corrosion in high-temperature water. Goldman and Thomas' and Pray and Peoples' have shown that the addition of tin, while increasing the rate of corrosion, counteracts the deleterious effect of nitrogen. The beneficial effect of iron, nickel and chromium was to improve the adhesion of the oxide to the metal as well as to counteract the deleterious effect of nitrogen. Mallet and Albrecht" have studied the oxidation of two zirconium-tin alloys. The cubic-rate law was found to fit the oxidation data for the 1.5 pct tin alloy while the parabolic-rate law was found to fit the data for the 2.5 pct alloy. Kendall' in a recent paper has studied the oxidation of Zircaloy-2 containing 1.5 pct tin in air atmospheres. Transition Phenomenon—In steam atmospheres Thomas' has observed fora 1.8 pct tin alloy containing small amounts of iron, nickel and chromium that transition to a more rapid rate of corrosion at 400°C

Jan 1, 1959

By R. I. Jaffee, E. S. Bartlett, D. N. Williams

The oxidation resistance and fabricability of molybdenum powder-metallurgy alloys containing up to 20 wt pct nickel in the form of a fine dispersion were studied. The effects of dispersion distribution and of amount and type (pure nickel or nickel compounds) of additive were considered. A definite improvement in oxidation resistance was observed, but the amount of improvement fell far short of requirements for an oxidation-resistant alloy. Fabricability by hot-rolling was limited. INVESTIGATIONS at Ohio State university1 and Battelle Memorial institute2 have indicated that the attainment of a truly oxidation-resistant molybdenum-base alloy for high-temperature service, with the coincident retention of high-temperature strength and toughness, will be a difficult, if not impossible, feat. Among the most promising alloy systems studied was the molybdenum-nickel system shown in Fig. 1. Alloys in this system show good oxidation resistance at temperatures well above the normal melting point of molybdenum trioxide because of the regenerative formation of protective nickel-molyb-date (NiMoO4) on the surface of the alloy during exposure at high temperatures. Unfortunately, the required alloy content to obtain oxidation resistant molybdenum-nickel alloys far exceeds the limits of the narrow terminal solid-solution boundary, and closely approaches the peri-tectic composition involving the brittle intermetal-lic compound, MoNi. Because of the peritectic reaction, fusion alloys are characteristically brittle, since the MoNi phase, being the last to form, tends to occur as a continuous grain-boundary network around each molybdenum grain. An added problem with this system is that the protective nickel-molybdate layer formed at high temperatures is unstable, undergoing one or more allotropic modifications upon cooling. The volume changes associated with this modification during cooling are such as to cause violent expulsion of the protective molybdate coating from the surface of the piece. This is, of course, quite detrimental in material exposed to cyclic temperature during service. The research reported here resulted from an attempt to overcome the aforementioned problems associated with the molybdenum-nickel alloys primarily by controlling the amount, size, and location of the MoNi phase. By using powder-metallurgy techniques of alloy preparation and sintering the blended molybdenum-nickel powder mixtures at a temperature below the peritectic reaction temperature, molybdenum-nickel alloys with a randomly dispersed MoNi phase were produced. MATERIALS The molybdenum powder used in the preparation of alloys for this study was commercial hydrogen reduced, minus 325-mesh (Tyler) material. Master alloys, by which nickel was added, consisted of elemental carbonyl nickel powder (12 average particle size), an alloy of 50 wt pct Ni-50 wt pct Cr, and compounds of MoNi, Ni,Si, and Ni2B. The nickel-chromium powder was prepared by filing a vacuum-arc-melted ingot, separating impurities magnetically, and screening to minus 200-mesh. The MoNi powder was prepared by pulverizing a hydrogen-sintered powder-metallurgy compact to minus 325-mesh material. Further sizing of this powder for study of effects of dispersion distribution was accomplished by air classification of the minus 325-mesh powder. The Ni2Si and Ni2B powders were prepared by crushing vacuum-sintered powder-metallurgy compacts to minus 200-mesh material. EXPERIMENTAL PROCEDURE Specimen Preparation—The general procedure followed in the preparation of alloys for testing is described as follows: 1) Blending. Either hand-blending of the powders in a ceramic mortar and pestle for X 1/2 or mechanical blending was used. Hand-blending seemed preferable for optimum homogeneity. 2) Compacting. Most of the blended powders were pressed to green compacts at pressures of 15 tons per sq in. in a single-action die, although some were pressed at 80 tons per sq in. A 1 X 11/4 X 1/4-in. green compact was the standard size for oxidation test material, and 7 X 1/2 X 1/4-in. compacts were used for fabricability test specimens. 3) Sintering. All green compacts were sinteredat

Jan 1, 1959

By P. R. Swann, J. G. Parr

Quenched structures were studied in alloys containing up to 12.5 pct cobalt. The subsequent decomposition of a 10 pct cobalt retained-ß phase alloy was investigated using metallographic and X-ray diffraction methods. Hardness measurements also were made during the decomposition process. Precipitation of Ti2Co is by nucleation and growth; and an activation energy of 50,000 cal per mole was determined. The values of the coefficient ß suggest that the precipitate is pearlitic at temperatures between 450 and 475°C, and spheroidal between 500 and 525°C. THIS paper describes part of a series of invesligations into phase transformations in binary alloys of titanium with transition elements. The general approach is similar to that taken in work on titanium-iron and titanium-nickel alloys.' Previous investigators'' have established the titanium-rich end of the titanium-cobalt phase diagram, reproduced in Fig. 1. Orrell and Fontana' showed that alloys containing more than about 6 pct" cobalt quenched from the ß range, produced 100 pcl retained-p phase. The isothermal decomposition of alloys containing between 0.8 pct Co and 15.5 pct CO was investigated by the same workers in the temperature range 650 to 1000°C. They reported that these alloys transformed into a or Ti,Co depending on the cobalt content, but no quantitative data were given. In the work to be described a series of alloys containing 0.8 pct Co to 12.5 pct Co was examined in the quenched condition. The 10 pct Co alloy (the lowest cobalt content to retain 100 pct ß on quenching) was selected for further work on the tempering kinetics of the ß decomposition. Experimental Procedure Since our own melting equipment was not installed at the outset of this work, the Physical Metallurgy Division of the Department of Mines and Technical Surveys (Ottawa, Canada) prepared the alloys. These were made of Japanese sponge, (which when melted had a value of 103 DPH, using a 1-kg load), and electrolytically prepared cobalt. The al- loys, made up to contain 0.8, 1.6, 3.3, 5.8, 8.3, 10.0 and 12.5 pct Co, were homogenized by swaging into rods at 900°C. Filings were taken from the rods, and any iron chips from the file were separated magnetically. Size fractions of both plus and minus 200 mesh (about 75p) were shown by their constitution, after annealing just below the eutectoid temperature, to contain the same cobalt content. Consequently, it was permissible to use the —200-mesh fraction, knowing it to be representative of the rod composition. Quenching in argon was carried out in a newly designed furnace, whose features include (1) an Inconel furnace tube, (2) a positive pressure of argon maintained at all times in the furnace—even when a sample is removed or inserted. The furnace is shown in Fig. 2 and is described in the Appendix. The tempering processes were carried out on powder samples sealed in evacuated quartz capsules. Since the highest tempering temperature was 525OC, no protection against reaction with the quartz was necessary. (Tests were made on filings of iodide titanium and showed no hardness increase after equivalent heat-treatments.) A thermocouple was attached to the capsule, which was heated to the

Jan 1, 1959

By J. J. Becker

Changes in magnetic properties with particle size are used to study the precipitation process in a Cu-Co alloy. In particular, the effect of a field during aging in producing anisotropy is shown to occur entirely during the growth of the particles, after precipitation is complete. HEAT-treatment in a magnetic field is done commercially to improve the magnetic properties of a number of materials. These can be divided into solid-solution alloys and precipitation alloys. The Permalloys are representative of the first type, and magnetic annealing greatly increases their maximum permeability. On the other hand, in precipitation alloys such Alnico 5 the important result is an increase in maximum energy product. The effect of the field in all cases is to bring about an additional magnetic anisotropy, uniaxial in nature, which makes the hysteresis loop more upright when measured in the direction in which the field was applied. The structural origin of the anisotropy brought about by magnetic annealing is not well understood. In the solid solution alloys, one possible explanation is based on ordering.' Another possibility is the orientation of like-atom pairs.' The precipitation systems known to respond to magnetic heat treatment are Alnico 2, in which the effect was first discovered," Alnico 5, cobalt ferrite (oxide),' and Cu-Co alloys.3 n these materials, the field affects the precipitation process itself in some way. Although there has been much work on Alnico 5. its nature is still incompletely understood. According to Geisler,' the precipitation reaction is of the

Jan 1, 1959

By D. L. Martin

The study of cobalt-platinum alloys has been of interest since they represent a class of permanent-magnet material in which the disorder-to-order transformation plays a controlling role. The magnetic properties of alloys in the range 40 to 60 at. pct have been found to be greatly influenced by composition and heat-treatment. The peak properties of 4700 coercive force and 9,000,000 gauss-oersteds energy product were obtained by controlled cooling and aging. These high values combined with ductility and machin-ability give the alloys useful characteristics although their high cost limits their application. THE cobalt-platinum alloys have been of interest in the study of permanent-magnet materials ever since the discovery by Jellinghaus that they had unusually high coerceive-force values.' The high coercive force was associated by Jellinghaus with the disorder-order reaction which occurred in these alloys. This was later verified by Gebhardt and Koster in a detailed study.2 An investigation of the structure, mechanism, and kinetics of the disorder-order transformation and resulting property changes in cobalt-platinum alloys has been in progress for some years. Certain phases of this study related to equilibrium rela- tions, and to the mechanism and kinetics of the ordering reaction have been published previously.3-5 In this paper, the results of the processing and heat-treatment studies on 40 to 60 at. pct CO alloys are presented. The magnetic properties have been found to be influenced greatly by the composition, by the cooling rate from the disordering treatment, and the final ordering time and temperature. Coercive force values, Hc, of 4700 oersteds and energy values, (BH)m, approaching 9,000,000 gauss-oersteds have been obtained by controlled cooling and ordering. PROCESSING OF THE ALLOYS The composition range of interest for permanent-magnet properties centers around the equiatomic composition Copt. In this region the alloys are dis-

Jan 1, 1959

By R. G. Charles, E. A. Gulbransen, S. Barnartt

KINETICS of the reaction of zirconium with pure oxygen at elevated temperatures have been studied by several workers for periods of time up to 6 hr.1-1 In two cases,3-4 . the experimental values of oxygen uptake, w, as a function of time, t, were best fitted to the parabolic rate law w2 = kPt + constant. In others,3,4 the cubic rate law w3 = kot + constant, showed better agreement. The most recent data of Gulbransen and Andrew4 indicate that the choice between the parabolic and cubic laws for empirical representation of the data will often be arbitrary. This is particularly true if the first few minutes of the reaction with a clean zirconium surface is attributed to a different oxidation mechanism, for deviations from either rate law were found primarily during the initial period. Thus, the kinetics of this reaction have been too uncertain to permit safe extrapolation to oxidation periods of practical interest (many hundreds of hours). The data to be described are of interest, for they indicate that the cubic rate law applies over long oxidation times. The reaction of zirconium with oxygen at 1 atm pressure was followed at 350" and 450°C for 500 and 200 hr, respectively. Abraded test specimens of pure zirconium sheet' 3.0 X 2.0 X 0.012 cm in size were oxidized by the procedure previously described,3 which included periodic cooling to room temperature for weighing. The surfaces were polished to a 4/0 finish using polishing paper wet with kerosene, then wiped with petroleum ether and washed in redistilled acetone. Fig. 1 shows plots of log ? vs log t. Each curve represents the average of duplicate measurements, and deviations from the average were generally less than 3 pet. The cubic rate law (slope = 1/3) is closely followed. The rate constants, 5.2, x 10 -6 and 2.4, X 10- (mg cm-2)3 per hr at 350" and 450 oC, respectively, are plotted as log k, vs 1/T in Fig. 2, together with cubic constants calculated from the data of Gulbransen and Andrew4 for abraded specimens from the same lot of zirconium. Their data refer to runs of 6-hr duration at a pressure of 0.1 atm 0 and under conditions of uninterrupted heating. In spite of these differences, the latter data yield a straight line which appears to apply equally well to the new extended time data. The energy of activation for the oxidation process, calculated from the slope of this line, i.s 38 keal per mole. This may be compared with the value of 47 keal per mole found by Belle and Mallett3 at higher temperatures. It may be concluded tentatively that extrapolation of short-term oxidation data for zirconium to obtain the long-term behavior is best done through the cubic equation ?3 = kpt + constant. References ' E. A. Gulbransen and K. F. Andrew: AIME Trans., 1949, vol. 185, p. A.515; JouRNal OF Metals, August 1949. 'D.p. Cubicciotti Journal Amer Chemical August1949.Soc., 1950, Vol. 72, P. 3 V. Belle and M. W. Mallett: Joulnal Electro chemical Soc., 1954, ' E. A. Gulbransen 339.and K. F. Andrew: Oxidation of Zirconium Between 400" Gulbransenand 800'C.and AIME Trarzs.. 1957, vol. 209, p. 394; JOUR-Nal of Metals, April 1957. IS Barnartt, B G. Charles, and E. A. Gulbransen: Oxidation of 50 weight pet uranium-zirconium alloy, Journul Electrochemical SOC., 1957, vol. 104, p. 218.

Jan 1, 1959

By J. W. Freeman, J. P. Rowe, R. F. Decker

HEAT-to-heat variations in properties of an alloy of constant nominal chemical composition have been a perplexing problem to the metallurgist. These heat-to-heat differences have been especially baffling in high-temperature metallurgy. In order to establish fundamental reasons for these heat-to-heat variations, the National Advisory Committee for Aeronautics has sponsored and financially assisted an extended research program on heat-resistant alloys at the University of Michigan. As part of the program to find the contribution of processing variables, Frey, Freeman, and white' studied effects of heat treating on nickel-base alloys and Ewing and reeman' investigated effects of hot-working practice on N155 alloy. To extend the program to the study of effects of melting practice on high-temperature properties, a 55 Ni-20 Cr-15 Co-4 Mo-3 Ti-3 pct A1 composition was selected for experimentation. The objective of this program was to establish the melting-practice variables which influenced the hot-working characteristics and creep-rupture properties and, at the same time, establish the metallurgical mechanisms for the effects. During the course of the investigation of practices using vacuum melting, it became increasingly evident through chemical analyses supplied by industrial concerns that a major variable was melt reaction with the crucible. This paper is devoted to the results of this phase of the melting-practice study. EXPERIMENTAL PROCEDURES Experimental 10-lb heats were induction melted in the University of Michigan vacuum-melting unit with the melting practices outlined in Table I. Aim analysis for the basic alloy, in wt pct, for all heats was as follows: Cr Co Mo Ti Al 20.0 15.0 4.0 3.1 3.1 Mn Si C Ni 0.12 0.12 0.08-0.15 Bal. Small amounts of boron and zirconium were added to certain heats as listed in Table I. These additions

Jan 1, 1959

By S. Kado, G. Derge, L. Yang

Self-diffusion coefficients of silver in molten silver have been measured by means of the capillary-reservoir method in the temperature range 1002" to 1105°C. The results can be .represented by the equation D = (7.10 i 0.06) X 10-4 exp [(—8150 ± 1130)/RT]. The heat of activation agrees within the limit of experimental uncertainty with that for the viscous flow. The validity of the Eyring and the Stokes-Einstein equations are examined on the basis of the self-diffusion coefficients obtained and the known viscosity data of molten silver. MEASUREMENT of the self-diffusion coefficient of silver in molten silver was made in the temperature range 1275° to 1378°K, using the capillary-reservoir method and &"' as the radioactive tracer. The experimental arrangement is shown in Fig. 1. Silver of 99.99 pct purity (fine silver), was melted and degassed in vacuum in a graphite crucible situated inside a McDanel vacuum jacket. The crucible (4 in. tall and 1 in. ID) was protected both at the top and at the bottom with graphite shields and contained about 220 g of silver. The sample holder was a piece of graphite rod (1 in. long and 1/2 in. diam) with 4 capillaries drilled longitudinally into it. The holder was screwed onto a long graphite rod (12 in. long and 74 in. diam) which was connected to a steel disk hanging on a nylon string through a glass pulley. The steel disk kept the sample holder at the center of the McDanel tube and was heavy enough to overcome the buoyancy when the holder was lowered into the molten silver. By turning a handle connected to the pulley through a tapered glass joint, it was possible to raise or lower the sample holder without breaking the vacuum. Two such arrangements were constructed, sitting side by side in 2 Kanthal furnaces. One with non-radioactive silver in its crucible was used for the diffusion run and the other with radioactive silver in its crucible was used for filling the capillaries. To fill the capillaries with radioactive silver, the sample holder was degassed first and then lowered into the radioactive molten silver in vacuum. Purified argon gas was then admitted into the system to push the liquid silver into the capillaries. After cooling in argon, the filled capillaries were polished on emery paper to expose the top of the rod and used immediately as samples for the diffusion run which was carried out at the same temperature as that used for filling the capillaries. During the diffusion run, the samples were degassed in vacuum and lowered slowly into the nonradioactive molten silver before purified argon was admitted into the system. After a predetermined period of time, the samples were raised out of the melt and cooled in argon. The temperature of the melt was measured before and after the run with a chromel-alumel thermocouple inside a McDanel protection tube. Another chromel-alumel thermocouple attached to the outside wall of the McDanel vacuum jacket was used to indicate any fluctuation in the temperature of the furnace during the run, which was found to be less than ± 2°C for the longest run made (93 min). The temperature gradient inside the molten silver was found to be negligible. No significant difference was observed in the results obtained whether the melt was stagnant during the run or was stirred by raising and lowering the sample holder slowly a few times a minute for a distance of about 1/4 in. inside the melt.

Jan 1, 1959

By C. M. Schwartz, A. E. Austin, W. B. Wilson

High-temperature X-ray diffraction studies were conducted with Th-U alloys with up to 10 wt pet U. The solid solubility of uranium in thorium as a function of temperature was determined by the method of lattice parameters. Thorium will dissolve up to 2.5 wt pet U at 950°, 4.5 wt pet U at 1150°, and 7.5 wt pet U at 1250°C. Determinations were made of the temperature of the transition of thorium and of the effect of uranium upon the transition. The a to ß transition for thorium was observed to occur at 1330' ±20°C. Mean coefficients of expansion were calculated for thorium and two alloys, and for ThO2 in contact with the thorium, using X-ray lattice-parameter data. Values obtained at 950° C for thorium and Tho2 were 12.1 and 9.40 X 10-6 per OC, respectively. Impurities obtained during the X-ray exposure were identified by diffraction and were essentially Tho2 and ThC, with two additional unknown phases being detected. The effect of the impurities upon the results is discussed. DIRECT investigation (i.e., high-temperature X-ray diffraction studies) of the phase diagram of thorium-rich uranium alloys has been shown to be necessary since recent work1 - has disclosed the presence of an allotropic transformation near 1400°C in pure thorium with the room temperature face-centered-cubic phase transforming to a body-cen-tered-cubic structure at the elevated temperature. The effect upon the transition of the addition of uranium to thorium and of the solubility of uranium in thorium at high temperatures remained unknown, yet was of interest in understanding fabrication procedures and elevated temperature use. The present work was undertaken to provide information in this area by determining the transition temperature, the effect of uranium on the transition temperature, and the solubility of uranium in thorium as a function of temperature. Experimental Work The high-temperature diffraction data were obtained using a camera especially designed for the purpose3 and capable of reaching temperatures in excess of 2000°C at pressures as low as 1 x 10." mm Hg. Temperature regulation was provided by regulating the power input to ±0.1 pet variation, and by regulating the water flow through the camera jacket to provide a constant thermal load. The X-ray sample was a rod nominally 80 mil diam, which was further turned down to 20 mil and then etched to 18 mil over 1/2 in. of one end. This was placed in the sample holder and mounted on the camera so that the smaller part was surrounded by a cylindrical tantalum-sheet radiation-type heating element. Diffraction from the sample was recorded on film after passing through a slot in the heating element and radiation-baffle shield and through beryllium vacuum windows. The X-ray film mounting was of the Straumanis type4 with a camera diameter of 114.59 mm. Since previous work of Chiotti' indicated that impurities considerably alter the transition temperature, chemical analysis of the arc melted iodide crystal-bar thorium samples was obtained prior to testing. The analysis disclosed the material to contain as low as 0.001 ±0,0002 wt pet H and 0.007 ±0.001 wt pet 0. Carbon was 0.003 wt pet and nitrogen less than 0.002 wt pet. This material was sealed in mild steel in an inert atmosphere and subsequently hot rolled to 3/8-in. diam rods at a temperature of 732°C. Following removal of the jacket, the material was pickled and cold swaged to 1/8-in. rods, from which the diffraction samples were prepared. The alloys were similarly prepared, with the uranium being added during arc melting. The uranium analyses of the alloys prepared appear in Table I. The experimental procedure for diffraction examination of the three samples of high-purity thorium differed from those of the Th-U alloys. The original practice, later modified, consisted of pumping down the camera with the diffusion pump on and then admitting liquid nitrogen to the cold trap of the system. This was modified for the Th-U alloys by maintaining liquid nitrogen in the cold trap at all times before and while the diffusion pump was heated. This minor change produced a reduction in the amount of carbon pickup by the sample during exposure to the diffusion-pump vapors. The sample was brought to the desired test temperature and exposed for 21/2 hr at pressures which were usually 2 x 10-6 mm Hg, or lower. Exposures were made at

Jan 1, 1959

By D. A. Stevenson, T. Alden, J. Wulff

A portion of the liquidus curve has been determined for the binary alloy systems Ni-Pb and Cr-Pb. The solubility of nickel is 0.53 atomic pet at 372° and 18.63 atomic pet at 1200°C. Chromium shows low solubility, 0.634 atomic pet at 1210°C. Molybdenum and tungsten were also studied and found insoluble in lead, less than 0.005 atomic pet at 1200°C. INCREASED use of liquid metals of low melting X point for heat transfer, coating, joining, and other purposes has renewed interest in the solubility of structural metals in these liquids. A study of Hansen1 and current literature indicates that few liquidus curves at the low melting end of the binary diagrams have been accurately delineated. This statement applies particularly to the binaries of lead. The present paper is limited to nickel, chromium, tungsten, and molybdenum in lead. In early studies2, 3 of the lead end of the Pb-Ni system, a monotectic at 1340°C was established. Tammann and Oelsen' determined the solid solubility of nickel in lead at 20°C to be 0.023 wt pet. Recently Pelzel5 determined the liquidus curve from the eutectic temperature of 327° up to 727°C using a segregation method. In the present paper this part of the curve has been checked and extended to 1244°C. The Pb-Cr system was first studied by Hindrichs.6 He pointed out the existence of a monotectic at 1470°C and indicated a tentative liquidus. Recent corrosion studies of Fe-Cr alloys in lead suggest that chromium is more soluble than iron in lead.7-8 The solubility of tungsten in lead according to Inouye8 is about 30 wt pet at 1200°C. Appreciable solubility of molybdenum in lead might therefore be expected. Experimental Various experimental techniques have been employed in the determination of solubility in liquid metals. For low solubility, thermal analysis is unsatisfactory. A segregation method was used by Pelzel3 in his study of the Pb-Ni system. In this procedure separation of liquid and solid is possible due to difference in density. In the technique of Kleppa10 a single piece of material is maintained in contact with the liquid metal in evacuated Vycor vials. After equilibration, solid and liquid are separated by tilting. Keck and Broder" measured the weight of a piece of the solid solute before and after immersion in a pure solvent bath; the weight loss was a measure of the solubility. All of the above procedures are time-consuming since they permit only one determination per run. Numerous samples for analysis may be taken from the melt in the method described by Gurinsky and CO-workers.10 The rate of extraction of samples is limited only by the time required for equilibration. In the present work, a modification of this method was employed. A 150-g charge of analytical reagent grade lead and the added metal* were contained in an Alun- dum crucible. It rested on firiely divided silica at the closed end of a 45 mm Vycor tube, 500 mm long. The top of the tube was provided with an inlet and

Jan 1, 1959

By J. C. Danko, R. D. Stout, A. H. Holtzman

The deformation characteristics of pearlite have been studied by light and electron microscopy.1,2 In the electron-microscopic work, deformation was found to take place by 1) ferrite slip which is parallel to the lamellae, 2) slip transverse to the lamellae with both cementite and ferrite deforming, and 3) ferrite-cementite interfacial slip. The transverse slip gives a step-like appearance to the lamellae in light microscopic work. It was thought that spheroidization of deformed pearlite would commence at the regions of maximum cementite deformation, the "stepped" areas. Although there is no possibility for seeing slip in the microstructure if the specimen is polished after deformation, the step-like appearance of the lamellae clearly indicates the transverse deformation. Thus, the areas of cementite deformation are apparent after polishing and the effect of deformed areas on spheroidization may be studied by the usual metallographic techniques. This note reports the result of a metallographic investigation which substantiates that spheroidization begins in the "stepped" areas. An AISI 1080 steel was normalized, re-austeni-tized at 1040°C, and isothermally transformed at 700 ± 4°C for 4 hr. Cubes, 5 mm to a side, were compressed between parallel plates to strains of 20, 40, and 50 pct. After deformation, specimens were heated to 600, 650, and 700°C; withdrawn at increasing time intervals and examined metallo-graphically for the percentage and distribution of spheroidite. The percentage of spheroidite was determined by lineal analysis. A micro structural region considered as spheroidized was one in which a lamellar skeleton was not distinguishable. Table I gives the times necessary for 95 pct spheroidization for each condition of strain and annealing temperature. Fig. 1 shows the microstructure of coarse pearlite compressed 20 pct, then polished and etched. Here the lamellae form a step by bending at two

Jan 1, 1959

By O. J. Huber, P. D. Frost, H. A. Robinson

URANIUM is a (ß-stabilizing, eutectoid-forming element when alloyed with titanium. Udy and Boulger1 have reported that an alloy of 48.6 pet uranium in titanium retains ß-phase when quenched from the ß-region, while compositions of approximately 30 pet uranium transform to martensite during such quenching. Since the eutectoid reaction is rather sluggish, titanium-uranium alloys should be capable of being strengthened by the ß — a trans-

Jan 1, 1959

By S. B. Twiss, P. R. Basford

The relationship between areas of iron powders, briquettes, and sintered compacts and tensile strength has been determined. It has been found necessary to distinguish between two types of areas which exist in such powders—a macroscopic area due to the shape and size of particles and a microscopic area due to pores and cracks in the surface. Only the macroscopic area, specifically the area due to particle irregularity, contributes to tensile strength; the microscopic area cannot be forced into contact with adjacent particles ond does not participate in bond formation. Of the two methods of area measurement employed in this study—permeability to liquids and gas-phase adsorption—only the former is useful for determining the roughness factor. A measure of this roughness, (area measured by permeability to liquid) -f- (orea of powder with the same size distribution, but made up of spherical particles), is shown to be uniquely related to tensile strength at constant density. The other important factors in determining the strength of sintered-metal compacts are the density and presence or absence of surface oxide. THE manufacture of metal parts by the process of powder metallurgy is an important and rapidly growing industry. Progress has been rapid and continuous, largely because of the excellent research in the field. Nevertheless, the process remains inherently complex and empirical. Several investigators have shown that the properties of the final compact must depend on many variables; namely, shape,' size distribution,"-" nd compositiona of the original particles, the pressure necessary to compress to the desired density, the density of the compact, the time and temperature of sintering, and so on. Through the application of some new techniques to the study of powders and compacts, and the correlation of a number of observations of known variables, the present paper attempts to clarify and simplify the underlying theory of the powder-metallurgy process. Any theory must start with the obvious fact that the strength of a compact, its most useful property, is due to the formation of welded areas between adjacent particles, and attempt to deduce what effect other variables will have on (a) the area and (b) the intrinsic strength of these welds. Such welded areas can be demonstrated by electron micrographs, as in Fig. 1. It was believed that (a) could be most directly studied by means of surface-area measurements on the original powders and on the compacts made from them; the area decrease should be related closely to the welded area. A representative group of eleven iron powders from commercial sources, and made by a variety of processes, was chosen for this study. In addition to the surface-area measurements, correlations were established between the tensile strength and all the known variables which might possibly affect it. The results are quite unexpected. They indicate that the situation is much simpler than the authors had anticipated. The strength of the sintered compact is determined, indeed, by no more than three variables; viz., the irregularity of the original particles, the density of the compact and, in exceptional cases, the amount of surface oxide. All three had been recognized previously as having some effect on the tensile strength, but in the absence of the special techniques and interpretations to be developed here, there could be no suspicion that they were the only relevant variables. Materials and Methods Material—All the iron powders were commercial products obtained from the Amplex Division of Chrysler Corporation. Powders A, B, C, and J were very pure electrolytic iron. Powder D was made from oxidized scrap reduced by heating with an excess of cast iron. Powder E was a high-grade iron ore reduced by hydrogen. Powder I was prepared by atomizing molten cast iron in an air blast, quenching the droplets in cold water, and crushing the coarse powder. Mill scale (oxide) is added and the mixture heated to reduce the high carbon content. The other powders were all prepared by reduction of iron oxides, such as mill scale. They

Jan 1, 1959

By J. Doig, A. A. Bauer, F. A. Rough

AN investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems was conducted by studying alloys ranging in composition from uranium-31.5 at. pct Mo to uranium-34 at. pct Ti. A ternary cut showing these phase relationships is presented upon the basis of thermal-analysis data obtained and upon the basis of metallographic and X-ray examination of heat-treated and quenched specimens. Isothermal ternary sections, inferred from phase relationships determined between the two 6 phases, are presented for the uranium-molybdenum-titanium system. In the compositional range investigated, a y-ura-nium solid solution exists at elevated temperatures. At about 900°C the 6-U2Ti phase, with limited molybdenum solubility, forms. Epsilon, a molybdenum-titanium-rich solid solution appears at the same temperature and appears in all phase regions that exist below this temperature except in the terminal 6-phase regions. The y phase is stable to approximately 660°C in titanium-rich alloys; the y and 6-U,Ti phases decompose at this temperature to a uranium in a peritectoid reaction. The y phase in molybdenum-rich alloys of the ternary cut studied decomposes in an apparent eutectoid reaction, at about 593°C, to the 6-uranium-molyb-denum and a-uranium phases. The e phase while present, presumably plays a negligible role in these reactions. Titanium was found to markedly decrease the stability of retained y in these alloys. Age-hardening characteristics developed in titanium-contain ing uranium-molybdenum alloys quenched from 900°C and aged at 500°C are ascribed to decomposition of Y to the a and E phases. INTRODUCTION Alloys of uranium with molybdenum, titanium, and zirconium, respectively, are of great interest because of their potential use as reactor fuels. As a result, this interest extends to the constitution of these alloys, particularly in view of their uniqueness of constitution. In these systems, alone, among known uranium-alloy systems, an intermediate phase forms by direct decomposition of the high-temperature y-uranium phase. As a prelude to possible future alloy development, an investigation has been undertaken of the phase relationships that occur between the intermediate phases of these systems. These phase relationships have already been reported for the intermediate 6 phases of the uranium-zirconium and uranium-titanium systems.' The results of an investigation of the phase relationships between the 6 phases of the uranium-molybdenum and uranium-titanium systems are reported here. The phase relationships that occur in the binary systems pertinent to this investigation are shown in Fig. 1. Phase nomenclature appearing throughout this report is as shown in these diagrams; the crystal structure of the phase is given in Table I. EXPERIMENTAL PROCEDURE Alloys were cast and fabricated to flat plate. Specimens were heat treated and examined metal-

Jan 1, 1959

By L. O. Brockway, W. C. Bigelow, J. A. Amy

Specimens of Inconel-X alloy solution-treated at 2050°F and aged for periods of 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F have been examined by electron microscopy and by electron and X-ray diffraction. Four minor phases were identified: titanium nitride, niobium nitride, an M23C6 complex carbide, and the intermetallic ? phase. The two nitrides were found in all of the aged specimens and in the solution-treated alloy, the y' phase formed at all aging temperatures, while the M23C6 carbide formed only on aging at 1200° and 1400°F. Variations in the hardness, rupture strength, creep strength, and yield strength of the alloy have been shown to be related to variation in the size and distribution of the particles of the y' phase within the matrix grains of the alloy, with maximum values of these properties occurring when there is a maximum amount of the phase present and a fine state of dispersion of the particles prevails. THE nickel-chromium alloys containing titanium and aluminum are widely used in applications requiring high strength at elevated temperatures. Studies on relatively simple ternary and quaternary alloys'-4 have indicated that the favorable high-temperature properties of these alloys are related to the precipitation of an intermetallic ?'-phase having a structure based On that of the Ni3A1 phase of the nickel-aluminum system. The present investigation was undertaken to identify the minor phases and to study the microstructural changes occurring in one of the more complex commercial alloys as a result of aging in the service temperature range, with particular emphasis on investigating the role of the ?' -phase. The microstructural changes were studied by electron microscopy and the minor phases were identified by X-ray and electron diffraction. MATERIALS AND METHODS Inconel-X alloy was selected for this investigation because the previous studies of Frey, Freeman, and white6 provided extensive information on the variations in metallurgical properties of this alloy resulting from high-temperature aging treatments. Specimens aged 1, 10, 100, and 1000 hr at 1200°, 1400°, and 1600°F were made available for the present use. These were taken from 1-in. round-bar stock of a commercial heat having the following weight composition: 0.04 C, 0.56 Mn, 6.59 Fe, 0.007 S, 0.38 Si, 0.03 Cu, 73.22 Ni, 14.97 Cr, 0.78 Al, 2.38 Ti, and 1-02 Nb. They were solutjon-treated at 2050 for 4 hr and then water-quenched prior to aging. Powder X-ray diffraction patterns were obtained from insoluble minor phases which were separated from the alloys by digestion in the reagent of Mahla and Nielsen.6 Back-reflection patterns were obtained from electrolytically polished surfaces of the bulk search to detect the ?'-phase' Cu-K a radiation was used in both cases. In the electron-diffraction studies, the general method developed by Heidenreich, Sturkey, and

Jan 1, 1959

By R. C. Hall

In the present work, experiments determined the effect of the order-disorder reaction near the Fe,Al composition on the magnetic anisotropy and magnetostriction of single crystals: A material which is more difficult to magnetize in one direction than in another is anisotropic, that is, the ease with which ferromagnetic materials may be magnetized in different crystallographic directions determines the anisotropy. Two investigators have estimated the anisotropy of the aluminum iron alloys from poly-crystalline data;1,2 however, these estimates should not be considered to be reliable. Siege1 made two accurate measurements of the first anisotropy constant* from single crystals of 4.0 wt pct aluminum sotropy throughout the ferromagnetic aluminum iron system have been described. These results were obtained from single crystals which were slowly cooled and, hence, ordered near the Fe3Al composition.4 Magnetostriction is the change in length per unit length resulting from applying a magnetic field to a ferromagnetic material. For the purpose of this report, the saturation magnetostriction was measured. This is the maximum change in length per unit length resulting from an applied magnetic field large enough to saturate the material in a given direction. This magnetostriction has been determined for single crystals of the ferromagnetic aluminum-iron system.' The crystals near Fe3Al were also ordered. PREPARATION AND TREATMENT OF SINGLE CRYSTALS Single crystal bars were grown from the melt.' The raw materials for these crystals were iron and aluminum of 99.9 and 99.99 pct purity, respectively. From the bars, crystals in the shape of circular

Jan 1, 1959