By L. W. Davies

ONE of the most important applications of the zone-melting process of Pfann1 concerns the refining of materials with respect to impurities whose distribution coefficient k differs from unity. The repeated passage of molten zones along an ingot concentrates the impurities for which k < 1, for example, towards the end to which the zones move. It is desirable to know the ultimate distribution of impurity after the passage of an infinite number of zones of constant length; this is also the distribution which is unchanged by the passage of a further molten zone.

Jan 1, 1959

By L. M. Pidgeon, W. Curlock

FREE energies of formation of zinc sulfide and magnesium sulfide had previously been estimated to an accuracy of ± 5.0 kcal per g mol. In the present work, these values were determined experimentally. As the determinations of the free energies of formation of zinc sulfide and magnesium sulfide presented different problems, separate experimental procedures were employed for each. ZINC SULFIDE It is difficult to measure the free energy of formation of either zinc sulfide or magnesium sulfide by measuring their decomposition pressures directly, as they are very stable compounds. An attempt was made by Jellinek and zakowski3 to study the equilibrium. zns(s) + H2(g) = Zn(g) + H2S(g) [I] They passed hydrogen over zinc sulfide and analyzed the gases leaving the reaction zone for H2S. They were unable to determine the true partial pressures of the H2S by this method, as some of the H2S on being cooled from the reaction temperature, reacted with the zinc in the gas to produce ZnS. Consequently, they were unable to establish any true equilibrium data for reaction [I]. More recently,&apos; the equilibria ZnS(sphaledte) + Fe (s) — FeS(s) + Zn(g) [2] and ZnS(sphalerite) + 2Cu(s) — Cu2S(S) + Zn (g) [3] were studied. As the standard free energy of formation of Cu2S is known to * 3.0 kcal, and of FeS to ± 1.0 kcal, it should be possible upon performing equilibrium studies on reactions [2] and [3] to deduce the standard free energy of formation of ZnS (sphalerite). However, as both of these equilibria involve 2 solid sulfides, and as it is possible for these sulfides to dissolve in one another, it is necessary first to ascertain the activities of the various sulfides in these solid phases.

Jan 1, 1959

By J. R. Johnson

ZIRCONIUM&apos;S corrosion rate by reactor fuel solutions increases with increasing reactor power. It is believed that the protective oxide film is affected by radiation damage. Observations of the

Jan 1, 1959

By D. W. Lillie

It has been demonstrated that considerable bend ductility exists in bulk specimens of polycrystalline high-purity silicon. The possibility of hot-forming at 1200°C is suggested. EXCELLENT corrosion resistance in many media and low cross section for absorption of thermal neutrons (0.13 barn) would make silicon of interest to nuclear engineers were it not for extreme brittle-ness and the difficulty of fabrication by any reasonable means. The use of silicon for structural purposes also has been considered in view of its light weight and oxidation resistance. Johnson and Han-sen&apos; have investigated the properties of silicon-base alloys and concluded that there was no way of making pure silicon or silicon-rich alloys ductile at room temperature. In view of reports of appreciable ductility in germanium single crystals above 550°C&apos;." and some plastic deformation in single-crystal silicon above 900oC,&apos; the present investigation was undertaken to define more precisely the limits of high-temperature ductility in pure silicon. After this investigation was begun torsion ductility in both germanium and silicon was reported by Greiner." Through the courtesy of F. H. Horn, a small bar of cast extra high-purity silicon was obtained and small bend specimens were made from it by careful machining and grinding. All of the reported tests results were obtained from samples from this bar (bar No. 1) and one other of similar source (bar No. 2). No complete analysis was obtained but, based on analysis of similar semi-conductor grade material, metallic impurities were under 0.01 pct total. Vacuum-fusion analysis for oxygen showed a value of 0.0018 2 0.0003 pct for the first bar tested and metallographic analysis showed no evidence of a second phase. Bend tests were carried out on an Instron tensile machine using a bend fixture with a 1 -in. span loaded at the center. Supporting and loading bars were 0.250 in. round and the load was applied by downward motion of the pulling crosshead of the machine. Specimen thickness and width were approximately 0.10 in. and % in. respectively. Loading rate was controlled by holding crosshead motion constant at 0.02 ipm. In some cases a smaller specimen was used on a 5/8-in. span with a 0.129-in.-diam loading bar. The entire bend fixture was surrounded by a hinged furnace and all heating was done in air atmosphere. Temperature measurement was made with thermocouples fastened directly to the bend fixture within less than 1 in. from the specimen. Autographic stress-strain curves were recorded during each test, and breaking load, total deflection, and plastic strain could be obtained from these curves. Stress was calculated from the beam formula S = 3PL/2bh2, where P is the load in pounds, L the span in inches, b the specimen width in inches, and h the specimen thickness in inches. This formula is strictly correct only in the elastic range but has been used to calculate a nominal stress for convenience in the plastic range. The stress given is the maximum stress in the specimen. Results The results of the complete series of tests are shown in Table I. The first group of tests (specimens Nos. 1-6) showed the beginning of plastic flow at a test temperature of 900°C, so two additional tests (Nos. 8 and 9) were made at 950°C on small-size specimens from bar No. 2. Specimen No. 8 was tested in the as-machined condition, and No. 9 was heat-treated in hydrogen at 1300°C for 2 hr, cooled to 1200°C and held 1 hr, cooled to 1000°C and held 1 hr, cooled to 900°C and held 1 hr, and finally cooled to a low temperature before removal from the hydrogen. It is apparent that the heat-treatment had a significant effect on yield strength and ductility. In addition, the magnitude of the yield point was conslderably reduced in the heat-treated specimen as is shown m Fig. 1 by tracings of the stress-strain curves. After obtaining a furnace capable of reaching higher temperatures specimens Nos. 10 to 13 were tested at 1100 and 1200°C. Strain rate was increased by up to a factor of 10 to see whether the ductility observed was excessively strain sensitive. Specimen NO. 10, strained at 0.02 ipm and 1100oC, was still bending at a deflection of 0.322 in. when the load rate was increased to 0.2 ipm, resulting in immediate

Jan 1, 1959

By W. F. Carew, F. A. Crossley

Tensile, creep-rupture, and stability tests were employed to evaluate the effect of a-strengthening and ß-complexing additions on the base composition Ti-6Al-3Mo. The ultimate objective was to produce an alloy of greater strength than the Ti-7A1-3Mo alloy. Strengthening of a was accomplished by additions of 2 and 4 pct Ge, 4 pct Sn, 4 pct Zr, and 2 pct Sn-2 pct Zr. Making the ß more complex while keeping the total of ß-stabilizing additions constant at 3 pct resulted in higher tensile strengths but lower creep and rwpture strengths, especially at 1000°F. None of the more complex versions of the base alloy offers greater promise than the Ti-7A1-3Mo alloy. However, some improvement in the strength of the latter may follow from additions of zirconium perhaps up to 4 pct. PREVIOUS work directed at the development of titanium-base alloys with: 1) minimum room-temperature tensile elongation of 10 pct in 1 in., 2) high creep resistance at elevated temperature, and 3) the ability to retain original room temperature tensile ductility following exposure to creep conditions at elevated temperatures, demonstrated Ti-Al-Mo ternary compositions in the range 5 to 7 pct Al-3 to 6 pct Mo to be the most promising. Of this group the Ti-7Al-3Mo alloy was the strongest.&apos;-= The objective of the present work was to determine if alloys of this type could be further strengthened by making additions which dissolve preferentially in the a-phase and by making the ß-phase more complex. For this study the base composition Ti-6Al-3Mo was selected rather than Ti-7Al-3Mo in order to minimize the possibility that in a more complex alloy with a-strengthening additions, low ductility might obscure the strength contribution. The metals

Jan 1, 1959

By A. J. Griest, P. D. Frost, H. A. Robinson

The flow characteristics and uniform elongation of alpha-beta titanium alloys in the solution-treated condition were shown to be markedly affected by the solution temperature. Two classes of alpha-beta alloys were distinguished, based on the effect of solution temperature on the uniform elongation. Martensitic alpha-beta alloys, which are relatively weakly beta-stabilized, showed decreasing values of uniform elongation as the solution temperature was initially increased. However, after solution-treatment at still higher temperatures in the alpha-beta field, the uniform elongation of these alloys was again high, and often attained its maximum value. Nonmartensitic alpha-beta alloys, which are more heavily beta-stabilized, showed a continuous decrease of uniform elongation with increasing solution temperature. The behavior was rationalized in terms of the alpha-beta ratio and the alloy content of the beta existing at the solution temperature. The data indicate that in commercial practice close temperature control may be required to get maximum uniform elongotion, and hence, maximum potential formability, in solution-treated sheet. Bend-test data also were obtained for the solution-treated conditions. A MOST important objective of current titanium research is the development of age-hardenable alloys with superior formability in the solution -treated condition. Alpha-beta titanium alloys have been shown to be amenable to high-strength aging treatments after solution-treatment in the alpha-beta field.&apos; However, heat-treatment data on the properties of solution-treated sheet, such as uniform elongation, minimum bend radius, and flow properties, which have a bearing on the potential formability, have not been widely available. This paper presents only the most significant results of a research program conducted at Battelle for the Air Force in an effort to develop sheet alloys that can be formed readily as solution-treated and subsequently aged to very high strengths. Data for 10 compositions representative of the more than 25 alloys studied in this program are presented. A primary objective of the paper is to demonstrate the pronounced dependence of the flow characteristics and uniform elongation on solution-treatment temperature. This effect is believed to be vitally important in the commercial heat-treatment of age-hardenable titanium sheet alloys. Experimental Procedures Melting and Fabrication—The nominal and actual compositions, beta transi temperatures, and rolling temperatures of 10 of the 30 alloys studied are presented in Table I. Stock :€or two of the alloys, E (Ti- 8Mn) and J (Ti-6A1-4V) was obtained from commercial heats. The remaining heats, except D and I, were double melted as 10-lb heats in a consumable-electrode furnace. Melting stock was 120 Brine11 hardness sponge. The oxygen and hydrogen analyses spotted throughout the heats indicate the range of interstitial levels resulting from the melting practice used. Heats D and I were melted as 20-lb ingots with the same grade of sponge. These ingots were cut in half and one portion used in the present evaluation. The ingots, which were about 4 in. diam and 4 in. in height, were upset forged and drawn at 1750°F to sheet bar 5/8 in. thick by 2 1/2 in. wide in such a manner that the top of the ingot corresponded to the top of the sheet bar. Slabs of the sheet bar, 5 1/2 in. in length were scalped to 1/2 in. thickness and rolled at the temperatures indicated in Table I to approximately 0.055 in. sheet. Elongation during rolling took place at 90" to the original forged length. The fabrication procedure used is described in some detail since the experimental heats showed considerable directionality in mechanical properties. The rolling procedures for the commercial heats were unknown, but were such as to produce essentially isotropic properties. All heats, as rolled, showed microstructures typical of alpha-beta alloys worked in the alpha-beta field; that is, the structures consisted of equiaxed alpha particles in a beta matrix. Heat Treatment— The effects of solution and aging heat-treatments on the properties of the alloys were evaluated uSing longitudinal and transverse tensile and bend coupons sheared from the sheet. Two or three solution-treated conditions were evaluated for each alloy. In addition, the alloys were also tested after annealing at 1200°F for 4 hr and furnace cooling. The solution-treated and annealed conditions were those in which the alloys might be expected to

Jan 1, 1959

By C. Feng, C. Elbaum

Knoop hardness measurements were carried out on large grains of iodide titanium containing different amounts of oxygen. For each oxygen content the hardness is recorded ainingas a function of the crystal orientation and of the angle 4 between the indenter diagonal and the projection of the C (hexad) axis in the surface. The results can be expressed by the following relation; hardness = n-k cos 2ø, where n and k are constants for a given oxygen content and crystal surface orientation. A NISOTROPY of hardness is a well-known phe-nomenon and has been reported for many metals.1-3 At the present time, however, such information is not available in the literature for titanium. Consequently, a systematic study of the simultaneous effects of oxygen content and crystallographic orientation on the hardness of titanium was undertaken in this laboratory. Evaluations of oxygen content in titanium are frequently carried out through hardness tests. Although such procedures may be justified in small grain specimens, the results of the present investigation indicate that the anisotropy of hardness should be taken into account in the case of coarsegrained specimens as well as in the case of pronounced preferred orientation. Materials and Experimental Procedures Iodide titanium, 99.99 pet pure and containing of the order of 0.002 wt pet O, was used throughout this investigation. The metal was arc melted in an argon atmosphere and cold rolled into strips 1/16 in. thick. These strips were subsequently recrystal-lized and strain annealed in vacuum (10" mm Hg or better) at 850°C in order to produce crystals varying in diameter from 10 to 25 mm. Oxygen was introduced into selected large crystals by heating at 700°C in an atmosphere of pure oxygen under an observed pressure of approximately 50 mm Hg. Each sample was subsequently annealed in vacuum at 850°C for 100 hr, in order to homogenize the oxygen content throughout the specimen. It was found that longer annealing was not necessary, for no change of surface hardness in a given direction was detected after prolonged annealing. The oxygen content was determined by the difference in weight of the specimens before and after the oxidation-annealing cycle. The accuracy of oxygen determination is within ±0.1 mg in samples weighing 0.5 to 1 g. A vacuum fusion analysis of oxygen was performed on several samples and gave results in good agreement with the ones obtained by the weight change. It should be emphasized that expected weight losses through evaporation of the metal in vacuum at 850°C&apos; are many orders of magnitude lower than the precision of these measurements. Following the annealing treatment, both oxidized and unoxidized crystals were carefully polished. All detectable traces of surface cold working were removed by repeated polishing and etching. Laue back reflection X-ray patterns were taken for each crystal for the purpose of determining the orientation and ascertaining the absence of substructures detectable by this method. Hardness measurements, using a 1 kg load, were subsequently carried out on a Tukon hardness tester equipped with a Knoop indenter. The Knoop indenter was used throughout this work because indentations obtained by means of a Vickers indenter are considerably distorted due to the anisotropy of the elastic constants in titanium. Such distortions are much less pronounced in the case of Knoop indentations, although for some orientations a cer-

Jan 1, 1959

By C. S. Barrett, D. B. Masson

Martensitic transformations have been found in AgCd both upon cold-working at room temperature and cooling to lower temperatures. The crystal structures of the transformation products were found to be close-packed hexagonal in the first case and or-thorhombic in the latter. The transformation characteristics also were studied. Similar treatment of AuZn alloys failed to yield any transformation. THE literature on martensitic transformations of body-centered cubic metals and alloys indicates widespread instability of this structure at low temperatures, a tendency which merits further study. The body-centered cubic ß-phase of CuZn, for example, when it contained less than 42 wt pct Zn, was found by Greninger and Mooradian&apos; and others&apos; to transform on cooling to subzero temperatures to a phase that was tentatively considered to be tetragonal. Further work by Massalski and Barrett" demonstrated that cold work at low temperatures causes a partial transformation of ß CuZn of higher Zn content. The structures of the strain-induced transformation products were found to be different from those induced by simple cooling. Another well-known martensitic transformation among body-centered cubic phases is that of ß AuCd, first studied with X-rays by Olander,&apos; then very thoroughly by Chang and Read.5,6 Here again transformation was found to occur both as a result of cooling and of strain. The alkali metals Li and Na, as well as certain Li-Mg alloys, also undergo transformation from their normal body-centered cubic structure, both on cooling and on cold-working. The phase AgCd, the subject of the present report, should be expected to behave quite similarly to CuZn for a number of reasons. It is the chemical analogue of CuZn, silver being directly below copper and cadmium directly below zinc in the periodic table. The size factors (percent difference in size) of the atoms, possibly a consideration in the stability of the ß-phases, are +3.1 in AgCd and + 4.2 in CuZn. Likewise the relative electronegativities of the two pairs of metals are about the same, CuZn possessing an electronegativity difference of 1.0 and AgCd one of 0.8. These values are from a table of electronegativities given by Darken and Gurry." The phase diagrams of the two systems around 50 atomic percent are similar, both possessing a disordered body-centered cubic phase, ß, at high temperatures and an ordered bcc phase, ß, at room temperature; however, the ß and ß&apos; phases of AgCd are separated by a hexagonal phase, [, stable in the range 220-440oC, which has no analogue in CuZn. There has been confusion in the literature as to the structures of the ß&apos; and [-phases. The phase diagram in the ASM handbook&apos;" has the structures of the two phases interchanged; however, Hansen" reports the correct relative positions and Muldawer" verified that ß&apos;, the low-temperature phase, is body-centered cubic. Work by the present authors also

Jan 1, 1959

By W. M. Parris, P. D. Frost, H. A. Robinson

The effects of hydrogen content and strain rate on the static tensile and notch-rupture properties of the Ti-3Mn-complex alloy heat-treated to differed strength levels were investigated. The extent of embriulement was found to be proportional to the amount of hydrogen present and the strength to which the specimens were heat-treated. The research suggests the possible necessity of specifying lower hydrogen limits than are now allowed when titanium alloys are heat-treated to higher strengths than are presently used. The research also supports a hypothesis advanced earlier for a mechanism of hydrogen embrittlement. MUCH attention has been focused on the effects of hydrogen in in Most of the published in- formation has dealt with the effects of hydrogen on alloys in the annealed or lowest-strength condition. The work of Kotfila and Erbin3 is one of the few exceptions. In view of the fact that heat-treatments are now being used to produce high strength in titanium alloys,&apos; it is necessary that more attention be given to the effects of hydrogen on these alloys in the heat-treated condition. Research was initiated to establish the effects of hydrogen on the properties of the Ti-3Mn-complex alloy at various strength levels. This research, which supplemented that of Kotfila and Erbin, was started because it was found that high-strength tensile specimens of this alloy were strain-rate sensitive. The essential results of the research are summarized in this paper. MATERIALS AND EXPERIMENTAL PROCEDURES Material for this investigation was a 41/2-in.-diam bar forged from a single commercial heat of the Ti-3Mn-complex alloy having the composition given in Table I. The as-received forging was reduced further by forging at 1750°F to 3/4-in. square bars. About one fourth of this material was vacuum annealed at 1400°F for 24 hr to obtain a base hydrogen content of 25 ppm. The remaining bars were hydrogenated to levels of 90, 140, and 260 ppm in a large Sievert&apos;s apparatus in the following manner: Four 3/4-in. square bars, 5 in. long, were placed in the reaction chambzr. The chamber was evacuated, heated to 1400°F, and a measured amount of hydrogen was introduced. When absorbtion was complete, as indicated by the drop in pressure, the reaction tube was cooled and the bars removed. Each batch of bars was then sealed in individual evacuated Vycor containers and heated for 24 hr at 1400°F in order to distribute the hydrogen homogeneously. After vacuum-annealing or hydroge nation, the bars were rolled at a temperature (1400°F) below the ß-transus to 1/2 - in. - diam rounds. Groups of the rolled specimens representing each of the hydrogen levels were given the following heat-treatments: 1) One hr at 1300°F, water-quenched. 2) One hr at 1300°F, water-quenched, and aged 8 hr at 1100°F. 3) One hr at 1300°F, water-quenched, and aged 4 hr at 1000°F. 4) One hr at 1300°F, water-quenched, and aged 48hr at 800°F. Heat-treated bars were machined into standard 0.250-in.-diam tensile specimens having 1-in. gage lengths. Throughout the processing and testing of this material, hydrogen analyses were made by vacuum-fusion methods to check for accuracy of hydrogen additions, homogeneity, and possible losses during processing. A summary of these analyses is given in Table II It may be seen that the actual hydrogen contents were reasonably close to the desired levels. In addition, it was noted that the variation in hydrogen content within any one bar did not exceed

Jan 1, 1959

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. &apos;These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness&apos; when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.&apos; In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By W. B. Triplett, H. I. Aaronson, G. M. Andes

THE morphology and mechanism of the proeutectoid a and the eutectoid reactions have been recently investigated in some detail in an iodide-base Ti—7.22 pct Cr alloy.&apos; These studies have now been extended to an iodide-base Ti—10.8 pct Cr alloy in order to evaluate the effects of composition on the proeutectoid and eutectoid transformations in titanium-chromium alloys. The alloy used in this investigation had the following composition: 10.8 Cr, 0.0327 0, 0.011 N, 0.0063 H, and 0.011 pct C. Specimens of this alloy were heat treated in evacuated and internally get-tered Vycor capsules. The specimens were solu-

Jan 1, 1959

By L. C. Weiner

THIS study was undertaken to round out an investigation on the effects of solid environments on the brittle fracture of zinc single crystals.&apos; In the previous work it was demonstrated that the presence of a surface film increased the cleavage strength of crystals whose basal planes were oriented almost parallel to the tensile axis by some 43 pct. This increase was observed to be independent of the type of surface-coating material, as well as of thickness of film above a certain small critical value (about 200 to 300A). These observations were described sat- isfactorily by a dislocation-pile-up-at-a-barrier model of brittle fracture2 in which twins modifying the dislocation path act as barriers, their increase in number and homogeneity of distribution brought about by the presence of the surface film. From previous work reported on the strength of ductile metal crystals as affected by gaseous and liquid environments,3 it may be concluded that the effects of these media are present only when the environment produces a surface film on the initially clean-surfaced crystal, or when it has a disintegrating effect on a previously existing surface layer. Similarly, it might be expected that an increase in cleavage strength of initially clean zinc crystals (xo = 3", A, - 28") will result only when the gas or liquid reacts with the crystal to produce a solid, adherent surface film. Clean-surfaced crystals,l 2 1/12 in. in length, were tested in tension at room temperature in an Instron

Jan 1, 1959

By H. I. Aaronson

The nucleation of pearlite at proeutectoid ferrite is inhibited, to an increasing extent, at the following locations: At twin boundary-nucleated ferrite, between closely spaced ferrite sideplates, and at intragranular plates. These effects are discussed in terms of the influence of transformation strain energies and of the interfacial free energy of austen-ite:ferrite boundaries on the rate of pearlite nucleation. The growth of pearlite into the interiors of austenite grains from the region of the grain boundaries is markedly restricted when low reaction temperatures and large austenite grain sizes permit the development of interlocking networks of intragranular ferrite plates. PREVIOUS investigators have made extensive studies of the interactions which occur between the proeutectoid ferrite and the pearlite reactions from the viewpoint of the mechanisms through which pearlite interferes with the nucleation and growth of proeutectoid ferrite.1-3 In the present investigation, the processes through which proeutectoid ferrite (hereafter termed simply "ferrite") can reduce the rate of formation of pearlite have been explored in some detail. A steel with a relatively low carbon content, in which the ferrite reaction can compete successfully with the pearlite reaction over a wide range of reaction temperature, and exceptionally coarse-grained specimens, which further emphasize the role of the ferrite reaction, have been employed for most of this work. A brief examination also has been made, however, of the effects of smaller austenite grain sizes upon these processes. Experimental Procedure The steel employed had the following composition: 0.29 pet C, 0.76 pet Mn, 0.25 pet si, 0,007 pet S, and 0.005 pct P. This alloy was homogenized for 48 hr at 1250°C. The investigation was performed

Jan 1, 1959

By A. Keil

TO measure the absolute conductivity of metallic specimens it is generally necessary to have exact geometrical shapes and good electrical contact with the test-piece. To overcome limitations of the standard methods, an electronic conductivity-meter* Trade name, Sigmatest; model Dr. F. Forster; Reutlingen, Ger-many. has been developed, which works on the principle of inducing high frequency eddy-currents in the specimens and measuring the reaction of these curients on a measuring coil.&apos;,&apos; To attach the instrument to the test specimen, a flat area of about 10 mm diam is all that is necessary. The reading is taken off a scale calibrated in pet of International Annealed Copper Standard. The induced eddy-currents are propagated in a circular motion parallel to the surface. Thickness of the layer included in a measurement depends on the frequency used. With a frequency of 60 kc per sec, the penetration of the currents was 0.8 mm at the upper limit of the scale, and 2 mm at the lower limit. The method is limited to nonferrous metals and other applications have been described elsewhere." The object of the present investigation was to detect the formation and growth of surface layers of differing conductivity, and to determine the depth to which these changes could be observed. A well known phenomenon which illustrates the problem is the internal oxidation of certain silver alloys containing base metal solutes, such as copper or cadmium, when they are annealed in an oxidizing atmosphere.4, 5 Until now, the only methods available for following these phenomenon have been metallo-graphic examination and hardness tests.0, 7 Changes in mechanical properties of copper alloys by internal oxidation were recently discussed in a more general way by Martin and Smith." When measuring these conductivity changes it must be remembered that the only absolute values of conductivity are those of 1) the nontreated homogeneous specimen, and 2) the final values obtained with a surface layer of depth comparable to the penetration of the eddy-currents. All intermediate values refer to the mixed conductivities of the transformed surface layer and the untransformed alloy, and are thus readings of relative value only. Experimental Results Specimens were annealed for 1/2 hr at 800°C in hydrogen, and the internal oxidation was carried out by thermal treatment in air at 800°C. Fig. 1 shows the results of the first series of experiments. With internal oxidation of a solid solution of 8 pet Cd in silver, the conductivity rises continuously until the surface layer formed has become thick enough to be the deciding factor (about 400µ). Precipitates of CdO are mainly in the form of points, Fig. 2, and, as a result, the electric contact between the silver crystals is not distorted by them. Brine11 tests were run with a 1.25 mm ball and a 7.812 kg load. The specimen annealed in hydrogen and oxidized to a depth of 400µ had a hardness of 40 Bhn,

Jan 1, 1959

By D. D. Pollock, D. I. Finch

PREVIOUS work&apos; on a four-component system (Cu-Mn-Ni-Fe) resulted in the development of consistent relationships between the chemical composition and the electrical properties of these manganin-type alloys. The present study was undertaken to develop alloys with temperature coefficients of resistivity and thermoelectric properties more desirable than those of the manganin type, and to determine whether the relationships which had been found for the Cu-Mn-Ni-Fe alloys could be extended to five-and six-component alloy systems. PREPARATION OF ALLOYS The five- and six-component alloys were made from OFHC copper rod, ARMCO iron, electrolytic nickel, manganese cathode chip, and special high-purity aluminum and indium. A Cu-Mg master was used for deoxidation. The compositions of these materials are given in Table I. The alloys were melted and cast as indicated previously,&apos; except that no cover was used and the melts were teemed. EXPERIMENTAL PROCEDURE The finished wire size of 0.0808 in. diam was again selected for the reason that the test specimens would be self-supporting, thus eliminating any extraneous effects which might have been introduced by winding smaller diameter wire on spools or forms. The following tests were performed on the finished wires: A) Chemical Analyses—All of the components of these alloys were determined by premium gravimetric methods. The principle residual impurity contained in these alloys is 0.008 pct Mg (by weight), maximum. Tables II and 111 present the mean analyses computed from at least four determinations of each constituent. B) Electrical Characteristics—The test procedures forthe determination of the thermal emf vs copper, resistivity, and the resistance-temperature relationship are given in detail in Ref. 1. It was also shown that the resistance-temperature relationship is of the form Pt = P,n + At -B/2, [1] where P, is the resistance at t C expressed in percent of a given standard resistance, P, is this per- 0 centage at 0°C, and A and B are constants for a given, properly treated, composition. The results of the electrical tests are also given in Tables II and 111. INTERPRETATION OF DATA The modified Linde2 formula, known to be valid for dilute binary solid solutions, was applied to the complex Cu-Mn-Ni-Fe type alloys. This relationship is of the form where Ap is the increase in resistivity. Zb the valence of the solute, Zn the valence of the solvent, and K and K are designations assigned by Robinson and Dorn3 to the constants for the periodic group to which solute element belongs. The units of K, are -cm per valence difference squared per at. pct; those of K2 are pa-cm per at. pct. For the sake of brevity, these units are not repeated in the following discussion. Calculations were made to determine if this formula was accurate for five-component systems. No experimental studies were made of the Cu-In and Cu-A1 binary systems. The effects of indium additions upon the resistivity of copper are given by Linde. These data, along with those of the effects of Mn and Fe, permitted the calculation of the effects of Al.

Jan 1, 1959

By A. P. Young, F. C. Holden

IN many of the early investigations of the aging of titanium alloys, it was observed that the retained beta phase could be aged to a high hardness without an apparent change in microstructure; moreover, in some alloys it was found that even a very rapid quench produced beta having an anomalously high hardness. What appeared to be hard beta phase was designated as "beta prime," to distinguish it from the softer normal retained beta phase. Frost and co-workers&apos;.&apos; demonstrated that the increased hardness is caused by the formation of a metastable phase, omega, which can be identified from its X-ray diffraction pattern. This reaction also has been studied by Brotzen, et a1.,3 and the structure of the omega phase has been published by Silcock, et al.," and by Austin and Doig.3 The X-ray diffraction analysis by Austin and Doig indicated that omega is low in alloy content, approaching the composition of the stable alpha. The aging process proceeds by the path Thus, overaging results in the formation of alpha and the ultimate disappearance of omega. This is accompanied by a decrease in hardness and a recovery of ductility. The present work represents a study of the aging process in a high-purity Ti-6.4 Mn alloy, in which optical and electron microscopy, X-ray diffraction, and hardness data were correlated. The specimens, 1/8-in. sections cut from 1/4-in.-diam rod, were heated in argon to a temperature just into the beta field (810°C), held for 1 hr, and water-quenched. The aging samples were heated in air for 1 hr at 300 to 500°C. The specimens were ground and mechanically polished, finishing with alternate etching and polishing on a slow-speed wheel to remove disturbed metal from the surface. The surface finally was swab-etched, rinsed with tap water, and air-dried. The etchant used was an aqueous solution containing 1 1/2 pct HF and 3 1/2 pct HNO3. This procedure is identical with that used for preparing metallographic specimens, except that the optimum degree of final etching required for electron microscopy may vary from that used for light microscopy. Metal replicas, backed with silica, were prepared from plastic strip-pings for examination with the electron microscope. Complete details of the procedures used for preparing these replicas are available elsewhere." Fig. 1 shows a comparison between the structures revealed by the electron microscope and those obtained by conventional light microscopy. Hardness and X-ray diffraction data are listed in Table I. No evidence of a second phase is apparent in the optical micrographs for the as-quenched sample, or for the specimens aged at 300 or 400°C; fine alpha particles can be seen in the specimen aged at 500°C. In the electron micrographs, visible equiaxed pocks appear in the as-quenched specimen, and, with increasing density, in the samples aged at 300 and 400°C. After aging at 500°C, the structure becomes markedly coarser and develops an oriented appearance of a second phase, coincident with the appearance of visible alpha particles in the light micrographs. These observations are confirmed by X-ray diffraction and hardness data. In these specimens, aged for 1 hr, the intensity of the omega pattern increases to a maximum at the 400°C aging temperature, corresponding to maximum hardness and the maximum density of pocks in the electron micrographs. At this point the beta phase shows a definite enrichment in Mn. At 500°C, little or no omega re-

Jan 1, 1959

By W. A. Backofen, M. L. Ebner, D. H. Avery

Slip on (11221 planes, which do not contain a close-packed direction, has been identified on crystals strained at —190°C. Evidence is also presented to show that (1071) pyramidal slip is a mode of deformation at 25ºC in a limited orientation range. PYRAMIDAL slip (l011) <1120> in magnesium at elevated temperatures has been established for some time.1-2 More recently, Burke and Hibbard reported this mode of deformation at 25"C, but their results were questioned by Craig.&apos; Also, as far as the present authors know, slip in magnesium on pyramidal planes of the second order, Type II (1122)) has not previously been reported, although Gilman"," identified (1122) slip in another hexagonal metal

Jan 1, 1959

By D. E. Swets, P. C. Frank, D. L. Fry

THE hydrogen-steel system has received considerable attention in the past several years. Recent experiments in this laboratory have shown that another group of operations, namely, sanding and grinding,&apos; must be added to the already well-estab- lished list of phenomena that cause hydrogen to permeate steel. Qualitative tests which have been made with a very sensitive ion-gage type of detector similar to that used by Norton,&apos; showed that sanding a steel surface caused hydrogen permeation. A metal type 6~6 vacuum tube was used as the ion gage with an electrometer to measure the ion c~rrent.~ The protective enamel coating was removed from the tube.

Jan 1, 1959

By W. J. Feuerstein

STRUCTURAL imperfections in crystals, in recent years, have received the attention of metallurgists concerned with single-crystal properties. Certain etching solutions cause local variations in the rate of etching at dislocations.&apos; Dislocations are expected to be preferred segregation sites for impurities&apos; and Dash" has shown that precipitation of copper occurs preferentially at edge-type dislocations in silicon. Diffusion rates along dislocations are probably higher than rates through more perfect crystalline regions.&apos; These and other phenomena which may be influenced by dislocations may be studied by revealing dislocations as etch pits. This study was undertaken to develop an etch solution for silicon crystals to reveal low-angle grain boundaries associated with dislocation arrays and also etch pits with good contour definition. Additional etches have been reported by Dash," Vogel and Lovell.T rystals were sectioned on crystal lographic planes at various angles from the growth direction for microscopic examination of the etch pits. Experimental Crystals of 75-100 g mass and 3 cm diam were oriented and cut on crystallographic planes. Crystals were grown by Czochralski technique from a quartz crucible. Lapped wafers were chemically polished in a modified CP-4 etch for 1 min (bromine was deleted from the etch solution). The polished wafer was then etched* at room temperature for 5 min. The use of larger amounts of H2O and/or CH2COOH slows the reaction. The Cu(NO3),.3H2O was added to increase the reaction rate and give more definition to the etch pits developed. Some pertinent features concerning the attack of this etch on silicon can be summarized as follows:

Jan 1, 1959

By H. W. Weart, D. J. Mack

SINCE the first recognition of eutectic solidification as the simultaneous formation of 2 solids from one liquid,1 many complex structures thus produced have been observed. Despite many attempts to ascertain it, however, the detailed mechanism by which these structures develop remains obscure. In an attempt to clarify the origin of eutectic structures, the study described in this paper was undertaken. The broad objective of the study was to investigate the effect of different solidification conditions on the structure of single eutectic grains. It was expected that the eutectic structure would thereby be isolated for study, but preliminary experiments revealed another structure within each grain. When a literature surveye revealed only 1 previous mention of the subgrain structure,&apos; it was decided to determine the origin of the structure and to study its response to various growth conditions. Before presenting the details of the investigation, it is apropos to distinguish carefully among the 3 structures produced during eutectic solidification. This is especially desirable in view of the apparent confusion existing in the literature concerning the structures in a eutectic specimen. The confusion is due largely to the existence of the subgrain structure noted above which is easily mistaken for the grain structure. In the following paragraphs, an effort is made to distinguish the 3 structures by briefly describing their origin during solidification, even though the results are thereby anticipated slightly. The 3 structures produced during eutectic solidification are the grain structure, the colony structure, and the eutectic structure, each one contained by the one preceding it. The grain structure is analogous to the polycrystalline structure of a metal or inle-phase alloy in that each grain grows from a single nucleus. A somewhat broader interpretation is needed here, however, because of the presence of 2 phases in each grain. Since in most eutec-tics particles of 1 phase are dispersed in a matrix of the other, a grain may be taken to be the region in which the matrix phase is monocrystalline.*

Jan 1, 1959