By M. E. Wadsworth, T. L. MacKay

Sintered UO, samples were leached in sulfuric acid solutions of various concentrations. A pressurized system was used so that it was possible to investigate the kinetics of the reaction to 270°C with oxygen overpressures as high as 900 psi. The rate was observed to be a function of the concentration of hydrogen ions and directly proportional to the partial pressure of oxygen. Evidences are presented which indicate that a UO2 surface site reacts with a molecule of water to form a hydroxyl complex which in turn can dissociate with the characteristics of a weak acid. A rate determining step has been proposed which involves the reaction between an oxygen molecule and the hydroxyl complex on the surface of UO,. ThE 2 principal methods for uranium dissolution are carbonate and acid leaching. The sulfuric acid leach is the more popular and is used for the treatment of the majority of the ores of Africa, Canada, and the United States. Low recoveries in basic leach circuits led investigators at the University of British columbia1 to study leaching of uranium ores in pressurized vessels. Early in the study of dissolution of uranium it was found that only uranium in the hexava-lent state could be leached in acid or basic circuits. Therefore, the use of oxygen over-pressure in an autoclave offered an interesting approach to solving the low recovery problems of carbonate leaching. UO, was used in this study because it could be obtained in high purity and also because it is representative of the most refractory of the primary uranium minerals. A pressurized system was used to provide a means whereby important temperature and pressure parameters could be varied for the evaluation of the kinetic processes. The mechanism for the dissolution of UO2 should be similar for any of the uraninite type minerals. At the present all of the kinetic studies that have been conducted have been in carbonate media. Peters and Halpern2 carried out a kinetic study of the leaching of pitchblende. Their specimens were pitchblende ores selected on the basis of high grade and homogeneity. Pearson and wadsworth3 conducted a kinetic study of the dissolution of UO2 in carbonate solutions with results very similar to those obtained by Peters and Halpern. EXPERIMENTAL The UO2 as received* was found by spectroscopic *Mallinckrodt reagent, supplied by the Atomic Energy Commission. analysis to have a purity of 99.94 pct 0.03. It was ground in a mechanical agate mortar and screened through a 400-mesh sieve. Thin flat disks of UO2 were prepared by pressing the sized powder in a specially constructed die at a total pressure of approximately 25 tons per sq in. The pressed disks were approximately 0.25 cm thick, 1.6 cm diam, and 3.5 g in weight. As pressed, the samples were approximately 65 pct of theoretical density. It was essential that a binder such as poly-vinyl alcohol be added before pressing to prevent formation of cracks when fired. It was found by trial and error that pressed disks sintered close to 1870°C in a hydrogen atmosphere, reach densities between 91 and 91.5 pct of the theoretical density. At this density the samples had no measurable porosity based upon a 2-hr emersion in boiling water. An X-ray examination of these sintered UO2 disks showed them to be identical with the original UO2 received. Reaction of UO2 with the alundum furnace core was prevented by placing molybdenum between the samples and the core according to the method of Corwin and Eyerly.4 Leaching studies were carried out in a specially designed autoclave, the details of which have been presented e1sewhere.6 The main features of the equipment as applied to a kinetic study are: 1) solution samples may be removed during the course of a single run; and 2) temperature and agitation are carefully controlled. Two-ml samples removed from the autoclave during the course of a run were analyzed for U3O8 content with a Beckman model DK-2 spectrophotometer by the method of

Jan 1, 1959

By F. E. Lathe, L. Hodnett

This paper summarizes extensive data supplied by 40 copper converter plants in 18 countries, and includes a partial analysis and comments on the effect of converter slag composition and temperature on the fomzation and elimination of magnetite and the life of basic and neutral refractories. APRELIMINARY draft of this paper, including data from 26 companies which had submitted replies to a questionnaire, was presented at the Annual Meeting of the AIME held in New York in February, 1956. Publication was delayed in the expectation that additional replies would be received, and justification for the subsequent delay may be found in the fact that the present revised paper contains data from 40 converter plants situated in 18 different countries. The suggestion that a questionnaire be sent to the major copper and copper-nickel plants outside the U.S.S.R. and associated countries arose at the Los Angeles Annual Meeting in February, 1953, where several papers dealing with converter construction and operation were presented. In private discussions which followed, a group of metallurgists and refractories engineers raised the question why practices varied so much at different plants. Why did magnesite brick give superior service to chrome-magnesite in some plants but chrome-magnesite prove superior in others? Would metallurgical studies point the way to the development of still better refractories? Could magnetite formation be prevented in converter slags and reverber-atory furnace mattes? If this was feasible, why was a heavy circulating load of magnetite tolerated, when, in all probability, it increased copper losses in the reverberatory slags and, in some cases, made it necessary to shut down the furnaces periodically to clean out the accumulated magnetite? Was the sole purpose of coating brick with magnetite that of

Jan 1, 1959

By F. A. Forward, A. H. Ross, J. Halpern

Application of the carbonate leaching process to carno-tite ores has often been limited by the difficulty of obtaining simultaneous high recoveries of uranium and vanadium. The chemical aspects of this problem are discussed and the effect of prior roasting procedures on this discovery is described. IN treating carnotite ores by carbonate leaching it is often necessary to subject the ore to a prior roast. Among the advantages that may result from roasting are: 1) improvement in settling and filtering characteristics of the ore; 2) destruction of carbonaceous impurities that would otherwise contaminate the leach solution and consume carbonate reagent; and 3) substantial increase in extraction of vanadium, which is usually low when the un-roasted ore is leached. Recovery of vanadium may be an important factor in processing carnotite ores, and the fact that vanadium is usually recovered in good yield by acid leaching has often been an economic advantage over results obtained with carbonate leaching. It has been found that response of an ore to carbonate leaching, following roasting, depends primarily on its composition and on the conditions of the prior roast treatment, particularly with regard to the roasting temperature, the atmosphere maintained above the charge during roasting and cooling, and the presence of certain reagents. These factors, especially the last, virtually determine the extractions of uranium and vanadium attainable by carbonate leaching, as well as the reagent consumption on leaching, whereas adjustment of the leaching conditions has only a limited influence. These variables were examined systematically to elucidate roasting and carbonate leaching of carnotite ores and to establish a treatment yielding high recoveries of both uranium and vanadium. Tests were conducted on samples of four different Colorado Plateau ores, described in Table I. Roasting Procedure: The roasting tests were conducted in an electrically heated furnace in which the temperature was controlled to ±15°C. The ore (usually a 500-g charge) was ground to —100 mesh, mixed with the desired reagent, and spread in a silica tray to a bed depth of about 1/2 in. During the roast the charge was rabbled at intervals of 15 min. To provide free access of air the furnace was usually ventilated; however, in a few experiments a controlled atmosphere such as carbon dioxide or hydrogen was maintained above the charge. Leaching Procedure: The pulp, generally comprising 500 g of ore and a 2000-cc solution containing 80 g per liter of Na2CO8 and 20 g per liter of NaHCO3, was agitated in an autoclave at 120°C, under 30 psi 02. Samples were withdrawn periodically, and the solution and ore residue were analyzed. Under the conditions employed, maximum attainable extractions were generally achieved in 4

Jan 1, 1959

By J. D. H. Strickland, K. J. Jackson

IN previous papers' ' details were given of the constructlon and use of an apparatus to study the rate of chlorine consumption and the rate of sul- fate and sulfur production when dilute aqueous chlorine solutions were allowed to react with pyrite and galena in acid solutions at or near room temperature. The reaction with pyrite was very rapid, and hence entirely transport-controlled in its kinetics, and produced only ferric and sulfate ions. The behavior of galena was much more complex and was studied in some detail. Sulfur monochloride could be detected as a reaction product and both

Jan 1, 1959

By S. Senderoff, D. E. Couch

A PROCESS for the electrolytic preparation of molybdenum from molten salts has been described previously. This previous work centered on electrowinning and electroplating characteristics of the process. In this paper the properties of the process as a refining medium are discussed. In producing metals from ores, it frequently has proven most economical to obtain a comparatively impure metal by smelting, and to purify the product by electro refining. Direct electrowinning from molten salts is rather difficult when a porous diaphragm is required in the process, as in the case of molybdenum, since satisfactory refractory materials for such a diaphragm in molten salts have not yet been developed. In electrorefining, however, a soluble anode is used. By suitable control of anode and cathode current densities, the lower-valent molybdenum compound used in the electrolyte is not oxidized, and a diaphragm is not needed, thus avoiding difficulties which are encountered with other electrowinning processes. Electrorefining may result from two different processes in the cell: Dissolution of the molybdenum and the less noble impurities with a separation of the more noble impurities as an anode sludge; the electrodeposition of molybdenum and the more noble metals at the cathode, leaving the less noble metals in the electrolyte. The amount of separation which occurs in each process is determined by the potential of the operating electrode and the relative concentration of the various species at (or in) that electrode. Since molybdenum has a comparatively noble position in the EMF series in molten alkali halides,2 most refining would be expected to occur at the cathode. In this work only the cathodic process was studied. The objective was to determine to what extent various metallic ions, if they dissolve from the anode or are otherwise introduced, were concentrated in the electrolyte. The necessary conditions for the separation of each and the limiting concentration which may be tolerated in the electrolyte for effective refining were studied. The deposits were chipped from the cathode and analyzed spectrochemically for metallic impurities. Besides determining the major contaminant, a general qualitative analysis was obtained to be sure that other metallic ions were kept at a very low level during each series of runs and to be sure that the baths were not being contaminated accidentally. Samples of the bath, for analysis, were taken at the temperature of operation so there was no chance of selective crystallization during cooling. In this way the ratio of molybdenum in the bath to the other metal could be determined readily. These data permitted a check on the anode efficiency and any volatilization that took place during the electrolysis. Experimental Apparatus—The apparatus as shown in Fig. 1 was used to determine the effect of the various foreign ions upon electrodeposited molybdenum. The entry chamber A allowed the cathodes to be removed without cooling the bath and without allowing oxygen or moisture to enter." The cathodes were made Prom 0.25-in. tungsten rods and were rotated during the electrolysis. The balloon in the lower arm B was inflated with helium after the cathode was drawn up into the upper section for removal. A new cathode was then placed into the entrance chamber A after which the chamber was flushed

Jan 1, 1959

By H. K. Najarian

This paper describes recent development work on the Wheaton-Najarian Vacuum Condenser for Zinc at Josephtown Zinc Smelter, wherein, to dissipate the heat of condensation, the "airlift" action of gases bubbling through the molten zinc in the condenser is utilized to circulate the zinc through an outside "cooling well" and cooling it continuously. AN earlier paper1 gave an account of initial development of the Wheaton-Najarian Vacuum Zinc Condenser at the Josephtown Zinc Smelter of the author's company. This paper is a progress report of further development work over the years directed toward improving the efficiency and increasing the capacity of the condenser. In this type of zinc condenser, zinc vapor with accompanying noncondensable gases from electro-thermic zinc smelting furnaces is passed upwardly through a mass of molten zinc confined in a refractory-lined U-tube. The zinc vapor condenses in the molten zinc and the noncondensable gases are drawn out of the condenser by suction applied over the surface of the molten zinc. The heat of condensation of zinc, amounting roughly to 1000 Btu per lb of zinc condensed, is absorbed by the molten zinc and, in turn, is dissipated continuously to keep the temperature of molten zinc in a range to permit effective condensation. At the time of publication of our first paper, we had at Josephtown Smelter five units of 69-in.-bore metal furnaces and one larger metal furnace having 96-in. bore. Each 69-in. metal furnace had a condenser with 22-ft overall length. The 96-in.-bore furnace had a condenser with overall length of 31 ft. Condensers were of circular cross section, with corrugated steel outer shell and carborundum lining. Diameter of these condensers was 32 in. inside the refractory lining. Molten metal in the con- denser was kept cool by spraying cold water on the outside of the condenser shell. Under good operating conditions, 22-ft condensers produced some 12 tons of metal per day; and the 31-ft condenser, about 22 tons. When the furnaces produced zinc vapor at higher rates, invariably the condenser temperature would rise to levels where excessive blue powder would form and accumulation of accretions in the condenser would be accelerated. We found that, with the system of cooling in use, we had to provide heat-exchange surface of some 150 sq ft to condense 1000 lb of metal per hr with reasonable efficiency. The wall of the condensers was made up of 5/8-in.-thick corrugated-steel shell having next to it several layers of mica and inner refractory lining of special carborundum shapes to fit the corrugation in the steel shell, and having a minimum thickness of about 2 in. Relatively low rate of heat transfer through the thick condenser wall and slow internal circulation of the molten zinc limited the rate of heat exchange between hot metal within the condenser and the cold water flowing over the outer steel shell. The thickness of the condenser wall was about minimum that we considered suitable for continuous operation. As we learned to operate the electrothermic furnaces with higher power input, producing zinc vapor at higher rates, it became apparent that we needed condensers having larger heat-exchange surfaces. Our 96-in.-bore furnace had 6 single-phase power circuits with transformers rated at 500 kva each and normally good for power input of 3000 kw.

Jan 1, 1959

By E. R. Macgregor, J. Halpern

The kinetics of the reduction of cupric salts in aqueous solution by molecular hydrogen to metallic copper are described. The rate of reduction appears to be homogeneously determined and shows a marked inverse dependence on the hydrogen-ion concentration. Precipitation of copper is more rapid and complete in sulfate than in per-chlorate solution. A mechanism is proposed which accounts for this behavior. IN recent years a number of important hydro-metallurgical processes have been developed in which metallic salts in aqueous solution are reduced by gaseous hydrogen, usually at elevated temperatures and pressures, and thereby precipitated either in metallic form (e.g. Ni, Co, Cu) or as an oxide or salt of lower valence (e.g. VO, and VA).1 ; In connection with applications such as these, most of which involve heterogeneously catalyzed reactions, recent demonstrations"-" that salts of certain metals, e.g., Cu", Ag' , Hg" , and Hg,+ can activate molecular hydrogen homogeneously and thus catalyze hydrogenation reactions in aqueous solution, are of considerable interest. For example, cupric salts catalyze the otherwise slow homogeneous reduction of dichromate and ceric salts by hydrogen, i.e. Cr,O; + 3HL. + 8H1 ? 2Cr'- -- 7H,O [1] 2Ce ' ! H.. ? 2Ce" | 2H . [2] In perchloric-acid solution, where Cu" is not appreciably complexed, the kinetics have been found" " to be of the form -d [H,] _- k,[HJ [CU"]' dt -LCu+' l+ (k ,/k,) [H] [3] where, K = 1x10"' exp [—26,600/RT] 1, mole-' min-' ... [4] and (k ,/k,) - 0.25 at 110°C. This kinetic behavior suggests that the reaction proceeds by a mechanism involving the following sequence of steps kt Cu" +H1CuH' 4-HA [51 k., CUH + CU" ? + 2Cu f H' [GI 6Cu'+ Cr,07 + 14H'+ 2Cr- (¦ 7H,O + 6Cu" ['i] fast The catalytic activities of the undissociated cupric-sulphate and cupric-acetate complexes are somewhat greater (by factors of 6.5 and 120, respectively) than that of the simple hydrated Cu" ion.'" These considerations suggest that, in contrast to the other hydrometallurgical hydrogenation reactions, referred to previously, reduction of cupric salts in aqueous solutions by molecular hydrogen, should proceed homogeneously, and in the absence of an extraneous catalyst. This has already been demonstrated" for acetate-buffered solutions where the product of the reaction is a precipitate of cuprous oxide (Cu,O). In the present paper, an investigation of the reduction of cupric salts in perchloric-acid and sulphuric-acid solutions, leading to the precipitation of metallic copper, is described. Some results for the sulphate system, which is of considerable hydrometallurgical interest, have been reported previously by Ipatieff",' " and by Schaufel-berger' but these do not give a quantitative account, of the kinetics and mechanism of the reaction. Experimental The reduction experiments were conducted in the 1-gal, titanium-lined autoclave described in connection with earlier related investigations," " and using a similar procedure. The solutions were made up by dissolving known amounts of CP grade Cu(ClO,), and HC10, (or CuSO, and HISO,) in dis-tilled water. While in the autoclave, the solution was stirred and maintained at a constant temperature (±loc) and under a constant partial pressure of hydrogen gas. It was ascertained that the agitation (provided by two 3-in., four-bladed stirrers, rotating at 900 rpm) was adequate so that at no time was the rate of reaction limited by solution of hydrogen. During each experiment, samples of the solution were withdrawn periodically, allowed to cool, and the concentration of copper remaining in solution was then determined electrolytically. Some Cu' is formed during the reaction, but undergoes disproportionation when the solution is cooled to room temperature. For purposes of kinetic calcula-

Jan 1, 1959

By P. A. Beck, S. Kohara, M. N. Parthasarathi

IT has been shown1,3 that many observed phenomena related to annealing textures in f.c.c. metals can be adequately accounted for, at least in a qualitative way, by considering the orientation dependence of the boundary mobility, without any hypotheses concerning preferred orientation of nuclei. It was noted1 that this approach is particularly successful in the common cases of primary recrystallization in highly cold-worked polycrys-talline metals, where nuclei occur in great abundance, and that in the other extreme case, where the number of nuclei is very limited, or even only a single crystal is grown, the orientation dependence of boundary mobility has only a small effect, or none at all, on the orientations resulting from annealing. Recently Dunn described examples3-6 where observed secondary recrystallization textures apparently cannot be accounted for on the basis of oriented growth alone, but also require oriented nuclei, or at least the absence of nuclei in certain orientation ranges. In general, the great difficulty in correlating the preferred orientation of recrystallized grains with that of nuclei is inherent in the fact that nuclei are by nature very small, and that they are usually identifiable as "nuclei" only after growth, i.e., after they have already been subject to growth selectivity. An investigation was carried out by Liebmann and Lücke,' and also a very similar one by Graham and Cahn,' to obtain quantitative information on the orientation depend- ence of boundary migration rates in the recrystallization of slightly deformed aluminum single-crystal rods or plates, in which artificially nucleated recrystallized grains of predetermined orientation were grown. Liebmann and Lücke foupd maximum boundary mobility for boundaries across which the misorientation corresponded to a rotation of 40 deg around a common [Ill] axis, in accordance with earlier conclusions.9,1 Also, they confirmed that such an orientation relationship predominates among crystals growing into slightly extended single crystals from presumably random artificial nuclei. On the other hand, Graham and Cahn found no preferred orientation among crystals grown in a similar manner. It is not as yet known how these observations may be reconciled with each other. The view has been expressed in various papers5'10,21 that selective growth based on the orientation dependence of boundary mobility is not in itself sufficient to account for the formation of sharp re-crystallization textures, such as those often observed in highly deformed polycrystalline metals after annealing. The present work was undertaken to ascertain whether or not it is possible to obtain a sharp re-crystallization texture in a case where random nuclei are assuredly present in large numbers. It was previously found1' that high-purity aluminum crystals rolled 80 pct on the (110) plane in the [1T2] direction, when suitable precautions are taken, may be annealed for periods of about 1000 sec at 350°C without recrystallization. It was also found that the reluctance to recrystallize in this case is due to the scarcity of material in sufficiently deviating orientations to serve as nuclei. By using such a matrix,

Jan 1, 1959

By J. C. McDonald

A DDITIONAL experimental data are presented in this note on a phenomenon which has been touched on but lightly in the literature. The common magnesium base rolling alloy (AZ31B) contains about 3 pet A1 and 1 pet Zn. When cold rolled, it hardens until it starts to break up in the rolls at 30 to 50 pet reduction. When it is heated after rolling to full hardness, it softens. However, other magnesium alloys have shown themselves capable of being cold rolled indefinitely, provided the ratio of roll diameter to starting gage is sufficiently high. As measured by the tensile test, these alloys actually soften when the reduction becomes large (60 to 90 pct). A subsequent heating at 300' to 500°F can produce hardening of this metal. Heating at higher temperatures (600' to 800°F) causes recrystalliza-tion and softening. Menzen' has shown that a magnesium base alloy can be cold rolled without intermediate anneals as much as 90 pet. The alloy studied, Mg-1.5 pet Mn, softened considerably between 20 and 90 pet reduction, as measured by tensile properties; a decrease in yield strength of 30 pet, and an increase in elongation from 3.2 to 16.7 pet (longitudinal direction of the sheet). However, Menzen gives no data on the reaction of this metal. to heating. Ansel and Betterton2 and Hurst and Hatch3 report a similar effect in Mg-1.5 pet Mn-0.1 pet Ca. Their data show an initial hardening, followed by softening. The former authors also show that the alloy softened by cold rolling will harden when heated at low temperatures, and that these effects are absent in Mg-3 pet Al-1 pet Zn. In the course of work4, 5 some years ago, the author observed similar effects with alloys containing cerium, thorium, or zirconium; but not with elements like aluminum, silver, or zinc. Table IA contains the results of an experiment which shows these effects rather well. A binary alloy with 0.3 pet total rare earths (Mischmetal* added) was rolled hot to 1/16 in. and then annealed to full softness by heating 30 min at 800°F. Rolling was continued at 1.5 pet per pass to 80 pet total reduction on 8 in. diam rolls. The metal was harder after 20 pet work than initially but, at 80 pet reduction, properties were back to their original values. Heating for 1 hr at 450°F produced about the same hardness whether the reduction was 20 or 80 pet. At intermediate reductions, the metal hardened, but not to as high values. Extensive cold rolling may also be carried out on metal hot rolled at temperatures sufficiently low to produce a semihard temper. Mg-0.6 pet Zr was rolled to 0.1 in. at 700° to 800°F, 30 pet per pass. As shown in Table IB, a further cold reduction of 85 pet, at 1.5 pet per pass, definitely softened the metal.

Jan 1, 1959

By M. W. Burkart, B. Lustman

Uranium-base alloys exposed to high temperature water fail either by uniform oxidation or by sudden cracking and disintegration of the metal. The disintegration results from the oxidation of a second phase which is precipitated during the corrosion process. The precipitate has been identified as a metastable hydride of uranium. URANIUM-BASE alloys consisting of the body-centered-cubic ? phase are susceptible to two different modes of corrosion failure when exposed to high temperature water. In the first process, a smooth oxide film is formed on the metal surface which continually flakes off during exposure and results in a uniform weight loss of the specimen. The oxide is present as a thin, adherent layer whose thickness remains approximately constant. As the metal oxidizes during corrosion, a nonadherent layer is built up on this film and continually sloughs off. Coincident with the uniform corrosion just mentioned, another process occurs which eventually leads to failure of the metal by cracking and general disintegration. The failure takes place during a relatively short time compared to the total exposure. To distinguish this type of failure from the uniform corrosion, the cracking or disintegration of the metal will be referred to as discontinuous failure. For the ? phase uranium alloys it is discontinuous failure rather than uniform corrosion that limits the useful corrosion life of the alloy. This paper will be concerned primarily with the mechanism of discontinuous failure. Physical Changes During Corrosion—The alloys used in this investigation were ? phase uranium alloys containing 7 to 12 wt pet Mo or Cb. The preparation of the alloys, the method of corrosion testing, and the actual corrosion results are presented in another paper.' The ? quenching treatment consists of annealing the alloy for 24 hr at 900°C in a sealed Vycor glass tube filled with helium and then water quenching to room temperature without breaking the tube. The corrosion behavior typical of a ? phase uranium alloy is shown in Fig. 1. This specimen was a U-12 wt pet Mo alloy tested in pressurized, degassed water at 650°F. The corrosion rate was practically constant at 0.28 mg per sq cm per hr or increased slightly until about 15 to 20 days of exposure, when the onset of discontinuous failure occurred in this particular sample, and the specimen soon began to crack and disintegrate. The simultaneous increase in the observed corrosion rate is a result of the increased area of exposure due to cracking of the specimen. The microstructure of a specimen that failed by cracking is shown in Fig. 2. The presence of a plate-like precipitate can readily be seen. Metallographic examination of corrosion specimens reveals that the onset of discontinuous failure is always preceded by the formation of a plate-like second phase in the ? uranium matrix. Hydrogen analyses of specimens periodically withdrawn from corrosion test reveal that the hydrogen content of the alloy increases on exposure to the high temperature water, as shown in Fig. 3. The hydrogen is available as a corrosion product resulting from the formation of UO2 by the reaction of the alloy with water. Specimens analyzed just prior to discontinuous failure contained as much as 1200 ppm H, whereas the plate-like phase appears to precipitate out at a hydrogen concentration of between 10 and 25 ppm. The observed increase in hydrogen content prior to and during the formation of the plate-like precipitate suggests that this constituent may be a hydride of uranium. Additional evidence linking the identity of this phase to a hydride is that it can be removed by vacuum annealing at temperatures of 100°C and above. Decomposition products of the ? phase would certainly not dissolve at such temperatures, nor could other likely products of corrosion, such as oxides, be dissipated at any of the test temperatures. The precipitation and growth of the second phase during corrosion is accompanied by an increase in hardness of the specimen. The hardness increase results from the dispersion of the harder precipitated

Jan 1, 1959

By J. J. Gilman

WHEN a cleavage crack that is moving through a crystal intersects a screw dislocation, a jog is created in the crack front. As the crack continues to move, the jog leaves behind a cleavage step. This mechanism was proposed by Amelinckx and Votava,' Pratt, bnd Gilmanh t about the same time. At that time the evidence for the mechanism was largely indirect. Other evidence has been presented by Low, Bilby and Smith,5 and Forty.' It is the purpose of this paper to present more direct evidence of this mechanism and to show that observations of cleavage steps can be used to detect screw dislocations. Experimental Lithium-fluoride crystals that were purchased from the Harshaw Chemical Company, as well as natural mineral crystals and metal crystals, were used in the experiments. Although cleavage steps can be observed on transparent crystals with a metallurgical microscope, the contrast is poor. Marked improvement in the contrast is obtained by depositing thin (1000A) films of silver or aluminum onto the surfaces. The contrast also can be improved by using a phase-contrast microscope, but the simpler silvering method gives just as good results. Tolansky interferometric microscopy, and electron microscopy were used to measure the heights of cleavage steps. The etching techniques developed by Gilman and Johnstonh ere used to detect dislocations in the LiF crystals. Results The dislocations that create cleavage steps can originate in three ways: a) They can be grown into crystals b) They can be introduced by plastic deformation prior to cleavage c) They can be formed just in front of the tip of a propagating cleavage crack.' These three situations will be considered in turn. Grown-in Dislocations—It is not possible to see the individual monomolecular cleavage steps that emanate from isolated screw dislocations in crystals.

Jan 1, 1959

By O. D. Sherby

In 1938, Kanter' revealed that the steady-state creep rate of low-carbon iron alloys could be correlated by an activation energy expression, where the activation energy for creep, Qc, was found equal to about 90.0 kcal per mole for most of the alloys investigated. He suggested that creep at high temperatures might be controlled by some sort of solid self-diffusion process since the value of Qc was about equal to the known value for self-diffusion, Qd. Correlations were not further attempted along these lines until many years later, when new evidence2-8 was presented suggesting that Qc = Qd for many metals. This equality now appears to be established for ten metals (Al, Pb, Ni, Mg, Cd, In, a Fe, y Fe, Cu, and Au). This experimental fact prompted several investigators to postulate various mechanisms of dislocation motion which would yield an activation energy for creep equal to that for self-diffusion.7-9 Possibly the most accepted theory is that based on dislocation climb7 where a dislocation is envisioned to surmount a barrier by an atom-vacancy exchange process, thereby "climbing" from one slip plane to another. Such a model would suggest that the steady-state creep rate, i, should be directly proportional to the rate of self-diffusion, D, for a given creep stress. In order to more clearly reveal the relationship between creep and diffusion, and to eventually determine the correct model, it would be desirable to obtain data showing correlations between i and D, rather than with a comparison of the temperature coefficients, Q. It has been known for some time that the self-diffusivity of iron atoms is greatly decreased when body-centered-cubic (a) iron transforms to face-centered-cubic (y) iron. This has been ascribed to the more close-packed structure of y iron. The diffusivity ratio at the transition temperature is Da/Dy =350. Correlations of creep data for a and y iron5 reveal that the creep rates under a given stress at the transition temperature differ by about the same ratio (ea/ey 2 200). It would be difficult to reconcile these results on any other basis than that the diffusivity of atoms probably controls creep of iron in some very direct way. No other published data on other allotropic metals appear currently available for further checking such a possible correlation between i and D. Thallium transforms from a hexagonal close-packed (a) structure to a body-centered-cubic (ß) structure at 230°C (503°K) and the self-diffusivities of the two structures have been determined by shirn.10 His results are plotted in Fig. 1 where it will be noted that Dß/Da = 25 at the transition temperature. It would appear desirable, therefore, to determine the creep rates of polycrystalline a and ß thallium at the transition temperature, as well as determine

Jan 1, 1959

By J. B. Newkirk, W. G. Martin

Oxidized cobalt powder is known to have a magnetic hysteresis loop which is asymmetric with respect to the magnetization axis. The experiment described herein shows that the orientation relationship between the basal plane of hexagonal cobalt and the oxide which forms upon it at 400°C is {111}ux//{100.1 }co <110>ux//<11.O> This orientation relationship allows a magnetic interaction between the antiferromagnetic oxide and the ferromagnetic substrate which could account for the offset hysteresis loop. Oxidized nickel powder has a symmetrical hysteresis loop and so is apparently not influenced by any magnetic interaction between metal and oxide. The orientation of the oxide (cubic) was found to be identical with that of the nickel substrate when the oxide forms on a polished surface parallel with {111} Ni. IN 1956 W. H. Meiklejohn and C. P. Bean discovered that fine particles of cobalt which had been prepared in a certain way have a magnetic hysteresis loop which in a strong field is asymmetric relative to the magnetization axis.&apos; The cobalt powder exhibited this unusual magnetic property only after it had been oxidized in air or oxygen; it lost the shifted hysteresis loop when the oxide was reduced in hydrogen. X-ray and neutron diffraction&apos; experiments showed the presence of cobaltous oxide (COO) and hexagonal cobalt in samples exhibiting the biased hysteresis loop and specifically showed no indication of any other compound with the exception of mercuric oxide.* The magnetic hysteresis loop becomes symmetrical above the Nee1 temperature (paramagnetic state) of COO. Therefore, it was concluded that the anomalous magnetic behavior is associated with the influence of cobaltous oxide upon the metallic cobalt. It has been proposed that crystallographic coherency may exist between the cobalt and a plane of some antiferromagnetic material which has unbalanced spin distribution and sufficient magnetic anisotropy to hold its spin in the direction which existed when the specimen was cooled. COO has these properties. Therefore, Roth&apos; has suggested that cobaltous oxide may form with a {111} plane parallel and coherent with the basal plane of the hexagonal cobalt metal and proposed that, as consequence of the antiferromagnetic interaction between COO and the underlying cobalt, the magnetization direction in oxidized fine Co particles may be ro-lated from the easy c-direction.2 Such a relationship, he proposed, would explain the observed magnetic effect in oxidized cobalt powder. The main purpose of this study was to determine the orientation relationship, if any, between the basal plane of cobalt and the oxide which forms upon it. Attempts to produce a film of COO which was strong enough to be handled were not successful. However we did succeed in making a film of CoCo2O, which was strong enough to be removed from the cobalt substrate and mounted on an electron-microscope grid. Because of the close structural similarity of COO and CoCo2O, we believe the orientation relation found for CoCo2O, on cobalt probably also holds for COO on cobalt. The epitaxial relationship of NiO and Ni also was investigated. To date no shifted hysteresis loop has been observed with nickel powder. However, the similarity of atomic array in cobalt and nickel leads to the prediction that a {111} of NiO may be parallel with a (111} of nickel. Experimental Method Cobalt-Cobalt Oxide—A coarse-grained specimen of a (hexagonal) cobalt was prepared by allowing a large crystal of fee cobalt to transform slowly at 400°C. The crystal was then cut to expose a surface parallel with the basal plane. A back reflection Laue X-ray photograph showed that the 00.1 plane was within 2" of the cut surface. The surface was mechanically polished and then electro polished in 85 pet orthophosphoric acid after which the crystal was held for 30 min at 400°C in air. During this heat-treatment the surface darkened slightly due to the oxide film which formed. The film was not thick enough to give an X-ray diffraction pattern, even by a glancing-angle technique. Glancing-angle electron diffraction was not possible either, owing to the interference of the electron beam with the high magnetic fields which exist at the 00.1 surface of the cobalt. However, it was possible to make an electron-diffraction photograph of the oxide film by stripping it from the cobalt substrate using the method described later. By maintaining reference marks carefully, it was possible to preserve the orientation relationship between the stripped film and the substrate on which it was formed. The oxidized surface of the crystal was first covered with a 1 pet solution of collodion (cellulose nitrate) in amyl acetate. When the film was dry, small rectangles were scored on the surface with a needle point. The specimen was then repolished

Jan 1, 1959

By D. W. Lillie

It has been demonstrated that considerable bend ductility exists in bulk specimens of polycrystalline high-purity silicon. The possibility of hot-forming at 1200°C is suggested. EXCELLENT corrosion resistance in many media and low cross section for absorption of thermal neutrons (0.13 barn) would make silicon of interest to nuclear engineers were it not for extreme brittle-ness and the difficulty of fabrication by any reasonable means. The use of silicon for structural purposes also has been considered in view of its light weight and oxidation resistance. Johnson and Han-sen&apos; have investigated the properties of silicon-base alloys and concluded that there was no way of making pure silicon or silicon-rich alloys ductile at room temperature. In view of reports of appreciable ductility in germanium single crystals above 550°C&apos;." and some plastic deformation in single-crystal silicon above 900oC,&apos; the present investigation was undertaken to define more precisely the limits of high-temperature ductility in pure silicon. After this investigation was begun torsion ductility in both germanium and silicon was reported by Greiner." Through the courtesy of F. H. Horn, a small bar of cast extra high-purity silicon was obtained and small bend specimens were made from it by careful machining and grinding. All of the reported tests results were obtained from samples from this bar (bar No. 1) and one other of similar source (bar No. 2). No complete analysis was obtained but, based on analysis of similar semi-conductor grade material, metallic impurities were under 0.01 pct total. Vacuum-fusion analysis for oxygen showed a value of 0.0018 2 0.0003 pct for the first bar tested and metallographic analysis showed no evidence of a second phase. Bend tests were carried out on an Instron tensile machine using a bend fixture with a 1 -in. span loaded at the center. Supporting and loading bars were 0.250 in. round and the load was applied by downward motion of the pulling crosshead of the machine. Specimen thickness and width were approximately 0.10 in. and % in. respectively. Loading rate was controlled by holding crosshead motion constant at 0.02 ipm. In some cases a smaller specimen was used on a 5/8-in. span with a 0.129-in.-diam loading bar. The entire bend fixture was surrounded by a hinged furnace and all heating was done in air atmosphere. Temperature measurement was made with thermocouples fastened directly to the bend fixture within less than 1 in. from the specimen. Autographic stress-strain curves were recorded during each test, and breaking load, total deflection, and plastic strain could be obtained from these curves. Stress was calculated from the beam formula S = 3PL/2bh2, where P is the load in pounds, L the span in inches, b the specimen width in inches, and h the specimen thickness in inches. This formula is strictly correct only in the elastic range but has been used to calculate a nominal stress for convenience in the plastic range. The stress given is the maximum stress in the specimen. Results The results of the complete series of tests are shown in Table I. The first group of tests (specimens Nos. 1-6) showed the beginning of plastic flow at a test temperature of 900°C, so two additional tests (Nos. 8 and 9) were made at 950°C on small-size specimens from bar No. 2. Specimen No. 8 was tested in the as-machined condition, and No. 9 was heat-treated in hydrogen at 1300°C for 2 hr, cooled to 1200°C and held 1 hr, cooled to 1000°C and held 1 hr, cooled to 900°C and held 1 hr, and finally cooled to a low temperature before removal from the hydrogen. It is apparent that the heat-treatment had a significant effect on yield strength and ductility. In addition, the magnitude of the yield point was conslderably reduced in the heat-treated specimen as is shown m Fig. 1 by tracings of the stress-strain curves. After obtaining a furnace capable of reaching higher temperatures specimens Nos. 10 to 13 were tested at 1100 and 1200°C. Strain rate was increased by up to a factor of 10 to see whether the ductility observed was excessively strain sensitive. Specimen NO. 10, strained at 0.02 ipm and 1100oC, was still bending at a deflection of 0.322 in. when the load rate was increased to 0.2 ipm, resulting in immediate

Jan 1, 1959

By C. S. Barrett, D. B. Masson

Martensitic transformations have been found in AgCd both upon cold-working at room temperature and cooling to lower temperatures. The crystal structures of the transformation products were found to be close-packed hexagonal in the first case and or-thorhombic in the latter. The transformation characteristics also were studied. Similar treatment of AuZn alloys failed to yield any transformation. THE literature on martensitic transformations of body-centered cubic metals and alloys indicates widespread instability of this structure at low temperatures, a tendency which merits further study. The body-centered cubic ß-phase of CuZn, for example, when it contained less than 42 wt pct Zn, was found by Greninger and Mooradian&apos; and others&apos; to transform on cooling to subzero temperatures to a phase that was tentatively considered to be tetragonal. Further work by Massalski and Barrett" demonstrated that cold work at low temperatures causes a partial transformation of ß CuZn of higher Zn content. The structures of the strain-induced transformation products were found to be different from those induced by simple cooling. Another well-known martensitic transformation among body-centered cubic phases is that of ß AuCd, first studied with X-rays by Olander,&apos; then very thoroughly by Chang and Read.5,6 Here again transformation was found to occur both as a result of cooling and of strain. The alkali metals Li and Na, as well as certain Li-Mg alloys, also undergo transformation from their normal body-centered cubic structure, both on cooling and on cold-working. The phase AgCd, the subject of the present report, should be expected to behave quite similarly to CuZn for a number of reasons. It is the chemical analogue of CuZn, silver being directly below copper and cadmium directly below zinc in the periodic table. The size factors (percent difference in size) of the atoms, possibly a consideration in the stability of the ß-phases, are +3.1 in AgCd and + 4.2 in CuZn. Likewise the relative electronegativities of the two pairs of metals are about the same, CuZn possessing an electronegativity difference of 1.0 and AgCd one of 0.8. These values are from a table of electronegativities given by Darken and Gurry." The phase diagrams of the two systems around 50 atomic percent are similar, both possessing a disordered body-centered cubic phase, ß, at high temperatures and an ordered bcc phase, ß, at room temperature; however, the ß and ß&apos; phases of AgCd are separated by a hexagonal phase, [, stable in the range 220-440oC, which has no analogue in CuZn. There has been confusion in the literature as to the structures of the ß&apos; and [-phases. The phase diagram in the ASM handbook&apos;" has the structures of the two phases interchanged; however, Hansen" reports the correct relative positions and Muldawer" verified that ß&apos;, the low-temperature phase, is body-centered cubic. Work by the present authors also

Jan 1, 1959

By W. M. Parris, P. D. Frost, H. A. Robinson

The effects of hydrogen content and strain rate on the static tensile and notch-rupture properties of the Ti-3Mn-complex alloy heat-treated to differed strength levels were investigated. The extent of embriulement was found to be proportional to the amount of hydrogen present and the strength to which the specimens were heat-treated. The research suggests the possible necessity of specifying lower hydrogen limits than are now allowed when titanium alloys are heat-treated to higher strengths than are presently used. The research also supports a hypothesis advanced earlier for a mechanism of hydrogen embrittlement. MUCH attention has been focused on the effects of hydrogen in in Most of the published in- formation has dealt with the effects of hydrogen on alloys in the annealed or lowest-strength condition. The work of Kotfila and Erbin3 is one of the few exceptions. In view of the fact that heat-treatments are now being used to produce high strength in titanium alloys,&apos; it is necessary that more attention be given to the effects of hydrogen on these alloys in the heat-treated condition. Research was initiated to establish the effects of hydrogen on the properties of the Ti-3Mn-complex alloy at various strength levels. This research, which supplemented that of Kotfila and Erbin, was started because it was found that high-strength tensile specimens of this alloy were strain-rate sensitive. The essential results of the research are summarized in this paper. MATERIALS AND EXPERIMENTAL PROCEDURES Material for this investigation was a 41/2-in.-diam bar forged from a single commercial heat of the Ti-3Mn-complex alloy having the composition given in Table I. The as-received forging was reduced further by forging at 1750°F to 3/4-in. square bars. About one fourth of this material was vacuum annealed at 1400°F for 24 hr to obtain a base hydrogen content of 25 ppm. The remaining bars were hydrogenated to levels of 90, 140, and 260 ppm in a large Sievert&apos;s apparatus in the following manner: Four 3/4-in. square bars, 5 in. long, were placed in the reaction chambzr. The chamber was evacuated, heated to 1400°F, and a measured amount of hydrogen was introduced. When absorbtion was complete, as indicated by the drop in pressure, the reaction tube was cooled and the bars removed. Each batch of bars was then sealed in individual evacuated Vycor containers and heated for 24 hr at 1400°F in order to distribute the hydrogen homogeneously. After vacuum-annealing or hydroge nation, the bars were rolled at a temperature (1400°F) below the ß-transus to 1/2 - in. - diam rounds. Groups of the rolled specimens representing each of the hydrogen levels were given the following heat-treatments: 1) One hr at 1300°F, water-quenched. 2) One hr at 1300°F, water-quenched, and aged 8 hr at 1100°F. 3) One hr at 1300°F, water-quenched, and aged 4 hr at 1000°F. 4) One hr at 1300°F, water-quenched, and aged 48hr at 800°F. Heat-treated bars were machined into standard 0.250-in.-diam tensile specimens having 1-in. gage lengths. Throughout the processing and testing of this material, hydrogen analyses were made by vacuum-fusion methods to check for accuracy of hydrogen additions, homogeneity, and possible losses during processing. A summary of these analyses is given in Table II It may be seen that the actual hydrogen contents were reasonably close to the desired levels. In addition, it was noted that the variation in hydrogen content within any one bar did not exceed

Jan 1, 1959

By W. S. Hyler, L. W. Berger, R. I. Jaffee

Hydrogen additions of 390 ppm to A-55 titanium and 368 ppm to Ti-8 pet Mn have no deleterious Hydrogenadditionseffect on the unnotched and notched rotating-beam fatigue properties of these materials. &apos;These amounts of hydrogen, however, are sufficient to cause severe notch-impact thesematerials.embrittlement in A-55 titanium and pronounced loss of tensile ductility in Ti-8 pet Mn. The lack of embrittling effect in fatigue in the latter alloy is consistent with the postulated strain-aging mechanism of hydrogen embrittlement in a-ß alloys. There is a significant strain-agingincrease in the unnotched endurance limit of A-55 titanium with the addition of hydrogen. This increase may be explained as the result of internal heating effects which would dissolve the hydride and cause solid-solution strengthening. TITANIUM and its alloys may be seriously embrittled by relatively small amounts of hydrogen. The form which this embrittlement takes has been shown to vary with alloy type. The a alloys, for example, suffer most strongly from loss of notch-bend impact toughness&apos; when sufficient hydrogen is added, and this effect has generally been associated with the presence of hydride phase in the micro-structure. In a-ß alloys, on the other hand, hydrogen is most detrimental to tensile ductility in slow-speed tests,2-1 and the embrittlement may be detected in a most convincing manner by means of rupture tests at room temperature. This particular kind of embrittlement has not been associated with a change in microstructure, but has been classified rather generally as associated with a strain-aging type of mechanism.&apos; In the present paper, the effect of an embrittling amount of hydrogen on the rotating-beam fatigue properties of both an a and an a-ß titanium alloy is covered. For this study, annealed commercially pure (A-55) titanium was chosen as an a alloy, and equilibrated and stabilized Ti-8 pet Mn as representative of a typical a-ß alloy. Nominal hydrogen levels of 20 and 400 ppm were evaluated, the latter amount having been shown previously to be severely detrimental to the impact toughness of commercially pure titanium and to cause pronounced strain-aging embrittlement in the Ti-8 pet Mn alloy. The only report of the effect of hydrogen on the fatigue properties of titanium is given by Anderson et al.,° in which a push-pull type of fatigue test was conducted on as-received commercial-purity titanium sheet. Much scatter was found in the results, but generally the presence of hydrides slightly decreased the fatigue strength of unnotched specimens in the longitudinal direction. The results of notched tests were masked too greatly by scatter to be significant. Experimental Procedure Preparation of Materials—Analyses of the A-55 titanium and the Ti-8 pet Mn alloy used in this investigation are given in Table I, which indicates the 8 pet Mn alloy to be more nearly a 6 pet Mn alloy. This alloy will be referred to as Ti-8 pet Mn, however, since this is the commercially designated composition. Both alloys were received in the form of5/8-in. diam rod and, after suitable surface preparation, 5-in. lengths were vacuum annealed at 820°C. Half of the rods for each material were then hydrogenated at 820°C to a nominal hydrogen content of 400 ppm. The hydrogenated and vacuum-annealed A-55 rods were hot swaged at 700°C from 5/8-in. diam to 1/4-in. diam, and then annealed 1 hr at 800°C and air cooled prior to preparation into test specimens. Fabrication of the Ti-8 pet Mn alloy was by hot swaging to 3/8-in. diam at 760" and then 1/4-in. diam at 704°C. This material was then annealed 1 hr at 704", followed by furnace cooling to 593"C, and finally air cooling to room temperature. Evaluation—In order to examine more completely the effects of hydrogen on the particular materials studied, slow-speed tensile and notch-bend impact properties were determined in addition to fatigue data. Tensile specimens were of the standard ASTM type with a reduced section of 1/8-in. diam and a gage length of 1/2 in. A subsize cylindrical Izod specimen was used for impact tests. These specimens had a 45" notch with a 0.005-in. radius and a 0.150-in. root diam, and the stress concentration factor of this notch in bending was Kr = 3. Both the ten-

Jan 1, 1959

By L. C. Weiner

THIS study was undertaken to round out an investigation on the effects of solid environments on the brittle fracture of zinc single crystals.&apos; In the previous work it was demonstrated that the presence of a surface film increased the cleavage strength of crystals whose basal planes were oriented almost parallel to the tensile axis by some 43 pct. This increase was observed to be independent of the type of surface-coating material, as well as of thickness of film above a certain small critical value (about 200 to 300A). These observations were described sat- isfactorily by a dislocation-pile-up-at-a-barrier model of brittle fracture2 in which twins modifying the dislocation path act as barriers, their increase in number and homogeneity of distribution brought about by the presence of the surface film. From previous work reported on the strength of ductile metal crystals as affected by gaseous and liquid environments,3 it may be concluded that the effects of these media are present only when the environment produces a surface film on the initially clean-surfaced crystal, or when it has a disintegrating effect on a previously existing surface layer. Similarly, it might be expected that an increase in cleavage strength of initially clean zinc crystals (xo = 3", A, - 28") will result only when the gas or liquid reacts with the crystal to produce a solid, adherent surface film. Clean-surfaced crystals,l 2 1/12 in. in length, were tested in tension at room temperature in an Instron

Jan 1, 1959

By H. I. Aaronson

The nucleation of pearlite at proeutectoid ferrite is inhibited, to an increasing extent, at the following locations: At twin boundary-nucleated ferrite, between closely spaced ferrite sideplates, and at intragranular plates. These effects are discussed in terms of the influence of transformation strain energies and of the interfacial free energy of austen-ite:ferrite boundaries on the rate of pearlite nucleation. The growth of pearlite into the interiors of austenite grains from the region of the grain boundaries is markedly restricted when low reaction temperatures and large austenite grain sizes permit the development of interlocking networks of intragranular ferrite plates. PREVIOUS investigators have made extensive studies of the interactions which occur between the proeutectoid ferrite and the pearlite reactions from the viewpoint of the mechanisms through which pearlite interferes with the nucleation and growth of proeutectoid ferrite.1-3 In the present investigation, the processes through which proeutectoid ferrite (hereafter termed simply "ferrite") can reduce the rate of formation of pearlite have been explored in some detail. A steel with a relatively low carbon content, in which the ferrite reaction can compete successfully with the pearlite reaction over a wide range of reaction temperature, and exceptionally coarse-grained specimens, which further emphasize the role of the ferrite reaction, have been employed for most of this work. A brief examination also has been made, however, of the effects of smaller austenite grain sizes upon these processes. Experimental Procedure The steel employed had the following composition: 0.29 pet C, 0.76 pet Mn, 0.25 pet si, 0,007 pet S, and 0.005 pct P. This alloy was homogenized for 48 hr at 1250°C. The investigation was performed

Jan 1, 1959

By A. Keil

TO measure the absolute conductivity of metallic specimens it is generally necessary to have exact geometrical shapes and good electrical contact with the test-piece. To overcome limitations of the standard methods, an electronic conductivity-meter* Trade name, Sigmatest; model Dr. F. Forster; Reutlingen, Ger-many. has been developed, which works on the principle of inducing high frequency eddy-currents in the specimens and measuring the reaction of these curients on a measuring coil.&apos;,&apos; To attach the instrument to the test specimen, a flat area of about 10 mm diam is all that is necessary. The reading is taken off a scale calibrated in pet of International Annealed Copper Standard. The induced eddy-currents are propagated in a circular motion parallel to the surface. Thickness of the layer included in a measurement depends on the frequency used. With a frequency of 60 kc per sec, the penetration of the currents was 0.8 mm at the upper limit of the scale, and 2 mm at the lower limit. The method is limited to nonferrous metals and other applications have been described elsewhere." The object of the present investigation was to detect the formation and growth of surface layers of differing conductivity, and to determine the depth to which these changes could be observed. A well known phenomenon which illustrates the problem is the internal oxidation of certain silver alloys containing base metal solutes, such as copper or cadmium, when they are annealed in an oxidizing atmosphere.4, 5 Until now, the only methods available for following these phenomenon have been metallo-graphic examination and hardness tests.0, 7 Changes in mechanical properties of copper alloys by internal oxidation were recently discussed in a more general way by Martin and Smith." When measuring these conductivity changes it must be remembered that the only absolute values of conductivity are those of 1) the nontreated homogeneous specimen, and 2) the final values obtained with a surface layer of depth comparable to the penetration of the eddy-currents. All intermediate values refer to the mixed conductivities of the transformed surface layer and the untransformed alloy, and are thus readings of relative value only. Experimental Results Specimens were annealed for 1/2 hr at 800°C in hydrogen, and the internal oxidation was carried out by thermal treatment in air at 800°C. Fig. 1 shows the results of the first series of experiments. With internal oxidation of a solid solution of 8 pet Cd in silver, the conductivity rises continuously until the surface layer formed has become thick enough to be the deciding factor (about 400µ). Precipitates of CdO are mainly in the form of points, Fig. 2, and, as a result, the electric contact between the silver crystals is not distorted by them. Brine11 tests were run with a 1.25 mm ball and a 7.812 kg load. The specimen annealed in hydrogen and oxidized to a depth of 400µ had a hardness of 40 Bhn,

Jan 1, 1959