Search Documents

By A. W. Henderson

This investigation was performed to develop chlorination methods for extracting tungsten from scheelite and from an ore concentrate containing a mixture of scheelite and wolframite. On a laboratory scale with proper temperature control using elemental chlorine, over 90 percent extraction of tungsten is achieved. Carbon and sulfur dioxide were studied as reducing agents. The effects of salts such as calcium fluoride and sodium chloride were studied as additives to increase extraction and to reduce impurities in the volatile tungsten chloride product. Sodium chloride reacts with ferric chloride to form a nonvolatile double salt; whereas the chlorides and oxychlorides of tungsten are volatile and consequently condense free of iron. Separation of tungsten from molybdenum from an equal molar mixture was successful by fractionally distilling the oxygen-free chlorides and by selectively condensing the oxychlorides. Yields of 60 and 80 percent, respectively, were achieved for separating the less volatile tungsten chlorides containing less than 0.5 percent molybdenum.

Jan 1, 1965

By D. Harrington

A uniform hoisting-signal code for mines hoisting from more than one level, if adopted by all mining States, would be beneficial to employees and owners alike and should largely reduce the number of hoisting accidents. Misunderstood hoisting signals cause many shaft accidents involving injuries to men, damage to equipment, and loss of production from the resultant delay. Many of the metal-mining States have adopted codes for hoisting that are effective within the borders of that State but usually entirely different from the signal code, if any, in use in an adjoining State. For many years safety engineers have recognized this lack of uniformity as a distinct hazard, but a uniform code has never been adopted by the States or by the mining industry in those States that have not incorporated signal codes in their mining laws or mining regulations.

Jan 1, 1944

By Rafael Amboss Pinto

O objetivo do SHTPN (Solution Heat Treatment after Plasma Nitriding) é a adição de nitrogênio em solução sólida na superfície, formando austenita durante o tratamento térmico de solubilização, possibilitando a obtenção de martensita de nitrogênio após o resfriamento. Foram ensaiadas amostras nas condições: de fornecimento (microestrutura ferrítica); nitretada (com camada de compostos); após SHTPN (martensita não revenida); e SHTPN seguido de quatro temperaturas de revenimento (martensita revenida). Os ensaios tribológicos foram realizados em placa contra esfera de metal duro, movimento recíproco. Os mecanismos de desgaste foram caracterizados por microscopia eletrônica de varredura (MEV) e as profundidades das pistas foram medidas em rugosímetro 3D. A condição de maior resistência ao desgaste foi a nitretada. Entretanto, a superfície desgastada destas amostras apresentou microtrincas. O comportamento tribológico da amostra revenida a 600°C foi similar ao observado para amostra no estado de fornecimento, pois apresentaram predominância do mecanismo de adesão, com grandes deformações plásticas na superfície. Todas as outras condições apresentaram menores profundidades de desgaste do que o estado de fornecimento, com mecanismos predominantes transitando de abrasão para adesão com o aumento da temperatura de revenimento. Na amostra após SHTPN, a baixa capacidade de deformação plástica da camada martensítica não revenida causou fratura do material nas laterais da pista, o que não ocorreu para as condições revenidas.

Aug 8, 2018

By A. Saigal

A finite element analysis based investigation using DEFORM software was undertaken to model the extrusion of 15% alumina and 15% silicon carbide reinforced aluminum metal matrix composites. The study dealt with predicting the extrusion load as a function of ram displacement and initial billet temperature. The finite element simulation was also used to determine the maximum extrusion load, temperature distribution, maximum temperature, strain rate, velocity and stress distributions in the billet during the hot extrusion process. The constitutive equation used was of the type: Z = E exp(Q RT) = A{sinh(ao-)}" where Z is the Zener-Hollman parameter (temperature compensated strain rate), s is the strain rate, Q is the activation energy, R is the gas constant, T is the absolute temperature, a is the flow stress and A, a and n are constants. Based on the work of Davies et al and McQueen and Konopleva, the values of Q (KJ/mol), a (MPa-1), n and A for aluminum 6061 composites reinforced with 15% alumina and 15% silicon carbide used are 181, 0.024, 4.15 and 1.33x10'2 and 233, 0.052, 2.60 and 1.26xl0'4, respectively. Even though the individual parameters are quite different, it was found that the predicted maximum extrusion load, temperature distribution, maximum temperature, strain rate, velocity and stress distributions are quite similar and differ by no more than 1-2 percent between the two composites indicating that the deformation behavior is primarily controlled by the matrix material and is not a function of the type of reinforcing ceramic particulates.

Jan 1, 2004

By R. P. King

A new device, called the dual impact load cell, has been developed and built at the Comminution Center to measure fracture energy and damage accumulation in brittle particles that are subject to impact. The results show that damage accumulation during impact is not a significant factor in determining the fracture energy or the particle strength. However, predamage induced by thermal pretreatment of the particles has a significant effect on both fracture energy and particle strength.

Jan 1, 1995

By Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Liang Yin, Xiaohui Fan

Straw char exhibited considerably faster burning speed than coke breeze for its porosity, which significantly degraded sinter quality when it replacing coke breeze as sintering fuel. In this investigation, preforming technology has been employed to densify raw straw. The properties of straw char preformed show that its density was increased, and the structure was also densified, which made the difference of combustibility between the straw char and coke breeze smaller. The proper preforming temperature, residence time and pressure were 200℃, 1min and 120MPa respectively. Sinter pot trials show that the product carbonized from preformed straw made the proper replacement ratio to coke breeze increase from 20% to 40%, and the emission reduction of SOx, NOx in flue gas increase from 11.50%, 14.15% to 37.85%, 23.60% respectively, compared with non-preformed straw char.

Jan 1, 2015

Radioisotope x-ray and neutron techniques of analysis can be used for the determination of a wide range of elements in minerals. The most important applications of these techniques to the mineral industry are for onstream analysis of slurries and solids, and for geological assay.The radioisotope x-ray techniques are the more developed ones and two installations for on-stream analysis are in routine use in mineral processing plants in Australia. Neutron techniques are being developed, and should prove valuable for geological assay of large numbers of mineral samples, for borehole logging, and for specific on-stream analysis when the cost of the equipment is warranted.

Jan 1, 1970

By Mehmet Guney

At the Armatcuk mine in Turkey, various modifications of sublevel methods have been tried during the last decade in an effort to eliminate gob fires, dangers from roof falls, and surface subsidence, and also to increase extraction efficiency. From the experience thus gained, it was decided that the most likely system to give maximum benefits, considering the existing geological conditions and coa1-seam characteristics, was hydraulic stowing. This paper examines trends in the working techniques of hydraulic stowing and discusses the favorable results and technical problems that the method produced at Armutcuk. The Armutcuk mine, a subsidiary of Eregli Coal Mines (EKI), produces 1300 tons of run-of-mine coal daily from thick (about 10-90 ft) and highly dipping (about 50-90°) coal seams. The coal is highly volatile with good coking properties that make it highly suitable for industrial use. Most of this coal is used in the iron and steel industry at Eregli on the Black Sea coast. Complete recovery of the coal is of vital importance to industrial development and progress. Initial coal extraction was carried out by means of a sublevel mining system modified to accommodate local geological conditions and coal seam characteristics. This method is similar to that employed in metalliferous mines. Several problems arose from the application of the method, one of them being the prevalence of gob fires which caused periodic shutdowns in some sections. To achieve maximum coal extraction with minimum dilution, to eliminate gob fires and surface subsidence, and to reduce fatal accident rates, a decision was taken to change from this method to a hydraulic stowing system. The pres- ence of large deposits of conglomerate and sandstone on the surface contributed to the decision to employ this new method. Although hydraulic stowing practices have been carried out in America and Germany, Upper Silesia may, so far as coal is concerned, be considered the birthplace of the method. Here the process was adapted to thick coal seams on a large scale to reduce dangers from gob fires and damage from surface subsidence. Today, the mining system is not only widely used in the coal mines of France, the Saar, India and Poland, but has also been successfully applied to the iron ore and potassium salt mines in Russia and Germany. LOCATION AND HISTORY The Kandilli-Armutcuk coal field, the most western outcrop of the North Anatolian coal basin, extends for five miles along the Black Sea coast (Fig. 1). The Armutcuk Mine is situated on the southern boundary of the coal field about 40 miles from Zonguldak and about 12 miles from Eregli. The history of coal mining in the North Anatolian coal basin goes back more than a century. Mining commenced on a small scale in the Kandilli-Armutcuk coal field in the late 1880's, and from this time until nationalization in 1940 the mines were operated by private Turkish and foreign interests. In 1940, Eregli Coal Mines was established to takeover the management of these enterprises. The Armutcuk Mine was developed for the first time in the mid-1940's. Since then it has been in continuous production and it now produces an annual 440,000-ton run-of-mine output from which 320.000 tons of salable coal is obtained. MINE GEOLOGY The carboniferous inlier of the Kandilli-Armutcuk coal field crops out over an area about three miles long and one mile wide. The major part of the inlier consists of the Namurian formation with only a relatively small area of Westfalian-A visible on the surface (Fig. 2). The Namurian formation, which has no exploitable coal seams in the Armutcuk Mine, consists mostly of arkose sandstones and black shales often having

Jan 1, 1969

By Richard Havens

Acidic and basic uranium leach plant residues located on the Navajo Indian Reservation, Tuba City, Ariz., were successfully stabilized against wind erosion using a relatively low-cost chemical method. An elastomeric polymer chemical was applied to the dike areas and a calcium magnesium lignosulfonate to the beach areas of three tailings ponds. The water-soluble chemicals were applied with an automated sprinkling system. The stabilization cost was $335 per acre for the 34.5-acre tract.

Jan 1, 1969

By T. R. Stanley

Introduction The purpose of this paper is to interest mining men in the economic possibilities of sand deposits suitable for modern foundry work. Many members of the profession are constantly travelling over the country and it is felt that some knowledge of the necessary properties of foundry sands will enable these men t0 recognize such deposits. It is the experience of the writer that good sands suitable for the varied work of a foundry, such as that of the Consolidated Mining and Smelting Company, at Trail, are almost impossible to obtain from western Canadian sources. It is hoped that the following discussion may arouse some interest in the search for such sands. Sands are used in foundries for two purposes. The main use is for making moulds suitable for receiving hot metal. The mould must retain the? required shape until the metal has solidified. The second use of sand in the foundry is as an abrasive in sand blasting. This is a relatively minor use, and consequently will not be dealt with in detail. Any coarse sand with a high content of quartz will serve this purpose, but round-grained sands are superior to angular types, because they have not the same tendency to shatter on impact with the casting. Sand plays an extremely important part in the successful production of sound castings. This is more evident today than ever before, due to the greater variety of castings and alloys, each of which requires special sand characteristics. Poor sand is responsible for a great many foundry troubles which formerly were attributed to bad? metal; in fact, one investigator goes so far as to say that ninety per cent of bad castings can be traced directly to the sand. Very little of the vast amount of sand distributed over the earth's surface is suitable for moulding. It is the purpose of this paper to describe briefly the properties which are essential in good moulding sand. Sand for this work must be able to withstand the wash and hydrostatic pressure of molten metal, and yet be sufficiently porous to allow the gases generated in the mould to escape.

Jan 1, 1935

By Junli Xu, Xianwei Hu, Kaiyu Xie, Liangxing Li, Zhongning Shi, Zhaowen Wang, Bingliang Gao, Aimin Liu

Al-Ti master alloys were prepared by aluminothermic reduction between the dissolved titanium dioxide and aluminum in cryolite melts at 960oC. The kinetic analysis by differential scanning calorimetry indicated that the apparent activation energy of the reaction of reducing titanium dioxide by aluminium is 22.3 kJ/mol, and the reaction order is 0.5. The products were analyzed by means of X-ray diffraction, X-ray fluorescence, scanning electron microscopy and energy dispersive spectrometer. Results from X-ray diffraction showed that the phase compositions of produced alloys are Al and Al3Ti. In addition, Al-Ti master alloys containing 2-6 mass% Ti were formed at different reduction time of 2-5h in aluminothermic reduction experiment.

Jan 1, 2015

By Rafael Duclou Rito

Com temperaturas altíssimas atingidas, os fornos são equipamentos responsáveis pelo aquecimento de materiais na produção de tubos sem costura. Assim, o investimento requerido de um forno em bom funcionamento é quase todo em combustível. Este trabalho foi desenvolvido objetivando a qualidade dos produtos e a otimização dos períodos em que o forno não produz. Durante os períodos citados, o forno é desligado ou mantido a uma temperatura menor que a de operação. Estudando a transferência de calor, principalmente no refratário, é possível analisar a melhor prática em situações improdutivas. Portanto, foi desenvolvido um simulador da temperatura dos refratários ao longo do tempo do forno em questão, sendo possível espelhar parâmetros reais para encontrar o controle de temperatura ótimo do forno, em que a temperatura da atmosfera interna é a principal entrada no programa. Termopares foram instalados ao longo das paredes refratárias para que o modelo fosse validado e aprimorado. Paralelamente, pontuou-se a relação dos materiais enfornados com as medições dos termopares, a fim de encontrar uma temperatura ideal de enfornamento. Os resultados foram positivos e permitem o uso de artifícios de refinamento dos resultados.

Oct 30, 2017

By Camila Soares Fonseca

Os aços inoxidáveis duplex possuem uma microestrutura austeno-ferrítica com fração média de cada fase de cerca 50%. A microestrutura duplex é responsável por melhorar as propriedades mecânicas do material. A soldagem destes aços é frequentemente uma operação crítica. O objetivo desse trabalho é analisar a influência do aporte térmico sobre a microestrutura de juntas soldadas do aço duplex SAF2205. As chapas de aço duplex 2205 foram soldadas pelo processo de soldagem GMAW (Gas Metal Arc Welding), variando apenas o aporte térmico. Após essa etapa, as chapas foram cortadas, preparadas para a análise metalográfica, difração de raio X (DRX) e ensaio de microdureza Vickers. As microestruturas do metal base (MB), da zona termicamente afetada (ZTA) e da zona fundida (ZF) foram caracterizadas nesse estudo. Foi verificado que quanto maior o aporte térmico menor a quantidade de ferrita e maior o crescimento de grão da austenita na região fundida. Os ensaios de microdureza mostraram que quanto maior o aporte térmico maior será a ZTA do material.

Aug 8, 2018

By Dina M. Aloi

In today?s evolving and globalized world, mining companies are being pressured to move beyond compliance towards long-term sustainability and sustainable development. Companies are expected to ?engage? communities without a clear understanding of ?how? to do this or to what end. This move, away from compliance, develops more of a focus on ?Community? Social Responsibility and sustainability. This shift leads to the development of world-class projects that provide sustainable development for people, reduce the incidence of costly delays, and promote good global citizenship for companies. The process of ?engaging? communities in mining project design and development leads to a stronger license to operate, and a reduction in social and political risk. To create this mutually beneficial relationship between communities and companies, communities must be ?engaged? in the project development and risk assessment processes as early as possible, preferably during the exploration or the concept phases. How to create this ?engagement? and manage this risk will be discussed.

May 1, 2007

By Colin Dessemond

Since 1950, the traditional process has been dominating the production of lithium compounds from spodumene ores to sustain the lithium market because of its economic viability and the markets need for technical grade (99.5% purity) product. This traditional process includes thermal conversion, acid roasting and lithium leaching. However, this process has not been challenged and very few studies have tried to explain its limitation (95% lithium yield) or optimize the thermal treatment. Here, α to β spodumene conversion and lithium extraction were performed in a rotary kiln on a 2 mm to 2 cm spodumene concentrate instead of a micrometric one using a 1050 °C, 30 min conversion treatment and 250 °C, 30 min, 30% H2SO4 excess leaching treatment. X-Ray Diffraction analyses were performed on the converted material to determine the conversion rate by Rietveld analysis. It was observed after thermal treatment that the α-spodumene particles fractured and divided while the impurities remained compact. A sifting was performed after thermal treatment and it was determined that 65% of the initial mass became finer than 180 μm. X-Ray diffraction analyses and lithium content measurement were performed on both fractions and it was determined that the finer fraction had a very high lithium content of 3.24 wt%. Lithium extractions were performed on both fractions separately. While the coarser fraction’s lithium yield was only 61% the finer fraction’s lithium yield went up to 99% without any additional treatment. These observations may open more economical ways for the traditional process by potentially bypassing two third of costly steps such as grinding.

By Dennis Molvik, Omar Fulton, Chris D. Breeds, Don Gonzales

This paper presents and describes the South Interceptor Parallel Phase III Contract C93012C, which involved construction of a nominal 2.7 m (9-ft) finished diameter sewer conveyance using both pipe jacking and conventional tunneling methods. Earth Pressure Balance (EPB) excavation was required to minimize the potential for settlement beneath a main rail line, overpass, sensitive wetland, areas of contaminated soils, and nearby structures. Ground conditions predicted in the Geotechnical Baseline Report included low plasticity, clayey silt (40 to 10%) and silty sand (60–90%) with pieces of wood such as logs, stumps, branches and other tree fragments. Soil cover ranged from 2.7 m (9-ft) to 5.4 m (18-ft) over the tunnel crown with a groundwater table between 1.5 m (5-ft) and 3.7 m (12-ft) deep.

Jan 1, 2003

By B. Dyck, C. Rodgers

ABSTRACT Cameco Corporation is revitalizing its Key Lake Operation uranium mill in northern Saskatchewan. The mill currently uses ammonia stripping in solvent extraction (SX) and ammonia yellowcake precipitation. As part of the revitalization, the company considered installing strong acid stripping in solvent extraction (used at its Rabbit Lake Operation), which would lead to using hydrogen peroxide for uranium precipitation. As part of the process evaluation, tests were carried out to study how the drying temperature in indirect fired dryers would affect the uranium peroxide yellowcake precipitate properties. This paper discusses the test work results, including the relationships between drying temperature and product reactivity with water, product colour, product grade, and energy input requirements.

Jan 1, 2012

This paper focuses on the dissolution of various Manganese based compact additions into liquid Magnesium. The experimental procedure employed cylindrical compacts with various Manganese compositions. The various temperatures of the additions and the Magnesium bath were measured simultaneously during the immersion of the additions into Magnesium bath. The exothermicity level of these additions during their dissolution into liquid Magnesium was determined. The relation of the exothermicity level with the dissolution kinetics was also examined. In addition, SEM and EDX work was conducted for additions, which were withdrawn from the Magnesium bath. Finally, the recovery of these additions was estimated by taking samples from the Magnesium bath and conducting ICP analyses.

Jan 1, 2006

By Thales Renó Grilo

O presente trabalho teve como objetivo analisar as diferentes microestruturas do aço inoxidável duplex UNS S32304 obtidas pelo processo de soldagem Gas Metal Arc Welding (GMAW). As regiões do metal base, zona fundida e zona afetada pelo calor foram investigadas nos corpos de prova com diferentes aportes térmicos. As microestruturas obtidas foram caracterizadas utilizando-se a microscopia óptica (MO). As imagens de Mo obtidas na zona afetada pelo calor mostram que a fração de austenita aumentou com o aumento do aporte térmico. Este aumento está relacionado ao alto teor de cromo e molibdênio presentes no metal de adição utilizado na soldagem. Na zona fundida, a fração de austenita de widmansttaten foi observada com maior frequência na microestrutura do corpo de prova soldado com o aporte térmico de 1,87KJ/mm. Essa maior fração de austenita de widmansttaten observada para o aporte térmico de 1,87KJ/mm está relacionada com o maior tempo de permanência em altas temperaturas deste corpo de prova em relação aos outros corpos de prova investigados. Vale ressaltar que a adição de nitrogênio também promove a formação desta fase. De modo geral, os resultados da metalografia quantitativa mostram que a porcentagem de ferrita foi superior a 65% nas zonas termicamente afetadas e fundidas.

Aug 17, 2017

By João Lucas Lautenschlager Cortez Alves

Foi implementado um modelo matemático transiente e tridimensional para prever os campos de temperatura e composição presentes no sólido e poça de fusão durante um processo de soldagem a arco. O modelo foi desenvolvido com base nas equações de conservação macroscópicas de calor, massa e espécies químicas, que foram solucionadas pelo método dos volumes finitos. Os resultados do modelo mostraram boa aderência com soluções analíticas. Foram apresentados os efeitos de mudança na velocidade e potência de soldagem na distribuição de temperatura obtida e no formato da poça de fusão para soldagem em uma chapa de liga Al-6,5%Cu.

Oct 30, 2017