By Irving Cadoff, Kurt Komarek, Edward Miller

Barium can be purified by equilibration with titanium. The melting point of barium was found to be 726.2° i 0.5 °C. The room-temperature lattice parameters of BaTe and Bask are 7.004 * 0.002A and 6.600 * 0.002A. Melting points for BaTe and Base were found to be 1510° * 30°C and 1830° ± 50°C, respectively. HIGH-purity barium and its compounds are difficult to prepare because of the reactivity of barium with the atmosphere and the large heats of formation of the compounds. Purification of barium by vacuum distillation,' and the preparation and properties of barium oxide2 and barium sulfide3 have been reported. However, little has been done on the homologous compounds barium selenide and telluride. PURIFICATION OF BARIUM Distilled barium obtained from King Laboratories was used as the starting material. The analysis supplied with the metal showed the presence of: 0.4 wt pct Sr, 0.001 pct Mg, 0.02 pct F, 0.003 pct Cu, 0.005 pct Na and less than 5 x 10-3 wt pct of any other metallic impurity. Analyses for oxygen and nitrogen were not available. Since there is evidence4 that any barium nitride present in the starting material may decompose on distillation producing nitrogen which can contaminate the distillate, further purification was performed. At elevated temperatures, any nitrogen and oxygen present in barium should be removed by reaction with titanium. Assuming that the solubility of oxygen in liquid barium is negligible near the melting point of barium, any oxygen present will be in the form of BaO. Removal of oxygen from molten barium is expressed by the equation: BaO(S)+ TixOy(S) = Ba(l)+ TixO(y+1)(s) where Ti,Oy and TixO(y+1) are solid solutions of oxygen in titanium. At 1000°C, the change in free energy for this reaction is negative for (y+1)/x +y+1) x (100) 17.5 at. pct O.5 Since reaction with commercially pure titanium (containing 0.07 wt pct oxygen) results in a free energy change for the reaction of -19 kcal per g-atom, slight solubility of oxygen in barium would not hinder the oxygen removal. Since comparable thermodynamic data are not available to permit calculation of the partition of nitrogen between liquid barium and titanium, a similar quantitative relationship cannot be obtained. However, on the basis of work by Kubaschewski and Dench,5 complete removal of nitrogen from liquid barium can be expected. Since the melting point of barium is depressed markedly by small additions of nitrogen,' the change in melting point during reaction of barium with titanium was used to follow the purification reaction. MELTING POINT OF BARIUM A 50-g sample of barium was sealed by arc welding under argon into an all titanium crucible provided with a thermocouple well. The melting point of the sample was determined by thermal analysis, using a Pt/Pt-10 pct Rh thermocouple which was calibrated according to National Bureau of Standards specification6. The crucible was then heated for 48 hr at 950°C in vacuum and the melting point redetermined. This procedure was repeated until three successive thermal analyses agreed within ±0.5oC, the limits of error of the analysis. The melting point increased from an initial value of 720.0°C to a final value of 726.2°C. Analysis on samples quenched from 950°C gave a solubility value of 0.004 wt. pct Ti. Assuming that the titanium-barium phase diagram is similar to those of titanium-magnesium7 and titanium-calcium,8 the solubility of titanium in liquid barium decreases with decreasing temperature. Therefore, the solubility of titanium in liquid barium should be less than 0.004 wt. pctat the melting point (726oC), and the effect of dissolved titanium on the melting point would be negligible. Addition of up to 3 wt pct Sr does not significantly change the melting point of barium,7 so that the effect of the 0.4 wt pct Sr in the starting material will also be negligible. The value of 726.2" ± 0.5C obtained for the melting point of barium can be compared .with a determination carried out by Keller and coworkers in low-carbon steel crucibles,' who obtained a value of 725± 1C, using barium purified by fractional distillation. The higher value obtained in the present investigation is indicative of the effectiveness of titanium in removing traces of nitrogen. PREPARATION OF BaTe AND Base The compounds were prepared by direct reaction

Jan 1, 1961

By A. M. Kiwior

In 1969, the Congress of the United States declared that "the first priority and concern of all in the mining industry must be the health and safety of its most precious resource - the miner," Therefore, Public Law 91-173, Federal Coal Mine Health and Safety Act of 1969, was enacted. Since haulage accidents account for a high percentage of coal mining accidents, Section 314e, ?Hoisting and Mantrips,? was included in the law. This section states: "Each locomotive and haulage car used in an underground coal mine shall be equipped with automatic brakes, when space permits. Where space does not permit automatic brakes, locomotive and haulage cars shall be subject to speed reduction gear, or similar devices approved by the Secretary which are designed to stop the locomotive and haulage cars with the proper margin of safety."

Jan 1, 1975

By G. R. St. Pierre, M. J. Pool, R. Speiser

The activities of chromium in solid Cr-Ti solulions contaitning from 10 to 90 at, pct Cr were measured over the temperatutre range 1250" to 1380°C. The Knzudsen effusion technique with direct weighing of the Knudsen cell was used. This was possible because the vapor pressure 0f chromium is about 600 times greater than the capor pressure of titanium so that the amount 0f titanium effusing could be neg-Lected. the activities of titanium were determined by g-raphical integration of the Gibbs-Duhertz equatiotz. The solutio~ls sllcdied exhibited positive deviations from Raoult's law, but they approached ideality as the temperature was raised from 125 to 138t C. The integral free energy of mixing was calclated from the activity values. AF has a maximum value of - 1.66 kcal a1 1390°C and a composition oj 55 at. pcl Cv. The free energy of formation of 'TiCr, is —0.76' lzcal a1 1250°C. The heats and entropies of mixing usere determined using the second law and thus tile mlues could be in error by a considerable amount. The Cv-Ti system is not a regular solution. ThE increasing emphasis on application of various models to alloy formation and solution behavior has led to an intensified interest in the thermochemistry of alloys. In a majority of the cases where different models have been applied the alloy system used was a simple one. However, the amount of data available on more complicated systems is small and in order to fully understand the behavior of metallic solutions more experimental work has to be carried out on these systems. The Cr-Ti system is reasonably complex and even though this system was being investigated as early as 1937 by Kroll,' no previous work has been done on the thermodynamic properties of either the liquid or solid state. This research was undertaken to determine the thermodynamic properties of solid Cr-Ti alloys. EXPERIMENTAL PROCEDURE The experiments on the Cr-Ti system were carried out in a water-cooled metal vacuum system. This system is composed of a brass vaporization chamber wound with copper tubing for cooling purposes, a brass liquid-nitrogen trap, an oil diffusion pump, and a Duo-Seal forepump. The pressure in the system is measured with an ionization gage. The interior of the vaporization chamber is shown schematically in Fig. 1. The Knudsen cell is supported by the molybdenum tripod, and a magnetically operated shutter is provided to protect the Pyrex sighting glass against deposition of metallic vapors in the intervals between temperature measurements. Heating is accomplished by means of a 20-kw 450-kc Westinghouse oscillator. The susceptor in this case is 10-mil tantalum seamless tubing which also forms the outside of the sample container. The remainder of the sample container consists Of an im~ervims re-crystallized alumina crucible and a 10-mil-thick tantalum lid. Two holes are drilled in the lid. The diameters of these holes were measured with the calibrated stage of a "Tukon" microhardness tester. The thicknesses were measured with a micrometer. A Leeds and Northrup disappear ing-filament optical pyrometer was used to measure the temperature. This is sighted through the smaller of the two holes in the lid and corrections for the emissivity of the sample were not necessary since the ratio bf cell length to hole diameter was large enough to insure a hohlraum. The pyrometer was calibrated at the ~~t~~~l Bureau of Standards, and the correction for the Pyrex sighting window was determined in the laboratory. The titanium used in this investigation was obtained from Mallory-Sharon and the chromium from The Union Carbide Metals Co. The reported purities were

Jan 1, 1968

By R. J. Quigg, G. S. Doble

Commercial stress -relieved TD Nickel bar was shown to retain room- and elevated-temperature tensile strength after exposure up to 2501°F. Cold swaging increased both room -temperature and 2000°F tensile strength. After annealing at 2500°F the strengthening due to swaging was retained at 2000°F hilt eliminated at room temperature. Annealing produced changes in hardness and X-ray half peak width indicating the presence of recovery processes as 1071° as 1000°F but no recrystallization of swaged material was noted at any temperature. In contrast to swaging, rolling induced a recrystal-lized structure after annealing. The tensile strength of this recrystallized structure was comparable to the cold-worked condition. High-temperature tensile properties of as -received bar were highly anisotropic with the transverse tensile strength being one fifth the longitudinal value. The aniso-/ropy is affected by working direction and may he partially reversed by changing the direction of metal flow. The divergence in tensile strength, beginning above 550°F or- approximate one third the absolute melting point, is strain-rate dependent. T D Nickel is a commercial dispersion-hardened alloy containing 2 vol pct thoria. The dispersion, consisting of spherical particles 0.030 to 0.050 in diameter with an interparticle spacing of less than 1 is reported to maintain stable properties up to 2400°F.1 This stability of second phase results in maintenance of elevated-temperature strength at higher temperatures and longer times than normal nickel-base superalloys.2 The purpose of this paper is to describe the effect of various mechanical working operations on the strength and microstructural stability of TD Nickel bar. MATERIAL AND PROCEDURES All material used in this study was commercial TD Nickel bar. This material is produced by a chemical process which results in a nickel powder containing a dispersion of thoria particles. The powder is then pressed, sintered, extruded, and subsequently worked to bar stock. Three starting materials from three separate lots were used: as-extruded bar. 1-in.-diam stress-relieved bar, and 1/2-in.-diam stress-relieved bar. Since TD Nickel bar stock is cold-worked without a recrystalliza-tion anneal, the accumulated deformation or degree of cold work in these materials increases as the bar diameter decreases. Some of the 1/2-in.-diam bar was swaged to 1/4 in. diameter at room temperature in order to produce an as-worked condition for comparison with the stress-relieved stock. Tensile testing was performed on an Instron Tensile Tester at a constant crosshead speed of 0.020 in. per min. The 0.2 pct offset yield strength was measured from the load-crosshead movement plot. Specimen gage dimensions were 0.080 in. in diameter by 0.40 in. in length, producing a strain rate of approximately 0.050 min-1. Specimens were tested in air and heated within a resistance-wound furnace controlled to ±5°F. A 15-min soak at temperature was employed before testing. Samples were heat-treated in air and specimens machined after exposure with sufficient material removed to eliminate any surface contamination. X-ray line breadth was determined from a diffractometer scan of a transverse face of a bar using copper K, radiation. Metallographic preparation utilized standard mechanical polishing with Carapella's etch. Specimens for electron microscopy were electropolished in a 1:7 sulfuric/methaol solution and chromium-shadowed collodion replicas prepared. RESULTS AND DISCUSSION I) Effect of Elevated-Temperature Exposure on the properties of TD Nickel. The effect of various elevated-temperature exposures on the room-temperature tensile strength of TD Nickel is shown in Table I. In the unexposed condition the tensile strength, reduction in area, and hardness all increase with increasing accumulated deformation while the elongation decreases. After exposure at 2500°F the strength of all three materials decreases to about 65,000 psi and the elongations increase slightly. The apparent increase in strength of the 1-in. bar after a 2000°F treatment is probably experimental scatter. These results indicate that the room-temperature strengthening due to additional deformation is annealed out upon elevated-temperature exposure. In contrast to the room-temperature data, the 2000°F tensile strengths increase in order of increasing deformation even after exposure. Although some loss of strength occurs after exposure, much of the effect of working is still maintained at 2000°F. The room-temperature hardness after various

Jan 1, 1965

By M Lee, J F. Carswell, G Reitsema

"The increased costs of underground mining have continually challenged engineers to identify opportunities for alternatives to common approaches to underground development. Considerations to the design of horizontal and vertical development at the Dugald River mine targeted inclined raise boring to reduce horizontal development, not only to reduce cost, but to allow development activities to focus on other areas of the mine.The mine plan consists of 50 raise bored ventilation shafts, of which 17 have been mined to date with diameters ranging from 3.1 m to 5 m and lengths from 30 m to 200 m. The expected performance and stability of these shafts has been determined using methodologies proposed by McCracken and Stacey (1989) and further refined by Peck, Coombes and Lee (2011). Actual raise performances have been collated and compared to a database of raise bore performances across Australia as presented by Coombes, Lee and Peck (2011), and form a database of raise bore performance specific to Dugald River.Opportunities to further optimise the mine plan and reduce costs have seen the introduction of large diameter-inclined raise bored ventilation shafts to minimise the required lateral development to connect the ventilation circuits. Large diameter inclined shafts ranging between 3.1 m and 4.5 m in diameter have been successfully mined with dips down to 70°, reducing the cost of lateral development by more than $1 million over the next two years.Both technical and operational challenges were overcome in the mining of large diameter-inclined raise bores, including modification of: existing methodologies of assessing shaft wall stability for inclined raises. These included variations of the McCracken and Stacey method and the utilisation of the modified stability number (N’) previously developed for stope performance (Potvin, 1988). both the collar and toe development profiles, including the general set-up of the raise bore drill rig to reduce the operational risks associated with angled raises.Due to their success, inclined raises have been designed for subsequent stages of the life-of-mine ventilation system at Dugald River. This has resulted in significant capital cost savings for the mine.CITATION:Carswell, J F, Reitsema, G and Lee, M, 2017. Vertical and inclined raise bore performance at Dugald River mine, in Proceedings 13th AusIMM Underground Operators’ Conference 2017, pp 313–320 (The Australasian Institute of Mining and Metallurgy: Melbourne)."

Oct 16, 2017

By H. H. Claudet

PROBABLY the first flotation mill for treating molybdenite ores was put into operation .in Norway during 1913, when the writer was employed to introduce and apply the Elmore vacuum flotation process at a mine in southern Norway. These operations proved successful and led to other similar installations in that country. It remained, however, for Norwegian engineers themselves to iron out their difficulties and establish the molybdenum industry on a basis which ultimately attained world importance. Just as today, an urgent demand for molybdenum arose during the world war of 1914-18. By 1916, many molybdenite properties were in operation in Canada and several small concentrating mills were under construction. At one of these, in the Ottawa Valley district, the opportunity came for applying the Elmore vacuum flotation process, using a flow-sheet similar to that adopted in Norway. Later, as one of the staff of the General Engineering Company, who had already developed a highly efficient flowsheet for treating molybdenite ores, using the Callow pneumatic flotation process, the writer devoted considerable time to research work and investigations on a number of molybdenite projects and deposits in eastern Canada. The bulk of Canada's production of molybdenite was coming at that time from the Moss mine at Quyon, Que., where concentration of the ore was effected by water-film flotation. It is of interest to note that this process, based on the principle of surface tension, had been developed and introduced by the late Henry E. Wood, of Denver, Colorado- one of the original owners of the Moss mine-at the time he was investigating the Elmore vacuum process in his Denver plant. The process, with certain modifications, was used at several other properties in eastern Canada, and notably in the ore dressing laboratories of the Department of Mines at Ottawa and in a plant at Renfrew, Ont., in both of which ore from deposits in various parts of Canada was treated, with recovery of very appreciable amounts o much needed molybdenite. During the summer of 1917, the water-film flotation mill at the Moss mine was dismantled and the plant was re-modelled by the General Engineering Company to include the Callow system. This installation, using improved flotation methods, was highly successful both as to recovery and grade of concentrate, and proved a decided advance in molybdenite concentration, a recovery of upwards of 90 per cent being obtained, with a concentrate grading over 90 percent MoS2.

Jan 1, 1944

By Franz Wilhelmstoetter, Christian Karner

"The Confederation Line is phase one of Ottawa’s light rail transit, which consists of 13 stops and stations. The project’s center piece is a 2.5 kilometer (1.6 miles) long tunnel with three underground stations leading underneath downtown Ottawa and is constructed within feet of adjacent buildings. The downtown stations, Lyon and Parliament, are caverns approximately 16.5 m (54 ft) by 18 m (59 ft) in a horseshoe configuration constructed in rock, while the third station, Rideau, is approximately 22 m (72 ft) by 18 m (59 ft) in an oval configuration and constructed in mixed ground. The paper will discuss design decisions made early on in the project such as excavation method, unique construction sequencing, and equipment selection, and go on to include corresponding progress rates. The paper also documents design and construction challenges of large caverns in very close proximity to existing buildings and varying ground conditions. Finally, an overview of achieved construction milestones and a current construction progress will be presented. Station cavern excavation is expected to be completed in early 2016. INTRODUCTION The number of urban metro construction projects has certainly increased over the last decades. Cities are growing rapidly all over the planet and many are striving to keep up with the increased demand for public transportation. One of the most feasible types of inner-city transportation with the capacity for large quantities of passengers are metro (subway) systems. Still, large construction projects in dense urban areas often affect the city’s residents in mostly negative ways. During construction, residents face the obstacles of road closures, noise, dust, economic loss for businesses, and property value losses are common. In other words, individuals are directly affected by the way new infrastructures are planned, designed, built and operated. The tunneling industry offers unique opportunities of keeping these side effects to a minimum and possibly avoiding them all together. Although challenged by a variety of constraints (some of which will be discussed in this paper), urban tunneling applications offer a chance to keep cities environmentally, economically, socially, and culturally sound during construction."

Jan 1, 2016

By Vas Choudhry

The eighties are likely to witness the first commercial-size coal-to-gasoline plant(s) in the U.S., although uncertainty regarding crude prices and cautious involvement of the Federal Government in the synfuels development are evident. The formation of The U.S. Synthetic Fuels Corporation with passage of the Energy Security Act is projected to pave the way for some of the projects on a moderate scale. The corporate objectives (1) are to provide funds for supporting a number of feasibility studies and loan guarantees for the construction of at least some commercial-size plants and the possibility of product price supports or purchase commitments. There are a number of coal conversion processes (2) currently under evaluation for producing either gaseous or liquid plus gaseous fuels, the other processes such as SRC I are for producing desulfurized deashed clean solid fuel for commercial use.

Jan 1, 1982

The complicated mining-geological conditions in the Kuzbass have led to some difficult mining situations in the past. Now, with historical data, supplemented by geomechanical information and measurements, together with an appropriate kinematic theory, a more reliable basis exists for prediction and control of the geomechanical state during extraction, with caving and with backfilling. Continued progress and improving reliability comes from data banks and computations, and now prediction of geomechanical situations is upgraded by more routing measurements and monitoring. Not only in the Kuzbass, but throughout the USSR, 14 dedicated groups are ready to solve various specific problems of prediction an control of geomechanic situations with assured increase in the quality of mining.

Jan 1, 1991

By Alain Broussaud, Guy Fourniguet, Jacques Franck, Pierre Conil

Steady-state simulation is now in current use to assist mineral processing plant design and optimization. However, the reliability of results generated by simulators has not until now been seriously investigated. A simulator supervision algorithm was designed and programmed to study both the influence of the reliability of experimental data on the accuracy of unit operation model calibration, and the influence of unit operation model accuracy on the results of direct plant simulations. An application to a grinding flotation plant is described and discussed. The approach may open the way to the quantitative analysis of the risks taken in mineral processing projects, which would be similar to the application of geostatistics to mining projects.

Jan 1, 1990

By H. J. McQueen

Before 1950, hot working was simply deforming above the recrystallization point and gave a soft product compared to cold working. From 1960 onwards, improved testing in compression and torsion (stress, strain rate, temperature, quenching) provided valid specimens for microstructural analysis by polarized optical and transmission electron microscopy (TEM). Indeed, TEM was essential to uncovering the hot working mechanisms because it could distinguish between cold and hot substructures (dynamic recovery) in either initial or new grains (dynamic recrystallization). Over the years, teams at Concordia, McGill and UBC obtained NSERC support for students and equipment. CANMET built up a hot forming group having capabilities from high-rate cam-plastometer compression to rolling of experimental alloy billets; this was combined with latest metallographic instruments for fundamental research. Al alloys of every class (2000, 3000, 5000, 7000, 8000) were studied to understand the effects of solutes, precipitates, dispersoids and composites. The complex flow patterns in extrusion were clarified and modeled by finite element methods. Physical simulations of rolling schedules (up to 20 passes and reductions of 98%) by torsion provided evidence of microstructure development during both the passes and the softening intervals, thus clarifying development of texture in different alloys. The results frequently appeared in proceedings of Light Metals symposia and Canadian Metallurgical Quarterly

Jan 1, 2011

By G. C. Baker

Despite the attention belatedly bestowed on tidal power in recent years, it remains largely a potential rather than an actual source of energy. The resource is, practically speaking, non-depletable. Extraction is technically feasible and environmentally acceptable. The restraints against development are economic, and they could be removed by technical improvements, changes in the cost or availability of other energy sources, or simply by a change in the cost of money. The exponential rise in the demand for energy makes it inevitable that the tides will be harnessed sooner or later.

Jan 1, 1972

By Richard D. Miller, Geraldine P. Norrell

This publication contains routine analyses and related source data for 295 natural gas samples from 18 States collected during calendar year 1963 as part of a continuous survey of the United States for occurrences of helium in natural gas. This survey has been conducted by the Bureau of Mines since 1917. The analyses published herein were made by mass spectrometer and a special helium analysis apparatus, which are described in Bureau of Mines Bulletins 4863 and 576.4 Five previous publications have been made to present the results of 5,998 gas analyses made by the Bureau of Mines Helium Activity , prior to 1963. The first three , Bulletin 486,5 Bulletin 576,6 and Bulletin 617,7/ contain analyses and source data on 5,214 gas samples collected from 1917 to January 1 , 1961. The fourth and fifth publications , which are published as Information Circulars , supplement the three Bulletins and contain 784 analyses of samples collected during 1961 and 1962. The present Information Circular is the third annual publication supplementing the three Bulletins .

Jan 1, 1965

By Allan E. Martin, Harold M. Feder, Irving Johnson

The cadmium-uranium system was studied by thermal, metallographic, X-7-ay and sampling techniques; special emphasis was placed on the establishment of the liquidus lines, The single inter metallic phase, identified as the compound UCd11 melts peritectically at 473°C to form a-umnium and melt containing 2.5 wt pct uranium. The cadmium-rich eutectic (0.07 wt pct uranium) freezes at 320.6°C. Solid solubilities in uraizium and cadmium appear to be negligible. Between 473°C and 600°C the liquidus line is retograde. NO publication relating to the cadmium-uranium phase diagram was found in the literature. The establishment of this diagram was of considerable interest to us because of a possible application of the system to the pyrometallurgical reprocessing of nuclear fuels. Analysis of liquid samples, metallographic examination, thermal analysis, and X-ray diffraction analysis were used to establish the phase diagram from about 300° to 670°C. Particular emphasis was placed on the establishment of the liquidus lines. The same system was concurrently studied in this laboratory by the galvanic cell method.' Both studies benefited from a continual interchange of information. MATERIALS AND EXPERIMENTAL PROCEDURES Stick cadmium (99.95 pct Cd, American Smelting and Refining Co.) contained 140 ppm lead as the major impurity. Reactor grade uranium (99.9 pct U, National Lead Co.) was most often used in the form of 20-meshspheres. This form was particularly suitable because it does not oxidize as readily as finer powder. The liquidus lines were determined by chemical analysis of filtered samples of the saturated melts. The liquid sampling technique is described elsewhere2 alumina crucibles (Morganite Triangle RR), tantalum stirring rods, tantalum thermocouple protecthecadmiumtion tubes, Vycor or Pyrex sampling tubes, and grades 60 or 80 porous graphite filters were used. Uranium dissolves in liquid cadmium rather slowly. In order to achieve saturation of the melts it was necessary to modify the procedure of Ref. 2 by the use of more vigorous stirring and longer holding periods (at least 3 hr) at each sampling temperature. The samples were analyzed for uranium by spectro-photometry (dibenzoyl methane method) or by polar- ography. The analyses are estimated to be accurate to 2 pct. Thermal analysis was performed on alloys contained in Morganite alumina crucibles in helium atmospheres. Standard techniques were employed; heating and cooling rates were about 1°C per min. For the determination of the peritectic temperature, Cd-10 pct U charges were first held for at least 50 hr at temperatures in the range 435° to 460°C to form substantial amounts of the intermediate phase. For the determination of the effect of cadmium on the a-p transformation temperature of uranium, charges of Cd-25 pct U (-140+100 mesh uranium spheres) were first held near the transformation temperature, with stirring, to promote solution of cadmium in the solid uranium. The holding times and temperatures for these treatments were 18 hr at 680°C for the cooling run and 28 hr at 630°C for the heating run. Alloy specimens for X-ray diffraction and metallographic examination of the intermediate phase were prepared in sealed, helium-filled Vycor or Pyrex tubes. Ingots from solubility runs and thermal analysis experiments also were examined metallographically. Crystals of the intermediate phase were recovered from certain cadmium-rich alloys by selective dissolution of the matrix in 20 pct ammonium nitrate solution at room temperature. Temperatures were measured with calibrated Pt/Pt-10 pct Rh thermocouples to an estimated accuracy of 0.3°C. However, the depression of the freezing point of cadmium at the eutectic is estimated to be accurate to 0.05°C because a special calibration of the thermocouple was made in place in the equipment with pure cadmium just prior to the measurement. EXPERIMENTAL RESULTS The results of this study were used to construct the cadmium-uranium phase diagram shown in Fig. 1. This diagram is relatively simple; it is characterized by a single intermediate phase, 6 (UCd11), which decomposes peritectically, and which forms a eutectic system with cadmium. The solid solubilities in the terminal phases appear to be negligible. An unusual feature of the diagram is the retrograde slope of the liquidus line above the peritectic temperature. The Liquidus Lines. The liquidus lines above and below the peritectic temperature are based on three separate solubility experiments. The data are shown in Fig. 1 and are given in Table I. It is apparent from the figure that the solubility data obtained by the approach to saturation from higher temperatures fall on substantially the same lines as those obtained

Jan 1, 1962

By Adrian C. Dorenfeld, Theodore Balberyszski, Strathmore R. B. Cooke

This paper reports results of studies of sulfidiza-tion of base-metal oxides and silicates with gaseous sulfur, hydrogen sulfide gas and pyrite and of their subsequent flotation with xanthate collectors. It has been established that a 100% conversion of the oxides of lead, zinc, copper and manganese into their respective sulfides is possible and is a function of reaction time and temperature. Sulfidization of chrysocolla (with malachite and azurite inclusions) resulted in a product containing covellite, chalcocite and digenite in proportions depending on conditions of sulfidization. Reacting cassiterite with gaseous sulfur, H2S or pyrite at various reaction temperatures resulted in its partial conversion to a tin sulfide. Flotation of the products of sulfidization indicated that their behavior is similar to that of natural sulfide minerals, the recovery being a function of the con-version of the oxides to their respective sulfides. The gradual depletion of high-grade sulfide mineral deposits has turned the attention of the mineral industry to the recovery of metals from the oxides and silicates. Anionic (fatty acid) and cationic collectors have in some cases made flotation of nonsulfides possible, although, in general, flotation of oxide ores is not as yet an economic process. Consequently, many attempts have been made to sulfidize the surface of the relevant oxide mineral and thus make it amenable to to In recent years, Bautista and sollenberger4 have investigated the conversion of a number of oxides to sulfides by reacting them with molten sulfur. This paper presents the results of .investigations carried out at the School of Mineral and Metallurgical Engineering at the University of Minnesota to study the flotation characteristics of some sulfidized minerals. It is divided into two parts: The first describes the sulfidization of a number of oxides and a silicate, and the second presents the flotation behavior of the products of sulfidization. SULFIDIZATION OF METAL OXIDES AND SILICATES Experimental Procedure: SULFIDIZATION WITH HYDROGEN SULFIDE GAS — Sulfidization with H2S gas was carried out in a horizontal tube furnace (Fig. 1). The temperature of the furnace was regulated by means of a Variac and determined with a chromel-alumel thermocouple. The constant temperature zone in the furnace was about 6 in. in length, and it was within this zone that the experiments were carried out. The gases employed were supplied from standard compressed gas cylinders, and passed through a glass-wool filtering tower before entering the Pyrex reaction tube. Gaseous products were bubbled through a water tower (used as a flow indicator) and excess H2S was burned off at the end of the outlet tube. Samples of reagents or minerals were placed in a 3-in. Alundum boat and inserted within the constant temperature zone of the furnace. Nitrogen gas (6 ppm O2 content) was passed through the tubes at room temperature to remove air in the tube, and continued to pass while the furnace was heating up. When the required temperature was reached, H2S was allowed to enter the tube and the supply of nitrogen was shut off. At the end of the reaction period, the reverse procedure was carried out, the samples being cooled to room temperature in a nitrogen atmosphere. The flow rate of H2S gas was maintained fairly constant in all experiments, although the rate was not determined. SULFIDIZATION WITH SULFUR POWDER - To study the sulfidization of minerals with sulfur (liquid or gaseous), samples of the mineral, together with a measured quantity of sulfur powder, were placed in a stainless steel (SS316) reaction vessel (Fig. 2). The reaction vessel was heated in a vertical resistance coil furnace, the temperature being regulated through a Variac. At the end of the experiment the vessel was cooled to room temperature before the sample was removed. Cooled products were leached with CS2 to remove any free sulfur. SULFIDIZATION OF TIN CONCENTRATES - Fifty gram samples of sulfidized tin ore were prepared by mixing -48 mesh Bolivian tin concentrate with -48 mesh Ottawa sand in various proportions and sulfi-dizing these samples with H2S in the horizontal tube

Jan 1, 1969

By J. A. Marts, R. C. Gilmore, Jr. Bogin, S. Saki, J. F. Brune, J. W. Grubb

"Researchers at the Colorado School of Mines have studied the influence of headgate side ventilation controls near the longwall start-up room on the formation of explosive gas zones (EGZs) in underground coal longwall bleeder ventilated gobs. In a project funded by the National Institute for Occupational Safety and Health (NIOSH) researchers developed a Computational Fluid Dynamics (CFD) model to study the formation of methane-air mixtures in the gob, start-up room, and bleeder entries. The relative change in size and location of EGZs are examined in response to ventilation controls in the headgate side bleeder entries near the start-up room. Modeling suggests that adjustments to the ventilation controls can be made to minimize the size of the EGZ. However the EGZ may form in or around active working areas regardless of the ventilation control settings. Research found regulators on the crosscuts into start-up room and first entry inby can force air into to crosscuts outby the start-up room causing more air to flow through the gob. INTRODUCTION Underground longwall mine ventilation systems may operate with either a bleeder ventilated gob or a progressively sealed gob. Bleeder ventilated gobs must meet the standards for safe operation of the bleeder system by examining bleeder system effectiveness. As defined in the United States Mine Safety and Health Administration (MSHA) Program Policy Letter (PPL) No. P13-V-12 (MSHA 2013), the pillared area or gob is “any area where a reduction in pillar size has occurred during retreat mining” and includes the “caved and broken material, the interstices within the caved material, and the open spaces surrounding the caved material.” The PPL further states that the intended purpose of ventilating the gob is “to protect active workings from the hazards of methane accumulations …” The requirements for operating a bleeder system as stated in The United States Code of Federal Regulations (CFR 2013) Title 30 §75.334(b) is to pass ventilation air though the gob “and to continuously dilute and move methane-air mixtures [from the gob] away from active workings and into a return air course …” where the concentration cannot exceed 2 percent methane (CFR 30 § 75.323). Further clarification of the bleeder system as described in the PPL states the following: “A bleeder system includes the area from which pillars are wholly or partially recovered, bleeder entries, bleeder connectors, and all associated ventilation control devices that control the air movement through the area. Bleeder entries are air courses designed and maintained as part of the bleeder system.”"

Jan 1, 2015

By Raymond Ward

IN the past few years several papers have appeared dealing with different aspects of the oxidation of dilute alloys, especially with respect to the formation of internal oxides or subscales. Subscale has been defined1 as that layer or zone of oxide particles precipitated in a matrix of metallic metal in which the oxide particles are dispersed uniformly and occur by diffusion of the oxygen inward from the metal surface. Alloys composed of a solvent metal more noble than the alloying elements are subject to subscaling or internal oxidation. In these alloys the solute must be present in such quantities that if the alloy is exposed to an oxidizing atmosphere at elevated temperatures, the rate of diffusion of the oxygen into the metal will be greater than the rate of diffusion of the solute outward. There is a composition range of the iron-silicon system that falls into this classification. Knowledge of the nature and rates of oxidation of iron-silicon alloys is of great commercial importance, but very little information of this nature is available. Darken2 recently has made calculations to show the limits of concentration of silicon for which subscales are produced in iron-silicon alloys; however, the main thesis of his paper was to analyze and to explain the already existing data. The purpose of this paper is to present the effect of com position, temperature, time, and atmosphere on the type of scale-metal layer obtained and to give some qualitative indication of the effect of these variables on the rates of oxidation. Since this paper is a study of silicon steels that are available commercially, extremely low-silicon and high-silicon alloys are not included. EXPERIMENTAL PROCEDURE The alloys used in the experiment were taken from heats of silicon steel that ranged in analysis from 0.70 to 5.8 per cent silicon. This composition range takes in most of the commercial silicon steels. In Table I are listed the compositions of alloys used. Other than iron and silicon, the alloys normally contained approximately the following impurities: carbon, 0.03 per cent; manganese, 0.07; phosphorus, 0.008; sulphur, 0.02; copper, 0.07; tin, 0.01, and from nil to a trace of chromium, nickel and copper. All of the alloys used were melted in open-hearth furnaces, except where otherwise noted, and were hot-rolled to 0.100-in. plate. Samples approximately 1/2 in. square were then cut from these materials. So that the surface conditions of the samples used for oxidation would be standardized, each sample was ground through 000 emery paper immediately before oxidation. Two different techniques were employed in carrying out the oxidizing treatments. One consisted simply of heating the samples with free access to air. In this treatment the samples were set on edge on a refrac-

Jan 1, 1945

By E. Miller, K. Komarek, W. Johnson

The activity of aluminum in solid Cr-A1 alloys has been measured by an isopiestic technique between Cr-A1890' and 1126" and 13 and 80 at. pct Al. The integral free energy of mixing has a minimum value of —5600 cal per g-atom at 59 at. pct Al. The maximum solid solubility of aluminum in chromium was determined to be 43 at. pct Al, and the composition limits of the compounds CrA14, Cr4A19, and Cr5Al, at 1000"~ were found to be 79 to 80, 66 to 70, and 59 to 63 at. pct Al, respectively. The thermodynamic properties of the Cr-A1 system have been investigated as part of a thermodynamic study of aluminum-transition metal systems.172 Little information is available on the equilibrium properties of the Cr-A1 system. The heats of formation of solid Cr-A1 alloys have been determined by Kubaschewski and Haymer at 600" and low-temperature specific heat data have also been obtained.~ More extensive work has been performed on the phase diagram, and a compilation has been provided by Hansen and Anderko,~ their phase diagram at elevated temperatures being essentially based on the work of Bradley and LU.~ The high-temperature portion of the phase diagram shows an intermediate phase CrA14 decomposing peritectically at 1018°C and existing at 82 at. pct A1 at 1000°C. They also identified the compounds with solubility limits of 72 to 75 at. pct A1 at 1000°C, and Cr5A1,, existing at 61 at. pct A1 at 1000°C. The maximum solid solubility of aluminum in chromium at 1000°C was found to be 46 at. pct Al. These elevated-temperature data were obtained by examination of quenched samples and were considered as less precise than the lower-temperature data. Koester, Wachtel, and Grube7 have revised the phase diagram as a result of their magnetic susceptibility and X-ray study. The results of this work differ appreciably from those of Bradley and Lu at temperatures above 800°C. The CrA1, compound is given as existing between 79 and 81 at. pct A1 at 1000°C, and they do not indicate the presence of a CrA13 phase reported by Bradley and Lu. They also report the compound Cr4Alg as having solubility limits of 66 to 70 at. pct A1 at 1000°C, while Bradley and Lu show this compound stable only up to 870°C. Koester et al. state that the high-temperature modification of the compound Cr5A18 is stable down to 1125"C, and not 980°C as stated by Bradley and Lu, and that the low-temperature modification of Cr5Al, has a range of homogeneity of 58 to 63 at. pct A1 at 1000°C. They also report that the maximum solid solubility of aluminum in chromium is 43 at. pct A1 at 1000°C. APPARATUS AND EXPERIMENTAL PROCEDURE An isopiestic method was employed which has been successfully applied to the determination of aluminum activities in solid ~e-All and Ni-Al alloys. Alloy specimens were held at different positions in a temperature gradient and were equilibrated with aluminum vapor from an aluminum reservoir kept at the temperature minimum of an impressed thermal gradient in a closed alumina system. Diffusion of aluminum into the specimens occurred until equilibrium was reached, at which the partial pressure of aluminum in each of the specimens was given by the vapor pressure of the pure aluminum reservoir. The activity of aluminum referred to liquid aluminum as the standard state in a given equilibrated sample at temperature T could therefore be expressed by: vapor pressure of pure aluminum at _ the temperature of the reservoir Vapor pressure of pure liquid aluminum, at specimen temperature T Since both the temperature of the aluminum reservoir and the specimen temperatures were determined experimentally, and the vapor pressure of pure aluminum is known as a function of temperature,' the activity of aluminum in a given aluminum alloy of known composition could be calculated. Initial runs were made with samples consisting of pure chromium chips placed in alumina crucibles. These runs exhibited large inconsistencies, indicating that equilibrium was not attained. High aluminum content Cr-A1 alloy powders were therefore substituted for the pure chromium specimens. The starting composition of the alloys was adjusted through experimentation until the concentration change necessary to attain equilibrium was small. In this manner, consistent results were obtained in reasonable times. SPECIMEN PREPARATION Alloy specimens were prepared from chromium of 99.997 pct minimum metallic purity: with 0.028 to 0.038 pct H, 0.0002 pct N, and 0.27 to 0.46 pct 0 (Aviquipo, Inc.). The aluminum had a purity of 99.99+ pct and the following impurities: 0.003 pct Cu; 0.002 pct S; 0.002 pct Fe; 0.001 pct Pb; 0.001 pct Ga (Aluminum Corp. of America). Alloy powders were prepared from weighed mixtures of chromium and aluminum by double-arc melt-

Jan 1, 1969

By R. K. Buhr, H. Thresh, M. Bergeron, F. Weinberg

The microsegregation of nickel and chromium in directionally solidified AISI 4340 steel castings has been measured using electron probe microanalysis. Minimum concentrations were observed to occur at the center of the dendrite stalks, as reported previously. However, the position of the maximum concentrations could not be determined from the dendrite configuration. An etching technique has been developed which shows the position of maximum concentration. Measurements were made of the distribution of nickel and chromium in the dendritic structure. The ratio of maximum to minimum concentration was determined as a function of primary dendrite arm spacing for both as-cast and partially homogenized materials. The results are compared with observations reported in the literatuve. A S part of an investigation of solute segregation in directionally solidified AISI 4340 steel casting, electron probe microanalysis was used to measure the distribution of nickel and chromium in the dendritically segregated material. This complemented the observations on the segregation of radioactive phosphorus obtained by autoradiographic techniques in the same castings.' Kattamis and I?lemings2 have reported similar measurements, using electron probe microanalysis, on dendritically segregated AISI 4340 steels. They found minimum solute concentrations occurred at the center of dendrites, maximum concentrations occurred in the center of interdendritic regions, for symmetrically oriented dendrites, and a regular variation of concentration within dendrite arms. The ratio of maximum to minimum concentration was found to be essentially independent of position in the castings, except near the chill surface where it was somewhat higher. Assuming complete diffusion in the liquid and no diffusion in the solid during freezing, they considered that isoconcentration curves in the steel were homothetic. As a result, isoconcentration curves of the various elements, contour surfaces of dendrites produced by isothermal-transformation studies, and the contour of the solid-liquid interface would all be similar, and could be superimposed by a uniform expansion or contraction of the contours. Preliminary results of the present investigation suggested that isoconcentration curves were not homothetic. It was also evident that points of maximum concentration could not be predicted from the dendrite configuration. Since the ratio of maximum to minimum concentration appeared to be an important parameter in defining the overall segregation in a casting, other techniques for determining the point of maximum concentration were investigated. In addition the overall solute distribution associated with the dendritic structure was examined for both nickel and chromium, and the consistency of the distribution for neighboring dendrites was determined. METHOD Fifty-pound heats of AISI 4340 steel were cast in a manner similar to that used by Flemings et al3 with a water-cooled copper base plate and exothermic sides and top. The nominal composition of the material was C, 0.41 pct; Mn, 0.66; Si, 0.35; S, 0.012; P, 0.010; Ni, 1.88; Cr, 0.95; Mo, 0.28. The steel solidified directionally from the chill surface, with a dendritic structure which increased in dendrite arm spacing with increased distance from the chill. Results of the general investigation of the cast structure and segregation of radioactive phosphorus in these castings have been reported elsewhere.' For the present measurements, sections were cut from the casting at several distances from the chill surface. The sections were subsequently heat-treated, mounted, and then polished on a plane perpendicular to the general freezing direction of the casting. Electron probe microanalysis was carried out with the JEOL-JXA3 microprobe using a voltage of 25 kev and beam current of 0.15 µa. The take-off angle is 22 deg. Quartz crystals were used in the spectrometers and measurements made for Ka radiation from both nickel and chromium simultaneously. A thin layer of carbon was deposited on all specimen surfaces prior to examination in the microprobe. Early measurements were made on polished surfaces, with indentation marks produced by a hardness tester to indicate the area of interest. It was found desirable to use etched surfaces, as opposed to polished surfaces, to reduce sample preparation time and more readily relate the microprobe scan to the structure. To determine if this could be done, without introducing significant errors, a series of measurements were made on polished and etched surfaces of the same specimen. Both polished and etched surfaces produced similar results within normal scatter as shown in the observations. Subsequent measurements were then made on etched surfaces. Measurements with the microprobe analyzer were made by point counting, for periods of 100 sec, at 10-µ intervals. Ten-second counts were made on pure nickel and chromium standards, incorporated in the specimen mount before and after each set of measurements. The results were adjusted for background, then corrected for dead time using the expression:

Jan 1, 1969

By A. Muan

Liquidus data are presented for mixtures in the ternary system FeO-Fe2O3-SiO2 in equilibrium with a gas phase with O2 pressures ranging from 10-10.9 to 1 atm. Data obtained are combined with previously published data to construct lines of equal 02 pressures and lines of equal CO2/H2 mixing ratios along the liquidus surface. Courses of crystallization of selected mixtures under conditions of constant total composition, constant O2 pressures, and constant CO2/H2 mixing ratios are discussed. PHASE equilibrium studies of silicate systems where iron is one component are complicated by the fact that iron readily occurs in three different states of oxidation: Fe3+, Fe2+, and Fe0. Success or failure in work with iron silicate systems is to a large extent dependent on control of the oxidation state of iron and all investigations therefore must be carried out under carefully controlled atmospheric conditions. Silicate systems containing only strongly electropositive metals (like Na+, Ca2+, Mg", etc.) can, for simplicity, be treated as condensed systems, that is, the gas phase can be neglected and the phase relationships discussed in terms of the phase rule written in the well known simplified form P + F = C + 1. In the case of iron silicate systems, however, the composition of the condensed phases varies with the gas composition, and a complete picture of phase relationships can be obtained only by varying the gas composition over a wide range. In order to understand the phase relationships in the more complicated multicomponent silicate systems with iron oxide as one of the constituents, a knowledge of the ternary system FeO-Fe2O3-SiO2 is essential, since it constitutes a bounding portion of all such systems. It was with this in mind that the present study was undertaken. Previous Work A considerable amount of work has been done on various aspects of the chemistry and metallurgy of systems containing silica and iron oxides. The two bounding binary systems FeO-Fe2O3 and FeO-SiO2" The first attempt to obtain information on phase relationships of iron oxide-SiO, mixtures at different 0, pressures was made by Greig.' Darken" determined the melting points of iron oxide on solid silica under various atmospheric conditions. Darken did not determine experimentally the composition of the melts at liquidus temperatures but discussed very ably the principles involved in applying the phase rule to the system. In a recent study Schuhmann, Powell, and Michal8 determined experimentally the liquidus surface of a portion of the ternary system and combined the new information with data in the literature to construct a phase diagram. Their method was briefly as follows: Homogeneous mixtures with various contents of SiO2, FeO, and Fe2O3 were made up by melting together stock mixtures in various proportions. Samples of the homogeneous mixtures, the compositions of which were determined by chemical analysis, were then heated in platinum crucibles in an inert atmosphere until equilibrium among the condensed phases was achieved. The samples were quenched to room temperature and the phases present determined by microscopic examination. Assuming that no change in composition takes place during the equilibration run in inert atmosphere, the liquidus surface can be determined, but no information is obtained regarding the partial pressures of 0, of the gas phase in equilibrium with the condensed phases. The author's method, to be described in the next section, permitted the location of points at the liquidus surface as well as a calculation of the corresponding partial pressures of O2. Experimental Method General Procedure: The standard quenching technique was adapted for a study under controlled variable atmospheric conditions. Premelted mixtures of silica and iron oxides in platinum envelopes were held at constant temperature under chosen atmospheric conditions until equilibrium was reached among solid, liquid, and gas phases. The sample was then quenched to room temperature, the phases present identified, and, for the most significant runs, the composition was determined by chemical analysis. The corresponding partial pressure of 0, was calculated from known equilibrium constants of the gas reactions occuring in the furnace atmosphere. Materials: Starting materials were oxides of commercially highest available purity; cp silicic acid was dehydrated by heating to 1350°C for 6 hr and cp Fe2O3 was dried at 400° C for the same length of time. Samples of 10 g were made up by mixing

Jan 1, 1956