By Kazuaki Mita

There are various intermetallic compounds in the Zn-Fe system. We synthesized them at about 673K. A specimen was examined chemically and X-ray diffraction was applied to ensure the formation of intermetallic compounds. Material containing two phases was placed in a Knudsen type effusion cell and the mass spectrum studied to evaluate the vapor pressure of zinc. The thermodynamic properties of intermetallics was then evaluated through measured intensity.

Jan 1, 1999

By Carvalho A. Felipe de

The search for environmentally friendly and cost-effective methods for gold extraction has been undertaken in order to provide alternatives to the use of cyanide leaching in the gold industry. Among such alternative reagents is the combination of chloride and hypochlorite ions due to their oxidation of metallic gold and its complexation. Therefore, the current work aims at investigating gold leaching from an oxidized material by means of a solution comprising calcium hypochlorite and sodium chlorite. The sample used in the current research contained 66.1% Fe2O3, 20.4%SiO2, and 35.7 g/t of Au. In addition, XRD and SEM-EDS analysis revealed iron oxide, quartz and muscovite as the main crystalline phases in the sample. For comparison purposes, cyanidation of the oxidized material resulted in 90% gold extraction in 24 h. The reference conditions for the leaching tests with the chlorite-hypochlorite system were: particle size −37 μm, solid/liquid ratio of 10% (w/v), 10 g/L NaCl, 10 g/L Ca (OCl)2, pH 5–6, 3 h of leaching. The effects of the: (i) Ca(OCl)2 concentration, (ii) NaCl concentration, (iii) pHrange and (iv) the effect of pulp density in the extraction of gold were assessed. In addition, the stability of the hypochlorite solutions (OCl−) was investigated. The ideal concentrations of Ca(OCl)2 and NaCl were determined as 25 g/L and 15 g/L, respectively, whereas the optimal pH range was 4–6. Under these conditions, the final gold extraction reached approximately 84%. By varying the solids content of the pulp (10%, 20% and 30%), it was observed that the lower solids value resulted in greater gold extraction (84%). The degradation of the hypochlorite solution and the possible catalytic effect of the presence of the solid were evidenced. To sumup, in the experiment, high gold extractions were achieved in shorter periods of time (3 h), as compared to the cyanidation of the same sample. On the other hand, itwas necessary to use significant amounts of the reagent due to hypochlorite instability at the pH conditions recommended for high gold extractions.

By Isabella Lancellotti, Fabrizio Passarini, Luisa Barbieri, Fernanda Andreola, Ivano Vassura, Luciano Morselli

"The techniques able to incorporate wastes by means of a heat treatment present the advantage to fix the residue with chemical bonds. Among these techniques there are vitrification and sintering which are characterised by different operating temperatures in the range of 950-1500°C and the involved raw materials develop silicatic crystalline phases and glassy matrices capable to immobilize heavy metal contents in the waste matrix. In this work incinerator bottom ash, polishing and glazing ceramic sludges have undergone to thermal treatments in order to valorise the waste as secondary raw material for the obtainment of re-products. The chemical efficiency of the process adopted has been evaluated by comparing the results of release tests applied to the as-received wastes and to the thermally treated materials in order to verify the effectiveness of the different matrices to fix the waste components.IntroductionVitrification is one of the most promising technological options for the treatment of some kinds of waste. The high temperature involved in the process (1200-1500°C) leads to the complete destruction of organic pollutants, such as dioxins, and glassy network formed can incorporate heavy metals. Some vitrification processes naturally occur: glasses produced by volcanic eruptions, such as obsidians (Na2O-K2O-Al2O3-SiO2) and basaltic (CaO-MgO-Al2O3-SiO2) rocks, are basically inert materials even when they contain toxic elements, because these are embedded in an extremely stable glassy matrix. The disadvantage of vitrification is that it is an energy-intensive process involving relatively high costs, therefore its use is better justified if a high-quality product with optimised properties can be fabricated. The most effective way to improve the properties of the vitrified material is the transformation into glass ceramic. This is a fine-grained polycrystalline material (typically from 50% to 98% of the volume may be crystalline) formed when a glass of suitable composition is heat treated and hence undergone to controlled crystallisation (phenomenon named devitrification). The three key variables in the design of a glass-ceramic are: glass composition which controls glass viscosity related to the effectiveness of nucleation and rapidity of crystallisation; glass-ceramic phase assemblage (that is, the types of crystals and the proportion of crystals to glass) which is responsible for many of the physical and chemical properties; nature of the crystalline microstructure (crystal size and morphology and the textural relationship among the crystals and glass) which is the key to many mechanical and optical properties. In particular, a partly crystalline material can be obtained by powder sintering."

Jan 1, 2008

By Kwang-Ho Lee

The Onsan copper smelter of LS-Nikko Copper Inc. has operated the Mitsubishi continuous process along with Outokumpu process since 1997. Mitsubishi process is a bath smelting process which needs adequate melts for smelting reaction in the furnace. After a campaign shutdown it requires time to make a start melt. Onsan smelter has had much experience in flash smelting, including the improvement of the concentrate burner which is one of the most important parts in a flash smelting furnace. Based on this experience, the lances of the Mitsubishi smelting furnace were modified in order to making the starter melt with flash reaction. In 2004, the flash reaction in the Mitsubishi S-furnace was completed and was able to make the starter melt using these modified lances. Although at that time it was still under development it reduced the time required to make the initial bath-melt by about half.

Jan 1, 2006

By I. Perus, M. Fazarinc, G. Kugler, M. Tercelj

"Ledeburitic tool steels are highly alloyed steels used for specific highly loaded applications but are characterized by low and variable hot workability. In this contribution the importance of selecting the right choice of some essential process parameters, i.e. casting temperature, solidification rate and soaking temperature, needed for improving the intrinsic hot deformability of ledeburitic tool steels, is studied. An inappropriate selection of casting temperature and cooling rate results in precipitation of unusual eutectic carbides that decreases the hot workability, whereas with the selection of appropriate soaking temperature the temperature range of safe hot working can be broadened. For each initial as-cast microstructure individually determined soaking temperature should be selected.IntroductionThe surface cracking during hot deformation of ledeburitic tool steels reduces mechanical properties and their industrial yield. These tool steels have high hardness, wear resistance and high tempering resistance on one hand, and high flow stresses and low hot deformability on the other. Decreased hot deformability of the tool steels is attributed to the type, size, shape, distribution, fraction of eutectic carbides and/or other phases, grain growth, etc. at upper limit while precipitation of secondary carbides and decreased recrystallization rate at lower limit of the safe hot deformation temperature range, [1-6].The occurrence of cracks on most exposed areas of workpiece are related to the areas where similar conditions related to upper and/or lower limit of temperature working range prevail, i.e. areas with accelerated cooling, areas with higher value of accumulated strains where also decreased recrystallization rate with simultaneously presence of higher tensile stresses takes place, furthermore areas of workpiece which are due to combustion conditions in furnace heated to higher temperatures, etc. Thus the areas, where combination of previously mentioned conditions prevails, are more exposed to cracking. This additionally requires that hot deformability of ledeburitic tool steel should be considered as a complex problem. Publications in the literature with regards to hot deformability of tool steels are predominately of a partial nature thus all reasons for unexpected occurrence of cracks are not sufficiently explained in available literature so far. Furthermore modern practice proves that previous processing parameters significantly influence the hot deformability and thus this cannot be considered as a constant value. During heating, soaking and hot deformation various processes take place: decay (decomposition) of carbides, formation of new carbides, dissolution of carbides and of alloying elements, etc. Thus depending on variation of process parameters and chemical composition, that consequently influences the processes related to carbides, shifting of decreased deformability at both limits of temperature working range to higher and/or to lower temperatures can occur, [1-14]."

Jan 1, 2012

By J. Daniel Bryant

Deformation processing of rapidly solidified powder alloys presents a technical challenge different in several ways from the processing of ingot based alloys. The metastable phases formed during planar flow casting of aluminum alloy 8009 (FVS0812) must be safe-guarded from high temperature excursions during processing to avoid decomposition; this restriction prohibits liquid phase sintering of particles during consolidation. The development of strong particle-particle adhesion, therefore, relies on the imposition of very large strains during forming operations to insure sufficient mechanical meshing of the aluminum particles and break-up of prior particle oxide boundaries. These strains are generally much greater than those required for metallurgical transformations in ingot based alloys. In an attempt to quantify the deformation required to improve interparticle bonding, the finite element method (FEM) was employed. Preliminary results which predict the metal flow and strain distribution in several workpiece configurations are discussed. These predictions are then correlated to measurements made on experimental subscale forgings. Lastly, experimentally measured quantities which reflect the degree of interparticle bondingg are related back to FEM model predictions.

Jan 1, 1992

By San-chuan Tang, Wen Chen, Shun-ming Ning, Kan-ping Yu, Qiang Zhao, Xue-yong Xing

"A new type of desilication agent (PA-2) was selected by experiment based on the analysis of the characters of silica gel, and the influence of desilication type, desilication dosage, pH value, temperature and aging time on the desilicating effect was studied. The test results showed that on the conditions that pH was 2.0, temperature was 20""C, aging time was12 hours and the dosage of desilication agent was 0.23%, the desilication rate was higher than 93% in solution.IntroductionVanadium is an important strategic resources, which applies to steel industry and petrochemical industry. The main materials for vanadium product are steelmaking vanadium slag, stone coal and containing vanadium waste catalyst, etc. And stone coal is a low-grade carbonaceous silicified vanadium resource, which is unique material for vanadium extraction in China. Meanwhile, our stone coal reserves is No.l throughout the world.The silica acid solution containing vanadium is produced by acid leaching of raw stone coal or its roasted ore. The silica content of this solution is mostly high, besides, when pH is higher than 2 , the solution is unstable. Furthermore, it is very easy to generate gel substance with the increasing of pH value and standing time. 'Ibis silica gel is composed of colloidal particles with the size in 0.001 - 0.1 um. As a result, it is very hard even impossible for the following operation of solution."

Jan 1, 2013

By Renxing Li, Yongyong Gong, Yufeng Cheng, Zhenxing Yin, Xin Cao, Qijie Zhai

"The influence of electric current pulse (ECP) on the solidification structure of SUS430 ferritic stainless steel (FSS) was investigated in the current study. The technology of ECP has been widely used to improve the properties of metals with relatively low cost. The parallel electrodes were inserted into the free melt surface to constitute a current loop. The different influences of three parameters on solidification structure were studied by changing the peak current value, frequency and treating time respectively. The results indicated that the ECP significantly increased the number of equiaxed grains of SUS430 FSS. The as-cast structure without ECP treating was almost wholly columnar, while the number of equiaxed grains of the specimen, which was treated 3min with a peak current of 400kIA, increased to 2698 in the observed surface. To get the best refinement, an optimum range of these three parameters is required and the peak current value plays the most important role.IntroductionFor the lack of nickel resource and the pressure of environment protection, ferritic stainless steel is increasingly adopted to replace the austenite stainless steel because of its low nickel content and good mechanical properties. SUS430 steel is a typical example with excellent performance and relatively low price to replace the application of austenitic stainless steel[1-3]. This type of steel with high thermal conductivity coefficient, low expansion coefficient, good oxidation resistance, excellent stress corrosion resistance and other fantastic characteristics is often used to make components which need to have resistances for atmosphere, water, steam and oxidizing acid corrosion[4]. Since the developing of columnar grains and low toughness at high temperature, its products are easily crinkled and cracked during the subsequent rolling process[5]. The application of ferritic stainless steel is limited by these defects[6-8]."

Jan 1, 2012

By G. Achurra

The products of the smelting of copper concentrates in an El Teniente Converter (CT) are a high grade matte, analyzing 74-76% Cu; and a highly oxidized slag, typically containing 15-20% Fe3O4 and 4-10% Cu. The El Teniente Division of CODELCO¬CHILE has developed a slag reduction-cleaning process, that is practised in a tilting, horizontal furnace, to recover copper from these slags. The El Teniente slag cleaning process has been successfully implemented at the El Teniente Caletones smelter and various other smelters in Chile: Today, eight such slag cleaning furnaces, each with a capacity of 800-1000 tonnes/day, are in operation in Chile. This paper discusses basic laboratory research and industrial tests that led to substantial reductions in the slag cleaning cycle time and the specific consumption of fuel and reductants. Simultaneously, the slag cleaning off-gas quality was improved. Based on the experimental results, recommendations were made to improve the practice of the El Teniente slag cleaning process. The recommended modifications have been fully implemented at the Caletones smelter.

Jan 1, 1999

By Jong-Jin Pak

The present work reports the commercialization of a recycling process of spent acid to recover molybdenum. The process consists of ammonia gas neutralization of spent acid containing molybdenum, crystallization and filtration of ammonium molybdate, roasting and hydrogen reduction of molybdic oxide to produce a commercial grade molybdenum metal powder. The mother liquor, highly nitrogeneous residual solution after the filtration of ammonium molybdate, can be utilized to produce chemical fertilizers.

Jan 1, 2006

By Lu Lin, Yanping Bao, Xiang Li, Linzhu Wang, Xiaobai Yan

The results showed the microinclusions were mainly Al2O3 and sulfide inclusions from tapping to the beginning of LF refining. Al2O3 inclusions were modificated into calcium aluminates after calcium treatment. Lots of spherical calcium aluminates composite inclusions containing MgO, TiO2 and MnS were found after soft blowing and during tundish metallurgy and left in the slab which caused the defects of beam plates. Pure Al2O3 inclusions were observed again after soft blowing 8min. Average sulfur content in inclusions decreased because of the high desulfurization ability of refining slag. Average Ca/Al ratio value in inclusions increased during LF refinging because of the reduction of CaO in slag by carbon and it increased obviously during the process of soft blowing 8min because of the dissolusion of calcium wire.

Jan 1, 2015

By Tatsuro Ariyama, Michitaka Sato, Atsushi Sakai, Sumiyuki Kishimoto, Ryota Murai

"In order to achieve high pulverized coal injection operation in a blast furnace, optimization of the injection lance arrangement was carried out using an experimental furnace and mathematical models. To increase the injection rate of pulverized coal, it is required to raise the combustion efficiency of pulverized coal. It became clear that multi-point injection and the lance arrangement to avoid interference among the coal streams injected were so effective in increasing combustion efficiency. With these findings, the eccentric double lance arrangement has been newly developed.At NKK, Fukuyama No.4 Blast Furnace, after the improvement of the lance arrangement, the maximum injection rate reached up to 230 kg/thm and an average monthly record of 218 kg/thm was successfully achieved.IntroductionFrom the viewpoints of reducing the production cost of pig iron and prolonging coke oven life, high pulverized coal injection over 200 kglthm is actively pursued by ironmaking industries[1-2].Coal particles injected into the blast furnace are consumed by combustion in the raceway and also in-furnace reaction like solution-loss reaction (C + CO2 = 2CO). The amount of coal consumed by the latter process is determined by the carbon balance in the blast furnace and there is a limit. Therefore, to increase the injection rate, it is desirable to improve the combustion efficiency in the raceway. For these purposes, the optimization of the lance arrangement was examined by a hot model and mathematical models."

Jan 1, 1996

By Lauri E. K. Holappa

Ferrochrome, as the central constituent in stainless steels is one of the most rapidly growing primary metallic products. In this contribution results of a comprehensive study on the reduction process of chromite ore to FeCr are presented including thermodynamic examination, experimental work on kinetics and mechanisms in solid state, and smelting reduction conditions as well as kinetic modelling of solid state reduction.

Jan 1, 1999

By Dong Liang, Qijie Zhai, Zhichen Zhang, Qixin Li, Zhishuai Xu

"The formation, distribution and survival of pure Al nuclei under surface pulsed magneto oscillation (SPMO) treatment were investigated with thecombination of experiments and numerical simulation. The results indicated that the nuclei originated from the whole top surface of melt owing to the oscillation of top surface induced by SPMO. The temperature field significantly affected the survival of the nuclei The electromagnetic force and flow field of the melt with SPMO treatment were simulated by finite element software ANSYS. The electromagnetic force mainly distributed below the top surface near the mould wall. The electromagnetic farce not only made the melt oscillate but also increased the convection of meh below the top surface vigorously. The oscillation near the top surface of the melt promoted the nucleation largely, and the convection increased the uniform of the temperature distribution in the whole meh which favored the survival of nucleiIntroductionAs we all know, fine equiaxed grains are beneficial fur the improvement of the mechanical property, process ability and the uniformity of metallic materials [1-2]. With the researches of recent decades, people discovered that the electromagnetic field is an efficient method to refine the solidified structure of metals [3-7]. Pulsed magnetic field technology obtains more and more attentions in recent years due to its smaller power consumption, bigger instantaneous magnetic field intensity, non-contacting with the meh and simple convenient equipment manufacturing [8-9]. However, the melts would splash fiercely when pulsed magnetic field is applied with a slightly higher power. Thus, based on the understanding of the solidification refinement mechanism of electric current pulse (ECP) [10], Gong et al [11] developed a novel technology called pulse magneto-oscillation (PMO) to refine the solidification structure. The technology can be easily applied in the solidification structure refinement of continuous casting slab. But fur aluminum continuous casting, the sump is very shallow, which greatly limits the application of pulse magneto-oscillation technology."

Jan 1, 2014

By Bo Jiang, Lianyun Liu, Hongmin Zhu, Kai Huang

"Watermelon peel is selected as a novel adsorbent to remove Pb(II) from aqueous solution. A simple saponification process is proposed to modify the peel and the adsorbent is characterized by SEM and FTIR. The effects of pH, contact time, initial concentration of Pb(ll), biosorbent dosage and temperature on adsorption of Pb(II) are investigated. Different models are used to fit experimental data. These models indicate that the adsorption process follows the Langmuir model and pseudo-second-order model. The maximum adsorption capacity obtained from Langmuir model is 1.05mol kg-1 for the prepared sorbent. Equilibrium time is attained in 5-10 min for the studied concentrations. The watermelon peel can be used as an effective and low-cost biosorbent for removal of Pb(ll) from aqueous solution.IntroductionRecently, removal of heavy metal ions from industrial effluents by biosorption has become a very attractive topic, since the more serious pollution issues caused by heavy metals emerge frequently, and more strict requirements for its control are called upon by society [1,2]. In this case, most conventional purification technologies are not suitable due to poor cost-effectiveness [3]. For example, chemical precipitation by alkaline reagents usually can not decrease the metal ion concentration below the permissive levels, and also it will produce a large amount of sludge containing toxic metals. Membrane separation techniques can realize deep purification of wastewater easily, although its operating cost is usually high. Thus, considering the high effectiveness, low cost and free-sludge operation, bisorption has become a promising technique in water treatment [4]. The most important thing for this technology is the synthesis of a suitable biosorbent, whose adsorption properties will determine the removal efficiency and economic cost for the whole process. Watermelon is one of the most popular fruits for mankind for its delicious flavor. Usually, the watermelon is consumed mainly for its edible pulp, and its peel is discarded or only used as feed for livestock. Considering the pectin contained in the watermelon peel, just like that in orange wastes in the reported literatures [3], the idea of using it as the raw material to prepare the biosorbents for heavy metal ions removal from the aqueous solution was evaluated in this study."

Jan 1, 2012

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Min Chen, Nan Wang, Zhen Tian, Yingying Shen

"The enrichment behavior of phosphorus in CaO-SiO2-FeOx-P2O5 slag was studied by making an investigation on the distribution of phosphorous content in slag and 2CaO·SiO2 phase. The research results showed that the existing 2CaO·SiO2 solid particles in slag were the sites for the phosphorous enrichment. The enrichment process of phosphorus in CaO-SiO2-FeOx-P2O5 slag can be recognized as: mass transfer of phosphorus from bulk slag toward the surface of 2CaO·SiO2 particle, superficial dissolution reaction of phosphorus to 2CaO·SiO2 and diffusion of phosphorus through the product layer of 2CaO·SiO2-3CaO·P2O5 solid solution to the inner of 2CaO·SiO2 particle. Compared to the 2CaO·SiO2 particles with larger size (500µm to 1000µm), the completion time of enrichment was shorter for the particles with smaller size (less than 50µm).IntroductionDuring ironmaking and steelmaking, significant amounts of slag are produced. Contrast to the high utilization of ironmaking slag, the treatment of steelmaking slag is more difficult and challengeable, and therefore, an alternative approach is to recycle the steelmaking slag inside the ironmaking and steelmaking process itself. The main limitation to the reuse of steelmaking slag inside the process is that the refining process may be aggravated caused by the phosphorous accumulation if it is used in the blast furnace burden [1]. At the same time, the phosphorous content of steelmaking slag (approximately 1%~5% P2O5) is too low for it to be used as raw material for fertilizer [2, 3]. Moreover, owing to the diminishing supply of global iron ores with low phosphorous content, the control of phosphorus in iron and steelmaking processes has become an increasing problem, and as a result, more amounts of high phosphorus containing steelmaking slag are produced. Therefore, a valuable approach is quite appreciated in which the steelmaking slag is recycled within the ironmaking and steelmaking process and at the same time, the high phosphorus-containing phases in the steelmaking slag, suitable for use as fertilizer can be separated and recycled effectively [4]."

Jan 1, 2011

By Alexandr I. Volkhin

It is practically useful to separate copper from nickel at the fire refining stage of blister copper by transferring nickel in electrochemical inert silicides which are being concentrated further into the tank-house slimes. The treatment of copper melt by silicon-containing reagents is resulted in lowering the interfacial tension of the melt, its deoxidizing, selective siliconizing of in-melt nickel and forming a by-product with fluxing properties. Si-containing reagents have positive influence on results of fire and electrolytic refining, and further pulverizing of copper in plant conditions.

Jan 1, 2006

By William Petruk

"Heap leaching is a developing technology for recovering native gold and electrum from low grade deposits and from tailings. Recovery depends on permeability of the rock and ore minerals, size of particles in the heap, and ore textures that influence exposure of gold grains to cyanide solutions. These ore textures include gold-bearing veinlets and microveinlets along fractures and microfractures, gold grains in porous minerals and rocks, and gold graim. occurring along grain boundaries of other minerals. On the other hand, small encapsulated gold grains arc not likely tote exposed even with fine grinding. Most gold grains that occtir along grain boundaries of other minerals can be exposed with a moderate to fine grind, but the. resulting material will be too fine-grained to be permeable in a heap. Such finely ground ore, as well as tailings from flotation operations, can however be prepared for heap leaching by agglomerating the material into porous briquettes. Oxidized and weathered zones above. orebodies are frequently amenable to heap leaching because the gold-bearing pyrite and arsenopyrite have become permeable by conversion to porous iron oxides and ferric oxyhydroxides. A review of ore textures in several types of gold deposits suggests that:(1) the gold in vein deposits would gtmerally be amenable to heap leaching of both oxidized ores and fresh non-refractory ores,(2) the gold in Carlin-type deposits and in volcanogenic massive sulfide deposits is not likely to be amenable to heap leaching fresh ore, but oxidized zones above the orebodies are generally amenable to cyanidation, and(3) the gold in porphyry copper-gold deposits and in Witwatersrand-type deposits would likely be amenable to heap leaching of both fresh and oxidized ores but with high cyanide consumption."

Jan 1, 1997

By C. A. Nogueira, F. Pedrosa, F. Margarido, R. N. G. Guerra

"A hydrometallurgical process for recycling spent Zn-MnO2 batteries was developed, involving leaching with sulfuric acid, purification by precipitation and metals separation for further recovery. Leaching of zinc oxide was easily attained while for manganese oxide was rather difficult depending on temperature and acid concentration. At 90°C and with the liquid/solid ratio of 20 L/kg, more than 95% of zinc is recovered in 30 minutes with 0.5M H2SO4. To attain similar recovery for manganese, higher levels of acid concentration and time are needed (e.g 0.7 M and 2 hours). After leaching a purification step is necessary to remove iron co-dissolved through Fe(III) precipitation. Separation of zinc from manganese by solvent extraction with 1M DEHPA follows in the process route. The countercurrent multistage separation diagram developed allows the production of a zinc electrolyte with 120 g/L Zn and 0.005 g/L Mn, and a raffinate with 16 g/L Mn and 0.013 g/L Zn.IntroductionThe recycling of spent Zn-MnO2 batteries is carried out by dedicated recyclers using several process alternatives [1]. Most of the running processes use pyrometallurgical technologies [2] based on zinc distillation. Alternative treatments by hydrometallurgy have been reported [3-5] but its application is scarce.In order to contribute to the development of alternative solutions, a process for recycling batteries based on Zn-MnO2 systems has been studied. The process is based on the hydrometallurgical treatment of spent batteries in sulfuric acid media (Figure 1). The process starts with the physical processing by shredding using cutting grinders, where the batteries are opened and size reduced, allowing the liberation of the interior electrode particles or pastes. The fines can be then separated and the coarse material containing the steel scrap can be treated to remove the remaining aggregate electrode. The final scrap also contains some plastics and other non-metal materials and can be further valorized."

Jan 1, 2008