By A. J. Schindler, F-P Sawyer, T. Logan, M. L. Shutey-McCann, R. M. Perry

"Test work on biooxidation pretreatment of low-grade refractory gold ores has been ongoing at Newmont Gold Company since 1988, including laboratory testing and pilot biooxidation heaps (360 to 23,000 tonne). Metallurgical results of the biooxidation process utilizing Thiobacillus ferrooxidans (T. ferrooxiddans) have culminated in the design, construction, and operation of a biooxidation demonstration facility. The facility has processed 708,000 tonnes of refractory ore, using a batched process with separate pads for biooxidation and ammonium thiosulfate gold extraction. Siliceous sulfidic refractory (SSR) and carbonaceous sulfidic refractory (CSR) ores are treated separately during biooxidation pretreatment unit operation. Following biooxidation, the ores are neutralization with lime and placed on oxide leach pads or stacked on the ammonium thiosulfate leach pad. Gold is leached with either cyanide for SSR ores or ammonium thiosulfate for preg-robbing CSR ores.This paper will only address the biooxidation pretreatment process of the SSR and CSR ores.AcknowledgmentsThe authors appreciate the cooperation and approval of Newmont Gold Company Carlin Operations management for its support and permission to publish this paper. The paper draws on efforts and assistance of the following people and several others which are to many to list who participated over the past five years in bringing this project to its fruition: Dr. James A. Brierley, Chief Microbiologist, Newmont Metallurgical Services; Dr. Rong-Yu Wan, Metallurgical Manager, Newmont Metallurgical Services."

Jan 1, 1997

By S. W. White

Plasma arc technology is increasingly being used to process a number of waste materials. In present research, plasma technology is being investigated to treat waste magnesium baghouse dust, which is a waste material from the Magnetherm process. This dust contains mostly MgO, but also contains NazO, CaO, and KzO. Plasma energy is to be used along with a reducing agent to produce pure gaseous magnesium while keeping the other materials in a slag. The magnesium will then be collected by rapid quenching. A non-transferred arc plasma torch is ideal for this reaction because of its high enthalpy and improved energy efficiency over conventional methods. Another advantage of plasma is that it allows for the pre-heating or pre-reacting of fine particles before contact with the melt. Thermodynamic calculations using the Gibb energy minimization method were used to determine the most stable compositions of the materials at various temperatures. Energy balances have also been calculated. These results conclude that we can recover approximately 98% of the magnesium with a proper quenching technique. The calculated results are compared with the experimental data, and good agreement between them was observed.

Jan 1, 1999

By C. A. Silva

The kinetics of chlorination of titanium-bearing raw materials has been investigated. For comparison purposes pellets of controlled macro-porosity, made of analytical grade TiO2 and anatase concentrate (Brazil) , have been exposed to different combinations of gas composition - CO, CO2, C12 -, gas flowrate and temperature. A thermogravimetric technique and an adapted grain model have been used in order to assess the influence of the several experimental parameters upon the chlorination behavior.

Jan 1, 1997

By D. P. Cook, Jr. Jones, J. W. Evans

"It is well understood that the flow of liquid metal in the mold region of the caster can have a notable effect on the overall solidification behavior in aluminum casting. Previously our group has characterized the flow in this region in a water model, using particle imaging velocimetry. The flow is significantly effected by the specifics of the metal delivery system, i.e. size, geometry, used during the cast. Recently, a time-averaged 3D numerical model of the nozzle, combo bag and sump region has been developed and its validity has been tested against experimental data. Cases were run for different sized combo bags as well as bags that have been blocked. The results show satisfactory agreement between the physical and mathematical models.IntroductionFluid flow in the head of an electromagnetic (EM) and direct chill (DC) ingots has been shown to effect many important operational parameters in casting such as superheat removal, macrosegregation, and hot cracking. In most cases, the momentum from the nozzle is diverted through a delivery system, termed a bag, before entering the mold region. The specific geometries of the bags vary widely from operator to operator suggesting that there is still some question as to the optimum design. Several studies [1-4] have been carried out to understand the influence of the bag design on the solidification behavior in aluminum casters. However, few studies have included numerical prediction with experimental verification. Unfortunately, many simulations performed today still do not accurately account for flow in such devices.Recently, a significant amount of research into the flow resulting from the metal delivery systems has been performed [5-8]. The thrust of this research has been characterizing the flow patterns by a measurement technique called particle imaging velocimetry. The data suggest that the method of delivering the liquid metal into the mold region has a significant effect on the nature of the flow. With a detailed set of quantitative data from a water model, a numerical model can be built and tested to ensure a proper description of the flow field. The computational model used in these simulations is designed to represent a laboratory scale model of a caster in which ""combo"" bags were simulated. Such bags are mostly of a densely woven glass fiber material with low permeability to aluminum. ""Windows"", of a more open weave, permit aluminum to flow from the bag, see Fig. I. Two different sized combo bags were modeled, each subject to two different outflow window configurations. Furthermore, experimental measurements [9] were used to validate the model results."

Jan 1, 1999

By Zhang Hengzhong

Based on thermodynamics of surfaces and a proposed two-dimensional state equation for surfaces, the relationship between the surface tension (Y) of a solution and the activity (a1) of its component (i) was derived: (1/Y)r2-.¬E (ai/Yl) The derived equation was verified with reported experimental data of water-alcohol systems and water-acetone system, the calculated results showed astonishing coincidence with experimental. Applications of the equation to the five matte systems Cu2S-FeS, Ni3S2-FeS, FeS-PbS, Cu2S-PbS and FeS-Cu22S-PbS also demonstrated that at given matte compositions the calculated surface tensions agreed with experimental fairy well.

Jan 1, 1993

By A. W. Bryson, S. P. Fox, S. A. Godorr

"This work is an extension of a previous investigation on the development of surface roughness during electrodeposition of copper. A comprehensive model based on diffusion and migration in a force field together with surface diffusion and sticking probabilities is used to generate profiles which are compared to those produced experimentally. The roughness is characterized by using the technique of fractal geometry which is shown to describe both qualitatively and 9uantitatively the development of surface morphology during electrodeposition.The work is extended to the deposition of copper in the presence of various concentrations of thiourea. The development of roughness is observed experimentally on the edge of a thin copper disc mounted between two glass plates. This enables photographs to be taken at various stages during growth. The surface outline is digitized using an image analyzer which enables the fractal dimension to be determined as growth proceeds. As expected, the presence of thiourea at low concentrations produces a fractal dimension which is closer to unity (i.e. the surface becomes smoother).IntroductionThe development of surface morphology during electrodeposition has far-reaching implications for copper plating in the electrowinning and electrorefining processes. Short circuits as the cathode surface grows unevenly require operator intervention in a dangerous environment and imply processing delays, and the inclusion of electrolyte in small gaps in the plated cathode have implications in downstream processing of the cathode. Higher current densities are obviously desirable, as they result in greater production rates, but as shown by Ettel et. al.(l), Harvey et. al.(2), Cook (3), and Harvey et. al.(4), it is not possible to operate near the projected economically optimum conditions because the electrodeposition of copper from sulphate and acid solutions is a mass transfer controlled process. It has been shown (Ettel et. al.(l), Harvey et. al.(2)) that the closer a system operates to mass transfer limiting conditions, the poorer the resulting cathode quality. One solution is to use agitation techniques to increase the limiting current density. Another is to add surface active additives to the electrolyte which has been shown by Ettel et. al.(l), Harveyet. al.(2) and Afifi et. a1.(5) to allow higher rates of production without decreasing cathode quality. The second proposed solution is of interest in this work, since there is very little knowledge of the conditions under which these additives operate effectively, and little fundamental understanding of the mechanism by which they operate. The current work seeks to contribute to this field by correlating a simulation model with experimental results to describe the development of surface morphology in the electrodeposition process."

Jan 1, 1997

By S. Prasad

The effectiveness of ultrasonic velocity measurements and attenuation of the propagating pulse was evaluated as a means of Non-Destructive characterization of cold worked and annealed copper. Commercial copper is subjected to mechanical working such as forging, rolling and thermal treatment to induce re-crystallization. The microstructural changes that occur in copper and a variation in its mechanical properties are subjected to analysis using the ultrasonic technique. The signal processing is carried out using the wavelet analysis technique. The features of wavelet analysis namely, localization in space and the presence of an infinite set of basis functions allows removing noise from the time series and components of a non-stationary signal to be analyzed. This is seen to improve the accuracy of the results obtained from the ultrasonic technique in the case of copper, which has distinct coarse grains that are difficult to inspect due to backscattering from the grain boundaries.

Jan 1, 2010

By W. Petruk

The behaviour of galena, chalcopyrite and tetrahedrite during floration of a fine-grained base metal ore from New Brunswick was investigated by image analysis study of the mill concentrates and tailings. The minerals were analyzed to determine the grades and recoveries as related to free and unliberated mineral grains and their size distributions. The results show that only 37 wt % of the galena was liberated but 88 wt % of the free galena was recovered, indicating good mill performance for the lead. The lead recovery was 65 wt %, with the main loss due to unliberated galena. Most of the unliberated galena lost to mill tailings is so fine-grained that galena liberation and Pb recovery would not improve significantly by re-grinding. Chalcopyrite liberation was 56 wt % but only 75 wt % of the free chalcopyrite was recovered. Copper recovery was 45 wt %, with the chalco-pyrite loss in the mill tailings being both as large free grains, and as small and large unliberated grains. It was calculated that copper recoveries could be improved about 8 to 10 wt % by changing the concentrator operations and by regrinding. Concentrator operations hive already been modified and copper recoveries have improved about 5 wt %. About 29 wt % of the silver was lost to tailings mainly as both free and unliberated, large and very small, Silver-bearing tetrahedrite grains. It was calculated that about 25 wt % of the silver in the tailings might be recovered by improved milling conditions and by regrinding.

Jan 1, 1981

By Youliang He

Twin-roll casting is an integrated casting and rolling process that involves the continuous solidification of a melt and the plastic deformation of the solidified metal between two rotating rolls. Computer modeling is a valuable tool to help engineers understand the metallurgical process during twin-roll casting. However, commercially available software can only model either the fluid flow/heat transfer of the melt or the plastic deformation of the solid, but not both. In this study, an object-oriented finite element program was developed to simulate the steady-state fluid flow, solidification and plastic deformation of an A7,31 magnesium alloy in a horizontal twin-roll caster. The melt, the mush zone and the solid were treated as a generalized Newtonian flow in an Eulerian reference frame and different constitutive equations were employed to describe the material behaviours. The effect of operational parameters on the solidification process was discussed based on the simulation results.

Jan 1, 2010

By Ryo Sasai, Takeshi Itakura, Haruki Imaizumi, Hideaki Itoh

"Emission of industrial wastewater containing harmful oxoanions is one of the serious problems on account of its toxicity and the environmental pollution, especially caused by boric, phosphinic, arsenic and antimonic species. In this study, we developed a novel treatment technique of such polluted-water by hydrothermal mineralization. The treatment is “Geomimetic” method for precipitating oxoanions in aqueous media as natural ore resources by using hydrothermal treatment with calcium salts mineralizer. The treatment made it possible not only to detoxify the polluted-water, but also to recover the calcium minerals such as Ca2B2O5·H2O, Ca5(AsO4)3(OH), etc. Concentration of each ion in treated-water was lower than that of effluent standard in Japan. Moreover, the residual concentration of each ion was independent of the initial concentration, but it depends only on the solubility of the formed mineral under hydrothermal condition. Therefore, the hydrothermal treatment could be recommended as one of the treatment techniques of polluted-water.IntroductionVarious oxoanions such as boron and arsenic oxo-anions have high toxicity against human health and the environment. They are important resources, however, for plating or advanced material manufacturing industries[1-3], from which the wastewater containing these oxoanions is generated every day. An appropriate treatment is often required for industrial wastewaters to attain national effluent standards of Japan (NESJ, B: 10 mg/dm3, As: 0.1 mg/dm3). On the other hand, there is no production of arsenic and boric resources in Japan, and they are expected to be recycled. Therefore, the establishment of a system for the removal and recycling of arsenic and boron from wastewaters is of global significance.Several methods to remove them from aqueous media have been already reported by using adsorption[4], electro-coagulation[5], membrane separation[6-8] and biological techniques[9]. However, these methods have the following problems because of their stability in water. (1) Removal yield is low, especially for tri-valent arsenite ion (AsIIIO3 3-) and borate ion. (2) The applicable concentration range is narrow. In addition, the used adsorbents or collected residues after treatments are sill hazardous wastes, so that they must be treated by a proper method. But, it is very difficult to convert them to recyclable resources at most industrial plants. These problems are caused by the difficulty to recover these oxoanions as stable solid precipitates with low solubility in water. The establishment of recycling system of these hazardous compounds will be one of the world-important issues, especially, in Japan, which is poor in natural resources. On the other hand, compounds that contain high arsenic concentrations and are insoluble in water, are often found in natural minerals, for example, as haidinglite (Ca(AsO3OH)·(H2O) or Johnbaumite (Ca5(AsO4)3(OH)). This fact suggests that nature has an ability to produce insoluble As-bearing minerals. Similar phenomena can be found in case of boron, antimony, etc."

Jan 1, 2008

By Neil Rowlands

Particle liberation studies are commonly used in the determination of the proportion of locked and liberated phases in ground ores at various stages of mineral processing. These studies may range from a qualitative assessment of a polished specimen in an optical microscope to a full quantitative analysis of the liberation characteristics of fine grained complex sulfide ores using scanning electron microscopy and high level image analysis. However, the conversion of quantitative data to meaningful information on a mill operations level is by no means a simple task. This paper reviews the errors inherent in the SEM/Image Analysis technique and looks at the various methods available to minimize errors in data collection.

Jan 1, 1992

By S-L. Jämsä-Jounela

Fault diagnosis systems have attracted growing interest in a number of engineering fields. The number of applications has increased and successful results have been widely reported. The fault diagnosis system presented in this paper is integrated, and it monitors the states of the process and performs fault detection and diagnosis on the process equipment. The monitoring of process states is carried out by means of Kohonen Self-Organising Maps that is a powerful tool in visualisation and analysis of high dimensional data in engineering applications. This paper presents the results of SOM analysis carried out on the Outokumpu flash smelting process. The subsystems analyzed in more detail are the condition of the concentrate burner, the condition of the gas line on the basis of the pressure distribution in the process and the cooling water circulation of the waste heat boiler, and the condition of the furnace and furnace equipment on the basis of the temperature distribution in the furnace and gas line. Keywords: Fault diagnosis, Process monitoring, Kohonen Self-Organising Maps, flash smelting

Jan 1, 2001

By W. F. Ranson, R. C. Progelhof

"I. THE PROBLEM: MANUFACTURING PRODUCTIVITYThe 1985 President's Commission [I] on Industrial Competitiveness found compelling evidence of the declining economic position of the United States in world markets. The annual rate of increase in the United States productivity is approximately one-seventh that of our major trading partners over the last decade: profit levels in manufacturing investments are below those of the mid-1960's; an increasingly negative trade balance since 1971; and a sharp decline in the United States share of world trade in manufactured goods for more than two decades. A particularly dramatic example of the shifting economic balance is the fact that Japanese productivity growth has been five times greater than that of this country since 1960. In face, Japan's productivity now exceeds that of the United States in such critical industries as steel, transportation equipment, electronics and electrical machinery.American employees have experienced the competitive consequences of this nation's lagging industrial performance. Between 1980 and 1984 alone, the population of non-farm employees engaged in manufacturing dropped from 22.4% to 20.6%. This reduction in manufacturing must be arrested.Commissions RecommendationsThe comprehensive set of recommendations offered by the President's Commission recognized the nation's ""key competitive advantages"", technology and human resources, and calls for their strengthening. Particular emphasis is placed on manufacturing technology and the fact that this country does not translate research into new technologies rapidly and fully.""Perhaps the most glaring deficiency in America's technological capabilities has been our failure to devote enough attention to manufacturing or 'process' technology. It does us little good to design state-of-the-art products if within a short time our foreign competitors can manufacture them more cheaply. The United States has failed to apply its own technologies to manufacturing. Robotics automation and statistical quality control were all first developed in the United States but in recent years they have been more effectively applied elsewhere""."

Jan 1, 1988

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By Fathi Habashi

Laboratory autoclaves for hydrometallurgical investigations are available in a variety of sizes, models, and materials of constructions. They vary in sizes from 25 mL to 2 liters for laboratory studies and 5 to 50 gallons for pilot plant work. They are essential tools for studying aqueous oxidation of sulfide concentrates, dissolution of oxide minerals at high temperature and pressure and hydrothermal precipitation reactions. The maximum pressure and temperature at which any pressure vessel can be used will depend upon the design of the vessel and the materials used in its construction. Since all materials lose strength at elevated temperatures, any pressure rating must be stated in terms of the temperature at which it applies. A review of existing models and their accessories will be given.

Jan 1, 2000

By Simon N. Lekakh, D. G. C. Robertson

A new integrated CFD-combined reactors approach is proposed for the description of processes in metallurgical vessels. CFD simulations were used to obtain the melt flow pattern in the vessels (ladle, tundish, and continuous caster mold). From these simulations, the characteristic curves were derived: (i) the residence time distribution curves (RTD) for flow-through systems (at tundish exit or at dendrite coherency surface in the mold) and (ii) the mixing curves for closed systems (ladle). In the next step, the melt flow was represented in a “combined reactors” system consisting of a combination of unit reactors (Plug Flow, Mixer, and Recirculated Volume). An inverse simulation was used to define the volumes of the reactor units and the melt flow rates between them by fitting to the characteristic curves from both methods (CFD and combined reactors). The suggested approach is demonstrated for multiple designs of Ar-stirred ladles, tundish, and SEN. This methodology can be used to enhance traditional post-processing CFD analysis and also as a tool for on-line process control.

Jan 1, 2014

By Y. Shigeno

The reactivity of a porous solid is a strong function of its pore structure (porosity, pore surface area and pore size distribution). It follows that reactivity could be altered by altering pore structure; one way to achieve this is by chemical vapor infiltration whereby a gaseous species is reacted in the porous solid to produce a solid. Experiments were carried out in which the pore structures of various carbons were modified by cracking methane within the pores; oxidation rates of the carbons were then measured for both infiltrated and original samples. For coke it was found that two indices of coke performance used in the steel industry (CRI and CSR) can be greatly improved following a small amount of infiltration. Infiltration/oxidation results are interpreted in terms of measured pore structure changes.

Jan 1, 1993

By A. D. Zunkel

The zinc in electric arc furnace dust (EAFD) arises from the fuming and oxidation of the zinc present, mainly as galvanizing, in automotive scrap. The dust is collected from the electric furnace offgases in bag filters and is classified by the EPA as a hazardous waste (K061). As more zinc is used in galvanized sheet on automobiles and more automobile scrap is recycled via the EAF, the more zinc will be available for recovery and recycling. EAFD will become a more prevalent and important source of zinc compared to the traditional zinc sulfide concentrates ifit can be cost effectively processed.

Jan 1, 1995

By Valdeci Paula Alvarenga, Sergio Luiz Costa, Itavahn Alves da Silva, Filipe Bueno Carvalho, Varadarajan Seshadri, Carlos Antonio da Silva

Use of fluorspar in steel refining operations is one of the environmental concerns and as such reduced consumption of this material or substitution of the same is one of the objectives. Industrial runs were carried out at Aperam Steel making convertor unit (Timóteo, MG, Brazil) using recycled/briquetted slag for partial or complete substitution of fluorspar. Samples were collected from the metal bath and slag after oxygen blowing to assess dephosphorization with several combinations of recycled/briquetted slag and fluorspar. The results showed that partial substitution of fluorspar by BOF slag briquettes did not affect the efficiency of dephosphorization. In general average Phosphorus content was reduced to 0.010% in the case of partial substitution compared to 0.016% in the regular refining procedure with no substitution. This replacement also resulted in 40% reduction of the fluorspar consumption in the converter

Jan 1, 2015

By C. Cánepa

In the treatment of many problems related with the optimization of a given ore dressing process, microscopic studies can provide invaluable assistance. Such studies are generally carried out through mineralogical determinations both qualitatively and quantitatively. Frequently the solution of a specific problem requires the combination of these in adequate proportions. Often the nature? of the problem poses some conditions regarding the way the microscopic determinations are made in order to yield useful information. Most publications applied to mineral beneficiation show results of ore microscopy without mentioning the methodological details involved in the determinative work and therefore it is not possible to judge their reliability and/or their relevance. As methodology must necessarily change from case to case, it is very important for the microscopist to identify first the direct and indirect mineralogical information required to solve the problem. Without such guidelines selection of methods for the qualitative and/or quantitative determinations cannot be made.

Jan 1, 1981