By Moto Goto

PT Smelting, located in Gresik, East Java, is the first copper smelter and refinery in Indonesia. Since the first charging concentrate in December 1998, many equipment troubles have been systematically eliminated, and the present operation is smooth and has accomplished the design capacity of 200,000 tonnes per year of LME, grade-A copper cathode. This paper describes troubles and countermeasures, which were experienced until now.

Jan 1, 2002

By Georges J. Kipouros

Anhydrous neodymium trichlorids (NdCl3), containing ~1 weight percent neodymium oxychloride (NdOCI) was prepared by the dehydration of neodymium trichioride hexahydrate (NdC13.6H2O). Dehydration of the hexahydrate was conducted in three steps. First, the hexahydrate was slowly heated in air to about 250 °C until all the low temperature water of crystallization was removed. In the second stop, the neodymium hydroxychloride (Nd(OH)2C1) fanned in the first step was decomposed by heating under argon to 430 ° C. Finally the salt was ground and then treated with HCl gas at 330 °C until practically all of the NdOCl was converted to NdCl3.

Jan 1, 1992

By S. Kurama

Incorporation of de-watering sieve waste of borax (TSW) from Etibor Kirka Borax Company (Turkey) on the mechanical and physical properties of a commercial floor tile composition was investigated. In order to achieve this aim, TSW was partially employed in place of feldspar in the standard composition up to 20 wt %. The formulated compositions were wet milled, dried, shaped and then fired at 1190C for a total firing time of 38 minutes (from cold to cold) under industrial conditions. It was found that using of TSW up to 15 wt % improved the physical and mechanical properties of final product. The results indicated a good prospect for TSW as a co-flux in floor tile formulations.

Jan 1, 2006

By L. Salinas

Lance injection of gas and particles into a molten bath is currently practised in metallurgical processes (Mitsubishi lances for example). Several experimental and theorical studies have been conducted in the past on this topic. However, neither detailed calculations nor experimental studies of local flow patterns have been published. In the present work, a numerical simulation of the interaction of a gaseous vertical descending jet and a liquid surface was done, using the turbulence k-e model. There is a fair agreement between the calculated and the experimental values. The results of this study demonstrate that it is crucial that the gas jet velocity profile and turbulent characteristic are correctly formulated in order to correctly simulate the system.

Jan 1, 1999

By Melissa L. Trapani

The removal of molten products from metallurgical furnaces is one of the most hazardous and labour intensive processes in a non-ferrous smelter. The proximity of operators to the molten metal and slag during tapping and the oxygen lancing that facilitates the flow have led to many reported injuries on tapping floors. In most cases, tapholes are opened and closed periodically leading to extreme thermal cycling in the tapping assembly. As a consequence, refractory wear rates are high and unpredictable in the taphole. This paper provides a review of the current state of taphole development, and gives a methodology that is now being applied to gain a better understanding of the taphole region to allow design improvements.

Jan 1, 2002

By Michael J. Virnig

The formation of crud is a normal part of operating a solvent extraction circuit for the recovery of copper. It periodically must be removed from the circuit. This results in significant costs in terms of manpower, downtime, and loss of circuit organic. Field studies have been carried out that show that the presence of a thermodynamic modifier in the organic phase contributes to crud formation. In an effort to better understand what factors contribute to crud formation, laboratory studies involving competitive adsorption studies with model solids have been carried out. The results of these laboratory studies will be integrated with the results of the field studies to present a better understanding of crud formation.

Jan 1, 1999

By Peter Kong

This paper provides a general discussion of atmospheric-pressure plasma generation, processes, and applications. There are two distinct categories of atmospheric-pressure plasmas: thermal and nonthermal. Thermal atmospheric-pressure plasmas include those produced in high intensity arcs, plasma torches, or in high intensity, high frequency discharges. Although nonthermal plasmas are at room temperatures, they are extremely effective in producing activated species, e.g., free radicals and excited state atoms. Thus, both thermal and nonthermal atmospheric-pressure plasmas are finding applications in a wide variety of industrial processes, e.g. waste destruction, material recovery, extractive metallurgy, powder synthesis, and energy conversion. A brief discussion of recent plasma technology research and development activities at the Idaho National Laboratory is included.

Jan 1, 2006

By Emmanuel N. Zevgolis Ismene-Polyxeni Kostika

Keywords: reduction, kinetics, laterites, rotary kiln, dust In this work, the reduction kinetics of dust from nickeliferous Greek laterites is investigated. The dust is a by-product from laterite treatment in rotary kilns and it comes from washing towers, electrostatic filters and polycyclones. Laboratory made pellets from this dust were also examined. Reducibility was studied in the temperature range of 700°C to 850°C in a laboratory tube furnace. Kinetic analysis of the results showed that at lower temperature values the mixed kinetic model verifies the experimental results of dust and pellet samples. At higher temperatures (800° and 850°C) diffusion becomes the rate controlling mechanism. The calculated activation energy values verify also the above mentioned results.

Jan 1, 2005

By Takeo Fujino, Nobuaki Sato, Yarong Wang, Kohta Yamada

"Ternary mixed sulfides of some transition metals MTS3 (M=Ba, ·Pb, T=Ti, Zr) were synthesized by a relatively low temperature process using sulfur melt. The mixture of starting materials, such as, metals and/or binary sulfides and a large excess of sulfur was reacted in a vacuum-sealed Pyrex or quartz ampoule at 350- 600 °C for one to three weeks. After the reaction, the remaining sulfur was completely removed by a process composed of filtration of sulfur melt and followed dissolution in CS2• The binary sulfides impurities coexisted in the products were removed by rinsing the products in water and acetone. By using the above method, BaTiS3, PbTiS3 and BaZrS3 'Were obtained in pure form. The effect of addition of halides on the yields of these ternary sulfides were also discussed.IntroductionThere have been a vast number of studies on the preparation and physical and /or chemical properties of mixed metal oxides. As is well known, some of such compounds exhibit excellent materials properties, causing them for use in mechanical, electronic, magnetic and chemical devices. Not a few mixed metal sulfides show similar physico-chemical properties to those of the corresponding mixed metal oxides. However, the study of the mixed sulfide crystals is rather sparse mainly due to difficulties in preparing these compounds. In various methods which have been adopted for preparing mixed sulfides, the simplest method would be the solid-solid reaction of the component binary sulfides or elements. However, there are always diffusional constraints with regard to the reactions in solid phases causing it necessary to heat the reactants at sufficiently high temperatures, viz. 800-1200°C. On the other hand, some mixed sulfides are unstable at high temperatures or to change their materials properties due to sulfur nonstoichiometry and structural modification depending on temperature, i.e., synthesis of such compounds needs to be made at lower temperatures. Processing in alkali halide melts is hopeful to overcome the above problems but to obtain the halide melts the temperatures above ~ 600 °C is needed. Low temperature reaction has been carried out for the preparation of Hg1.24TiS4, which was formed by the ·combination of TiS2 and molten Hg metal at 320°C[l]. Reaction of WS2 with LiBH4 melt at 350°C yielded LixWS2[2]. These sophisticated methods, however, can be applied only to the vary special cases."

Jan 1, 2000

By K. Yamaguchi, Y. Takeda

"Partial pressure - temperature - composition correlation diagrams of the Ga-As, In-As, Ga-P and In-P systems were contracted based on the obtained experimental data of the phase diagram and thermodynamic properties for the III-V systems. The total vapor pressures of arsenic or phosphorus at melting point of GaAs, InAs, GaP and InP were determined as 101, 10.1, 1510 and 253 kPa, respectively, at the corresponding melting points of 1509, 1211, 1739 and. 1336K , These diagrams are applied to the analysis of the horizontal Bridgman method and the liquid phase epitaxial growth technique. On the other hand, the analysis of the equilibrium state of the. chloride-CVD process was carried out using the data of the Gibbs energy of the compounds obtained by· authors.IntroductionThe group III-V compound semiconductors ate important materials used in optoelectronic liquid high speed electronic device. The crystal growth of the III-V compounds can involve processes that require contact between the solid, liquid and vapour phases at near equilibrium condition. Examples of processes that involve contact between the solid, liquid and vapour phases include bulk crystal growth such as the horizontal Bridgman and the liquid encapsulated Czochralski method and liquid epitaxy, and between the solid and vapor include chemical vapour deposition and molecular beam epitaxy. Therefore, the knowledge of the phase diagram and thermodynamic properties for the III-V binary alloys is essential for the analyses of crystal growth techniques of III-V compounds.For these reasons, a series of different · types calorimetric measurements had been carried out: (1) The heat contents of alloys for the Ga-As, In-As, Ga-P and In-P systems by a drop calorimeter [1;2,3]; (2) the heats of formation of the GaAs, InAs, GaP and InP compounds by a twin solution calorimeter [4]; and (3) the standard entropy of these compounds by an adiabatic calorimeter [5]. Based on the third law method, the Gibbs energies of these compounds were derived from the heat capacity, standard heat of formation and standard entropy data obtained by authors. Integral molar thermodynamic quantities of the liquid III-V .alloys were also determined from combining the heat contents of alloys with standard heat of formation and standard entropy data of the compounds· by applying the thermodynamic analysis method developed by Oelsen [6]. In the present study, the thermodynamic calculations for the crystal growth processes of the III-V compound were carried out using newly experimental data of the phase diagram and thermodynamic .properties measured by authors"

Jan 1, 2000

By Sheng Dai, Yuan Lee, Haiming Xiao, J. P. Young

"There are numerous analytical applications of scatter-emission and/or absorption spectroscopy applied to liquids and solids in the temperature range of 0 to 350°C. In this paper an all-silica fiberoptic probe is described which is useful for spectral analyses from 0 to 1600 K and can be used in harsh chemical environments. The probe has been used for Raman spectral analyses of many molten salt and solid material systems to 1000°C. It has applications for such studies at higher temperature ranges. The instrumentation required along with the demonstrated and proposed applications of the all-silica probe are presented and discussed.IntroductionThere are many kinds of scatter-emission spectroscopies that are of value for analytical measurements. Fluorescence, reflectance, arc or spark emission are descriptors for some of these. Raman scatter spectroscopy is also quite a useful technique for analytical measurements.In Figure 1, we give a simplified explanation of the Raman effect. If one shines monochromatic light into a sample, light may be absorbed, exciting the sample to some virtual state. We know from experience that almost all of the light is re-emitted in the same wavelength range. This is called Rayleigh or Mei scattering and is designated in the figure by the arrows in both examples that point up and down from the same lower energy state. A very small percentage (the order of 10-4%) of the monochromatic light is re-emitted leaving the sample at a vibrationally-excited state. Thus, this light is at a distinctly lower energy compared to the exciting radiation. This is called a Stokes shift and is represented in the left-hand example by an arrow descending to a more energetic vibrational state. If the sample is not at a temperature of absolute zero, some of this vibrationally excited state will be thermally populated. That portion of the sample still absorbs and re-emits exciting radiation as Rayleigh scattered light, but a small percentage of the exciting light is re-emitted as the sample relaxes to the lower vibrational state. The energy of this light is of higher energy and is called an anti-Stokes shift, depicted in the example to the right. Notice that the energy separation of the Stokes or anti-Stokes shifted emission from that of the exciting radiation is the same, and expressed in ~cm-I. The intensity of either shifted emission is a function of the population of the vibrational energy states; therefore, the ratio of the intensity of Stokes to anti-Stokes signal varies with absolute temperature. We will come back to this point later."

Jan 1, 1997

By Kunihiko Takeda, Kimio Imaizumi, Tsuyoshi Arai

"The study on the preparation of mono-dispersed liquid droplet was performed using ultrasonic as one of the steps of producing the perfectly mono-dispersed particle. The ultrasonic system was a 33.6kHz ultrasonic generator, an amplifier, an electric distortion element, and a bolted Langevin type horn installed in .a cell. For the first time, a liquid pillar under a nozzle of the cell ·was stably formed. Then, dense and coarse parts were alternatively constructed by oscillating the wavelength of the ultrasonic.· The diameter of those liquid droplets were found to be· perfectly uniform, therefore, it was measured by ""multiplex photography"" using a synchronized stroboscope with the ultrasonic.- From the results, more than 30,000 of perfectly uniform liquid droplets in 1 second were observed by this method.IntroductionRecently, research on the control of physical form is done in various fields of industry. Some examples are the processing technology of the minute compound material of micro-machines and integrated circuits, and the form control of molecule size like catalysts. There is a need for such material to take on various forms in correspondence to its use. ""Form control"" as used in this study will indicate ""research on physical chemistry factors which determine the size of the material"" and will refer to the contour uniformity of comparatively little particles. A well-known method of preparing particles is to spout a mist of liquid and slurry from a nozzle l) 2). Particles for metals, catalysts and food have been prepared by this method. In this case, although an approximate particle diameter can be decided by controlling the nozzle diameter and the violent outflow velocity, it is not easy to completely control ·the contour and to prepare a particle with uniform diameter. ·However, the preparation of perfectly uniform particles is necessary for solders for the adhesion of electronic wiring 3), ion exchange resins4), catalysts and so on. Large quantities of fine particles and super-fine particles are generated when manufactured in the usual way. Large quantities of these fine· particles and super-fine particles have polluted the internal and external' environments of factories. The products yield' ·decreases, also. From such a background, this study examines the preparation of perfectly uniform particles that could be· collected -100% as products. Recently, NASA has succeeded in the preparation of perfectly uniform particles in zero gravity 5). But the preparation of 'perfectly uniform particles by this method is difficult, and it can not be used in general industry"

Jan 1, 2000

By Carlos Maurício Fontes Vieira, Sergio Neves Monteiro

"A ceramic body traditionally used to produce bricks and roofing tiles with kaolinitic clays was reformulated by the addition of sand and illitic clay. The objective was to obtain a ceramic product with better technological properties. Specimens were made by uniaxial press-molding at 20 MPa and then fired at 850, 900 and 950°C. The determined technological properties were: linear shrinkage, water absorption and flexural rupture strength. The results showed that both sand and illitic clay contribute to reduce the water absorption of the industrial clayey body. With respect to the flexural behavior, it was observed that the incorporation of sand decreased the mechanical strength. On the other hand, the illitic, incorporated in an amounts of 30 wt.% contributed to increase the mechanical strength of the clayey ceramic.IntroductionCeramic bodies industrially fabricated in the county of Campos, north of the State of Rio de Janeiro, in Brazil, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral in nature, associated with high plasticity and elevated weight loss during the firing stage. Due to the excessive plasticity of the ceramic bodies, dimensional defects, which occur after drying and firing are usually obtained. Moreover, the kaolinitic nature and the presence of aluminum hydroxide (gibbsite) confer a refractory behavior to the local clays, which impairs sintering during the firing operation. In the case of clay ceramic products for civil construction, this results in greater porosity associated with elevated values of water absorption and low mechanical strength [1,2]. To avoid these problems, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative.As an alternative to reduce the plasticity of clayey ceramics sand, which is predominantly constituted of silica, can be used. The incorporation of sand in amounts of up to 25 wt.% to a clayey ceramic body used for roofing tiles fabrication was studied by Vieira et al. [3]. In that work specimens were prepared by extrusion and fired at 850°C. The results indicated that in the pre-firing stages the sand improved the workability of the investigated clayey ceramic body and facilitates the drying stage. It was also observed that the incorporated sand significantly improved the physical and mechanical properties of the clayey ceramic after firing. On the other hand, the apport of flux oxides could be done by the use of illitic clays that have a higher amount of alkaline oxides in comparison with the kaolinitics clays."

Jan 1, 2013

By Chu Yong Cheng

The solvent extraction (SX) processes of the three pressure acid leach (PAL) nickel plants in Western Australia have been reviewed. The use of intermediate precipitation, solids/liquid separation and re-leach in the three W A nickel plants make these processes complicated and costly in capital and ?operation. The research work carried out by the SX group at the AJ Parker Cooperative Research Centre for Hydrometallurgy I CSIRO Minerals has led to the development of direct solvent extraction (DSX) processes to recover and purify nickel and cobalt from leach solutions. The simplicity of the process flowsheets and the expected savings in capital and operating costs are the major advantages of the new DSX processes over the reviewed processes. By using a new synergistic organic system in semi-continuous tests with a pilot plant leach solution (after iron precipitation) from BHP-BiIliton Stainless Steel Materials, the metal values (Ni and Co) together with zinc and copper were separated from the major impurities (Mn, Mg and Ca, together with Cl) in the first SX circuit. The co-extracted manganese, magnesium and' calcium were easily scrubbed out. After stripping, the metal values (Ni and Co) together with zinc and copper were concentrated, resulting in a much smaller second SX circuit and equipment in the down stream processes. The extraction and stripping kinetics of the metals with the new synergistic organic solution were very fast. The extraction and stripping almost reached steady state within 0.5 minutes. Semi-continuous test work with a synthetic leach solution, a cobalt pilot plant leach solution from Peko Rehabilitation Project Pty Ltd and a synthetic solution to simulate a concentrated laterite leach solution from BHP-Billiton Stainless Steel Materials showed that manganese, calcium, copper and zinc can be effectively and efficiently separated from nickel, cobalt and magnesium by extraction, scrubbing and stripping. This led to the development of another DSX process using D2EHPA to recover nickel and cobalt from leach solutions.

Jan 1, 2003

By Manfred K. Walther

"Tests were conducted on instrumented plates cast in the Abex Experimental Foundry to compare recorded solidification histories with results computed for corresponding models simulated with the C.A.S.T. program. The first plate was cast of low alloy steel and the second of carbon steel with a graphite chill at one end. Both were cast in molds of bonded silica sand. Temperature histories were recorded in the castings, molds and chill. Exceptionally good agreement was achieved between computed and experimental data. Other investigators will find the results useful as a benchmark against which they can compare the results of their own calculations.IntroductionSince the early 1970's our foundry engineers have used both two- and three-dimensional versions of the G.A.S.T. program to gain knowledge of the solidification process [1,2,3]. Study of the computed data gave insight as to how the rigging and risering of specific castings might be changed or adjusted to improve quality and yield. New schemes based on such analyses were then recommended for implementation on the foundry floor. The degree of success of the new practice was subsequently evaluated after the part had been poured, shaken out and examined. Similar conditions were noted in the sectioned castings whenever porosity and voids had been predicted by the computations. Appropriate modifications, when found successful in the model, were applied to the process. This led to a reduction, if not complete elimination, of the defects. Such results gave credence to the use of these programs as an aid in the production of better castings.Earlier investigations on simple shapes revealed excellent correlation between output derived with the G.A.S.T. program and exact solutions. Results also compared favorably with data calculated using other codes as reported in the literature [4] and summarized in the Appendix. However, since the computer program had not been verified by direct experiment, it was decided to run instrumented tests to check the theoretical predictions with actual measurements."

Jan 1, 1986

By H. Hahn, B. H. Kear, K. Kan, S. C. Danforth, G. Skandan, W. Chang

"A new chemical synthetic process for the production of non-agglomeratednano structured ceramic (n-ceramic) powders, starting from metalorganic precursors, is described. The process combines rapid thermal decomposition of a precursor/carrier gas stream in a hot tubular reactor with rapid condensation of the product particle species on a cold substrate. Critical to the success of this Chemical Vapor Condensation (CVC) process are (1) a low concentration of precursor compound in the carrier gas, (2) rapid expansion of the gas stream through an uniformly heated tubular reactor under a reduced inert gas pressure of 1-35 mbar, and (3) rapid quenching of the gas phase nucleated clusters or nanoparticles as they exit from the reactor tube. A wide variety of metal organic precursors is available commercially, all of which can be utilized in the CVC process to produce n-ceramic powders, including single phase, multiphase and multicomponent systems.The CVC process has been used to synthesize non-agglomerated n-SiCxNy and n-ZrOxCy powders, with controlled particle size in the range 2-20 nm. Heat treatment of the assynthesized n-powders in various high purity gas streams causes compositional and structural modifications, including particle purification and crystallization, as well as transformation to a whisker-like morphology. Thus, as-synthesized amorphous n-SiCxNy particles transform to (1) cubic n-SiC particles, when heated in flowing argon at temperatures> 1350 °C, (2) hexagonal n-Si3N4 whiskers, when heated in flowing NH3IH2 at 1400 °C, and (3) cubic nSiC whiskers, when heated in flowing H2 at 1400 °C.Non-agglomerated n-ceramic powders form uniformly dense powder compacts by cold pressing, which can be sintered to theoretical density at temperatures as low as 0.5 Tm' For example, full densification ofn-Zr02 powder compacts under free sintering conditions can be achieved at 1125 °C."

Jan 1, 1994

By M. J. Bagshaw, J. D. Hunt, R. M. Jordan

"Continuous casting processes, and the roll casting process in particular, offer considerable potential to the Aluminium industry, both meatallurgically and economically.The three major limiting process problems that occur during roll casting are Centre Line Segregation', 'Sticking' where metal adheres to the rolls during casting, and 'Heat Line' formation. 'Heat Lines' are localised semi-continuous longitudinal defects, usually a few cms in width, where the cast metal leaves the roll bite partially molten. These defects occur at relatively low casting speeds when the mean slab exit temperature remains several hundred degrees below the solidus temperature. The objective of the work described here is to develop a better understanding of the roll casting process in general, and in particular, to understand the phenomenon of 'Heat Line' formation.A steady state two dimensional finite difference model has been developed to describe the roll casting process, incorporating a variable heat transfer coefficient through the roll bite. In the model the difference equations are formulated using a control volume method and latent heat is incorporated according to the Scheil equation. A Gauss-Seidel type technique is used to obtain the solution. Because the rate of heat evolution is non-linear the temperature in each box is determined by using a Newton-Raphson method. The solution for a box can be multi valued and therefore lead to instability particularly near the vicinity of the front. A stability 'criterion is presented which shows that to obtain a stable solution it is better to have long narrow boxes rather than boxes with small dimensions in both directions.The model explains why heat lines form in terms of the variable slab/roll heat transfer coefficient.Experimental measurements of slab exit temperatures are also presented. These were obtained on a Hunter twin roll caster for the binary AI-Cu system, at two compositions over as wide a range· of casting speeds as possible. The experimental results are compared with the predicted ones."

Jan 1, 1986

By Jun Zhu, Jilai Xuel, Tao Li

"Coal gangue is industrial waste containing Al2O3 and SiO2 with great recycling and reuse values. This work is aimed at extracting Al2O3 content in the coal gangue by a process of carbonthermal reduction - alkaline leaching. The Al2O3 and SiO2 contents first became a mixture of SiC and Al2O3 in the process of carbonthermal reduction, and then Al2O3 was separated by leaching in NaOH solution, thus producing the sodium aluminate solution for Al(OH)3 precipitation. The products generated at various stages in the process were inspected using XRD and chemical analysis. The effects of parameters such as reduction temperature, carbon ratio, NaOH concentration, leaching time, leaching temperature, stirring speed, etc were investigated in details.IntroductionCoal gangue is an industrial residue resulted from the process of coal mining and washing, accounting for 100 - 150 kg with 1 ton raw coal mined. The existence of coal gangue in large quantities has become a serious problem for environment pollution. On the other hand, the chemical compositions of coal gangue are Si02 and Ah03 primarily. In China, the accumulation storage capacity of Ah03 in coal gangue is not less than 600 million ton at a rough estimate, which should be considered as an abundant second resource [1]. If the alumina can be recycling and reused effectively from coal gangue, it will not only reduce the imperilments caused by coal gangue, but also yield good economic returns.Generally, the processes of extracting Al2O3 from coal gangue can be divided into acid leaching (vitriol or hydrochloric acid) and alkaline leaching (mostly NaOH) [2]. The acid leaching processes have many problems, such as lower leaching ratio, corroding the equipments, recycling the spent acid hardly, etc. The primary matter of alkaline leaching process is silica dissolving with alumina, which brings perplexing desilication process, alumina loss seriously and higher energy consumption."

Jan 1, 2011

By Tatsuo Inoue, Marnoru Mizuno, Toru Matsuoka, Kenichiro Abe

"The distribution of particle reinforcements and the residual stresses in metal matrix composite are simulated by considering the motion of particles and the solidification of matrix associated with temperature variation in the course of centrifugal casting process. In the analysis, a heat conduction equation including heat generation due to latent heat and also mechanical work as well as heat input from successively accumulated element on the air/metal boundary is solved by the finite element technique. After the movement of particles subjected to the centrifugal force and drag are analyzed, the residual stresses are elucidated by using a unified constitutive equation which can describe the behavior both in liquid and solid states. Results of the simulation are compared with the experimental data, and the validity and utility of the procedure is confirmed.IntroductionProcess simulation of metal matrix composite (MMC) is required to determine the mechanical properties of the materials and the efficient process and conditions of the fabrication. Properties of bonding matrix with reinforcements in the course of the processing, for example, affects the strength of the composite, while the final costs of the productions depends on the efficiency of fabrication. Therefore, the simulation of processing of MMC is prerequisite in order to clarify the mechanism to fabricate the material which has been expected to maintain high mechanical properties and the cost performance.Some techniques of processing MMC[l] have been developed so far. Among them, the centrifugal casting technique [2-5] has many attractive characteristics as processing of the MMC: The centrifugal casting technique makes the reinforcements such as particles or short fibers to be distributed in the radial direction by the centrifugal force acting on reinforcements due to the difference in density between reinforcements and matrix. Since the distribution of reinforcements affect the mechanical properties of MMC, the composite with functionally gradient mechanical properties can be provided by the centrifugal casting technique."

Jan 1, 1994

By Jong-Ren Tarng, Gin-Hwa Chen, Wen-ku Chang, Ke-Ming Lin, Yuan-Haun Lee

"The majority of early studies used X-ray diffraction, but this requires a model to interpret the diffraction processes. A turbostratic model has been applied by Warren, Franklin and Bacon to a wide range of materials including both soft and hard carbons. Maire and Mering applied the same methods to the interpretation of the (001) lines of a series of graphitic carbons. In our case, graphitic carbons undergone high temperature and high pressure graphitization processes have been evaluated by the same methods. It were found that most technological XRD data were obtained by a Rietveld method with the least-squares refinements could be in the simplest way since the full correction technique is very laborious. The behavior of carbon materials as it proceeds through the graphitization process is characterized by changes in the measured interlayer spacings (d) a~ a function of temperature. A series of graphitic carbons including the transformation of diamond to graphite through the process under high temperature and high pressure have been evaluated. A simple calibration equation has been established. IntroductionRecently, in battery industry, carbon materials are used as cathode in lithium ion batteries. However, graphitization of those carbon materials is concerned as if lithium ion intercalated into those carbon cathode. Both high-graphitization and low-graphitization carbon materials are suitable for this kind of application.As for graphitization, the starling materials from which carbons may be prepared vary extensively from pure chemical compounds, to mixtures containing II wide range of molecular weights, such as pitches. So its graphitizing, perhaps the most notable feature of the process, is the very wide range of temperature over which the perfection increase, unlike the more common transformations of solid state materials which occur in a narrow temperature range. The variables involved in the conversion of the initial hydrocarbon to a carbon residue, which may vary widely in final perfection, are time, temperature, stress and impurity content"

Jan 1, 1996