By R. J. Kuczynski

The U.S. Bureau of Mines Reno Research Center operated a batch pilot plant to demonstrate high-temperature cyanide leaching for recovering platinum group metals (PGM) from automobile catalysts. Approximately 1,600 kg of used pellet, monolith, and metal support catalyst containing 1,680 g (54 tr oz) of PGM were processed. Forty-five-kilogram batches of used catalyst were leached with sodium cyanide solution at 160° C for 1 h under basic conditions in a countercurrent processing sequence to dissolve the PGM. Extractions from the used pellet catalyst ranged from 94 to 95 pct for Pd, 95 to 97 pct for Pt, and 64 to 81 pct for Rh. Extractions from the used monolith catalyst ranged from 7B to BB pct for Pd, 75 to 90 pct for Pt, and 43 to 71 pct for Rh. Heating the pregnant leach solutions to 275' C for 4 h destroyed the PGM-cyanide complexes, resulting in over 99.7 pct of the PGM precipitating from solution. The PGM precipitate was predominantly a powder metallic concentrate, typically analyzing greater than 50 pct PGM. Heating destroyed cyanide to less than 0.2 mg/L. Both the pellet and monolith residues were evaluated for disposal using the EPA Toxicity Characteristic Leaching Procedure.

Jan 1, 1995

By Kota Nakashima

Residues from titanium smelting tend to contain scandium. The scandiumis discarded because no suitable process exists for its recovery from the residue. Valuable-metal recovery from discharged residue is critical for environmental conservation and to achieve a sustainable society. Since 2015, JXNippon Mining&Metals has been developing a process for scandium recovery from the residue of a titaniumsmelting process. The process consists of the following steps: scandium concentrating by classification or neutralization, selective scandium leaching, impurity removal by neutralization, solvent extraction of scandium by using D2EHPA, purification, and roasting. We optimized the above steps to achieve an effective process to obtain scandium oxide (Sc2O3). In this paper, we introduce results from the bench-scale test of the scandium recovery flowsheet developed by JX Nippon Mining & Metals.

By P. Kerr

Iron segregation is pre-dated by copper and nickel segregation processes for which the experimental methodology and reaction chemistry were established. The accepted reaction sequence for segregation involves the generation of hydrogen chloride, the chloridization and volatilization of the metal chloride, and precipitation of the metal from the metal chloride in the vicinity of carbon. Iron segregation roasting offers a potential extraction solution for processing oxide deposits with complex mineralogy or waste streams such as Minette-type iron deposits, nickel laterites, ilmenite, red mud, electric arc furnace (EAF) dust, mill scale and slag. After subsequent magnetic separation, one is left with a high grade metallic iron powder which can be marketed for powder metallurgy or briquetted to serve as a direct reduced iron (DRI) product. The non-magnetic product is typically concentrated oxides including rutile, alumina, or oxides of V, P, and rare earths, etc. that may be economically recoverable with subsequent processing. While operating conditions vary for different metals, they share the requirements of an elevated operating temperature and a mixture of oxide ore, carbonaceous additive and a chloride additive in varying amounts all in a closed reactor to allow for reducing conditions and contain the volatile chlorides. This process is then followed by some form of physical separation. Testwork performed by the authors shows promising results that may aid in future development of the process. Segregation roasting of iron will likely never displace traditional beneficiation and ironmaking technologies; however, it has great potential in niche markets where traditional technologies have failed or current technologies generate substantial waste.

By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By N. Y. Ma

Solid wastes produced in ironmaking and steelmaking off-gas cleaning systems often contain zinc. The zinc level in these solid wastes is generally too high to recycle the wastes for iron through blast furnaces, but too low to economically treat the wastes for zinc through zincrecovery facilities. The behavior, status, and distribution of zinc in the ironmaking and steelmaking off-gas cleaning systems have been analyzed from three aspects: thermodynamics of zinc condensation, oxidation and deposition, correlation of zinc concentration with particle size and density, and aerodynamics of dust particles in the off-gas cleaning systems. Theory and supporting data show that spontaneous separation of zinc from iron-bearing dust occurs in the ironmaking and steelmaking off-gas cleaning systems. Dry off-gas cleaning systems provide the most favorable conditions and environments for zinc to separate from the dust. If highefficiency dry separators were applied and appropriately arranged in the off-gas cleaning systems, zinc would be concentrated, and the majority of the solid wastes could be recycled for iron recovery through blast furnaces.

Jan 1, 2008

By D. Lui, B. G. Thomas, B. Ho

"Results from mathematical models and plant experiments are combined to quantify the effect of transverse depressions and oscillation marks on heat transfer in the continuous casting mold. A heat transfer model has been developed to calculate transient heat conduction within the solidifying steel, coupled with the steady-state heat conduction with the continuous casting mold wall. The model features a detailed treatment of the interfacial gap between the shell and mold, including mass and momentum balances on the solid and liquid powder layers. The model predicts the solidified shell thickness down the mold, temperature in the mold and shell, thickness of the resolidified and liquid powder layers, heat flux distribution down the mold, mold water temperature rise, ideal taper of the mold walls, and other related phenomena. The important effect of non-uniform distribution of superheat is incorporated using the results from previous 3-D turbulent fluid flow calculations within the liquid cavity. Results from plant experiments confirm that transverse surface depressions and oscillation marks form at the meniscus and move down the mold. Measurements of mold thermocouple temperatures and breakout shell thickness were used to calibrate the models. The results indicate that the surface depressions and oscillation marks are filled with mold flux, but still have a significant effect on decreasing heat transfer. The predicted mold temperature fluctuations are consistent with measurements. If the depressions become filled with air, their effect is greatly increased. These results should be useful in the difficult task of interpreting transient mold thermocouple signals for on-line quality monitoring.IntroductionMany different types of intermittent surface defects on steel slabs arise during initial solidification in the mold of the. continuous casting machine. These defects include deep oscillation marks, surface depressions, and cracks. They may lead to quality problems, such as slivers, in the final rolled product. In severe cases, breakouts may occur, where liquid steel bursts through a thin section of the shell and drains over the casting machine below the mold."

Jan 1, 1997

By Jingbo Liu, Zhimin Wang, Wenchao Li

"IntroductionThe advantages of non-stoichiometric perovskite material are highlighted in many papers[l]and many of this family of materials are well-suited to integration into microsensor devices. Among them, barium titanate is the most promising due to it's piezoelectric, pyroelectric, dielectric properties. Through modification, BaTiO3-based materials can be utilized in many kinds fields, such as surface wave probe; pholoconducting devices, field-effect transistor, permanent memory permanent storage, and ultrasonic transducerl2-3l. In this Paper, a series of BaTiO3-based polycrystals were synthesized by sol-gel processing which appears to be a very promising method for the manufacture of ceramic, because it offers significant advantages such as high purity, chemical homogeneity, controlled particle sizes of ceramics, and lower processing temperatures [4]. In a sol-gel process, alkoxides of the constituent elements show different reactivity toward water so that the preparation of multi-component homogenous system is difficult. In the experiment, inorganic salt was substituted for some of the alkoxides. Acetic acid which is employed for the solvent and catalyst, acts as donor ligand to titanium alkoxide and controls, the hydrolysis polycondensation reaction. Taking these aspects into consideration, we select the system Ba(OAc)2, , La(OAc)3, Ti(O11Bu)4 and acetic acid which is used as both solvent and homogeneous catalyst for the first time.ExperimentalA series of La3+-doped BaTiO3-based nano-crystals were prepared with sol-gel technology using various parameters. The precursor solution was prepared in the presence of barium acetate, lathanium acetate, and titanium tetrabutoxide monomer in butyl alcohol. According to the flow chart (fig. I.), Ba(OAc)2, La(OAch dissolved in the glacial acetic acid (0. lmol/40ml) in a three-neck flask were mixed with a solution of titanium tetrabutoxide monomer in butyl-alcohol(l 7ml/20ml) at room temperature and under constantly, vigorous stirring conditions. In most cases, the resultant solution was golden yellow and stable in the air. To this precursor solution, containing Ba, La, Ti in the desired ratio, water was added incrementally for hydrolysis under continuous stirring until sol was formed. After aging for more than 2 hours, sol was transformed to gel at room temperature. If heated during aging, the gel was formed in a shorter time. The wet gel was allowed to dry at 50°C for more than 10 hours. The dried gel was transparent or light yellow. In order to obtain BaTiO3-based nano-crystals, the amorphous dry gel was calcined at 600°C, 700°C, 800°C, 900°C, 1000°C respectively[5]. The ceramic humidity sensor was formed through the cold-pressed, aged, capsulated routes. The dried gels were crushed in an agate mortar and then pressed into discs of ? 1.5 X l.5mm (l.5mm diameter and l.5mm thickness), then held at about 16.5 MPa pressure for 3 min [6]. The disc was sintered at 1350°C and 1400°C for I hour respectively. During the processing, an Ag-Pt electrode was inserted in the sensor [7]. (See the flow chart.)"

Jan 1, 2000

By D. Mukerjee, Ramen Datta, Sanak Mishra, R. Veeraraghavan, K. L. Rohira

"Recent efforts at Steel Authority of India Limited (SAIL) has led to the successful development of atmospheric and marine corrosion resistant high tensile Thermo Mechanically Treated (TMT) bars with minimum specified yield strength of 50 kg.mm-2. These rebars are increasingly being used for a wide range of end-applications, namely, concrete reinforcement structures, bridges, flyovers, dams etc. Welding is an important processing tool for each of the above applications. In view of the importance of welding, a comprehensive evaluation of the weldability properties has been carried for the two grades of steels using Submerged Metal Arc Welding (SMAW) process; the most popularly used technique of welding of reinforcement bars (re bars).Implant tests were conducted to assess the cold cracking susceptibility of the steels. The static fatigue limit (SFL) value, determined for the atmospheric corrosion resistant (Cu-TMT) rebars under no preheat and no rebalcing conditions was found to be 63.8 kg mm-2, which was significantly higher than the Minimum Specified Yield Strength (MSYS) (50 kg.mm-2). This indicates adequate resistance to hydrogen induced cracking (HIC). On the other hand, the SFL value obtained for the marine corrosion resistant rebars (Cu-Cr TMT) under no preheat, no rebaking conditions was found to be inconsistent. Repeat of the test with fully rebaked electrodes (350°C-2h) resulted in a high SFL value (60.3 kg mm-2)_The rigidity of the structure or restraint influences the susceptibility of the weld joint to cracking. The cracking tendency increases with restraint intensity (K) of an assembly. The critical restraint intensities determined for the two steels were found to be· in excess of 1680 kg/mm.mm, indicating good welding behaviour with the following welding conditions : for Cu-TMT rebars with no preheat and no rebaking and for Cu-Cr TMT rebars with no preheat and fully baked electrodes; that is under low hydrogen levels."

Jan 1, 1998

By Jacques J. Eksteen

Metallurgical accounting around toll treatment smelters pose a number of challenges. This paper reviews the requirements for good sampling practice, and how conflicting requirements for good furnace operation and design often makes reliable closure of the metallurgical balance tenuous at best. Typical physical causes of variance and bias will be identified. The propagation of error (in the form of variance) will be discussed for a copper smelter.

Jan 1, 2006

By Gus Van Weert

Solvent extraction of iron from zinc refinery liquors has been investigated before, mainly on the MEHPA / HC1 stripping combination. Leakage of chloride into the zinc electrolyte and the costs of handling the ferric chloride eluate have prevented this option from being adopted. This work explores the stripping of the ferric loaded organic phase with nitric acid to take advantage of the possibility of regenerating up to 6N nitric acid, and clean spheroidal hematite production by autoclave treatment of ferric nitrate solution. The work was carried out with DEHPA (di 2-ethyl-hexyl phosphoric acid) in kerosine. Degradation testing proved the DEHPA to be very stable, when exposed to nitric acid solutions up to 6N and temperatures up to 70" C over a period of five days. Ferric iron was removed completely froma synthetic hot acid leach liquor, irrespective of the DEHPA concentration. Stripping the ferric turned out to be the problematic step. Although the stripping efficiency was considerable better at 50 than at 20° C, it decreased with increasing DEHPA/Fe ration in the organic phase. Eluates of no more than 5-10 g/l ferric nitrate were produced. surprisingly, nitric acid was found to be a less efficient stripping agent than sulphuric at equivalent normality and its efficacy levelled off above 4N. It was concluded that DEHPA does not appear to be the S.X. reagent to take advantage of the low cost autoclave decomposition of ferric nitrate opportunity in zinc hydrometallurgy and that another S.X. reagent, also resistant to nitric acid, but based on weaker compound formation is needed.

Jan 1, 1998

By Jose R. Parga

In mining operations, cyanidation is the ,predominant method by which gold and silver are recovered from their ores and it is recognized that cyanide consumption can be a major factor that contributes to the operating costs for such operations. Also after extraction and recovery of precious metals a certain amount of cyanide is delivered to the tailings pond and must be considered with respect is environmental problems due to the toxicity of cyanides. In this regard, the Air-Sparged Hydrocyclone (ASH) has been used as a reactor for the treatment of cyanide solutions in two ways; first for cyanide recovery by acidulation using the Mexican modification of the Mills-Crowe process and second for cyanide destruction by oxidation with the use of chlorine dioxide (ClO2). In both cases, excellent performance can be achieved using the high capacity ASH system.

Jan 1, 1998

By Torma A. E.

Biotechnological processes are considered to be cost effective especially for situations where the recovery of metals from 'Very large volumes containing trace metal concentrations (less than 10 ppm) is concerned. Microorganisms, alive or dead, or their products can be highly efficient and selective biosorbents for metal concentration. It is important that the metal bound to the biosorbent can be stripped by suitable agent(s) and regenerated for repeated use. The stripped solution should be concentrated enough to be introduced into the common metal recovery circuit. The industrial acceptance of biosorption processes is dictated by increased competitive advantage over other processes. This paper reviews the pertinent literature?, regroups the information, and points out future possibilities for the mineral and metal processing industries.

Jan 1, 1992

By Kazuyuki Kikuta

MMAJ, a govemmental organization in Japan, has carried out a 4 year project for the development of the decontamination and metals recovering technology for the fly ashes from municipal waste incineration. Heavy metals (zinc, lead and copper) are recovered as raw materials for the non-ferrous metals production, without formation of any waste materials to be disposed. More than 500 thousands tonnes a year of fly ashes generation from the municipal waste incineration has been one of the main social issues in Japan, because most of them need to be disposed to the registered areas after decontamination, and occupy 5% of the municipal wastes disposed. The segregation, flotation and chemical process are applied to the treatment of the primary fly ash from municipal waste incineration, and MF (Mitsui-type blast furnace) Process after the chlorine removal to the secondary fly ash. The main results of experiments are -About 90% of heavy metals, zinc, lead and copper, can be recovered from the primary and the secondary fly ashes to the products for the non-ferrous metals production. -Both of the leaching residue from the primary fly ash treatment and the slag from the secondary fly ash treatment can be used as a raw material for the cement production, meaning that the decontamination technology for the ashes without the landfill has been established. -Dioxins in the primary ash can be decomposed satisfactorily, and the dioxins content in the segregation furnace gas is less than O.lng-TEQ/Nm3 without any gas cleaning system

Jan 1, 2003

By Cleusa Cristina Bueno Martha de Souza

Hydrometallurgical techniques for processing metals are becoming an efficient method for recovering metals. Although batteries' manufacturers have got rid of mercury content, some efforts have been made for recovering other metals enclosed in the battery formula. This paper discusses the bench scale experiments in the purification process of leached solutions from alkaline spent batteries. After leaching process using sulfuric acid as leachant, the solutions containing Fe, Cd, Pb, MIl, Zn and K were neutralized to precipitate iron hydroxide. In a second step, the purification experiments were carried out with excess of zinc dust to try to remove Cd while Mn and Zn still remain in the solution to be recovered in an electrolysis stage. The purification experiments procedures were conducted at different temperatures and times to find out properly conditions from the viewpoint of metals removal After filtration the solutions were submitted to chemical analysis to certify the metals content extracted.

Jan 1, 2001

By Xiang Ma, Halvor Dalaker, Kai Tang, Stefan Andersson

Silicon carbide (SiC) is one of the most important non-oxide ceramic materials for many industrial applications and is mainly synthesized by carbothermic reduction of silicon oxide by coke above 2200°C. Replacing natural gas (mostly methane, CH4) for coke in SiC synthesis could considerably reduce energy consumption and CO2-emissions owing to higher carbon activity of CH4 at lower temperature. The generally accepted reaction mechanism is that SiC is synthesized through gaseous intermediate silicon monoxide, SiO. In the present study, the reaction mechanism for the SiO and CH4 gaseous mixture has been examined using atomic scale modelling. Molecular dynamics (MD) using a reactive force field (ReaxFF) has been utilized to examine the initial stages of reactions involving a gas mixture of SiO and CH4 and surfaces of SiC. The MD results revealed some interesting SiC formation mechanisms. The reaction energies of the critical intermediate species were also estimated by density functional theory (DFT) calculations and the implications for the force field parameters used in ReaxFF was discussed.

Jan 1, 2015

By Ailton S. Ferreira, Rubén J. Sanchez Rodriguez, Sergio N. Monteiro, Felipe Perissé D. Lopes, Teresa E. Castillo

"Polyester composites reinforced with natural lignocellulosic fibers have, in recent times, been gaining attention in engineering areas as lighter and cheaper alternatives for traditional composites such as the ""fiberglass"". One of the strongest, the curaua fiber, is today being considered as reinforcement of composites for automobile interior parts. In fact, several research works are currently being dedicated to curaua fiber composites since physical and mechanical properties are required for practical uses. In this work, the thermal behavior of polyester composites reinforced with up to 30 % in volume of curaua fibers was investigated by differential scanning calorimetry, DSC. The results showed endothermic and exothermic events associated with water release and possible molecular chain amorphous transformation. Comparison with similar composites permitted to propose mechanism that explains this DSC thermal behavior.IntroductionThe modem composite materials, especially those reinforced with synthetic fibers such as glass and carbon, have been used since last century to attend the demands required by most technological fields, from home appliances to aerospace [1]. In fact, fiber composites offer significant advantages over monolitic materials, such as common metallic alloys, plastic and ceramics. One of the most important is the ratio between the ultimate stress and the density, known as the specific strength. For example, in common glass fiber polymer composites, the so called ""fiberglass'', the specific strength of around 400 MPa.cm3/g is higher than any conventional monolitic material. However, drawbacks exist. The energy required to fabricate ""fiberglass"" generates large emissions of C02, which are responsible for global warming. Moreover, ""fiberglass"" is not recyclable and cannot be incinerated [2]. As a result, most synthetic fiber composites end up in landfills or contribute to rivers and oceans pollution."

Jan 1, 2011

By Wilson Acchar

The accelerated growth of urbanization processes and current environmental concerns brought to light the existing enormous quantity of construction and demolition waste (C&DW). Considering the frequent lack of adequate landfill areas available for the disposal of these materials, their use in the manufacture of ceramic products has been attracting a growing interest from researchers and is becoming common practice, with the consequent relief in public administration concerns for the C&DW appropriate management. This work describes the study of clay-based products added with C&DW collected directly from the construction industry. Samples containing up to 50 wt.% C&DW were uniaxially pressed and sintered in air in an electric furnace (950-1150 °C, 1 hour). Sintered test pieces were characterized by X-ray diffraction, apparent density, open porosity and flexural strength. The results showed that up to 50 wt.% C&DW can be added to the clay material, with no degradation in the final product properties.

Jan 1, 2009

By Xiping Chen, Wangxing Li, Jiemi Zhou

"Desulfurization methods suitable for anode-grade petroleum coke (coke for short) used in primary aluminum industry are coke desulfurization during calcination, desulfurization in soakage and desulfurization in mediums. Coke desulfurization during calcination is discussed in this paper. Influences of calcination temperature, holding time and coke granularity on coke desulfurization were discussed. Experimental results show that calcination temperature has a remarkable influence on coke desulfurization. When the temperature is high enough desulfurization ratio of coke can reach 85% only by calcination. Holding time has a definite influence on coke desulfurization, but desulfurization ratio is low at the temperature of 900~1300°C. The influence of holding time is obvious when calcination temperature surpasses 1400°C. The influence of coke granularity is smaller compared with calcination temperature and holding time.IntroductionPetroleum coke is main raw material for carbon anode in primary aluminum industry, and its weight percentage in carbon anode is about seven percent. Green coke can not be directly used for anode production because of its immanent moisture and volatiles. Green coke must be calcined in order to meet the request of anode production. Calcination is a heat-treatment process during which green coke is heated to a given temperature to remove volatiles, moisture and some sulfur. Real density, strength, electrical conductivity and anti-oxidation ability of petroleum coke can be improved by calcination and calcined coke can be received [1, 3, 4]. Sulfur in calcined coke finally goes into carbon anode. During baking or aluminum smelting, the sulfur in anode ultimately changes into SO2 and emits from anode into the atmosphere. Excess SO2 easily leads to acid rain which brings heavy pollution to the environment [1, 2]. With the development of Chinese aluminum industry, consumption of anode-grade petroleum coke increases year by year, the total consumption in 2007 surpassed 4.5 million tones and the yearly emission of SO2 from aluminum smelters has exceeded 270 kilotones. From 2005 Chinese government began to limit the emission of SO2 from primary aluminum industry, so desulfurization of anode-grade petroleum coke becomes more and more urgent. Some relationship need to be found and used to guide desulfurization of petroleum coke."

Jan 1, 2008

By Norihiro Murayama

Syntheses of zeolitic materials were carried out from coal fly ash by alkali hydrothermal treatment as part of the reuse and recycle technologies of coal ash, For the obtained zeolites, the cation exchange capacity and acid resistance, which are very important in the practical use of cation exchanger in aqueous solution, are investigated during this stufY, The cation exchange amounts of the NaP, CaP and K-CHA zeolites are measured for various cations such as K+, Na +, NH4+ Ca2+, Mg2+, Pb2+, Cd2+ and so on. The change in crystallization degree are researched as a function of pH. The simultaneous removal ability of NH4+ and PO43- in solution is examined for an example of the water purification with CaP zeolite. From these results, the characteristic and its mechanism of cation exchange are clarified for the various zeolitic materials obtained from coal fly ash.

Jan 1, 2003

By Gaifeng Xue, Lei Zhang, Aimin Duan, J. Y. Hwang, Lina Wang

"The removal of chemical oxygen demand (COD) from coking wastewater was experimentally investigated using a three-dimensional electrode reactor. The experimental results showed that the refractory organics in coking wastewater can be effectively removed by this process, and COD removal efficiency was affected by the operating parameters, such as electrolytic retention time, particle electrode dosage, initial pH, current density, aeration amount and electrical conductivity. The experimental results show that the three-dimensional electrode could have a COD removal efficiency of more than 60% and a running cost of no more than 6 YUAN (RMB)/t. This indicates the great potential of a three-dimensional electrode reactor in engineering applications as an advanced treatment methods for coking wastewater.IntroductionCoking wastewater is generated from coal coking, coal gas purification, and by-product recovery processes of coking; it is composed of phenolic compounds, heterocyclic compounds, polycyclic aromatic hydrocarbons, ammonia, cyanide, polycyclic nitrogen-containing aromatics, acyclic compounds, etc. Most of these constituents are refractory, poorly biodegradabile, toxic and carcinogenic [1-3]. Currently, coking wastewater is usually treated by different forms of A/O biological nitrogen removal processes as the primary treatment means, but the aforementioned processes are not efficient enough to meet the requirements of the National Discharge Standard in China (GB13456-1992). According to the continuous requirement on improving environmental protection for the coking industry (revised 2008), increasing wastewater utilization ratios and reducing the discharge of effluent in the coke industry have to be implemented for cleaner production and sustainable development. Therefore, advanced technologies need to be developed to treat coking wastewater and reutilize the product as industrial cooling water, which would be one of the best choices to achieve zero discharge of wastewater and reduce water consumption per ton of steel produced. In this study, a three-dimensional fluidized bed electrode reactor was adopted for the advanced treatment of coking wastewater, and the effects of operating conditions, including particle dosage, initial pH, current density, supporting electrolyte, as well as aeration amount on the COD removal rate, were investigated. Its running costs were also estimated."

Jan 1, 2012