By E. A. Román

An ion exchange pilot plant, provided by Mesco Inc., was tested for antimony control in the electrolyte at three Chilean tankhouses for copper electrorefining: Chuquicamata, Potrerillos and Enami -Ventanas. The pilot plant, with a nominal extraction capacity of 1.2 kg Sb/day, worked connected to both experimental and commercial circuits, performing a total of 310 loading and elution cycles. An innovation in this process is the use of a chelating organic elution reagent, which presents some advantages over the traditional 6N HCI. This new eluent is amenable to continuous regeneration and recycling with high recovery efficiency. Antimony removal starting at initial, concentrations of 0.5 to 0.6 g/l of Sb down to steady concentrations of 0.1 to 0.0.6 g/l Sb, resulted in the production of High Grade copper cathodes with Sb contents below 0.1 ppm. Anodic slimes showed Sb contents below 1%.

Jan 1, 1999

By Naoki Hiroyoshi

It is generally accepted that ferric ions are effective for leaching chalcopyrite as an oxidant and ferrous ions contribute to the leaching only as a source of the oxidant ferric ions. However, this paper shows that ferrous ions are more useful for leaching chalcopyrite than oxidant ferric ions in sulfuric acid solutions in air at ambient temperatures. Leaching experiments and dissolved oxygen consumption measurements were carried out with a very pure chalcopyrite and 0.001 - 1 mol dm-3 sulfuric acid solutions containing 0 - 0.1 mol dm-3 ferric or ferrous ions at 303 K. Chalcopyrite oxidation with dissolved oxygen was promoted by ferrous ions but suppressed by ferric ions. As a result, the amount of extracted copper was larger with ferrous ions than with ferric ions. Effects of Thiobacillus ferrooxidans on the ferrous promoted chalcopyrite leaching were also investigated and discussed based on the experimental data.

Jan 1, 1999

By Heikki Jalkanen

Oxygen converting of hot metal (LD/BOF) is contemplated as an object of simulation. Oxygen converting is a highly complex thermo-chemical process comprising a series of matter and energy transformation and transportation steps that makes the simulation very challenging. The basic principles of CONSIM 5 oxygen converter simulator are presented. Simulator is a comprehensive combination of a physical model with several empirical submodels describing all properties and processes that affect the final result of a converter blow, final mass and composition of steel, slag, dust and converter gas as well as the end temperature of steel. CONSIM simulator is used for simulation of series of high and low carbon steel blows. Simulated steel temperatures, oxygen consumption, blow time and iron oxide content of slag are compared with measured values. Problems of simulation and requirements for quantitative simulation of oxygen converter process are discussed.

Jan 1, 2006

By L. B. Tsymbulov

Sulphide melts formed in the course of smelting of nickel and copper-nickel feed (matte) actually are sulphide-metallic melts since sulphur contained in the melts is in deficiency with respect to metals. The level of metallization is rather relevant feature of sulphide melts and is widely used in calculating material and heat balances for pyrometallurgical processes. Despite of the above parameter? importance, the investigators have no single opinion on what should be understood under metallization level and the method of its determination. In the present study we present the results of our own experimental and theoretical researches that have allowed determination of some mechanisms of sulphide melts? crystallization. Based on the mechanisms revealed new scientifically justified approach has been offered for determining level of metallization of the components present in sulphide melts. It has been demonstrated that sulphur distribution between the melts is substantially different from generally accepted concept.

Jan 1, 2006

By Joël P. T. Kapusta

Although Peirce-Smith converting remains the workhorse in matte converting, the copper and nickel industries are still confronted with production hindrances such as tuyere blockage, excessive refractory wear and limits in the oxygen enrichment levels of the blast air. The knowledge acquired on high-pressure gas injection technology as well as the invention of the concentric tuyere for steelmaking led to the development of the Air Liquide Shrouded Injector (ALSI) technology for copper and nickel converting. Following a technology demonstration in 1997-98 with four shrouded injectors installed in a Peirce-Smith converter, Falconbridge Limited implemented ALSI Technology on a commercial scale in May 1999 as an integral part of its new Slag Make Converter at Sudbury, Ontario, Canada. The paper presents the various aspects of commissioning ALSI Technology, as well as the operating changes and injector design modifications over the five years the shrouded injectors have been in operation.

Jan 1, 2005

By Jose Luis Lopez Mendez

In May 1992, MEXICANA DE CANANEA, S.A. DE C.V. finalized the life of its Reverberatory Furnace which lasted 16 years. This created the need to prepare the Smelter for the next campaign.

Jan 1, 1994

By Z. Sun, H. A. Davies

"Current understanding of the mechanisms by which glassy and crystalline thin ribbons are formed in high speed continuous casting processes is considered. A computer model of the combined heat and momentum transfer during melt spinning has been developed. The influence of roll velocity and of heat transfer coefficient (between the melt and the roll) on the temperature and velocity distributions within the melt puddle is analysed and the thickness of the extracted ribbon computed. The relative importance of heat and momentum transfer under different conditions is assessed and differences between the casting of crystalline and amorphous strip highlighted.IntroductionHigh speed continuous casting of thin metallic ribbon and strip is currently of considerable interest both to metal processers and to those studying process mechanisms. The practical interest arises both from the potential economic benefits to be gained from a shorter and more energy-efficient production route and from the ability to obtain extended and uniform thin strip having a metastable microcrystalline or amorphous structure with enhanced or unique properties. The latter arise from the rapid solidification associated with the cooling of very thin sections of melt brought into intimate thermal contact with one or two rapidly moving heat sinks.The principal processes for casting thin strip include free jet, chill-block melt-spinning (GBMS) (1), melt drag (MD) (2), planar flow casting (PFG) (3) and twin-roll casting (TRG) (4). For the first three of these, all essentially variants of melt-spinning, melt flows through a nozzle onto the circumferential surface of a rapidly rotating roll, whereas for TRG the melt passes into the nip between two contra-rotating rolls. We shall be concerned in this paper with the single-roll melt spinning processes only. For these, a puddle is established where the melt contacts the roll surface and the length of this puddle l is a function of the process conditions, notably the circumferential velocity of the roll Us and the volumetric flow rate of the melt Q. The contact time between any point on the roll surface and this puddle, or residence time eR(= l /Us) determines the thickness of ribbon t extracted from the puddle. This thickness, in turn, partly governs the cooling rate T and the amount of undercooling in the melt and thus the microstructure of the solidified ribbon."

Jan 1, 1986

By Neng-Wen Yu, Shau-Jun Zhu, Ji-He Wei

The desulfurization process by powder injection and blowing in the RH refining of molten steel and its mechanism have been considered and analyzed. Based on the two-resistance mass transfer theory and the mass balance of sulfur in the system, a kinetic model for the process has been developed. The related parameters of the model, including the mass transfer coefficients and the effective amount of powder in the molten steel being treated for desulfurization, have been more reasonably determined. Modeling and predictions of the process of injecting and blowing the lime-based powder flux under assumed operating modes with the different initial contents of sulfur and amounts of powder injected and blown in a RH degasser of 300 t capacity have been carried out using the model. The relevant circulation rate of the liquid steel and the powder injection and blowing rate were taken to be 100 t/min and 150 kg/min, respectively. The initial contents of sulfur in the liquid steel to be treated and the amounts of powder injection and blowing were respectively assumed to be 0.007, 0.006, 0.005, 0.004, 0.003, 0.002 mass-% and 10, 8, 6, 5, 4, 3 kg/t-steel. The total treatment time for desulfurization under each mode was set up at 24 min, equivalent to eight circulation cycles of the liquid steel to be treated. The results indicated that the predictions made with this model are in good agreement with some data of the industrial experiments and practice. Injecting and blowing the lime-based powder flux with the composition of 85 mass-% lime (CaO) + 15 mass-% fluorspar (CaF2) of 3-5 kg/t-steel, it is possible to decrease the sulfur content in the molten steel to ultralow level below (5-10)x10·4 mass-% from (60-80)x 10·4 mass-%. The total treatment time needed will appropriately be 12-20 min. Intensifying the powder injection and blowing operation and increasing the circulation rate of the liquid steel may effectively' raise the rate of the process in RH refining. The model may be expected to offer some useful information and a reliable basis for determining the reasonable process parameters and help in optimizing the technology of desulfurization by powder injection and blowing in the RH refining of molten steel.

Jan 1, 2000

By James M. Fragomeni

"The mechanical behavior of an Al-Li alloy was studied and related to the extrusion processing parameters, the plastic metal flow during defonnation, the anisotropy, and the microstructure. The extrusion temperatures, strain rates, extrusion ratios, billet temperatures, and extrusion geometries were varied during processing and correlated with the microstructure and properties. The extrusion processing variables were related to the mechariicar behavior, anisotropy, and microstructure through the ZenerHollomon parameter i.e., the temperature compensated strain rate. Based on optical and electron microscopy studies it was found that regardless of the extrusion conditions, the various microstructures for the most part were unrecrystallized for both the as-extruded and the solution heat-treated conditions. Smaller grain sizes were correlated to larger Zener-Hollomon parameters. The extrusion temperature and ratio did not significantly affect the strength or ductility as did the section geometry, which had a large affect on these mechanical properties. The anisotropy of the properties varied substantially when comparing the extruded longitudinal versus transverse grain orientations.IntroductionThe extrusion process also has a substantial influence on: the microsfructure and mechanical properties of a material that is Athens, Ohio, 45701 fonned The plastic defonnation that occurs during the extrusion process alters the grain size, crystallographic texture, anisotropy, subgrain size, dislocation density and various other microstructural features. Often the material being extruded is not homogeneous, therefore variations in the microstructure and properties occur across the cross-section of the final extruded product. The mechanical properties and microstructure can also vary with length since it is hard to maintain a constant temperature throughout the extrusion process. The extrusion temperature often varies from the heat generated during the extrusion process. The demonstration material that was extruded for this .study was an aluminum alloy containing 2.6wt, % lithium and 0.09wt.% zirconium. This alloy was strengthened by heat treatment causing nucleation, growth, and coarsening of coherent metastable o' (Al3Li) precipitates in the microstructure. The ? precipitates which are a consequence 9f artificially aging the AlLi alloy, are spherical, ordered, and coherent with the aluminum matrix and impede the dislocation glide inotion during plastic defonnation. Theo particles grow homogeneously in the matrix, and have the Cu3Au (L 12)"" superlattice crystal structure. Aluminum-lithium alloys are used primarily for aerospace structural applications since they have attractive properties such as a lower density and higher elastic modulus than conventional 2XXX and 7XXX alloys."

Jan 1, 2000

By M. Neises, M. Roeb, C. Sattler, S. Stenger

"A two-step thermo-chemical cycle process has been developed and investigated. It is based on metal oxide redox pair systems, which can split carbon dioxide as well as water molecules by extracting oxygen atoms and reversibly incorporating them into their lattice. If concentrated solar radiation is used as the heat source, a promising method exists to produce synthesis gas from water and CO2. An easy way of operation is gained by the combination of a ceramic substrate as the absorber structure, which can be heated to high temperatures with concentrated solar radiation, and of a metal oxide coating which is capable to carry out the redox reactions. The performance and kinetics of a ferrite based redox material coated on ceramic substrates were investigated in a laboratory set-up. CO2 could be reduced with significant conversions. In addition, several side reactions were observed like the formation of carbon and like the Boudouard reaction.IntroductionThe search for alternative energy carriers and for processes able to reuse carbon dioxide stimulates the research for sustainable routes of alternative fuel production. In the scope of this search thermo-chemical processes combined with sources of concentrated solar energy have become more and more attractive. Ideally, the only raw materials for such processes are water (H2O) and carbon dioxide (CO2) enabling not only a process free of emissions, but also allow to reduce emissions of other processes by reusing CO2 to provide synthesis gas, which itself can be applied to produce chemical commodities or even better synthetic fuels like methanol or petrol.In contrast to the direct splitting of those raw materials, thermochemical cycles split water and CO2 in several steps and enable hydrogen (H2) and carbon monoxide (CO) generation at temperatures controllable by today’s technical equipment. One of the most interesting thermochemical cycles is a two-step process using metal oxide based redox systems. During the first step of this cycle (the regeneration step) the metal oxide is reduced setting some of its lattice oxygen free according to reaction (1). In the next step (the splitting) the reduced and activated material is oxidised by withdrawing oxygen from water and CO2 and at the same time hydrogen and CO is set free according to reactions (2a) and (2b) respectively."

Jan 1, 2011

By L. M. Abrantes, A. P. Paiva

"A brief review of some innovative methods for the direct recovery of metals from loaded organic phases is presented; emphasis is given to electroreductive stripping and cementation, which are described and illustrated by examples: of current research. The recovery of silver using a two-phase electrolysis - by direct application of an electrical potential to a mixture of a metal loaded organic phase· containing Cyanex 471X, obtained by solvent extraction, and a stabilized sodium thiosulfate solution - is more extensively discussed. The overall efficiencies are analyzed and compared with data obtained by conventional stripping procedures. Some preliminary results achieved for the recovery of the precious metal using galvanic stripping, applied directly to similar organic solutions and involving zinc and iron powders as reducing agents, are also evaluated.Introductory ReviewThe application of hydrometallurgical methods to the recovery of metal values from ores and concentrates has been receiving a growing interest, either from researchers or from the mining industry [1].For the concentration / purification of the relatively low concentrated metallic solutions resulting from the leaching of those raw materials, solvent extraction (SX) is a well established technique [2]; the loaded organic solvent is then conventionally contacted with a suitable aqueous solution, the metal in its final form being usually recovered from this solution by electrowinning.As an efficient and / or selective stripping is sometimes difficult to achieve, depending on the specific characteristics of the system under consideration, some alternative procedures have been analyzed in order to overcome this problem. One of the chosen routes, mainly developed by Hirai and Komasawa, is to promote the reduction of the desired metal species in the organic phase, in such a way that the stripping stage becomes feasible; for the selective stripping of vanadium from a solvent containing a mixture of vanadium and molybdenum, the authors successfully used reductive [3], electro-reductive [4,5] and photo-reductive [6] techniques. The two latter methodologies have also been applied to the recovery of europium from a solvent containing europium, samarium and gadolinium [7,8].However, further processing is necessary to recover the metal in its solid state; therefore, methods causing the direct reduction of the metal species in the organic phase to their fmal metallic form would be of interest, as an intermediate step would be avoided"

Jan 1, 1997

By S. C. Flood, J. D. Hunt

"The columnar-equiaxed transition (CET) has been studied numerically under unsteady-state conditions using mathematical models that: (i) include a non-equilibrium undercooling at the columnar front;and(ii) describe the simultaneous evolution of the columnar and equiaxed zones.The results are discussed and compared with those produced by a steady-state analysis.IntroductionThe majority of the previous work on the columnar-equiaxed transition (CET) has concentrated on the production of equiaxed nuclei, regarding this as being the critical step in the formation of an equiaxed zone. Recently, the growth of equiaxed grains has been considered and this is not unreasonable because, for an equiaxed zone to be present, the grains must grow as well as nucleate. Since the growth rate of the grains will be determined by the thermal environment at and ahead of the columnar tips, it was decided to model the liberation and flow of heat during solidification to discover whether the various trends in the columnar range might be explained by their effect on the temperature profile throughout the casting. The models presented here for the solidification of a casting are the first to include the latent heat liberated ahead of the columnar front. Burden and Hunt (1) consider its effect only qualitatively, and although Lipton et al (2) adopt a criterion for the CET which is based on the thermal interaction of the columnar and equiaxed grains, they do not actually include the latent heat in their calculations.It can be argued that the latent heat liberated by the equiaxed grains in the bulk will retard the columnar dendrites in a casting: once the equiaxed grains are sufficiently well-established, the latent heat that they evolve could slow down the columnar growth to such an extent that the equi axed would dominate. Alternatively, the latent heat produced by the equiaxed grains might suppress further equiaxed solidification by raising the bulk temperature. The nature of the thermal interaction between columnar and equiaxed growth is not obvious, and because it is dependent on the material parameters and the dimensions of the system, it cannot be considered effectively in a qualitative way but has to be studied quantitatively: hence the need for the mathematical models discussed in the following pages. The results of the models are discussed in the light of a steady state analysis."

Jan 1, 1986

By Edilson Marques Magalhães, Danielly Da Silva Quaresma, José Antônio da Silva Souza, João Nazareno Nonato Quaresma, Emanuel Negrão Macêdo

"The production of alumina from bauxite using the Bayer process generates the residue known by red mud. This material can be used as a source for concentration and recovery of valuable metals such as titanium. The greatest difficulty of concentrating titanium compounds is the large amount of iron oxide present in red mud > 30% by weight. This paper shows the extraction of the iron oxide, increasing the concentration of the titanium compounds. The red mud is leached with H2SO4 at 30% concentration and temperature range of 60°C, 80°C and 90°C. Analysis of the leached and concentrated was made to verify the effectiveness of the iron oxide extracting process and the titanium compounds concentration viability.2- IntroductionIn the state of Para is located the Industrial Unit Alumina of North of the Brazil S/A (Alunorte), created to produce and commercialize alumina, aluminum oxide, Al2O3. The ALUNORTE with Aluminum Brasileiro S/A (Albras) and Mining Rio do Norte S/A (MRN) complete the production cycle of aluminum in the state. Although the production of alumina has a importance great for the socio-economic status, as in any area other, generates a amount large of waste, thus causing environmental impacts. Pará State has produced 25 million tons of bauxite (Pinto, 2010), of which 60% were transformed into alumina plant in Pará and Maranhão by ALUNORTE by ALCOA, generating approximately 9,000,000 tons of waste known as Red Mud (RM). Due to the high reactivity this material is considered dangerous, and currently there is no operating process capable of reuse all the material produced at any refinery. The search for industrial processes in order to reuse these wastes can contribute to reducing the overall impact of the production process of alumina. In this context, this paper estudied, within the research line of Solid Waste valorization the mining industry and metallurgy, a process that makes possible the red mud as a source of raw material, in other words, seeks to maximize the use of red mud as raw material for concentration and or recovery of titanium compounds in both the crystalline form of anatase, rutile and ilmenite, avoiding the predatory extraction of natural resources of these materials. Applying definitely the concept of self-sustainability of the mining industry and metallurgy."

Jan 1, 2012

By Kimio Itagaki, Torn Matsumoto, Makoto Ohtsuka, Kentarou Harada

"The structure and hydrogen-absorption properties of LaNis thin films were investigated in the present study. LaNis thin films were prepared by a sputtering method with a radio-frequency power, Ws, of 50 -400 Wat substrate temperature, Ts, of323 -573 K. Nickel content of the films decreased with increasing Ws, however, there was no dependence on Ts. At low Ws and low Ts, amorphous films were deposited. In other conditions, the films were polycrystalline. The films prepared at high Ws and low Ts, or at low Ws and high Ts, exhibited only a (h k · 0) peak in the X-ray diffraction profiles. This indicates that the c-axis of crystalline films was oriented parallel to the substrate plane. At high Ws and high Ts, the films with columnar structure were obtained. Hydrogen-absorption capacity of the thin films increased with increasing Ws. The pressure plateau did not appear on the pressure-composition isotherms. The films deposited at high Ts represented a higher equilibrium pressure.IntroductionThin films of hydrogen storage alloys can be applied for an electrode of rechargeable battery or fuel cell, a filter for H1 purification and various kind of sensor. Some studies on the preparation of the thin films of LaNi5 intermetallic compound, which is a typical hydrogen storage material, have been done hitherto. Adachi et al. , 2) and Sakaguchi et al. 3) prepared amorphous and crystalline LaNi5 thin films using flash evaporation of alloy powders and measured the pressure-composition isotherm for the prepared film utilizing a quartz crystal mass monitoring (QC:MM) method. It was found that the prepared amorphous film absorbed hydrogen without disintegrating into the powders and the hydrogen-absorption capacity of the films increased with the degree of crystallinity. Sakai et al. 4) reported that the maximum hydrogen storage capacities of amorphous and crystalline LaNi5 thin films, fabricated by a RF sputtering method using combination targets, were about 40 mA h g-1 (LaNisHo.7) and 160 mA h g-1 (LaNi5H2.6), respectively. Uchida et al. 5, 6) prepared LaNi5 thin films using flash evaporation of alloy powders and measured volumetrically the pressure-composition isotherm for the prepared film. It was reported that the hydrogen-absorption capacity of the films changed by the annealing treatment."

Jan 1, 1998

By Viktor. P. Popov, Oleksandr. V. Derev'yanko, Oleksandr. I. Raychenko

"This paper is devoted to scrutiny problem of obtaining electro-contacts by electro-discharge sintering technology. A new unconventional method of electro contacts production (on Aggraphite base) can yield essential optimization resource.Review of three electro-technological methods of processing contacts materials is presented:- using graphite powder cladded by Ag;- mixture of graphite powder(which is a non-cladded powder) with Ag powder and addition of Fe powder particles;- method of infiltration of melted Ag into graphite piece without deformation and rupture of object.This technological approach can give the possibility to increase of compression strength of electro-contacts materials up to 340 MPa and more under conditions of additional reinforcing components (for example, by Fe).IntroductionThe electric current can be an active ""participator"" of the powder metallurgy technology [l]. At the passage of electric current through powders or some powder mixtures the phenomena including phase transformations arise. Here such effects, which are observed in the Ag-graphite and Ag-Fe-graphite powder mixtures and in the pair Ag-porous graphite, are described.The Ag-graphite composition materials (CM) are used, for example, as electric contacts [2, 3]. Since a material being produced is destined for the contacts it is necessary to take into account the following aspects: commutating current, its character and voltage, active or reactive character of working load, geometrical dimensions of contacts, quantity and frequency of switching on and switching off, pressure on contacts, distance between contacts, method of arc control, surrounding medium, its content, pressure and temperature. Thus, these and, maybe, choice of some other circumstances influence design, materials and production technology of contacts. The range of problems concerned dictates such steps as alloying of contact materials, optimization of structure, selection of kind of graphite, its connection with metal [4-10]. It is expedient to recall the main procedures of the first stage of the conventional technology: dosage of the initial graphite powder and binder-phenolic resin plastic varnish (for example, Bakelite), mixing, densification, thermal treatment, crushing, grinding, sieving, drying, dosage of grained graphite, dosage of the initial silver powder, obtaining of the silver salt solution, settling of salt, filtration, washing, drying of the cladded graphite powder, thermal treatment, obtaining of the graphite powder of particles cladded by silver. The second stage of the convectional technology starts by obtaining of the cladded graphite powder and finishes by annealing of the pressed blanks (Fig. 1)."

Jan 1, 2004

By Renxing Li, Yongyong Gong, Yufeng Cheng, Zhenxing Yin, Xin Cao, Qijie Zhai

"This paper investigated the refinement effect of pulse magneto-oscillation (PMO) on the solidification structures of medium carbon steel S45C in metal mould. The induction coil was positioned at the middle of ingot. The results showed that solidification structure of the treated ingots was remarkably modified with a transformation from well-developed dendritic structures to small dendritic structures or globular structures compared to the untreated ingot. The area fraction of modified microstructure regions reached more than 80 percent. A further experimental investigation had been done to understand the influence of refinement effect on the solidification structure under different mould size. Theoretical analysis demonstrated that the mechanism for the refinement of solidification structure was that PMO promoted nucleation near the mould walls and changed the interface temperature gradient and concentration gradient in liquid, eventually leading to a transition from the columnar crystals to the equiaxed crystals.IntroductionIn recent two decades, the electromagnetic processing of materials (EPM) has been widely used in many fields such as ironmaking, steelmaking, and solidification processing [1-6], where EPM can control melt flow, modify melt shape, reduce macro-segregation and refine microstructure. Pulse magneto-oscillation [7-9] (PMO), as a novel technique of EPM, has a remarkable effect on grain refinement and high potentiality to be used in industrial production. Compared with ultrasound refinement technique, PMO can be easily employed to metal solidification processing for long time in no contact with hot metal liquid by using a water-cooled coil. Another important advantage is that PMO needs smaller energy compared to pulsed magnetic field which needs a very high current to obtain a strong magnetic field to get a satisfactory effect. These advantages mentioned above are beneficial for industrial application, which make it potential to be widely used in future. Gong et al. [7] have studied the refinement effect of PMO on pure aluminum and find that PMO can significantly modify the solidification structure of pure aluminum. Li et al. [9] have reported the effect of temperature field on solidification structure under the influence of PMO. On the basis of these works, this paper has studied the effect of PMO on solidification process of medium carbon steel S45C in a metal mould, which can also provide some information for industrial application of this new technique."

Jan 1, 2012

By Bing Hu, Zhu-Cheng Huang, Guang-Bin Xia, Hu Peng, Hua Wang

"The temperature rising characteristics and reaction of the reduction of iron oxide pellets with anthracite fines were studied using a MW-L0316V microwave oven and Leica-DM-RXP polarizing microscope. The results show that iron oxide pellets and anthracite fines have good microwave absorbing properties, and high temperature and reducing atmosphere in a relatively short time for reduction of iron oxide pellets can be achieved. The reduction reaction, which follows the unreacted core model, is rapid and the metallization increases from 13.41% to 56.57% as the reduction end point temperature increases from 850oC to 950oC. The iron is formed, fine grain crystals of iron are transferred and the contraction of metal phase occurs firstly at the surface of pellets, which hinders the reduction reaction at the center of pellets. The rate of reduction reaction increases slowly as the reduction end point temperature increases from 950oC to 1050oC.IntroductionIron ore direct reduction can be divided into gas-based reduction and coal-based reduction. Owing to the effect of the resource and the related economic benefits [1, 2, 3, and 4], the development of gas-based direct reduction technology is restricted, but the development of coal-based direct reduction supported by the relevant industrial policy has very good prospects for application.As a source of clean energy, in China microwaves have been applied in many fields [5, 6, and 7]. Chen Jin studied the reduction of carbon pellets under microwaves, and has made some progress on reduction kinetics and reaction mechanisms. Other countries also have related research in this field [8 - 15], for example, Kotaro Ishizaki and Kazuhiro Nagata have done research on the reduction reaction of carbon magnetite heated by microwaves. The research shows that Fe3O4 is deoxidized to FeO at about 800oC, and FeO is deoxidized to Fe at 1000oC-1025oC. Due to the very good heat absorbing properties of iron oxide pellets and anthracite fines, the selective and rapid heating of microwaves can rapidly raise the temperature of pellets and anthracite, and the iron oxide pellets can be rapidly reduced. In order to provide enough theoretical basis for direct reduction by microwave heating, this paper studies the temperature rising characteristics, behavior of the reduction reaction and the changes of the iron oxide pellets and anthracite in the microwave field."

Jan 1, 2011

By Hai-Xing Fang, Chao Liu, Tao Zhang, Bing Xie, Hong-Yi Li, Cui Li

"Hongge Ore, a kind of vanadium-titanium magnetite ore containing high content of chromium, is valuable resource for extracting Fe, V and Cr in China. During present processing of the ore, vanadium and chromium were both concentrated in slag, leading to higher content of chromium in the vanadium slag than that of common one in Pan-Steel. Mineral phases and characteristics of spine! crystals, which influenced greatly subsequent roasting process, in the vanadium slag under different cooling conditions were investigated by using XRD and SEM/EDS. Results showed that vanadium slags containing various contents of chromium were composed of spine!, in which V and Cr were both concentrated, olivine and pyroxene. Growth rate of spine ls decreased sharply below 1350°C. The non-isothermal crystallization process could be described by modified Avrami equation and Ozawa equation. Avrami exponent and Ozawa index were calculated and growth mechanism of spine! crystals was discussed.IntroductionVanadium (V) as well as chromium (Cr) is important non-ferrous metal widely used in materials and chemical industries [1, 2]. Especially, both of them are important alloying elements for the production of high alloyed steels to achieve desired physical-chemical and mechanical properties. Vanadium-titanium magnetite ore in Panzhihua-Xichang area (China) is an important raw material for extracting vanadium. During the extracting process, vanadium is firstly reduced into hot metal and then concentrated in slag phase by blowing oxygen into the hot metal in converter [3]. This kind of slag containing 5~20 wt% V20 3 are usually roasted with sodium or calcium salts and then leached to obtain vanadium containing solution and final products. Current vanadium slag obtained from normal vanadium-titanium magnetite ore contains low content of Cr20 3 and chromium extraction is thus ignored. However, chromium content in the vanadium slag would be increased intensively when the Hongge Ore used, which is also important vanadium titanium magnetite in Panzhihua-Xichang area containing 0.2~0.8 wt% Cr203. Therefore, this kind of vanadium slag with high content of chromium would also be important sources for vanadium and chromium extraction. According to previous work [4], both vanadium and chromium could be extracted from vanadium slag with high content of chromium by salt roasting and leaching, which is illustrated in Fig.1."

Jan 1, 2013

By Tzu-Chien Lin, Jack Tsai, Ming-Yu Lin, Der-Ray Huang, Jiin-Sen Chen, Jing-Xuan Lin

"In this paper, some DVD-R discs have been selected for long time light exposure test and high temperature and humidity test. Generally, recordable media under long time light exposure maybe be defected seriously. If we use Jitter value 8% as a reference to determine the life time of DVD-R samples, some discs defect after 5 hours of light exposure while some discs can endure over 25 hours. Also if we use reflectivity 45% to determine the life time, some discs defect after 30 hours light exposure while some discs can endure over 40 hours. From our results, the good samples show good characteristics of PI error. The absorption spectrum of recordable media is a good reference to justify the quality of dye media. These results can be used to estimate the life time of recordable discs.IntroductionIn general, the life time of DVD-R with a layer of organic dye recording layer is required for preservation in decades. In addition to optical characteristics and thermal properties, we still need to consider the stability of the dye in recording media. The presentation of the color on organic dye is not only related to the material's property but also related to the light exposure. In this study, we focus on the absorption characteristics and reflectivity of organic dye in optical recording layer after light exposure. The optical properties of discs depend on the functional groups and molecular structure [1]. According to ""DVD Specifications for Recordable Disc (DVD- R)"", the reflectivity should higher than 40%. From measured reflectivity, we can confirm that the important issue is whether dye be affected by light exposure or not. Because each specific functional group absorbs the specific spectrum, we can check the characteristics of functional groups from their UV/Visible Spectra. We also use High-performance liquid chromatography (HPLC) to detect the different components of dye on the recording layer [2]. The jitter value test is to test the error cause by digital signal of recording media. If we use jitter value 8% as a reference to determine the life time of DVD-R samples, the purpose of this study is to investigate the jitter values of recording media after high light exposure and high temperature/humidity test. The results of these test will be helpful for the development of long-life optical storage media."

Jan 1, 2012

By D. F. Liub, Z. Y. Liu, W. Y. Xue, Y. F. Shenb, Y. D. Wang

"The microstructure characteristics and deformation behavior of ultrafme grained (UFO) 304SS fabricated by accumulative rolling and armealing have been investigated by means of tensile tests, electron-backscatter-diffraction (EBSD) and transmission electron microscopy (TEM) techniques. The volume fraction of martensite phase decreases with increasing armealing temperature. In the grain sizes ranging from 300 nm to 10 µm, the strength held Hall-Petch relationship. The sample with an average grain size of 300 nm exhibited extra high yield strength of 1700 MPa and a tensile strength of 1780 MPa, while the elongation retains 12%. The limited uniform elongation in the UFO materials could be explained in terms of plastic instability. Very interestingly, for the bulk material with an average grain size of 1.200 µm, the high yield strength and uniform elongation were simultaneously achieved to be as 1000 MPa and 18%, respectively.IntroductionUltra-high strengths have been achieved in elemental metals by employing heavy plastic deformation, or by creating ultra-fine-grained (UFO) structure. Here UFO materials are defined as polycrystalline solids with property-controlling microstructural features below the 1 µm level. Typical processing routes include severe plastic deformation (SPD) [1, 2], which decomposes the grains through dislocation accumulation and reorganization (polygonization). Several different kinds of SPD process for bulk materials are typically as equal-charmel angular pressing (ECAP) [3], high-pressure torsion (HPT) [4] and accumulative roll-bonding (ARB) [5]. One of the main motivations for such a push for the very small grain sizes stems from the expectation of unprecedented mechanical strength, as predicted by the well-known Hall-Petch relationship that projects a continuous rise of strength with decreasing grain size [6]. However, these ultra-high strength metals no longer have the high ductility typical of their conventional coarse-grained counterparts, because the undesirable inhomogeneous deformation on the microstructure level can lead to the early onset of failure, severely limiting the useful ductility [2]. Recently, the interesting strategies have been performed to increasing simultaneously the ductility and strength ofUFG pure copper and nanostructured alloys by Zhao et al [7, 8]. In a pure copper, a high ductility has been achieved without sacrificing strength by introducing a high density of pre-existing twins and a large fraction of high-angle grain boundaries. Their encouraging results trigger our motivation to obtain high strength and ductility from the commercially bulk material."

Jan 1, 2013