By Masayasu Kawahara

"The extraction and separation of nickel, cobalt and copper were investigated with a solvent impregnated resin which was produced from UX84-I and XAD-4. The extraction behavior of metals with the solvent impregnated resin is similar to that with solvent extraction. The extraction ability of solvent impregnated resin improves when using finer particle resin and with a higher concentration of extraction solvent.IntroductionSolvent extraction is well known-as a method for separation of metallic elements in solution. However there are problems with intermediate phase and solvent loss. Ion exchange resin is also used in hydrometallurgy, but it is not fit for separating a large quantity of metals. Amberlite XAD-4 resin is known as a absorption agent of organic matter in water. It is expected that the resin which has the ability of extracting metals can be made by absorbing organic extractant on XAD-4 resin In this study, solvent impregnated resin (SIR) was produced from LIX84-I and XAD-4, and extraction and separation of nickel, cobalt and copper were conducted using SIR. The extraction properties of SIR were investigated, and a comparison between ordinary solvent extraction and SIR was made.Experimental ProcedureAmberlite XAD-4 was used as absorption resin for the organic extractant in this study. The physical properties of XAD-4 are shown in Table I. Amber lite XAD-4 has a large surface area and shows good ability to absorb organic matter in water, but the: resin does not have the ability of exchanging metallic ion."

Jan 1, 2000

By Chikabumi Yamauchi, Mitsuru Tanahashi, Jutaro Miura, Takaharu Iwadachi, Toshiharu Fujisawa

"Tue oxidation behavior of molten Cu-Be alloys was investigated by exposing· the molten Cu-Be alloys to various Ar-O2 atmospheres to control the oxygen partial pressure, PO2 = 10 ~105 Pa at 1423 K. The following results were obtained:• The oxygen · partial pressure in gas phase affects the morphology of the oxide formed on the surface of the alloy and · the oxidation rate of beryllium.• At lower oxygen partial pressure, a molten Cu-Be alloy is covered with a homogeneous and compact internal layer of BeO. Thus, the beryllium oxidation rate can be minimized.• By adding a small amount of calcium or zirconium into the molten Cu-0.5 mass% Be alloy, a protective BeO layer is formed even at higher oxygen partial pressure. Thus, the beryllium oxidation rate can be reduced.IntroductionCopper-beryllium (Cu-Be) alloys are well recognized for their unique properties, such as high electrical conductivity, high strength, high fatigue strength, excellent properties at elevated temperatures, good formability and good corrosion resistance. .This extraordinary collection of properties are the reasons why Cu-Be alloys are expected to be ""Key-materials"", which are necessary to further advance science and technology and to be applied in.various fields such as electronic devices, machine parts, repeater housings of undersea optical fiber communication cables, etc.However, a large amount of beryllium is oxidized to BeO in melting stage of the current Cu-Be alloy production process, because beryllium is a highly reactive element. This is one of the ·main factors that negatively affect the production yield and th_e product quality."

Jan 1, 2000

By Y. Sako, E. Nomura, K. Muraguchi, K. Shibata

In 1998, Mitsui Mining & Smelting Co., Ltd. (MMS) produced 70,000 tonnes of lead, 231,000 tonnes of zinc and 214,000 tonnes of copper. MESCO, Inc. has been in charge of the automation and mechanization of smelting facilities promoted by MMS as well as the construction of facilities for chemical production and electronics materials plants, by which MESCO has contributed to the development of MMS. Initially, MESCO developed a casting machine for refined lead in the early 1960's, and thereafter, it developed a casting machine for refined zinc, a stripping machine for zinc tankhouses and energy saving facilities. In the field of copper smelting, it has also developed automation and mechanization facilities.

Jan 1, 2000

By Yoshinobu Fukumori, Testuya Watanabe, Futoshi Shikata, Hiroyuki Tokumitsu, Hideki Ichikawa, Masahito Miyamoto

Nano-particulate systems have attracted much attention recently in pharmaceutical field as drug carriers and functional components of pharmaceutical dosage forms. This paper describes our approaches in design and preparation of nano-particulate systems, including lipid nano-emulsions, chitosan nanoparticles and thermosensitive acrylic nanoparticles, for certain pharmaceutical applications mentioned below. The lipid nano-emulsions with their particle size smaller than 100 nm were prepared for gadolinium neutron-capture therapy (Gd-NCT) of cancer by a thin-film hydration method with sonication, and intraperitoneally injected into Greene's melanoma (melanotic No. 179)-bearing Syrian hamsters. This provided such a high gadolinium concentraton in tumor as 107 µg/g tumor (wet basis) at 48 h after administration. As an alternative gadolinium nano-carrier for Gd-NCT, biodegradable and highly gadopentetate-loaded chitosan nanoparticles (Gd-nanoCPs, 426 mTI in particle diameter and 9.3% in Gd content) were prepared by a novel emulsion-droplet coalescence technique. A significant tumor-killing effect could be obtained when Gd-nanoCP suspension was injected intratumorally twice 24 and 8 hours before neutron irradiation into B 16Fl O melanoma-bearing mice and subsequently thermalneutron was irradiated toward tumor site with a flux of 2 x 109 n/cm2/sec for 60 min. As one another application of nanoparticles, a novel acrylic composite latex with a hydrophobic core and a thermosenstively swellable shell was designed for fabricating microcapsules showing thermosensitive mode of drug release. The microcapsules with the composite latex-dispersing membranes exhibited an exceptionally rapid on-off response of drug-release in a thermosensitive manner.

Jan 1, 2000

By Uchil Jayagopal, P. V. Krupakara, S. Manjunath

"This paper deals with the corrosion characterization of quartz particlate ZA-27 alloy metal matrix composites (MMCs). Quartz particles of size 50-80 microns are used as reinforcement. MMC's are prepared according to ASTM standards. Composites containing. 2, 4, and -6% by weight of quartz and unreinforced matrix were tested using 1 -N hydrochloric acid: The composite was found to be more corrosive resistant than matrix alloy. In each test the corrosion resistance of both alloy and composites were found to decrease with the exposure time.1. IntroductionMetal matrix composites- (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and light weight 1-5. The trend is towards safe usage of the MMC parts in the automobile engine, which work particularly at high temperature and pressure environments Particles reinforced MMCs has been the most popular over the last two decades.ZA alloy MMCs have most popular families being represented by. ZA-27 alloy reinforced with ceramic particulate. Although the incorporation of the second phase into a matrix material can enhance the physical and mechanical properties of the base metal, it could also significantly change the corrosion behavior.ZA alloys have been used extensively in industry. This is attributed to their excellent fludity, castability and good mechanical properties. Among the zinc-based foundry alloys, the ZA family of alloy have been widely used during the past few years. ZA alloys have many advantage over aluminium based ones, especially high strength with a low casting temperature 8."

Jan 1, 2000

By Jun Iwai, Osamu Takai, Yasushi Inoue, Hiroyuki Sugimura

"Infrared reflection absorption measurement was performed during plasma-enhanced chemical vapor deposition of silicon dioxide films at room temperature. Hydrocarbon contaminants adsorbed onto growing film surface are oxidized by oxygen radicals in plasma resulting functional groups which include C=O and C-O bondings. These groups exist only near the surface and are hydrolyzed rapidly after exposure to air.IntroductionRecently low-temperature silicon dioxide (SiO2) deposition has been in a growing industrial demand in pa1ticular, polymelic substrates such as polycarbonate and polyethylene telephthalate, which have poor heat resistance, need low process temperature (near room temperature) in coating of SiO2 which is a suitable material to improve optical and mechanical properties of polymenc products. Plasma enhanced chemical vapor deposition (PECVD) using organosilicon reactants is one of the most promising technique for lowering process temperature, so that it has been extensively studied1-12. In the present; however, hydrocarbon contaminants and a plenty of Si-OH termination in Si-O-Si networks tend to exist in the films, which degrade mechanical, optical and electrical properties of the films. It is necessary to understand the deposition mechanism at, low temperature in order to solve the problems. We have studied the low-temperature PECVD of Si02 by spectroscopic diagnosing techniques such as optical emission and mass analysis6-7, 11- 12Infrared reflection absorption spectroscopy (IR-RAS) has been a well-established technique for characterization of thin films on metals as· well as on semiconductors and insulators13-17. In this paper, we report on' the surface reaction of room-temperature PECVD of Si02by using in situ IR-RAS."

Jan 1, 2000

By P. Klut, D. Groult, R. Marechalle, B. T. H. Bonnema

In the past 5 years, Compagnie Europeenne de Dezingage (CED) has developed a successful dezincing process and the St. Saulve pilot plant has evolved into a commercially successful production plant. Currently the plant meets all the required standards for scrap and zinc quality, output capacity, availability, and meets the prescribed environmental emissions standards. The initial process problems relating to zinc recovery, uncontrollable explosions and sodium hydroxide aerosol emissions have all been solved. Presntly, the yearly production of dezinced scrap is around 50.000 tonnes/year; this capacity is enough to supply the local market. This capacity can be increased easily to 65.000 tonnes/year or more. The market for dezinced material is growing due to the increased consumption of galvanized material on one hand and on the other hand the higher demand for high quality scrap. The proven technology of CED is currently patented worldwide, but CED is inviting licensees to implement the dezincing technology in other parts of the world.

Jan 1, 2000

By M. J. Collins, L. C. Trytten, K. R. Buban, I. M. Masters

Both pressure leaching of zinc concentrate, in an autoclave, and atmospheric leaching, in stirred tanks, have been employed in the expansion of zinc production at plants employing roast-leach-electrowin technology. These direct leaching methods result in the conversion of the sulphur in the feed to the elemental form, rather than to sulphur dioxide, decoupling zinc production from acid production. Atmospheric and pressure leaching methods are also readily implemented over a wide range of production rates. In choosing the best technology for expansion, capital and operating costs, zinc recovery, byproduct quality and the compatibility of recycle streams with the existing refinery must be compared. Leach testwork with several zinc concentrates using both methods has been performed by Dynatec. Recent results are presented, along with a discussion of their implications for process selection.

Jan 1, 2000

By P. J. Uggowitzer, H. Kaufmann

"New Rheocasting is a novel route of semi-solid casting, in which the globular semi-solid precursor material is produced by controlled cooling of only slightly superheated melts in conventional steel crucibles. The resulting semi-solid slugs are placed into the sleeve of a vertical Squeeze Casting Machine and then filled into steel dies. Solidification occurs under hydraulic pressures up to 100 MPa Due to the reduced cost of precursor material, reduced investment cost and easier recycling, the New Rheocasting process offers cost reductions of up to 25% over conventional semi-solid casting · routes. The New Rheocast products are pore free, pressure tight, weldable and heat treatable castings.In the present work the New Rheocasting Process is introduced and the influence of heat treatment on mechanical properties of the New Rheocast alloy A356 is discussed.The alloy A356 is cast under ideal New Rheocasting conditions into a step die on an UBE HVSC 350 Squeeze Casting machine. As-east, TS and T6 heat treatment conditions with variations in solutionizing and aging time/temperature parameters are applied and the samples are tested by tensile testing. Alternatively, the same heat treatment conditions are applied to conventional Squeeze Casting parts and compared with New Rheocasting.Questions of potential cost savings due to modified heat treatment conditions are also addressed in this paper."

Jan 1, 2000

By M. Okido, R. Ichino, K. Kuroda

"Compound semiconductor, ZnTe, was electrodeposited in an acidic solution with K2TeO3, ZnSO4 and Na2SO4 solution. Since the reduction potential Te(IV)/Te(O) is remarkably noble from the solution comparing to Zn(II)/Zn(O), code position of Te and Zn was thought to be difficult from this solution. Resulting from EQCM analysis, furthermore, Te(IV) reduced to Te(O) and Te(-II) in this order so that Te catholically dissolved from the electrode surface at more negative potential. But ZnTe alloy were formed by the UPD of Zn at -0.7V at 298K on Te surface in lmM K2TeO3, 100mM ZnSO4 and 100mM Na2SO4 solution adjusted at pH 4. Content of Te in the deposits is, however, more than 80%.Electrolytic temperature is well known to affect on the deposits characteristics. The higher bath temperature was, the better ZnTe crystal was detected in this study. Thermal electrode method is a. process of heating only substrate by flowing ac current in substrate. This process makes the surface temperature of substrate higher than boiling point of the solution, 373K. From EDX analysis, deposits without thermal current were Te-rich, Te content in the deposits with thermal current decreased with increasing of thermal current. Te content was 62% for 5A ac current, 51 % for I OA and 45% for 20A, respectively. The deposits that produced with ac current of IOA were closed to the stoichiometric ratio, i.e. ZnTe.Consequently, thermal electrode method is more effective to obtain a good crystallized ZnTe without heat treatment after deposition.IntroductionThe current subject of solar cell materials is silicon. Compound semiconductors including GaAs and II-VI group are generally used in the developing field of digital information such as the rapid cellular phone and car telephone. Compound semiconductors consist of more than 2 kinds of element. There are many materials for these compound semiconductors such a SiC, InSb, CdS for binary system and CuinSe2 for ternary system. It becomes generally difficult, to produce high quality crystal with increasing of kinds of element due to a complicated structure and a compound ratio of element. Semiconductor materials as a device are usually simple binary compounds and/or these mixed crystals. Properties of compound semiconductors have variety of the forbidden band and lattice constant and that can be change easily by addition of another element for the usage of the solar cell. Since most compound semiconductors are direct interband transition type, which has steep optics absorption edge and large light absorption coefficient."

Jan 1, 2000

By V. D. Tathavadkar

Chromite ore is of immense importance for the extraction of metallic chromium and chromium chemicals. The mineralogy and crystal structure of chromite phase are therefore important part of our investigation on the extraction chemistry of chromium species. In this investigation, we have studied the effect of the processing parameters, i.e., the temperature and the oxygen potential on the microstructure and composition of mineral phases formed in the Cr2O3 ?Al2O3 -FexOy -MgO system. In particular the importance of the spinodal decomposition reaction is emphasized in the extraction of chromium as sodium chromite and sodium chromate. Experiments were carried out in order to study the differences in the crystallography of different chromite minerals. Phase equilibria in natural chromite minerals were investigated by calcining chromite mineral in air, argon, and 5% hydrogen + argon atmospheres over a temperature range from 200 to 1200 °C. The effect of the oxygen partial pressure and temperature on the phase constituents of the calcined product has been discussed. The microstructural changes were examined using scanning electron microscope (SEM) and the changes in elemental composition in different phases were analysed by electron probe micro analyser (EPMA). The results obtained from EPMA studies were used to calculate lattice parameter of the spinel lattice, and these values were compared with the values obtained from X-Ray powder diffraction data. On the basis of the experimental data, the mechanism of the spinodal decomposition of complex spinel phases is described under the influence of oxygen partial pressure and temperature.

Jan 1, 2000

By Tadashi Aiura, Yasuhiro Miura

"A small amount(0.2mass%) of Scandium(Sc) was added to the 7.NOl and 5083 Al alloys as a refiner and stabilizer of microstructure, and the resulting microstructures were discussed in comparison with the effects of the conventional additives. The followings are summarized: 1) in the as-solidified structure, a ·decreased tendency of constitutional supercooling and increased solubility of Mg were recognized for the Sc-added 5083 alloy. Sc is a -better microstructure refiner for the 7N01 alloy than Zr, in a sense that it does not suppress the favorable effect of· coexisting Ti. 2) Sc effectively suppresses recrystallization both in the 5083 and 7N01 alloys. 3) The rod like primary Al3Sc crystals formed during solidification, as well as the fine dispersion of Al3Sc precipitates formed by subsequent heat treatment, can act as a strong recrystallization suppresser. IntroductionThe 7N01 and 5083 alloys are the most popular industrial Al alloys and they are widely' used for various structures because of their superior properties. Fine macro and micro structures of the materials are required for obtaining acceptable sec resistance,consistent appearance of anodized surface and good weldability, as well as good mechanical properties. In order to produce fine grain structures, transition metals, such as Cr, Zr, and Mn, have been conventionally added.It has been reported that Sc is an efficient refiner [l, 2] and can be an alternative for the conventional and also suppresses recrystallization in Al alloys [3,4]. Scandium is the lightest transition element and forms an equilibrium intermetallic phase. The equilibrium phase, Ll2-Al3Sc, is coherent with the matrix, and of _spherical shape. A fine dispersion of the spherical precipitates is obtained by quenching and aging after solutionizing annealing. The authors have already reported a part of the experimental results on the effect of Sc on the as homogenized microstructure of the 5083 alloy [5]. In the present study, the effects of Sc on the macro and micro structures of the industrial high strength Al alloys(7N01 and 5083) for extrusion are investigated, and the superior role of Sc as a grain refiner is shown"

Jan 1, 2000

By J. E. Jacoby

Scrap recycling has become an increasingly important source of metal units for the aluminum industry during the past 25 years. Aluminum scrap from the manufacture and recycling of cans, automobiles, buildings and other products has created an industry that melts these products and delivers the metal in molten or sow form to companies that make cast parts or fabricated products This rapidly developing recycling industry has contributed a large number of severe (Force 3) molten aluminum explosions (25) with associated fatalities (19) to the Aluminum Association data accumulated during the past nineteen years. The explosions that occurred in recyclers plants represent 17% of the total explosions, 33% of the Force 3 explosions and 37% of the fatalities reported. These explosions can be prevented! This paper will identify causes of these explosions and procedures that can be used to prevent them.

Jan 1, 2000

By Takayoshi Fujii, Mitsumasa Hoshi, Chikashi Suenaga, Yoshiaki Suzuki

"In a bid to renovate its Saganoseki Smelter & Refinery and to establish a leading production unit in terms of global competitiveness, Nippon Mining & Metals undertook major - restructuring efforts since 1993.One of its themes was the shift from a two-flash furnaces operation to a single-flash furnace operation. The shift was successfully completed in 1996 while maintaining the production at the same level (330,000 metric tons per year of copper) by adopting such measures as improvements in pneumatic concentrate dryers, the concentrate feeding system, concentrate burners, the furnace cooling system, and a new cryogenic oxygen plant was constructed.With a view to realizing high matte grade operation (at 65%Cu) and increasing the concentrate feeding rate, further steps were taken the capacity of waste heat boiler was expanded and technical improvements were added, including optimization of the smelting reaction in the furnace shaft. As a result, the smelting capacity, as of the year 2000, has increased to 450,000 metric tons per year of copper.IntroductionThe feed rate to the flash furnace was doubled to 140 t/h from 70 t/h in 1996. Teething problems, as a result of the renovation, were almost solved by the end of 1996, and the operation of the single furnace operation has become stable.The main theme was the shift from a two-flash furnaces operation to a single-furnace operation to maintain the production capacity at the same level, namely 330,000 metric tons of copper per year. Then, in a bid to further renovate the Saganoseki Smelter & Refinery and to establish a leading production unit in terms of global competitiveness, further enhancement of the flash furnace's productivity was planned.The purpose of this plan was to raise the copper production capacity to 450,000 mtpy building on the potentialities of existing plants and without installing new equipment."

Jan 1, 2000

By Toshiyuki Hiranami, Keizou Uematsu

"AbstractionSpray freeze drying method was proposed to fabricate ·ceramic: powder granules for high performance ceramics. Obtained granules and their green compact were characterized by SEM and immersion liquid technique. Granules have a spherical shape of about l 00 µ m in diameter, ·and no binder segregation was found with the immersion liquid technique. The granule had sufficient strength for usual handling, while the strength was much lower than that of granules prepared by conventional spray-drying. Unlike the conventional green compacts, granule interfaces were not observed in the green body made with the spray-freeze dried granules.IntroductionIt was well kn9wn that spray-dried granules have binder segregation layer on their surfaces. The trace of this segregation layer survives in the later processes i.e. compaction and firing, and behaves as fracture origins in the sintered bodies. The origin of this problem is solvent drying process from slurry droplet surface in spray drying system. As alternative method we propose a freeze drying process for granule preparation, in which solvent is remove by sublimation though the process, binder segregation can be prevent.In this study, we applied spray freeze drying method to fabricate alumina powder granule, and characterized the obtained granules, and their green compacts and sintered bodies.Experimental procedure.Alumina powders and additives aqueous solution were mixed for 24 hours using a ball mill to· prepare the slurry for spray freeze drying. .The solid loading of the slurry was 30vo1%. Deflocculant (PAA-NH4 type) was added 0.5mass%, and the binder (PVA). 1.0, 2.0 or 3.0mass% of alumina. Obtained slurries were sprayed into liquid nitrogen to make frozen granules. The granules were freeze dried.For the characterization of the granules, immersion, liquid technique observation and single granule strength test were carried out. Strength of individual granule wa5 measured using micro compression testing machine (MCTM, SHIMADZU). Granule strength was calculated from following equation."

Jan 1, 2000

By K. Iwami, K. Abe

"Onahama Smelter and Refinery has been operated-since 1965 arid currently produces 243,000 metric tons per year of cathode copper. The Onahama tankhouse consists of conventional-type No.1 and 2 tankhouses with the capacity of 123,000 metric tons per year and No.3 tankhouse with 120,000 metric tons per year, adopting jumbo tank system, using hazelett anode respectively.In October, 1996, for the purpose of improving the - anode verticality, new anode copper body press machine has been installed in No.1, 2 tankhouses; by increasing Walker type anode copper weight by 35kg to 365kg. Consequently, it is possible to raise current density from 191 to 222 A/m2 and the No.1 and 2 tankhouses capacity was increased by 15,000 metric tons per year to 138,000 metric tons per year.At present, the refining capacity is 258,000 metric tons per year in total including No.3 tankhouse.This figure is the largest one in Japan.IntroductionSince the Onaham tankhouse was put into operation in 1965, the cathode copper production has increase with much labor cost saving.The following two cases to increase Walker type anode copper weight by 35kg to 365kg were studied.a) To increase the cathode copper production by raising current density.b) To save the labor cost by prolonging the anode cycle in order to decrease the exchanging time of electrodes.So the electrolytic tests were carried out to confirm· the effect of current efficiency, cathode copper quality and working conditions for space adjustment.As a result, we concluded that it was indispensable to introduce the anode body press machine to keep usual current efficiency and cathode copper quality with same workers, and to be possible to increase cathode copper production.In addition, the high-speed press machine was needed to maintain same working time and which specifications were decided through various investigations. In October 1996, the new anode body press machine made by Kawazoe Machine Works, Ltd. has been installed in No.1 tankhouse."

Jan 1, 2000

By S. Vellinga, G. H. R. Janssen, C. J. N. Buisman, C. F. M. Copini

Non-ferrous metallurgical plants are often confronted with the need to neutralize bleed streams or effluents containing sulfates. The treatment of these streams could produce large amounts of gypsum. With a biological sulfate-reduction process, the production of gypsum is avoided and the metals can be recovered as sulfides. In this paper, the biological treatment of an industrial stream is presented. The bleed solution from a roaster gas scrubber was treated by means of a two-step process. First, the acid was neutralized with calcine. The resulting zinc sulfate solution was converted to ZnS with bacteria using PAQUES-THIOPAQ® technology. The precipitated ZnS was de-watered to 70 wt% solids, and was returned to the roasters. The quality of the effluent stream complied with the environmental regulations.

Jan 1, 2000

By C. Frias, M. Garcia, G. Diaz

Advances in hydrometallurgy promoted by Tecnicas Reunidas are providing increasingly simple and clean means for controlling the entire lead recycling chain. Used in parallel with pyrometallurgy, these processes allow furnace temperatures to be reduced and fumes and atmospheric pollution to be minimised. Furnace slags are digested, and residues (mainly gypsum) are non-toxic and convertible into marketable products. In addition, the global economy of the process is substantially improved by reducing the operating cost, increasing the lead recovery above 99% and obtaining a 99.99% pure lead product. These new PLACID and PLINT processes may provide the cleanest and healthiest practicable means for recycling lead from batteries.

Jan 1, 2000

By Shigehito Deki

"A new wet process has been developed for the synthesis of various kinds of oxide thin films on various kinds of substrates, even which have complex surface morphology, from aqueous solution. The process was named as the LPD, Liquid Phase Deposition, method, which has some advantages over the conventional dry processes. This process can be applied to an on-site synthesis of advanced materials in the thin film technology. In this paper, some current topics on the synthesis of the composite thin oxide films by the LPD method, are presented.IntroductionGenerally, metal oxide thin films have been made by different preparative processes such as r.f. sputtering, chemical vapor depositon, CVD, laser ablation and sol-gel method, etc [1-3]. Each method has it own advantages and disadvantage. In some cases, the process is not suitable for the preparation of thin film on substrate with large surface area or complex surface morphology, and makes the deposition apparatus complicated and expenisve. By using Liquid Phase Deposition, LPD, method which overcomes some of those problems, metal oxide or hydroxide thin film can be formed on the substrate with large surface area and complex surface morphology, which are immersed into the aqueous solution only at ambient temperature and under atmosphere without any special equipments and high energy. And also, multicomponent oxide thin films can be formed readily by mixing solutions containing the objective metal ions, because it is performed in the aqueous solution which is typically a homogeneous mixing system. This process utilizes ligand-exchange, hydrolysis, equlibrium reaction of metal-fluoro complex species, MF x (x-2n>-, and F consumptive reaction. In the aqueous solution, MFx<x-2n>-is hydrolyzed with water to release F ions by a ligand exchange equilibrium reaction as following;"

Jan 1, 2000

By P. A. Treasure

The EMEW® cell has been developed to overcome a number of inherent limitations in conventional electrowinning technology, particularly the high cost and restricted process windows characteristic of conventional hardware. The technology has been widely demonstrated to achieve high performance for various metals under chemical conditions well outside the limits required for efficient operation of conventional cells. This process flexibility offers significant opportunities for cost savings. in recovery of zinc from primary and secondary sources. The EMEW® technology is now available on a fully engineered basis, as a versatile commercial alternative to conventional electrowinning hardware. Application of the EMEW® cell for recovery of secondary zinc material offers significant advantages to the recycling industry. For example, a selective caustic leach can be used where there are high levels of iron or other contaminants in the target material. The reagent requirement is minimal as most of the caustic is regenerated in the bell and zinc dust that may be required for electrolyte purification is produced in the cell. A high purity zinc powder or cathode is produced in the cell. In the case of acidic zinc electrolytes, the cell is capable of operating over a much wider range of operating conditions than a conventional cell.

Jan 1, 2000