By Xiaolong Lin, Yuanbo Zhang, Tiancheng Nie, Guanghui Li, Zhizhong Li, Zhiwei Peng, Tao Jiang

The coal-based direct reduction process has gradually become the focus of research concerning direct reduced iron production due to its advantages, including high reduction rate, stable chemical composition, and good metallurgical properties of products. Based on coal-based reduction theory and briquetting technique, this paper reports the use of microwave energy for intensifying the reduction of carbon-containing briquettes mainly consisting of magnetite concentrate and biochar. The heating behaviors of the raw materials show that under the conditions of microwave power of 1250 W, N flow rate of 4 L min −1 and briquetting pressure of 400 N, the briquettes present the highest heating rate. The average heating rate reaches 35.16 °C min −1. When the briquettes are irradiated by microwaves at 1050 °C for 45 min, the metallization degree of the reduced briquettes reaches 93.58%.

Mar 1, 2017

By Zhanjun Wang, Mei Zhang, Zuotai Zhang, Min Guo

In this study, the viscous flow and crystallization behavior of CaO–SiO2–MgO–Al2O3–FetO–P2O5–TiO2 steelmaking slags have been investigated over a wide range of temperatures. The results indicated that the viscosity of the slags slightly decreased with increasing TiO2 content. The constructed non-isothermal continuous cooling transformation (CCT) diagrams revealed that the addition of TiO2 lowered the crystallization temperatures. This can mainly be ascribed that the addition of TiO2 promotes the formation of [TiO6]-octahedra units, thereby MgFe2O4–Mg2TiO4 solid solution is formed. Moreover, the decreasing viscosity has a significant effect on the diffusion of ion units, such as Ca2+ and [TiO4]-tetrahedra, from bulk melts to crystal-melt interface. The crystallization of CaTiO3 and CaSiTiO5 was therefore accelerated, which can improve the phosphorus content in P-enriched phase.

Mar 1, 2017

By Geoffrey Brooks, Mehedi Bin Mohammad, M. Akbar Rhamdhani

Molten alkali nitrates are used commercially as thermal storage fluids (HTF) for solar thermal electricity generation. Their range of operation is limited by the thermal stability and this limits the energy (steam-Rankine cycle) efficiency of these processes. In this study, the effect of atmosphere on the thermal stability of nitrates was investigated using simultaneous thermal analysis techniques (STA). The use of oxygen (O2) as a blanket gas was found to delay the decomposition point of the ternary NaNO3–KNO3–LiNO3 (13.23–57.14–29.63 weight ratio) mixture by 55 °C. By which operating range will increase 65 °C more compared to the binary solar salt. Higher heating rates increased the decomposition point but had less effect on premelting and melting properties. Nitrogen monoxide, and O2 evolution after melting indicates concurrent reversible reactions. Similar phenomena were observed for single and binary nitrates. The eutectic melting point of ternary nitrate obtained from the STA agreed well with FactSage eutectic composition prediction.

Mar 1, 2017

By Bowen Li, Jiann-Yang Hwang, Mingsheng He, Huaguang Wang

Kyanite is one of the major high-alumina minerals for producing refractory ceramics. At high temperature, kyanite can be decomposed into mullite and amorphous silica. This change is an irreversible decomposition and provides potentials for fiber reinforcement of ceramic matrix. In this study, kyanite powder was compressed into a cylinder green body of ceramic and heated at 1150–1450 °C.The phase transformation of kyanite and sinterability were investigated by X-ray diffraction and scanning electron microscopy. The results showed that the phase transformation of kyanite started at 1150 °C when rising the temperature. At 1350 °C, kyanite is completely converted into mullite and silica. The compressive strength of the ceramics reached 73.3–134.8 MPa, while the bulk density was 1.95–2.47 g/cm3. The microstructure indicated the correspondence of the compressive strength to mullitization degree of kyanite.

Mar 1, 2017

By Francisco M. S. Garrido, Fabiano A. C. M. Passos, Carla N. Barbato, Karoline K. Ferreira, Danielle C. Castro, Adriana A. S. Felix, Luiz C. Bertolino, Fernanda A. N. G. Silva, Karla M. A. Simões

Cancrinite and sodalite are characterized by high capacity of adsorption due to its porous structure. The aim of this work was to use kaolin from Borborema-Seridó/Brazil as a source of aluminium and silicon to hydrothermal synthesis of sodalite and cancrinite and to evaluate the best conditions to the formation of these phases. Therefore, kaolin was heated at 700 and 900 °C for 2 h in order to transform kaolinite in metakaolin. Thereafter, experiments with the calcined kaolin’s were carried out between 150 and 230 °C for 30–270 min on a stainless steel pressure vessel using NaOH, Na2CO3 and H2O. The samples were characterized by X-ray diffraction, nuclear magnetic resonance, scanning electronic microscopy, thermogravimetry, and Zeta potential. The most pure sodalite phase was obtained at 230 °C, with the kaolin/NaOH ratio of 1:1, low concentration of Na2CO3 and smaller time of synthesis (30 min). On the other hand, for the synthesis of cancrinite phase at 230 °C, it was necessary to use kaolin heated at 900 °C, a longer time of synthesis (270 min) and a higher concentration of Na2CO3.

Mar 1, 2017

By Shigeru Ueda, Shin-ya Kitamura, Shohei Koizumi, Xu Gao

Steelmaking slag was confirmed to be a useful fertilizer for paddy growth as it efficiently supplies Ca and Si to soil water. In addition, supplement of Fe from slag fertilizer has been expected to suppress the H2S generation in paddy soil, especially for the degraded paddy soil. However, on the basis of our previous research, the Fe dissolution ability changed with slag brands, and even some brands could dissolve Fe under paddy soil pH, the supplying ability were not high. To improve Fe dissolution, we found that among various kinds of Fe-rich mineralogical phases in slag, the CaO–SiO2–FeO glassy phase showed highest water solubility of Fe. Because the CaO–SiO2–FeO glassy phase was a quenched molten phase, its dissolution behavior may depend on chemical composition, and this is important for controlling slag composition to produce fertilizer which can easily release Fe. Therefore, in this research, the CaO–SiO2–FeO glassy phase of various CaO/SiO2 ratio, Fe2+/T–Fe ratios, and FeO contents were synthesized, and the dissolution behaviors of Fe as well as other cations from these synthetic glassy phases into an aqueous solution at pH of 5 were investigated. The result showed that the dissolution ratio of Fe increased significantly by increasing Fe2+/T–Fe ratio. An increase in FeO content of glassy phase also increased the dissolution of Fe. In addition, the Fe dissolution ratio showed a local maximum with increasing CaO/SiO2 ratio.

Mar 1, 2017

By Heric Henrique Souza e Silva, Johne Jesus Mol Peixoto, Natalia Barros Barony, Itavahn Alves da Silva, Weslei Viana Gabriel, Carlos Antonio da Silva, Varadarajan Seshadri

In this work the circulation rates have been determined in a 1:7.5 scale physical model of RH reactor (Ruhrstal Heraeus) and using oil/water and oil/zinc chloride solution to simulate steel melt/slag in the prototype with the objective of evaluating the influence of density and viscosity on the entrainment of oil simulating slag. A technique based on strain gage bridge and particle image velocimetry was developed to assess the circulation rate, as the usual tracer method is not feasible due to the presence of chloride ions in ZnCl2. The critical velocity and critical diameter of oil drops for slag (oil) entrainment in water/oil and ZnCl2/oil systems were estimated using equations from the literature. Due to the difference in density, the ZnCl2/oil system, showed a critical velocity that is 28% higher than the silicone oil/water system while the maximum size of the entrained droplets was about 65% lower than that for water/oil system.

Mar 1, 2017

By Ramana G. Reddy, Yudong Li

Numerical modeling of the thermal plasma process was carried out based on the thermal plasma reactor in our lab and confirmed using experimental data. The inlet boundary conditions of a non-transferred DC arc thermal plasma reactor were used in modeling the temperature and fluid flow distribution in the reactor. Different mesh grid sizes were used to confirm the model is independent of grid size. Temperature profile and gas flow distribution in the thermal plasma reactor were developed by the computational fluid dynamics (CFD) with ANSYS Fluent. The predicted temperatures are in good agreement with the experimentally measured temperatures in the reactor. The influence of plasma torch input power as well as the plasma gas flux on the temperature distribution was investigated using this model. The influence of power input and gas flow rate on temperature and velocity distributions are not independent. Generally, higher power input and lower gas flow rate will give rise to the temperature increase in the reactor.

Mar 1, 2017

By Jorge Alberto Soares Tenório, Amilton Barbosa Botelho Jr, Denise Crocce Romano Espinosa, Mónica M. Jiménez Correa

Wastewater from nickel lateritic process still has valuable metals that could be recovered. Using an ion exchange to recovery these metals, the iron becomes a problem due to the fact that it precipitate at pH 2. The aim of this research was to make iron soluble by reducing Fe+3 to Fe+2. A synthetic solution was prepared with sulfate ferric. The reducing agent sodium dithionite was used and the potential was varied (initial potential: 700, 600, 500, 450 e 400 mV) using as a reference the Pourbaix diagram for iron created by HydroMedusa software. The pH was ranged between 0.5 and 2.5, the reducing agent’s concentration was 0.5 M and the reaction time ranged between 30 and 120 min at room temperature. The ferric iron and total iron concentration were verified using a spectrophotometer with 5-sulfosalicylic acid (SSA) to determine Fe(III) and ammonia to determine Fe(II) and Fe(III) in 500 and 425 nm, respectively. The results indicated that total reduction was at 400 mV in any pH between 0.5 and 2, but less than 40% in pH 2.5 at this potential value.

Mar 1, 2017

By Dachun Liu, Xuepeng Li

Smelting-acid leaching process is a way to treat high-content arsenic containing copper dust. However, smelting makes a low recovery of valuable metals and acid-leaching produces large amounts of arsenic-iron slag. Arsenic sulphuration volatilization at low temperature was studied, followed by pressure leaching to selectively recover Cu, Zn, and In from copper smelting dust while minimizing arsenic contamination.

Mar 1, 2017

By Gisele Azimi, Jason Tam, Adrian Lambert

Many advanced technologies in modern society require the use of rare earth elements (REEs). Since these technologies are dominating the world, the demand for REEs is increasing fast. Finding new sources for them is highly of interest. One secondary source of REEs is phosphogypsum (PG), a by-product of the phosphate fertilizer industry. Microwave treatment is investigated as a method to enhance hydrometallurgical recovery of REEs from phosphogypsum, with results showing a 30% improvement in leaching efficiency.

Mar 1, 2017

By Muhammad A. Imam, Ramana G. Reddy

This study provides a reasonable evaluation of the Mg-B binary system. Magnesium and Boron (Mg-B) alloys were investigated to determine their thermodynamic properties employing solid state electrochemical cells based on CaF2 electrolyte represented as –Pt; Ar= MgþCaMgF4 f gCaF2 k kf½Mg B alloy þ CaMgF4 g=Ar; Pt+ Investigations were performed over the temperature range of 773–873 K to measure the electromotive force (EMF), which was used to derive the partial Gibbs Free energies of the alloys in the composition range of XB = 0.07 to 0.95. The activities of Mg were also calculated from partial Gibbs Free energies. The activities of Mg in MgB2, MgB4, and MgB7 were expressed as a function of temperature respectively, ln aMg = 4.27–9.32 × 103/T, ln aMg = −7.54 + 6.67×103/T, and ln aMg = 4.93–19.57 × 103/T, where T is the temperature in K. From this expression, the activity of Mg for these intermediate phases can be extrapolated at a higher temperature to get the accurate phase boundaries for the Mg-B system.

Mar 1, 2017

By Wei Lv, Xuewei Lv, Senwei Xuan, Chenguang Bai, Kai Tang

The contact angle between six iron ores and water were determined by the capillary pressure method with cyclohexane as the perfect wetting liquid. The factors influencing the contact angle were discussed, and a relationship between the content of oxy–hydroxides and the contact angle of iron ores was obtained. The results show that the ore F has the lowest contact angle but the ore D get the biggest, which are 32.09° and 78.16°, respectively. The volume fraction of oxy–hydroxides is linearly dependent on the contact angle. The contact angle decreased with increasing the volume fraction of Fe2O3*H2O.

Mar 1, 2017

By S. Chama, P. Chishimba, Tina Chanda Phiri, J. Machona, S. Parirenyatwa, G. Kaluba, Y. R. S. Hara, D. M. Musowoya

The investigation focuses on leaching of copper (2 wt%), cobalt (0.5 wt%) and iron (2.4 wt%) from complex tailings material from the Democratic Republic of Congo. The highest recovery of copper and cobalt into the leach solution were 78 and 10%, respectively, under direct leaching with sulphuric acid. Higher recoveries (90% for copper and 96% for cobalt) were attained when the material was pre-reduced with coal for 1.5 h in the temperature range of 700–950 °C. The increased recoveries were due to metallisation of all the copper and cobalt which is in the silicate matrix. The effects of pre-reduction temperature and sample to carbon weight ratios were analysed and found to be important in; (i) achieving high recoveries of copper and cobalt and (ii) decreasing the amount of iron in the leach solution. The samples were characterised by atomic absorption spectroscopy and scanning electron microscopy (SEM) techniques.

Mar 1, 2017

By Leiv Kolbeinsen, Vincent Canaguier, Ingeborg-Helene Svenum

The syntheses of stoichiometric iron chromite and chromites with chosen impurity content have been developed using the induction skull melting technique. The aim for this synthetic material is to obtain pure samples to study the carburization by methane-hydrogen gas mixtures. For each synthesis, the parameters influencing the skull melting experiment have been considered. The product phases have been analyzed using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Spectroscopy (EDS) and X-ray Photoelectron Spectroscopy (XPS). The synthetic material was subsequently pelletized and sintered in argon. The use of excess iron was found to improve the quality of the final product as well as to help the melting. The difference in magnesium content between first and last solids formed seem to indicate a segregation phenomenon, while no evidence could support a similar trend for aluminum substitution in chromite.

Mar 1, 2017

By Uday Pal, Shizhao Su, Thomas Villalon

Compared with the current Hall–Héroult process for smelting aluminum, the Solid Oxide Membrane (SOM)-Based electrolysis process brings various advantages such as simplified design, lower cost, lower energy use, and many other environmental bene fits. However, the state-of-the-art SOM electrolysis process is limited by the solid oxide membrane’s stability and its compatibility with the molten salt and the electrode materials. This work will identify cost-effective molten salt compositions and membrane materials/architecture along with electrodes and current collectors that are all chemically compatible and provide optimum electrochemical properties for efficient aluminum oxide electrolysis.

Mar 1, 2017

By Bora Derin

This study is a collection of both newly published and/or presented works on impurity capacity predictions in molten melts which were carried out by Derinetal. Some sulfide capacity prediction results of iron oxide containing ternary silicate melts and industrial lead and copper slags using the Reddy-Blander model and some impurity capacity predictions of multicomponent oxide and salt melts obtained using a Artificial Neural Network Approach are discussed.

Mar 1, 2017

By Laura Angeles, Martin Reyes, Ivan Reyes, Miguel Perez, Francisco Patiño, Mizraim Flores, Elia Palacios

Chemical and mineralogical characterization of a sulphide ore from the mining district of Zimapan, Hidalgo, Mexico, was performed in order to obtain accurate information on the composition of the ore to optimize the subsequent flotation process. A combination of techniques was used: Scanning Electron Microscopy (SEM) with Energy Dispersive Spectrometer (EDS), X-ray diffractometry (XRD), Inductively Coupled Plasma (ICP) and Fourier transform infrared spectroscopy (FTIR). The SEM mapping confirmed the presence of the elements: Ca, Si, Fe, K, S, Al, Zn, Mg and Mn. The XRD analysis suggests that the ore matrix is calcite; additional species found were wollastonite, johannsenite, and pyrite, among other impurities. The FTIR analysis performed for the aqua regia insoluble showed the presence of calcium oxide, copper oxide and silicon oxide. The results for the ICP analysis were:13.31% S, 2.55% Fe, 0.46% Zn, 0.03% Cu, 0.06% Pb, 0.07% Mn, 0.09% As, 0.01% Sb and 0.08 grton-1 Ag.

Mar 1, 2017

By Chengyi Ding, Xuewei Lv, Senwei Xuan, Jie Qiu, Yun Chen, Kai Tang

Isothermal reduction kinetics of CF2 by 30% CO and 70% N2 at 1123, 1173 and 1223 K was investigated by TGA in this study. The reduction rate analysis indicated that reduction of CF2 comprises three stages during the whole reduction process, Apparent activation energy of samples CF2 reduction is 34.37 kJ/mol. The ln-ln analysis implied the reduction of CF2 was expressed initially by a 2D subsequently by 3D shrinking layer reaction.

Mar 1, 2017

By Mostafa Maazouz, Jeff Blackwood, Mauricio Gordillo, Sang Hoon Lee, Micah Ledoux, Liang Zhang

To meet rising requirements for the low-damage ultra-fine process with the focused ion beam (FIB) in the materials science and semiconductor industry, the advanced ion column and corresponding advanced applications as a solution are developed and demonstrated. Novel high-speed high kV milling, low kV cleaning and imaging capabilities have enabled the creation of impeccable ultra-thin structures such as TEM samples and nanometer scale structures. Minimizing Ga+ induced sample damage is achieved through the optimized final cleaning at 500 eV ion landing energy with the new ion optics, which utilizes close control of the ion dose, beam incidence angle, spot size, pattern algorithm and imaging performance. Newly introduced process solutions achieve the improved process throughput. Initial demonstration is performed on the latest 14 and 10 nm scale FinFET device. Validation of the thinnest <0.8 nm thick ion damage layer on the <7 nm thick lamella structure was confirmed through TEM analysis.

Mar 1, 2017